METALS Recap: metallic bonds, metal properties

SummaryMetal lattice, defectsFormation of crystals (crystallisation)Dislocations and Burgers vectorPoissons ratio Case studies: metal whiskers, intergranular corrosion

METALLIC BONDS = A SEA OF ELECTRONSMetal atoms have one or two outer electrons easily moving around, not "belonging" to any one atom, but as a part of the whole crystal, formed by cations (kernels).

Electrons act as a "cement, holding the kernels in their relatively fixed positions.

This structure explains metal characteristics: good conduction, hardness, stiffness, isotropy

How would motion (i.e, plastic deformation) be possible in metals ?

DEFECTS IN METALS Defects in metals have a negative effect, in that they create internal stresses. However, they also allow plastic deformation, which may reduce brittleness In principle, impurities have also to be removed, but alloying may confer useful properties to the metal (e.g., resistance to corrosion, higher surface hardness, improved workability)

CASE STUDY 1: WHISKERSWhiskers are metal crystalsideally without defects.A number of metals can be solidifiedso to get whiskers, including tin, zinc, cadmium, silver, iron and nickel.

Limitations of whiskers are their very small dimension (length of up to 10 mm), their brittleness and their cost, due to the high reject rate in the manufacturing processTin whisker (diameter 150 m)Whiskers are nowadays confined to few applications (reinforcement in heat exchangers, turbines, catalysts or catalyst carriers), whilst the formation of whiskers in plated surfaces can create problems (e.g., short circuits in electromagnetic relays)

HOW DEFECTS ARE FORMED:SOLIDIFICATION OF METALSMetal crystals are formed through two phases: nucleation i.e., creation of small crystals (nuclei) and growing of nuclei.Since a number of nuclei are formed in the same liquid metal, when they come into contact, they are likely not to fit each other exactlyAs a consequence, metals are formed with grains, having well defined boundariesA characteristic which affects mechanical properties of metal is their grain size.

CASE STUDY 2: INTERGRANULAR CORROSIONInter-granular corrosion is localised attack along the grain boundaries or close to them, while the bulk of the grains remain largely unaffected.This happens because some elements present in the alloy (e.g., chromium in stainless steel) are segregated at the grain boundaries, so that resistance to corrosion in the area is reduced.The problem can be addressed e.g., by reheating a welded component, so that chromium is absorbed in the grain. Inter-granular corrosion in aluminiumfor zinc precipitation(failed aircraft component)

IMPERFECT SOLIDIFICATION: DENDRITESDuring metal solidification, if solid does not grow from the side wall e.g., of the mould evenly, some of the heat involved in the process is absorbed again by the metal.If this is the case, dendrites (tree-like structures) form as the metal solidifies out into the melt, leaving molten metal behind. Dendrite formation is common: however the better a melt is inoculated, the fewer dendrites.Dendrites modify metal hardness and stiffness, allow corrosion in harsh environments, reduce electrical conductivity and make welding difficult.

Dendrite(dendron is Greek for tree)

HOW DEFECTS MOVE AROUND:DISLOCATIONSThe theory of dislocations explains how defects in metals can produce plastic deformation. Two types of dislocations are possible: edge and screw dislocations. Most observed dislocations are a mix of the two types.Edge dislocationScrew dislocation

DISLOCATION CYCLE(BURGERS VECTOR)Edge dislocation:an extra sheet of atoms within the latticeScrew dislocation:a number of atoms sheetsare transformed in a helice-like surfaceBurgers vector represents the deformation produced by a dislocation

MAIN TYPES OF METAL UNIT CELLS Body-centred cubic (b.c.c.) (9 atoms per unit cell): e.g., chromium, iron , tungsten, vanadium

Face-centred cubic (f.c.c.) (14 atoms per unit cell): aluminium, nickel, iron

Hexagonal compact (h.cp.) (17 atoms per unit cell): magnesium, zinc, titanium Face-centred cubic and hexagonal compact give the maximum possible packing

SHEAR DEFORMATION:POISSONS RATIOLike Youngs modulus E measures the resistance of materials to deformation in the longitudinal direction, another modulus G (shear modulus) measures their resistance to deformation in the transverse direction.G is important to measure the slip between atom sheets in metals, hence the plastic shear deformationA relation between G and E exists for homogeneous and isotropic materials, which is: (nu) is the negative ratio between transverse and longitudinal strain (Poissons ratio)

THE VALUE OF POISSONS RATIOAND WHAT IT SUGGESTS Poissons ratio gives a measure of how much the material cross-section changes as far as the material is elongated. The higher is, the more the material cross section is reduced.Typically, metals have Poissons ratios around 0.3Rubbery materials have Poissons ratios close to 0.5Soft materials with a large amount of porosity(foams) have Poissons ratio close to 0As a consequence of these values, most materials are stiffer in the direction they are loaded than in shear