PPG Catalog

7/13/2019 PPG Catalog

1/331

AMERCOAT

A PPG brand

Protective Coatings Product Catalog


2/331

Epoxy Coatings and Linings

Section 3 Product Description

AMERCOATOne Multi-Purpose Single Component Epoxy

Amercoat78HB Amine-Cured Coal Tar Epoxy

Amercoat90HS Epoxy Phenolic Tank Lining

Amercoat91 Epoxy Novolac Tank Lining

Amercoat100A Sprayable Epoxy Surfacer

Amercoat133 Solvent Free Cycloaliphatic Amine Tank Lining

Amercoat235 Multi-purpose Phenalkamine Epoxy

Amercoat240 Universal Amine Epoxy Coating

Amercoat240LT Low Temperature Cure Amine EpoxyAmercoat 242HB Solvent Free Glass Flake Reinforced Lining

Amercoat253 Novolac Epoxy Tank Lining

Amercoat333 Solvent Free Cycloaliphatic Amine Tank Lining

Amercoat351 Solvent Free Modified Phenolic Amine Tank Lining

Amercoat370 Fast Dry Multi-Purpose Epoxy Coating

Amercoat385/385PA Multi-Purpose Polyamide Epoxy Coating

Amercoat399 Fast Dry, High Solids Epoxy Coating

www.ppgpmc.com/northamercia

AMERLOCKEpoxy


Amerlock2 Fast Dry, Surface Tolerant, High Solids Epoxy Coating

Amerlock2AL Fast Dry Aluminum Epoxy Mastic Coating

Amerlock2VOC Low VOC, Fast Dry, High Solids Epoxy Coating

Amerlock2/400GF High Solids Glass Flake Epoxy Coating

Amerlock400 High Solids Epoxy Coating

Amerlock400AL Aluminum Epoxy Mastic Coating

Amerlock400VOC Low VOC, High Solids Epoxy Coating

Amerlock400BF Epoxy Masonry Block Filler

AmerlockSealer Penetrating Epoxy Primer Sealer

2014 PPG Industries

PSXEngineered Siloxane Topcoats


PSX700 Engineered Siloxane

PSX700A Clear Coat Engineered Siloxane Clear Coat

PSX700X Engineered Siloxane Coating

PSX1001 High Solids, Single Pack Acrylic Polysiloxane

Protective Coatings Product Catalog Index


3/331

Zinc Rich Primers


Amercoat68HS Zinc Rich Epoxy Primer

Amercoat68HS VOC Low VOC, Zinc Rich Epoxy Primer

Amercoat68MCZ Moisture Cure Urethane Zinc Primer

DIMETCOTE9 Inorganic Zinc Silicate Primer

Dimetcote9 VOC Low VOC, Inorganic Zinc Silicate Primer

Dimetcote9H Inorganic Zinc Silicate Primer

Dimetcote21-5 Water Based Inorganic Zinc Silicate Primer

Dimetcote302H Reinforced Inorganic Zinc Primer

Urethane LiningsSection 4 Product Description

AMERTHANE490 Elastomeric Polyurea Hybrid

Epoxy Coatings and Linings (contd)


NOVAGUARD 810 High Build, Rapid Return to Service Novolac Epoxy Tank Lining

Novaguard840 Solvent Free Amine Cured Novolac Phenolic Epoxy Coating

Novaguard890 Solvent Free Amine Cured Novolac Phenolic Epoxy Coating

PHENGUARD 930 High Build Amine Adduct Cured Novolac Phenolic Epoxy Primer

Phenguard935 High Build Amine Adduct Cured Novolac Phenolic Epoxy Coating

Phenguard940 High Build Amine Adduct Cured Novolac Phenolic Epoxy Finish

SIGMAGUARD CSF 650 Solvent Free Amine Cured Epoxy Coating

Sigmaguard720 Reinforced High Solids Polyamine Adduct Cured Epoxy Coating

Primers


Amercoat185H Universal Phenolic Alkyd Primer

Amercoat5105 Alkyd Primer

Amercoat5108 Alkyd Shop Primer

DSP-3 Water Based Inorganic Zinc Silicate Pre-Construction PrimerSIGMACOVER 280US Polyamide Cured Epoxy Primer

Sigmaguard260 High Build Amine Adduct Cured Novolac Phenolic Epoxy HoldingPrimer

SIGMAWELD 199US Moisture Curing, Reduced Zinc (Ethyl) Silicate Pre-Construction Primer

Index (continued)

2014 PPG Industries



4/331

Topcoats


Amercoat220P Int./Ext. Gloss DTM Industrial Enamel

PITT-TECHPlus 90-912 Int./Ext. Low VOC DTM Industrial Primer

Pitt-TechPlus 90-1110 Int./Ext. Satin Low VOC DTM Industrial Enamel

Pitt-TechPlus 90-1210 Int./Ext. Semi-Gloss Low VOC DTM Industrial Enamel

Pitt-TechPlus 90-1310 Int./Ext. Gloss Low VOC DTM Industrial Enamel

Amercoat229T Gloss Epoxy Acrylic Topcoat

Amercoat450H Gloss Acrylic Aliphatic Polyurethane Topcoat

Amercoat450HSG Semi-Gloss Acrylic Aliphatic Polyurethane Topcoat

Amercoat5420 Gloss Alkyd Enamel

AMERSHIELD Polyester-Acrylic Aliphatic Polyurethane Topcoat

AmershieldVOC Low VOC, Polyester-Acrylic Aliphatic Polyurethane

DURETHANE DTM DTM Urethane Mastic

FLEXSET TCX Gloss aliphatic polyaspartic topcoat

Fire Proofing Coatings


ALBI CLAD800 Solvent based intumescent mastic for cellulosic and hydrocarbon fires

ALBI CLADTF Interior, Water Base Thin Film Intumescent Coating

PITT-CHAR XP Thick Film Intumescent Coating for Hydrocarbon and Cellulosic Fires

STEELGUARD FM550 Thin Film Intumescent Coating for Cellulosic Fires

High Heat Coatings


Amercoat741 High Temperature Self Cure, Inorganic Topcoat

PPGHI-TEMP 500 V High Temperature Silicone Acrylic Topcoat

PPG Hi-Temp 500 VHA Hot Applied Silicone Acrylic for PPG Hi-Temp 1027

PPG Hi-Temp 500 VS High Temperature Silicone Acrylic Topcoat

PPG Hi-Temp 600 ZN High Temperature Silicone Acrylic Zinc Primer

PPG Hi-Temp 1000 V High Temperature Silicone Topcoat

PPG Hi-Temp 1000 VHA Hot Applied Silicone Topcoat for PPG Hi-Temp 1027

PPG Hi-Temp 1000 VS Silicone Topcoat for PPG Hi-Temp 1027

PPGHi-Temp1050 ZN High Temperature Silicone Zinc Primer

PPGHI-TEMP1027 High Build, Multipolymeric Matrix CUI Coating

PPG Hi-Temp 222 G High Temperature, High-build Multi-polymeric Composite forCarbon Steel

PPG Hi-Temp 707 HB Thermal Waterborne Liquid InsulationPPG Hi-Temp 850 TC Waterborne Acrylic Topcoat for PPG Hi-Temp707 HB

Index (continued)

2014 PPG Industries



5/331

Index (continued)

Specialty Products & Additives


AMERASE Graffiti Cleaner

Amercoat114A Epoxy Filler Compound

Amercoat851 Flow Control Additive

Amercoat861 Epoxy Accelerator

Amercoat866M Urethane Accelerator

Amercoat880 Glassflake Additive

Amercoat884 Thixotropic Fumed Silica Additive

Amercoat965 Acrylic Modified Cement

Prep 88 Water Based Alkaline Cleaner

TIDEGUARD 171A Sprayable Epoxy Cladding

AMERCOAT, AMERLOCK, AMERTHANE, DIMETCOTE and PSX are registered trademarks of PPG IndustrieOhio, Inc. AMERSHIELD, AMERASE and TIDEGUARD are trademarks of PPG Industries Ohio, Inc. PITT-CHAR Xand PITT-TECH are registered trademarks of PPG Architectural Finishes, Inc. FLEXSET, NOVAGUARD, PHENGUARDSIGMACOVER, SIGMAGUARD, SIGMAWELD, STEELGUARD are trademarks of PPG Coatings Nederland B.V

PPG HI-TEMP and PPG HI-TEMP 1027 are trademarks of PPG Coatings Europe B.V.

