Research Doctorate School in Biological and Molecular Sciences
Ph D. in BIOMATERIALS – XXV Cycle (2010-2012)
“Assessment of Biodegradation in Different
Environmental Compartments of Blends and
Composites Based on Microbial
Poly(hydroxyalkanoate)s”
Hayan Chen
Supervisor: Prof. Emo Chiellini Co.Supervisor: Dr. Brunello Ceccanti*
Tutors: Dr. Lucia Pérez Amaro, Dr. Arianna Barghini, Dr. Andrea Corti
Dr. Serena Doni*, Dr. Grazia Masciandaro*
Laboratory of Bioactive Polymeric Materials for Biomedical and Environmental
Applications (BIOlab) – Department of Chemistry and Industrial Chemistry
(University of Pisa)
*National Research Council (CNR)-Institute of Ecosystem Study (ISE)
Index
INDEX ACKNOWLEDGMENTS ...................................................................................................... 1
ABSTRACT ............................................................................................................................ 3
1. INTRODUCTION .............................................................................................................. 4
1.1. Global And European Production/Consumption of Plastic And Polymers
Materials ................................................................................................................... 4
1.2. The Advantages And Disadvantages of Conventional Packaging Materials ......... 6
1.3. The Probably Solutions Based on the Available Investigations .............................. 7
1.3.1 Waste Materials Disposal and Potential Risks ................................................... 10
1.4 Development of Polymeric Materials from Renewable and Fossil Fuel Resources,
Biopolymers and Relevant Plastic Items. ............................................................. 11
1.4.1. Poly (hydroxyalkanoates) (PHAs) ..................................................................... 12
1.4.2. Poly (lactic acid) (PLA) .................................................................................... 15
1.5. Different Media as Tool Boxes for Biodegradation of Plastic .............................. 16
1.5.1. PHAs Biodegradation in Soil ........................................................................... 17
1.5.2. PHAs Biodegradation in Mature Compost ........................................................ 21
1.5.3. PHAs Biodegradation in Aqueous Medium ....................................................... 23
1.5.4. Microbial Biodegradation Mechanism (intra and extra-cellular) ..................... 27
1.5.5. PHAs Biodegradation Provided by Enzymes .................................................... 29
1.5.6. PLA Biodegradation Mechanism in Compost ................................................... 31
1.5.7. The Role of the Organic Filler on the Biodegradation Behavior and Final
Properties of PHAs Composites. ...................................................................... 34
1.5.7.1. PHAs-Cellulose Derivatives Blends and Composites ...................................... 35
1.5.7.2. PHA-Natural Fiber Composites ....................................................................... 36
1.5.7.3. PHAs Lignin Blends and Composites .............................................................. 40
1.5.8 The Role of the Organic Filler on the Biodegradation Behavior and Final
Properties of Petro-based Polymers Composites (PE, PP, PS) ........................ 41
1.5.9. The Role of the Inorganic Filler on the Biodegradation Behavior and Final
Properties of PHAs .......................................................................................... 45
1.5.10. The Role of the Inorganic Filler on the Biodegradation Behavior and Final
Properties of Petro-based Polymers (PE, PP, PS) ........................................... 50
1.6 Biodegradation of Fossil Fuel Based Polymers (ECOFLEX, PE and PS) in Soil-
Plant Systems (Avena sativa –Raphanus sativus) ................................................ 53
1.6.1. Biodegradation of plastics in soil ...................................................................... 55
1.6.2. Polyethylene ...................................................................................................... 56
1.6.3. Polystyrene ........................................................................................................ 58
1.6.4. Aliphatic–aromatic (AAC) copolyesters ............................................................ 58
1.7 Polyvinylics Biodegradation ..................................................................................... 59
1.7.1 The Role of Plastics in Agriculture ..................................................................... 60
1.7.2 Biodegradation of pro-oxidant-free polyethylene by natural occurring
microorganisms ................................................................................................ 63
1.7.3 Preliminary data or studies ................................................................................ 65
Chen Haiyan PhD Thesis
2. OBJECTIVES .................................................................................................................. 73
3. EXPERIMENTAL PART ............................................................................................... 75
3.1. Materials .................................................................................................................. 75
3.1.1. Reagents and Solvents ...................................................................................... 75
3.1.2. Joncryl ADR-4368-CS ...................................................................................... 75
3.1.3. Hazelnut Shells ................................................................................................. 76
3.1.3.1. Lignin Functionalization ................................................................................. 77
3.1.4. Organophilic Clay (Dellite 72T) ...................................................................... 77
3.1.5. Perkalite F100 .................................................................................................. 78
3.1.6. Poly(3 hydroxy-co-3 valerate) (PHBV) ............................................................ 78
3.1.7. Poly(lactic acid) (PLA) ..................................................................................... 81
3.1.8. Poly(butylene adipate-co-terephthalate) (Ecoflex)........................................... 82
3.1.9. Ecovio ............................................................................................................... 83
3.2. Preparation of the Sample ...................................................................................... 84
3.2.1. Pre-blend .......................................................................................................... 84
3.2.2. Melt blending .................................................................................................... 84
3.2.3. Press ................................................................................................................. 85
3.3 Characterization of the Samples ............................................................................. 86
3.3.1. Thermogravimetric Analysis (TGA) ................................................................. 86
3.3.2. Differential Scanning Calorimetry (DSC) ........................................................ 86
3.3.3. Transmision Fourier Transform Infrared Spectroscopy (FTIR) ....................... 86
3.3.4. Nuclear Magnetic Resonance (1H-NMR) ......................................................... 86
3.3.5. Gel Permeation Chromatography (GPC) ......................................................... 86
3.3.6. Determination of Total Organic Carbon (TOC) and Total Nitrogen (TN) ....... 87
3.3.7. PH and Electrical Conductivity ........................................................................ 87
3.4. Experimental Setup for Biodegradation Experiments ......................................... 87
3.4.1. Soil Burial Biodegradation Tests...................................................................... 87
3.4.2. Mature Compost Respirometric tests ................................................................ 91
3.4.3. River Water respirometric Test ........................................................................ 93
3.4.4. Carbon Dioxide Determination and Evaluation of the Degree of
Biodegradation in Respirometric Tests ........................................................... 94
3.5. Specific Biotests to Assess Eco-toxicity of Biodegradable Polymer Materials
Ecoflex, PE, PS in Soil-Plant systems .................................................................. 95
3.5.1 Materials ........................................................................................................... 95
3.5.1.1. Soil and Plants used in the experiments .......................................................... 95
3.5.1.2. Testing materials ............................................................................................. 96
3.5.2. Experimental Setup ........................................................................................... 97
3.5.2.1. Degradation in a soil-plant system .................................................................. 97
3.5.2.2. Biodegradation of PHB in soil ........................................................................ 97
3.5.3. Methods ............................................................................................................ 97
3.5.3.1. Chemical Parameters (pH, electrical conductivity, total organic carbon, total
nitrogen, water soluble carbon, nitrate, ammonia, total and available
elements) ....................................................................................................... 97
3.5.3.2. Biochemical Parameters ................................................................................. 98
Index
3.5.3.3. Biological parameters ...................................................................................... 99
3.5.3.4. Germination and Growth Test ......................................................................... 99
3.5.4. Statistical Analisys ............................................................................................ 99
4. RESULTS AND DISCUSSION ..................................................................................... 101
4.1. Differential Scanning Calorimetry (DSC) ............................................................ 101
4.1.1. PHBV Based Blends and Composites.............................................................. 101
4.1.2. PLA Based Blends & Composites ................................................................... 106
4.2 ThermoGravimetric Analysis (TGA) .................................................................... 110
4.2.1. PHBV Based Blends & Composites ................................................................ 110
4.2.2. PLA Based Blends & Composites ................................................................... 114
4.3. Molecular Weight by Gel Permeation Cromatography (GPC) Analysis .......... 118
4.4 PHAs Based Composites Processing Characteristic ............................................ 119
4.5. PHBV Based Blends and Composites Structural Characteristic by Infrared
Spectroscopy (IR) ................................................................................................. 127
4.6. Biodegradation Experiments ................................................................................. 129
4.6.1 PHBV Based Blends and Composites in Soil Medium ..................................... 130
4.6.2. PHAs Based Blends and Composites Biodegradation in Mature Compost ..... 132
4.6.3. PLA Based Blends and Composites Biodegradation in Mature Compost ....... 133
4.6.4 Qualitative Compost Experiment ..................................................................... 134
4 .6.5. River Water Respirometric Test ..................................................................... 136
4.7. Biodegradation of Fossil Fuel Based Polymers (ECOFLEX, PE and PS) in Soil-
Plant Systems (Avena sativa –Raphanus sativus) ................................................ 138
4.7.1. Potential Eco-toxicological Effects of Polymer Materials .............................. 138
4.7.2. Soil biochemical parameters .......................................................................... 139
4.7.3. Chemical parameters of soil samples treated with different polymers ............ 142
4.7.4. Statistics analyzes about Biplot PC1 versus PC2 ............................................ 144
4.8. PHB biodegradation in soil ................................................................................... 149
5. CONCLUSIONS ............................................................................................................. 151
REFERENCES ................................................................................................................... 154
Acknowledgment
- 1 -
ACKNOWLEDGMENTS
It is pleasure to thank everybody who made this thesis possible including my supervisory
team, my family. I am very thankful to financial support by Research Doctorate School in
Biological and molecular Sciences, Laboratory of Bioactive Polymeric Materials for
Biomedical and Environmental Applications (Biolab), Department of Chemistry, University
of Pisa, Italy (UNIPI) and the National Research Council (CNR)-Institute of Ecosystem
Study (ISE). Part of this work was performed within framework of EC-funded project:
Animpol CT: GA-245084, the financial support is greatly acknowledged.
First of all, I would like to express my deepest sense of gratitude to my principal supervisor,
Prof. Emo Chiellini, who gave me the opportunity to achieve this important objective, his
able guidance and constructive critism helped me to progress in research pursuit, I am
thankful for his constant encouragement and valuable contribution of his time throughout the
course of my thesis; and sincere thanks to my secondary supervisor, Prof. Brunello Ceccanti,
who trust me and quickly discovered my potential and interest in the research area, it‘s been
a great honor for me to work under his inspiring guidance; my gratitude goes to Prof. Yao
Jun, my previous supervisor during my master degree, for her constant encouragement and
guidance.
My sincere thanks to my tutor Dr. Andrea Corti, who is sharing his academic experience for
the successful completion of the objective undertaken. His valuable suggestions and timely
discussions enabled me to achive this work with precision. Secondly, I would like to express
my heartfelt gratitude to Dr. Serena Doni, Dr. Lucía Pérez Amaro and Dr. Arianna Barghini,
who led me into the world of scientific methodology, the standard training of chemical,
engineering, biological experimental epistemology and technical ability, they has walked me
through all the stages of the writing of this thesis. Without their consistent and illuminating
instruction, this thesis could not have reached its present form.
I also very thank the reading committee members who kindly agreed to read my manuscript
and participate in this discussion. And many thankful to Prof. Mingreng Wang, professorate
senior engineer, China GuoDian(Group)Corporation, for his suggestions and discussions
during the part of my research work.
I am very much thankful to Dr. Federica Chiellini, Dr. Andrea Morelli, Dr. Vassilka IIieva, Dr.
Stefania Cometa, and Dr. Marcella Ferri during laboratory work.
My special thanks to Maria Caccamo, Maria Viola, and Elisa Romano. Persons that help me
in all situations!
I would like to thank several people from the BIOLAB for all the time we spent together in
these years, for share the good times and for the help that they gave me in the mo ments I
needed. Great colleagues like, Anna Maria Piras, Antonella Lisella, Alberto Dessy,
Alessandro Pirosa, Carlos Mota, Cesare Errico, Chiara Migone, Cristina Bartoli, Chongbo
Chen, Dino Dinucci, Dario Puppi, Dash Mamoni, Giulia Ciampi, Francesca Scalesse,
Muniyasamy Sudhakar, Matteo Gazzarri, Mohamed Abdelwahab, Stefania Sandreschi, Silvia
Volpi, Kaili Yang, Xuanmiao Zhang and all the others that are too long to list.
I also would like to thank several people from the ISE-CNR for all the time we spent
together in these years, for share the good times and for the help that they gave me in the
Chen Haiyan PhD Thesis
- 2 -
moments I needed. Great colleagues like, Cristina Macci, Eleonora Peruzzi, Grazia
Masciandaro, Giulia Bondi, Mariarita Arenella, and all the others people helped me during
three years.
Finally, my thanks greatly indebted go to my beloved family for their loving considerations
and great confidence in me all through these years, they always encouraged me in all
moments providing emotional support and love for my carrier. I also owe my sincere
gratitude to my good friends and my officemates, fellow classmates who gave me their help
and time in listening to me and helping me work out my problems during the difficult course
of the thesis.
Introduction
- 3 -
ABSTRACT
The packaging industry nowadays relies strongly on the use of petroleum-derived plastic
materials, which raises some concerns from both economical and environmental perspectives.
The continuing use of finite oil resources implies a likely eventual decrease in availability
and thereby increasing costs of raw materials. Furthermore, being non readily biodegradable,
petroleum-based products can pose significant waste disposal problem in some area.
Packaging is a substantial part of our everyday life, and the consumer use of packaging
materials has shown a continuous increase over time. Packaging products manufactured from
renewable materials currently only represent about 2% of the market, except the traditional
fiber-based packaging.
The research work of my doctoral thesis, performed in the BIOLAB (Laboratory of
Bioactive Polymeric Materials for Biomedical & Environmental Applications, Department of
Chemistry and Industrial Chemistry, University of Pisa) facilities deals with the assessment
of the biodegradation propensity in different media (soil, compost, river water) of synthetic
polyesters (Ecoflex and Ecovio) and bio-based polymers such as poly(hydroxybutyrate-co-
hydroxyvalerate) (PHBV), poly(lactic acid) (PLA) and their blends and composites loaded
with fillers of organic (lignin), inorganic (montmorillonite named Dellite) nature and chain
extenders (Joncryl).
The composites obtained by melt-blending and the neat polymers have been analyzed also
for their processing profile and thermal properties (TGA, DSC) with the aim to know the
effect of each component on the overall composite biodegradation behavior.
The experiments performed at the CNR-ISE (National Research Council-Institute of
Ecosystem Study) have been essentially two topics.
In the first investigation, the potential eco-toxicological effects of polymer materials such as
Polyethylene (PE) and Polystyrene (PS) in soil-plant systems (Avena sativa and Raphanus
sativus) were studied; the PE and PS polymer effects were compared with those of the
biodegradable materials Ecoflex and Cellulose, used as positive controls. Several chemical
and biochemical parameters, usually used to assess soil quality and its response to xenobiotic
compounds, have been selected in order to follow the effect of biopolymer degradation on
soil properties. Polymers seemed to stimulate the soil metabolic activity during the time, thus
indicating their possible biodegradation propensity in soil. These effects were more evident
in Raphanus sativus plant treatments than in Avena sativa, suggesting the higher sensitivity
of the former to the polymer treatments. At the end of experimentation, Ecoflex compared to
PE and PS showed the higher nitrate/ammonia ratio and the lower water soluble carbon
content (WSC), thus indicating its higher ability to promote the carbon cycle and in turn to
activate organic nitrogen metabolism, bringing the soil plant system towards the nitrate
nutrient production.
In the second experiment, the biodegradation of the PHB polymer, added to the soil at two
different concentrations (1% and 2%) was investigated. The biodegradation process was
followed by monitoring specific microorganisms and enzyme activities involved in PHB
metabolism. Total microbial cultivable population and Pseudomonas genus significantly
increased in both PHB dose treatments with respect to the untreated soil. The stimulation of
microbial growth and activity was confirmed by the activation of the arylesterase and PHB
depolymerase activities.
Chen Haiyan PhD Thesis
- 4 -
1. INTRODUCTION
1.1. Global and European Production/Consumption of Plastic and Polymers Materials
Synthetic and bio-based plastics technology was developed not only as expected to continue
its unique properties for more and more innovative applications, The recalcitrance of some
plastic items to biodegradation has led to an increase public concern about the hazards
associated with plastic residues in the environment has triggered activities by scientific,
industrial, and regulatory bodies to assess the exposure and effects of these macromolecular
compounds in different environmental compartments during past decades
(www.plasticeurope.com). The synthetic plastics are definitely important in modern daily life
and have brought many societal benefits. They show some advantages such as low price,
easy disposal, physical, chemical and thermo-mechanical properties thermo property,
physical and chemical stability, that make them very convenient materials for industrial
process and consumption. A wide variety of synthetic polymers are produced worldwide to
the extent of approximately 300 million tons per year and remarkable amounts of these
polymers are introduced in the ecological system as industrial waste products (Shah et al.
2008).
Global plastics production increased by 10 million tonnes (3.7%) to around 280 million
tonnes in 2011 (Fig.1.1), continuing the growth pattern that the industry has enjoyed since
1950 approximately by 9% per annum (www.plasticeurope.com).
Figure 1.1. Global Plastic Production Until 2011.
Figure 1.2 reports the European plastic demand by resin type, whereas Figure 1.3 shows the
demand segmentation by sector for the year 2011.
Introduction
- 5 -
Figure 1.2. European Plastic Demand by Resin Type 2011 (Year 2011).
Figure 1.3. European Plastic Demand by Sector (Year 2011).
The biobased world production raises 1161 k-tons in the year 2011 as observed from Figures
1.4 and 1.5. The last one reports the capacity for the biodegradable biobased materials and
the non-biodegradable ones in 2011 (European Bioplastics Bulletin, Issue 05/2012).
Chen Haiyan PhD Thesis
- 6 -
Figure 1.4. Biobased Plastics World Production.
(a) (b)
Figure 1.5. Bioplastics Production Capacity or Biobased Biodegradable Materials (a) and
Biobased non Biodegradable Ones (b).
1.2. The Advantages and Disadvantages of Conventional Packaging Materials
Polyolefins are widely used, and it was reported that they accumulate in the environment at a
rate of 25 million tons per year (Orhan et al. 2000, Eubeler et al. 2010). The thermoplastic
such as polyethylene (PE) and polystyrene (PS) have a broad scale of applications in the past
few years. Whist polyethylene is available in many varieties (liner low density, high density,
high molecular weight, etc.), the low-density polyethylene (LDPE) is used extensively in
rigid packaging industry because of several favorable physical properties, for instance its low
vicat softening point aids in low temperature forming and heat sealing, which makes it very
favorable in the form-fill and seal-packaging industry (Paabo et al. 1987, Dilara et al. 2000),
and it attributes the form-fill and seal package industry to optimize equipment cycle-times.
Low density polyethylene (LDPE) shows general properties such as low cost, chemical
resistance, food grades available, good moisture barrier properties that make it one of most
life-partner materials in our daily life. In fact, LDPE is often used in conjunction with
another polymer like polystyrene (PS), for the improvement of the moisture barrier
transmission properties. The faeatures (optical clarity and thermal stability, easy processing
Introduction
- 7 -
conditions, good property retention and creep resistance, toughness) similar to polyethylene,
make it suitable mainly for packaging applications (Lim et al. 1999, Arkedi et al. 2007).
The literature research considers also other application field such as the production and use
of the agricultural plastic films (Mulching by putting a thin plastic film directly over the soil
surface) as a standard technique (green house) for vegetable.
The advantages and purposes by using these films are (1) the control and/or the increase of
the soil temperature, (2) the maintaining of soil humidity, (3) the reduction of germination
time, providing early or out of season crop production for better market value products, (4)
the reduction for weeds and plant diseases, guarantying the efficiency in the usage of water
and fertilizers with the aim to improve the quality of horticultural products (Lamont 1999,
Sedlacek et al .2011, Espì et al. 2006, Kijchavengkul, et al. 2008)
On the other hand, the dramatic increase in production and lack of biodegradability of
commercial polymers, particularly commodity plastics used in packaging, industry and
agriculture, focused public attention on a potentially huge environmental accumulation and
pollution problem that could persist for centuries. About 40% of such production is discarded
into landfills (Shah et al. 2008). The plastic waste is disposed off through landfilling,
incineration and recycling. Because of their persistence in our environment, several
communities are now more sensitive to the impact of discarded plastic on the environment
(Shah et al. 2008, Albertsson et al. 1987). Despite all advantages of these conventional
polymers, there are several major concerns about using films which are the costs of removal
and disposal of the used plastics and environmental issues..
1.3. The Probably Solutions Based on the Available Investigations
The American Society for Testing and Materials (ASTM) and the International Organization
for Standardization (ISO) give some definitions: a) degradation as ―An irreversible process
leading to a significant change for the material structure, typically characterized by a loss of
properties (e.g. integrity, molecular weight, structure and mechanical strength) and/or
fragmentation (Figure 1.6) (Chiellini 2007). Degradation is affected by environmental
conditions and proceeds over a period of time comprising one or more steps‖ (ISO-472,
ASTM 883-1991, ASTM D6400-04).
Figure 1.6 Polymeric Materials and Plastics Nomenclature
Chen Haiyan PhD Thesis
- 8 -
Biodegradable plastic is ―A degradable plastic in which the degradation results from the
action occurring by microorganisms such as bacteria, fungi and algae‖. Two main types of
commercially viable biodegradable plastics have been developed:
1) Oxo-biodegradable polymers and hence relevant plastic items, for which degradation is
the result of oxidative and cell mediated phenomena, either simultaneously or step by step;
2) Hydro-biodegradable polymers and hence relevant plastic items, for which degradation is
the result of hydrolytic and cell-mediated phenomena, either simultaneously or step by step.
For both types of biodegradable polymers, the molar mass reduction in the environment,
follows two sequential steps, where the first one is basically an abiotic degradation (Figure
1.7) whereas the second one represents a bioassimilation of the molecular fragments that are
generated in the first stage (Scott 1999). Abiotic mechanisms are generally regarded as too
slow by themselves to be adequate in a variety of disposal environments.
Figure 1.7. General Features of Environmentally Degradable Polymeric Materials.
There are several applications in which really quite rapid degradation of plastics after use is
required. For example, there is a lot of plastics disposable by chemical, physical or biological
treatments in liquid or sewage sludge system. The non-toxic products can be reused or
recycled in the environment as fertilizer, in which situation they lose their integrity
relatively, in order to avoid plugging pumps, filters and so on. Hydrolytically unstable
biodegradable plastics can provide an answer here. In many other uses (e.g., food
packaging), one of the disadvantages is hydrolytic instability. However, overall stability is
required during shelf storage and use, even though this method should follow relatively rapid
abiotic degradation within a specific time, which probably is depending on the disposal
environment. In order to avoid the accumulation of plastic fragments in virtually all disposal
environments, it requires that these be consumed through biodegradation by microorganisms.
Introduction
- 9 -
Effective biodegradation of such residues can be achieved when originally hydrophobic
plastics become wettable (hydrophilic) and characterized by a relatively low molecular
weight so that there is a significant number of molecular ends accessible at the surface. The
science and technology of the development of oxo-biodegradable plastics can meet these
criteria (Muniyasamy 2011).
The mechanisms of oxidative degradation of polymers, have been extensively studied and
reviewed (Chiellini et al. 2003, Scott 1965). It is generally accepted that the key
intermediates are hydro-peroxides, which decompose under the influence of heat, light or
transition metal catalysis, producing free radicals. They enter a chain reaction with oxygen
and C-H bonds (hydrocarbonyl) in the polymer, to produce a range of oxidation products.
This can be expressed as the interlocking cycle of reactions depicted in Figure 1.8.
Figure 1.8. Biodegradation Routes for Oxo- and Hydro-Biodegradable Polymers.
According to the earlier research, a number of polymeric materials has been developed with
varying degrees of success (Rutiaga et al .2005, Mecking 2004, Chandra et al. 1998).
The biodegradable mulching films represents a really promising alternative to the common
plastic films (mostly polyethylene and polystyrene) for enhancing sustainable and
environmentally friendly agricultural activities. These biodegradable mulching films can be
incorporated into the soil at the end of the crop season and undergo biodegradation by soil
microorganisms. The possible biodegradation of the plastic mulches can abate several major
concerns about their wide usages: (1) costs of removal and disposal (2) environmental issues
(3) possible toxic effects on plant germination and growth. Only extensive analysis over the
entire life cycle of a particular polymer application can assess eventual risks for the
environment and plant health and, a selection of safer raw material can be made.
Additionally, some additives such as pro-oxidants and starch have been applied in science
materials, with the aim to improve the biodegradation propensity of the materials.
Chen Haiyan PhD Thesis
- 10 -
Recent researches have showed that thermoplastics derived from polyolefins, traditionally
considered resistant to biodegradation in the environment, can biodegrade following a photo-
degradation or a chemical degradation mechanism (Zheng et al. 2005). Thermoset plastics,
such as aliphatic polyesters and polyurethanes, can be attacked by microorganisms that break
down the hydrolytic bonds contained in the esters or urethanes chemical structure.
Aliphatic-co-aromatic polyesters, such as Ecoflex and Ecovio, have e commercial
applications because they show good mechanical properties and biodegradation propensity.
(Yamamoto et al. 2002, Muller et al. 2001).
Ecoflex has been reported to biodegrade easily under compost conditions (Yamamoto et al.
2005). At high temperature, the material reached a complete degradation in 22 days of
incubation without showing any adverse eco-toxicological effects on the environment (Witt
et al. 2001). This lack of toxicity represents an evidence that Ecoflex could be an excellent
material for the production of short-life products such as protective packaging and films for
agricultural applications. The analyses were carried out under thermophilic conditions to
reproduce those in municipal or industrial composting facilities. The biodegradation
experiments were also performed under moderate environmental soil conditions with 29
strains of enzyme-producing soil bacteria, fungi and yeasts. A screening procedure was
developed and the results showed that, after 21 days of exposure, the polymer could be
degraded by some of the microorganisms (MOs) (Eubeler et al. 2010).
Degradation of poly [(1, 4-butylene terephthalate)-co-(1, 4-butylene adipate)] (Ecoflex,
BTA) monofilaments (rods) in standardized sandy soil was investigated (Rychter et al.
2010). Changes in the microstructure and chemical composition distribution of the degraded
BTA samples were evaluated and changes in the pH and salinity of post-degradation soil, as
well as the soil phytotoxicity impact of the degradation products, are reported.
A macroscopic and microscopic evaluation of BTA surface of some rod samples after
specified periods of incubation in standardized soil, indicated that its erosion starts from the
fourth month of their incubation, with almost total disintegration of the incubated BTA
material observed after 22 months. However, the weight loss after this period of time was
about 50% and only a minor change in the Mw of the investigated BTA samples was
observed, along with a slight increase in the dispersity (from an initial 2.75 up to 4.00 after
22 months of sample incubation). The multidetector SEC and ESI-MS analysis indicated
retention of aromatic chain fragments in the low molar mass fraction of the incubated
sample. Phytotoxicity studies revealed no visible damage, such as necrosis and chlorosis, or
other inhibitory effects, in the following plants: radish, cress, and monocotyledonous oat,
indicating that the degradation products of the investigated BTA copolyester are harmless to
the tested plants (Rychter et al. 2010).
1.3.1 Waste Materials Disposal and Potential Risks
Many of the wastes produced today remain in the environment for hundreds years so the
creation of non-decaying waste materials, combined with a growing consumer population,
could produce a waste disposal crisis. One solution to solve this crisis is constituted by the
solid waste management (Arnio et al. 2008) that provides some rules with the aim to recycle
waste into useful products.
For this purpose, different waste management techniques such as material recovery facilities,
landfilling, a source separation system able to distinguish the recyclable materials, a system
Introduction
- 11 -
suitable for the recovery of the organic fraction, an incineration process and a composting
facility were investigated only on an environmental point of view with the aim to obatain
decision-making tools that consider the economic and social effects of solid waste
management (Banar et al. 2009, Huang 1995).
A large range of materials such as metal, glass, wood, paper or pulp-based materials, plastics
or combination of more than one materials as composites are used for packaging
applications. Among other materials, a huge range of oil-based polymers is also currently in
use. They are largely non-biodegradable so it is difficult to recycle or to reuse them due to
the levels of contamination (Davis et al. 2006).
Implementation of more fundamental regulatory testing procedures which reflect the
behavior of materials in end use applications, is recommended to allow better control over
environmental impact in the wide variety of utilization and disposal practices (Van der Sloot
1990).
Another option adopted to reduce the waste disposal is the development and production of
biodegradable materials with similar functionality to that of the oil-based synthetic polymers.
It is anticipated that, as the materials are from renewable resources and biodegradable, they
would contribute to sustainable development and if properly managed would reduce their
environmental impact upon disposal methods (Davis et al. 2006, Van der Sloot 1990,
Consonni et al. 2011, Dias et al. 2007).
The goal of this sustainable growth should be a reaching of a maximum level for the
efficiency of energy utilization in every step of the system, from the production of the goods
to the disposal of the wastes. Many highway agencies, private organizations, and individuals
have completed or are in the process of completing a wide variety of studies and research
projects concerning feasibility, environmental suitability, and performance in using recycled
products in highway construction. (Subramanian 2000). These studies try to meet society's
need for safe and economical disposal of waste materials with the highway industry's need
for better and more cost-effective construction materials.
Bio-based packaging material is defined as a packaging containing raw materials derived
from agricultural sources such as starch and/or man-made monomers. These materials are not
necessarily biodegradable (Petersen et al. 1999, Goddard 1995). Some articles and current
researchers are focused on those waste materials that become promising as substitutes for
conventional materials (Petersen et al. 1999, Goddard 1995).
Environmental issues are becoming increasingly important to the European consumer.
Consequently, consumer pressure may attract the attention of research and usage on bio-
based packaging materials as an alternative to materials produced from resources that don‘t
have renewable ability (Goddard 1995).
1.4 Development of Polymeric Materials from Renewable and Fossil Fuel Resources,
Biopolymers and Relevant Plastic Items.
Natural polymers and most synthetic macromolecules cannot be assimilated by
microorganisms. Although polymers represent slightly over 10% of total municipal waste,
the problem of non-biodegradability is highlighted by overflowing landfills, polluted marine
waters, and unsightly litter so the existing government regulations in Europe and anticipated
Chen Haiyan PhD Thesis
- 12 -
regulations in the United States will greatly limit the use of these materials in large volume
applications (packaging, water treatment, paper and textile sizing, etc.) unless acceptable
means of waste management are available.
Total management of polymer wastes requires complementary combinations of
biodegradation, incineration, and recycling. Biodegradation is the most desirable long-term
future solution and requires intensive research and development before it becomes practical.
On the other hand, incineration and recycling can become operational in a relatively short
time for the improvement of the situation at present and in the near future (Hoang et al.,
1995). Waste disposal is an increasing problem as available landfill areas diminish. Plastics
currently account for about 7% by weight (18% by volume) of municipal solid waste, with
half of this plastic waste derived from plastics used in packaging. Growing environmental
concern has created an urgent need to develop new biodegradable materials that have
properties comparable with conventional polymeric materials such as polyethylene and
polypropylene. To reduce the environmental impact of synthetic plastics, some industries
have started to produce biodegradable plastics (Rosa et al. 2003).
Suitable alternative methods such as biodegradable sodium alginate-based spray mulch,
biobased polymers films, are used in agriculture (De Prisco et al. 2002, Immirzi et al. 2009,
Malinconico et al. 2002, Dincheva et al. 2007). At the end of their life, biodegradable
materials can be integrated directly into the soil where bacterial floras transform them into
carbon dioxide or methane, water, and biomass. So they could represent a sustainable
ecological alternative to LDPE films (Immirzi et al. 2009). Among the wide range of
biopolymers available, polysaccharides are very interesting materials for film applications
because they are widely available and are renewable (Malinconico et al. 2002, Avella et al.
2007).
The innovative approach consisted of forming the mulch coating directly in field by covering
the soil with a thin protective geo-membrane obtained by spraying water-based solutions of a
natural polysaccharide, such as sodium alginate (NaAlg), glucomannan, chitosan and
cellulose.
Barrier coatings were obtained when the water content of polymeric network was removed
through evaporation. The spray technology used was similar to that used to apply fertilizers,
pesticides, hormones and other useful plant health products.
Nowadays, the adoption of a new material becomes a need for the manufacturing industry
that has to well know its behavior under various processing, manufacturing and usage
conditions (Sen et al. 2009). Various blends of conventional and biodegradable plastics have
been studied (Guo et al. 1999). Polymeric blends consist of a mixture of two or more
polymers or copolymers and they are a good alternative for reducing the final product cost.
Natural additives such as starch, cellulose, lignin, and other polysaccharides have been used
in these formulations (Tseng et al., 2007).
1.4.1. Poly (hydroxyalkanoates) (PHAs)
Poly(hydroxyalkanoate)s (PHAs) are a class of biopolyesters mainly produced by microbial
fermentation of renewable fossil fuel feedstocks or combination of both types of sources
(Reddy et al. 2003).
Introduction
- 13 -
The PHAs accumulate as granules within the cytoplasm of cells and serve as a microbial
energy reserve material (ota, 1993).
PHAs have a semicrystalline structure, the crystallinity degree ranging from about 40% to
around 80% (Abe & Doi, 1999).
PHAs have a generic formula where x is 1 and R can be an alkyl chain (C1-C15) (Fig. 1 &
Tab. 1.1).
H COO (CH2)x OH
n
CH
R
Figure 1.9 Generic formula structure of PHAs
The main members of the PHA family are:
poly(3-hydroxybutyrate), P(3HB), [R= CH3]
poly(3-hydroxyvalerate), P(3HV), [R= ethyl]
poly(3-hydroxyhexanoate), P(3HHx), [R= propyl]
poly (3-hydroxyoctanoate), P(3HO), [R= pentyl]
poly(3-hydroxydecanoate), P(3HD), [R= heptyl]
the medium-chain-length poly(3Hpd), [R= pentadecyl].
