Slide 2 LDC borstpltering www.ldc-brushplating.com2 LDC Portable
Electroplating 1.Cold process: used at room temperature, no stress
or adjustments because of termal distorsion. 2.To tolerance:
normally no machining required 3.Quick metal build-up: 0,05 mm in
10-15 min. 4.Plating: on all conductive materials, cast iron,
stainless, mild steel, copper, chrome etc 5.Dense deposits: no or
very little porosity in most coatings 6.Many differens metals:
nickel, gold, silver, copper, cobolt, zinc and alloys. 7.Excellent
bonding: molecular bonding results in very god adhesion, all
coatings can be machined, ground or polished. 8.Mobile equipment:
the repair can be done on site Slide 3 www.ldc-brushplating.com 3
On site repair of the crankshaft in a conversion press. LDC
borstpltering Tele: + 46 248 174 40 E-mail: [email protected] Slide 4
www.ldc-brushplating.com 4 LDC borstpltering Tele: + 46 248 174 40
E-mail: [email protected] Damaged /worn flywheel bearing areas on the
crankshaft in a conversion press. Slide 5 www.ldc-brushplating.com
5 LDC borstpltering Tele: + 46 248 174 40 E-mail: [email protected]
Prepare and masking off surrounding areas. Slide 6
www.ldc-brushplating.com 6 Plating procedure going on. LDC
borstpltering Tele: + 46 248 174 40 E-mail: [email protected] Slide 7
www.ldc-brushplating.com 7 Damaged bearing journal plated to size.
LDC borstpltering Tele: + 46 248 174 40 E-mail: [email protected]
Slide 8 www.ldc-brushplating.com 8 LDC borstpltering Tele: + 46 248
174 40 E-mail: [email protected] Crankshaft is finished and the
original tolerances and measurements are obtained. Ready to
assemble the flywheel. Slide 9 www.ldc-brushplating.com 9 Repair on
site. Lower bed die in a conversion press with local wear damages
LDC borstpltering Tele: + 46 248 174 40 E-mail: [email protected]
Slide 10 www.ldc-brushplating.com 10 Plated/repaired damage on the
lower bed die. LDC-2904 copper hi-speed HB250 were used to fill the
damage up. Top coated with LDC-2807 Nickel acid for wear and
corrosion protection. LDC borstpltering Tele: + 46 248 174 40
E-mail: [email protected] Slide 11 www.ldc-brushplating.com 11 Repair
on site. Lower bed die in a conversion press with local wear
damages LDC borstpltering Tele: + 46 248 174 40 E-mail:
[email protected] Slide 12 www.ldc-brushplating.com 12 Damaged area in
the lower bed die. LDC borstpltering Tele: + 46 248 174 40 E-mail:
[email protected] Slide 13 www.ldc-brushplating.com 13 One worn out
slide. There are damages from the pistons and micro vibrations. And
causes oil leaking. LDC borstpltering Tele: + 46 248 174 40 E-mail:
[email protected] Slide 14 www.ldc-brushplating.com 14 Damaged area
inside the slide LDC borstpltering Tele: + 46 248 174 40 E-mail:
[email protected] Slide 15 www.ldc-brushplating.com 15 The damages is
being plated with a hard copper of 250 Brinell and grinded to
original tolerances. LDC borstpltering Tele: + 46 248 174 40
E-mail: [email protected] Slide 16 www.ldc-brushplating.com 16 Area
has now a new top coating with a nickel with a hardness of 400
brinell and also gives a excellent protection from new damages. LDC
borstpltering Tele: + 46 248 174 40 E-mail: [email protected] Slide 17
www.ldc-brushplating.com 17 Plating is now finished and the slide
is ready for assembly. LDC borstpltering Tele: + 46 248 174 40
E-mail: [email protected] Slide 18 www.ldc-brushplating.com 18 Oil
leakage from scratched and damaged main pistons brush plated on
site. LDC borstpltering Tele: + 46 248 174 40 E-mail:
[email protected]