2014 PPG Industrieswww.ppgpmc.com/northamercia


6/331

July 2013

Revision of June 2013

DESCRIPTION Engineered Siloxane

PRINCIPAL CHARACTERISTICS Unique, high gloss epoxy siloxane

Virtually HAPs free, ultra-low VOC

High durability in challenging environments

Abrasion resistant

Resists dirt pickup, easily cleaned

Can be applied directly to zinc primers as a 2-coat system

Can be applied direct-to-steel in ISO 12944 C1-C3 environments

COLORAND GLOSS Gloss

Standard and Custom Colors available

Yellow, red, and orange colors will fade faster than other colors due to the replacement of lead-based pigments

with lead free pigments in these colors.

BASIC DATA

Volume solids 90% 3%

VOC* 0.7 lbs/gal (84 g/L)

* The mixed and applied coating cure reaction will produce VOC of mixed alcohols. For 100 g/l VOCrequirements, a VOC - exempt thinner such as 97-939 may be used as needed.

Recommended

Dry film thickness* 3 - 7 mils per coat (75-175 microns)

* When applying more than one coat, it is recommended that the total dry film thickness not exceed 10 mils.

Theoretical Spread Rate 1444 ft2/gal @ 1 mils dft

289 ft2/gal @ 5 mils dft

Components 2

Dry Temperature Resistance* Continuous 200F Intermittent 250F (


7/331

A test patch is recommended to confirm adhesion. Not recommended over chromate

sealed galvanizing without blasting to thoroughly remove chromates. Adhesion

problems may occur.

Aged Coatings Contact your PPG representative. A test patch ofPSX700 over in-tact cleancoating and observation for film defects and adhesion over a period of time may be

required, dependent upon the type of coating.

PSX700 is compatible overAmercoat450-series.

ENVIRONMENTAL CONDITIONS

Ambient temperatures 32F to 100F (0C to 32C) (FD cure should be used below 40F)

Material temperatures 32F to 100F (0C to 32C)

Relative humidity 40% minimum

Work area can be artificially humidified by atomized water spray and/or ponding water under the coated

structures.

Surface temperature 32F to 120F (0C to 49C)

Surface temperature must be at least 5F above dew point temperature.

Note: PSX 700 should be allowed to reach a Dry-to-Touch condition before force curingabove 140F

General air quality Area should be sheltered from airborne particulates and pollutants. Ensure good

ventilation during application and curing. Provide shelter to prevent wind from affecting

spray patterns.

INSTRUCTIONS FOR USE

Mixing ratio by volume 4 parts base to 1 part hardener

Only mix full kits. Pre-mix base component with a pneumatic air mixing at moderate

speeds to homogenize the container. Pour in the hardener component and power

agitate until thoroughly mixed.

Pot life

Airless spray Standard airless spray equipment, 30:1 pump or larger, 0.015 0.017 fluid tip

recommended

Air spray Thin up to 10%, standard conventional equipment, 0.070 fluid orifice. A moisture and oil

trap in the main line is recommended. Separate regulators for air and fluid pressure are

recommended. Use an agitated pressure pot.

Brush & roll Use a well loaded, high quality natural bristle brush. Maintain a wet edge.

Use a high quality, well loaded, solvent resistant, low nap (1/4-3/8) roller. Amercoat851

flow control additive may be used to enhance flow and leveling of brush strokes and

roller stipple.

Be aware that multiple coats may be required to achieve uniform and sufficient film

thickness to provide proper hiding when applying by brush or roller.

Thinner Amercoat911, Amercoat101 (recommended for > 90F)Cleaning solvent Amercoat12 Cleaner orAmercoat911 thinner

Primers Dimetcote9-series,Dimetcote21-5,Dimetcote302H,Amercoat68HS,Amerlock2/400,

Amercoat370,Amercoat385,Amercoat240,Amercoat235

A mist coat / full coat application technique is required when applying over inorganic

zincs to prevent application bubbling. Thin the mist coat up to 15% with Amercoat911 or

Amercoat101. Ensure dry spray is removed from the surface.

Limitations for use For Industrial or Professional Use Only

Safety precautions For paint and recommended thinners see safety sheet 1430, 1431 and relevant material

safety data sheets

This is a solvent borne paint and care should be taken to avoid inhalation of spray mist

or vapor as well as contact between the wet paint and exposed skin or eyes.

PSX700

page 2/4

Temperature 50F 70F 90F

PSX700 &PSX700FD 6.5 hours 4 hours 1.5 hours


8/331

page 3/4

PSX700

DRY/CURE TIMES* PSX700 @ 4 mils dft and 40% relative humidity

* Surface must be power washed as needed to remove all surface contaminants. Surface must be clean anddry. Use Prep 88 for very dirty surfaces. When re-coating between the dry through time and 7 days, solvent

wipe the surface with Amercoat 911 or Amercoat 12 prior to application of the second coat.

PSX700FD @ 4 mils dft and 40% relative humidity


wipe the surface with Amercoat 911 or Amercoat 12 prior to application of the second coat.

PRODUCTQUALIFICATIONS SSPC Paint 36 Level 3 Performance

NFPA Class A Flame Spread

USDA Incidental Food Contact

AWWA D102-08 Outside Coating SystemAVAILABILITY

Packaging Available in 1 gallon and 5 gallon kits

Product codes PX70023 Pearl Gray Base

PX7003 White Base

PX7009 Black Base

PX700T1 Deep Tint Base*

PX700T2 Light Tint Base*

PX700T3 Neutral Tint Base*

PX700T4 Red Tint Base*

PX700T5 High Hiding Yellow Tint Base*

PX70071 Safety Red Base

PX70081 Safety Yellow Base

PX700-B Hardener componentPX700FD-B Fast Dry hardener component

* Product must be tinted with special PSX tints only. Tintable with UCD PS Line colorants only.

Worldwide statement While it is always the aim of PPG Protective & Marine Coatings to supply the same product

on a worldwide basis, slight modification of the product is sometimes necessary to comply

with local or national rules/circumstances. Under these circumstances an alternative product

data sheet is used.

32F 50F 70F 90F

Dry to touch 7 hours 4.5 hours 2 hours 1 hour

Dry through 16 hours 8.5 hours 4.5 hours 3 hours

Dry to overcoat* 12 hours 7 hours 3 hours 2 hours

Maximum overcoat unlimited*

40F 50F 70F 90F

Dry to touch 9 hours 6 hours 3 hours 1.5 hoursDry through 24 hours 11 hours 6 hours 4 hours

Dry to overcoat* 20 hours 9 hours 4.5 hours 3 hours



9/331

page 4/4

WARRANTYSTATEMENT

PPG warrants (i) its title to the product, (ii) that the quality of the product conforms to PPGs specifications for such product ineffect at the time of manufacture and (iii) that the product shall be delivered free of the rightful claim of any third person forinfringement of any U.S. patent covering the product.

