High Quality • User-Friendly Epoxies - Resins - Coatings - Adhesives
415 E. Venice Avenue
Venice, FL 34285
(800) 828 8929 Tel
(941) 488 0747 Fax
www.dcdynamis.com
Innovation Custom Formulas
Marine • Automotive • Electrical • Industrial
MRO Products - Concrete Repair
3-Component epoxy compound for resurfacing large areas of worn concreteAvailable Colors: 270 Medium Grey 630 Light Grey 076 Tile Red 3-Component epoxy compound for resurfacing large areas of worn concreteLow-temperature cure (or fast cure at room temperature)Available Colors: 270 Medium Grey 630 Light Grey 076 Tile Red
3-component epoxy compound for patching holes in concrete or for use as grout for setting machinery or tile.
3-component epoxy compound for patching holes in concrete or for use as grout for setting machinery or tile. Low-temperature cure (or fast cure at room temperature)Available Colors: 270 Medium Grey 630 Light Grey 076 Tile Red
Epoxy compound for adhering thin layers of new concrete to old, without cracking of new concrete as it dries. Clear in color.
3-component epoxy compound for cementing anchor bolts into concrete.Available Color: 630 Light Grey
Semi-rigid epoxy compound for filling saw-cut joints in concrete.Available Colors: 270 Medium Grey 630 Light Grey 076 Tile Red
Semi-rigid epoxy compound for filling saw-cut joints in concrete.Low-temperature cure (or fast cure at room temperature)Available Colors: 270 Medium Grey 630 Light Grey 076 Tile Red
Product Name Part No. Unit Size Mix Ratio Description
EPO Resurfacer
EPO Resurfacer LTC
EPO Patch & Grout
EPO Patch LTC
EP-Unite Clear
EPO Anchoring Cement
EPO Joint Sealant
EPO Joint Sealant LTC
RES50
RESLT50
EP.75
EP3EP10EP50 EPLT.75
EPLT3EPLT10EPLT50
EU.75EU3
EA10EA45
EJ1EJ2EJ10
EJLT1EJLT2EJLT10
50 lb Kit
50 lb Kit
3/4 Gal. Kit (PT A&B only) 3 Gal. Kit 10 Lb. Kit50 Lb. Kits
3/4 Gal. Kit (PT A&B only) 3 Gal. Kit 10 Lb. Kit50 Lb. Kits
3/4 Gal. Kit 3 Gal. Kit
10 Lb. Kit 45 Lb. Kit
1 Gal. Kit 2 Gal. Kit10 Gal. Kit
1 Gal. Kit 2 Gal. Kit10 Gal. Kit
2:1
2:1
2:1
2:12:12:1
2:1
2:12:12:1
2:12:1
2:12:1
1:11:11:1
1:11:11:1
EPO Coat VA
EPO Coat Zinc Rich Primer
EPO Coat H3H
EPO Coat NS-100
EPO Seal 100
VA.5VA1VA2VA10
ECZP22
ECH3P.75ECH3P3
NS100.5Ns100.1
ES100.75ES1003ES10015
1/2 Gal. Kit 1 Gal. Kit 2 Gal. Kit 10 Gal. Kit
22 Lb. Gal. Kit
3/4 Gal. Kit3 Gal. Kit
1/2 Gal. Kit1 Gal. Kit
3/4 Gal. Kit 3 Gal. Kit15 Gal. Kit
High-Solids general purpose 2-component epoxy coating for concrete floors and for machinery.Available Colors: 270 Medium Grey 672 Green 531 Medium Beige 642 Light Beige 076 Tile Red 386 Off White 001 White 907 Safety Yellow 630 Light Grey 526 Light Blue 000 Black
Heavily zinc-filled corrosion-resistant epoxy metal primer
100% Solids chemical-resistant and wear-resistant 2-component epoxy coating.Available Colors: 270 Medium Grey 076 Tile Red 001 White 531 Medium Beige Clear
100% Solids non-slip epoxy coatingAvailable Colors: 270 Medium Grey 076 Tile Red 907 Safety Yellow
100% Solids 2-component general purpose epoxy concrete sealer.
MRO Products - CoatingsProduct Name Part No. Unit Size Mix Ratio Description
1:11:11:11:1
2:1
2:12:1
3:13:1
2:12:12:1
Adhesives Products
How to Apply Epoxy Floor Coating Paint
Floor coating with epoxy paint before Finished ApplicationMixing Epoxy Floor Paint
After proper surface preparation, application technique is the next most important step in floor coating. First you must assess the mix ratio of the product you are using.
