KAJIAN APLIKASI EKSTRAK KAYU PIONERA BIOPOLYMER

L-800 DALAM MENINGKATKAN KINERJA PROSES LEACHING

DAN ADSORPSI EMAS-PERAK OLEH KARBON AKTIF

DI PT ANTAM TBK UBPE PONGKOR Preliminary Study on Aplication of Pionera Biopolymer L-800 Wood

Extract to Increase the Mechamism of Gold-Silver Leaching Process

and Adsorption by Activated Carbon

at PT Antam Tbk UBPE Pongkor

TUGAS AKHIR

Oleh DEA ISMARLINA NIM. 091411006 GIFTIANI CITRA NIM. 091411011

PROGRAM STUDI DIII TEKNIK KIMIA

JURUSAN TEKNIK KIMIA

POLITEKNIK NEGERI BANDUNG

2012

 

 

 

 

 

 

 

 

 

 

 

 

KAJIAN APLIKASI EKSTRAK KAYU PIONERA BIOPOLYMER

L-800 DALAM MENINGKATKAN KINERJA PROSES LEACHING

DAN ADSORPSI EMAS-PERAK OLEH KARBON AKTIF

DI PT ANTAM TBK UBPE PONGKOR Preliminary Study on Aplication of Pionera Biopolymer L-800 Wood

Extract to Increase the Mechamism of Gold-Silver Leaching Process

and Adsorption by Activated Carbon

at PT Antam Tbk UBPE Pongkor

Diajukan untuk memenuhi salah satu persyaratan dalam menyelesaikan Program Studi Diploma III Teknik Kimia Jurusan Teknik Kimia

TUGAS AKHIR

Oleh DEA ISMARLINA NIM. 091411006 GIFTIANI CITRA NIM. 091411011

PROGRAM STUDI DIII TEKNIK KIMIA

JURUSAN TEKNIK KIMIA

POLITEKNIK NEGERI BANDUNG

2012

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Curiculum Vitae

Nama : Dea Ismarlina

NIM : 091411006

Tempat Tanggal Lahir : Bandung, 29 September 1991 SD Lulus Tahun : 2003 di SDN Perumnas Cijerah II SMP Lulus Tahun : 2006 di SMPN 36 Bandung SMA Lulus Tahun : 2009 di SMKN 7 Bandung

Nama : Giftiani Citra

NIM : 091411011

Tempat Tanggal Lahir : Bandung, 12 Maret 1991 SD Lulus Tahun : 2003 di SDN Krida Utama SMP Lulus Tahun : 2006 di SMPN 1 Cimahi SMA Lulus Tahun : 2009 di SMAN 3 Bandung

 

 

 

 

 

 

 

 

 

 

 

 

KATA PENGANTAR

Puji dan syukur penyusun panjatkan kehadirat Allah SWT yang senantiasa memberikan rahmat dan karunia-Nya sehingga penulis dapat menyelesaikan Tugas Akhir beserta laporannya yang berjudul “Kajian Aplikasi Ekstrak Kayu Pionera Biopolymer L-800 dalam Meningkatkan Kinerja Proses Leaching dan Adsorpsi Emas-Perak oleh Karbon Aktif Di PT Antam Tbk. UBPE Pongkor”.

Tugas Akhir ini merupakan salah satu syarat untuk menyelesaikan Pendidikan Diploma III Teknik Kimia Jurusan Teknik Kimia Politeknik Negeri Bandung.

Pada kesempatan ini penyusun ingin menyampaikan rasa terima kasih atas segala bantuan, dukungan, kerja sama, dan saran yang telah diberikan antara lain kepada: 1. Ir. Dwi Nirwantoro, M.T, selaku Ketua Jurusan Teknik Kimia Politeknik

Negeri Bandung. 2. Rispiandi, M.T, selaku Ketua Program Studi D III Teknik Kimia dan Koordinator

Tugas Akhir 3. Ir. Ninik Lintang, M.T, selaku pembimbing I. 4. Adam Pratomo, S.T, selaku pembimbing II. 5. Semua pihak yang telah banyak membantu namun tidak dapat disebutkan satu

persatu. Penyusun menyadari bahwa laporan Tugas Akhir ini masih sangat

jauh dari sempurna. Oleh karena itu, penyusun menerima dengan tangan terbuka segala saran dan kritik yang membangun dari semua pihak demi perbaikan ke depannya.