THESE ARE THE ONLY WARRANTIES THAT PPG MAKES AND ALL OTHER EXPRESS OR IMPLIED WARRANTIES,UNDER STATUTE OR ARISING OTHERWISE IN LAW, FROM A COURSE OF DEALING OR USAGE OF TRADE, INCLUDINGWITHOUT LIMITATION, ANY OTHER WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE OR USE, ARE DISCLAIMEDBY PPG.

Any claim under this warranty must be made by Buyer to PPG in writing within five (5) days of Buyers discovery of the claimeddefect, but in no event later than the expiration of the applicable shelf life of the product, or one year from the date of the deliveryof the product to the Buyer, whichever is earlier. Buyers failure to notify PPG of such non-conformance as required hereinshall bar Buyer from recovery under this warranty.

LIMITATIONOF LIABILITY

IN NO EVENT WILL PPG BE LIABLE UNDER ANY THEORY OF RECOVERY (WHETHER BASED ON NEGLIGENCE OF

ANY KIND, STRICT LIABILITY OR TORT) FOR ANY INDIRECT, SPECIAL, INCIDENTAL, OR CONSEQUENTIAL DAMAGES

IN ANY WAY RELATED TO, ARISING FROM, OR RESULTING FROM ANY USE MADE OF THE PRODUCT.

The information in this sheet is intended for guidance only and is based upon laboratory tests that PPG believes to be reliable.PPG may modify the information contained herein at any time as a result of practical experience and continuous product

development. All recommendations or suggestions relating to the use of the PPG product, whether in technical documentation,

or in response to a specific inquiry, or otherwise, are based on data, which to the best of PPGs knowledge, is reliable. The

product and related information is designed for users having the requisite knowledge and industrial skills in the industry and it

is the end-users responsibility to determine the suitability of the product for its own particular use and it shall be deemed that

Buyer has done so, as its sole discretion and risk.

PPG has no control over either the quality or condition of the substrate, or the many factors affecting the use and application of

the product. Therefore, PPG does not accept any liability arising from any loss, injury or damage resulting from such use or

the contents of this information (unless there are written agreements stating otherwise). Variations in the application environment,

changes in procedures of use, or extrapolation of data may cause unsatisfactory results.

This sheet supersedes all previous versions and it is the Buyers responsibility to ensure that this information is current prior to

using the product.

Current sheets for all PPG Protective & Marine Coatings Products are maintained at www.ppgpmc.com. The English text of

this sheet shall prevail over any translation thereof.

PSX700

PSX is a registered trademark of PPG Industries Ohio, Inc.


10/331

February 2014

Revision of October 2012

DESCRIPTION Engineered Siloxane Clear Coat


Low HAPs, ultra-low VOC


Abrasion resistant


Isocyanate free

COLORAND GLOSS Clear

Gloss

BASIC DATA


VOC 0.9 lbs/gal (108 g/L) based on (EPA Method 24)* The mixed and applied coating cure reaction will produce VOC of mixed alcohols.

Recommended

Dry film thickness* (per coat) 2 3 mils (50 75 microns)

Theoretical Spread Rate @ 1 mil dft 1283 ft2 / gallon

@ 3 mils dft 428 ft2 / gallon

Components 2

Shelf Life 2 years from date of manufacture when stored indoors in the original unopened container.

Store product in dry conditions at temperatures of 40-100F.

SURFACE PREPARATION Coating performance is proportional to the degree of surface preparation. See specific

primer for surface preparation details.

Aged Coatings Contact your PPG representative. A test patch ofPSX700A Clear Coat over in-tactclean coating and observation for film defects and adhesion over a period of time

may be required, dependent upon the type of coating. PSX700A Clear Coat should

be applied over a UV-resistant coating in applications exposed to direct sunlight.

PSX700A Clear Coat is compatible overAmercoat450-series.


Ambient temperatures 32F to 120F (0C to 49C)

Surface temperature must be at least 5F above the dew point temperature.




structures. After the film is dry-to-touch, a fine mist may be applied over the coating to expedite curing in low

humidity environments.


Surface temperature must be at least 5F above the dew point temperature.

General air quality Area should be sheltered from airborne particulates and pollutants. Ensure good ventilation

during application and curing. Provide shelter to prevent wind from affecting spray patterns.


Mixing ratio by volume 5 parts base : 1 part hardener

Add hardener component and thinner (as needed) to the base component. Mix using a

power mixer at low speed for 1-2 minutes being careful not to whip air bubbles into the

product. For clear coats, allow bubbles to escape from the surface for a few minutes prior

to application and spray a test area to ensure the film is clear.

PSX 700A Clear Coat

page 1/3


11/331

Pot life*

Airless spray Standard airless spray equipment,30:1 pump or larger, 0.015 0.017" fluid tip recommended





Use a high quality, well loaded, solvent resistant, low nap (1/4"- 3/8") roller. Amercoat851


roller stipple.



Thinner Amercoat911,Amercoat101 (recommended for > 90F)

Cleaning solvent Amercoat12 Cleaner orAmercoat911 thinnerPrimers* Amerlock2/400,Amercoat370,Amercoat385,Amercoat240,Amercoat235,

AmerlockSealer,Pitt-guardEpoxies

* Epoxies should be topcoated with a UV-resistant coating such as PSX polysiloxanes, Amercoat 450H-series,or Pitthane polyurethane for applications with direct sunlight exposure.


safety data sheets



DRY/CURE TIMES* PSX700A Clear Coat @ 4 mils dft and 40% relative humidity

* Surface must be power washed as needed to remove all surface contaminants. Surface must be clean anddry. When re-coating within 72 hours, solvent wipe the surface with Amercoat 911 thinner prior to application ofthe second coat.

PRODUCTQUALIFICATIONS NFPA Class A Flame Spread


AVAILABILITYPackaging Available in 1-gallon kits

Product codes PX700A0 Base component

PX700A0B Hardener component




data sheet is used.

PSX700A Clear Coat


PSX700A Clear Coat 6.5 hours 4 hours 1.5 hours

page 2/3

32F 50F 70F 90F

Dry to touch 4.5 hours 2.5 hours 1.5 hours 1 hour

Dry through 24 hours 7 hours 4 hours 3 hours

Dry to overcoat* 20 hours 6 hours 3 hours 2 hours

Maximum overcoat 30 days


12/331

page 3/3

PSX700A Clear Coat

WARRANTYSTATEMENT

PPG warrants (i) its title to the product, (ii) that the quality of the product conforms to PPGs specifications for such product ineffect at the time of manufacture and (iii) that the product shall be delivered free of the rightful claim of any third person for

infringement of any U.S. patent covering the product.THESE ARE THE ONLY WARRANTIES THAT PPG MAKES AND ALL OTHER EXPRESS OR IMPLIED WARRANTIES,UNDER STATUTE OR ARISING OTHERWISE IN LAW, FROM A COURSE OF DEALING OR USAGE OF TRADE, INCLUDINGWITHOUT LIMITATION, ANY OTHER WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE OR USE, ARE DISCLAIMEDBY PPG.

















using the product.

Current sheets for all PPG Protective & Marine Coatings Products are maintained at www.ppgpmc.com. The English text ofthis sheet shall prevail over any translation thereof.



