7/29/2019 Lecture 1-Proportioning Concrete Mixtures
1/58
Proportioning Concrete Mixtures
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
2/58
What is concrete?
Concrete, is a product or mass made by the
use of a cementing medium.
Generally, this medium is the product of
reaction between hydraulic cement and water
(Neville and Brooks, 1987).
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
3/58
HOW??
Concrete is prepared by mixing cement (binder), sand (fineaggregate), gravel (coarse aggregate) and water with specificproportions.
The cement and the water will react through the hydration process.The hydrated cement composed of four major compounds namely,tri-calcium silicate (C3S), di-calcium silicate (C2S), tricalciumaluminate (C3A) and tetracalcium aluminoferrite (C4AF). The mostimportant products of the hydration reaction are the calcium silicatehydrate (C-S-H) and the calcium hydroxide (CH).
The hydration reactions of the major compounds can be written asbelow:
23233 )(362 OHCaHSCHSC
23232 )(42 OHCaHSCHSC
633 6 AHCHAC
636324 10)(2 FHCAHCHOHCaAFC
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
4/58
Proportioning of concrete mixtures
The proportioning of concrete mixtures is the process ofarriving at the right combination of cement, aggregates,water, and admixtures for making concrete according togiven specifications.
The process is considered an art rather than a science Although many engineers do not feel comfortable, with an
understanding of the underlying principles and, with somepractice, the art of proportioning concrete mixtures can bemastered.
Given an opportunity, the exercise of this art is veryrewarding because the effect of mix proportioning on thecost of concrete and several important properties of bothfresh and hardened concrete can be clearly seen.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
5/58
The mix design process
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
6/58
Components of Modern Concrete
Concreteis a composite material that consistsessentially of a binding medium within whichare embedded particles or fragments ofaggregate.
To obtain concrete with certain desiredperformance characteristics the followingsteps are essential:-
1. The selection of component materials2. A process called mixture proportioning, which
means achieving the right combination ofcomponents.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
7/58
Purpose of mix proportioning
Conventionally, the two most essential requirements ofmix proportioning are the workability of fresh concreteand the strength of hardened concrete at a specifiedage.
Durability is another important property, but it isgenerally assumed that under normal exposureconditions durability will be satisfactory if the concretemixture develops the necessary strength.
Another purpose of mix proportioning is to obtain aconcrete mixture satisfying the performancerequirements at the lowest possible cost.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
8/58
Purpose
The overall objective of proportioning concrete
mixtures can therefore be summarized as selecting thesuitable ingredients among the available materials anddetermining the most economical combination thatwill produce concrete with certain minimum
performance characteristics. The tools available to the engineer to achieve this
objective are limited. An obvious constraint in concretemixture proportioning is that within a fixed volume youcannot alter one component independent of others.
For example, in a m3 of concrete, if the aggregatecomponent is increased, the cement paste componentdecreases.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
9/58
Purpose
With concrete-making materials of given
characteristics and with given job conditions (i.e.,structural design, and equipment for handlingconcrete), the variables generally under thecontrol of a mix designer are as follows:
The cement paste-aggregate ratio in the mixture, thewater-cement ratio in the cement paste, the sand-coarse aggregate ratio in the aggregates, and the useof admixtures.
The task of mixture proportioning is complicated by
the fact that certain desired properties of concretemay be oppositely affected by changing a specificvariable.
The process of mixture proportioning boils down tothe art of balancing various conflicting requirements.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
10/58
Approaches for concrete mix design
The weight method and the absolute volumemethod.
In the weight method, the unit weight of freshconcrete is known from previous experience forthe commonly used raw materials and is used tocalculate the weight of the last unknowncomponent of concrete, usually the sand.