PHAs copolymers vary in the type and proportion of monomers, and they are typically
random in sequence. All the reported monomers and relevant monomeric units are
characterized by the presence of an asymmetric carbon atom characterized by (s)
configuration (Chen et al. 2001).
Table 1.1 shows some PHA molecular structures.
Table 1.1. Structures of Polyhydroxyalkanoates (PHAs).
PHA short name PHA full name χ R
PHB P(3HB) 1 -CH3
PHV P(3HV) 1 -CH2CH3
PHBV P(3HB-co-3HV) 1 -CH3 and -CH2CH3
PHBHx P(3HB-co-3HHx) 1 -CH3 and –CH2CH2CH3
PHBO P(3HB-co-3HO) 1 -CH3 and –(CH2)4CH3
PHBD P(3HB-co-3HD) 1 -CH3 and –C6H8CH3
PHBO P(3HB-co-3HOd) 1 -CH3 and –(CH2)14CH3
P(HB4HB) P(3HB-co-4HB) 2 -CH3 and –H
P(HB4HV) P(3HB-co-4HV) 2 -CH3 and –CH3
The range of PHA structural architectures that is now accessible has opened up a wide range
of possibility, encompassing rigid thermoplastics, thermoplastic elastomers, as well as
suitable grades for waxes, adhesives, and binders (Metabolix, 2007a, Ishida et al. 2005).
Feedstocks currently being utilized for PHA production are high value substrates such as
sucrose, vegetable oils and fatty acids (Li et al. 2007, Suriyamongkol et al. 2007). In theory,
Chen Haiyan PhD Thesis
- 14 -
any carbon source can be utilized, including lignocellulosics from agricultural by-products
while in practice, as for PLA and the other polyesters already discussed, further
improvements in fermentation yields by metabolic engineering of microorganisms, together
with technological advances in feedstock pre-treatment, such as new enzymatic processes,
are prerequisites for a shift to lower-value feedstocks.
PHAs have mechanical properties such as Young modulus and tensile strength resembling
those of thermoplastics like polyethylene and polypropylene (Matsusaki et al. 2000),
moreover, PHA is also biodegradable and bio-compatible.
Industrial production of poly-3-hydroxybutyrate (PHB) (Patnaik 2006), poly(3-
hydroxybutyrate-3-hydrox-yvalerate) (PHBV) (Jung et al. 2000) and poly(3-
hydroxybutyrate-3-hydroxy-hexanoate) (PHBHHx) (Chen et al. 2001) has been reported. By
careful control of the process they are encouraged to accumulate large quantities of PHB as
discrete intercellular granules. The transmission electron micrograph in Figure 1.9 shows a
thin section through a bacterial culture.
Figure 1.10. Transmission Electron Micrograph Showing Section Microbial Cells
Containing Discrete Granules of PHB (Magnification. 6300x)
The individual microorganisms can be clearly seen and each is full of white granules of
polymer. In fact up to 80% of the cell‘s dry weight can be in the form of PHB granules. The
polymer was first isolated and characterized in 1925 by Lemoigne at the Pasteur Institute in
Paris. Since then it has been extensively studied by biochemists that have come to the
general conclusion that bacteria store PHB as an energy reserve in much the same way that
mammals accumulate fat.
This polymer has unique physicochemical properties like thermoplasticity, biodegradability,
biocompatibility, and particularly its tensile properties, which are quite similar to that of
isotactic polypropylene (Vasile et al. 2003; Combeaud et al. 2004). Because of its properties,
PHB is useful in a wide variety of applications ranging from packaging to suture, bone
prostheses, and medicine capsules (Selke et al. 2006, Bucci et al. 2007). The use of PHB also
has limitations. One such limitation is its narrow processing window. The polymer is
thermally unstable at temperature above the melting point (about 180oC), and a drastic
reduction in molecular weight occurs during processing at temperatures between 180-200oC
Introduction
- 15 -
(Biresaw et al. 2002a). Another limitation of it is relatively low impact resistance. In order to
overcome these shortcomings, efforts have been made to co-polymerize PHB repeating units
with other monomers (Mohamed et al. 2007a, Biresaw et al. 2002b, Mohamed et al. 2007b,
Biresaw et al. 2008, Biresaw et al 2004, Sudesh et al 2000, Arrifin et al. 2008, Yang et al.
2004, Erceg et al. 2005), but the cost is considerably high, which limited its usage. One
possible approach to obtain a less expensive thermoplastic polymer of improved mechanical
properties is to blend PHB with another suitable polymer. Considerable work on blending
PHB with other polymeric matrix has been reported, indicating the total or partial miscibility
and the immiscibility of PHB with the second polymer. Earlier studies have shown that
blending polymers could lead to improve properties, decrease the cost and impart
functionalities in blends (De Carvaho et al. 2008).
For their versatility PHAs find application in many daily sectors such as packaging,
agriculture, furniture, transportation, textile, electric & electronic, houseware and biomedical
field (Philip et al. 2007).
1.4.2. Poly (lactic acid) (PLA)
In recent years, biodegradable polymers have been developed to become an attractive
alternative to petrochemical and chemosynthetic polymers. They offer upon conversion a
viable alternative to commodity plastics in a number of bulk applications where recycling is
impractical or uneconomical. Poly(lactic acid) (PLA) is a well-known biodegradable
thermoplastic polymer and appears to meet the safety environmental requirements (Iovino et
al. 2008, Tuominen et al. 2002).
Lactic acid can be produced by anaerobic fermentation of carbon based substrates such as
glucose, sucrose and starch, by using micro-organisms such as bacteria or certain fungi (Patel
et al. 2009, Johansson et al. 2012).
The physical and mechanical PLA properties make this polymer a good candidate as a
replacement of petrochemical thermoplastics in several application areas. While the PLA
high price long restricted its use to medical and specialty applications, recent breakthroughs
in lactide and polymerization technology opened up possibilities for the PLA production in
bulk volumes (Drumright et al. 2000).
Lactic acid may be produced by anaerobic fermentation of carbon substrates, such as
glucose, sucrose and starch, using micro-organisms such as bacteria or certain fungi.
The raw materials range suitable for lactic acid fermentation includes hexoses such as D-
glucose, together with a large number of compounds that can be easily split into hexoses
such as sugars, molasses, sugar beet juice, sulfite liquors and whey, as well as rice, wheat,
and potato starches.
In the future, it is expected that hydrolysis of lignocellulosics such as woody or herbaceous
biomass originating from wood, straw or corn stover, will become a viable pathway through
the enzymatic processes, together with the pressure on resources driving the increased
utilization of agricultural waste, thus avoiding the negative interference with food chain
resources.
The hardness, stiffness, impact strength and elasticity of PLA, are important for applications
such as beverage flasks, are similar to values for PET (Patel et al. 2009). It is a recyclable
Chen Haiyan PhD Thesis
- 16 -
and compostable material that provides significant energy savings (Drumright et al. 2000;
Bogaert et al. 2000).
PLA has a low vicat softening point so the obtained containers are not suitable for being
filled at elevated temperatures and exists the problem for the products warehousing and the
use in automobiles. On the other hand, PLA‘s low heat deflection temperature (HDT) and the
high heat seal strength lead to good performance in film sealing.
PLA has high odor and flavor barrier properties, high resistance to grease and oil, thus
finding application in the packaging of viscous oily liquids, dry and short shelf-life products.
It is not suitable for the packaging of carbonated beverages and other liquids due to its poor
O2, CO2 and water vapor barrier. This property is resulted interesting for some applications
such as the clothing sector where the high water transmission (high wick) for fabrics (Gruber
& O‘Brien, 2002) is a desirable characteristic. The hydrolytic stability conditions close to
some laundering, dyeing and finishing processes are borderline (Woodings, 2000).
PLA exhibits good chemical resistance to aliphatic molecules such as mineral oils and
terpenes.
Since PLA is a polar material it has a high critical surface energy and is thus easy to print,
metalize and dye. It is possible to print PLA using natural dyes and pigments that are heavy
metal free and thus eligible for the DIN norm compostable logo.
PLA is largely resistant to attack by microorganisms in soil or sewage at ambient
temperature, so the polymer must first be hydrolyzed at elevated temperatures (>58°C) to
reduce the molecular weight before biodegradation can commence. Thus, PLA will not
degrade in typical home composting, while it does break down in a typical industrial
composting facility.
Stereocomplex PLA is more resistant to biodegradation. Under typical use and storage
conditions PLA is quite stable. Additives which retard hydrolysis may be used for further
stabilization (Brandrup et al., 1999).
1.5. Different Media as Tool Boxes for Biodegradation of Plastic
Because of the low density of the majority of plastics, the volume fraction of plastics waste
in the municipal solid waste is by far greater than the weight fraction and plastics waste takes
up a lot of landfill space. Plastics rubbish, which makes up about 5±8 wt% of the municipal
solid waste, remains undegraded in the environment for such a long time that it causes
serious environmental problems. Therefore, a great deal of research has focused on
developing biodegradable plastics (Kim et al. 2000).
Biodegradation represents the key property for any form of material recycling or reuse and it
depends on the features of the disposal environment such as the moisture level, the surface
area and structure, the microbiological activity, and other nutrient materials.
Some researchers (Eubeler et al. 2010) reported methods such as standardized
biodegradation tests, analytical tests, enzymatic tests or tests of physical properties to
evaluate the biodegradability of synthetic and/or polymers for different types of
environmental compartments (e.g., soil, compost or river water).
The background used in performing biodegradation studies is constituted by a simple method
(Chiellini and Corti, 2003), the ASTM D5988–03, CEN/TR 15822/09 and EN 14046
Introduction
- 17 -
standards used to follow biodegradation experiment in soil medium, the ISO 14855, ISO
17088-12, EN 13432 standards for the analyses in mature compost and the EN ISO 14593
standard for experiments in river water.
1.5.1. PHAs Biodegradation in Soil
PHA degradation has been recorded in nature and attributed mainly to bacteria (Matavulj et
al. 2000, Lee 1996).
Fungi are another potent group of the degrading micro-biota and they may play an important
role in PHA breakdown, so only recently, fungal breakdown of PHA has attracted
considerable attention of many scientists (Rheddy et al. 2003, Sang et al. 2001, Sang et al.
2002, Garcia de Maria & Dominguez 2010).
One of the first indications of microbial, including PHAs fungal degradation in nature was
published by Lepidi et al. 1972 , who found that micro-fungi could be accumulated from
radioactive compounds originating from bacterially synthesized 14C labelled PHB.
Various traces, cavities, and grooves observed on the dented surface of PHBV films
demonstrated that the degradation was a concerted effect of a microbial consortium
colonizing the film surface, including fungi, bacteria, and actinomycetes.
The succession of microbial consortia in the soil around the PHBV films during the
degradation showed a distinctive increase in the fungal population, resulting in its
dominance. Comparison of the degradation ability of microbial strains isolated from soil
where PHBV films were degraded, revealed that fungi showed the highest contribution to
PHBV degradation, growing very rapidly along the film surface with their high degradation
ability and then expanding their hyphae in a three-dimensional manner (Sang et al. 2002).
Soil micro-organisms are able to degrade the BIOPOL component of blends with ethylene-
vinylacetate. In a few cases the enzymatic breakdown process of PHB by fungi has been
investigated in detail (Matavulj et al. 2000).
Medium-chain-length polyhydroxyalkanoates (mcl-PHAs), which have constituents with a
typical chain length of C6-C14, are polyesters that are synthesized and accumulated in a
wide variety of Gram-negative bacteria, mainly Pseudomonas (Kim et al. 2007). mcl-PHAs
can be degraded by micro-organisms that produce extra-cellular mcl-PHA depolymerase.
mcl-PHA-degraders are relatively uncommon in natural environments and, to date, only a
limited number of mcl-PHA depolymerases have been investigated at the molecular level.
The ability to degrade PHAs depends on the secretion of specific extra-cellular PHA
depolymerases that hydrolyze the polymer to water-soluble products. These enzymes are also
divided into two groups, short-chain-length polyhydroxyalkanoates (scl-PHAS)
depolymerases and mcl-PHA depolymerases, which differ with respect to substrate
specificity for scl-PHAs or mcl-PHAs.
Although a few bacteria have been reported to degrade both scl-PHAs and mcl-PHAs by
producing two types of depolymerases (Klingbeil et al., 1996; Kim et al., 2003), the great
majority of PHA-degrading micro-organisms produce only one type of PHA depolymerase
that acts upon either scl-PHAs or mcl-PHAs.
Recently, Nam et al. 2002 described a list of taxa (60 different species belonging to 13
genera) of mcl-PHA degrading bacteria isolated from various soil samples and demonstrated
Chen Haiyan PhD Thesis
- 18 -
that Gram-negative bacteria belonging to the genera Stenotrophomonas and Pseudomonas
are the predominant mcl-PHA degraders in soil (Kim et al. 2007).
Degradation of polyhydroxyalkanoate (PHA) by three Pseudomonas sp., isolated from fuel-
oil contaminated soil and identified as Ps. fluorescens, Ps. aeruginosa and Ps. putida on the
basis of 16S rRNA sequence analysis, was investigated by Colak and Guner 2004. This
property was determined as molecular weight loss measured by gel permeation
chromatography and morphological changes in poly-3-hydroxybutyrate films observed by
scanning electron microscopy. Both, decrease in molecular weight (7–17%) and weight loss
(up to 29%) of solution-cast films were evidence of the isolates secreting an active
depolymerase responsible for degradation of PHA. Stimulation of activity by Na+, K+, Ca2+
and Mg2+ at 1 mM concentration indicated a requirement for metal ions as a cofactor for
activity. Inhibition of the extra-cellular depolymerases of the three strains in the presence of
p-methylphenyl sulfonylfluoride, cyanide, azide, deoxycholate or EDTA confirms the
presence of an enzyme in the isolates similar to poly(3-hydroxybutyrate) degrading
hydrolases (Colak and Guner 2004, Jendrossek 2001, Champrateep 2010).
A selected polyhydroxyalkanoate (PHA) film was evaluated (Srideshi et al 2006, Yew et al.
2006) for its degradation trends, in a tropical mangrove environment or in tropical climate
environment (Akmal et al. 2003). The biodegradability of PHB and its co-polymers PHBV
[P (3HB-co-5 mol% 3HV)] or PHBHHx [P(3HB-co-5 mol% 3HHx)], was investigated along
with PHB films containing 38 wt% titanium dioxide (TiO2) [PHB-38 wt% TiO2]. The
degradation of these formulations was monitored for 8 weeks at three different zones in an
intermediate mangrove compartment along Sungai Pinang, adjacent to a famous fishing
village on south of Penang Island. The degradation rate was observed both on the surface and
in the sediment and it was expressed in percentage of weight loss. The microbial
enumeration done using sediment from the different zones indicated similar colony-forming
unit (CFU) counts even though differences were noticed in the degradation profile of the
various films in the respective zones.
The results obtained revealed that co-polymers disintegrated at similar or higher rate than the
homopolymer, PHB. However, the incorporation of TiO2 into PHB films caused the
degradation rate of PHB -38 wt% TiO2 composite film to be far slower than all the other
PHA films. The overall rate of degradation of all PHA films placed on the sediment surface
was slower than those buried in the sediment. Microscopic analyses showed that the surface
morphology of P (3HB-co-5 mol% 3HHx) was more porous compared to PHB and P (3HB-
co-5 mol% 3HV) films, which may be an important factor for its rapid degradation.
The biodegradation of films made of poly-β-hydroxybutyrate (PHB) with a molecular mass
of 1500 kDa was studied by Bonartseva et al. 2002 using a model soil community in the
presence and absence of nitrate and at different concentrations of oxygen in the gas phase.
The PHB biodegradation was investigated with respect to changes in its molecular mass,
crystallinity, and some mechanical properties, surface composition and morphology (Sadi et
al. 2010, Lucas et al. 2008, Correa et al. 2008). The multi-block copolymers has been
evaluated by Zhao et al. 2006 using a soil suspension system.
Mergaert et al. 1992 isolated from soil more than 300 microbial strains capable of degrading
PHB in vitro, of which denitrifying bacteria are of particular practical interest due to their
Introduction
- 19 -
potential ability to be used in the immobilized state on PHB films for the purification of
water from nitrates.
The PHB film biodegradability was studied under aerobic, micro-aerobic and anaerobic
conditions (Maergaert et al. 2011) in the presence and absence of nitrate by microbial
populations of soil, sludges from anaerobic and nitrifying/denitrifying reactors, and sediment
of a sludge deposit site, as well as to obtain active denitrifying enrichment culture degrading
PHB.
Changes in molecular mass, crystallinity, and mechanical properties of PHB have been
studied.
The biodegradation of PHB films in soil suspension has been studied during 2 months under
different aeration conditions and nitrate was added as an additional nitrogen source (and as
an electron acceptor). PHB degradation was highest under aerobic condition, and practically
did not proceed under anaerobic condition. The addition of nitrate enhanced the degradation
under all of the aeration conditions studied and stimulated the development of denitrifying
microbial populations.
The presence of nitrate promoted the degradation and enhanced the decline in the Mw of
PHB films. The most degraded PHB exhibited the highest values of the crystallinity index.
As it has been shown by Spyros et al. 1997, PHAs contain amorphous and crystalline
regions, of which the former are much more susceptible to microbial attack. If so, the PHB
microbial degradation must be associated with a decrease in its molecular weight and an
increase in its crystallinity.
The total number of micro-organisms on the surface of the PHB films degraded under micro-
aerobic and aerobic conditions in soil was 4 x 104 to 5 x 106 (fungi) and 1 x 105 to 2 x 107
(bacteria). The PHB film degraded under anaerobic conditions contained no micro-
organisms. The bacteria detected on the degraded PHB films were dominated by the genera
Pseudomonas (Shimao 2001, Bhatt et al. 2008), Bacillus, Azospirillum, Mycobacterium,
Streptomyces (Hermida et al. 2009, Kulkarni et al. 2011, Rai et al. 2011), Actinomadura sp
(Shah et al. 2010) while the fungi were dominated by the genus Penicillium.
The microbial degradation of PHB tensile test pieces or its copolymer made of 3-
hydroxybutyric acid (90%) and 3-hydroxyvaleric acid (10%) was studied in soils by
Mergaert et al. 1993. The samples were incubated at a constant temperature of 15, 28, or
40°C for up to 200 days and the degradation was measured through loss of weight (surface
erosion), molecular weight, and mechanical strength. The erosion rate was enhanced by
incubation at higher temperatures, and in most cases the copolymer lost weight at a higher
rate than the homopolymer. The molecular weight decrease is due to simple hydrolysis and
not to the action of biodegrading micro-organisms.
The degradation resulted in loss of mechanical properties (Mergaert et al. 1993).
The number of denitrifying bacteria was about 102 cells per flask in almost all experimental
variants (Bonartseva et al. 2002).
PHB biodegradation in the enriched culture obtained from soil on the medium used to
cultivate denitrifying bacteria has been also studied. The dominant bacterial species,
Pseudomonas fluorescens and Pseudomonas stutzeri, have been identified in this enrichment
Chen Haiyan PhD Thesis
- 20 -
culture. Under denitrifying conditions, PHB films were completely degraded for seven days.
Both the film weight and Mw of PHB decreased with time.
The data were in contrast with those of Doi et al. 1990 who found that Mw of PHB remained
unchanged upon enzymatic biodegradation in an aquatic solution of PHB- depolymerase
from Alcaligenes faecalis. The average viscosity of the higher- and lower-molecular weight
polymers decreased gradually from 1540 to 580 kDa and from 890 to 612 kDa, respectively.
The "exo"-type cleavage of the polymer chain, such as the successive removal of the
terminal groups, is known to occur at a higher rate than the "endo"-type cleavage, such as the
random breakage of the polymer chain at the enzyme-binding sites. Thus, the former type of
polymer degradation is primarily responsible for changes in its average molecular weight.
Biodegradation of the lower-molecular polymer, which contains a higher number of terminal
groups, is more active, probably, because the "exo"-type degradation is more active in lower
than in higher molecular polymer (Bonartseva et al. 2002, Bonartseva et al. 2003, Doi et al.
1997).
The PHB samples have been tested for fungicidity and resistance to fungi by estimating the
growth rate of test fungi from the genera Aspergillus, Aureobasidium, Chaetomium,
Paecilomyces, Penicillum, Trichoderma under optimal growth conditions. PHB film did not
exhibit neither fungicide properties, nor the resistance to fungal damage, and served as a
good substrate for fungal growth (Mokeeva et al. 2002).
The degradability of poly(propylene carbonate)/poly(β-hydroxybutyrate-co-β-
hydroxyvalerate) (PPC/PHBV) blends has been investigated in soil suspension cultivation
and in vitro degradation testing by Tao et al. 2009. The changes of structure and molecular
weight for blends have been also studied by 1H nuclear magnetic resonance spectroscopy
(1H-NMR), scanning electron microscopy (SEM) and gel permeation chromatography
(GPC) before and after degradation. Although the PPC/PHBV blends were immiscible, the
addition of PHBV could improve the thermal stability of PPC. PHBV has been degraded
mainly by the action of microbial enzymes in the soil suspension, which biodegraded it more
rapidly than PPC in a natural environment.
PPC has been degraded mainly by chemical hydrolysis and random hydrolytic scission of
chains in the PBS solution in vitro, and degradation of PPC was more rapid than that of
PHBV in a simulated physiological environment.
Poly (lactic acid) degradation is a complex phenomenon characterized by morphological
changes correlated with the soil conditions.
The biodegradation propensity for flax fiber reinforced PLA based composites in presence of
amphiphilic additives was investigated by using the soil burial test (Kumar et al. 2010). PLA
removal from the composites surface depends on biodegradation as evidenced in SEM
study.. About 4.2% weight loss was observed in neat PLA of burial in soil for 20 days. After
90 days, composite samples partially disintegrated.
Poly (L-lactide) (PLLA) films were buried in outdoor environment for two years for testing
the biodegradability as Gallet et al. 2001 reported. After 20 months lactic acid and lactoyl
lactic acid appeared as the products of hydrolysis. After 24 months the amount of lactoyl
lactic acid decreased due to the biotic hydrolysis of the film. So PLLA was degraded by a
combination of hydrolysis and biotic activity. In first stage, after an induction period of 1
Introduction
- 21 -
year, PLLA film undergoes hydrolysis, while in second stage microorganisms assimilate the
small degradation products also hydrolysis happened. The thermal properties (Tg and Tm)
were significantly affected during the period (Karjomaa et al. 1998, Hakkarainen et al. 1996,
Hakkarainen et al. 2000a and 2000b).
Soil biodegradation were performed experiments by using 2mm thick racemic PLA plates
during 8 weeks (Torres et al. 1996).
Although no significant changes were observed in PLA oligomers concentration, lactic acid
was removed from the film by microorganisms‘ assimilation while hydrolysis formed large
amount of them. Thus both hydrolysis and microbial assimilation affect PLLA degradation at
same time.
The long-term degradation/disintegration behavior of PLA films and fibres, with eleven-
month trial, was investigated, in the experimental field of natural Mediterranean soil, by
Rudnik et al. 2011. Different thicknesses for PLA films, are responsible of mechanical
degradation or partially disintegration.
The mechanical, thermal and biodegradable properties of poly [(D, L-Lctide)] (PDLLA),
together with other polymers (PEG- poly (ethylene glycol)) were assessed by Wang et al.
2008.
The degradation test showed that PEG addition could accelerate the blends biodegradation in
soil under room temperature significantly, and proximately 20 % mass loss was got by the
end of 30 days by means of storage.
Shogren et al. 2003 found that burning PLA in soil for 1 year, from outside to inside along a
narrow zone, weight losses were due to starch only with the degradation proceeding.
1.5.2. PHAs Biodegradation in Mature Compost
PHA production and degradation in waste environment as well as its role in biological
phosphorus removal were reviewed by Lee et al. 1999. In biological phosphorus removal
process, bacteria accumulating polyphosphate (polyP) uptake carbon substrates and
accumulate these as PHA by utilizing energy from breaking down polyP under anaerobic
condition. In the following aerobic condition, accumulated PHA is utilized for energy
generation and for the regeneration of polyP. PHA production from waste has been
investigated in order to utilize abundant organic compounds in waste water. Since PHA
content and PHA productivity that can be obtained are rather low, PHA production from
waste product should be considered as a coupled process for reducing the amount of organic
waste. PHAs can be rapidly degraded to completion in municipal anaerobic sludge by
various micro-organisms.
Aiba et al. 2009 have isolated a thermophilic Streptomyces sp., capable of degrading various
aliphatic polyesters, from a landfill site. The isolate, Streptomyces sp. BCC23167,
demonstrated rapid aerobic degradation of several polyesters, including
polyhydroxyalkanoate copolymers, poly(ε-caprolactone) and poly(butylene succinate) at
50◦C and neutral pH. The degrading activity was repressed by glucose and cellobiose, but
tolerant to repression by other carbon substrates.
Degradation of a commercial poly [(R)-3-hydroxybutyrate-co(R)-3-hydroxyhexanoate]
(PHBHHx) by Streptomyces sp. BCC23167 progressed from surface to bulk as suggested by
the slight decrease in polymer molecular weight. Differential scanning calorimetry analysis
of PHBHHx film degradation by Streptomyces sp. BCC23167 showed that relative
Chen Haiyan PhD Thesis
- 22 -
crystallinity of the film increased slightly in the early stage of degradation, followed by a
marked decrease later on. The surface morphology of degraded films was analyzed by
scanning electron microscopy, which showed altered surface structure consistent with the
changes in crystallinity.
The isolate is thus of potential interest for application in composting technology for
bioplastic degradation (Rheddy et al. 2003, Weng et al. 2010, Weng et al 2011).
A Gram-positive poly (3-hydroxybutyrate) (PHB)-degrading bacterial strain was isolated
from compost by Takaku et al. 2006. This organism, identified as Bacillus megaterium N-18-
25-9, produced a clearing zone on opaque PHB agar, indicating the presence of extracellular
PHB depolymerase. A PHB depolymerase gene, PhaZBm, of B. megaterium N-18-25-9 was
cloned and sequenced, and the recombinant gene product was purified from Escherichia coli.
The N-terminal half region of PhaZBm shared significant homologies with a catalytic
domain of other PHB depolymerases.
Also the PHA-degrading isolate, strain P37C, was enriched from residential compost for its
ability to hydrolyze the medium chain length PHA, poly(β-hydroxyoctanoate) (PHO). It was
subsequently found to grow on a wide range of PHAs, including both short chain length and
medium chain length PHAs. The isolate was identified as belonging to the genus
Comamonas. Strain P37C formed clear zones on PHB, PHO and poly(β-
hydroxyphenylvalerate) (PHPV) overlay plates (Quinteros et al. 1999).
PLA blends are degradable under both aerobic and anaerobic conditions, indicating that
composting, landfilling and anaerobic digestion represent all possible options for handling
the waste. However, pretreatment technologies, such as thermal, enzymatic, ultrasonic
treatment and the application of adapted microorganisms, must be combined with
composting in order to enhance the reduction of the waste volume (Cho et al 2011, Zeid et al.
(2001).
Biodegradation rates of PLA/starch blends and PLA/wood- flour composites were lower than
pure cellulose but higher than pure PLA. This value increased from 60% to 80% when the
starch content was increased from 10% to 40% after 80 days (Kunioka et al. 2006). It means
that an higher starch content makes faster PLA biodegradation in composting facilities.
Many authors have prepared PLA based nano-composites and studied several properties
including biodegradability in composting.
Bacillus licheniformis could be considered as one of the responsible bacterium for PLA
biodegradation in compost. The influence on the chemical structure as the interaction of the
bacterium toward clay, are clear effects exerted on the polymer bacterial degradation.
In the case of 4% by weight of filler content, the silicate layers were homogeneously
dispersed in the PLA matrix and these hydroxy groups start heterogeneous hydrolysis of the
PLA matrix after absorbing water from compost. The weight losses and PLA hydrolysis
degree for the pure sample and the composite containing 4% by weight of filler remained
almost same up to one month that became a critical time for PLA degradation rate (Pandey et
al. 2005).
Poly (l-lactide) (PLLA) could rapidly biodegrade under mixed culture of compost
microorganisms‘ conditions (Hakkarainen et al. 2001, Nampoothiri et al. 2010). The films
was fragmented to fine powder and analyzed after 5 weeks in biotic environment. The
Introduction
- 23 -
performed analysis in the biotic environment showed that microorganisms assimilated lactic
acid and lactoyl lactic acid from the films rapidly. At the same time, a new degradation
product that is an ethyl ester of lactoyl lactic acid was formed and a rapid molecular weight
and polydispersity increase was observed.
The SEM micrographs results showed a large number of bacteria and mycelium of fungi
growing on the surface of the biotical aged films. On the other hand, in the abiotic
environment only a slight molecular weight decrease was observed and the polydispersity
decreased towards 2.0.
Moreover, preferred degradation happened near the chain ends in the biotic environment
whereas a random hydrolysis of the ester bonds in abiotic environment occurs.
The compostability of three commercially available biodegradable packages made of PLA,
in particular water bottles, trays and deli containers, to composting and to ambient exposure
were studied by Kale et al. 2006 that investigated the properties breakdown of these
packages exposed to compost conditions by several experimental procedure involving GPC,
DSC, TGA and visual inspection. The compost pile was prepared with cow manure, wood
shaving and waste feed, at a temperature above 60°C. After 3 weeks the pile was put on
asphalt pad. The initial pile temperature, relative humidity and pH was 65 ± 5 °C, 63 ± 5%
and 8.5 ± 0.5, respectively.
The packages were subjected to composting for 30 days and the packages exposed to
ambient conditions were also studied. This is because it is well known that PLA absorb
water, resulting in the hydrolysis and cleavage of the ester linkages, auto-catalyzed by the
carboxylic acid end groups.
Kale et al. (2006) found that the degradation rate changes with the initial crystallinity and L-
lactide content of the packages, with lower degradation for the polymer with the highest
content of L-lactide (96 versus 94%) due to the higher crystallinity, which makes more
difficult the degradation of the whole structure. During the hydrolysis process the sample
decreased in size and became tough with a trend that depends to the shape.
The dimension of the containers before and after composting was calculated by measuring
the variation on width, length, height and thickness. During the first period of the ambient
exposure (within the first 15 days) the molecular weight of the sample Mw showed a small
increase probably due to UV or gamma radiation that produce chain cleavage and subsequent
recombination, which can result in cross-linking and hence an increase in the Mw. The
increase in molecular weight produced an increase in the Tg and leading to slower
degradation since glassy polymers degrade more slowly than rubbery ones. The same trend
was observed for the sample exposed to the compost pile; the Mw increase could be
attributed to cross-linking or recombination reactions. Subsequently, during exposure, the
degradation produced a molecular weight decrease that followed a first order kinetic
associated to a first order hydrolysis process affected by the initial crystallinity, thickness
and shape of the sample (Tsuji et al. 1998).
1.5.3. PHAs Biodegradation in Aqueous Medium
Fungi were probably involved in the degradation of BIOPOL shampoo bottles under marine
conditions. More recently, fungal breakdown of thermoplasts, including PHA has been
simulated in the deep sea conditions.
Chen Haiyan PhD Thesis
- 24 -
BIOPOL (Zeneca BioProducts) (Matavulj et al. 2000), a copolymer of PHB and PHV, has
been commercially produced and is used as packaging material. In vitro bacterial degradation
of BIOPOL and several other PHAs has been proven (Fedulova et al. 1980, Tanio et al.
1982, Jendrossek et al. 1992, Jendrossek et al. 1996, Schirmer et al 1993).
In addition to the type of micro-biota involved, the rate of biodegradation depends also on
many other factors, notably those related to the ease of microbial colonization.
Environmental factors, such as humidity, temperature, electrochemical reaction, biological
oxygen demand and supply of other nutrients (nitrogen, phosphorus), are also important.
The BIOPOL degradation (Matavulj et al. 2000) as well as its blends degradation with other
plastic materials such as poly(caprolactone), polystyrene, poly-L-lactide and polystyrene-co-
acrylonitrile can be performed by using PHA depolymerase from the culture supernatant of
the fungus Penicillium funiculosum.
The tested blends showed higher weight losses with increasing content of the BIOPOL
component.
Doi et al. 1999 have evaluated the biodegradabilities of (P(3HB-co-14%3HV)) monofilament
fibers at 25°C for 28 days by monitoring the time-dependent changes in the biochemical
oxygen demand (BOD) and weight-loss (erosion) of fibers under aerobic conditions in a
temperature-controlled reactor containing natural waters from various aquatic environments
such as sea, lake and river (Rheddy et al. 2003, Luzier et al. 1992, Khanna & Srivastava
2005).
Two types of fibers with different diameters (213 and 493μm) were used in this test and their
biodegradabilities decreased in the following order: river > lake > sea. By analyses of
scanning electron microscopy and X-ray diffraction of eroded fibers, it has been concluded
that the biodegradation proceeded from amorphous regions on the surface of fibers by the
function of micro-organisms in fresh water or seawater. In addition, 13 strains of PHB-
degrading bacteria were isolated from different sources of seawater and identified. Majority
of isolates grew well on PHB or P(3HB-co-14%3HV) as sole carbon source and excreted
extra-cellular polyhydroxybutyrate (PHB) depolymerases (Ohura et al. 1999).