13/331

November 2013

Revision of September 2013

DESCRIPTION Engineered Siloxane Coating


Virtually HAPs free, ultra-low VOC


Abrasion resistant


Can be applied directly to zinc primers as a 2-coat system

Resists high humidity environments

COLORAND GLOSS Gloss

Standard and Custom Colors available

Yellow, red, and orange colors will fade faster than other colors due to the replacement of lead-based pigments

with lead free pigments in these colors.

BASIC DATA


VOC* 0.62 lbs/gal (75 g/L)

* The mixed and applied coating cure reaction will produce VOC of mixed alcohols. For 100 g/l VOCrequirements, a VOC - exempt thinner such as 97-939 may be used as needed.

Recommended

Dry film thickness* 3 - 7 mils per coat (75-175 microns)

* When applying more than one coat, it is recommended that the total dry film thickness not exceed 10 mils.

Theoretical Spread Rate 1556 ft2/gal @ 1 mils dft

311 ft2/gal @ 5 mils dft

Components 2

Dry Temperature Resistance* Continuous 200F Intermittent 250F (


14/331

A test patch is recommended to confirm adhesion. Not recommended over chromate

sealed galvanizing without blasting to thoroughly remove chromates. Adhesion

problems may occur.

Aged Coatings Contact your PPG representative. A test patch ofPSX700X over in-tact cleancoating and observation for film defects and adhesion over a period of time may be

required, dependent upon the type of coating. PSX700X is compatible over

Amercoat450-series.


Ambient temperatures* 40F to 120F (5C to 49C)




structures.


Surface temperature must be at least 5F above dew point temperature.

Note: PSX 700X should be allowed to reach a Dry-to-Touch condition before forcecuring above 140F

General air quality Area should be sheltered from airborne particulates and pollutants. Ensure good


spray patterns.



Only mix full kits. Pre-mix base component with a pneumatic air mixer at moderate

speeds to homogenize the container. Pour in the hardener component and power

agitate until thoroughly mixed.

Pot life

Airless spray Standard airless spray equipment, 30:1 pump or larger, 0.015 0.017 fluid tip

recommended





Use a high quality, well loaded, solvent resistant, low nap (1/4-3/8) roller. Amercoat851


roller stipple.



Thinner Amercoat911,Amercoat65, Amercoat101 (recommended for > 90F)

Cleaning solvent Amercoat12 Cleaner or thinner

Primers Dimetcote9-series,Dimetcote21-5,Dimetcote302H,Amercoat68HS,Amerlock2/400,

Amercoat370,Amercoat385,Amercoat240,Amercoat235

A mist coat / full coat application technique is required when applying over inorganic

zincs to prevent application bubbling. Thin the mist coat up to 15% with Amercoat911 or

Amercoat101. Ensure dry spray is removed from the surface.

Limitations for use For Industrial or Professional Use Only


safety data sheets



PSX700X

page 2/4


PSX700X 6.5 hours 4 hours 1.5 hours


15/331

page 3/4

PSX700X

DRY/CURE TIMES* PSX700X @ 4 mils dft and 40% relative humidity


wipe the surface with Amercoat 12 cleaner prior to application of the second coat.

PRODUCTQUALIFICATIONS SSPC Paint 36 Level 3 Performance


AWWA D102-08 Outside Coating System

AVAILABILITY

Packaging Available in 1 gallon and 5 gallon kits

Product codes PX700X3 White Base

PX700X9 Black Base

PX700XT1 Deep Tint Base*

PX700XT2 Light Tint Base*

PX700XT3 Neutral Tint Base*

PX700X-B Hardener component

* Product must be tinted with special PSX tints only. Tintable with UCD PS Line colorants only.



with local or national rules/circumstances. Under these circumstances an alternative productdata sheet is used.

WARRANTYSTATEMENT








The information in this sheet is intended for guidance only and is based upon laboratory tests that PPG believes to be reliable.

PPG may modify the information contained herein at any time as a result of practical experience and continuous product






40F 50F 70F 90F

Dry to touch 14 hours 8 hours 3.5 hours 2 hoursDry through 36 hours 13 hours 9 hours 5 hours

Dry to overcoat* 20 hours 9 hours 4.5 hours 3 hours



16/331

page 4/4




changes in procedures of use, or extrapolation of data may cause unsatisfactory results.This sheet supersedes all previous versions and it is the Buyers responsibility to ensure that this information is current prior to

using the product.



PSX700X



17/331

January 2014


DESCRIPTION Single Pack Acrylic Polysiloxane

PRINCIPAL CHARACTERISTICS High gloss topcoat with unlimited recoatability

Ease of application, brush, roll, or spray

Isocyanate free

Excellent gloss retention

Meets SSPC Paint 36 Level 3

COLORAND GLOSS Standard Color Offering, Safety Colors, Custom Colors

Gloss

* Certain colors, especially red, orange, and yellow may require additional coats for adequate hiding, especially ifapplied over primers with a significant color contrast.

BASIC DATA


VOC 3.2 lbs/gal (384 g/L)

Recommended

Dry film thickness (per coat) 2 3 mils; (50 75 microns)

Theoretical Spread Rate @ 1 mil dft 882 ft2 / gallon

@ 2 mils dft 441 ft2 / gallon

Components 1

Shelf Life 1 year from date of manufacture

SURFACE PREPARATION Coating performance is proportional to the degree of surface preparation. Refer to the

application instructions for specifc primers and intermediate coats for application and curing

procedures. Ensure epoxies are free from amine blush prior to overcoating. All previous

coats must dry and free of contaminants. Adhere to all minimum and maximum topcoat

times for specific primers and intermediate coats. Aged epoxy coatings may require abrad-

ing prior to applyingPSX1001. A test patch over unknown coatings is recommended.


Ambient temperatures 40F to 120F (5C to 49C)


Surface temperature 40F to 120F (5C to 49C) Surface temperature must be at least 5F above the dew

point temperature.

Relative humidity 20% 90%

General air quality Area should be sheltered from airborne particulates and pollutants. Avoid combustion

gases or other sources of carbon dioxide that may promote ambering of light colors.

Ensure good ventilation during application and curing. Provide shelter to prevent wind

from affecting spray patterns.

INSTRUCTIONS FOR USEMixing Agitate with a power mixer for 1-2 minutes until completely dispersed.

Airless spray 28:1 pump or larger, 0.013-0.015 fluid tip


trap in the main line is essential.

Brush & roll Use a high quality natural bristle brush and / or solvent resistant, 1/4" or 3/8" nap roller.

Ensure brush / roller is well loaded to avoid air entrainment. Multiple coats may be

necessary to achieve adequate film build. Amercoat851 flow control additive can be

used to for enhanced flow and leveling with brush and roll application.

Thinner Amercoat911

Cleaning solvent Amercoat12 Cleaner orAmercoat911 thinner

PSX1001

page 1/3


18/331

Primers AmercoatOne,Amercoat5105,Amercoat185H,Amercoat370,Amercoat399,

Amerlock2/400,Amercoat235,Amercoat240


safety data sheetsThis is a solvent borne paint and care should be taken to avoid inhalation of spray mist


DRY/CURE TIMES* PSX1001 @ 2 mils dft

PRODUCTQUALIFICATIONS Compliant with USDA Incidental Food Contact Requirements

NFPA Class A Flame Spread

AVAILABILITY

Packaging Available in 1-gallon and 5-gallon kits

Product codes PX1001-23 Pearl Gray base

PX1001-3 White base

PX1001-9 Black base

PX1001-T1 Deep tint base*

PX1001-T2 Light tint base*

PX1001-T3 Neutral tint base*

PX1001-T4 Red tint base*

PX1001-T5 High Hiding Yellow tint base** Tintable using UCD V-Line colorants only.




data sheet is used.