All Dynamis epoxy products have simple 1:1 or 2:1 mix ratios. You mix either 1 unit of part “A” by volume to 1 unit of part “B” by volume or you mix 2 units part “A” by volume to 1 unit part “B” by volume.
Our simple mix ratios allow you to easily measure out partial kits if you will not be coating enough floor to use an entire kit. Our EPO Coat H3H 100% solids epoxy coating system has a 2:1 mix ratio.
After making note of the mix ration, you must find measuring containers and a mixing container. Ideally you’ll want a separate measuring container for part “A” and part “B”.
You should then mix each component thoroughly in its original container in case the material has separated, to ensure a good mix. Measure out your components into the mixing container observing the proper mixing ratio.
Once measured out, it’s best to use a drill with a mixing blade to ensure a thorough mix. Stir with the drill for 2-3 minutes. Then carefully scrape the sides and bottom of the container with the mixer and then stir for another 1-2 minutes.
After mixing, it’s important to note that some epoxy coatings require a “sweat-in” time of 15-30 minutes. This helps to achieve a more rapid and thorough cure for a slower-curing product once the material is on the floor. Our EPO Coat H3H 100% solids epoxy coating system does not require this “sweat-in” period.
After mixing, and the sweat-in period if necessary, you must choose a roller. For epoxies you will generally want to choose a roller with a very short nap, 1/8” to ¼”, with a phenolic core. This type of roller will hold up and won’t shed hairs into your beautiful new floor even as the epoxy becomes thicker and stickier as it approaches the end of its working life.
Roll the coating out observing the approximate coverage information for the specific coating that you are using. It’s important not to stretch the material too thin as it will simply soak into the concrete and leave you with very little external protection or aesthetic effect.
On bare concrete you will want to apply two coats, the first one thinned with acetone or MEK (please check your local laws to ensure that this is legal at your location) to provide a solid mechanically-bonded base coat.
When going over an existing epoxy floor that is mostly intact one coat will generally suffice. If applying two coats, the second coat can be applied as soon as the first coat is dry to walk on and tack-free.
Once rolled, remove any masking as soon as possible to avoid it sticking to the freshly coated floor. You will be able to walk on it after 8-12 hours, but avoid any car or forklift traffic for 72 hours to avoid leaving tire marks.
If you follow these steps you will have a very durable epoxy floor that will take a lot of abuse and look very good at the same time.
Surface Preparation
Best coating system only as good as the surface it is applied to
Surface abrasion, where it is difficult to contain water used in acid-etching
Acid-etching, dissolve concrete dust on unprepared concrete
The first and arguably most important step in any floor coating job is surface preparation. After all, even the very best coating system is only as good as the surface it is adhered to. With that in mind, the first step is cleaning.
All dust and dirt must be removed from the surface. Any loose chips of a previous coating must be removed. Any oil must be carefully removed with soap and hot water or else the coating will surely peel in those areas.
After cleaning, the grain of the concrete must be exposed to ensure maximum adhesion of the coating to the concrete. There are a primary types of surface preparation for a concrete floor: acid-etching and surface abrasion.
Prepare the concrete surface with acid etching
Acid-etching is the process of using an acid, usually muriatic acid, to dissolve the concrete dust that is always present on unprepared concrete. Since concrete dust is alkali, the acid does a good job of reacting to and dissolving the dust and then it can be removed with a simple wash-down.
To accomplish acid-etching, simply take muriatic acid, available at any pool supply store, and dilute it with water at a ratio of 1 part acid to 3 parts water.
This can be applied to the concrete using a watering can. When you can just start to see the grain of the concrete coming through, neutralize the acid solution with clear ammonia. The resulting solution is nonhazardous and can be washed down with water.
There are multiple methods for surface abrasion including sandblasting, shot-blasting, and grinding. Each of these methods provides a good solid grain in the concrete for the coating to adhere to.
The primary disadvantage of surface abrasion vs acid-etching is the large amount of concrete dust that is generated. However, surface abrasion is ideal for situations where it would be difficult to contain the large amount of water used in acid-etching.
All of these procedures may seem like a lot of extra work, but ultimately a good surface preparation will ensure that your floor coating will withstand the test of time. When it’s time to recoat, a basic cleaning and a quick sanding with a sanding disk will be all that’s required to prepare the epoxy surface for a new coating.
Epoxy compound for dynamic balancing of rotating parts. Ideal for use in electric motor manufacturing and repair. 40-year industry history.
