SSL-UCB, ALD MCP Test Progress. Sent two MCPs for Al 2 O 3 ALD coating of half surface Both MCPs standard glass MCPs ~ 90Meg Ω. SSL-UCB, ALD MCP Test Progress. The two MCP assemblies were tightened differently, the 12nm sample (left) shows a shadow where the MCP was - PowerPoint PPT Presentation
Citation preview
Space Sciences Laboratory, University of California, BerkeleySSL-UCB, ALD MCP Test Progress
Sent two MCPs for Al2O3 ALD coating of half surface
Both MCPs standard glass MCPs ~ 90Meg Ω
Space Sciences Laboratory, University of California, Berkeley
SSL-UCB, ALD MCP Test Progress
The two MCP assemblies were tightened differently, the
12nm sample (left) shows a shadow where the MCP was
clamped in, the 6nm (right) sample shows no deposits at all.
The 12nm MCP was a bit loose, and the 6nm was tight.
Space Sciences Laboratory, University of California, BerkeleySSL-UCB, ALD MCP Test ProgressML201-B-2 12nm ALD shows some debris and smudging that was removed in cleaning
Before cleaning
After cleaning
Space Sciences Laboratory, University of California, BerkeleySSL-UCB, ALD MCP Test ProgressML201-B-1 6nm ALD shows less debris and smudging, - was removed in cleaning
Before cleaning
After cleaning
Space Sciences Laboratory, University of California, Berkeley
Initial Imaging Results on Standard MCPswith 6nm ALD coating
1150v MCP, 2800v Screen, UV floodPhotonis ML201-B-1 MCP, 86MΩ
1050v MCP, 2900v Screen, UV floodPhotonis ML201-B-1 MCP, 86MΩ
Shows definite enhancement of brightness in ALD areaNo degradation of image quality, except at the boundary zone for coating