WARRANTYSTATEMENT


THESE ARE THE ONLY WARRANTIES THAT PPG MAKES AND ALL OTHER EXPRESS OR IMPLIED WARRANTIES,

UNDER STATUTE OR ARISING OTHERWISE IN LAW, FROM A COURSE OF DEALING OR USAGE OF TRADE, INCLUDINGWITHOUT LIMITATION, ANY OTHER WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE OR USE, ARE DISCLAIMEDBY PPG.






PSX1001

page 2/3

50F 70F 90F

Dry to touch 3 hours 2 hours 1 hour

Dry through 24 hours 12 hours 8 hours

Dry to recoat 12 hours 4 hours 2 hours

Maximum recoat Unlimited


19/331

page 3/3

PSX1001





product and related information is designed for users having the requisite knowledge and industrial skills in the industry and itis the end-users responsibility to determine the suitability of the product for its own particular use and it shall be deemed that







using the product.





20/331

March 2014

Revision of May 2013

DESCRIPTION Fast Dry, Surface Tolerant, High Solids Epoxy Coating

PRINCIPAL CHARACTERISTICS Fast dry Low VOC

High performance general maintenance coating for new or old steel

Self priming over most existing coatings

Compatible with prepared damp surfaces

Compatible with adherent rust remaining on prepared surfaces

Dry temperature resistance up to 450F on insulated or uninsulated surfaces when

mixed withAmercoat880 glass flake additive

Suitable for use in many industries including off-shore, water/wastewater, power,

steel fabrication and public use facilities.

Proven coating as a bulk rail lining and dtm exterior coating

COLORAND GLOSS* Semi-gloss

Standard primer colors, custom colors, and aluminum* Epoxy coatings will chalk and fade with exposure to sunlight. Light colors are prone to ambering to some

extent. Note that product tinted to custom colors are not recommended for immersion service. Only use factory

grind batches for immersion.

BASIC DATA


VOC 1.5 lbs/gal (180 g/L) EPA Method 24

(UseAmerlock2 VOC when


21/331

The maximum allowable moisture transmission is 3 lbs / 1,000 ft2/24 hours. Refer toInformation Sheet 1496ACUS for further details regarding moisture measurements.

Galvanized Steel Remove oil or soap film with detergent or emulsion cleaner. Lightly abrasive blastwith a fine abrasive in accordance with SSPC SP-16 guidelines to achieve a profile of1.5-3.0 mils. When light abrasive blasting is not possible, galvanizing can be treatedwith a suitable zinc phosphate conversion coating. Galvanizing that has at least 12months of exterior weathering and has a rough surface with white rust present maybe over-coated after power washing and cleaning to remove white rust and othercontaminants. The surface must have a measurable profile. A test patch is recom-mended to confirm adhesion. Not recommended over chromate sealed galvanizingwithout blasting to thoroughly remove chromates. Adhesion problems may occur.

Non-Ferrous Metals and Abrasive blast in accordance with SSPC SP-16 guidelines to achieve a uniform andStainless Steel dense 1.5-4.0 mil anchor profile. Size and hardness of abrasive should be adjusted

as necessary based on the hardness of the substrate. Aluminum may be treatedwith a surface treatment compliant with Mil-DTL-5541 or equivalent (non-immersionapplications only).

Aged coatings All surfaces must be clean, dry, tightly bonded and free of all loose paint, corrosionproducts or chalky residue. Abrade surface, or clean with Prep 88. Amerlock2 is

compatible over most types of properly applied and tightly adhering coatings, however,a test patch is recommended to confirm compatibility.

Repair Prepare damaged areas to original surface preparation specifications, featheringedges of intact coating. Thoroughly remove dust or abrasive residue before touch-up.


Ambient temperatures* 20F to 122F (-6C to 50C)

* Amerlock 400 hardener can be used with the Amerlock 2/400 base component for applications that require along pot life. The A component is the same for Amerlock 400 and Amerlock 2. The B components are inter-

changeable.


Relative humidity 0 to 100%, surface must be free of visible moisture. For immersion service and for

optimum performance, surface temperature must be at least 5F above the dew point

temperature.

Surface temperature 20F to 122 F (-6C to 50C)

* Amerlock 2 may be applied to surfaces as hot as 250F (121C) for non-immersion service. When applyingAmerlock 2 to surfaces between 122F and 250F, Amerlock 2 must be thinned at 1/2 pint per gallon with only

Amercoat 101 thinner. Multiple thin passes may be required to achieve film build and to avoid solvent blistering.


gases or other sources of carbon dioxide that may promote amine blush. Ensure good


spray patterns. Refer to Information Bulletin #1489 for further information on prevention,

detection, and mitigation of amine blush.


Mixing ratio by volume 1 part base to 1 part hardener

Pre-mix pigmented components with a pneumatic air mixer at moderate speeds tohomogenize the container. Add hardener to base and agitate with a power mixer for 1-2

minutes until completely dispersed.Pot life

Induction time None required

Airless spray 45:1 pump or larger, 0.017-0.019 fluid tipCan be sprayed with plural component application equipment.

Air spray Thin up to 20%, standard conventional equipment, 0.070 fluid orifice

Brush & roll Use a high quality natural bristle brush and / or solvent resistant, 3/8 nap roller. Ensurebrush / roller is well loaded to avoid air entrainment. Multiple coats may be necessary toachieve adequate film build.

AMERLOCK2

page 2/4

32F 50F 70F 90F

2 4 hours 2 hours 1 hour 0.5 hour

2AL 3 hours 1.5 hours 0.75 hour 0.5 hour


22/331

page 3/4

AMERLOCK2

Thinner Amercoat65 (xylene), Amercoat101 (recommended for > 90F),AmercoatT10,Amercoat8 (to extend pot life 10-20%)

Cleaning solvent Amercoat12 Cleaner orAmercoat65 thinner (xylene)

Primers Direct to substrate;Dimetcoteseries primers, Amercoat68HS,Amercoat68MCZTopcoats Amercoat450 Series Polyurethanes,Amershield,PSX700,PSXOne,Amercoat220

Series Acrylics,PitthanePolyurethanes


safety data sheets



DRY/CURE TIMES Amerlock2 @ 5 mils dft

Amerlock2 Aluminum @ 5 mils dft

* Dry times are dependent on air and surface temperatures as well as film thickness, ventilation, and relativehumidity. Maximum recoating time is highly dependent upon actual surface temperatures not simply air

temperatures. Surface temperatures should be monitored, especially with sun-exposed or otherwise heated

surfaces. Higher surface temperatures shorten the maximum recoat window.An extended recoatable window

may be allowable in some circumstances. Please contact your PPG PMC representative for more details.

Surface must be clean and dry. Any contamination must be identified and removed. A detergent wash with

Prep 88 or equivalent is required prior to application of topcoats after 30 days of exposure. However, particular

attention must be paid to surfaces exposed to sunlight where chalking may be present. In those situations, a

further degree of cleaning may be required. PPG Technical Service can advise on suitable cleaning methods.

If maximum recoat/topcoat time is exceeded, then roughen surface.