If the unit weight of fresh concrete (wet concrete)
is known, we have
admixturesandaggregatewatercementconcretewet WWWWWW
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
11/58
Absolute volume method
In the absolute volume method, the total
volume (1m3) is equal to the sum of volume of
each ingredient given by:-
1)( airvolumeWWWWW
admixture
admixture
sand
sand
aggregate
aggregate
water
water
cement
cement
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
12/58
Density (unit weight) of fresh concrete
= density (unit weight) of fresh concrete, kg/m3
a = weighted average bulk specific gravity (SSD) ofcombined fine and coarse aggregate
A = air content, %
C = cement content, kg/m3
= specific gravity of cement (generally 3.10 for Portlandcement)
W = mixing water requirement, kg/m3
31110010 mkgWCA aaa
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
13/58
Rough estimate Density (unit weight) of
fresh concrete
31110010 mkgGWG
GCAGU am
c
amam
where Um is the weight of fresh concrete, kg/m3; Ga
is the weighted average bulkspecific gravity (SSD) of
combined fine aggregate and coarse aggregate,
assuming reasonable weight proportions; Gc is thespecific gravity of cement; A is the air content, %;
Wm is the mixing water content, kg/m3; Cm is the
cement content, kg/m3.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
14/58
Mass of fine aggregate
The volume method is an exact procedure forcalculating the required amount of fineaggregate. Here, the mass of fine aggregate,Af, is given by:
3/101000 mkgAACWAc
cff
where
Ac = coarse aggregate content, kg/m3
f= bulk specific gravity (SSD) of fine aggregate
c = bulk specific gravity (SSD) of coarse aggregate
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
15/58
General Considerations
When the aggregate under consideration
contains alkali-reactive minerals, the use of
pozzolanic admixtures in combination with a
high-alkali cement may turn out to be themore cost-effective alternative, at times.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
16/58
General
Further cost reduction is possible, without
compromising the essential performance
characteristics of a concrete mixture, if
cheaper and suitable materials are found toreplace a percentage of Portland cement.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
17/58
Specific Principles
When reviewing the following specific principlesfor selecting concrete mixture proportions, it willbe helpful to remember again that the underlyinggoal is to strike a reasonable balance between
the workability, strength, durability, and cost ofconcrete.
A key consideration governing many of theprinciples behind the procedures forproportioning concrete mixtures is therecognition that; cement costs much more thanaggregates.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
18/58
Specific
Among all the constituents of the concrete,the admixture has the highest unit cost,followed by cement.
When a material is available from two or moresources and a significant price differentialexists, the least expensive source of supply isusually selected unless there are
demonstrable technical reasons that thematerial will not be suitable for the job athand.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
19/58
Workability
Workability embodies certain characteristics of freshconcrete, such as consistency and cohesiveness.
Consistency, broadly speaking, is a measure of the wetnessof the concrete mixture, which is commonly evaluated interms ofslump.
To obtain the specified slump, the mixture waterrequirement generally decreases as:1. The maximum size of a well-graded aggregate is increased;
2. The content of angular and rough-textured particles in the
aggregate is reduced;3. The amount of entrained air in the concrete mixture isincreased; and
4. Coal fly ash is used as a partial replacement for a cement.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
20/58
Cohesiveness
Cohesiveness is a measure of compactibility andfinishability, which is generally evaluated by
trowelability and visual judgment of resistance to
segregation.
In trial mixtures when cohesiveness is judged as
poor, it can usually be improved by taking one or
more of the following steps:
increase the sand/coarse aggregate ratio, partially replacethe cement or sand with coal fly ash, and
increase the cement paste/aggregate ratio.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
21/58
Cohesiveness
Obviously, due to its lower density, fly ash has the
ability to increase the cement mortar/aggregate ratio
by volume without an increase in the cement, water,
or sand content of the mixture. There are no standard requirements for workability
because they may vary from one job to another,
depending on the type of construction and the
equipment used to transport and consolidateconcrete.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
22/58
Strength
From the standpoint of structural safety, the
strength of concrete specified by the designer is
treated as the minimum required strength.
Therefore, to account for variations in materials;methods of mixing, transportation, and
placement of concrete; and curing and testing of
concrete specimens, ACI Building Code 318requires a certain degree of strength overdesign,
which is based on statistical considerations.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
23/58
Strength
In other words, depending on the variability oftest results, the mixture proportions selectedmust yield a mean or average strength higherthan the minimum or the specified strength.
It should be noted that the average strength, notthe specified strength, is used in mixture designcalculations.
Although other factors also influence strength,
the tables and charts used for the purposes ofmixture proportioning assume that strength issolely dependent on the water-cement ratio andthe content of entrained air in concrete.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
24/58
Selection of design strength
The mix design process will deal with a targetaverage strength. The average strength
selected must take into account:
1. The degree of variability anticipated.
2. The degree of certainty of avoiding rejection
required.