Akhir kata, penyusun berharap semoga laporan Tugas Akhir ini dapat memberikan manfaat kepada setiap pembaca.

Bandung, Juli 2012

Penyusun

 

 

 

 

 

 

 

 

 

 

 

 

ABSTRAK Salah satu proses penting dalam mengolah emas (Au) dan perak (Ag) di PT Aneka Tambang Tbk. Unit Bisnis Pertambangan Emas Pongkor adalah proses leaching dan Carbon In Leach. Pada proses leaching, slurry dilarutkan dengan pelarut NaCN sampai diperoleh senyawa kompleks NaAu(CN)2 dan NaAg(CN)2. Pada proses Carbon In Leach senyawa kompleks NaAu(CN)2 dan NaAg(CN)2 kemudian diadsorp oleh karbon aktif. Dikarenakan kandungan emas dan perak dalam bijih/ore semakin berkurang, maka perolehan emas dan perak pun ikut menurun. Oleh karena itu dilakukan pembaharuan peningkatan kinerja leaching dan adsorpsi yaitu dengan penambahan ekstrak kayu Pionera Biopolymer L-800. Penelitian ini bertujuan untuk mengetahui pengaruh dari penambahan ekstrak kayu Pionera Biopolymer L-800 pada proses leaching dan carbon in leach sehingga diharapkan recovery emas dan perak dapat meningkat. Variasi ekstrak kayu yang ditambahkan pada proses leaching adalah 0; 195; 390; 585; dan 780 ppm, sedangkan variasi karbon adalah 526; 2532; 5064; dan 12908 ppm. Hasil penelitian menunjukkan bahwa konsentrasi optimum ekstrak kayu yang digunakan adalah 240 ppm yang dapat menaikkan recovery emas dari 85% menjadi 89% (peningkatan 4%) dan perak dari 83% menjadi 90% (peningkatan 7%). Secara ekonomis keuntungan yang diperoleh setelah dilakukan penambahan ekstrak kayu adalah Rp. 3,3 M setiap bulan.

Kata Kunci : ekstrak kayu, leaching, adsorpsi, recovery.

 

 

 

 

 

 

 

 

 

 

 

 

ABSTRACT The main processes in gold (Au) and silver (Ag) processing at PT Aneka Tambang Tbk. Gold Mining Bussiness Unit Pongkor are leaching and Carbon In Leach process. In Leaching process, slurry is dissolved by NaCN until producing the complex compounds NaAu(CN)2 dan NaAg(CN)2. In Carbon in Leach process, complex compounds NaAu(CN)2 dan NaAg(CN)2 then adsorped by activated carbon. Lately, contents of gold and silver in ore keep decreasing and so does the gold and silver recovery. Therefore the company try to make innovation in the process, one of which is by using wood extract of Pionera Biopolymer L-800. The purpose of this research was to find out the relation influence of Pionera Biopolymer L-800 extract to leaching and carbon in leach process so that the gold and silver recovery will increase. Variation of wood extract used in this research were 0; 195; 390; 585; and 780 ppm, meanwhile the carbon variation used were 526; 2532; 5064; and 12908 ppm. Based on the research result, optimum concentrate of wood extract used was 240 ppm which increase from 85% to 89% (increased 4%) of gold recovery and 83% to 90% (increased 7%) for silver. It also can increasing economic profit as much as Rp. 3,3 billion per month.

Key word : wood extract, leaching, adsorption, recovery.

 

 

 

 

 

 

 

 

 

 

 

 