NFPA Class A for Flame Spread and Smoke Development

Qualified for ANSI/NSF Standard 61 (potable water) for tanks, pipes, valves, and fittings.For NSF application instructions, please visit our website at:www.ppgamercoatus.ppgpmc.com/NSF/

AWWA C210-98

AWWA C550-98

AWWA D102-06 ICS #1, #2, #3, #5

LEEDs compliant for Anti-corrosive Paint category

Nuclear Service Level 2 (ANSI N 5.12, ANSI N 101.2)

NORSOK M501 Rev. 5, System 7 Subsea surfaces

32F 50F 70F 90F

Dry to touch 24 hours 8 hours 2 hours 1 hour


Dry to recoat/topcoat 24 hours 12 hours 6 hours 3 hours

Max recoat, self 90 days 60 days 30 days 14 days

Max topcoat,urethanes,PSX

30 days 21 days 7 days 4 days

Cure to immersionfactory colors only


Cure to immersion -potable water

Refer to: www.ppgamercoatus.ppgpmc.com/NSF/for specific application and curing requirements

32F 50F 70F 90F

Dry to touch 30 hours 11 hours 3.5 hours 2 hours

Dry through 48 hours 17 hours 7 hours 3.5 hours

Dry to recoat 30 hours 12 hours 6 hours 3 hours




Cure to immersion 21 days 7 days 4 days 3 days


23/331

page 4/4

AVAILABILITY


2-gallon kits have 1 full gallon of base and 1 full gallon of hardener

5 gallon kits have 2.5 gallons of base and 2.5 gallons of hardenerInventory (made to order, etc..) Global availability

Product codes AK2-1 Buff

AK2-3 White

AK2-9 Black

AK2-23 Pearl Gray

AK2-72 Oxide Red

AK2-81 Safety Yellow

AK2-T1 Deep Tint base*

AK2-T2 Light Tint base*

AK2-T3 Neutral Tint base*

AK2-T4 Red Tint base*

AK2-T5 High Hiding Yellow Tint base*

AK2-B Hardener componentAK2-01A Amerlock 2AL Aluminum Base

AK2-01B Amerlock 2AL Aluminum Hardener

* Tintable using UCD V-Line colorants only.




data sheet is used.

WARRANTY STATEMENT


THESE ARE THE ONLY WARRANTIES THAT PPG MAKES AND ALL OTHER EXPRESS OR IMPLIED WARRANTIES, UNDERSTATUTE OR ARISING OTHERWISE IN LAW, FROM A COURSE OF DEALING OR USAGE OF TRADE, INCLUDING WITHOUTLIMITATION, ANY OTHER WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE OR USE, ARE DISCLAIMED BY PPG.



IN NO EVENT WILL PPG BE LIABLE UNDER ANY THEORY OF RECOVERY (WHETHER BASED ON NEGLIGENCE OFANY KIND, STRICT LIABILITY OR TORT) FOR ANY INDIRECT, SPECIAL, INCIDENTAL, OR CONSEQUENTIAL DAMAGESIN ANY WAY RELATED TO, ARISING FROM, OR RESULTING FROM ANY USE MADE OF THE PRODUCT.


development. All recommendations or suggestions relating to the use of the PPG product, whether in technical documentation,or in response to a specific inquiry, or otherwise, are based on data, which to the best of PPGs knowledge, is reliable. Theproduct and related information is designed for users having the requisite knowledge and industrial skills in the industry and itis the end-users responsibility to determine the suitability of the product for its own particular use and it shall be deemed thatBuyer has done so, as its sole discretion and risk.

PPG has no control over either the quality or condition of the substrate, or the many factors affecting the use and application ofthe product. Therefore, PPG does not accept any liability arising from any loss, injury or damage resulting from such use orthe contents of this information (unless there are written agreements stating otherwise). Variations in the application environment,changes in procedures of use, or extrapolation of data may cause unsatisfactory results.

This sheet supersedes all previous versions and it is the Buyers responsibility to ensure that this information is current prior tousing the product.

Current sheets for all PPG Protective & Marine Coatings Products are maintained at www.ppgpmc.com. The English text ofthis sheet shall prevail over any translation thereof.

AMERLOCK2

Amerlock is a registered trademark of PPG Industries Ohio, Inc.


24/331

November 2012

Revision of November 2012

DESCRIPTION Fast Dry Aluminum Epoxy Mastic Coating

PRINCIPAL CHARACTERISTICS Fast dry, Low Temperature Curing

Low VOC

High performance general maintenance coating for new or old steel

Self priming over most existing coatings

Formulated with lamellar aluminum flake for enhanced corrosion protection

Compatible with adherent rust remaining on prepared surface

COLOR AND GLOSS* Dull Metallic

Aluminum

BASIC DATA


VOC 1.0 lbs/gal (120 g/L)Recommended

Dry film thickness (per coat) 4 8 mils (100 200 microns)

Theoretical Spread Rate @ 1 mils dft 1411 ft2/gal

@ 6 mils dft 235 ft2/gal

Components 2

Shelf Life 3 years from date of manufacture

SURFACE PREPARATION Coating performance is, in general, proportional to the degree of surface preparation.

Steel Remove weld spatter, protrusions, and laminations in steel. Remove all surface

contaminants, oil and grease in accordance with SSPC SP-1.

Abrasive blast with an angular abrasive to an SSPC SP-10 cleanliness or higher for

immersion service. Achieve a surface profile of 2.0-4.0 mils. For atmospheric service,

abrasive blast to SSPC SP-6 standards.

The product may be applied over an SSPC WJ-2(L) where a previous blast profile

can be exposed.

For maintenance and repair in atmospheric service, the product can be applied

over surfaces prepared in accordance with SSPC SP-2 or SSPC SP-3 (hand and

power tool cleaning).

Amercoat 114A may be used as a pit filler for severely pitted steel and surface dis-

continuities.

Check with PPG technical service for the maximum allowable soluble salt level for

water immersion service. This will vary based on the water chemistry and service

temperatures.

Non-ferrous metals Lightly abrasive blast in accordance with SSPC SP-16 to achieve a uniform and

dense 1.5-4.0 mil anchor profile.

Aged Coatings and Repairs Ensure the coating system is sound and well adhered. Do not apply over acrylic

coatings or coatings that exhibit poor solvent resistance. A test patch is recommended.

Sweep blast or otherwise thoroughly abrade the existing coating in accordance with

SSPC SP-7. Alternately, Prep 88 may be used to prepare some existing coatings.

Please refer to Prep 88 data sheet for details. Feather the edges of tightly adhered,

in-tact coatings at the perimeter of repair areas. Power tool clean the existing steel

in accordance with SSPC SP-3 (atmospheric service) or SSPC SP-11 (immersion

service).

AMERLOCK2AL

page 1/3


25/331


Ambient temperatures 20F to 122F (-6C to 50C)


Relative humidity 0 to 90%, For immersion service and for optimum performance, surface temperature

must be at least 5F above the dew point temperature.

Surface temperature 20F to 122 F (-6C to 50C)

* The surface should be inspected to ensure there is no ice present on the substrate in cold weather conditions.


gases or other sources of carbon dioxide that may promote amine blush. Ensure good


spray patterns. Refer to Information Bulletin #1489 for further information on prevention,

detection, and mitigation of amine blush.



Pre-mix pigmented components with a pneumatic air mixer at moderate speeds to

homogenize the container. Add hardener to base and agitate with a power mixer for 1-2minutes until completely dispersed.

Pot life



Can be sprayed with plural component application equipment.

Air spray Thin up to 20%, standard conventional equipment, 0.070" fluid orifice

Brush & roll Use a high quality natural bristle brush and / or solvent resistant, 3/8" nap roller. Ensure

brush / roller is well loaded to avoid air entrainment. Multiple coats may be necessary to

achieve adequate film build.