During the summers of 1999-2001 the dynamics of polyhydroxyalkanoate degradation in a
small recreational eutrophic reservoir or in anaerobic sediment (Castelli et al. 1995) was
studied (Volova et al. 2006, Volova et al. 2007, Volova et al. 2010).
It has been shown that biodegradation of polyhydroxyalkanoates in the environment is
determined by the structure and physicochemical properties of the polymer and by local
weather conditions, which influence the state of the aquatic ecosystem. Species (clones) of
bacteria able to utilize polyhydroxyalkanoates in the reservoir were identified using
molecular phylogenetic analysis of 16S rRNA genes.
The attempts to examine the abundance and diversity of mcl-PHA-degrading micro-
organisms in marine environments showed that mcl-PHA degraders in seawater samples
were less than 1.4% of all the heterotrophic bacteria and that Pseudomonas and
Stenotrophomonas strains accounted for approximately 65% and 23%, respectively, of the
total mcl-PHA degraders isolated (Kim et al. 2007, Doi et al. 1992). These results suggest
that mcl-PHA biodegradation in soil and marine environments may be predominantly
performed by Pseudomonas and Stenotrophomonas species. Among Gram-positive bacteria,
Introduction
- 25 -
the presence of mcl-PHA depolymerase activity has been found only in Streptomyces sp.
(Klingbeil et al., 1996; Kim et al., 2003) and Rhodococcus equi (Lim, 2006). Particularly,
members of the genus Rhodococcus have attracted great interest due to their capabilities to
degrade various hydrophobic substances such as petroleum hydrocarbon, benzene,
polychlorinated biphenyls, and scl-PHAs (Jang et al., 2005; Taki et al., 2007; Valappil et al.,
2007). The ability of Rhodococcus to degrade mcl-PHAs suggests that Rhodococcus may
play a considerable role in decomposing various materials in natural environments (Kim et
al. 2007).
Biodegradabilities of 21 samples of biosynthetic and chemosynthetic polyesters were
measured at 25°C (Doi et al. 1996, Kasuya et al. 1998, Ohura et al. 1999), under aerobic
conditions in a temperature-controlled reactor containing 200 ml of natural water from the
river Arakawa (Saitama, Japan) as an inoculum, by monitoring the time-dependent changes
in the biochemical oxygen demand (BOD), weight loss (erosion) of polyester film and
dissolved organic carbon concentration (DOC) of the test solution. The microbial
copolyesters, such as PHBV, poly(3- hydroxybutyrate-co-4-hydroxybutyrate) and poly(3-
hydroxybutyrate-co-3- hydroxypropionate), were degraded in the river water at a rapid rate,
and the weight-loss and BOD-biodegradabilities of the majority of biosynthetic polyesters
were 100 and 80% ± 5% for 28 days, respectively (Doi et al. 1996).
The same polyesters have been studied (Abou-Zeid et al. 2001, Hablot et al. 2008) in two
anaerobic sludges and individual polyester degrading anaerobic strains were isolated,
characterized and used for degradation experiments under controlled laboratory conditions.
Two methods for accurate poly (3-hydroxybutyrate) (PHB) depolymerase activity
determination and quantitative and qualitative hydrolysis product determination are
described by Gebauer and Jendrossek 2006. The first method is based on online
determination of NaOH consumption rates necessary to neutralize 3-hydroxybutyric acid
(3HB) and/or 3HB oligomer produced during the hydrolysis reaction and requires a pH-stat
apparatus equipped with a software controlled microliter pump for a rapid and accurate
titration. The method is universally suitable for hydrolysis of any type of
polyhydroxyalkanoate or other molecules with hydrolyzable ester bonds, allows the
determination of hydrolysis rates of as low as 1 nmol/min, and has a dynamic capacity of at
least 6 orders of magnitude. By applying this method, specific hydrolysis rates of native PHB
granules isolated from Ralstonia eutropha H16 were determined for the first time. The
second method was developed for hydrolysis product identification and is based on the
derivatization of 3HB oligomers into bromophenacyl derivates and separation by high
performance liquid chromatography. The method allows the separation and quantification of
3HB and 3HB oligomers up to the octamer.
The two methods were applied to investigate the hydrolysis of different types of PHB by
selected PHB depolymerases (Gebauer and Jendrossek 2006).
An effective technology for production of PHB and PHBV of different molecular weight
(from 200 to 1500 kDa) by diazotrophic bacteria of Azotobacter and Rhizobium genus has
been developed (Bonartsev et al. 2007). In order to clarify mechanism of PHB
biodegradation degradation of PHB at different conditions in vitro and in vivo have been
studied.
Chen Haiyan PhD Thesis
- 26 -
The mechanisms of PHB biodegradation is correlated with a PHB hydrolysis in vitro
(Shangguanna et al. 2006). Degradation of films from PHB of different Mw (300, 450, 1000
kDa) in vitro has been demonstrated under three different conditions that showed
simultaneously the increase of crystallinity and the decrease of Mw. As consequence,
mechanical properties became worse: PHB films became more rigid and fragile; the surface
of PHB films became distended, micro-cracks appeared. At second relatively short-term
phase rapid fragmentation and following complete degradation of small fragments of PHB
films were observed.
PHB degradation by activated sludge from reactor treating pig manure wastewater and from
nitrifying/denitrifying reactor of the plant treating municipal wastewater (Moscow) in the
presence and absence of nitrate at 20°C has been studied (Kallistova et al. 2002, Hong et al.
2008, Chen & Li 2008, Wang et al. 2004). The activated sludge from both reactors had
similar properties for PHB degradation and average rates of denitrification. In both presence
and absence of nitrate, the intensity and properties of PHB degradation were also similar.
The rate of PHB degradation in the presence of nitrate was only 1.11 times higher, than in
absence of nitrate. The activated sludge from anaerobic reactor showed a bit higher average
rates of denitrification and acetate accumulation.
The contribution of bacteria, isolated from sewage sludge, towards the microbial degradation
of PHBV was studied by Shah et al 2007.
A microbial consortium (De Lucas et al. 2005) was inoculated on mineral salt agar plates
containing different concentrations of PHBV as a substrate. The PHBV degraders showed
optimum depolymerase production at pH 7.0, 37°C, and 0.4% substrate concentration during
2–5 weeks of incubation. Additional carbon sources like glucose, fructose, sucrose, lactose
and nitrogen sources including yeast extract were used as co-metabolites. The highest degree
of degradation of PHBV was observed in the presence of glucose. When the PHBV
depolymerase activity of isolates present in the consortium was determined separately, it was
found that the enzyme activity was higher in case of Bacillus sp. AF3. The purification steps
included ammonium sulphate fractionation and gel permeation chromatography on Sephadex
G-75. The enzyme has been purified to homogeneity as judged by sodium dodecyl sulphate-
polyacrylamide gel electrophoresis (SDS-PAGE) and molecular weight was found to be
approximately 37 kDa (Shah et al. 2007).
The hydrolytic degradation of poly(3-hydroxyalkanoates), PHA blends with low and high
molecular weight additives have been examined by Renarda et al. 2004. The PHA films were
characterised by Differential Scanning Calorimetry, DSC, and Atomic Force Microscopy,
AFM, which revealed that hydrolyzable PLA and hydrophilic PEG, selected as additives
which might accelerate hydrolytic degradation, were immiscible with PHAs over the range
of compositions studied. PHA blends were incubated in tetraborate buffer (pH 10) at 37°C
for periods ranging from 7 to 160 days.
Film degradation was studied by weight loss and Size Exclusion Chromatography (SEC).
The results showed that the presence of a second component, whatever its chemical nature, is
sufficient to perturb the crystallization behaviour of highly crystalline, PHBV, and increase
hydrolytic degradation. In contrast, the degradation of poly(3-hydroxyoctanoate), PHO, was
unaffected by blending with PLA or PEG. PHO degradation is a very slow process, requiring
Introduction
- 27 -
several months of incubation. However, the introduction of polar carboxylic groups in side
chains led to an increase in the degradation rate.
PLLA mineralization (Reeve et al. 1994), in the aerobic aquatic headspace test, was very
slow at room temperature showing that its polymer structure has to be hydrolysed before
microorganisms can utilize it as a nutrient source so, as occurs for other
polyhydroxyalkanoic acids (Jendrossek et al. 1996), PLLA crystalline structure reduces
chemical hydrolysis and therefore its susceptibility to biodegradation.
When PLLA is exposed to high temperatures, fundamental microstructural changes and
molecular rearrangements occur and hydrolysis starts (Itavara et al. 2002). The flexibility of
the polymer chain increases at temperatures higher than the glass transition temperature. In
addition, water absorption into the polymer matrix increases at high temperatures. This may
not only accelerate chemical hydrolysis, but also facilitate the attachment of microbes and
enzymes on the polymer surface by increasing polymer hydrophilicity.
The molecular size of the PLLA oligomers that microorganisms are able to utilise is critical,
as reported in our earlier study (Karjomaa et al. 1998).
1.5.4. Microbial Biodegradation Mechanism (intra and extra-cellular)
Deep studies haven been conducted recently by Hidayah Ariffin et al 2008 and 2009 about
the thermal degradation mechanisms of PHB. They confirmed that random chain scission by
β-elimination is the main mechanism of PHB thermal degradation. The authors previously
have been suggested the possibility of additional mechanism where an auto-accelerated
random degradation has been favored by the carboxylic groups self-proliferated in bulk. The
unzipping reaction occurring at the end of the molecules was kinetically favored by the
scission of polymer chains that generates a large number of crotonic acid moieties. The
author suggested that this is an ideal self-proliferation reaction of carboxyl compounds and is
the key factor in the auto-accelerated random degradation. An upgrading of this study
conducted by Ariffin et al., to hypothesize a new mechanism for PHB thermal degradation
(Scheme 1.1) where anhydrides production has been proposed as an additional pyrolysis
mechanism of the biopolymer.
O CH2
C
O
CHO
H2CH
CH2
C
O
CHO
CH3
O CH2
C
O HC
CH2+
CH2
C
O
CHO
H3C
Scheme 1.1. Thermal PHB-chain Breakdown with Formation of Crotonic and Carboxilic
End Groups.
Chen Haiyan PhD Thesis
- 28 -
Moreover, they observed a wide range of activation energy value (Ea) for the PHB thermal
degradation and they hypothesized that probably this wide range can be correlated with a
deviation from the random chain scission statistics suggesting the presence of other kinds of
mechanism out of the random scission. To confirm other mechanisms out of the random
scission, minor pyrolyzates from PHB were characterized with 1H/13C-NMR, Fourier
transform infrared spectroscopy, and Fast Atom Bombardment Mass Spectrometry. As a
result, crotonic anhydride and its oligomers were detected as minor products from
condensation reactions between carboxyl groups. The anhydrides production must be one
reaction out of the conforming process to the random degradation statistics and contribute to
the complexity of PHB pyrolysis. Then, an expected thermal degradation pathway of PHB
was proposed (Scheme 1.1) (Arrifin et al. 2009).
Another mechanism that gives a decreasing in (PHA)s molecular weight is the hydrolytic
degradation (Scheme 1.2) promoted by the introduction of polar carboxylic groups in side
chains.
Scheme 1.2. PHB-Chain Breakdown by Moisture as Auto-catalyzed by Carboxilic End
Groups.
Renarda et al. 2004 characterized PHAs films by differential scanning calorimetry and
atomic force microscopy finding that hydrophilic components such as PLA and PEG might
accelerate the hydrolytic degradation correlated with a perturbation in the crystallization
behaviour of highly crystalline PHBV.
The hydrolytic degradation of PHB proceeds homogeneously and randomly via a bulk
erosion mechanism that proceed faster in the melt than in the solid state. The molecular
weight of PHB decreased exponentially without formation of low molecular-weight specific
peaks originating from crystalline residues (Saeki et al. 2005).
O CH2
C
O
CH
CH3
O CH2
C
O
CH
H3C
O
O CH2
C
O
CHOH
CH3 HO
CH2
CH
O
CH3
H3O
+ H
CO
+
H2O
Introduction
- 29 -
The activation energy for the hydrolytic degradation of PHB in the melt (180–250°C) was
30.0 kcal /molK, which is higher than 12.2 kcal/molK for PLLA in the melt in the
temperature range (180–250°C). So using this method is possible to obtain (R)-3HB and to
prepare PHB having different molecular weights without containing the specific low-
molecular weight chains, because of the removal of the effect caused by crystalline residues.
The molecular weight distribution of PHB shifted as a whole to a lower molecular weight
during the hydrolytic degradation without formation of any low molecular- weight specific
peaks arising from the chains in the crystalline residues. No formation of any low-molecular-
weight peaks is an important feature of the hydrolytic degradation of PHB above Tm, which
must contribute to its efficient hydrolytic degradation, resulting in rapid saturation of yields
of 3HBs.
The Mw/Mn value remained in the range of 1.5–1.8 during the hydrolytic degradation as
long as Mn was higher than 1x 104 g/ molK, while it increased to about 2.7 when Mn
became lower than 1x 104 g/ molK. The Mn decreased exponentially with the hydrolytic
degradation time and the decrease rates of Mn increased monotonically with the hydrolytic
degradation temperature.
1.5.5. PHAs Biodegradation Provided by Enzymes
PHA depolymerase obtained from some fungi or bacteria such as Penicillium funiculosum,
Alcaligenes faecalis, Pseudomonas leimoignei are a class of enzymes suitable for PHAs
degradation and its based blends (Hisano et al. 2006, Nojiri et al. 1997, Iwata et al. 2002).
Higher weight losses with increasing BIOPOL component were obtained. Similar results
were reported (Matavulj et al. 2000) by other researchers who assessed that only the
BIOPOL component of blends with ethylene-vinylacetate was degraded by soil
microorganisms (Verhoogt et al. 1995).
Enzymatic degradation of poly(3-hydroxybutyrate-co-3-hydroxyalkanoates) (PHBHA) bio-
polyesters consisting of HB and 15 mol % medium-chain-length HA was studied using the
enzyme PHA depolymerase produced by Ralstonia pickettii T1. It was found that PHBHA
films did not loose their weight after 25 h of depolymerase treatment. In contrast, three
commercially available PHAs including PHB, poly (3-hydroxybutyratee19 mol % 3-
hydroxyvalerate) (PHBV) and poly (3-hydroxybutyrate - 19 mol % 3-hydroxyhexanoate)
(PHBHHx) lost over 50% of their original weights. Slow degradation of PHBHA was also
confirmed by the absence of HA monomers, dimers or trimers as degradation products in
their depolymerase solution compared with abundance of degradation products released by
the other three PHAs under the same condition (Li et al. 2007, Hiraishi et al. 2006).
The photocatalytic activity and biodegradation of PHB films containing titanium dioxide
(TiO2) were evaluated. PHB-TiO2 based films (Yew et al. 2006) and after an hour under
solar illumination in garden soil, 96% of methylene blue solution was decolorized.
The antibacterial activity against Escherichia coli (E. coli) exhibited enhanced photocatalytic
sterilization activity over time. PHB-TiO2 based films showed slower degradation rate in
dark conditions than those receiving direct solar illumination. Interestingly, the latter
composite films showed faster degradation rates compared to pure PHB films indicating that
the degradation is mainly due to photocatalytic activity. PHB-TiO2 based films buried in soil
Chen Haiyan PhD Thesis
- 30 -
generally showed slower degradation rates than pure PHB films. These values were
dependent on the soil microbial activity.
Poly (lactic acid) depolymerases can be categorized into protease-type and lipase- type
(Kawai et al. 2011). During PLA hydrolysis process, the protease enzymes are selective for
PLLA whereas the lipase enzymes, including Cutinase-Like Enzyme (CLE) from
Cryptococcus sp. strain S-2 preferentially hydrolyze PDLA. Both enzymes degraded not only
PLA emulsion but also PLA film, in which amorphous region is preferentially attacked,
respect the crystalline crystalline one.
The different enantio-selectivity of these active enzymes toward PLLA and PDLA could be a
good indicator for categorizing PLA diastereoisomers.
Microorganisms such as Fusarium moniliforme and Penicillium Roquefort that carry out the
degradation of PLA oligomers (molecular weight ~1000) (Torres et al. 1996) or
Amycolatopsis sp and Bacillus brevis are able to degrade PLA polymer (Pranamuda et al.
1997, Pranamuda et al. 1999, Tomita et al. 19999. In addition, enzymatic degradation of low
molecular weight PLA (molecular weight ~2000) has been shown using esterase-type
enzymes such as Rhizopus delemer lipase (Fukuzaki et al. 1989).
Kunioka et al. 2006 have patented some methods with the aim to produce mechanical
crushing of PLA pellets and powder at low temperature, by using selected dry ice. The
biodegradation rate of these PLA based powders were evaluated with two methods:
enzymatic degradation and Microbial Oxidative Degradation Analyzer (MODA) technique,
both based on an international standard.
In the first case, PLA biodegradation degree was 91% for 35 days in a controlled compost
according to a protocol based on ISO 14855-1 (JIS K6953) at 58ºC whereas in the second
case, the PLA biodegradation degree was almost 80% for 50 days.
Proteinase K., a fungal serine protease of Tritirachium album (Williams 1982, Tomita et al.
1999, Wu 2009, Cai et al. 1996), results to be a suitable enzyme for PLA biodegradation able
to decrease the polymer molecular weight by hydrolysis accelerated in compost conditions.
PLA hydrolysis is a chemical reaction that depends on the pH and temperature conditions.
The degradation occurs at the particles surface and the polymer inside particles is not
degraded by this enzyme. Since polymer powders with a smaller particle size have a higher
surface area, the degradation speed depends on the total surface area of the particles.
About 60% of PLA films was degraded after 14 days from initial weight (Pranamuda et al.
1997) by using Mycolatopsis strain HT-32, which is an actinomycete was the first isolated
PLA-degrading microorganism (Ikura et al. 1999, Nakamura et al. 2001, Sakai et al. 2001,
Teeraphatpornchai et al. 2003, Jarerat et al. 2003, Tomita et al. 2004, Pranamuda et al. 2001.
Actually, there is little information about bacteria degrading PLA, just two thermophiles and
one mesophile have been isolated occasionally until now. One of them, isolated as first PLA-
degrading bacterium, was identified as a themophile belonging to Brevibacillus sp. (formerly
Bacillus brevi) (Torres et al. 1996). This microorganism is able to degrade PLA films
isolated from 153 soil samples with an enrichment culture technique performed at
temperature of 6°C (Ikura et al. 1999).
PLA-degrading fungi screen activity was first conducted by Kim et al. 2003. After 14 fungal
strains was tested, they found only two strains - F. Moniliforme and P. Roqueforti could
Introduction
- 31 -
assimilate or partially soluble PLA derivatives, D,L-lactic acid and the racemic oligomers
(Mw=1,000). They observed that one strain of F. Moniliforme was able to grow on a poly
(lactic acid-co -glycolic acid) copolyester (Mw=150,000) film, but its ability to mineralize
the polymer was poor.
A recent overview about PLA biodegradation (Tokiwa et al. 2004) reports that lactic acid
bacteria (LAB) and some filamentous fungi are the chief microbial sources of lactic acid. The
organisms that predominantly yield the L isomer are Lactobacilli amylophilus, Lacto-bacilli
bavaricus, Lactobacilli casei, Lactobacilli maltaromicus, and Lactobacilli salivarius. Strains
such as Lactobacilli delbrueckii, Lactobacilli jensenii, and Lactobacilli acidophilus give the
Disomer or mixtures of both.
PLA film degradation can occur by using Saccharo-thrix waywayandensis (renamed as
Lentzea waywayandensis) (Jarerat et al. 2003) and by Kibdelosporangium aridum (Wu 2009)
and it is an evidence that PLA can be degraded markedly by adding gelatin into the culture
medium.
The thermal properties for PLA based composites loaded with green coconut fiber (GCF)
were evaluated (Fukushima et al. 2009) and the biodegradation tests in Burkholderia cepacia
BCRC 14253 compost, showed that PLA can be completely degraded by this bacterium.
The photodegradation process was investigated by Tsuji et al. 2006 for some materials made
of PLA by using gel permeation chromatography, differential scanning calorimetry, tensile
testing, and polarization optical microscopy methods.
UV penetration into the specimens had no significant reduction effect on its intensity
(irrespective of the chemical structure and the crystallinity of biodegradable polyesters).
Although PLLA chains are photodegradable even in the crystalline regions, their
photodegradability of amorphous regions is lower. The significant increase in weight-average
molecular weight (Mw)/number-average molecular weight (Mn) was observed for PLLA-A
films, even there was small decrease in Mn by UV irradiation. Anyway, most of PLLA films
tensile properties of PLLA remain constant during UV irradiation.
1.5.6. PLA Biodegradation Mechanism in Compost
Iovino et al. 2008 used standard test methods for evaluating a composite aerobic
biodegradation.
Changes at different incubation times, confirmed by thermal properties‘ and SEM
micrographs, showed that the formation of patterns and cracks on the material surface aged
in the compost is an evidence of a significant loss of structure.
Biodegradation is caused by biological activity, especially by enzymatic action, leading to a
significant change in the chemical structure of the exposed material and resulting in the
production of carbon dioxide, water, mineral salts (mineralization) and new microbial
cellular constituents (biomass). It can occur by using two different conditions: aerobic in the
presence of oxygen and anaerobic with no oxygen available as Grima et al. (2000) reported.
From this research, the most productive phase for PLA mineralization occurred from 12 to
50 day (d) incubation. In addition, the PLA degradation was about 55.5% of its theoretical
carbon dioxide production, with a carbon content of 54.6 wt % in PLA. So this polymer was
degraded more easily for the presence of water inside the fibres.
Heterochain polymers, particularly those containing oxygen and/or nitrogen atoms in the
main chain, are generally susceptible to hydrolysis. For hydrolysis to occur, the polymer
must contain hydrolytically unstable bonds, such as ester, amide, or urethane, and it must
Chen Haiyan PhD Thesis
- 32 -
show some degree of hydrophilicity. In addition, the hydrolysis rate of the polymer is
affected by properties such as molecular weight, glass transition temperature, and
crystallinity and also hydrolysis conditions such as pH, temperature, and the presence of
enzymes and microorganisms. The hydrolysis of PLA polymers has been widely studied both
in vivo and in vitro. Hydrolytic degradation of poly (DL- and L-lactic acids) proceeds by
random hydrolytic chain scission of the ester linkages, eventually producing the monomeric
lactic acid. The mechanism by which PLA polymer degrade depends on the biological
environment to which it is exposed. In mammalian bodies, PLA is initially degraded by
hydrolysis and its oligomers are metabolized or mineralized by cells and enzymes. Abiotic
hydrolysis is known to participate at the initial stage of microbial biodegradation of PLA in
nature. However, the degradation rate has been shown to increase in the compost
environment in the presence of an active microbial community compared to the abiotic
hydrolysis (Hakkarainen et al. 2000).
Teramoto et al. 2004 gave another explanation for PLA degradation that could imply the
improvement of the interface interaction between matrix and fibre due to the presence of
maleic anhydride, therefore inhibiting water or microorganism penetration within polymers.
The decrease in melting temperature could be attributed to the gradual reduction of
polymeric chains with an increasing exposure time in the composting environment.
In the enzymatic PLA degradation mechanism (Ohkita et al. 2006), a surface erosion rather
than a non-specific inner degradation for unchanged in molecular weight by enzymatic
degradation. The mechanical properties loss after degradation was confirmed.
In neutral or alkaline medium the observed degradation for lactic acid oligomers, may be
explained by intramolecular trans-esterification, also called back-biting (De Jong et al.
2001).
Nucleophilic attack of the hydroxyl end group on the second carbonyl group leads to the
formation of a stable six-membered ring as an intermediate. This reaction is base-catalyzed,
since a base can interact with the hydroxyl end group, thereby increasing the nucleophilicity
of the oxygen atom (Fig. 1.11).
As evidence for the participation of the end group in the degradation, the hydroxyl end group
of lactic acid oligomer was modified by reaction with succinic anhydride to yield lactic acid
oligomer with a carboxylic acid end group. The degradation samples at pH 7 were analyzed
with MS and compared with the mass spectra of the degradation sample of unmodified lactic
acid oligomers at the same time points. In the studied time frame of 15 days, no significant
degradation of the lact-SA was observed, whereas the unmodified lactic acid oligomer was
almost completely degraded, showing the importance of the hydroxyl end group of the lactic
acid oligomer for hydrolytic degradation in alkaline medium.
Introduction
- 33 -
Figure 1.11. PLA Mechanism of Hydrolysis in Alkaline Environment (A) and Acid
Environment (B).
The preferential cleavage of the ester bond at the terminal hydroxyl end of the oligomer at
low pH can be explained as follows: the degradation is initiated by protonation of the OH
end group, followed by formation of an intra-molecular hydrogen bridge. Of all possible
intermediate structures, the five-membered ring is the most stable one (Fig. 1.10B). The
electrophilicity of the carbonyl group increased by hydrogen bridge formation and attack of a
water molecule at that site is therefore preferred. Lactic acid will be split off leaving lactic
acid oligomer with a DP of one unit less than the starting compound.
So under both acidic and basic conditions, the different ester groups in lactic acid oligomers
do not have the same susceptibility for hydrolysis. This means that the hydrolysis of these
oligomers does not proceed randomly as suggested for PLA (and related polymers such as
Chen Haiyan PhD Thesis
- 34 -
PLGA) but that, starting from the terminal hydroxyl group of the oligomer, the first and the
second ester bond are preferentially cleaved under acidic and basic conditions, respectively.
The degradation of bioerodable systems (implants, microspheres) based on PLLA and
PLGA, needs two remarks. First, due to the low concentration of the OH-end group in the
initial degradation phase of these systems, it is not unlikely that initially the hydrolysis
occurs randomly in the polymer chain (Arena et al. 2011). However, when the degradation
proceeds, the number of end groups increases, whereby the OH-end group-catalyzed
hydrolysis, as suggested here, might have an increasing contribution to the overall
degradation occurring in bioerodable systems.
Second, it has been demonstrated that within the PLLA and PLGA matrices the pH decreases
with increasing degradation. This is ascribed to the increasing number of COOH groups as
well as to the accumulation of water soluble, low molecular weight degradation products
inside these matrices.
Obviously, the fact that PLLA and PLGA matrices fully degrade when placed in an aqueous
environment suggests that the increase in hydrophilicity contributes more to the overall
degradation process than the decrease in pH.
1.5.7. The Role of the Organic Filler on the Biodegradation Behavior and Final Properties
of PHAs Composites.
Although biodegradable polymers have good biodegradability and biocompatibility, their
mechanical and thermal properties as thermoplastic elastomer, such as shock absorbance,
impact strength, tensile strength and thermal resistance, remain inadequate. Therefore, there
has been much interest in modifying their properties by the synthesis and/or modification of
polymer structure (Todo et al. 2007) that are time-consumable and/or uneconomical for the
production of plastic items made by these novel biodegradable polymers.
A solution suitable to improve the polymer biodegradation propensity and the material
mechanical properties is constituted by the blending with organic fillers. Depending on the
property requirement required for different applications, PHAs can be either blended, surface
modified or grafted with other polymers; enzymes or inorganic materials with the aim to
improve their mechanical properties and their biodegradation propensity (Doy et al. 1995,
Rezwan et al. 2006).
Biodegradable polymers including poly-saccharides and proteins can be inserted in
polymeric matrices as reinforcement. The same role is played by a variety of bio-fibers such
as lignocellulosic ones which are described in many research articles and reviews (Reis et al.
1996, Mohanty et al. 2000, Jandas et al. 2012).
Advantages of biofibres over traditional reinforcing materials such as glass fibres, talc and
mica are low cost, low density, high toughness, acceptable specific strength properties,
reduced tool wear, reduced dermal and respiratory irritation, good thermal properties, ease of
separation, enhanced energy recovery and biodegradability. The main drawback is their
hydrophilic nature which lowers the compatibility with hydrophobic polymeric matrix during
composite fabrications. The other disadvantage is the relatively low processing temperature
required due to the possibility of fibre degradation and/or the possibility of volatile emissions
that could affect composite properties. The processing temperatures for most of the biofibres
Introduction
- 35 -
are thus limited to about 200°C, although it is possible to use higher temperatures for short
periods (Mohanty et al. 2000).
Many composite materials are difficult to remove after the end of life time, as the
components are closely interconnected, relatively stable and therefore difficult to separate
and recycle. In the modern polymer technology it is a great demand that every material
should especially be adapted to the environment.
By embedding natural reinforcing fibres, (flax, hemp, ramie) into biopolymeric matrix made
of derivatives from cellulose, starch, lactic acid, etc; new fibre reinforced materials called
biocomposites were created and are still being developed (Keller et al. 2003).
Biocomposites consist of biodegradable polymers as continuous matrix and usually biofibres
as reinforcing element. Since both components are biodegradable, the composite as the
integral part is also expected to be biodegradable. Biofibres, i. e., natural polymers, are
generally biodegradable but they do not possess the necessary thermal and mechanical
properties desirable for engineering plastics. On the other hand, the best engineered plastics
are obtained from synthetic polymers, but they are non-biodegradable. A lot of R&D work
has been carried out on biofibre reinforced synthetic polymers. The composites of natural
fibres and non-biodegradable synthetic polymers may offer a new class of materials but are
not completely biodegradable.
The biofibres derived from annually renewable resources, as reinforcing fibres in both
thermoplastic and thermoset matrix composites provide positive environmental benefits with
respect to ultimate disposability and raw material utilization (Mohanty et al. 2000).
1.5.7.1. PHAs-Cellulose Derivatives Blends and Composites
Bourban et al. 1997 developed a biodegradable composite consisting of a degradable
continuous cellulosic fiber and a degradable matrix PHBV (HV19% mol) obtained by
impregnating the cellulosic fibers on-line with PHB/V powder in a fluidization chamber.
PHB/V-regenerated cellulosic fibers composite showed promising mechanical properties,
thus the cellulosic fibers significantly increased the stiffness and strength of the PHB/V
matrix while maintaining the biodegradability of this material.
Most of the natural fibers consist of single fiber packages, so called ‗fiber bundles‘ where the
cellulose is embedded in lignin which functions as a kind of matrix. Therefore, a natural fiber
(fiber bundle) can be considered as a naturally occurring composite.
Furthermore, the fiber properties differ depending on the fiber geometry. Moreover, due to
the varying chemical composition of natural fibers (cellulose, hemicellulose, lignin, pectin),
the orientation of the cellulose and the different structural defects along the fiber or the
fiber/matrix inter-phase, decrease consequently the composite mechanical properties
(Bledzki et al. 2010).
The higher aspect ratio (fiber length/fiber diameter; L/D) of the fine cellulose fibers may be
also the cause for a greater strength in the composite. For that reason, the stiffness of bio-
composites with man-made cellulose fiber is partially deteriorated compared to composites
with natural fibers that show a higher strength (Bledzki et al. 2010).
The incorporation of fibrous reinforcement causes a decrease in polymer chains mobility, as
shown by DMA analysis. PLA-based composites storage modulus remained much higher
than of un-reinforced PLA. The glass transition temperature derived from loss modulus
Chen Haiyan PhD Thesis
- 36 -
showed a slight shift to higher temperatures, if compared to matrix polymer. SEM
photographs showed fiber pull-outs from the polymer matrix: this is due to the surface
roughness, which is very smooth with regenerated cellulose. The adhesion was not strong in
any of the composites. The fiber orientation was analyzed via optical microscopy (Bledzki et
al. 2009).
Polylactic acid (PLA) nanocomposites were prepared using Cellulose NanoWhiskers
(CNWS) as a reinforcing element in order to assess the role of this filler in reducing the gas
and vapour permeability of the bio-polyester matrix. The crystallinity value and the fiber
dispersion in the polymer matrix, are connected with the CNWS treatment (solution casting,
acid hydrolysis, freeze-drying) as showed by TEM results.
From the DSC analysis, melting point and crystallinity increased with increasing CNWS
loading hence suggesting a filler-induced crystallinity development. The heat of fusion
seemed to increase slightly in the highly amorphous PLA bio-composites (Sanchez-Garcia et
al. 2008). From TGA results, it was concluded that the addition of low fractions of CNWS in
PLA matrix did not alter the matrix thermal degradation.
PLA nano-composites water permeability decreased with the freeze drying CNW addition by
up to 82% and the oxygen permeability by up to 90%: an optimum barrier enhancement was
found for composites containing loadings of CNWS below 3 wt% (Sanchez-Garcia et al
2010a).
The lowest water permeability was probably due to the high nano-dispersion of the
nanowhiskers across the matrix and the high crystallinity, the good interfacial adhesion and
dispersed morphology was seen in these nanobiocomposites (Sanchez-Garcia et al 2010a,
Sanchez-Garcia et al 2010b). The mechanical performance was evaluated lower than that of
neat PLA: this observation was ascribed to both the filler ranged screened being below the
percolation threshold and most importantly to filler-induced plasticization by sorbed
moisture. So CNWS exhibit novel significant potential in coatings, membranes and food
agro-based packaging applications (Sanchez-Garcia et al 2010a).
The plasticizing and compatibilizing action for nano-structured cellulose fibres and their
esters (Takatani et al. 2008), was demonstrated by the mechanical properties improvement,
when the fibres were added to the polymer in a concentration of 5% by weight. The
nanocomposite showed better barrier properties than pure PLA, being minor the free volume
that can be occupied by adsorbed water molecole, becouse during nucleation, the formation
of crystals (Sanchez-Garcia 2010).