3. Any early age strength requirement.
4. The required durability.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
25/58
Target mean strength
Characteristic strength is a lower limit ofstrength to be used in structural design.
As with all materials, concrete has an
inherent variability of strength, and anaverage cube compressive strength (or
target mean strength) somewhat above
the characteristic strength is therefore
required.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
26/58
deviationdards
strengthSpecifiedF
strengthaveragerequiredX
where
kFX
tan
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
27/58
Variability
Knowledge of the is required to determinethe target strength. which is a measure of thespread of results assuming concrete strength
to be a normally distributed variable.
For an existing concrete production facility will be known from previous tests.
Where limited or no data are available, the
upper values given in the Figure below whichhas been derived from analysis of the data
from many production facilities can be used.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
28/58
Variability
Values ofcan range from less than 2.0 MPa
to more than 6.0 MPa so that the required
target average strength can vary by 6 MPa or
more according to the degree of controlachieved.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
29/58
The normal distribution
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
30/58
k value
k = a constant depending on the proportion ofresults permitted to be below F.
The difference between the characteristic andtarget mean strength is called the margin; a 5%
failure rate is normally chosen for concrete
In the USA the permissible percentage defectiveis usually 10% giving a k value of 1.28.
In most of the rest of the world the percentage is5% giving a k value of 1.645 (which in the UK isrounded to 1.64 and in Australia to 1.65).
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
31/58
Durability
when concrete is subject to normal conditions
of exposure, the mix-proportioning procedures
ignore durability because strength is
considered to be an index of general durability.
However, under conditions that may tend to
shorten the service life of concrete, its
durability may be enhanced by specialconsiderations in mixture proportioning.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
32/58
Durability
For example, entrained air is required with allexposed concrete in climates where freezing andthawing cycles occur.
Concrete exposed to chemical attack by deicingsalts or acidic or sulfate waters may require theuse of water-reducing and mineral admixtures.
In such a situation, although a higher water-
cement ratio would have satisfied the strengthrequirement, a lower water-cement ratio isusually specified considering the exposureconditions.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
33/58
Procedures
Mathematical approaches to determine the
correct proportion of component materials of
a concrete mixture meeting a given set of
specifications generally do not work becausethe materials vary widely in their
characteristics large number of empirical
methods based on extensive test datadeveloped from local materials.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
34/58
Procedures
The method recommended by ACI Committee211, is popular in the USA and many othercountries in the world.
To the extent possible, the following
background data should be gathered beforestarting the calculations:
1. Sieve analysis of fine and coarse aggregate;
fineness modulus2. Dry-rodded unitweightof coarse aggregate
3. Bulk specificgravityof materials
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
35/58
Procedures
4. Absorptioncapacity or free moisture in the aggregate
5. Variations in the approximate mixing waterrequirement with slump, air content, and grading ofthe available aggregates
6. Relationship between strength and W/Cfor availablecombinations of cement and aggregate
7. Job specifications if any [e.g., maximum water-cement ratio, minimum air content, minimum slump,maximum size of aggregate, and strength at earlyages (normally, 28-day strength is specified)].
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
36/58
Steps in ACI 211 method
Step 1: Choice of slump
Step 2: Choice of maximum size of aggregate
Step 3: Estimation of the mixing water content
and air content Step 4: Selection of water-cement ratio
Step 5: Calculation of the cement content
Step 7: Estimation of the fine aggregate content Step 8: Adjustments for the aggregate moisture
Step 9: Trial batch adjustments
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
37/58
Flow chart forselection and
documentation
of concrete
proportions
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
38/58
Examples
Concrete is required for a column that will bemoderately exposed to freezing and thawing.
The cross section of the column is 300 300
mm. The smallest spacing between reinforcingsteel is 30 mm. The specified compressive
strength of concrete at 28 days is 40 MPa with
a slump of 80 to 100 mm. The properties of
materials are as follows:
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
39/58
Cement used is type I Portland cement with aspecific gravity of 3.15.
The available coarse aggregate has a maximumsize of 20 mm, a dry-rodded unit weight of 1600kg/m3, a bulk specific gravity (SSD) of 2.68,absorption capacity of 0.5%, and moisturecontent (oven-dried, OD) of 0.25%.