Thinner Amercoat65 (xylene), Amercoat101 (recommended for > 90F)Cleaning solvent Amercoat12 Cleaner orAmercoat65 thinner (xylene)

Primers Direct to substrate;Dimetcoteseries primers, Amercoat68HS

Topcoats Amercoat450 Series Polyurethanes,Amershield,PSX700,PSXOne,Amercoat220

Series Acrylics


safety data sheets



DRY/CURE TIMES* Amerlock2AL @ 5 mils dft

* Dry times are dependent on air and surface temperatures as well as film thickness, ventilation, and relativehumidity. Maximum recoating time is highly dependent upon actual surface temperatures not simply air

temperatures. Surface temperatures should be monitored, especially with sun-exposed or otherwise heated

surfaces. Higher surface temperatures shorten the maximum recoat window.






AMERLOCK2AL

page 2/3

32F 50F 70F 90F

2AL 3 hours 1.5 hours 0.75 hour 0.5 hour

32F 50F 70F 90F

Dry to touch 30 hours 11 hours 3.5 hours 2 hours

Dry through 48 hours 17 hours 7 hours 3.5 hours

Dry to recoat 30 hours 12 hours 6 hours 3 hours






26/331

page 3/3

AMERLOCK2AL

AVAILABILITY



5 gallon kits have 2.5 gallons of base and 2.5 gallons of hardenerInventory (made to order, etc..) Global availability

Product codes AK2-01A Amerlock 2AL Aluminum Base

AK2-01B Amerlock 2AL Aluminum Hardener




data sheet is used.

WARRANTY STATEMENT




LIMITATION OF LIABILITY















using the product.





27/331

November 2012


DESCRIPTION Low VOC, Fast Dry, High Solids Epoxy Coating

PRINCIPAL CHARACTERISTICS Fast dry, dry to recoat in 3 hours at 70F (21C)

VOC compliant for


28/331

Galvanized Steel Remove oil or soap film with detergent or emulsion cleaner. Lightly abrasive blast

with a fine abrasive in accordance with SSPC SP-16 guidelines to achieve a profile of

1.5-3.0 mils. When light abrasive blasting is not possible, galvanizing can be treated

with a suitable zinc phosphate conversion coating. Galvanizing that has at least 12months of exterior weathering and has a rough surface with white rust present may

be over-coated after power washing and cleaning to remove white rust and other

contaminants. The surface must have a measurable profile. A test patch is recom-

mended to confirm adhesion. Not recommended over chromate sealed galvanizing

without blasting to thoroughly remove chromates. Adhesion problems may occur.

Non-Ferrous Metals and Abrasive blast in accordance with SSPC SP-16 guidelines to achieve a uniform and

Stainless Steel dense 1.5-4.0 mil anchor profile. Size and hardness of abrasive should be adjusted

as necessary based on the hardness of the substrate. Aluminum may be treated

with a surface treatment compliant with Mil-DTL-5541 or equivalent (non-immersion

applications only).

Aged Coatings and Repairs All surfaces must be clean, dry, tightly bonded and free of all loose paint, corrosion

products or chalky residue. Abrade surface, or clean with Prep 88. Amerlock2VOC

is compatible over most types of properly applied and tightly adhering coatings, how-

ever, a test patch is recommended to confirm compatibility.

Repair Ensure the coating system is sound and well adhered. Do not apply over acrylic

coatings or coatings that exhibit poor solvent resistance. A test patch is

recommended. Sweep blast or otherwise thoroughly abrade the existing coating in

accordance with SSPC SP-7. Alternately, Prep 88 may be used to prepare some

existing coatings. Please refer to Prep 88 data sheet for details. Feather the edges

of tightly adhered, in-tact coatings at the perimeter of repair areas. Power tool clean

the existing steel in accordance with SSPC SP-3 (atmospheric service) or SSPC

SP-11 (immersion service).


Ambient temperatures 20F to 122F (-6C to 50C)


Relative humidity 0-100%, surface must be free of visible moisture. For immersion service and for opti-

mum performance, surface temperature must be at least 5F above the dew point tem-

perature.

Surface temperature 20F to 122F (-6C to 50C)


gases or other sources of carbon dioxide that may promote amine blush and ambering

of light colors. Ensure good ventilation during application and curing. Provide shelter to

prevent wind from affecting spray patterns.



Pre-mix pigmented components with a pneumatic air mixer at moderate speeds to

homogenize the container. Add hardener to base and agitate with a power mixer for 1-2

minutes until completely dispersed.

Pot life




Air spray Thin up to 20%, standard conventional equipment, 0.070" fluid orifice

Brush & roll Use a high quality natural bristle brush and / or solvent resistant, 3/8" nap roller. Ensure

brush / roller is well loaded to avoid air entrainment. Multiple coats may be necessary to


AMERLOCK2VOC

50F 70F 90F

2VOC 2 hours 1 hour 0.5 0.75 hour

page 2/4


29/331

page 3/4

AMERLOCK2VOC

Thinner PPG 97-739 and tert-butyl acetate are VOC exempt thinners which can be used

without limit to maintain < 100 g/L.

The following thinners may be used up to 2.5 oz. per gallon to maintain a VOC of

< 100 g/L.Amercoat65 (xylene), Amercoat101 (recommended for > 90F),

Amercoat8 (to extend pot life 10-20%)


Primers Direct to substrate;Dimetcote- Series Primers,Amercoat68HS,Amercoat68MCZ

Topcoats Amercoat450-Series Polyurethanes,AmershieldVOC,PSX700,PSXOne


safety data sheets



DRY/CURE TIMES Amerlock2VOC @ 5 mils dft

* Dry times are dependent on air and surface temperatures as well as film thickness, ventilation, and relativehumidity. Maximum recoating time is highly dependent upon actual surface temperatures not simply airtemperatures. Surface temperatures should be monitored, especially with sun-exposed or otherwise heated

surfaces. Higher surface temperatures shorten the maximum recoat window.surfaces. Higher surface tem-

peratures shorten the maximum recoat window.







AWWA D102-06 ICS #1, #2, #3, #5


AVAILABILITY



5 gallon kits have 2.5 gallons of base and 2.5 gallons of hardener

32F 50F 70F 90F

Dry to touch 24 hours 8 hours 2 hours 1 hour

Dry through 38 hours 13 hours 4.5 hours 2 hours

Dry to recoat/

topcoat 24 hours 6 hours 3 hours 1.5 hours


Max topcoat,

urethanes,PSX 30 days 14 days 7 days 4 days

Cure to immersionfactory colors only



30/331

page 4/4

Product codes AK2V-1 Buff base component

AK2V-3 White base component

AK2V-9 Black base component

AK2V-23 Pearl Gray base componentAK2V-72 Oxide Red base component

AK2V-81 Safety Yellow base component

AK2V-T1 Deep Tint base component*

AK2V-T2 Light Tint base component*

AK2V-T3 Neutral Tint base component*

AK2V-T5 High Hiding Yellow base component*

AK2V-B Hardener component

* Tintable using UCD V-Line colorants only.




data sheet is used.WARRANTYSTATEMENT

















the contents of this information (unless there are written agreements stating otherwise). Variations in the application environment,changes in procedures of use, or extrapolation of data may cause unsatisfactory results.


using the product.