1.5.7.2. PHA-Natural Fiber Composites
Many researchers (Zini et al. 2007, Shanks et al. 2004) investigated composites consisting of
a bacterial co-polyesters such as PHBHHx, and PHBV with 5% and 12% mol HV loaded
with flax fibers. A satisfactory reinforcing effect was observed in composites prepared by
compression molding and using long fiber mats (long fiber composites, LFC). The long flax
fibers successfully reinforced the bacterial PHBHHx copolyester. Surface acetylation or a
silane coupling agent employment is suitable for promoting fiber–matrix adhesion, thus
improving the mechanical properties of short fiber composites. The crystallization kinetics of
Introduction
- 37 -
PHBHHx is accelerated in the composite by the presence of fibers. The melting temperature
was influenced by the promoted adhesion and copolymerization. The bending modulus was
increased in the composites and DMA provided storage modulus of as much as 4 GPa at
25oC, with a smaller component as the loss modulus.
An earlier study showed that flax and P (3HB) had good interfacial adhesion, which was
decreased when plasticizers were present (Wong et al. 2002). Some plasticizer migrated from
the flax to the PHB and caused complex changes in the glass transition, crystallization and
crystallinity of the PHB.
The thermal and mechanical behavior of biotechnological polyester PHBV reinforced with
wheat straw fibers were reported by Avella et al. 2000. In order to improve the chemico-
physical interactions between the components, the reinforcing agent has previously been
submitted to treatment with high temperature steam, leading to fibers richer in cellulose and
more reactive.
The addition of straw fibers has been found to increase the rate of PHBV crystallization,
while it does not affect the crystallinity content. Furthermore, the wheat straw/PHBV based
composites showed higher Young's modulus and lower values of both stress and strain at
break than the neat PHBV matrix.
It was observed that the presence of straw did not affect the biodegradation rate evaluated in
liquid environments and in long term soil burial tests. In the composting simulation test, the
rate of biodegradation is reduced for composites with more than 10% straw content. The
morphology of the composites has also been investigated and correlated to the
biodegradation process.
Lignocellulosic fractions from wheat straw as natural fillers in loading composites of a
biodegradable polyester (poly(butylene adipate-co-terephthalate) (Le Digabel et al. 2004)
showing a reinforcing effect of these residues.
Bio-composites based on jute fibers and blends of plasticized starch and PHB were
investigated by Belhassen et al. 2009. Different amounts of glycerol and aliphatic polyesters
PHB have been added to native starch to obtain a processable biodegradable matrix. In the
same way natural jute fibers up to 30 wt.% loading were added to improve the mechanical
and thermal stability of the material. Significant enhancement in the mechanical properties
and water sensitivity were noticed by the addition of 8 wt % PHB.
The addition of jute strands to the starch-based polymer matrix leaded to a material with
higher capacities to support stresses keeping them even after 1.000 h of exposition under
humid environment. The addition of the fibers up to 30 wt. % content brings about an
enhancement in the strength and modulus of the material as much higher as the fibers loading
is important. This decrease in water sensibility and improvement in mechanical resistance
leads to a useful material in the field of packaging with the capacity of biodegradation after
working life.
PLA is a crystalline biodegradable polymer that has poor processing properties such as poor
impact strength, low heat distortion temperature, poor processability and relatively high cost
(Li et al. 2010). Copolymers of L-lactic acid and glycolic acid (PLGA) are frequently used in
biomedical applications to enable tailoring of flexibility and degradation rate.
Chen Haiyan PhD Thesis
- 38 -
A study on the PLA blending with soy flour (SF), wood flour (WF) and sodium bisulfite-
modified SF that was used for improving the PLA adhesion, is present in literature. The
coupling agent was methylenediphenyl diisocyanate (MDI) (0.5 wt. %). Mechanical and
thermal properties, morphology and relaxation characteristics of the blends were investigated
and the correlated results showed that MDI was an effective coupling agent for the WF/PLA
system in improving tensile strength and elongation. DSC results indicated that SF and
modified SF acted as nucleation agents and facilitated the PLA crystallization behaviour by
increasing the crystallinity percentage. Mechanical relaxation behaviors were well
characterized on the basis of DMA results. PLA and its blends exhibited highly
homogeneous relaxational dynamics in their transition from glass to liquid during heating
because of the high degree of hydrophobicity and densification effects of PLA, SF and MSF
(Li et al. 2010).
PLA biocomposites with abaca fibres were processed by using combined moulding
technology that were two-step extrusion coating process and consecutively injection
moulding.
The abaca fibres (30 wt. %) reinforcement effect enhanced E-Modulus, tensile strength and
the Charpy A-notch impact resistance for PLA/abaca based composites.
Abaca fibre causes in general better stiffness than man-made cellulose, while in comparison
to un-reinforced polymer; this natural material improves mechanical characteristics. Also the
physical bonding to the matrix, due to fibre surface roughness, seemed to have improvements
by using abaca fibres instead of manmade cellulose ones. Reinforcing PLA with natural
fibres (jute and abaca) led to better chemical bonding on the inter-phase as for PP composites
without coupling agent and the desired mechanical performances were obtained and analysed
by using tensile and impact tests.
The reinforcement promoted by fibres increased the tensile stiffness and strength
significantly; however, depending on the fibre type, different improvements of the
mechanical parameters were achieved. Within the natural fibre group, jute seems to achieve
the highest improvement (up to 30% in PLA composites). The obvious reinforcing effect is
caused by the fibre performance. SEM was carried out to study the fibre–matrix inter-phasial
adhesion. The fibre-size distribution was determined using optical microscopy and the
obtained results were compared to composites on PP basis with the same reinforcing fibres.
The broadest fibre-size distribution can be found in abaca composites.
Considering the fibre bundle diameter, the abaca fibre is characterised by a higher average
value compared to jute one. An increasing in the fibre diameter affects the aspect ratio and,
thus, decreases the mechanical performance of the composites. Jute fibre bundles undergoes
to separation during processing, allowing a better distribution and a favourable diameter,
which can be seen in the results of fibre-size distribution. Moreover, the critical fibre length
of abaca is much higher and the aspect ratio (LD) lower than those of jute and man-made
cellulose. Amongst others, this is the reason for deteriorated mechanical parameters of abaca
composites (Bledzki et al. 2010).
PLA/cotton composites can be reinforced by using lignin that improved the cotton fibres and
PLA adhesion: the relative composites can be compared with PLA/kenaf ones from the
mechanical properties that showed an increase for tensile strength and Young‘s modulus and
Introduction
- 39 -
a decrease for the impact resistance (Nishino et al. 2003). Lignin has also been added to PLA
in order to reduce its flammability, giving performance competitive with commercial
formulations (Reti et al. 2008).
PLA can also be used as a matrix material in composites with natural fibres such as flax as
reinforcement and triacetin as plasticizer for improving neat PLA and PLA/flax based
composites impact properties, rigidity and heat resistance (Oksman et al. 2003, Bax et al.
2008).
A decrease in tensile strength with the increasing of the triacetin content was observed
expecially in PLA/flax composites. The triacetin addition showed a positive effect on the
elongation at break values for neat PLA and PLA/flax based composites. The highest
triacetin addition (15%) clearly showed a negative effect for PLA/flax based composites,
strongly decreasing their stress and stiffness values.
The microscopy study of the composite microstructure showed poor adhesion between the
fibres and PLA matrix. The flax fibres were well dispersed in the PLA matrix and they are
separated in single fibres due to the compounding process. PLA thermal properties, which
are a drawback for PLA, were improved with an addition of flax fibres (Oksman et al. 2003).
Agricultural co-products of the alternative oilseed crops, cuphea (C), lesquerella (L) and
milkweed (MPLA and various levels of co-product (0–45%, w/w) derived from alternative
oilseed crops, were compounded by twin-screw extrusion and injection molded with PLA
polymer for adjusting the desired mechanical properties. As co-product content increased,
tensile strength for all PLA composites decreases. PLA-C exhibited increased stiffness, while
the modulus of PLA-M and PLA-L decreased slightly. So, PLA-M showed extensive stress-
cracking under tensile stress and exhibited an elongation value 50–200% greater than the
PLA control. Acoustic emission showed ductile behavior of the PLA-M composite
(Finkenstadt et al. 2007).
Some other works (Petinakis et al. 2010, Yu et al. 2006, Wang et al. 2007) were carried out
with the aim to test the effect of hydrophilic fillers (starch and wood-flour) on the
degradation and the decomposition of PLA based materials was investigated. Both starch and
wood-flour accelerated thermal decomposition of PLA starch exhibited a greater impact than
wood-flour. The PLA decomposition temperature was decreased from about 397 °C to 352
°C when the starch content was increased to 40% by weight. In the case of the wood-flour
component, the decomposition peak of PLA decreased to about 362 °C. Small polar
molecules may have been produced during decomposition of starch and wood-flour (Yu et
al. 2006).
The wood flour use in PLA based composite materials makes better their tensile strength and
elongation at break values, whereas the wood soy plays a role of nucleant agent, facilitating
PLA crystallization and increasing its percentage (Li et al. 2010, Perego et al. 1996).
The wood flour eliminates PLA isothermal crystallization, thus its fibres being characterizing
by major fibres dimensions than soy ones, PLA crystallites formation resulted inhibited. The
chains mobility makes difficult the crystals growth (Li et al. 2010).
Biobased and biodegradable polylactide (PLA)-pine wood flour (PWF) based composites
were investigated (Pilla et al. 2010) as a means to reduce the overall material cost and tailor
the material properties. The tensile modulus of the PLA-PWF composites increased with the
PWF content whereas the toughness and strain-at-break values decreased. The tensile
Chen Haiyan PhD Thesis
- 40 -
strength remained the same irrespective of the PWF content (up to 40%), while the degree of
cristallinity showed a significant increment.
1.5.7.3. PHAs Lignin Blends and Composites
Lignin is primarily a structural material to add strength and rigidity to cell walls and it
constitutes between 15 wt% and 40 wt% of the dry matter of woody plants. Lignin is more
resistant to most forms of biological attack than cellulose and other structural
polysaccharides. In vitro, lignin and lignin extracts have been shown to have antimicrobial
and antifungal activity, it acts as antioxidant, it absorbs UV radiation, and it exhibits flame-
retardant properties.
Lignin is a cross-linked macromolecular material based on a phenylpropanoid monomer
structure. Typical molecular masses of isolated lignin are in the range of 1000–20,000 g/mol,
but the degree of polymerization in nature is difficult to measure, since lignin is invariably
fragmented during extraction and it consists of several types of substructures which repeat in
an apparently random manner. Blending of PHA with lignin is one possible strategy for
overcoming the mechanical disadvantages of PHA.
Thermoplastic blends of several biodegradable polymers with organosolv lignin and
organosolv lignin ester based on both solvent casting and melt processing, were investigated
by Ghosh et al. 2000.
An addition of up to 20 wt% lignin to PHB gives improvements for Tg, melting point,
Young‘s modulus, and the degree of crystallinity. The addition of lignin reduced the
crystallinity of PHB more than addition of lignin butyrate, suggesting greater compatibility
of PHB with lignin than lignin butyrate.
The effect of 1 wt% lignin on the nucleation of PHB by studying the kinetics of both
isothermal and nonisothermal P(3HB) crystallization, was investigated by Weihua et al.
2004. DSC results showed that not only lignin act as a nucleating agent, decreasing the
activation energy of crystallization, but it reduced the size of the spherulites to give a less
brittle material.
The nucleant agents addition permits the control of crystallization rate for PLA, so its final
cristallinity and the optimization for the processing conditions in the injection process can
reached better mechanical properties that reflect an increment for tensile strength and
material module (Harris 2008, Yu et al. 2012).
The miscibility, between PHB and bagasse soda lignins (having distinct chemical group
functionality) based on the Tg of their blends, was examined by Mousavioun et al. 2010.
The Tg values were higher for the blends obtained from the lignin fraction with an higher
content of xylan and phenolic hydroxyl groups, but lower methoxyl and carboxylic acid
content, implying that the association between lignin and PHB is probably related to the
chemical functionality of the lignin polymer as the molecular weights of these lignin
fractions are similar, approximately 2400 g/mol. In fact it was shown by FTIR that the
miscibility between PHB and soda lignin was due to hydrogen bond formation between the
carbonyl group of PHB and the phenol hydroxyl group of lignin.
The major drawback connected with PLA applications, is constitued by its high glass
transition temperature (Tg= 60°C) that gives poor processing properties, easy formation of
cracks in based PLA composite materials (Li et al. 2003), low strain at break and high
Introduction
- 41 -
module values (Pillin et al 2006), that are all restrictive features for the PLA use in the rigid
and thermoformed packaging industry.
A strategy employed to decrease the material rigidity is represented by the blending with
organic (lignin) and inorganic fillers or natural fibres such as cotton, wood, Kenaf (Li et al.
2003, Graupner 2008, Li et al. 2010, Bledzki et al. 2009, Bledzki et al. 2010, Sanchez-Garcia
2010, Finkenstadt 2010, Pluta et al. 2002).
The lignin loading in a percentage below 20%, can decrease the finite product price, giving
the biodegradability requisite to thermoplastic polymers (Li et al. 2003).
The lignin shows also an adhesive and strentghing action between ligno-cellulosic fibres
such as kenaf (10-14% of lignin) and the polymeric matrix PLA, as observed from the
increment of the tensile strength (52.88 MPa) for the PLA/Kenaf composite (Graupner
2008), where the structure becomes a multilayer created by the linkages between its inner
layers.
The thermal and mechanical properties of the biodegradable blends of PLLA and lignin
prepared by manual mixing have been investigated. Both the results of DSC and FTIR
spectral analyses indicated the existence of intermolecular interaction between PLLA and
lignin.
Furthermore, FTIR elucidated the existence of an intermolecular hydrogen-bonding
interaction.
The mechanical properties of PLLA/lignin blends showed that the maximum strength and the
elongation at break values for the material decreased whereas the Young‘s modulus
remained almost constant when the lignin content reached 20%. Thermogravimetrical
analysis showed that lignin would accelerate the thermal degradation of PLLA when the
content of lignin was more than 20%. Compared with some other biodegradable polymers,
the blend of PLLA and lignin is thought to be a promising material, because the material
properties, as well as the price, are at an acceptable level when the content of lignin is less
than about 20% (Li et al. 2003).
1.5.8 The Role of the Organic Filler on the Biodegradation Behavior and Final Properties
of Petro-based Polymers Composites (PE, PP, PS)
Biofibers, natural lignocellulosics, have an outstanding potential as reinforcement in
thermoplastics. The preparation of lignocellulosic composites with a good interfacial
adhesion is generated by a combination of fiber and matrix modification and methods. PP
matrix was modified by reacting with maleic anhydride and subsequently bonded to the
surface of the modified lignocellulosic component, in-situ. A silane agent was used as a
surface modifier and the modified fibers are then extruded with the modified polymer matrix
to form the compatibilized composite. Various reactions between the lignocellulosic
fiber/filler and modified polymer chains were performed by Karnani et al. 1997 with the aim
to improve the interfacial adhesion by using the formation of covalent bonds between the
fiber surface and matrix. These composite blends were then injection molded for mechanical
characterization and the results were reported (Karnani et al. 1997).
Composites made by blending ethylene vinyl acetate (EVA) with wood fiber (WF)
(uncompatibilized) and EVA with poly (ethylene-co-glycidyl methacrylate) (EGMA)-WF
(compatibilized), were investigated for the morphology as well as mechanical, thermal, O2
permeability, and water absorption properties.
Chen Haiyan PhD Thesis
- 42 -
The results showed that there is a weak interaction between EVA and WF able to confere
poor properties to the obtained composites. The presence of a compatibilizer such as EGMA
improved
the mechanical properties with the increase of EGMA content, whereas thermal stability,
oxygen permeability and water absorption showed a decrement. The compatibilizer becomes
chemically bonded to the hydrophyllic WF, and it makes easier the wetting of the
hydrophobic polymer chain. (Dikobe et al.2007).
Natural fibers, used as fillers and reinforcement for polymers, represent one of the fastest-
growing types of polymer additives (Czvikovszky et al. 1996, Bengtsson et al. 2005). In
some studies, biobased composites are formulated from a blend of natural fibers, including
cane fibers, bamboo, oat, kenaf, hemp, flax, jute and sisal, wood fiber (WF), and
thermoplastic polymers, such as polypropylene and polyesters.
The obtained composites resulted stronger, stiffer, and light-weight, because the natural filler
plays a role of reinforcement agent for the matrix.
The structure-property relationship between wood flake- high density polyethylene (HDPE)
based composites was investigated in relation to the matrix agent melt flow behavior and
processing technique (Balasuriya et al. 2001). The flake distribution and flake wetting were
optimized with the aim to obtain better mechanical properties, as evidenced by impact
strength values.
The polymer matrix provides an environment for the fibers and it protects them from
scratches that might cause them to fracture under low stress. The fibrous filler adds strength
to the more fragile polymer material by shouldering much of the stress that was transferred
from the polymer to the fiber through their strong interfacial bonds (Balasuriya et al. 2001).
Different particle sizes can be used to produce composites with different properties
depending on their distribution. The resulting WF–polymer composites have high specific
mechanical properties (Selke et al. 2004).
The mechanical properties of compression-moulded polystyrenes loaded with sawdust wood
residue of softwood and hardwood species, with different particle size distribution, were
investigated by Maldas et al. 1988. The tensile modulus at 0.1% strain and the tensile
strength, elongation and energy at the yield point are reported. Moreover, to improve the
compatibility of the wood fibres with the polymer matrices, different treatments (e.g. graft
copolymerization) and coupling agents (e.g. silanes and isocyanates at various
concentrations) were also used. The extent of the improvement in mechanical properties
depends on the fibre loading, on the particle size of the fiber, on the concentration and
chemical structure of the coupling agents, and on whether special treatments (e.g. coating or
grafting of the fibre). The mechanical properties of the composites are improved up to 30%
in the case of fibres having a mesh size 60 and when up to 3% of isocyanates was used
(Maldas et al. 1988).
Different chemical substances have been used as compatibilizers of wood polymer
composites by various researchers.
To improve the compatibility between the WF and the LLDPE matrix, Liao et al. 1997
treated the WF with titanate coupling agents or grafted it with acrylonitrile. Both treatments
Introduction
- 43 -
resulted in an improvement of the mechanical properties for the composites compared with
the same ones loaded with the untreated WF.
The same results were also observed for the WF-PS based composites loaded with coupling
agents (e.g., silanes and isocyanates at various concentrations) that showed a compatibilizing
effect.
Another drawback is the high moisture absorption of the WFs. Moisture absorption can lead
to swelling of the fibers, and concerns on the stability of the fiber composites cannot be
ignored (Tserki et al. 2005). The moisture absorption of the fibers can be minimized by the
encapsulation into the polymer or by adopting chemical modification of some hydroxyl
groups present in the fiber. This second option reflects an increase in the cost of the fiber.
Good fiber-matrix bonding can also decrease the rate and amount of water absorbed by the
composite.
Fibres from pine or eucalyptus wood and also one-year crops such as coir, sisal, etc. are all
good candidates for replacing glass fibres in PP based composites (Espert et al. 2004) even if
the poor resistance towards water absorption is one of the drawbacks of these natural
composites materials.
A decrease in tensile properties, such as lower values of Young‘s modulus and stress at
maximum load was demonstrated, showing a great loss in mechanical properties of the
water-saturated samples compared to the dry samples. The morphology change was
monitored by scanning electron microscopy analysis before and after exposure to water and
the devastating effect of water on the fibre structure was shown.
Espert et al (2004) reported that WF-PP composites, without compatibilizer, show
mechanical properties dramatically affected by water absorption.
The ethylene vinyl acetate (EVA) acts a role of compatibilizer, decreasing the adsorbed
water amount (Espert et al. 2004): the adhesion to the PP matrix, and vinyl acetate could
bond be connected to its acetate groups to the hydroxyl groups on the fibres.
Elvy et al. 1995 reported that the usage of coupling agents such as vinyltriacetoxysilane,
before impregnation with MMA in order to evaluate the effects of the silane coupling agent
on the physical properties of wood-polymer composites. A decreasing for the strand between
the polymer and the cell wall of the wood connected with a reduction in water absorption
were reported.
Very little has been reported on EVA-natural fiber composites. Malunka et al (2006)
investigated EVA–sisal fiber composites in the absence and presence of dicumyl peroxide
(DCP). This oxo-polyethylene is able to initiate crosslinking, being effective in grafting EVA
to sisal fiber and creating composites with better physical properties.
Sedlakova et al 2001 analyzed the role of poly (ethylene-co-methacrylic acid) copolymer
(EMAA) as compatibilizer loaded into low-density polyethylene (LDPE) and wood flour
based composites. Both mechanical and dynamic mechanical properties showed that EMAA
is able to promote better interactions between LDPE and WF. A high content of WF and low
content of EMAA in the system yield materials with high modulus and high tensile strength.
Polymer blending is an effective way to obtain materials with specific properties. Most
polymers are immiscible, therefore, blending them, it is possible to obtain heterogeneous
morphologies.
Chen Haiyan PhD Thesis
- 44 -
Immiscible blends have quite lower mechanical properties than those of their components, so
methods to improve adhesion between two immiscible blends, have been a subject of
considerable research activities (Xanthos et al. 1991). When the copolymers may be added
separately or formed in situ by reactive processing, it is supposed that the chemical reaction
between the components inside the blend, may cause an interfacial tension able to decrease
the adhesion force at the interface. A variety of reactive copolymers have been identified as
effective compatibilizers in earlier literatures (Xanthos et al. 1991).
Natural organic fillers such as wood fiber have traditionally composed a small percentage of
the filler market for thermoplastics when compared to mineral or glass-fiber reinforcements.
These fibres (Ton-That et al. 2009) offer many advantages such as (i) low density, (ii) high
strength and modulus values, (iii) renewable nature, and (iv) less breakdown of the fiber
during mixing than the commonly used inorganic reinforced fibers. The main problem that
occurs by using the wood fiber – thermoplastic composites is constituted by the poor
interfacial adhesion between the hydrophobic polymer matrix and the hydrophilic wood
fiber. This can be solved by adopting chemical modifications on the wood fiber surface, e.g.,
grafting of a short-chain molecule onto the wood fiber surface as well as using various
coupling agents / adhesion-promoting agents such as stearic acid and maleated propylene
wax. Moreover, the method of preparation for the composites also affects the ultimate
properties of these latter.
From the previous work, the physical and mechanical properties of wood may be improved
by preparing composites of wood with vinyl monomers. However, since most vinyl
monomers are non-polar, there is a little interaction between them and the hydroxyl groups
of the cellulose fibres. Therefore the components inside the wood polymer composite (WPC)
simply bulks the wood structure by filling the capillaries, vessels and other void spaces
within the wood. It can be deduced that if the bonding were placed between the impregnated
polymers and the hydroxyl groups on the cellulose fibers, the physical properties of WPC
may be further improved (Elvy et al. 1995) .
The interfacial adhesion between the wood fiber treated with two different titanate coupling
agents and grafted acrylonitrile loaded into LLDPE matrix, was investigated (Liao et al.
1997).
The results showed a higher ratio of grafting for the untreated fibers compared to the pure
ones, as observed from SEM analysis.
LLDPE loaded with the untreated wood fibers showed more fibers pullout from the matrix
during the fracture, whereas the grafting modification made the fiber easily deformable and it
enhanced fiber adhesion at the interface. The failure of the material was caused by fiber
fracture rather than by fiber pullout from the matrix.
The wood fibers grafted with acrylonitrile or filled with a titanate based agent were loaded
into LLDPE matrix. The tensile strength and elongation at break values, recorded for the
treated composites, showed an increment with the increasing in the grafting ratio for the
wood fiber. The modulus was not much affected by the fiber treatment and it was dependent
primarily on the wood fiber concentration in the material.
Introduction
- 45 -
1.5.9. The Role of the Inorganic Filler on the Biodegradation Behavior and Final
Properties of PHAs
Some recent developments in the nano-biocomposites area for bio-based packaging
constitute the potential for the nano-fillers in the food packaging sector. The addition of
different types of clays, bio-fibers and their nanowhiskers, carbon nanotubes and carbon
nano-fibers to biopolyester matrices (PLA, PCL, PHB and PHBV) led not only to barrier
improvement but also to obtain novel functionalities such as UV and Visible protection and
to control the release of antimicrobial substances.
PHAs based composites mechanical properties can be improved also by adding epoxy chain
extenders, which maintain or increment the molecular weight at the polymer processing
temperatures, at which depolymeraization or chain scission reactions can occur, being
responsible of the viscosity and elasticity lack for the melt and of the material thermal and
mechanical properties (Pilla et al. 2009).
Lim et al. 2007 prepared hydrophobically modified silica hybrid composites based on
biodegradable PHBHHx using simple melt compounding and they investigated the effect of
hydrogen bonding on the crystallization behavior of the composites. The intermolecular
hydrogen bonding between PHBHHx and silica increased gradually with the increase of
silica content. The silica reduced the non-isothermal and isothermal crystallization rates of
PHBHHx in the hybrids, and these were ordered by the strength of intermolecular hydrogen
bonding between the PHBHHx and silica.
Recently, the utility of inorganic nanoparticles as additives to enhance the polymer
performance has been established. Various nanoreinforcements currently being developed
are nanoclay (layered silicates), cellulose nanowhiskers, ultra fine layered titanate, and
carbon nanotubes (CNs). Of particular interest are polymer and Organically Modified
Layered Silicate (OMLS) nanocomposites because of their demonstrated significant
enhancement, relative to an unmodified polymer resin, of a large number of physical
properties, including barrier, flammability resistance, thermal and environmental stability,
solvent uptake, and rate of biodegradability of biodegradable polymers (Ray et al. 2003). The
main reason for these improved properties in polymer/layered silicate nanocomposites is the
strong interfacial interactions between matrix and OMLS as opposed to conventional
composites (Ray et al. 1995, Chen et al. 2002 259, Chouzouri et al. 2007).
Maiti et al. 2003 reported the first preparation of PHB/OMLS nanocomposites (PHBCNs) by
melt intercalation method by using three different kinds of OMLS.
XRD patterns clearly showed the formation of well-ordered intercalated nanocomposites,
whereas TEM image of PHBCNs also supported the formation of the intercalated structure.
The fate of the polymer after nanocomposites preparation was measured by GPC. The
nanocomposites based on organically modified MMT showed severe degradation but
surprisingly no degradation was found with nanocomposites based on organically modified
fluoromica. There is no explanation how organically modified fluoromica played to protect
the system, but present authors believe presence of Al Lewis acid sites, which catalyze the
hydrolysis of ester linkages at high temperature, may be one of the reasons. The degradation
started just after one week and at the initial stage the weight loss was almost the same for
both PHB and its nanocomposites. Deviation was occurred after three weeks of exposure, but
Chen Haiyan PhD Thesis
- 46 -
degradation tendency of nanocomposites was suppressed. The intercalation of OMLS, inside
the nanocomposites, is able to make slow the biodegradation of PHB polymeric matrix and
to improve the barrier properties of the matrices.
PHB or PHBV clay nanocomposites can be prepared via solvent casting (Lim et al. 2003) or
by solution intercalation methods (Wang et al, 2005). FTIR analyses showed that two distinct
different phases coexisted. The thermal stability of the PHB/OMMT based nanocomposites
was also observed with the increasing of OMMT content. At higher clay contents (>6 wt%),
the nanocomposites degradation rates decreased due to restricted thermal motion of the
polymer chains in the OMMT interlayer. From both XRD and TGA analyses, the
aggregation tendency of OMMT was also found to increase with the OMMT content in these
systems and led to the intercalated structure.
The PHBV based nanocomposites showed a decrease in biodegradtion propensity in soil
suspension, melting temperature and enthalpy of fusion (DHm) increasing the OMMT
amount. It was demonstrated that the small-sized PHBV spherulites were formed, the
crystallinity of PHBV reduced and the range of the processing temperature for the
nanocomposites enlarged by intercalation of OMMT with PHBV. The biodegradability of
PHBV/OMMT based nanocomposites was related to the interaction and adhesion of PHBV
and OMMT, water permeability, degree of crystallinity, and anti-microbial property of
OMMT.
Hablot et al. 2008 reported that PHB enhanced degradation can also be caused by
decomposition products of clay organomodifiers which have a catalyzing effect on the
thermal or thermomechanical degradation. Eventually, the biodegradation studies also
highlighted the difference between montmorillonite and fluoromicas since the initial
degradation rate of PHB with MMT-NH3+(C18) was higher than with fluoromicas.
Choi et al. 2003 described the microstructure as well as the thermal and mechanical
properties of PHBV–organoclay (Cloisite 30B, a monotallow bis-hydroxyethyl ammonium-
modified montmorillonite clay) nanocomposites with a low clay content.
XRD and TEM analyses clearly confirmed that intercalated nanostructures were obtained,
dueing to the strong hydrogen bond interactions between PHBV and the hydroxyl groups of
the C30B organo-modifier.
The nanodispersed organoclay acted as a nucleating agent, increasing the temperature and
rate of PHBV crystallization. Moreover, the DSC thermograms revealed that the crystallite
size was reduced in the presence of nano-dispersed layers since the PHBV melting
temperature are shifted to lower temperatures. Thermogravimetric analyses revealed that the
temperature corresponding to 3% of weight loss increased with C30B content (+10◦C with 3
wt% of filler).
They explained these trends by the nanodispersion of the silicate layers into the matrix and
thus concluding that the well-dispersed and layered structure accounts for an efficient barrier
to the permeation of oxygen and combustion gas. Eventually, the mechanical properties
showed that clays can also act as an effective reinforcing agent since the Young‘s modulus
value significantly increases from 480 to more than 790 MPa due to strong hydrogen
bonding between PHBV and C30B.
Introduction
- 47 -
As clay organo-modifiers, also ammonium surfactants can be used, as suggested by Bordes
et al. 2009, which investigated the clay effect on thermal and thermo-mechanical degradation
of two PHBV grades and the neat PHB. The PHBV thermal degradation studies, with and
without quaternary ammonium cations, based on Tg data showed that all surfactants have an
effect on the polymer degradation. This effect is more pronounced when the initial Mw of
the polymer is low. The results regarding the thermal stability in the presence of surfactants
led to two additional statements: (i) the degradation mechanisms of both the purified PHBV
and the surfactant in the blend are interdependent, (ii) S-Alk and S-Bz appear to influence
PHBV thermal degradation the most. All these conclusions are totally in agreement with the
results obtained for PHB. The thermo-mechanical study has led to the same conclusions
regarding the effect of surfactants since the mechanical energy, and thus the viscosity, is
higher for neat PHBV. Moreover, according to the Mw values of PHA after processing, S-Bz
appears to be the most degrading surfactant. In addition to the molecular weight decrease, the
recorded low torque values could also be explained by a lubricating action of the surfactants
and/or of their degradation by-products.
PHBV processing with three-layered clay types using different mixing methods was
examined by Cabedo et al. 2009, with the aim to detect the effect of processing time, clay
type and content on polymer molecular weight and composite morphology. PHBV molecular
weight (Mw) decreased by 38% after extrusion processing and was further reduced in the
presence of montmorillonite (MMT). When PHBV was processed with kaolinite as additive,
no further reduction in polymer molecular weight was observed. Molecular weight decreased
as the MMT clay content increased from 1 to 5 wt %.
The results suggested that the release of tightly bound water from clay surfaces at high
temperatures may be responsible for PHBV degradation during processing. Evidence also
points to the possibility that the surface modifier present in organically modified MMT may
catalyze PHBV degradation in some way. X-ray diffraction studies indicated an intercalated
morphology in the presence of modified MMT but good dispersion was also achieved when
unmodified kaolinite was blended with PHBV. They concluded that the intercalated
morphology was found to be predominant when PHBV/MMT clay nanocomposites were
obtained either by solvent casting or melt mixing. Sub-micron aggregates were obtained
when the mixing method is the melt blending with unmodified kaolinite.
A nano-composite based on PLA and a layered silicate was prepared by adding trimethyl
octadecylammonium cation, an organically modified layered silicate (OMLS). WAXD and
TEM analyses confirmed that montmorillonite silicate layers were intercalated and nicely
distributed in the PLA-matrix. The neat PLA material properties improved remarkably after
nano-composite preparation. The neat PLA biodegradability and the corresponding nano-
composite one were studied under compost, and the rate of biodegradation of neat PLA
increased significantly after nano-composite preparation (Sorrentino et al. 2007, Sinha Ray et
al. 2002b).
Excellent yielding results for PLA/organically modified synthetic fluorine mica (OMSFM)
nano-composites, were obtained by adding synthetic fluorine mica (SFM), modified with N-
(coco alkyl)-N,N-[bis(2- hydroxyethyl)-N-methylammonium cation, that was nicely
distributed to a nanoscale level (Sanchez-Garcia et al. 2010a). All the nano-composites
Chen Haiyan PhD Thesis
- 48 -
exhibited dramatic improvement in various materials properties such as the rate of
crystallization, mechanical and flexural properties, heat distortion temperature, and O2 gas
permeability, with a simultaneous improvement in biodegradability for neat PLA. When
these composites are disposed of in compost, they can be safely decomposed into CO2 and
H2O through the activity of micro-organisms.
The barrier properties of PLA based nano-composites can also be improved by sinergistic
interactions between the superficial area of the inorganic filler layers and the polymer, that
try origin from intercalation and/or esfoliation of the inorganic structure (Pluta et al. 2002,
Chang et al. 2003, Kasuga et al. 2003).
Inorganic components such as talc or a complex of phosphoric ester combined with
hydrotalcite made better PLA melt crystallization, decreasing the material crystallization
temperature (207°C), thus the spherulites do not increase their dimensions (Urayama et
al.2003).