Improved epoxy compound for dynamic balancing of rotating parts. Ideal for use in electric motor manufacturing and repair. 1:1 Mix Ratio by weight or volume.
Intermediate cure epoxy compound for dynamic balancing of rotating parts. Ideal for use in electric motor manufacturing and repair.
Rapid cure epoxy compound for dynamic balancing of rotating parts.Ideal for use in electric motor repair.
Semi-flexible epoxy potting compound for sealing leads in submersible pumps.
Semi-flexible epoxy potting compound for sealing leads in submersible pumps. Slower cure version for larger pours up to 2 gallons at once.
EPO Dynaweight
EPO Dynaweight BAL-VI
EPO Dynaweight BAL-I-FS
EPO Dynaweight BAL-XV-FS
Pour Flex 150-2
Pour Flex 350-5
ED2ED15ED60ED150
ED62ED616ED676
ED12ED116
ED152ED1516
PF1PF2PF8
PF3502PF3508PF35016
2 lb. Kit15 lb. Kit60 lb. Kit150 lb. Kit
2 lb. Kit16 lb. Kit76 lb. Kit
2 lb. Kit16 lb. Kit
2 lb. Kit16 lb. Kit
1 Pint 16 oz. Kit1 Quart 32 oz. Kit1 Gallon 8 lb. Kit
1 Quart 32 oz. Kit1 Gallon 8 lb. Kit2 Gallon 16 lb. Kit
1:11:11:11:1
1:11:11:1
1:11:1
1:11:1
1:11:11:1
1:11:11:1
Epoxy Products - Potting Compounds
Epoxy Products - Industrial Dynamic Balancing CompoundProduct Name Part No. Unit Size Mix Ratio Description
Product Name Part No. Unit Size Mix Ratio Description
Industrial Adhesive Products
EPO Gel HT
PLA 5
PLA 10
PLA 60
PLA 100
EGHTQTETHTGLEGHT10GL
PLA550PLA5400
PLA1050PLA10400
PLA6050PLA60400
PLA10050PLA100400
1 Quart Kit 1 Gallon Kit10 Gallon Kit
50 ml cartridge400 ml cartridge
50 ml cartridge400 ml cartridge
50 ml cartrdige400 ml cartridge
50 ml cartridge400 ml cartridge
Highly thixatropic epoxy gel adhesive
Permanent Liquid Adhesive, 5 Minute Cure time
Permanent Liquid Adhesive, 10 Minute Cure time
Permanent Liquid Adhesive, 60 Minute Cure time
Permanent Liquid Adhesive, 100 Minute Cure time
Z-TEC 751Z-TEC 752Z-TEC 753
Steel-Tec 801
AS-PCL
ZT751ZT752ZT753
ST801
ASPCL-34
2 lbs. Kit2 lbs. Kit2 lbs. Kit
2 lbs. Kit
34 lbs. Kit
Ceramic-filled epoxy repair putty.Ceramic-filled epoxy repair base coat.Ceramic-filled epoxy repair top coat.
Steel-filled epoxy repair putty
Epoxy based ceramic wear compound
1:11:11:1
1:11:1
1:11:1
1:11:1
1:11:1
1:11:11:1
1:1
1:1
Product Name Part No. Unit Size Ratio Description
Wear and Abrasion Products
Marine Products
Laminating Resin
GP Resin
LAM/GP Hardener(10, 30, 60, or 120)
Teak Adhesive
EPO Coat CT 100
1 Quart Can1 Gallon Can5 Gallon Pail
1 Quart Can1 Gallon Can5 Gallon Pail
1 Quart Can1 Gallon Can5 Gallon Pail
2 Gallon10 Gallon
2 Pint2 Quart2 Gallon
Low-viscosity Epoxy laminating resin
Medium viscosity general purpose epoxy resin
Hardener for Lam and GP Resins. 10, 30, 60, & 120 min. po life available
Epoxy adhesive for adhering teak to surfaces
Coal-tar epoxy coating
LA 32LA 128LA 640
GP 32GP 128GP 649
LAM 32LAM 128LAM 640
TA 256TA 1280
EPO 10031EPO 10064EPO 100256
2:12:12:1
2:12:12:1
2:12:12:1
1:11:1
1:11:11:1
Product Name Part No. Unit Size Mix Ratio Description
Product Name Part No. Unit Size Mix Ratio Description
Product Name Part No. Unit Size Mix Ratio Description
415 E. Venice Avenue
Venice, FL 34285
www.dcdynamis.com
(800) 828 8929 Tel
(941) 488 0747 Fax
9/2013