AMERLOCK2VOC



31/331

May 2013


DESCRIPTION High solids glass flake epoxy coating

PRINCIPAL CHARACTERISTICS High build, up to 20 mils in one coat

Compatible with adherent rust remaining on prepared surfaces

Continuous dry temperature resistance of 425F on insulated or uninsulated

surfaces

Resistant to well defined cathodic protections

Decreased film permeability due to glass flake pigmentation

COLORAND GLOSS Flat

Standard primer colors and custom colors

* Epoxy coatings will characteristically chalk and fade upon exposure to sunlight. Light colors are prone to

ambering to some extent. Only use factory colors for immersion service.

BASIC DATA


VOC 1.4 lbs/gal (172 g/L)

Recommended

Dry film thickness (per coat)* 8 20 mils (200 500 microns)

* For high temperature applications above 250F, limit total film thickness to 10 mils dft with spot readings to 12mils.

Theoretical Spread Rate @ 1 mils dft 1347 ft2/gallon

@ 8 mils dft 168 ft2/gallon

@ 20 mils dft 67 ft2/gallon

Components 3

Shelf Life 3 years from date of manufacture

SURFACE PREPARATION Coating performance is, in general, proportional to the degree of surface preparation.Steel Remove weld spatter, protrusions, and laminations in steel. Grind welds smooth in

accordance with NACE RP-0178. Remove all surface contaminants, oil and grease

in accordance with SSPC SP-1.

Abrasive blast with an angular abrasive to an SSPC SP-10 cleanliness or higher for

immersion service. Achieve a surface profile of 2.0-4.0 mils. For atmospheric service,

abrasive blast to SSPC SP-6 standards.

The product may be applied over an SSPC SP-12 WJ-2(L) where a previous blast

profile can be exposed.

For maintenance and repair in atmospheric service, the product can be applied

over surfaces prepared in accordance with SSPC SP-2 or SSPC SP-3 (hand and

power tool cleaning).

Amercoat114A may be used as a pit filler for severely pitted steel and surface

discontinuities.Check with PPG technical service for the maximum allowable soluble salt level for

water immersion service. This will vary based on the water chemistry and service

temperatures.

Concrete Remove all surface contaminants such as oil, grease, and embedded chemicals.

Abrade the surface per ASTM D 4259 to remove all chalk and surface glaze or

laitance. Mechanical surface preparation should expose sub-surface voids and

provide a surface profile equivalent to 60 grit sandpaper or coarser. Surface should

be free from moisture in accordance with ASTM D4263. Refer to Information Sheet

#1496ACUS for further details regarding moisture measurements. Slabs on grade

should have a maximum moisture content of 3 lbs/1,000 ft2/24 hours when

measured by calcium chloride test.

AMERLOCK2/400GF

page 1/4


32/331

Non-ferrous metals Lightly abrasive blast in accordance with SSPC SP-16 to achieve a uniform and

dense 1.5-4.0 mil anchor profile.

Stainless Steel Abrasive blast with a hard angular abrasive to achieve a uniform and dense anchor

profile of 1.5-4.0 mils.Aged Coatings and Repairs Ensure the coating system is sound and well adhered. Do not apply over acrylic

coatings or coatings that exhibit poor solvent resistance. A test patch is recommended.

Sweep blast or otherwise thoroughly abrade the existing coating in accordance with

SSPC SP-7. Alternately, Prep 88 may be used to prepare some existing coatings.

Please refer to Prep 88 data sheet for details. Feather the edges of tightly adhered,

in-tact coatings at the perimeter of repair areas. Power tool clean the existing steel

in accordance with SSPC SP-3 (atmospheric service) or SSPC SP-11 (immersion

service).


Ambient temperatures* 20F to 122F (-6C to 50C)

* Amerlock 400 hardener can be used with the Amerlock 2/400 base component for applications that require along pot life. The A component is the same for Amerlock 400 and Amerlock 2. The B components are inter-

changeable

Material temperatures 40 to 90F (5 to 32C)

Relative humidity 0 to 100%, surface must be free of visible moisture. For immersion service and for

optimum performance, surface temperature must be at least 5F above the dew point

temperature.

Surface temperature 20F to 122F (-6C to 50C)


gases or other sources of carbon dioxide that may promote amine blush and ambering

of light colors. Ensure good ventilation during application and curing. Provide shelter to

prevent wind from affecting spray patterns.



Pre-mix pigmented components with a pneumatic air mixer at moderate speeds tohomogenize the container. Add hardener to base and agitate with a power mixer for 1-2

minutes until completely dispersed. Slowly incorporate glass flake additive under

agitation over 1-2 minutes to ensure the glass flake is thoroughly mixed.

Pot life




Air spray Thin up to 20%, standard conventional equipment, 0.070 fluid orifice

Brush & roll Use a high quality natural bristle brush and / or solvent resistant, 3/8 nap roller. Ensurebrush / roller is well loaded to avoid air entrainment. Multiple coats may be necessary to


Thinner Amercoat65 (xylene), Amercoat101 (recommended for > 90F),Amercoat8 (to extend

pot life 10-20%)


Primers Direct to substrate;Dimetcoteseries primers,Amercoat68HS,Amercoat68MCZ,

Amerlock2/400,AmerlockSealer

Topcoats Amercoat450 series polyurethanes, Amershield,PSX700,PSXONE,Pitthane

polyurethanes

AMERLOCK2/400GF

50F 70F 90F

2GF 2 hours 1 hour 0.5 hours

400GF 3 hours 2 hours 1 hour

page 2/4


33/331

page 3/4

AMERLOCK2/400GF


safety data sheets


or vapor as well as contact between the wet paint and exposed skin or eyes.DRY/CURE TIMES Amerlock2GF @ 8 mils dft

Amerlock400GF @ 8 mils dft

* Dry times are dependent on air and surface temperatures as well as film thickness, ventilation, and relative

humidity. Maximum recoating time is highly dependent upon actual surface temperatures not simply airtemperatures. Surface temperatures should be monitored, especially with sun-exposed or otherwise heated

surfaces. Higher surface temperatures shorten the maximum recoat window.



attention must be paid to surfaces exposed to sunlight where chalking may be present. In those situations, afurther degree of cleaning may be required. PPG Technical Service can advise on suitable cleaning methods.




AVAILABILITY



5 gallon kits have 2.5 gallons of base and 2.5 gallons of hardener

Add one 3-gallon can ofAmercoat880 glass flake additive for each 5 gallon kit.Add one 1-gallon can ofAmercoat880 glass flake for each 2 gallon kit.

Inventory (made to order, etc..) Global availability

32F 50F 70F 90F

Dry to touch 48 hours 16 hours 6 hours 2 hours


Dry to recoat/topcoat 48 hours 16 hours 7 hours 4 hours





50F 70F 90F

Dry to touch 28 hours 9 hours 4.5 hours

Dry through 48 hours 20 hours 12 hours

Dry to recoat/ topcoat 36 hours 16 hours 10 hours

Max recoat, self 90 days 90 days 45 days


60 days 30 days 14 days

Cure to immersion 21 days 7 days 4 days


34/331

page 4/4

Product codes AK2-1 Buff

AK2-3 White

AK2-9 Black

AK2-23 Pearl GrayAK2-72 Oxide Red

AK2-81 Safety Yellow

AK2-T1 Deep Tint base

AK2-T2 Light Tint base

AK2-T3 Neutral Tint base

AK2-T4 Red Tint base

AK2-T5 High HidingYellow Tint base

AK2-B Hardener component forAmerlock2GF

AK400-B Hardener component forAmerlock400GF

AT880 Glass flake additive


on a worldwide basis, slight modification of the product is sometimes necessary to complywit