The fine aggregate has a bulk specific gravity(SSD) of 2.65, absorption capacity of 1.3%, amoisture content (SSD) of 3%, and a finenessmodulus of 2.60.
The aggregates conform to the ASTM C33-84requirements for grading.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
40/58
With the given information, the mix design will be carried throughin detail, using the sequence of steps outlined.
Step 1: Choice of slump. The slump is given and consistent with
Table 3-7. Step 2: Maximum aggregate size. The maximum aggregate size is
20 mm, which meets the limitations of 1/5 of the minimumdimension between forms and 3/4 of the minimum clear space.
Step 3: Estimation of mixing water and air content. The concretewill be exposed to freezing and thawing; therefore, it must be airentrained. From Table 3-8, the recommended mixing water amountis 180 kg/m3, and the air content recommended for moderateexposure is 5.0%.
Step 4: Water/cement ratio (w/c).According to both Table 3-1 andTable 3-3, the estimate of the required w/c ratio to give a 28-day
compressive strength of 40 MPa is 0.35. Step 5: Calculation of cement content. Based on the steps 3 and 4,
the required cement contentis 180/0.35 = 514 kg/m3.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
41/58
Step 6: Estimation of coarse aggregate content. FromTable 3-11, for fineness modulus of the fine aggregateof 2.60, the volume of dry-rodded coarse aggregate per
unit volume of concrete is 0.64. Therefore, there willbe 0.64 m3 coarse aggregate per m3 volume concrete.And, the OD weight of the coarse aggregate is 0.64 1600 = 1024 kg. The SSD weight is 1024 1.005 = 1029kg.
Step 7: Estimation of fine aggregate content. The fineaggregate content can estimated by eitherthe weightmethod or the volume method.
(a) Weight method. From Table 3-12, the estimated
concrete weight is 2280 kg/m3
. Although for a first trial it is not generally necessary to use
the more exact calculation based on Equation, this valuewill be used here:
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
42/58
3
3
/2314
167.218015.3
67.21514510067.210
1110010
mkg
mkgGWG
GCAGU am
c
amam
Based on the already determined
weights of water, cement, and coarse
aggregate,the SSD weight of the fine aggregate is
2314 180 514 1029 = 591 kg.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
43/58
(b) Volume method. Based on the known
weights and specific gravity of water, cement,
and coarse aggregate, the air volume, the
volumes per m3 occupied by the different
constituents can be obtained as follows:
3
3
3
384.068.21000
1029:
163.015.31000
180:
18.01000
180:
mXG
WSSDAggCoarse
mXG
Wcement
mW
water
wateraggCoarse
aggcoarse
watercement
cement
water
water
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
44/58
Air: 0.05 m3;
Therefore, the fine aggregate must occupy avolume of 1 (0.180 + 0.163 + 0.384 + 0.05) =
0.223 m3.
The required SSD weight of the fine aggregateis:
0.223 2.65 1000 = 591 kg.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
45/58
Step 8: Adjustment for moisture in theaggregate.
Since the aggregates will be neither SSD norOD in the field, it is necessary to adjust theaggregate weights for the amount of water
contained in the aggregate. Since absorbed water does not become part
of the mix water, only surface water needs tobe considered.
For the given moisture contents, the adjustedaggregate weights become:
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
46/58
Coarse aggregate (stock): From
W(stock) = W(OD)[1 + MC(OD)]
Get: W(stock) = 1024 1.0025 = 1026 kg
The extra water needed for coarse aggregateabsorption is
W(SSD) W(stock) = 1029 1026 = 3 kg
Fine aggregate (stock): 591 1.03 = 609 kg/m
3
Extra water provided by fine aggregate: 609 591= 18 kg
The mixing water is then: 180 + 3 18 = 165 kg.
Thus, the estimated batch weights per m3 are asfollows: water, 165 kg; cement, 514 kg; coarseaggregate, 1026 kg; fine aggregate, 609 kg; total,2314 kg.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
47/58
Step 9: Trial mixes. Trial mixes should be
carried out using the proportions calculated.Theproperties of the concrete in the trial mix
must be compared with the desired
properties, and the mix design must becorrected as described.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
48/58
Proportioning of High-Strength
and High-Performance Concrete Mixtures
ACI Definition
HPC is defined as a concrete meeting specialcombination of performance and uniformity
requirements that cannot always be achievedroutinely using conventional constituents andnormal mixing, placing, and curing practices.