The gas barrier properties had been shown to improve dramatically upon exfoliation of clay
platelets in a number of polymeric matrixes. The mechanism for the improvement was
attributed to the increase in the tortuosity of the diffusive path for a penetrating molecule. In
agreement with the crystallinity data, which was found to generally increase with increasing
filler content, oxygen but specially water and D-limonene permeability coefficients were
seen to decrease to a significant extent in the bio-composites and an optimum property
balance was found for 5 wt % of clay loading in the biopolymer. Increasing clay content, the
light transmission of these biodegradable bio-composites decreased by up to 90% in the UV
wavelength region due to the specific UV blocking nature of the clay used (Sanchez-Garcia
et al. 2010a, Sinha Ray et al. 2003).
PLA/clay nano-composites loaded with 3 wt% of organo-modified montmorillonite and
PLA/clay micro-composites containing 3 wt% of sodium montmorillonite were prepared by
melt blending. A plasticizer like PEG 1000 (20 %wt.) was used (Yang et al. 2007, Paul et al.
2003).
The nano and micro-composites morphology and thermal properties were investigated
making a comparison with the unfilled PLA. As the polymer matrices of these samples could
be considered amorphous by their thermal histories (and, therefore, transparent), the opacity
of the Na+ montmorillonite-filled composite might have resulted from the light scattering on
the filler particles with their size comparable with the light wavelength. So the transparency
of the other composites suggested good dispersion of nano-clay particles within the polymer
matrices without noticeable agglomeration in areas of size comparable with the wavelength
of light.
The polymer chains intercalation between the alumino-silicates layers and morphological
structure of the filled PLAs were performed with DSC, TGA, XRD, SEC, and POM.
XRD measurements showed a good affinity between the organo-modified clay and the neat
PLA able to form intercalated structure in the nano-composite. The interlayer migration of
poly (ethylene glycol) 1000 plasticizer is mainly provocked by the polarity difference
between the PLA matrix and this type of clay.
DSC and LM analyses showed that the nature of the filler affected the ordering of the PLA
matrix at the molecular and super-molecular levels. According to TGA analysis, PLA based
Introduction
- 49 -
nano-composites exhibited improvement in their thermal stability in air. The significant
increase in thermal stability, even at very low levels of filler, for the nano-composite under
thermo-oxidative conditions suggested a change in the degradation mechanism.
At constant filler level, it appeared that among all the clays studied, the montmorillonite
organo-modified by bis-(2-hydroxyethyl)methyl (hydrogenated tallow alkyl) ammonium
cations brought the greater effect in terms of thermal stability. Increasing the amount of clay
allowed delaying the onset of thermal degradation of the plasticized polymer matrix by using
WAXS and DSC analyses. So a real competition between PEG 1000 and PLA for the
intercalation into the interlayer spacing of the clay exists (Chang et al.2003) as shown by the
morphological analyses (Paul et al. 2003).
A greater degree of disorder, which led to stronger interfacial strength and consequently
higher storage modulus for the organoclay based composites. It appeared that the crystal
network of the polymer contributed to the reinforcement that needed to amorphous
composites with desired properties controlled by the interfacial strength with dispersion of
clays (Chowdhury 2008).
For hybrid films, the tensile properties initially increased but then decreased with the
introduction of more of the inorganic phase. The hybrids ultimate strength increased
remarkably with the organoclay content and it possessed a maximum value for each clay
content loading.
Above the clay loadings corresponding to the ultimate strengths, all the hybrids strength
values started to decrease. Dispersion was very important because failure to disperse could
induce agglomerates. Failure initiated a lot of MMT agglomerates, and this meant that cracks
were initiated on and propagated inside them: a high MMT content led to an agglomeration
of MMT particles, which reduced the tensile strength. The modulus enhancement was
correlated to the resistance exerted by the clay itself and to the orientation and aspect ratio of
the clay layers. Additionally, the stretching resistance of the oriented backbone of the
polymer chain in the gallery also contributed to enhancing the modulus that started to
decrease when the organoclay content was greater than a critical weight percentage. PLA
elongation at break increased with the introduction of an organoclay in high content.
However, a certain organoclay loading corresponded to the maximum value, giving a 31–
41% increase in the elongation at break value. Therefore, it can be concluded that in a certain
organoclay content range, its introduction led to both a strengthening and a toughening for
PLA matrix. A further increase in the organoclay content led to a decrease in the elongation
at break, even though the elongations at break of nano-composites containing 8 wt %
organoclays were still much higher than those of neat PLA. From these results, it appeared
that there was an optimal amount of organoclay needed in a hybrid to achieve the greatest
improvements in its properties that might result from the strong interfacial interaction
between PLA and the organoclay (Chang et al. 2003).
Organophilic montmorillonite was obtained by the reaction of montmorillonite (MON) and
DiStearyldimethylAmmonium Chloride (DSAC). The modified clay and PLLA, were
solvent-cast blended using chloroform as co-solvent. The PLLA–clay blends were
investigated in regard of their structure and properties using thermal measurements that
revealed that cold crystallization took place in the solvent cast PLLA, and that the clay
Chen Haiyan PhD Thesis
- 50 -
served as a nucleating agent. From small and wide-angle x-ray scattering measurements, it
was found that silicate layers forming the clay could not be individually well dispersed in the
PLLA–clay blends. So the clay existed in the form of tactoids, which consist of several
stacked silicate monolayers. These structures formed a remarkable geometrical network in
the blend film surfaces. They can be layed almost parallel to the film surface, and they were
stacked with the insertion of PLLA crystalline lamella in the thickness direction of the film.
During the blend drawing process, fibrillation took place with the formation of plane-like
voids developed on the plane parallel to the film surface. Furthermore, delamination of the
silicate layers did not occur even under the application of a shearing force (Ogata et al.
1997).
PLA thermal degradation and its blends or composites have also been widely reported by
Bourban et al. 2007. They analyzed the filler dispersion in the polymer matrix and the
thermal degradation rate showing that the relative constants of the loaded nanocomposites
were significantly lower than those of the unloaded polymers and their micro-composites in
the air.
TGA data and kinetic analysis results also supported the findings that the thermal stability of
the amorphous PLA and its composites was higher than that of the semicrystalline polymer
and its composites and the thermal stability of the nano-composites was higher than that of
the micro-composites (Bourban et al. 1997).
1.5.10. The Role of the Inorganic Filler on the Biodegradation Behavior and Final
Properties of Petro-based Polymers (PE, PP, PS)
Plastics occupy wide place in the applications of automotive, electronics and house goods.
Especially reinforced plastics become popular because of their high strength besides their
advantages of low weight and easy manufacturability (Altan et al. 2010).
Mechanical and morphological properties of Polypropylene (PP) and High Density
Polyethylene (HDPE) matrix composites reinforced with surface modified nano titan dioxide
(TiO2) particles were investigated. Surface modification was made by coating the nano
powders with Maleic Anhydride grafted Styrene Ethylene Butylene Styrene (SEBS-g-MA)
and silane, respectively.
After surface modification, they assessed thermal and morphological analysis for PP/TiO2
and HDPE/TiO2 based composites that were obtained by loading of 1 wt.%, 3 wt.% and 5
wt.% of the inorganic filler.
SEBS-g-MA provided bridging effect between TiO2 particles and polymer matrix while
silane played a role of dispersing agent. Depending on that, homogenous structures without
agglomeration were obtained. Reinforced HDPE and PP moldings gave higher tensile
strength and elastic modulus due to the rigid structure of TiO2.
Slight increment was seen in stress at break value, whereas elongation and impact strength
values decreased due to the stiffness of the nano titan dioxide (Altan et al. 2010).
The influence of filler size and content on the properties (thermal conductivity, impact
strength and tensile strength) of Al2O3/high density polyethylene (HDPE) based composites
were studied by Zhang et al. 2011. Thermal conductivity and tensile strength of the
composites increased decreasing the aluminium oxide particle size, whereas the dependence
of impact strength on this parameter is more complicated. SEM micrographs of the fracture
Introduction
- 51 -
surface showed that Al2O3 with small particle size is generally more efficient for the
enhancement of the impact strength, while the 100 nm particles proned to aggregation due to
their high surface energy deteriorating the impact strength. Composite filled with Al2O3 of
0.5 μm at content of 25 vol% showed the best synthetic properties. It is suggested that the
addition of nano-Al2O3 to HDPE would lead to good performance once suitably dispersed.
The thermal properties and combustion behaviour of new PE-hydrotalcites nanocomposites
were described by Costantino et al. 2005. Hydrotalcites were synthesized and then
intercalated with stearate anion with a long alkyl chain that played the role of compatibilizer
for the polyethylene chains.
The presence of inorganic filler shields PE from thermal oxidation, shifting the temperature
range of volatilisation towards that of thermal degradation in nitrogen, and brings to a
reduction of 55% in heat release rate during combustion.
In order to manufacture micro-porous, breathable films applicable to absorbent articles,
LDPE, LLDPE, and HDPE/zeolite composite films filled with zeolite, uncoated and coated
with stearic acid, were prepared (Kim et al. 2006). The mechanical, thermal, morphological,
and rheological measurements pointed out that the stearic acid showed a role of coupling
agent. Its incorporation on the zeolite surface improved the flexibility of polymer matrices.
In particular in LLDPE and HDPE based composites, the increase in the area of the air holes
and the decrease in the number of the air holes by merging among neighboring air holes was
prominent upon higher filler loading, therefore resulted in enhanced modulus, elongation and
impact properties.
Whereas, the declined values were observed in melting temperature (Tm), crystallization
temperature (Tc), and complex melt viscosity (Kim et al. 2006).
Studies on composite materials based on low-density polyethylene (LDPE) with different
weight percent of kaolin are present in literature (Hindryckx et al. 1996).
Shnean et al. 2008 analyzed some mechanical and physical properties such as tensile
strength, tensile strength at break, Young modulus, elongation at break, shore hardness and
water absorption at different weight fraction of filler (0, 2, 7, 10 and 15%). The addition of
filler increased the modulus of elasticity, elongation at break, shore hardness and impact
strength values; on other hand, the tensile strength and tensile strength at a break showed a
decreasing trend. Absorption test was carried out in water at different immersion times and
different composite .The results showed that after the addition of kaolin the absorption rate
exhibited a decrease. Calcinations kaolin filler produces better mechanical properties, than
grain kaolin fillers.
Ethylene polymerization was done with the aim to obtain a polyethylene based nano-
composite with nano-aluminum nitride using zirconocene as catalyst (Sohail et al.2012).
Results showed that the catalytic activity is maximum at a filler loading of 15 mg nano-
aluminum nitride. DSC and XRD results showed that the percentage crystallinity was also
marginally higher at this filler amount.
Morphology of the composite with 15 mg aluminium nitride is more fibrous as compared to
0 mg aluminium nitride and higher filler loading as shown by SEM images. In order to
understand combustibility behavior, tests were performed on micro-calorimeter. These
Chen Haiyan PhD Thesis
- 52 -
results showed a decrease in combustibility for the polyethylene nano-composites as the
filler loading increased.
Mechanical properties for Linear Low-Density Polyethylene (LLDPE)/org-clay based
nanocomposites prepared by melt processing were investigated by Durmus et al. 2008.
TEM study pointed out that the nano-composite samples showed a mixed morphology that
could be defined as some exfoliated layers, intercalated clay stacks, and two or three layered
tactoids present together within the samples.
Bentonite filled PP composites were prepared by melt-blending and the effect of
compatibilisers on mechanical, thermal, water absorption and morphological properties of
bentonite filled polypropylene based composites was investigated by Othman et al. 2006.
Two types of compatibilisers namely, Palm Oil Fatty Acid additive (POFA) and
Polypropylene Grafted-Maleic Anhydride (PPMAH) have been used with the aim to improve
the composites mechanical properties. The impact strength and elongation at break values
increased with the presence of both compatibilisers whilst, tensile strength and Young‘s
modulus improved only with the addition of PPMAH. Morphological investigation using
SEM revealed that the improvement in impact strength and elongation at break values was
due to the enhancement of the interfacial adhesion between bentonite and PP. The thermal
stability of bentonite filled PP improved with the incorporation of POFA and PPMAH. From
DSC thermograms, fusion enthalpy for both crystallisation (∆Hc) and melting (∆Hm)
processes of composites with compatibilisers have significantly reduced as compared to
control. The melting, cooling temperatures and crystallinity also reduced as compatibilisers
were added into bentonite filled polypropylene based composites.
Less percentage of water absorption has been observed in PP-bentonite system with PPMAH
(Othman et al. 2006).
Melt compounding was used to prepare conventional composites of montmorillonite clay and
PE as well as nano-composites of exfoliated montmorillonite platelets dispersed in a
maleated polyethylene (PE-g-MAn) matrix (Gopakumar et al. 2002). The extent of clay
platelet exfoliation in the PE-g-MAn nano-composites was confirmed by X-ray diffraction
and it resulted in a significant reduction of the degree of crystallinity and an increase of the
polymer crystallization rates. Studies of non-isothermal crystallization kinetics suggested
that the exfoliated clay promotes heterogeneous nucleation and two-dimensional crystallite
growth.
PE/clay composites behaved in a similar manner as conventional macrocomposites,
exhibiting modest increases in their rheological properties and Young‘s modulus.
Conversely, the nano-scale dimensions of the dispersed clay platelets in the nano-composites
led to significantly increased viscous and elastic properties and improved stiffness. This was
attributed to the high surface area between the polymer matrixes (Gopakumar et al. 2002
Introduction
- 53 -
1.6 Biodegradation of Fossil Fuel Based Polymers (ECOFLEX, PE and PS) in Soil-
Plant Systems (Avena sativa –Raphanus sativus)
The utilization of plastic mulch has played a major role in the increase in vegetable yield
production. The advantages of using mulch films are to control or increase the soil
temperature, maintain soil humidity, reduce germination time, provide early or out of season
crop production for better market value produce, reduce weeds and plant diseases, provide
efficiency in the usage of water and fertilizers, and most importantly, increase the quality of
horticultural products by avoiding the direct contact of the fruit with the soil (Lamont, 1999;
Espi et al., 2006).
Opaque mulching film prevents the passage of photosynthetically active radiation (PAR)
(Jayasekara et al. 1999), thus inhibiting weed growth, while transparent mulching films allow
the passage of the solar radiation, which increases soil temperature, thus improving the
cultivation cycle or providing soil sterilization following harvest (Immirzi et al. 2009).
Fig. 1.12. Pictures of the Black Biodegradable Films During and After the Growing
Season (Bar Length Equals 5 cm) (Kijchavengkul et al. 2008)
Figure 1.13. Pictures of the White Biodegradable Films During and After the
Growing Season (Bar Length Equals 5 cm) (Kijchavengkul et al. 2008).
Chen Haiyan PhD Thesis
- 54 -
Plastic mulching films, made mainly with low density polyethylene (LDPE), have
appropriate mechanical characteristics to assure their easy handling and fast installation,
functionality and resistance throughout the cropping cycle. Mulching films are designed with
suitable radiometric properties. The world consumption of LDPE mulching films in
horticulture is at present around 700000 tons per year (Espì et al. 2006).
Despite all these advantages, there are several major concerns about using mulch films which
are the costs of removal and disposal of the used plastics and environmental issues.
The use of plastic film in agriculture poses a major environmental problem due to high
molecular weight and hydrophobic properties of polyethylene. This gives to the film high
chemical stability, requiring about 100 years for its complete decomposition (Rutiaga et al.
2005).
In view of this, the introduction of biodegradable films (BPs) represents a really promising
alternative to the common (mostly polyethylene) plastic films for enhancing sustainable and
environmentally friendly agricultural activities (Gross and Kalra 2002). BPs can be degraded
by microorganisms in the natural environment.
The biodegradation test of all the mulch film samples in laboratory conditions was conducted
based on ASTM D 5338 standard (ASTM, 2003b) using a direct measurement respirometric
(DMR) system.
Biodegradable films can be degraded by microorganisms in the natural environment, thus
reducing the amount of waste ending up in landfills. To date, many aliphatic polyesters
which can be degraded in compost and moist soils, such as poly-(butylene succinate) (PBS)
and poly-(butylene succinate-co-butylene adipate) (PBSA) have been developed as
biodegradable films with excellent formability like polyethylene (Xu and Guo 2010).
The degradation of these materials, however, is gradual and cannot be easily controlled
(Kyrikou and Briassoulis 2007). Degradation speed of biodegradable mulch films in
agricultural fields is sometimes very slow, as it is largely affected by the environmental
conditions. The desirable practical biodegradable film is a programmed degradable plastic
that has adequate performance properties during its planned useful life time, and is 100%
post-use biodegradable.
If some efficient biodegradable film-degrading microorganisms were available, farmers can
use them or their enzyme to degrade the used biodegradable mulch films immediately after
use, thus enabling them to manage efficiently the schedule of their next planting. Also, they
will be able to use stronger plastic products that are not easily broken during use, and could
degrade them by enzyme treatment whenever necessary (Kitamoto et al. 2011).
Only few studies, however, have been published so far on the use of such microorganisms to
enhance the degradation of used biodegradable mulch films in soil environment (Kasuya et
al. 2009; Abe et al. 2010) isolated a fungal strain NKM1712 from soil, and observed weight
loss of poly butylene adipare-co-butylene terephtalate (PBAT) film with inoculation of this
strain in soil. Scanning electron microscopy (SEM) observation of degraded film on soil and
comparative studies of the biodegradable film-degrading ability of isolated microorganisms
demonstrated the contribution of fungi to microbial degradation of biodegradable films (Sang
et al. 2002; Tan et al. 2008; Kasuya et al. 2009). Recent investigation of microbial
communities in biodegradable-degrading compost by using direct DNA extraction from
Introduction
- 55 -
compost followed by cloning and sequencing showed that Ascomycota comprised the most
dominant group of microorganisms during the biodegradation of biodegradable films
(Sangwan and Wu 2008; Sangwan et al. 2009). Although biodegradable mulch films are
degraded in soil, it has been very difficult to isolate the effective biodegradable film-
degrading microorganisms from it. The farmer could be oriented to utilize a grass cover in
order to stimulate microbial biomass in soil and its enzyme activities; this could enhance
biodegradation of xenobiotics recalcitrant and biodegradable compounds at rhizosphere
zone. It is, in fact, well known that plants promote the degradation of organic compounds by
immobilization, removal, and promotion of microbial degradation.
Kuiper at al. (2004) and Newman and Reynolds (2004) published reviews on
phytodegradation of organic pollutants, at root level (rhizodegradation), and Dzantor (2007)
addressed the state of rhizosphere ―engineering‖ for rhizodegradation of xenobiotic
contaminants. Soil microflora plays, in fact, vitally important role during rhizoremediation of
xenobiotics (Johnsen et al. 2005; Semple et al. 2007).
Plants have many important functions in the stimulation of the microbial metabolism,
providing a carbon source for microorganism activity, transferring the oxygen from air to the
soil (Olson et al. 2003; Yu et al. 2006), and releasing root exudates which can serve as
substrates for the total microbial community activity, thus increasing the number of
microorganisms (Salt et al. 1998). Recent studies have confirmed that effectively plants are
able to stimulate soil microbial activity also in extreme environments (Doni et al., 2012;
Bianchi and Ceccanti, 2010; Benitez et al., 2010).
Together with the biotic factors, abiotic agents, such as solar radiant intensity, temperature,
humidity etc., are of great importance in controlling the environmental degradability of
biodegradable films.
1.6.1. Biodegradation of plastics in soil
Biodegradation is governed by different factors that include polymer characteristics, type of
organism, and nature of pretreatment. The polymer characteristics such as its mobility,
tactility, crystallinity, molecular weight, the type of functional groups and substituents
present in its structure, and plasticizers or additives added to the polymer all play an
important role in its degradation (Artham and Doble, 2008; Gu et al., 2000b).
During degradation the polymer is first converted to its monomers, and then these monomers
are mineralized. Most polymers are too large to pass through cellular membranes, so they
must first be depolymerized to smaller monomers before they can be absorbed and
biodegraded within microbial cells.
The initial breakdown of a polymer can result from a variety of physical and biological
forces (Swift, 1997). Physical forces, such as heating/cooling, freezing/thawing, or
wetting/drying, can cause mechanical damage such as the cracking of polymeric materials
(Kamal and Huang, 1992). The growth of many fungi can also cause small-scale swelling
and bursting, as the fungi penetrate the polymer solids (Griffin, 1980). Synthetic polymers,
such as poly(caprolactone) (Toncheva et al., 1996; Jun et al., 1994), are also depolymerized
by microbial enzymes, after which the monomers are absorbed into microbial cells and
biodegraded (Goldberg, 1995). Abiotic hydrolysis is the most important reaction for
Chen Haiyan PhD Thesis
- 56 -
initiating the environmental degradation of synthetic polymers (Göpferich, 1997) like
polycarboxylates (Winursito and Matsumura, 1996), poly(ethylene terephthalate) (Heidary
and Gordon, 1994), polylactic acids and their copolymers (Hiltunen et al., 1997; Nakayama
et al., 1996), poly (α-glutamic acids) (Fan et al., 1996), and polydimethylsiloxanes, or
silicones (Lehmann et al., 1995; Xu et al., 1998).
Generally, an increase in molecular weight results in a decline of polymer degradability by
microorganisms. In contrast, monomers, dimers, and oligomers of a polymer's repeating
units are much easily degraded and mineralized. High molecular weights result in a sharp
decrease in solubility making them unfavorable for microbial attack because bacteria require
the substrate to be assimilated through the cellular membrane and then further degraded by
cellular enzymes. At least two categories of enzymes are actively involved in biological
degradation of polymers: extracellular and intracellular depolymerases (Doi, 1990; Gu et al.,
2000b). During degradation, exoenzymes from microorganisms break down complex
polymers yielding smaller molecules of short chains, e.g., oligomers, dimers, and monomers,
that are smaller enough to pass the semi-permeable outer bacterial membranes, and then to
be utilized as carbon and energy sources. When the end products are CO2, H2O, or CH4, the
degradation is called mineralization (Frazer, 1994; Hamilton et al., 1995). It is important to
note that biodeterioration and degradation of polymer substrate can rarely reach 100% and
the reason is that a small portion of the polymer will be incorporated into microbial biomass,
humus and other natural products (Atlas and Bartha, 1997; Narayan, 1993). Dominant groups
of microorganisms and the degradative pathways associated with polymer degradation are
often determined by the environmental conditions. When O2 is available, aerobic
microorganisms are mostly responsible for destruction of complex materials, with microbial
biomass, CO2, and H2O as the final products. In contrast, under anoxic conditions, anaerobic
consortia of microorganisms are responsible for polymer deterioration. The primary products
will be microbial biomass, CO2, CH4 and H2O under methanogenic (anaerobic) conditions
(Barlaz et al., 1989).
1.6.2. Polyethylene
Synthetic polyolefins are inert materials whose backbones consist of only long carbon
chains. The characteristic structure makes polyolefins non-susceptible to degradation by
microorganisms.
However, a comprehensive study of polyolefin biodegradation has shown that some
microorganisms could utilize polyolefins with low molecular weight (Yamada-Onodera et
al., 2001). The biodegradation always follows photodegradation and chemical degradation.
Polyethylene is one of the synthetic polymers of high
hydrophobic level and high molecular weight. In natural form, it is not biodegradable. Thus,
their use in the production of disposal or packing materials causes dangerous environmental
problems (Kwpp and Jewell, 1992). To make PE biodegradable requires modifying its
crystalline level, molecular weight an mechanical properties that are responsible for PE
resistance towards degradation (Albertsson et al., 1994). This can be achieved by improving
PE hydrophilic level and/or reducing its polymer chain length by oxidation to be accessible
for microbial degradation (Bikiaris et al., 1999). The degradation of polyethylene can occur
by different molecular mechanisms; chemical, thermal, photo and biodegradation.
Some studies (Lee et al., 1991; Glass and Swift, 1989; Imam et al., 1992; Gu, 2003) have
assessed the biodegradability of some of these new films by measuring changes in physical
properties or by observation of microbial growth after exposure to biological or enzymatic
Introduction
- 57 -
environments, but mostly by CO2 evolution. Since polyethylene (PE) is widely used as
packaging material, considerable work not only on biodegradable polyethylene but also on
biodegradation of polyethylene has been conducted (Bonhomme et al., 2003; Wang et al.,
2004). The results of these studies indicated that polyethylene was biodegraded following
photodegradation and/or chemical degradation. Biodegradation of polyethylene is known to
occur by two mechanisms: hydro-biodegradation and oxo-biodegradation (Bonhomme et al.,
2003). These two mechanisms agree with the modifications due to the two additives, starch
and prooxidant, used in the synthesis of biodegradable polyethylene. Starch blend
polyethylene has a continuous starch phase that makes the material hydrophilic and
therefore, catalyzed by amylase enzymes. Microorganisms can easily access, attack and
remove this part. Thus the hydrophilic polyethylene with matrix continues to be hydro-
biodegraded. In case of pro-oxidant additive, biodegradation occur following
photodegradation and chemical degradation. If the pro-oxidant is a metal combination, after
transition, metal catalyzed thermal peroxidation, biodegradation of low molecular weight
oxidation products occurs sequentially (Bonhomme et al., 2003; EI-Shafei et al., 1998;
Yamada-Onodera et al., 2001). EI-Shafei et al. (1998) investigated the ability of fungi and
Streptomyces strains to attack degradable polyethylene consisting of disposed polyethylene
bags containing 6% starch. He has isolated 8 different strains of Streptomyces and two fungi
Mucor rouxii NRRL 1835 and Aspergillus flavus. In a study, Low density polyethylene
pieces buried in soil mixed with sewage sludge were examined microscopically after 10
months, fungal attachment was found on the surface of the plastic, indicating possible
utilization of plastic as a source of nutrient (Shah, 2007) The isolated fungal strains were
identified as Fusarium sp. AF4, Aspergillus terreus AF5 and Penicillum sp. AF6. The ability
of the fungal strains to form a biofilm on polyethylene was attributed to the gradual decrease
in hydrophobicity of its surface (Gilan et al., 2004).
The structural changes in the form of pits and erosions observed through scanning
electronmicroscopy indicated surface damage of PE incubated with Fusarium sp. AF4. That
suggested that the fungal strains, especially Fusarium sp. AF4, were able to adhere to the
surface of LDPE and can cause surface damage (Shah, 2007). In a study by Bonhomme et al.
(2003), SEM evidence confirmed that microorganisms (fungi) build up on the surface of the
polymer (polyethylene) and after removal of the microorganisms, the surface became
physically pitted and eroded. The surface of the polymer after biological attack was
physically weak and readily disintegrates under mild pressure. Otake et al. (1995) reported
the changes like whitening of the degraded area and small holes on the surface of PE film
after soil burial for 32 years. Biodegradation of LDPE film was also reported as 0.2% weight
loss in 10 years (Albertsson, 1980). Ohtaki et al. (1998) tested LDPE bottles exposed in
aerobic soil for over 30 years, and observed some evidences of biodegradation using SEM of
the degraded parts and as reduction in molecular weight by Time of Flight Mass
Spectrometry (TOF-MS). Yamada-Onodera et al. (2001) isolated a strain of fungus
Penicillium simplicissimum YK to biodegrade polyethylene without additives. UV light or
oxidizing agents, such as UV sensitizer, were used at the beginning of the process to activate
an inert material, polyethylene. Polyethylene was also treated with nitric acid at 80 °C for 6
days before cultivation with inserted functional groups that were susceptible to
Chen Haiyan PhD Thesis
- 58 -
microorganisms. Bonhomme et al. (2003) has reported that with the fungal activity,
polyethylene with a starting molecular weight in the range of 4000 to 28,000 was degraded
to units with a lower molecular weight of 500 after three months of liquid cultivation, which
indicated the biodegradation of that polyethylene. In a similar study the Polyethylene pieces
were treated by exposing it to UV light and also nitric acid. That pretreated polymer was then
applied to microbial treatment using Fusarium sp. AF4 in a mineral salt medium containing
treated plastic as a sole source of carbon and energy. An increase in the growth of fungus and
some structural changes as observed by FTIR, were observed in case of treated PE which
according to Jacinto indicated the breakdown of polymer chain and presence of oxidation
products of PE. Non-degraded polyethylene exhibits almost zero absorbancy at those wave
numbers (http://www.dasma. dlsu.edu.ph/offices/ufro/sinag/Jacinto.htm). Absorbance at
1710–1715 cm−1 (corresponding to carbonyl compound), 1640 cm−1 and 830–880 cm−1
(corresponding to −C=C–), which appeared after UV and nitric acid treatment, decreased
during cultivation with microbial consortia (Hasan et al., 2007). Typical degradation of PE
and formation of bands at 1620–1640 cm−1 and 840–880 cm−1 was also reported by
Yamada-Onodera et al. (2001), attributed to oxidation of polyethylene.
Overall, polyethylene degradation is a combined photo- and bio-degradation process. First,
either by abiotic oxidation (UV light exposure) or heat treatment, essential abiotic precursors
are obtained. Secondly, selected thermophilic microorganisms degrade the low molar mass
oxidation products to complete the biodegradation (Bonhomme et al., 2003).
1.6.3. Polystyrene
Polystyrene (PS) is a synthetic plastic used in the production of disposable cups, packaging
materials, in laboratory ware, in certain electronic uses. PS is used for its lightweight,
stiffness and excellent thermal insulation. When it is degraded by thermal or chemical means
it releases products like; styrene, benzene, toluene and acrolein. There are very few reports
on the biodegradation of polystyrene but the microbial decomposition of its monomer;
styrene, have been reported by few researchers (Tsuchii et al., 1977).
1.6.4. Aliphatic–aromatic (AAC) copolyesters
Biodegradable polyesters are one family of polymers that have been considered as
replacements for conventional plastic resins. Aliphatic polyesters such as the naturally-
occurring polyhydroxyalkanoate family of materials and the synthetic polycaprolactone have
been investigated as possible alternatives to traditional plastics, but their material properties
seriously affect the versatility of these materials (Reddy et al., 2003; Khanna and Srivastava,
2005; Oda et al., 1995). A more promising alternative is an aliphatic–aromatic copolyester of
1,4-butanediol, adipic acid and terephthalic acid, which has been commercialized under the
trade names Ecoflex_ and Eastar Bio_. The co-polyester is produced from the random
polymerization of the diester oligomers of adipic acid/butanediol, and terephthalic
acid/butanediol.
The degradation of this co-polyester has been investigated in compost environments or with
compost isolates Kleeberg et al., 1998; Witt et al., 2001). The experiments with compost
isolates were all performed at elevated temperatures with Thermobifida fusca (known
previously as Thermomonospora fusca) and a hydrolase isolated from this bacterial strain.
Results from these studies demonstrated rapid degradation of the co-polyester, with
essentially complete degradation having been achieved in 21 days in the presence of a
Introduction
- 59 -
readily available carbon source. However, numerous questions remain unanswered regarding
the degradation of the synthetic co-polyester under more moderate environmental conditions
and with microorganisms other than thermophiles. This is an important consideration
because it is likely that much of the co-polyester will be disposed of and degraded under
these mesophilic conditions rather than in compost at elevated temperatures.
In a more recent paper (Trinh Tan et al., 2008), a screening procedure was developed to
assess the biodegradability of the co-polyester at mesophilic environmental conditions and to
investigate the mechanism of biodegradation. Results showed that the aliphatic–aromatic co-
polyester could be degraded by a number of different microorganisms. However, after 21
days exposure to even the most promising cultures of pure microorganisms, only partial
degradation of the Ecoflex was accomplished and only a few samples showed visible signs
of degradation as loosely defined by the mechanical weakening of the films. Weight loss was
not as obvious as the visual degradation and suggested broader types of microbial attack. The
bacteria studied preferentially degraded the bonds between aliphatic components of the
copolymer and the rate of biodegradation of oligomers was appreciably faster than that for
the polymer chains. Using GC–MS techniques, degradation intermediates were identified to
be the monomers of the co-polyester. Gel permeation chromatography results suggested exo-
enzyme type degradation, where the microbes hydrolysed the ester bonds at the termini of
the polymeric chains preferentially.
1.7 Polyvinylics Biodegradation
The present global situation in the production of synthetic polymers accounts for almost 85-
90% represented by full carbon-backbone macromolecular systems (polyvinylics and
polyvinylidenics) (Chart 2004), and for about 35-45% of usage as one-way use items
production (disposables & packaging). Therefore it is reasonable to envisage a dramatic
environmental impact as attributable to the accumulation of plastic litter and waste
constituted by full carbon backbone polymers, which basically are recalcitrant to physical-
chemicals and biological degradation processes.
In opposition to ―hydro-biodegradation‖ process of natural and synthetic polymers
containing hetero atoms in the main chain (polysaccharides, proteins, polyesters, polyamides,
polyethers, polyurethanes), the mechanism of biodegradation of full carbon backbone
polymers requires an initial oxidation step as mediated or not by enzymes followed by the
fragmentation again mediated or not by enzymes with substantial reduction in molecular
weight. The functional fragments become then vulnerable to microorganisms present in
different environments with production under aerobic conditions of carbon dioxide, water
and cell biomass. In Figure 1.7 are outlined the general features of Environmentally
Degradable Polymeric Materials and Plastics that are classified into the specific sectors of
the Hydro-biodegradables and Oxo-biodegradables. Typical examples of the so called ―oxo-
biodegradable‖ polymers are represented by polyethylene, poly(vinyl alcohol), natural rubber
(poly 1,4 cis isoprene) and lignin (a natural heteropolymer) (Scott and Wiles 2001). The
major biodegradation mechanism of PVA in aqueous media, is represented by the oxidative
random cleavage of the polymer chains,. the initial step being associated to the specific
oxidation of methylene carbon bearing the hydroxyl group, as mediated by oxidase and
dehydrogenase type enzymes, to give -hydroxyketone as well as 1,3-diketone moieties. The
latter groups are susceptible of carbon-carbon bond cleavage promoted by specific -
diketone hydrolase, leading to the formation of carboxyl and methyl ketone end groups
(Sakai K, et al. 1986; Suzuki 1979).
