DODATNI MATERIJALI ZA ZAVARIVANJE ALUMINIJUMA I ALUMINIJUMSKIH LEGURA

MIG POSTUPAK

Komercijalni

naziv Oznake po standardima Hem. sastav (wt %)

Mehanicke osobine Zastitni gas Prečnik

(mm)

Alumig 99.5

AWS A5.10-92 ER 1100 BS 2901-90 1050 A DIN 1732-88 SG-Al 99.5 NF A81-331 Al 99.5 Werkstoff no. 3.0259

≥99.5 Al; 0.01 Zn; 0.06 Fe

Rpo.2=30 N/mm2; Rm= 100 N/mm2;

A5= 37%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Alumig Mg 3

AWS A5.10-92 ER 5754 DIN 1732-88 SG-Al Mg 3 NF A81-331 AG 3/ AlMg 3 Werkstoff no. 3.3536

0.1 Zn; 3.2 Mg; 0.25 Fe

Rpo.2=120 N/mm2;Rm= 230 N/mm2;

A5= 22%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Alumig Mg 3.5 Mn

BS 2901-90 5154 A NF A81-331 AlMg3.5

0.4 Mn; 0.1 Zn; 3.3 Mg; 0.35 Fe;

Rpo.2=125 N/mm2;Rm= 245 N/mm2;

A5= 20%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Alumig Mg 4.5 Mn

AWS A5.10-92 ER 5183 BS 2901-90 5183 DIN 1732-88 SG-AlMg4.5Mn Werkstoff no. 3.3548

0.7 Mn; 0.08 Si; 4.9 Mg; 0.2 Fe;

Rpo.2=145 N/mm2;Rm= 275 N/mm2;

A5= 24%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Alumig Mg 5 AWS A5.10-92 ER 5356 BS 2901-90 5356

0.15 Mn; 0.05 Si;

Rpo.2=125 N/mm2;Rm= 255 N/mm2;

I1,argon=16-20 l/min; I2,helium=16-20 l/min;

Ø0.8; Ø1.0;

DIN 1732-88 SG-AlMg5 NF A81-331 AG 5/AlMg5 Werkstoff no. 3.3556

5.0 Mg; 0.15 Fe;

A5= 24%; I3, Ar/He=16-20 l/min; Ø1.2; Ø1.6;

Alumig Mg 5 Mn

AWS A5.10-92 ER 5556 BS 2901-90 5556 A NF A81-331 AlMg5 Mn

0.8Mn; 0.05 Si; 5.3 Mg; 0.15 Fe;

Rpo.2=135 N/mm2;Rm= 275 N/mm2;

A5= 15%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Alumig Si 12

AWS A5.10-92 ER 4047 BS 2901-90 4047 A DIN 1732-88 SG-AlSi12 NF A81-331 AlSi12 Werkstoff no. 1.2585

12.0Si; 0.01 Mn; 0.01 Zn; 0.30 Fe;

Rpo.2=80 N/mm2; Rm= 170N/mm2;

A5= 6%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Alumig Si 5

AWS A5.10-92 ER 4043 BS 2901-90 4043 A DIN 1732-88 SG-AlSi5 NF A81-331 AlSi12 Werkstoff no. 3.2245

5.0Si; 0.01 Mn; 0.01 Zn; 0.2 Fe;

Rpo.2=55 N/mm2; Rm= 140N/mm2;

A5= 10%;

I1,argon=16-20 l/min; I2,helium=16-20 l/min; I3, Ar/He=16-20 l/min;

Ø0.8; Ø1.0; Ø1.2; Ø1.6;

Struja zavarivanja: DC+

TIG POSTUPAK

Komercijalni

naziv Oznake po standardima Hem. sastav (wt %)

Mehanicke osobine Zastitni gas Prečnik

(mm)

Alutig 99.5

AWS A5.10-92 ER 1100 BS 2901-90 1050 A DIN 1732-88 SG-Al 99.5 NF A81-331 Al 99.5 Werkstoff no. 3.0259

≥99.5 Al; 0.01 Zn; 0.06 Fe

Rpo.2=30 N/mm2; Rm= 100 N/mm2;

A5= 37%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Mg 3

AWS A5.10-92 ER 5754 DIN 1732-88 SG-Al Mg 3 NF A81-331 AG 3/ AlMg 3 Werkstoff no. 3.3536

0.15Si; 0.20 Mn; 0.1 Zn; 3.2 Mg; 0.25 Fe;

Rpo.2=120 N/mm2;Rm= 230 N/mm2;

A5= 22%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Mg 3.5 Mn

BS 2901-90 5154 A NF A81-331 AlMg3.5

0.4 Mn; 0.2 Si;

3.3 Mg; 0.35 Fe;

Rpo.2=125 N/mm2;Rm= 245 N/mm2;

A5= 20%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Mg 4.5 Mn

AWS A5.10-92 ER 5183 BS 2901-90 5183 DIN 1732-88 SG-AlMg4.5Mn Werkstoff no. 3.3548

0.7 Mn; 0.08 Si; 4.9 Mg; 0.2 Fe;

Rpo.2=145 N/mm2;Rm= 275 N/mm2;

A5= 24%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Mg 5 AWS A5.10-92 ER 5356 0.15 Mn; Rpo.2=125 N/mm2; I1,argon=5-10 l/min; Ø1.6;

BS 2901-90 5356 DIN 1732-88 SG-AlMg5 NF A81-331 AG 5/AlMg5 Werkstoff no. 3.3556

0.05 Si; 5.0 Mg; 0.15 Fe;

Rm= 255 N/mm2; A5= 24%;

I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Mg 5 Mn

AWS A5.10-92 ER 5556 BS 2901-90 5556 A NF A81-331 AlMg5 Mn

0.8Mn; 0.05 Si; 5.3 Mg; 0.15 Fe;

Rpo.2=135 N/mm2;Rm= 275 N/mm2;

A5= 15%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Si 12

AWS A5.10-92 ER 4047 BS 2901-90 4047 A DIN 1732-88 SG-AlSi12 NF A81-331 AlSi12 Werkstoff no. 1.2585

12.0Si; 0.01 Mn; 0.01 Zn; 0.30 Fe;

Rpo.2=80 N/mm2; Rm= 170N/mm2;

A5= 6%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Alutig Si 5

AWS A5.10-92 ER 4043 BS 2901-90 4043 A DIN 1732-88 SG-AlSi5 NF A81-331 AlSi12 Werkstoff no. 3.2245

5.0Si; 0.01 Mn; 0.01 Zn; 0.2 Fe;

Rpo.2=55 N/mm2; Rm= 140N/mm2;

A5= 10%;

I1,argon=5-10 l/min; I2,helium=8-16 l/min; I3, Ar/He=5-10 l/min;

Ø1.6; Ø2.0; Ø2.4; Ø3.2; Ø4.0;

Struja zavarivanja: AC

REL POSTUPAK

Komercijalni naziv Oznake po standardima

Hem. sastav (wt %)

Mehanicke osobine Položaji zavarivanja Prečnik

(mm)

Elgaloy Alu DIN 1732-88 AlSi 5 95.0 Al; 5.0 Si;

A5= 10%; Tvrdoća=40HB; Svi Ø2.50;

Ø3.25; Struja zavarivanja: DC+ Za sve dodatne informacije obratite se na telefone: 011/25-00-234, 25-11-400,23-91-337 “REFIT inženjering” doo Beograd