DAFTAR ISI

HALAMAN DEPAN HALAMAN JUDUL LEMBAR PENGESAHAN KATA PENGANTAR .................................................................................................... i ABSTRAK ......................................................................................................... ii ABSTRACT ......................................................................................................... iii DAFTAR ISI ...................................................................................................... iv DAFTAR TABEL ............................................................................................... v DAFTAR GAMBAR ......................................................................................... vi DAFTAR LAMPIRAN ....................................................................................... vii BAB I PENDAHULUAN 1.1 Latar Belakang Penelitian ............................................................................ 1 1.2 Tujuan Penelitian ......................................................................................... 3 1.3 Ruang Lingkup Penelitian ............................................................................. 3 1.4 Tahapan Penelitian ....................................................................................... 5 1.5 Sistematika Penulisan .................................................................................. 6 BAB II TINJAUAN PUSTAKA 2.1 Pengolahan Emas dan Perak ........................................................................ 7 2.2 Leaching ........................................................................................................ 8 2.3 Ekstrak Kayu ................................................................................................. 13 2.4 Adsorpsi ....................................................................................................... 16 2.5 Karbon Aktif ................................................................................................ 19 2.5.1 Struktur Karbon Aktif .......................................................................... 20 2.5.2 Pori-pori Karbon Aktif ......................................................................... 21 2.6 Emas dan Perak ............................................................................................ 21 2.6.1 Sifat-Sifat Fisik dan Kimia Emas ............................................................ 21 2.6.2 Sifat-Sifat Fisik dan Kimia Perak .......................................................... 23 BAB III METODOLOGI PENELITIAN 3.1 Tahap Persiapan ............................................................................................ 24 3.1.1 Persiapan Bahan ............................................................................... 24 3.1.2 Persiapan Alat .................................................................................. 25 3.2 Tahap Percobaan .......................................................................................... 25 3.3 Tahap Analisis .............................................................................................. 26 3.4 Pengolahan Data ........................................................................................... 28 BAB IV HASIL DAN PEMBAHASAN ............................................................ 30 BAB V SIMPULAN DAN SARAN .................................................................. 40 DAFTAR PUSTAKA LAMPIRAN

 

 

 

 

 

 

 

 

 

 

 

 

DAFTAR TABEL Tabel 2.1 Spesifikasi Karbon Aktif Norit RO3515 ............................................... 20 Tabel 2.2 Sifat Fisik dan Kimia Emas ............................................................. 22 Tabel 2.3 Sifat Fisik dan Kimia Perak ............................................................ 23 Tabel 3.1 Perbandingan Kondisi Proses Skala Plant dengan Skala

Laboratorium ................................................................................... 26 Tabel 4.1 Matriks Persen Ekstraksi Percobaan Leaching dengan

Penambahan Ekstrak Kayu .............................................................. 35 Tabel 4.2 Kandungan Logam Au-Ag pada Ore .............................................. 38 Tabel 4.3 Pengaruh Ekstrak Kayu Terhadap Total Recovery dengan

Variasi Konsentrasi Karbon pada Kondisi 35% padatan ................ 38

 

 

 

 

 

 

 

 

 

 

 

 

DAFTAR GAMBAR Gambar 2.1 Diagram Alir Proses Pengolahan Bijih Emas ............................. 7 Gambar 2.2 Kurva Pengaruh Sianida terhadap Recovery ............................... 10 Gambar 2.3 Kurva Pengaruh pH Terhadap % HCN ...................................... 11 Gambar 2.4 Kurva Pengaruh Temperatur terhadap Recovery Au .................. 12 Gambar 2.5 Kurva Pengaruh Kecepatan Pengadukan terhadap Kecepatan Pelarutan Emas ......................................................... 13 Gambar 2.6 Struktur Kimia Pionera Biopolymer L-800 ................................ 14 Gambar 2.7 Mekanisme Dispersi ................................................................... 15 Gambar 2.8 Kurva Pengaruh Penambahan Ekstrak Kayu Terhadap Recovery ..................................................................... 15 Gambar 2.9 Kurva Pengaruh Penambahan Ekstrak Kayu terhadap Viskositas Slurry ........................................................................ 16 Gambar 2.10 Kurva Pengaruh Temperatur terhadap Adsorpsi Au .................. 17 Gambar 2.11 Kurva Pengaruh pH terhadap Adsorpsi ...................................... 18 Gambar 2.12 Foulants pada Karbon Aktif ....................................................... 19 Gambar 2.13 Struktur Karbon Aktif ................................................................. 21 Gambar 3.1 Diagram Alir Percobaan Leaching dan Carbon In Leach Variasi Dosis Ekstrak Kayu Skala Laboratorium dan Analisis Hasil Percobaan .......................................................................... 27 Gambar 3.2 Diagram Alir Percobaan Leaching dan Carbon In Leach Variasi Dosis Karbon Skala Laboratorium dan Analisis Hasil Percobaan .......................................................................... 28 Gambar 4 Diagram Alir Percobaan Roll Bottle ........................................... 31 Gambar 4.2 Pengaruh Konsentrasi Ekstrak Kayu terhadap Persen Ekstraksi Au dan Ag pada Kondisi Persen Solid 35% ............... 32 Gambar 4.3 Pengaruh Konsentrasi Ekstrak Kayu terhadap Viskositas .......... 32 Gambar 4.4 Pengaruh Konsentrasi Ekstrak Kayu terhadap Penggunaan Sianida pada Tahap Leaching dan CIL pada Kondisi Persen Solid 35% ........................................................................ 33 Gambar 4.5 Pengaruh Konsentrasi Ekstrak Kayu terhadap Persen CIL Recovery Emas-Perak pada Kondisi Persen Solid 35% .............. 34 Gambar 4.6 Pengaruh Konsentrasi Ekstrak Kayu terhadap Persen total Recovery Emas dan Perak pada Kondisi Persen Solid 35% ........ 34 Gambar 4.7 Pengaruh Konsentrasi Karbon terhadap Persen total recovery Emas-Perak pada Kondisi Persen Solid 35% dan Konsentrasi Ekstrak Kayu 240 ppm ............................................................... 36 Gambar 4.8 Hubungan Variasi Konsentrasi Karbon dengan Berat Logam yang Teradsorp oleh Karbon ...................................................... 37 Gambar 4.9 Skema plant test ekstrak kayu .................................................... 39