Chen Haiyan PhD Thesis
- 60 -
1.7.1 The Role of Plastics in Agriculture
The fundamental role acquired by plastics in agriculture since the middle of the last century
(Albertsson, et al. 1994) was suggesting the definition of ―plasticulture‖ as a new practice
where the use of plastics for crops production and preservation can be considered as a routine
practice capable of increasing unitary yields, inducing earlier harvests, limiting the use and
release of herbicides and pesticides, as well as to improve the more efficient water resources
utilization[www.plasticulture.com], thus contributing significantly to the economic viability
of farmers worldwide (Lamont 1991). Accordingly conventional plastic films, are therefore
extensively used as coverings of greenhouses, low tunnels and mulching, where low density
(LDPE) and linear low density poly(ethylene) (LLDPE) films represents the most employed
polymeric materials (Briassoulis 2005; Espí, et al. 2006) accounting for an estimated
worldwide market of 2.0- 2.5 million tons per year in the agricultural segments.
The large utilization of these materials in certain agricultural regions is posing increasing
concerns about their collection and disposal (Decree 2006) after their service life. In
addition, visual pollution and detrimental effects on soil management and fertility have been
also claimed as problems connected to plasticulture These problems can be solved,
specifically for the agricultural plastic wastes, by using in situ biodegradable materials
having unitary costs comparable to those of conventional plastics. In this case, however, the
requirement for a controlled life time ranging between several weeks up to one year or more
depending upon the practical utilizations (i.e. mulching films or tunnels covering) is needed.
In keeping, since the second half of the 20th century, strategies to achieve low cost
environmental degradable polyolefins were undertaken (Guillet, et al. 1974; Voigt 1966).
The knowledge (G. Scott and Wiles 2001; N. C. Billingham and Calvert 1983) on thermal
and photolytic peroxidation mechanisms of poly(ethylene) and poly(propylene) constituted
the basis for the development of reengineered polyolefins susceptible to be oxidized and
fragmented when exposed to heat or light irradiation, with the aim to overcome the intrinsic
recalcitrance of polyolefins to biodegradation. It was ascertained that at the beginning of the
sequence of reactions leading to polyolefins peroxidation and their subsequent instability in
the environment is the generation of sensitising impurities during the thermal processing of
polyolefin resins (Scott 1993).
Carbonyl groups and hydroperoxides groups particularly were recognized as the most
effective sensitizing impurities capable of promoting the radical chain reactions leading to
the carbon chains cleavage in polyolefins (Scott 1993; Guillet and Norrish 1954; Hartley and
Guillet 1968; Carlsson et. al 1979; Scott 1981; Malaika et. al 1968; Heskins and Guillet
1968). In particular it was ascertained that the starting point is the formation of peroxyl
radical as a consequence of homolytic bond cleavage from shear stresses during extrusion in
the presence of oxygen, which is converted to hydroperoxide group by hydrogen abstraction
from vicinal methylene groups. The high reactivity of hydroperoxide groups under both heat
and UV exposure further promote an autoaccelerating cycle of interlocking reactions
involving formation/decomposition of radical groups which lead to the carbon chain scission
(molar mass reduction) and formation of several different oxidized groups. In the overall
peroxidation process of PE, the hydroperoxide groups decomposition is therefore considered
as the rate-determining step (Erlandsson 1997). Hence, molecules and additives which are
capable of enhancing hydroperoxide formation and decomposition to other radicals are active
pro-oxidants or pro-degradants since they accelerate the polyolefin chains oxidation and
successive cleavage.
Taking into account these evidences, major strategies to enhance the environmental
degradation and biodegradation of polyolefins have been focused on copolymerisation,
blending or grafting with functional polymers and compounds, as well as in the addition of
pro-oxidant additives. UV-absorbing carbonyl groups capable to accelerate the photo-
oxidation process can be introduced by copolymerizing ethylene and carbon monoxide or
Introduction
- 61 -
vinyl ketones (Harlan and Kmiec 1995; Guillet 1973), the latter strategy being the technical
process used in the production of Ecolyte® polyethylenes.
Another strategy to improve the environmental degradability of polyethylene and
polypropylene films is represented by the addition of pro-oxidants additives during their
conversion to plastic items. It has been in fact suggested that this alternative may provide a
more efficient control of the degradation rate, thus making the shelf life and useful life of the
polyolefin‘s compatible with a wide range of applications (Wiles and Scott 2006).
Most of the used pro-oxidant additives are represented by organic complexes of metals
capable of yielding two metal ions differing in the oxidation number by one unit
(Jakubowicz 2003; Weiland et al 1995). Several polymer soluble metal carboxylates and
acetylacetonates of Co3+ and Fe3+ are very effective photo-prooxidants capable to initiate
the degradation process through the metal salts photolysis to give under UV irradiation the
reduced form of the metal ion and a free radical.
The anion radical promote a fast hydrogen abstraction from the polymer and the relevant
formation of hydroperoxide. Afterward the general radical oxidation mechanisms of the
polyeolefins is thought to proceed being enhanced by the usual redox reactions between
hydroperoxides and metal ions FeX2, + ROOH > RO* + FeX2.OH (3).
Another class of pro-oxidant additives is represented by compounds capable to induce the
peroxidation of polyolefins by absorbing energy as heat. Also this class of additives is based
on the activity exerted by transition metal ions typically added to the final product in the
form of stearate or acetylacetonate organic ligands. The most employed cations are Mn2+
(Jakubowicz 2003) and Co2+ (Weiland et al 1995). Instead of Fe3+
complexes which play
the main role in photo-oxidation processes, Mn2+
and Co2+
are needed to accelerate the
radical chain reactions of polyolefin oxidation through the decomposition of hydroperoxides
and peroxides as induced by heat absorption (Koutny 2006) (Scheme 2).
An other type of ―photosensitizer‖ pro-oxidants is constituted by Fe(III) dithiocarbamates
and dithiophospates. These compounds initially acts as antioxidants by decomposing
hydroperoxides by an ionic mechanism (Malaika 1983; Malaika and Scott 1983), after that
the ligands are destroyed, thus releasing free transition metal ions which start to behave as
pro-oxidant. Hence, in these compounds both antioxidant and pro-oxidant properties are
coexisting. This characteristic feature has been exploited in order to finely control the
lifetime before the photo-oxidation commences according to the so called Scott-Gilead
technology which leads to the production and commercialization under the trade name of
Plastor of photodegradable polyethylene mulching films.
Several studies have therefore reported the significant reduction of molecular weight after
thermal and photo degradation of PE samples containing pro-oxidants (Albertsson et. al
1995; Albertsson et. al 1998), as well as the extraction, isolation and identification of
oxidized products, including carboxylic acids, ketones, esters and low molecular weight
hydrocarbons (Albertsson 1993; Khabbaz and Albertsson 2000). Carbonyl groups along the
carbon backbone are produced by additive-catalyzed hydroperoxide decomposition. A side
reaction of hydroperoxides is also the conversion in alkoxy macroradicals that in a similar
way of peroxy radicals may be transformed (hydrogen abstraction) to produce a carbonyl
group and a chain-end radical through chain scission. Accordingly it has been repeatedly
ascertained a straightforward relationship between the amount of chain scissions and the
number of carbonyl groups. For that reason, quantitative FT-IR analysis can be currently and
effectively used to predict the extent of abiotic photo- and thermal degradation of polyolefins
(Chiellini 2006). As a consequence of the radical oxidation processes and relevant chain
scissions, a fairly high number of degradation products containing functional groups have
been recognized during several investigations
Aliphatic carboxylic and dicarboxylic acids have been found to be the most abundant
degradation products which are formed during both photo and thermal oxidation of
additivated polyethylenes.
Chen Haiyan PhD Thesis
- 62 -
These intermediates can be also formed from the oxidation of other functional groups such as
primary alcohol and aldehydes deriving from hydroperoxide decomposition followed by
hydrogen abstraction or -scission, respectively, particularly during thermal aging. Also the
photolytical cleavage of keto groups through Norrish I mechanism (Scheme 1.3) may lead to
the formation of aldehyde that can be then oxidized to carboxylic groups. In keeping,
dicarboxylic acids have been found as the most predominant products formed during photo-
oxidation processes of PE especially after many days of irradiation (Albertsson 1995).
Since the ultimate environmental fate of ―degradable‖ polyethylenes has to be considered as
the results of the combining action of abiotic factors and microorganisms which suggested
the definition of ―oxo-biodegradable‖ materials in keeping with the processes of
biodegradation of lignin and natural rubber (Wiles and Scott 2006) . The evaluation of the
extent and rate of peroxidation of these materials represents indeed a powerful tool to predict
their potential biodegradation. Several studies have been therefore carried out with the aim of
investigating the mechanisms of photo and thermal oxidation of polyolefins containing pro-
oxidant additives. Nevertheless, most of these studies have been carried out under strictly
controlled laboratory conditions, as well as under extreme accelerating stressing conditions
that can not be considered as representative of the natural environments. In particular, only a
few investigations have been carried out by assessing the synergic effects of temperature,
humidity and/or sunlight exposure that usually are jointly operative in outdoor exposure
conditions.
In any case, by considering the general mechanism of radical oxidation of PE (Scheme 5),
the following parameters can be currently monitored during the abiotic degradation step
sketched for a PE blown film : 1) weight variation; 2) carbonyl index (COi); 3) wettability;
4) molecular weight variation; 5) fractionation by solvent extraction; In particular,
gravimetric analysis can be effectively used to appreciate the weight variation as a
consequence of the oxygen uptake during the early stage of oxidation, as well as the weight
loss due to the volatilization of low molecular weight fragments at prolonged stage of
thermal and photo degradation.
Another powerful tool for the quantitative and qualitative evaluation of the oxidation
processes is constituted by the carbonyl index (COi) as determined by FT-IR spectroscopy. It
has been repeatedly reported that the most of the degradation intermediates of PE
peroxidation are bearing carbonyl groups, therefore their concentration, as determined by
COi can be used to monitor the progress of degradation (Gugumus 1996).
In general these determinations are carried out on test films by recording the ratio of the
optical density of the carbonyl absorption band at 1640 - 1840 cm-1 range and the optical
density of the absorption band at 1463 cm-1 (CH2 in plane occurring in the vibrations -
scissoring ). In addition, FT-IR analyses provide also information on the presence during the
time of absorption attributable to of different carbonyl containing oxidized products such as
carboxylic acids (1712 cm-1), ketones (1723 cm-1), aldehydes (1730 cm-1) and lactones
(1780 cm-1) ( Khabbaz and Albertsson 2000).
The determination of wettability of film surfaces during the degradation tests by contact
angle measurements may provide useful information about the increasing polarity of the film
surfaces as a consequence of oxidation and formation of functional groups. These
information are also useful in order to predict the feasibility of microbial attack of PE films,
by taking into account that one of the reason that have been suggested to explain the intrinsic
recalcitrance of PE to biodegradation is the hydrophobic character hindering the adhesion of
microbial cells.
In terms of potential ultimate biodegradation (e.g. conversion to CO2 and H2O,
mineralization), the assessment of molecular weight variation is a fundamental task. It is in
fact suggested that from a theoretical point of view, PE in force of its structure as a straight
chain hydrocarbon, should be metabolized according to the biochemical pathway of linear
alkanes. On the other hand, it has been established that there is a dimensional limit (i.e
Introduction
- 63 -
molecular weight) for the n-alkanes utilization as carbon source by microorganisms. In this
connection, Haines and Alexander established that linear hydrocarbons with more than 44
(tetratetracontane) carbon atoms can not be metabolized by soil microorganisms (Haines and
Alexander 1974).
Recently, in a study carried out with single bacterial strains, this dimensional limit has been
moved to 0.72 kDa corresponding to 60 carbon atoms (Heat et. al 1997). In any case, these
limits are though to be related to the bacterial metabolism of n-alkanes that need the
accessibility of the methyl chain ends by extracellular oxidizing enzymes to start the
biodegradation process. Therefore, the rate and eventually the ultimate extent of
biodegradation of solid n-alkanes is strongly affected by the availability of -CH3 chain ends
susceptible of enzymatic oxidation. It is obvious that the chain ends present at the surface of
a solid alkane decrease with the increase of the molecular weight up to extremely low
numbers in the case of high molecular weight polyethylenes.
Finally, other information about the relationship between the level of oxidation as reached
during the abiotic stage of degradation of ―degradable‖ PE, the molecular weight reduction
as well as the potential to be biodegraded in the environment can be effectively achieved by
fractionation of pre-aged specimens submitted to solvent extraction. This practice may also
provide, especially if carried out by using solvents with different polarity, further
information on the relative amount of different classes (e.g. carboxylates, alkanes etc.) of
degradation products deriving from peroxidation and cleavage of PE chains.
Further to the evaluation of the abiotic oxidation degradable PE, the final step to be
investigated in order to achieve information on the ultimate environmental fate of the
partially oxidized materials is the assessment of biodegradation under different conditions.
The requirement of two steps, abiotic and biotic, in the degradation mechanism of oxo-
biodegradable plastic items has recently inspired the definition and approval of the ASTM
D6954-04 ―Standard guide for exposing and testing plastics that degrade in the environment
by a combination of oxidation and biodegradation‖.
This standard provides a framework to assess and compare the degree of degradation
attainable under controlled thermal and photo-oxidation tests with the degree of
biodegradation and ecological impacts in defined disposable environments after abiotic
degradation. In accordance the ASTM D6954-04 guide is divided in three tiers as sketched in
Figure 6.
i) accelerate aging in standard tests for both thermal and photo-oxidation processes
and determination of the degree of abiotic degradation (Tier 1),
ii) measuring biodegradation (Tier 2),
iii) assessing the ecological impact after this processes (Tier 3).
In order to exploit the Tier 1, the standard norm suggests to use test conditions for thermal or
photo-oxidation likely to occur in application and disposal environment for which the test
material is committed. In other words, accelerated oxidation should be carried out at
temperatures and humidity ranges typical of test material application and disposal
environment. Test materials resulting from Tier are therefore exposed to appropriate disposal
or use environments (soil, landfill, compost) in standard respirometric (biometric) test
methods in order to assess the rate and degree of biodegradation (Tier 2). Finally, any
residues of the analyzed materials, as deriving from both the abiotic oxidation stage and from
biodegradation tests must be submitted to ecotoxicity tests to demonstrate their ultimate
environmental compatibility (Tier 3).
1.7.2 Biodegradation of pro-oxidant-free polyethylene by natural occurring
microorganisms
The contemplation of the inherent capabilities of microorganisms to promote the
biodegradation and eventually the utilization of polyethylene (PE) as carbon source seems to
Chen Haiyan PhD Thesis
- 64 -
be more controversial nowadays that in fairly recent past years. Conflicting results have been
indeed obtained that are suggesting from one side the ability of specific microbial strains to
degrade high molecular weight PE, whilst many studies are yet claiming the inertness to
biological attack of this polyolefin and structurally alike polymers also when exposed to very
stressing and active microbial environments such as the composting windrows. Degradation
of PE by microorganisms has been generally monitored in terms of microbial growth,
biometry (e.g. biochemical oxygen demand or carbon dioxide emission, including 14CO2
generation from radio-labelled samples), sample weight loss, mechanical properties,
variation of structural features (e.g. molecular weight, spectroscopic features, mechanical
properties).
Preliminary investigations are dating back to the early 1960s. At that time, the increase of
microbial cell numbers was taken as an indication of PE assimilation by bacteria in
comparison with low molar mass paraffins (Jen-hou and Schwartz 1961). From these studies
it was suggested that several bacteria can utilize as carbon source low molecular mass PE
fractions slightly below 5000, whereas no microbial activity was detected on higher Mw
fractions. Potts and co-workers assessed that linear paraffin with Mw below 500 were
utilized by different microorganisms (Potts 1972). Similar results were obtained later by
Albertsson and Banhidi that recorded the utilization of short oligomeric fraction of HDPE by
microorganisms after 2 years biodegradation experiments (Albertsson and Banhidi 1980).
Indeed, it can be suggested from a theoretical point of view that since PE is a nominally
straight-chain hydrocarbon, it should be metabolized according to the biochemical pathway
holding true for linear alkanes (Fig.1.14). On the other hand, it has been established that
there is a molecular weight upper limit for the utilization of n-alkanes as a carbon source by
microorganisms. Haines and Alexander established that linear hydrocarbons with more than
44 carbon atoms (tetratetracontane) cannot be metabolized by soil micro-organisms ( Haines
and Alexander 1974). More recently in a study carried out by using single bacterial strains
(Heat et al. 1997), this dimensional limit has been extended to 720 Dalton corresponding to
an hydrocarbon chain constituted by 60 carbon atoms. In any case these limits are thought to
be related to the bacterial metabolism of n-alkanes that need the accessibility to methyl chain
ends by extra cellular oxidizing enzymes to start the biodegradation process.
RCH3 RCH2OH RCHO RCOOH
H3CRCH3 H3CRCOOH HOCH2RCOOH OCHRCOOH HOOCRCOOH
RCH2CH2CH3 RCH2CH(OH)CH3 RCH2COCH3 RCH2OC(O)CH3 RCH2OH + CH3COOH
RCH3 RCH2OOH RCHO
RCH2OH
RCOOH
RCOOCR
Terminal oxidation (Pseudomonas)
Diterminal oxidation (Candida)
Subterminal oxidation (Nocardia)
Finnerty's pathway (Acinetobacter)
Figure 1. 14. Microbial oxidation pathways of n-alkanes.
Introduction
- 65 -
The first step is known as hydroxylation ( -oxidation) which give rise to the corresponding
primary alcohols which are further enzymatically oxidized to aldehyde and hence to
carboxylic acids. The resulting carboxylated n-alkanes can be metabolized according to the
β-oxidation process in analogy with the catabolism of fatty acids. Thus, the rate and
eventually the ultimate extent of biodegradation of solid n-alkanes can be strongly affected
by the availability of CH3 chain ends susceptible to enzymatic oxidation. It follows that the
number of chain ends present at the surface of a solid n-alkane decreases with the molecular
weight increase and hence with extremely low values in the case of high molecular weight
polyethylene.
On the other hand, it can not be at least hypothetically ruled out that oxidizing biological
processes other than the -oxidation of terminal methyl groups such as the random chain
cleavage as mediated by dehydrogenation/oxidation leading to carbonyl groups might play
an important role in the biodegradation of PE.
Taking into account these suggestions Kawai and her collaborators tried to establish a
numerical simulation model for the biodegradability of PE starting from experimental data
relevant to the biodegradation of PE-wax having 2900 Mw and 1100 Mn, respectively
(Kawai et al. 2002; Kawai et al. 2004). The computational model for the numerical
simulation was set up regarding to two main factors:
i) sample weight loss due to -oxidation;
ii) fast consumptions of low molecular weight fractions. Both factors were
substantiated by experimental data.
In particular the increase of both Mw and Mn of PE wax was observed after cultivation as an
indication of the microbial consumption, in the meanwhile the time profile of molecular
weight variation suggested the fast assimilation of the lower Mw fractions, as well as the
gradual decrease of assimilation rates with increase in molecular weight. By applying the
numerical model, which was validated by experimental results, to the biodegradation of PE,
the authors provide suggestions supporting the terminal oxidation and -oxidation as the
main processes involved in the microbial degradation of PE. In addition, by using this
approach it was possible to distinguish between the process of biodegradation as mediated by
bacteria such as Sphingomonads or Aspergillus sp. and Penicillium sp. fungi. It was
therefore evidenced that bacteria exhibited higher biodegradation rates that were attributed to
the higher affinity toward PE of Gram-negative bacteria cell walls with respect to the more
hydrophilic chitin walls of fungi (Kawai et al. 2004). Sphingomonas species were thought to
metabolize PE wax, preferentially with Mw below 2000, throughout primary terminal
oxidation followed by -oxidation with enzymatic systems located in the cell membrane
fraction, thus suggesting for the transport of oxidized PE wax into the periplasmic space
through outer membranes (Kawai 1999).
Regarding the capabilities of single microbial species to attack PE as carbon substrate, only a
few reports are so far available. Nevertheless, in the recent years evidences in the occurrence
of soil microorganisms directly involved in the biodegradation processes of PE have been
reported by Ohtake and collaborators (Ohtake et al. 1998; Watanabe et al. 2009).
1.7.3 Preliminary data or studies
Free radical oxidation, as induced by thermal and / or photolytic pre-abiotic treatment
constitutes the first step for promoting the fragmentation (Figure 1.15) and eventual
biodegradation of both LDPE and LDPE-containing pro-oxidant/pro-degradant additives.
This can be accomplished by monitoring the initial variation of sample weight, molecular
weight and other structural parameters (tensile strength, degree of crystallinity, level of
oxidation by FTIR and wettability by contact angle). Biodegradation is then observed when
degraded oxidized polymer fragments are exposed to biotic environments.
Chen Haiyan PhD Thesis
- 66 -
Figure 1.15. Fragmentation in outdoor exposure of PE Bags containing pro-oxidant/pro-
degradant additives
Additionally, the required degree of macromolecular breakdown for the microbial
assimilation of polyethylene to occur is substantiated by the observation of the propensity to
biodegradation of lower molecular weight hydrocarbon molecules. It has been demonstrated
that linear hydrocarbon having molecular weight below 500 (Potts 1972) or n-alkanes up to
tetratetracontane (C44H90, Mw = 618) (Haines and Alexander 1974) can be utilized as
carbon source by microorganisms. The degradation of higher molecular weight untreated
high-density poly(ethylene) with molecular weights up to 28,000 by a Penicillium
simplicissimum isolate it has been also reported (Yamada et. al 2001) even though the extent
of fungal attack of poly(ethylene matrix) has been monitored by physicochemical tools (FT-
IR, HT-GPC), and by growth-proliferation assays in agar plates containing the indicated PE
sample. No respirometric data have been unfortunately reported.
As the carbonyl group is representative of most of the oxidation products (carboxylic acids
ketones, aldehydes and lactones) (Hakkarainen and Albertsson 2004) of the oxidative
degradation of polyethylene, the concentration of carbonyl groups, as determined by the
carbonyl index (COi) can be used to monitor the progress of oxygen uptake and degradation
(Chiellini et al. 2006) . COi determinations have been therefore utilized in order to compare
the thermal oxidation behavior of test samples under dry and 75% relative humidity
conditions at 55 and 70°C (Chiellini et al. 2006).
First of all, the oxidation of the poly (ethylene) matrix in the thermally aged samples has
been clearly ascertained by the FT-IR spectroscopy. The increasing absorption and
broadening within time of the band in the carbonyl region has been recorded in all the
samples aged at 70°C . Overlapping bands corresponding to acids (1712 cm-1
), ketones (1723
cm-1
), aldehydes (1730 cm-1
) and lactones (1780 cm-1
) have been also observed, thus
indicating the presence of different oxidized species. Among these carboxylic acids and ester
groups have been shown to be produced in the early and later stages of polymer matrix
oxidation, respectively (Albertsson et al 1995). The increase of specimen weight up to a 4-
5% of the original value, as well as the increase of wettability of the thermally treated films,
Introduction
- 67 -
50,0
60,0
70,0
80,0
90,0
100,0
Conta
ct a
ngle
(°)
day 0 day 4 day 7 day 10 day 15
as determined by contact angle measurements, further demonstrated the polymer oxidation
(Figures 1. 16, 1. 17).
Figure 1. 16. Weight Variation Profile of LDPE Sample of LDPE Samples at Increasing
Level of Oxidation.
Figure 1. 17. Contact angle and density change Containing Pro-Oxidant Upon Aging at
70ºC
Thermally treated samples have been also characterized by HT-GPC, the recorded molecular
weight and molecular weight distribution (ID) have been compared with the COi values
detectable at the same time of thermal ageing (Chiellini et al. 2006). A drastic decrease of
Mw below 5 kDa and significant reduction of the ID have been thus recorded after a few
days of thermal degradation under both dry and 75% RH conditions. In HT-GPC
chromatograms relevant to LDPE samples retrieved at longest thermal degradation exposure,
thus having the highest level of oxidation, elution peaks having a bimodal shape and very
low (1.7 kDa) Mw fractions have been also detected. (Table 1.2)
Chen Haiyan PhD Thesis
- 68 -
Table 1.2 Molecular weight analysis of thermally oxidized LDPE-containing pro-
oxidant/pro-degradant additives
Figure 1.18. Relationship between the level of oxidation expressed as COi and Mw in
thermally oxidized LDPE-containing pro oxidant/pro-degradant additives.
The amount of oxidized degradation intermediates extractable by acetone, which can be
considered more prone to be diffused in the environment, has been shown to positively
correlate to the level of oxidation In addition, the relationship between the Mw and COi was
found to fit a mono-exponential trend (Figure 1.18).
Accordingly, COi values may be used in order to predict the rate of Mw decrease as a
function of the oxidation extent. Moreover, the recorded trend is in agreement with a
statistical chain cleavage mechanism, repeatedly suggested in the photophysical and thermal
degradation of polyolefin (Scott 1994; Gugumus 2001) thus reaching fairly high quantity
corresponding to 25-30% specimen weight (Figure 19).
Time COi Mw ID
(days) (kD)
0 0.61 39.4 4.24
1 1.14 19.5 2.96
2 2.32 9.7 2.59
9 5.44 4.5 1.27
Introduction
- 69 -
Figure 1. 19. Acetone extractable fraction of thermally oxidized LDPE-containing pro-
oxidant/pro-degradant additives
The recorded data have to be considered as partially representative of the overall amount of
low Mw fractions produced during the thermal oxidation of the test material. Indeed
molecular weights as low as 0.8-1.6 kDa for the acetone extracts of thermally treated
samples have been recorded by SEC. It is also worth noting that at higher level of oxidation,
increasing amounts of the extractable fractions are recorded, and in the meantime these
fractions are characterized by a very low Mw (Figure 14) (Chiellini et al. 2006). Therefore,
the reported data suggest that cross-linking reactions does not affect notably the oxo-
degradation behavior of the analyzed samples, which seems to proceed with cleavage of the
macromolecules up to low molecular weight fractions capable to be assimilated by
microorganisms (Volke-Sepŭlveda et al. 2002; Potts 1972; Kawai et al. 1999). Indeed, earlier
studies have demonstrated the microbial utilization as carbon source of the oxidation
products formed during the thermal and photo-oxidation of polyethylene (Arnaud et al.
1994). Accordingly, in a respirometric experiment, aimed at evaluating the biodegradation
behavior of low molar mass aliphatic hydrocarbons in soil, including linear docosane, (C22),
branched 2,6,10,15,19,23-hexamethyltetracosane, (Squalane - C30), and docosandioic acid,
(C22), a fairly high rate and extent of mineralization (70%) of the acetone extractable
1.49 kD
1.08 kD
1.06 kD
0.89 kD
0
5
10
15
20
25
30
COi 0.63 COi 2.24 COi 4.82 COi 5.44
Extract (%) Mw Extract (kD)
Chen Haiyan PhD Thesis
- 70 -
fraction from a thermally oxidized LDPE-TDPA sample was recorded (Chiellini et al. 2003).
(Figure 1.20)
Figure 1.20. Biodegradation profiles in soil burial respirometric tests of acetone extract of
pre-oxidized LDPE-TDPA samples and low molar mass aliphatic hydrocarbons.
This suggests that, similarly to low molar mass hydrocarbons, the oxidized fragments from
LDPE can be rapidly biodegraded in natural compartments (soil and surface waters).
There are several studies dealing on the evaluation of biodegradation of LDPE samples
containing pro-oxidant and natural fillers that show only limited and slow conversion to
carbon dioxide. The mineralization rate from long-term biodegradation experiments of both
UV-irradiated samples, non-pretreated, and additive-free LDPE samples, in natural soils
indicates more than 100 years for the ultimate mineralization of polyethylene (Ohtake et al.
1998).
In a soil burial test, carried out in the presence of forest soil as incubation media, the
biodegradation profile of a thermally pretreated LDPE-TDPA sample was monitored during
830 days of incubation (Chiellini et al. 2003). The recorded mineralization kinetic was
characterized by the presence of a first exponential step that approached a 4 % degree of
biodegradation within 30 days of incubation. Afterward, a prolonged (120 days) stasis in the
microbial respiration was recorded. At approximately five months of incubation it was noted
that a further and marked exponential increase in the biodegradation profile took place, thus
reaching the highest extent of biodegradation 63.0 %) after 85 weeks of incubation (Figure
1.21). This two-step mineralization profile of thermally fragmented LDPE-TDPA samples
has been repeatedly observed either in soil and mature compost biodegradation tests. In
contrast with previous studies (Ohtake et al. 1998; Albertsson et al. 1988 ), very large degree
of mineralization (70-80 %) have been then recorded, even though in a relatively long time
frame (more than 800 days) (Chiellini et al. 2003).
Figure 1.21. Biodegradation in soil burial respirometric tests of pre-oxidized LDPE-TDPA
samples
A substantial increase in the carbon-carbon unsaturation, as revealed by the increase of the
double bond index from 0.55 at the beginning to 0.88 after 62 weeks of incubation, was
recorded.
This can be attributed to enzymatically driven dehydrogenation (Ohtake et al. 1998;
Albertsson et al. 1998). Hence it is likely that the macromolecular cleavage of thermal-
Introduction
- 71 -
oxidized LDPE-TDPA can be achieved concomitantly by abiotic oxidation and biotic
enzymatically promoted action. Furthermore a dramatic change in the fingerprint region of
the FTIR spectrum between 1300 and 950 cm-1
was observed with increasing the incubation
time probably attributable to the presence of lower molecular weight fragments.
Therefore, it seems that the ongoing abiotic and biotic degradation of thermally degraded
LDPE-TDPA polymer bulk is occurring during the incubation in forest soil with the
production of large amount of degradation intermediates capable to be assimilated by the soil
microflora. This might explain the presence of the prolonged dormant phase (stasis), as well
the second, more pronounced, exponential phase repeatedly observed in the biodegradation
kinetic profiles of these materials recorded in soil burial respirometric tests.
A similar approach has been utilized in order to evaluate the propensity to biodegradation of
photo-degradable LLDPE samples for mulching purposes (Corti et al. 2010).
As expected, control sample without pro-oxidant/pro-degradant additives also showed a
steady increase in the COi but at a significantly slower rate compared to the level of
oxidation achieved in films with additives. The observed increase of COi in LLDPE films
under sunlight is attributed to the initiation of chain scission as a result of photo-oxidation
producing fragments in the form of shorter, more readily crystallizable molecules (Chiellini
et al. 2006; Chiellini et al. 2003; Sepúlveda et al. 1999).
The mere exposure to sunlight led to a considerably lowered value in the onset degradation
temperatures (Ton) in films with additives when compared to unexposed controls during
TGA analysis. As repeatedly ascertained, sunlight-induced aging resulted in the formation of
low molecular weight products
Photodegradable LLDPE films (LLDPE-TD1 and LLDPE-TD2) pre-exposed to sunlight for
93 days were submitted to biodegradation in the presence of single fungal strains previously
isolated from thermally oxidized LDPE fragments confined in forest soil.
A vibrant growth of mycelia on the surface of the film aged in sunlight was apparent
indicating a robust fungal metabolic activity. The growth of mycelia on the film surface
showing cracks in the film developing around the edge of mycelium were also visible at a
higher magnification (Figure 1.22) (Corti et al. 2010).
a) b) Figure 1. 22. SEM micrographs of the fungal mycelium mycelium growing on the surface of
outdoor exposed LLDPE-TD2 specimens (a). The b is a higher magnification of A, showing
fungal hyphae colonizing the film surface
A similar behavior has been also observed by Weiland et al. (Weiland et al. 1995) for
thermally oxidized PE films that were further treated in compost for a period of time. Film
surfaces were increasingly colonized by fungi as examined by SEM, and the increase in
fungal presence on the surface was accompanied by a decrease in molecular weight of the
film, providing a strong evidence of fungal bioassimilation of the amorphous regions of
Chen Haiyan PhD Thesis
- 72 -
thermally oxidized films.
The FT-IR spectra of the test and control samples reveal the prominence of absorption bands
attributed to the C=C within the polymer chain in films incubated with fungal strains.
Additionally, new absorption bands in the finger print region between 1700 – 1100 cm-1
of
the spectra and a considerably elevated -OH absorption peak in the OH stretching vibration
region, were also noticeable in the samples incubated with fungi for 65 days but not in the
controls. The appearance of new bands can be then associated with the formation of
metabolites generated by the fungal attack on the pre-oxidized fragments.
Mineralization tests were conducted to learn if soil fungi could utilize the breakdown
products derived from the oxidized LLDPE film as carbon source. To do this, pre-oxidized
LLDPE-TD1 film was incubated on a solid-agar media with soil fungi in the presence of
glucose as secondary carbon source. The control consisted of pristine LLDPE films that had
not been pre-exposed to sunlight.
The pre-oxidized LLDPE films submitted to the fungal exposure experienced an
enhancement in the amount of breakdown products as reflected by the increase in the FT-IR
peak intensities typical of several oxidized carbon functional groups. Interestingly, these
increases were only visible in pre-oxidized films incubated with fungi but not in controls.