Mehta and Aitcin suggested the term HPC
mixtures that possess the following threeproperties: high-workability, high-strength, andhigh durability.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
49/58
Proportioning of High-Strength
For a variety of reasons, the ACI211 procedure forconcrete mixture proportioning needs updating.
Since it was developed when concrete mixtures wererequired to meet rather narrow specifications for
compressive strength at 28 days (15 to 45 MPa, Table3-1) and consistency (25 to 175 mm slump).
To satisfy todays high-construction speeds with heavilyreinforced structural elements, concrete placement by
pumping is the common practice now, and this meansthat concrete mixtures are designed to have at least125 to 150 mm slump.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
50/58
Proportioning of High-Strength
Also, high-strength and high-performanceconcrete mixtures are being designed forcompressive strength values from 50 to 100 MPa,which is outside the range ofW/C- compressivestrength relationship given byACI-211 (Table 3-1).
The use of mineral admixtures andsuperplasticizers is much more prevalent now,
and ACI 211 guidelines do not adequately dealwith concrete mixtures containing thesecomponents.
M ht d Ait i P d f
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
51/58
Mehta and Aitcin Procedure of
proportioning HSC/HPC
Mehta and Aitcin developed a sequential, eight-step procedure for proportioning of high-performance concrete mixtures containingsuperplasticizers, mineral admixtures, and 28-day
compressive strength values between 65 to 120MPa.
To provide adequate dimensional stability (e.g.,high elastic modulus, and low drying shrinkage
and creep), the procedure assumes a fixed ratioof 35 to 65% by volume between the cementpaste and the aggregate.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
52/58
Mehta
For a 1 m3 batch of concrete containing 0.35 m3cement paste, having known the volume of waterand assuming a certain amount of entrapped orentrained air, the total volume of the
cementitious material can be computed bydifference.
Next, the procedure provides options in thechoice of the cementitious material, i.e, whether
to use Portland cement alone or to use partialreplacement of the cement by one or moremineral admixtures such as fly ash, slag, and silicafume.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
53/58
Mehta
To complete the computations for the first trialbatch, a 2:3 ratio by volume between the fineaggregate and the coarse aggregate is assumed.
This trial is used to determine the dosage of the
superplasticizer for obtaining the desiredconsistency and for adjustment of a proper ratiobetween CA : FA.
In general, depending on the type of the
superplasticizer and the physical-chemicalcharacteristics of the cementitious material, thesuperplasticizer dosage may vary from 1 to 3l/m3.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
54/58
Mehta
Note that a change of emphasis from the w/c-
strength relation to the water content-
durability relation will provide the necessary
incentive for incorporation of particle packingconcepts into the concrete mixture
proportioning methods.
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
55/58
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
56/58
Mix proportions and material properties for the
range of RCC concretes used at the Willow Creek
Dam are shown in the Table
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
57/58
Exercise 1
Use the American method to design a concretemix that is required to have a specified meanstrength of 30 MPa at 28 days. The presence ofreinforcement requires a slump of 75mm and amaximum size of aggregate of 10 mm. The
aggregates are of normal weight, and gradingsconform to the appropriate standard with afineness modulus of 2.8. (Assume that absorptionis 0.7% and moisture condition of the aggregates
is SSD; the bulk density of coarse aggregate is1600 kg/m3; and there will be extreme exposurecondition to freeze-thawing.)
7/29/2019 Lecture 1-Proportioning Concrete Mixtures
58/58
Exercise 2
Use the American method to design a concrete mixthat is required to have a specified mean strength of 25MPa at 28 days. The presence of reinforcementrequires a slump of 3050 mm and a maximum size ofaggregate of 40 mm. The aggregates are of normalweight and gradings conform to the appropriatestandard with a fineness modulus of 2.8. (Assumethere is negligible absorption and moisture content; adry-rodded bulk density (unit weight) of coarseaggregate is 1550 kg/m3, and there is a bulk specificgravity (SSD) of 2.70; the fine aggregate has a bulkspecific gravity (SSD) of 2.65; and the concrete will bein extreme exposure conditions.)