 

 

 

 

 

 

 

 

 

 

 

 

DAFTAR LAMPIRAN LAMPIRAN A ................................................................. Data Penelitian

LAMPIRAN B ................................................................. Perhitungan Data

LAMPIRAN C ................................................................. Prosedur Kerja Analisis

LAMPIRAN D ................................................................. Alat dan Bahan

LAMPIRAN E ................................................................. Gambaran Percobaan

LAMPIRAN F ................................................................. MSDS Reagen

LAMPIRAN G ................................................................. Form Bimbingan

LAMPIRAN H ................................................................. Form Perbaikan

 

 

 

 

 

 

 

 

 

 

 

 

DAFTAR PUSTAKA

Adukan Eko Mortar Bangunan Menggunakan Aditif Dispersan Natrium

Lignosulfonat dari Limbah Industri Pulp Kertas Atau Lindi Hitam.

http://journal.ipb.ac.id/index.php/jurnaltin/article/view/3143/2094. Diakses

tanggal 13 Mei 2012.

Dispersing Agent Functionalities Borregaard LignoTech.

http://www.lignotech.com/Functionalities/Dispersing-Agent. Diakses

tanggal 14 Maret 2012.

Ekstraksi Padat Cair (Leaching). http://heriut.blogspot.com/2011/05/ekstraksi-

padat-cair-leaching.html. Diakses tanggal 12 juni 2012.

Leaching. http://hanasoraya.blogspot.com/2009_10_01_archive.html. Diakses

tanggal 14 juni 2012.

Marsden, John and C. Iain House. 2006. The Chemistry of Gold

Extraction, 2nd edition. Society for Mining, Metallurgy and Exploration,

Inc. : USA.

Metalliferous Mining – Processing : Elution and Carbon Reactivation

Resource Book. rsteyn.files.wordpress.com/2010/elution-and-carbon-

reactivation- basics.pdf. Diakses tanggal 14 Juni 2012.

Metalliferous Mining – Processing : Leaching and Adsorption Resource Book.

rsteyn.files.wordpress.com/2010/leaching-adsorption-basics-and-

example.pdf. Diakses tanggal 14 Juni 2012.

Neville A. M. 1981. Properties of Concrete Admixtures. 3rd. Pitman Publishing.

Ouyang X, Qiu X, Chen P. 2006. Physico-Chemical Characterization of Calsium

Lignosulfonate. A Potentially Useful Water Reducer Colloids and Surfaces

A: Physico-Chem. Eng. Aspects. 283-286;489-497.

Pembuatan Natrium Lignosulfonat Berbahan Dasar Lignin Isolat Tandan

Kosong Kelapa Sawit : Identifikasi, Dan Uji Kinerjanya Sebagai Bahan

Pendispersi.

http://journal.ipb.ac.id/index.php/jurnaltin/article/view/1101/183. Diakses

tanggal 13 Mei 2012.

 

 

 

 

 

 

 

 

 

 

 

 

Pionera Biopolymer. Pioneering Solution in Mineral Processing. 2012.

Rosen M. J. Dan M. Dahanayake. 2000. Industrial Utilizasion of Surfactant :

Principle and Practice. Illinois AOCS Press, Champaign.

Wikipedia : http://id.wikipedia.org/wiki/Emas. Diakses tanggal 12 Juni 2012.

Wikipedia : http://id.wikipedia.org/wiki/Perak. Diakses tanggal 12 Juni 2012.