This fact once again is pointing towards the synergistic impact of biotic and abiotic factors in
achieving efficient LLDPE degradation.
The information pertaining the level of photo-oxidation required to achieve an effective and
sustained biodegradation in LLDPE, is crucial for the design of LLDPE-based products and
prediction their environmental fate. Nowadays information with respect to synergistic effects
of microbial/enzymatic attack and physical-chemical parameters in promoting the
degradation of partially oxidized LLDPE can be provided. The data suggest that the
degradation of oxo-biodegradable LLDPE samples is enhanced by the synergistic action of
both abiotic and biotic factors after their initial oxidation by exposure to direct sunlight.
The data substantiate the validity of oxo-biodegradable polymers and confirm that PE films
with pro-oxidant/pro-degradant additives are environmentally degradable by means of a
combination of abiotic and biotic factors. Thus, several conclusions can be drawn from the
fungal biodegradation studies on LLDPE films with pro-oxidant/pro-degradant additives:
(a) Prolonged sunlight exposure causes considerable oxidation in these films leading to their
deterioration and to the production of degradation products,
(b) Soil borne fungi are fully capable of utilizing degradation products as a carbon source,
(c) Presence of an additional carbon source (under co-metabolic conditions) could stimulate
fungal metabolic activities to further promote the degradation of the LLDPE polymer matrix,
possibly mediated by hydrolytic enzymes produced by fungi and
(d) More effective degradation of films with pro-oxidant additives could be achieved by a
combined action of abiotic and biotic factors.
Objective
- 73 -
2. OBJECTIVES
The research activity of my Doctorate Thesis was aimed at the assessment of biodegradation
extent in different solid media (soil and compost) and river water of blends and composites
based on poly(lactic acid) (PLA) and a poly(hydroxyalkanoate) copolymer consisting of
97.5% 3-hydroxybutyrate (HB) and 2.5% of 3-hydroxyvalearte (HV) indicated from now on
as PHBV.
The biodegradability tests have been carried out on a few selected blends and composites of
PHBV used as continuous phase in comparison with paper as positive control and the PHBV
matrix alone. The PHBV polymer was blended with new additives such as chain extenders,
organic and/or inorganic fillers and the produced composites and blends were investigated
for their biodegradation propensity upon a thorough characterization of the physical and
mechanical properties of the samples.
The study highlighted the effect of each component on the kinetic profiles of the biobased
polymeric formulations.
The PHBV sample behaves as a rigid and brittle material due to its high crystallinity (Scott
2002, Maiti et al. 2007). In order to improve its mechanical properties, blends and
composites were prepared and submitted to a thorough physical chemical characterization.
Three different strategies were adopted:
1) Plasticization of PHBV with compatible and biodegradable plasticizer together with
nucleating agents
2) Blending of PHBV with biodegradable polymers poly (butylen adipate terephthalate)
(Ecoflex)
3) Combination of components applied in the 1 and 2 strategic approaches.
A reactive additive (Joncryl ADR-4368C) was used for its ability in controlling the polymer
molecular weight eventually occurring during its processing in the melt. It promotes indeed
the reactions between the epoxide groups of the additive and the end capping groups present
in the PHBV original chains. Until now, the utilization of PHAs in the production of
commodity plastic items is extremely limited, due to their high production cost with respect
to conventional petrochemical polymers. In particular the preparation of blends and
composites of PHAs with conventional polymers and agro-industrial wastes respectively
constitutes a strategic approach aimed at overcoming the drawback bound to the relatively
high cost/performance of the PHAs. For that reason a powder of hazelnut shells was used as
organic filler either alone or with other additives. Such filler increases by a few degrees the
melting temperature of the final composite.
Specimens of the prepared blends and composites were submitted to biodegradation tests in
solid media (compost and soil). The biodegradation of PHBV organic composites in soil
seems be favored by the presence of hazelnut shell powder, but Joncryl appears to delay
somewhat the propensity to biodegradation under the same environmental conditions. In
compost medium similar trends to those assessed in soil medium, were detected.
The propensity of synthetic and biobased plastics products, such as Ecoflex, Ecovio, PHBV
and PLA and their composites, to biodegradation in soil medium, was followed also from a
biological point of view. Different polymers as powder samples (polyethylene, polystyrene,
Ecoflex and cellulose) at concentration of 1% by weight, were added to the soil, with the aim
Chen Haiyan PhD Thesis
- 74 -
to monitor the meso-scale experiment consisting of soil sample carried out after one and 45
days from the experiment set up. Chemical, biochemical and biological parameters were
used to evaluate the soil conditioning during the polymer biodegradation. Furthermore, two
terrestrial plants, oat (Avena sativa) and red radish (Raphanus sativum), were used to
evaluate the phytotoxicity of the polymers. For this purpose, after 35 days from the
experiment set up, 100 seeds of each plant species were sown uniformly in each pot. The
upper growth was checked at the end of the experiment. Polymers stimulated soil metabolic
activity, thus indicating their possible biodegradability in soil. These effects were more
evident in Radish treatments than in Avena, suggesting the higher sensitivity of radish to the
polymers treatment.
Meanwhile, the depolymerase activity of polymers was also determined as further
investigation to know the enzyme activity effect on the biobased polymers PHB and PLA.
Experiment
- 75 -
3. EXPERIMENTAL PART
3.1. Materials
3.1.1. Reagents and Solvents
The reagents and solvents employed in the experimental part and their respective
suppliers are listed below:
Potassium hydroxide pellets, technical grade (KOH), was supplied by CARLO
ERBA (Rodano-Milan-Italy).
Hydrochloric acid (HCl) volumetric standard, 0.1N, analytical grade, was supplied
by J.T.Baker (Italy).
Barium chloride (BaCl2), technical grade was purchased from CARLO ERBA
(Rodano-Milan-Italy).
3.1.2. Joncryl ADR-4368-CS
Joncryl ADR-4368-CS is a chain extender suitable for food packaging applications, supplied
by BASF, The Chemical Company (Germany) as a white granulate or a powder
characterized by a granulometry similar to the sugar one (Figure 3.1).
Figure 3.1. Powder of Joncryl ADR-4368CS.
Its chemical structure (Figure 3.2) shows the presence of epoxy groups able to react with the
terminal carboxylic and hydroxy groups of the polymer chains preventing the formation of
degradation products and oligomers with short chain during the reactive extrusion process.
Figure 3.2. Joncryl ADR-4368C Chemical Structure.
Chen Haiyan PhD Thesis
- 76 -
Table 3.1 reports the physical features of the material.
Table 3.1. Physical Features of Joncryl ADR-4368CS.
Property Value
Density at 25°C (g/cm3) 1.08
Mw (Da) 6800
Tg (°C) 54
Equivalent Epoxy Weight (g/mol) 285
Ton (°C) 320
Figure 3.3 shows the IR spectrum for the chain extender Joncryl ADR-4368CS.
Figure 3.3. Spettro IR per il Joncryl ADR-4368CS.
3.1.3. Hazelnut Shells
The hazelnut shells (Figure 3.4), supplied by Ferrero S.p.A (Italy), were grinded in a mill
Brabender Wiley, with a tri-phase engine (power = 0.75 kW), equipped with four static, six
strong blades and four interchangeable sieves (0.5 mm, 2 mm, 3 mm, 4 mm).
The material was sieved until the obtainment of a particle dimension of 39 micron: this value
results to be suitable for a good dispersion of the organic filler inside the polymeric matrix.
(a) (b)
Figure 3.4. Raw Hazelnut Shells (a) and After Grinding (b).
Experiment
- 77 -
The typical chemical composition for hazelnut shells is collected in Table 3.2, whereas
Figure 3.5 shows the IR spectrum for the obtained ligno-cellulosic material.
Table 3.2. Hazelnut Shells Chemical Composition.
Components (%) Hazelnut Shells
Lignin 45.5
Hemicellulose 9.5
Cellulose 24.97
Hydro-soluble Substances 9.9
Ashes 1.27
Fats & WAxes 1.2
Figure 3.5. IR Spectrum for the Ligno-cellulosic Sieved Below 39 Micron.
3.1.3.1. Lignin Functionalization
The functionalized lignin is obtained by using an acid catalyzed Fisher esterification.
The reactions have been carried out according to the Dean-Stark method. Typically, the
reactions have been carried out in 500 ml two necked round bottom flask equipped with a
Dean-Stark trap and a 20 ml addition funnel, by suspending 5.0 g LN in 100 ml toluene.
After 1 h at reflux a solution of 2.5 g of stearic acid (STEA) and 100 mg of p-toluensulfonic
acid monohydrate (pTSA), both supplied by Sigma-Aldrich, in 20 ml toluene was added
drop-wise and the reaction mixture was maintained other 5-7 h at reflux. After cooling under
N2 the suspended solid was recovered by vacuum filtration, washed with 50 ml of acetone to
remove the un-reacted aliphatic acid and finally dried under vacuum up to constant weight
before characterization.
In this way, the lignin becomes more hydrophobic and compatible with the polymeric
material.
3.1.4. Organophilic Clay (Dellite 72T)
Dellite 72T, supplied by Laviosa Mineraria S.p.A (Italy) as white powder, is a nano-clay
deriving from a natural purified montmorillonite modified with quaternariy ammonium salt.
Its density is 1.7 g/cc while the humidity can be reaching a value of 3%. This clay is directly
mixed in the composite with the aim to improve the O2, CO2 and water vapour barrier
properties.
Figure 3.6 shows the IR spectrum for this material.
Chen Haiyan PhD Thesis
- 78 -
Figura 3.6. IR Spectrum for Dellite 72T.
3.1.5. Perkalite F100
Perkalite F100 is a sinthetic clay organically modified and consisting of a double hydoxide
layers (LDH), named hydrotalcite. The polymer loading with Perkalite makes favourable the
clay delamination at nano-scale level, improving the thermo-mechanical, the barrier and
rheological properties of the polymeric materials.
3.1.6. Poly(3 hydroxy-co-3 valerate) (PHBV)
PHBV chemical structure is reported in Figure 3.7 while in Table 3.4 are summarized the
main thermal and mechanical properties of PHBV and commercial PHA copolymers,
compared with polypropylene and low density polyethylene (LDPE).
Figure 3.7.. Chemical Structure for Poly(3hydroxybutyrate – co – 3-hydroxyvalerate)
(PHBV).
O CH CH2 C
O
O CH CH2
CH2CH3CH3
C
O
* *
nm
Experiment
- 79 -
Table 3.4. PHB and Copolymers, Polypropilene (PP) and Low Density Polyethylene (LDPE)
Physical Properties[Scott 2002].
Property PHB 20V1)
6HA2)
PP LDPE
Melting Temperature, (˚C) 175 145 133 176 110
Glass Transition Temperature (˚C) 4 -1 -8 -10 -30
Cristallinity, % 60 ng ng 50 50
Density (g/cm3) 1,25 ng ng 0,91 0,92
E module, MPa 3,5 0,8 0,2 1,5 0,2
Tesile Stress, MPa 40 20 17 38 10
Strain at Break, % 50 680 400 600 400
1) poly(3-hydroxybutyrate-co-20 mol% 3-hydroxyvalerate)
2) poli(3-hydroxybutyrate-co-6 mol% HAs) [HAs (hydroxyalkanoate) = 3 %
3-hydroxydecanoate, 3% 3-hydroxydodecanoate, < 1% 3-hydroxyoctanoate, < 1%
5-hydroxydodecanoate, ng= negligible].
Table 3.5. General Properties for PHBV ENMAT Y1000.
Property Value Determination Method
Molecular Weight (Mw,
kDa)
450 GPC in chloroform
Polydispersity Index (IP) 1.5 GPC in chloroform
Appearance White
Powder
Visual observation
Melting
Temperature(Tm, °C)
167 DSC Mettler Toledo DSC822°
Standard Method:
1st heating from 25°C until to 200°C, withan
heating rate of 10°C/min and 80 ml/min N2
Isotherm for 3 min. at 200°C and 80 ml/min N2
Cooling from 200°C until to -50 °C with a
cooling rate of 10°C/min and 80 ml/min N2
Isoterma 1 min. a - 50°C 80 ml/min N2
2nd heating dfrom -50°C until to 200°C, with an
heating rate of 10°C/min and 80 ml/min N2
Glass Transition
Temperature (Tg, °C)
3-4 DSC Mettler Toledo DSC822
Cristallinity (%) 75 Xc = (ΔHm/ΔHm100%)100 where ΔHm PHBV100% cristalline =
146 Jg-1
Valerate Content (mol %) 2 1H-NMR spectrum Varian Gemini VRX 200
Onset temperature
(Ton, °C)
258 TGA
Chen Haiyan PhD Thesis
- 80 -
Figure 3.8. Picture of Commercial PHBV in powder form.
Figures 3.9-3.11 show all the characterizations (IR,DSC, NMR) for PHBV ENMAT.
Figure 3.9. IR Spectrum of PHBV ENMAT Sample.
Figure 3.10. DSC Thermograms of PHBV ENMAT Sample recorded at Different Scanning
Conditions (2nd Heating).
Experiment
- 81 -
Figure 3.11. 1H-NMR Spectrum of PHBV ENMAT Sample.
3.1.7. Poly(lactic acid) (PLA)
PLA was supplied by Proplast (Alessandria-Italy) as opaque granules (Fig. 3.12b) and the
polymer chemical structure is reported in Figure 3.12a.
(a) (b)
Figura 3.12. PLA Chemical Structure (a) and powder Shape (b).
The D isomer content, as indicated by NatureWorks, is comprised in the range of 1.2-1.6%.
The molecular weight is below 160 kDa and the polidispersity index (Mw/Mn) is 2.31.
Figure 3.13 shows the IR spectrum for pure PLA sample.
O CH
CH3
C
O
OHH
n
Chen Haiyan PhD Thesis
- 82 -
Figure 3.13. IR Spectrum fof PLA Sample.
3.1.8. Poly(butylene adipate-co-terephthalate) (Ecoflex)
Ecoflex® FBX 7011 is a biodegradable, statistical, aliphatic-aromatic copolyester consisting
of 1,4–butanediol, adipic acid and terephthalic acid monomers (Figure 3.14), supplied by
BASF The Chemical Company (Germany) as an white powder.
Figure 3.14. Ecoflex Chemical Structure.
It has properties (Table 3.6), similar to LDPE, that make it suitable for film extrusion.
Table 3.6. General Features for Ecoflex Sample.
Property Value
Density (g/cm3) 1.25-1.27
Melt Flow Rate (g/10 min)
(MFR, 190°C and 2.16 Kg)
2.7-4.9
Melt Volume Rate (mL/10 min)
(MFR, 190°C and 2.16 Kg)
2.5-4.5
Melting Temperature (Tm, °C) 110-120
Shore Hardness (D) 32
Vicat Point (°C) 91
Trasparency (%) 82
E module (N/mm2) 95-80
Tensile Strength (N/mm2) 35-40
Ultimate Strength (N/mm2) 36-45
Elongation (%) 560-710
Failure Energy (J/mm) 24
Oxygen Transmission Rate (cm3/ m
2d*bar) 1400
Water Vapour Transmission Rate (g/m2*d) 170
Figure 3.15 reports the IR spectrum for Ecoflex sample.
HO C
O
CH24
C
O
O CH2 O4
C
O
C
O
OH
Experiment
- 83 -
Figure 3.15. IR Spectrum of Ecoflex Sample.
3.1.9. Ecovio
Ecovio F Blend C2224, supplied by BASF Chemical Company (Germany) as white granules,
is a biodegradable co-polyester consisting of Ecoflex and PLA (45% by weight).
This material results suitable for packaging applications by flexible and compostable films
production.
Table 3.7 shows the general features of Ecovio F Blend C2224.
Table 3.7. General Features of Ecovio F Blend C2224 Sample.
Property Value
Melting Temperature (Tm, °C) 140-155 (PLA)
110-120 (Ecoflex)
MVR (mL/10 min)
(190°C, 2.16 Kg)
< 2.5
MVR (mL/10 min)
(190°C, 5 Kg)
< 6.5
Vicat Point (°C) 68
E module (N/mm2) 520-750
Tensile Strength (N/mm2) 27-35
Ultimate Strength (N/mm2) 27-36
Elongation (%) 250-320
Oxygen Transmission Rate (cm3/ m
2d*bar) 600
Water Vapour Transmission Rate (g/m2*d) 92
Chen Haiyan PhD Thesis
- 84 -
Figure 3.16 shows the IR spectrum of Ecovio sample.
Figure 3.16. IR Spectrum of Ecovio Sample.
3.2. Preparation of the Sample
3.2.1. Pre-blend
The composites were prepared by blending all the components manually and these pre-
mixtures were then dried in an oven at 80°C overnight (in order to remove the major amount
of moisture). The blends and composites compositions are collected in Table 3.8. In
particular, the blends and composites loaded with the polymeric chain extender Joncryl (J)
were dispersed at room temperature in a mixer at 2 rpm for a time of 35 min.
3.2.2. Melt blending
The obtained PHBV and PLA samples (Tables 3.8-3-9) were melt-blending in an internal
mixer chamber (55 cc) connected to a Brabender plastograph (Germany) (Figure 3.17).
The processing conditions were 30 rpm, residence time 7 min to 170oC and mixture weight
of 30 g for PHBV based blends and composites whereas for the PLA ones, were: 60 rpm,
residence time 7min at 180°C, mixture weight 40 g.
Figure 3.17. Brabender-Plastograph Apparatus
Experiment
- 85 -
Table 3.8. Composition of Organic, Inorganic and Hybrid Composites Based on PHBV.
Sample code PHBV
(% wt)
Lignin
(% wt)
(LN)
Joncryl
(% wt)
(J)
Inorganic
(% wt)
(D) (LHD)
PHBV 100 - - -
PHBV + J0.2 99.8 - 0.2 -
PHBV + J2 98 - 2 -
PHBV + J5 95 - 5 -
PHBV + LN5 95 5 - -
PHBV + LN10 90 10 - -
PHBV + LN20 80 20 - -
PHBV + LN10 + J5 85 10 5 -
PHBV + LN20 + J5 75 20 5 -
PHBV + LDH3 97 - - 3
PHBV + D3 97 - - 3
PHBV + D6 94 - - 6
PHBV + D3 + J2 95 - 2 3
PHBV + LN10 + D3 87 10 - 3
PHBV + LN20 + D3 77 20 - 3
PHBV + LN10 + D3 +
J2
85 10 2 3
PHBV + LN20 D3 + J2 75 20 2 3
PHBV + LNF10a)
90 10 - -
Table 3.9. Composition of Organic and Hybrid Composites Based on PLA.
Sample Code PLA
(%-wt)
Lignin
(LN)
(%-wt)
Joncryl
(J)
(%-wt)
PLA 100 - -
PLAJ0.2 99.8 - 0.2
PLAJ5 95 - 5
PLALN10 90 10 -
PLALN20 80 20 -
PLALN10J5 85 10 5
PLALN20J5 75 20 5
3.2.3. Press
The mixtures coming from Brabender had been processed by using a press. About 5-8 g of
blend were compression moulded in a laboratory mould press Collin (model Collin P 200E)
with a water cooling system to obtain round films of width around 300-500 m and diameter
of 12 cm.
The plate of the press has dimensions about 196x196 mm and maximum compression force
about 125 kN. Moulding conditions were constituted by an heating cycle until to 170-180°C
Chen Haiyan PhD Thesis
- 86 -
for 5 minutes by using a pressure of 200 bar following by a cooling cycle until room
temperature for 8 minutes.
3.3 Characterization of the Samples
3.3.1. Thermogravimetric Analysis (TGA)
TGA analyses were performed with a Mettler Thermogravimetric Analyzer TA500 equipped
with a Mettler TG50 furnace and a Mettler M3 microbalance.. About 10 mg of the samples
were heated from 30°c to 700°C and heating rate of 10°C/min, in air atmosphere (flux about
80 ml/min) and nitrogen atmosphere (about 60 ml/min). The onset temperature (Ton
), at
which the material starts to decompose, was determined as the temperature corresponding to
the tangent‘s intersection on both sides of the decomposition trace. The residue was
evaluated as the residual weight at the end of the experiment.
3.3.2. Differential Scanning Calorimetry (DSC)
The prepared samples (5-10 mg) were analyzed by using a differential scanning calorimeter
Mettler-Toledo, DSC Model-822 equipped with a sensor FRS5 connected to a STARe
software. The samples were placed in 40 μl aluminium pans, while an empty one was used as
reference. The temperature calibrations were performed utilizing indio, iron and zinc as
standards.
The standards were used in order to perform enthalpy (∆H) calibration.
The DSC thermograms were recorded according to the following scheme:
Heating from 25 °C to 200 °C, 10 °C/min @ 80 ml/min (N2 flux)
Isotherm @ 200 °C for 3 min. @ 80 ml/min (N2 flux)
Cooling from 200 °C to -50 °C, 10 °C/min @ 80 ml/min (N2 flux)
Isotherm @ - 50°C for 1 min. @ 80 ml/min (N2 flux)
Heating from -50 °C to 200 °C, 10 °C/min @ 80 ml/min (N2 flux)
3.3.3. Transmision Fourier Transform Infrared Spectroscopy (FTIR)
Fourier transformed infrared (FT-IR) spectroscopic characterization of the analyzed
materials was carried out with a Jasco model 410 spectrophotometer. The spectra were
recorded as an average of 16 scans with a resolution of 2 cm-1
.
3.3.4. Nuclear Magnetic Resonance (1H-NMR)
1H-NMR spectra were recorded with a Varian Gemini VRX 200 from solution of the
polymer samples in CDCl3. This characterization allows us the assessment for the structural
features in terms of monomeric units‘ composition of the polymer samples.
3.3.5. Gel Permeation Chromatography (GPC)
The molecular weights, comprised in the linear range 200-2.000.000 Da, were determined by
using an HPLC cromatograph, mod. Jasco PU-1580, connected with two spectrofotometric
detectors (λ = 260 nm), Jasco 830-RI for the infrared frequences and Perkin-Elmer LC-75 for
the ultraviolet ones and equipped with two microcolumns (5 microliters) PLgel.
Chloroform stabilized with amylene were employed as eluent with a flux of 1.0 ml/min.
Experiment
- 87 -
The average molecular weight for the selected samples was calculated by considering the
calibration curve, which was obtained for standards monodisperse polystyrene samples.
3.3.6. Determination of Total Organic Carbon (TOC) and Total Nitrogen (TN)
Total organic carbon (TOC) and total nitrogen (TN) were determined by RC- 412
MULTIPHASE CARBON DETEMINATOR (RC-412 LECO®, ST. JOSEPH. MI 49085-
2396, U.S.A) and FP-528 PROTEIN/NITROGEN (Leco corporation), respectively.
To test the total organic carbon (TOC) of original polymeric samples, EDTA (EDTA. CAL
IBRATION SAMPLE; Part No. 502-092; CARBON %, 41.01±0.13; HYDROGEN %,
5.56±0.02; NITROGEN, 9.58±0.02; LECO CORPORATION. U.S.A ) was used as
calibration standard.
3.3.7. PH and Electrical Conductivity
The pH and electrical conductivity were determined on the aqueous extracts (1 hour at room
temperature under shaking) using the 672 TITROPROCESSOR (Thermo) and the ION
SELECTIVE ELECTRODES (Electron Corporation N-1017969), respectively.
3.4. Experimental Setup for Biodegradation Experiments
3.4.1. Soil Burial Biodegradation Tests
A soil burial respirometric test specifically set up from ISO 17556 (17556-03 ―Plastics –
Determination of the ultimate aerobic biodegradability in soil by measuring the oxygen
demand in a respirometer or the amount of evolved carbon dioxide‖) and ASTM D5988
(ASTM D5988 - 03 ―Standard Test Method for Determining Aerobic Biodegradation in Soil
of Plastic Materials or Residual Plastic Materials After Composting‖)standard test in order
to test polymeric materials with low or moderate propensity to biodegradation, was utilized
to investigate the ultimate biodegradation behaviour of PHBV based samples. In this test
procedure the soil is partially substituted with a hygroscopic inert mineral substrate (perlite)
that ensure satisfactory incubation conditions and in the mean time a more favourable ―signal
to noise ratio‖ resulting in improved accuracy particularly when limited carbon dioxide
emissions are expected from the mineralization processes of the test samples (Chiellini E.
and Corti A. 2003).
A natural forest soil sample (Table 3.10), sieved at 1 mm in order to remove any plant and
root debris, was used as incubation substrate because its richness in microbial population
capable to metabolize a wide spectrum of organic compounds including aromatic
hydrocarbons.
Chen Haiyan PhD Thesis
- 88 -
Table 3.10. Soil Sample Properties.
Property Value
Electrical conductivity (dS m-1
) 0.15
pH 6.71
Total Nitrogen (TN, %) 0.16
Total Organic Carbon (TOC, %) 1.46
Total Inorganic Carbon (TIC, %) 0.01
Holding Water Capacity (WHC, %) 20.0
Electrical Conductivity (distilled water: soil, 5:1); TN, Total Nitrogen; TOC, total Organic
Carbon; TIC, Total Inorganic Carbon; WHC, Water Holding Capacity.
The tests were carried out in cylindrical glass vessels (Biometer Flask) (750 ml capacity)
containing a multilayer substrate in which defined amounts of forest sandy soil (10 g) sample
were mixed with 15 g of perlite and supplemented with 10-15 ml of 0.1% (NH4)2HPO4
solution. Finally the mixtures were sandwiched between two layers consisting of 20 g perlite
and wetted with 30 ml distilled water.
Filter paper (FP) was used as reference compounds with the aim to validate the adopted test
procedure.
Test materials and reference compound were tested at approximately 50 mg/g dry soil ratio,
in duplicate runs. All the cultures were incubated at 25°C in the dark.
Figures 3.18 and 3.19 collect the pictures showing the starting material and the final
soil/perlite mixture, respectively.
Figure 3.18. Starting Materials and Final Pre-Treated Soil.
Figure 3.19. Pre-Treated Soil (Blend of Soil, Perlite and Water).
Experiment
- 89 -
Under the adopted conditions, the biodegradation behaviour was assessed for PHBV based
composites prepared with a ligno-cellulosic material derived from the grinding of Hazelnuts
shell (organic filler), Dellite 72T (organically modified montmorillonite as inorganic filler)
kindly supplied by Laviosa Mineraria S.p.A (Italy), and special additives like polymeric
chain extender, Joncryl ADR-4368C (Basf-Germany).
In Table 3.11 the PHBV based samples compositions and the relevant sample amount used
for the biodegradation test, are reported. The particle size for the PHBV composites was < 2
mm (mesh n° 10). Figures 3.20 and 3.21 are showing the biodegradation set up design and
the final sample shape of the PHBV composites, respectively.
Figure 3.20. Biodegradation Experimental Setup (Respirometric Apparatus).
Figure 3.21. Polymer Test PHBV Composite Samples.
Chen Haiyan PhD Thesis
- 90 -
Figure 3.22. Mineralization Test System for Biodegradation.
Experiment
- 91 -
Table 3.11. Sample Composition for the Biodegradation Test in Soil.
Test Sample Code Description (weight %) Shape Sample 1
(mg)
Sample 2
(mg)
PHBV PHBV powder 382.4 380.1
PHBV-LN20-D3-J2 PHBV+20%
Lignin+3%Dellite+2% Joncryl
powder 380.7 380.3
PHBV-LN20 PHBV+20% Lignin powder 381.5 380.4
PHBV-LN20-J50 PHBV+20% Lignin+50% Joncryl powder 380.8 380.0
PHBV-LN20-D3 PHBV+20% Lignin+3% Dellite powder 380.1 380.5
PHBV-D3-J2 PHBV+3% Dellite+2% Joncryl powder 380.8 381.1
PHBV-LN10-D3-J2 PHBV+10% Lignin+3%
Dellite+2% Joncryl
powder 380.3 382.6
PHBV-LN10 PHBV+10% Lignin powder 381.7 380.0
PHBV-LNF10 PHBV+10% Functionalized
Lignin
powder 384.1 381.6
PHBV-D3 PHBV+3% Dellite powder 380.8 384.7
PHBV-J5 PHBV+5% Joncryl powder 380.3 382.4
PHBV-LN10-J5 PHBV+10% Lignin+5% Joncryl powder 381.3 382.7
PHBV-LN10-D3 PHBV+10% Lignin+3% Dellite powder 381.2 384.2
Cellulose Cellulose powder powder 382.2 381.6
LN: Lignin from Hazelnuts shell; D: Dellite (inorganic component); J: Joncryl (Chain
extender useful for polyesters); LNF: Functionalized lignin with stearate groups.
3.4.2. Mature Compost Respirometric tests
Mature compost respirometric tests specifically set up from ISO 14855 standard (ISO 14855-
99 “Plastics – Evaluation of the ultimate aerobic biodegradability and disintegration of
plastics under controlled composting conditions – Method by analysis of released carbon
dioxide) in order to test polymeric materials with low or moderate propensity to
biodegradation, was utilized to investigate the ultimate biodegradation behaviour of PHBV
and PLA test materials (Chiellini E. and Corti A. 2003).
The tests were carried out in cylindrical glass vessels (Biometer Flask) (750 ml capacity)
containing a multilayer substrate in which defined amounts of mature compost from organic
solid waste (Table 3.12), sieved at 1.0 mm (7 g dry weight) sample were mixed with 15 g of
perlite. Finally the mixtures were sandwiched between two layers consisting of 20 g perlite
and wetted with 30 ml distilled water. Filter paper (FP) as reference compound was used in
order to validate the adopted test procedure.
Chen Haiyan PhD Thesis
- 92 -
Table 3.12 Compost Parameters.
Parameters U. M. Value Limit(*) Methods
Humidity at 105 ℃ % 29.5 <50% s.t.q. UNI 10780/98
pH unit pH 7.3 6-8.5 EPA 9045D 2002
Ratio C/N - 27.5 <50 UNI 10780/98
Organic Corban (as C) % s.s. 35.5 >20 UNI 10780/98
Humic acids + Fulvic
acids (as C)
% s.s. 7.3 >2.5 UNI 10780/98
Organic Natrogen (as N) % s.s. 87.4 >80% Nitrogen tot. UNI 10780/98
Total Nitrogen % s.s. 1.29 - UNI 10780/98
Salinity meg/100g 11.8 - UNI 10780/98
Cadmium mg/kg s.s. <0.1 1.5 UNI 10780/98
Mercury mg/kg s.s. <0.1 1.5 UNI 10780/98
Nickel mg/kg s.s. 18.7 100 UNI 10780/98
Sodium mg/kg s.s. 500 - UNI 10780/98
Lead mg/kg s.s. 7.9 140 UNI 10780/98
Copper mg/kg s.s. 24.2 230 UNI 10780/98
Zinc mg/kg s.s. 34.6 500 UNI 10780/98
Chromium Hexavalent mg/kg s.s. <0.01 0.5 UNI 10780/98
Plastic, Glass and Metals>
2mm
% s.s. <0.01 0.5 UNI 10780/98
Lithoid aggregates> 5 mm % s.s. 0.45 5.0 UNI 10780/98
Test materials and reference compound were tested at approximately 25 mg/g dry mature
compost ratio, in duplicate runs. All the cultures were incubated at 58 ± 2°C in the dark.
The pre-treated compost was stabilized until the evolution of carbon dioxide was comprised
between 50 and 150 mg/g of solid in 10 days according to the international norm ISO 14855-
99.
In a first step the biodegradation in the process of mature compost was carried out without
carbon dioxide monitoring for screening purposes by analyzing the physical changes of the
samples as well as the weight loss within the time of the most representative samples related
to PHBV and PLA based composites. The tests in compost were carried by placing the
sample on a layer of a pre-treated compost. The pretreated compost was prepared in a similar
way as the biodegradation test in soil. The control parameters in this case were the humidity
inside the chamber (must be 50%) and the ratio compost/Perlite 1:2 by weight. In Figure 3.23
the biodegradation setup design for qualitative experiment in mature compost is depicted.
The respirometric biodegradation test in mature compost was carried out by analyzing the
propensity to mineralization of PHBV and PLA based composites prepared with a ligno-
cellulosic material derived from the grinding of Hazelnut shells (organic filler) and special
additives like polymeric chain extender, Joncryl ADR-4368C.
In Table 3.13 the composition and shape for PHBV and PLA relevant based composites
submitted to the respirometric test, are collected. The particle size for the PHBV and PLA
Experiment
- 93 -
composites was < 2 mm (mesh n° 10). The biodegradation test set up for compost was
similar to the biodegradation set up in soil (see Figure 3.23).
Figure 3.23. Biodegradation Setup for Compost tests (for Screening Purpose).
Table 3.13. Composition and Shape for Selected PHBV and PLA Based Composites.
N Test Sample Code Description
(% in wt.)
Shape Sample 1
(mg)
Sample 2
(mg)
1 PHBV PHBV film 146.4 134.1
2 PHBV-J5 PHBV + 5 % Joncryl film 145.0 149.2
3 PHBV-J0.2 PHBV + 0.2 % Joncryl film 148.9 167.3
4 PHBV-LN20 PHBV + 20 % Lignin film 148.3 142.5
5 PHB-LN20-J5 PHBV +20 % Lignin +5 %
Joncryl
film 146.1 148.3
6 PLA PLA film 165.0 154.0
7 PLA-J0.2 PLA + 0.2 % Joncryl film 156.0 158.0
8 PLA-J5 PLA + 5 % Joncryl film 148.0 145.0
9 PLA-LN20 PLA + 20 % Lignin film 156.0 147.0
10 PLA-LN20-J5 PLA +20 % Lignin +5 %
Joncryl
film 157.0 142.0
3.4.3. River Water respirometric Test
The biodegradation test was carried out in accordance with the OECD 301 Guideline for
testing of chemicals and in particular with the OECD 301 B method ―CO2 evolution
(Modified Sturm Test)‖ The test was carried out in 300 ml Erlenmeyer flasks equipped with
silicone rubber stoppers hanging 40 ml capacity plastic vials filled with CO2 absorbing KOH
solutions (Figure 3.24). Each flask contained 100 ml of salt solution as incubation medium
having the following composition per liter of distilled water: KH2PO4 85 mg, K2HPO4 218
mg, Na2HPO4 334 mg, (NH4)2SO4 10 mg, NH4NO3 10 mg, CaCl2 36 mg, MgSO4·7H2O 23
mg, and FeCl·6H2O 0.3 mg, pH 7.4±0.2 A river water sample was used as microbial
inoculum at 10% by volume ratio.
Chen Haiyan PhD Thesis
- 94 -
All the test materials were supplied to the microbial culture as sole carbon sources at 0.01-
0.02% by weight concentration.
Test flasks were then incubated at room temperature (25°C) in the dark on a rotatory shaker
(120 rpm). All the runs were carried out in duplicate. Every 5 -7 days CO2 absorbers,
containing 20 ml of KOH solution (0.05 N) will be retrieved and replaced with fresh KOH
solution in known aliquots. The retrieved KOH solutions were back-titrated with 0.1 N HCl
and the amount of adsorbed CO2 was computed.
At the end of the test all the test materials were withdrawn from aqueous cultures, carefully
washed and characterized by gravimetric analysis (e.g. weight variation), FT-IR
spectroscopy and thermal analysis (TGA and DSC).
Figure 3.24. Schematic Representation of Aqueous Medium Biodegradation Tests.
3.4.4. Carbon Dioxide Determination and Evaluation of the Degree of Biodegradation in
Respirometric Tests
The evaluation of biodegradation degree in the respirometric test is based on CO2
determination in the headspace of the culture vessels (biometer flask). CO2 evolution, inside
a sealed biometer, is a consequence of the microbial assimilation of the test sample, and it
can be trapped in each test vessel by means of 40 ml of 0.05N KOH solution contained in a
beaker set in the test vessel. The absorbing solution was back-titrated with 0.1N HCl at time
intervals. The addition of 1 ml of barium dichloride (BaCl2) 0.5N before the titration in one-
tenth proportion respect to the overall volume of the absorbing alkaline medium, was
necessary for the carbonate anions precipitation as an insoluble barium carbonate (BaCO3)
salt. Phenolphthalein was used as indicator. All the tests were carried out in duplicate.
Subsequently, biometer was recharged with a fresh KOH solution and immediately closed.
Eventually distilled water (20 to 25 ml) was added into the flask in order to control the
humidity inside the vessel. This procedure cycle was repeated periodically up to the end of
experiment. The above procedure is based on the following reactions:
Carbon dioxide uptake by KOH solution
CO2 + 2 KOH→K2CO3 (soluble) + H2O
Insoluble barium carbonate formation
K2CO3 + BaCl2→BaCO3 (insoluble) + 2 KCl
Experiment
- 95 -
To determine complete or ultimate aerobic biodegradability (mineralization to CO2), it is
necessary to know the initial amount of organic carbon (TOC) in the sample and the relevant
theoretical amount of CO2 (ThCO2).
The amount of TOC was calculated as follow:
CS = TOCS * WtS TOC=Cs*Ws
Where CS is the % amount of carbon in the sample, TOCS is the relative amount of total
organic carbon in the sample at time 0 and WtS the weight of sample.
The extension of biodegradation defined as mineralization percent was calculated by
subtracting the accumulated CO2 content evolved into the biometers of sample (CO2)S from
that of blank (CO2)B. The difference found is divided by the theoretical amount of CO2
(ThCO2) as calculated on the basis of the carbon content of the test sample
Biodegradation (%) = 100*[(CO2) S - (CO2) B]/ThCO2
All the biodegradation rate calculation are based on the European standard EN 14046-03:
Packaging - Evaluation of the ultimate aerobic biodegradability of packaging materials
under controlled composting conditions - Method by analysis of released carbon dioxide.
3.5. Specific Biotests to Assess Eco-toxicity of Biodegradable Polymer Materials
Ecoflex, PE, PS in Soil-Plant systems
In the present investigation, the extent of biodegradation and potential eco-toxicological
effects of synthetic biodegradable biomaterials were investigated under laboratory conditions.
3.5.1 Materials
3.5.1.1. Soil and Plants used in the experiments
Chen Haiyan PhD Thesis
- 96 -
The characteristics of the soil used for the laboratory experiment are reported in Table 3.14.
Table 3.14. Chemical, Biochemical and Microbiological Parameters of the Soil Used in the
Experiment
Soil characteristics
Original soil umidity (%) 3.26±0.13
pH 6.93±0.27
Electrical conductivity (dS m-1
) 114±1.4
Total organic carbon (%) 2.50±0.03
Total Nitrogen (%) 0.323±0.01
NO3- (mg kg
-1) 234±6
NH4+ (mg kg
-1) 3.43±0.72
Available Cu (mg kg-1
) 77.8
Available Zn (mg kg-1
) 17.48
Available K (mg kg-1
) 323
Available Mg (mg kg-1
) 108
AvailableFe (mg kg-1
) 19.4
Available P (mg kg-1
) 27.5±3.8
Total Cu (mg kg-1
) 64±7
Total Zn (mg kg-1
) 58±23
Total Ni (mg kg-1
) 63.6
Total Pb (mg kg-1
) 26.7
Total Cr (mg kg-1
) 41.9
Total Cd (mg kg-1
) 0.3
Total K (mg kg-1
) 6076±1067
Total Mg (mg kg-1
) 6890±583
Total Fe (mg kg-1
) 8395±1097
Total cultivable microbial population (UFC g-1
) 5.34E+07±7.31E+06
Pseudomonas (UFC g-1
) 4.1E+05±4.9E+02
β-glucosidase activity (mgPNP kg-1
h-1
) 580
Dehydrogenase activity (mgINTF kg-1
h-1
) 2.75
The selected plants were:
1. Avena sativa (oat);
2. Raphanus sativus (red radish).
3.5.1.2. Testing materials
The following polymers were selected:
1. Polyethylene (PE): Polimeri Europa Riblene FL30, CIBA specialty chemical oxo-
biodegradable LLDPE, thermally degraded
2. Polystyrene (PS): Polimeri Europa powder, EPI-INC. oxo-biodegradable PS,
thermally degraded
3. Ecoflex: BASF – Ecoflex ® FBX 7011 powder (Figure 3.14)
4.
Figure 3.14. Ecoflex Chemical Structure. HO C
O
CH24
C
O
O CH2 O4
C
O
C
O
OH
Experiment
- 97 -
4. Cellulose
5. Poly-(3hydroxy)butyrate
3.5.2. Experimental Setup
3.5.2.1. Degradation in a soil-plant system
The experiment at mesoscale level was carried out using pots with a diameter of 25 cm and a
height of 10 cm (mesocosms) containing 1 kg of soil.
The different polymers as powder at the final concentration of 1% were added to the soil.
The pots were incubated under controlled temperature, light and humidity. The moisture
content of each soil–biomaterial mixture was adjusted to 50% of water holding capacity. The
monitoring of the mesoscale experiment consisted of soil sampling carried out after 35 (T0)
and 45 days (T1) from the experiment set up.
Each soil sample was a composite of three sub-samples mixed, homogenized, sieved (2 mm)
and stored dried at room temperature until chemical analysis and stored at 4°C until
biological analysis.
In addition, two terrestrial plants, oat (Avena sativa) and red radish (Raphanus sativus), were
used to evaluate the phytotoxicity of the biomaterials. For this purpose, after 35 days from
the experiment set up, soil was sampled (T0) and characterized, then 100 seeds of each plant
species were sown uniformly in one of the two replicate pots and all mesocosms were
maintained under controlled temperature, light and humidity for further ten days. The plant
growth was checked at the end of experimentation (45 days-T1); at this time the plants were
eradicated, washed and the dry weight of shoots and roots and the plant length were
determined.
3.5.2.2. Biodegradation of PHB in soil
The experiment at microscale level was carried out using pots containing 50 g of soil.
The PHB polymers as sliced at the final concentration of 1% (low dose, L) and 2% (High
dose, H) were added to the soil. The following treatments were planned:
1. 50 g soil + 0.5g PHB (L treatment)
2. 50 g soil +1g PHB (H treatment)
3. untreated soil (B treatment)
The pots were incubated under controlled temperature, light and humidity. The moisture
content of each soil–biomaterial mixture was adjusted to 50% of water holding capacity. The
monitoring of the microscale experiment consisted of soil sampling carried out at one, three
and four weeks from the experiment set up.
3.5.3. Methods
3.5.3.1. Chemical Parameters (pH, electrical conductivity, total organic carbon, total
nitrogen, water soluble carbon, nitrate, ammonia, total and available elements)
Electrical conductivity (E.C.) and pH were measured in 1:10 (w/v) aqueous solution. Total
organic carbon (TOC) and total nitrogen (TN) content of soil were determined by RC-412
multiphase carbon and FP-528 protein/nitrogen determinator (Leco, USA), respectively.
Ammonium and nitrate were determined with selective electrodes. Water Soluble Carbon
(WSC) was determined spectrophotometrically at 590 nm by using the method of dichromate
Chen Haiyan PhD Thesis
- 98 -
oxidation (Garcia, et al. 1990) . Total and available elements were determined with Atomic
Absorption Spectrometry (AAS). Total and available phosphorus were determined by the
Murphy and Riley (1962) method
3.5.3.2. Biochemical Parameters
Protease activity
The proteases are a group of hydrolytic enzymes connected to the nitrogen cycle; they
catalyzed the hydrolysis of proteins in oligopeptides or dipeptides. The ammonium released
by the hydrolytic reactions was measured by an ammonium selective electrode (Bonmatı, et
al.2009).
Tests: 0.5g of soil with 2ml of phosphate buffer 0.1 M at pH 7 and 0.5ml of substrate BAA
(N- -Benzoil-L- -Arginammide-Hydrochloride) 0,03M.
Controls: 0.5g of soil with 2ml of phosphate buffer 0.1 M at pH 7.
Tests and controls were shacked in a thermostatic bath at 37°C for 1 hour and half. Then the
samples were brought to a final volume of 10 ml with bi-distilled water and centrifuged for
10 minutes at 3500 rpm. The supernatant was read with a NH3 electrode. The results are
expressed in mgNH3 kg-1
h-1
.
Phosphatase activity
The phosphatase catalyzes the hydrolysis of phosphoric ester to phosphate. The methodology
consists in the determination of the release of para-nitrophenol (PNF) from the hydrolysis of
the para nitrophenyl-phosphate- hexahydrate (PNP) (Tabatabai and Bremner 1969).
Tests: 0.25g of soil + 2ml of maleate buffer 0.1 M at pH 6.5 + 0.5ml of PNP substrate 0.12
M.
Controls: 0.25g of soil + 2ml of maleate buffer 0.1 M at pH 6.5.
Tests and controls were shacked in a thermostatic bath at 37°C for 1 hour and half. 0.5 ml of
substrate (PNP) was added also to the controls and they were made cold at 4°C for 10
minutes, to block the reaction. Then 0,5ml of CaCl2 0.5M and 2ml of NaOH 0.5M were
added and the samples were brought to a final volume of 10 ml with bi-distilled water.
Samples were centrifuged for 10 minutes at 3500 rpm. The supernatant was read with the
spectrophotometer at a wave length of 398 nm. The optic densities picked up by the
instrument are transformed in concentrations referred to a standard straight line obtained by
the known concentration of PNF. The results are expressed in mgPNF kg-1
h-1
.
Dehydrogenase activity
Dehydrogenase enzymes catalyze the oxidation of organic compounds. The reaction
substrate consist in the organic substance, while the synthetic cofactor utilized for the
measure of the dehydrogenase activity consists in the INT (P-Iodio-Nitro-Tetrazolium-
chloride) which makes a chlorate product through reduction, INTF (p-Iodo-Nitro-
Tetrazolium-Formazano) determinable with a spectrophotometric methodology. This
enzymatic activity was determined using the methodology studied by Masciandaro et al.
(2000).
Tests: 0.1g of soil with 0.2ml of INT substrate at 0.5% (in bi-distilled water) and 0.1ml of bi-
distilled water (to bring the sample at the 60% of the field capacity).
Controls: 0,1g of soil with 0,3ml of bi-distilled water (to bring the sample at the 60% of the
field capacity).
Tests and controls were let rest for 20 hours in dark place; the tubes were not covered
because the INT prevails oxygen (the natural substrate of the dehydrogenase) as electrons
acceptor. The INTF is the product of the oxido-reduction and it is insoluble in water; it was
extracted through the addition of an extractant solution (tetrachloroethylene/acetone, 1/1.5).
Experiment
- 99 -
The solution was vortexed for one minute and centrifuged at 3500 rpm for 10 minutes. The
supernatant was used for the spectrophotometric measure, using a wave length of 490 nm,
referring it to the control. The optic densities picked up by the instrument are transformed in
concentrations, express in mgINTF kg-1
h-1
, referred to a standard straight line obtained by
the known concentration of INTF.
Arylesterase activity
Arylesterase activity has been measured using p-nitrophenyl acetate (p-NPA) as substrate
and dimethylsulfoxide as solvent, modified universal buffer at pH 7.5. The product of the
reaction (p-nitrophenol), after an incubation at 55 °C for one hour, has been tested
spectrophotometrically at 298 nm.
PHB-depolymerase activity
PHB depolymerase activity assay was carried out at 37 °C in 0.1 M potassium phosphate
buffer (pH 7.4). The amount of 3-hydroxybutyrate (3HB) liberated from the P(3HB)
poliymer during the enzymatic hydrolysis was determined by the ultraviolet method (Abe et
al. 2010; Doi et al. 1994). Impurities with absorption at 210 nm decrease the sensitivity of
the assay.
3.5.3.3. Biological parameters
Colony forming units (CFU) were determined in aqueous solutions of soil (1:10 (w/v) soil:
water solutions) based on the surface-plate counting proce-dure (Jayasekara et al., 1998). The
extraction was carried out in tubes with sterile water and vortexing for 2 min at room
temperature. Serial dilutions were made for the extracts using distilled water. A volume of
0.2 ml was spread onto plates prepared with adequate growing medium: plate count agar
(Sigma Aldrich) for total cultivable microbial population and Pseudomonas agar base (Sigma
Aldrich) for Pseudomonas genus. Plates were incubated at 29 °C for 48 and 72 h for plate
count agar and Pseudomonas agar base, respectively. The CFU per gram of soil were
calculated (Picci and Nannipieri, 2002).
3.5.3.4. Germination and Growth Test
Germination and Growth test was done on the different soil treatments to evaluate the
seeding and growth capability of the plants Avena sativa and Raphanus sativus. For each
treatment, a pot sowed with 100 seeds of Avena sativa and a pot sowed with 100 seeds of
Raphanus sativus at a depth of 3 cm were carried out.
Plants‘ growth was measured after about 10 days.
The Germination and Growth Index (GI%) was calculated by using the following equation:
GI (%) = x x 100
3.5.4. Statistical Analisys
The STATISTICA 6.0 software (StatSoft Inc., Tulsa, Oklahoma, USA) was used for all
statistical analysis. All numerical parameters before statistical analysis were normalized and
autoscaled: the result for each variable is a zero mean and an unit standard deviation.
n. seed germinated test
n. seed germinated control
length plant test
length plant control
Chen Haiyan PhD Thesis
- 100 -
PCA is a multivariate statistical data analysis technique which reduces a set of raw data into
a number of principal components which retain the most of the variance within the original
data in order to identify possible patterns or clusters between treatments and variables
(Carroll, et al. 2004). The PCs were extracted by applying the principal of main axis method.
Only component loadings >0.7 were considered for interpretation of the PCs. In PCA
analysis, the data are decomposed into separate sets of scores and loadings for each of the
two modes of interest (treatments and variables) and the whole variability of the data is
explained in order to provide a clear and more interpretable visualization of data structure in
a reduced dimension. In addition, PCA analysis gives information that can also be clearly
presented graphically.
Result and Discussion
- 101 -
4. RESULTS AND DISCUSSION
As has been mentioned in previous chapter one of the aim of the present Doctoral Thesis is
to identify the influence of particular and innovative additive as it is Joncryl ADR-4368-CS
and hazelnuts shell powder (here labeled as Lignin) on the biodegradation (mineralization) of
binary and ternary composites in soil medium, mature compost and river water. In particular,
it has been also studied the concentration of Joncryl (J) and Lignin (LN) and the influence of
this parameter on the biodegradation propensity of the binary system.
It is well known that the main factors that affect the biodegradation behavior are the
chemical composition of the material, molecular weights, the chemical bonds in the structure,
the crystallinity of the material, the nature of the surfaces, the indigenous micro-flora and the
environmental conditions (Lutz and Falcao 2011). Then in order to explain the results
obtained from the biodegradation tests in soil, mature compost and river water, it is
important to assess the thermal properties of PHBV and PLA based composites by using
differential scanning calorimetric (DSC) and thermogravimetric analysis (TGA), the
structural analysis of the raw material and of binary composites by FT-IR, as well as, the
determination of the molecular weight for the raw materials and composites by GPC.
Moreover, the evaluation of the thermal properties of the composites prepared, together with
the results of the biodegradation experiments and their processability characteristic can be
useful for envisaging future applications and end life disposal strategies for the obtained
composites.
We start the present chapter by analyzing the results obtained from DSC and TGA thermal
characterization for PHBV and PLA based composites, followed by some of the
characterization done for PLA and PHBV through GPC analysis and FT-IR analysis. The last
part will deal with the discussion of the results related with the processability characteristics
of the raw materials and their composites in melt mixing discontinous experiments
(Brabender). And we will end with the biodegradation experiments in soil, mature compost
and river water
.
4.1. Differential Scanning Calorimetry (DSC)
4.1.1. PHBV Based Blends and Composites
From the DSC experimental data, it is possible to collect information related with the thermal
transition that characterizes amorphous and semi-crystalline polymers. The thermal
transitions are: melting temperature, (Tm); glass transition temperature, (Tg) and
crystallization temperature (Tc). In general, these properties are obtained from the second
heating run and the cooling run of each sample. An adequate experimental set-up for the
thermal analysis experiment is important to do with the aim to identify the real
thermodynamic behavior of the materials without the influence of their previous thermal
history. Another important parameters, also obtained from DSC thermal analysis, are the
enthalpy of fusion ( Hm) and crystallization ( Hc). In particular, the crystallinity (Xc %) of
the raw materials as well as the final composites is determined by considering the enthalpy of
fusion during the second heating run.
The crystallinity determination takes into account corrections related with the weight fraction
of the semi-crystalline component in the blend, the presence or not of the cold crystallization
Chen Haiyan PhD Thesis
- 102 -
(Tcc), and the theoretical enthalpy of the polymer used considering a crystallinity of 100%
(Wang et al. 2010, Avella et al. 2000, Sarasua et al.2005).
In the present part emphasis will be done in the correlation between the crystallinity degree
of the material and the composites prepared and its influence on the biodegradation
behaviour results. Additionally, the thermal properties will be analyzed in order to analyze
the influence of Joncryl and Lignin on the melting behaviour of the binary blends.
Table 4.1 shows the thermal properties of PHBV raw material and its based composites. The
influence of the concentration of Joncryl (J), Lignin (LN) and Montmorrillonite (Dellite – D)
have been also evaluated.
Table 4.1. Thermodynamic Parameters for PHBV Based Blends and Composites: Tm,
Tc, Tg and Xc.
Sample Tg
(°C)
Tcc
(°C) Hcc
(Jg-1
)
Tc
(°C) Hc
(Jg-1
)
Tm
(°C)
Xc§
(%) Hm
(Jg-1
)
PHBV - - - 84 103 170 80 117.0
PHBV + J0.2 - - - 96 91.4 165 73 106.6
PHBV + J5 2 47 6.0 79 65.3 163 65 96.3
PHBV + LN10 - - - 89 50.1 178 46 61.1
PHBV + LN20 - - - 91 63.4 174 69 80.5
PHBV + LN10 + J5 - - - 87 48.6 176 50 62.0
PHBV + LN20 + J5 - - - 89 44.7 183 51 56.1
PHBV + D3 - - - 88 64.8 171 55 78.4
PHBV + D6 - - - 88 56.5 170 49 67.3
PHBV + D3 + J2 - - - 73 77.7 160 73 100.9
PHBV + LN10 + D3 - - - 92 61.2 175 56 71.4
PHBV + LN20 + D3 - - - 91 54.7 178 50 56.2
PHBV + LN10 + D3 +
J2
- - - 85 52.8 177 56 69.8
PHBV + LN20 + D3 +
J2
- - - 88 37.2 179 43 47.2
PHBV + LNF10* -15 39 48.7 37 7.8 128 9 60.0
§ Xc =[(ΔHm –ΔHcc)/ΔHm100% x ]100 for samples with cold crystallization, Xc =
(ΔHm/ΔHm100% x )100 where ΔHm PHB100% crystalline= 146 Jg-1 (Wang et al.
2010) and is the weight fraction of PHB in the composite
* Sample with multiple melting point: Tm1 = 63 °C, Tm2 = 88 °C
From DSC results, lignin and inorganic component (Montmorrillonite - Dellite) decreases
the enthalpy changes (melting and crystallization) of composites compared with the raw
material (PHBV), a little amount of Joncryl (0.2%) has no effect on the enthalpy changes,
however 5% of its addition can also decrease the melting enthalpy as well as the
crystallization. In particular, the addition of 5% by weight of Joncryl produces on PHBV
matrix hindering effects on the crystallization ability of the PHBV polymer chain during the
cooling step and, as a consequence, a cold crystallization is observed during the second
heating.
Meanwhile, the addition of Joncryl and Dellite can decrease or maintain the melting
temperature of PHBV matrix, contrary, the lignin addition increases the PHBV melting
temperature from 4 until 8 degrees. The higher melting temperature value was obtained for
the sample named PHBV + LN20 +J5 having a melting peak at 183 °C, comparing this value
with the raw material, an increment of 13 °C was observed. The higher the melting
Result and Discussion
- 103 -
temperature of the final composite the higher will be the extension of the degradation during
an eventually second processing step. This statement is correlated with the fact that the
decomposition temperature of PHBV in the melt (140 - 170° C) is closer to the melting
temperature of the polymer (Arrifin et al. 2008, Arrifin et al. 2009).
All the composites (the inorganic and organic ones) prepared, posses a lower crystallinity
degree than the raw material (PHBV). For the binary systems the lower crystallinity degree
was obtained for the sample PHBV + LN10 with 46%, followed by the sample PHB + D6
having 49%. Instead the samples with the higher crystallinity degree are PHBV + J0.2 and
PHBV + D3 + J2, both with 73%. Nevertheless, a dramatic change in the crystallinity has
been found for the sample PHBV + LNF10 (with around 9%), this sample is characterized by
the presence of a functionalized lignin in a concentration of 10% by weight. The
functionalization of the lignin was done with the aim to improve its compatibility with the
hydrophobic PHBV matrix. The chemical components for the functionalization were stearic
acid in the presence of a catalyst. The conditions of the reaction as well as the analysis of the
functionalized lignin are out of the scope of the present doctoral thesis work.
The thermogram traces for the chain extender additive (Joncryl) are shown in the Figure 4.1.
It is possible to observe a double melting peak for the pure PHBV and by increasing the
amount of Joncryl in the blend the presence of a glass transition (Tg) temperature and a cold
crystallization (Tcc) are evidenced together with the disappearance of the first PHBV‘s
melting peak.
Figure 4.1. Thermogram Traces for PHBV Blended with Joncryl Additive at Different
Concentration, 0%, 0.2% and 5%.
Figure 4.2 shows the thermograms traces for the organic composites (PHBV + LN10 and
PHBV + LN20). Adding hazelnut shell powder in the composite, was observed an increment
in the melting temperature peaks of pure PHBV. In particular, with an higher concentration
of lignin an inversion in the heat flow was observed for the melting peaks of the sample. In
both composites the melting peaks are overlapped compared with the pure PHBV.
Chen Haiyan PhD Thesis
- 104 -
Figure 4.2. Thermogram Traces for PHBV Blended with Hazelnut Shell Powder (Lignin) at
Different Concentration, 0%, 10% and 20%.
Figure 4.3, shows the thermogram traces related with the addition of organic filler as
hazelnut shells powder (lignin) with different chemical treatment (original and functionalized
lignin at 10% by weight). Functionalized treatment on the lignin showed clearly more
significant effect on DSC traces compared with the unmodified lignin. The presence of a Tg,
a Tcc as well as multiple melting peaks suggest the presence of different PHBV crystal
population, that can be originated from the chemical and/or physical interaction between the
pure PHBV and the functional groups inserted in the lignin during the processing conditions.
Figure 4.3. Thermograms Traces of PHBV Based Composites with Different Chemical
Treatment: Original Lignin and Functionalized Lignin Powder.
Increasing the level of complexity by adding both Joncryl and lignin, in different weight
percentage, an interesting phenomenon was observed in Figure 4.4. The effect of the lignin
on the PHBV composite thermal transitions is more pronounced than the effect of the Joncryl
(at 5%). So it indicates that the lignin influence on the heat flow, in the analysis by DSC, is
more obviously than the Joncryl. In particular, the Tg and the Tcc (produced by adding 5% of
Joncryl) were completely disappears in the PHBV + LN20 + J5 composite.
Result and Discussion
- 105 -
Figure 4.4. Thermograms Traces of PHBV Based Composites with Different Lignin
Concentration: 10% and 20%, and with 5% of Joncryl.
The effects of addition of inorganic fillers as Montmorillonite (Dellite) on DSC behaviour
are shown in Figure 4.5. By doing a comparison between the organic and the inorganic filler
on their role in the final composite thermal behaviour one can draw conclusions as discussed
before. The overlapping in the PHBV melting peaks was observed for all the binary and
ternary systems and an increment in the higher melting peak was also observed.
Figure 4.5. Thermograms Traces of PHBV Based Composites with Different Concentrations
of Lignin (10% and 20%), Inorganic Filler as Montmorillonite (Dellite) (3% and 6%). PHBV
and its Binary Blends.
Final comparison for the blends containing inorganic fillers as Montmorillonite (Dellite) and
lignin at different percentage (20% and 10%), were also determined and analyzed by DSC
and the results are shown in Figure 4.6. From the DSC traces similar conclusions were
obtained when compared with the results of previously discussed (see values on Table 4.1).
The addition of 3% of Dellite and 2% of Joncryl in the PHBV, was not producing changes on
the PHBV thermal behaviour. Additionally, the ternary composites still shown the same
trend already discussed, that is: the higher the amount of lignin in the composite the higher is
its effect on the PHBV heat flow changes and this effect is similar to that observed in the
binary composite PHBV + LN.
Chen Haiyan PhD Thesis
- 106 -
Figure 4.6. Thermograms Traces of PHBV Based Composites with Different Concentrations
of Lignin (10% and 20%), Inorganic Filler as Montmorillonite (Dellite) (3%), Joncryl (2%).
PHB and its Ternary Blends.
4.1.2. PLA Based Blends & Composites
With the aim of assessing the influence of the chain extender additive (Joncryl) and the
organic filler (lignin) on the thermal properties of poly(hydroxyalcanoate) PHA, PLA based
composites characterized by similar compositions, in terms of additives, as PHB based
composites have been prepared.
The thermal properties of the new composites are shown in Table 4.2. The presence of
Joncryl and lignin in PLA based composites do not produce appreciable changes in the PLA
thermal properties. The glass transition temperature and the cold crystallization temperature
remain almost unchanged, as well as, the melting temperature. However, occurring as in the
case of PHBV, higher amount of Joncryl (5%) in PLA blends decreases the melting
temperature of PLA by 6 ℃.
Table 4.2. Thermodinamic Parameters for PLA based Blends and Composites: Tm, Tc,
Tg and Xc.
Sample Tg
(°C)
Tcc
(°C) Hcc
(Jg-1
)
Tc
(°C) Hc
(Jg-1
)
Tm
(°C)
Xc§
(%) Hm
(Jg-1
)
PLA 60 113 30.8 96 0.9 156 7.5 37.7
PLA + J0.2 61 115 31.6 75 0.5 153 0.5 32.1
PLA + J5 60 123 24.0 75 0.5 150 0.8 24.7
PLA + LN10 60 110 31.1 80 1.0 156 1.4 32.3
PLA + LN20 60 113 25.9 77 0.7 150 2.9 28.1
PLA + LN10 + J5 60 125 18.2 74 0.8 152 5.1 22.2
PLA + LN20 + J5 61 125 13.2 76 0.4 155 1.6 14.3
§ Xc =[(ΔHm –ΔHcc)/ΔHm100% x ]100 for samples with cold crystallization, Xc =
(ΔHm/ΔHm100% x )100 where ΔHm PLA 100% crystalline= 93 Jg-1 (Sarasua et al.
2005) and is the weight fraction of PLA in the composite.
Result and Discussion
- 107 -
The major influence found for both additives (Joncryl and lignin) was on the PLA
crystallinity degree. Normalizing the crystallinity degree value by dividing it by the Xc value
of the pure polymer, it was found that both Joncryl and lignin reduce dramatically the PLA
crystallinity degree when their effect on PHBV (Table 4.3). In particular, the major
modification was obtained for Joncryl at low concentration (0.2%). This result suggests that
the chain extension reaction, promoted by the epoxides functional groups contained in the
Joncryl chemical structure, has been more favored in the PLA than in PHBV. Probably the
concentrations of reactive functional groups in the PLA main chain and in the end-chain are
higher than in the case of PHBV. Similar behavior was also found for the effect of lignin in
the PLA based composites.
Molecular weight determinations have been done in order to clarify the above mentioned
hypothesis. The results are shown in Table 4.4.
PLA sample, containing 0.2% by wt. of Joncryl shows the higher variation in the molecular
weight (Mw) and in the polydispersity index (P.I) compared with the pure PLA. This result is
in agreement with the crystallinity degree variations observed for the PLA + J0.2% sample
(see Table 4.3). Probably, the lower concentration of chain extender additive favored its
dispersion inside the melted polymer and its compatibility with the PLA. Thus, the reactive
conditions are favored and, in this way, the chain extension reaction is effective. It is
expected that an increment in the molecular weight weight, through chain extension reaction
with chemically different reagent, and the formation of branching can reduce the crystallinity
of the neat PLA. The presence of lignin in the PLA and in the samples containing Joncryl at
5% did not produce significant variations in the cristallinity values.
Unfortunately, molecular weight determinations for the PHBV samples and composites were
difficult to perform due to the fact that the final samples were all insoluble in chloroform.
The insolubility can be due to the high crystallinity of the PHBV before and after blending or
by the formation of crosslinking between polymer chains thus hindering their solubility.
PHBV has higher molecular weight than PLA (see Table 4.4), however its P.I is slightly
lower. This fact is in agreement with the above mentioned tendency related with the
effectiveness of Joncryl on PLA matrix instead of PHBV matrix.
Figure 4.7 is showing the general reaction mechanism between Joncryl as reactive additive
and the functional groups present in the melt.
Figure 4.7. General Mechanism of Chain Extension Reaction Between Polymers and Joncryl
Additive (Arrifin et al. 2008, Arrifin et al. 2009, Pilla et al. 2009).
Chen Haiyan PhD Thesis
- 108 -
Table 4.3. Normalized Crystallinity Degree for PLA and PHBV Based Blends and
Composites.
Component XcPHA / XcComposite
PLA PHB
J0.2 15.0 1.1
J5 9.4 1.2
LN10 5.4 1.7
LN20 2.6 1.2
LN10 + J5 1.5 1.6
LN20 + J5 4.7 1.6
Table 4.4. Molecular Weight Values for PHBV and PLA Blends & Composites.
Sample Molecular weight by GPC
Mw Mn P.I
PHBV 482.620 311.800 1.5
PLA 163.390 89.193 1.8
PLA + J0.2 208.500 90.213 2.3
PLA + J5 233.000 148.720 1.6
PLA + LN10 152.200 100.900 1.5
PLA + LN20 163.000 105.220 1.5
PLA + LN10 + J5 238.630 141.880 1.7
PLA + LN20 + J5 226.520 144.950 1.6
In the case of PLA samples with Joncryl additive at 0.2 and 5 % by weight, the results are
shown in Figure 4.7. Similar results can be obtained by comparing it with the PHBV thermal
behavior. The addition of Joncryl can significant modify the heat flow trace, higher is the
percentage of additive was added, higher is the heat flow variation is observed.
Figure 4.8. Thermograms Traces of PLA Samples at Different Concentration of Joncryl: 0%,
0.2% and 5%.
Figure 4.8 shows the thermogram traces recorded for PLA based composites with 10% and
20% of lignin from hazelnut shell.
PLA thermogram (Figure 4.9) shows an endothermic peak connected to the isothermal
crystallization (T = 110°C) of this material that, having an high glass transition temperature
Result and Discussion
- 109 -
compared to the ambient temperature, shows an amorphous part also in the melt state of the
polymer (Day 2006). Not significant variation in the heat flow traces were observed by
varying the amount of lignin in the composite. This observation is in agreement with the
obtained DSC analytical results (see Table 4.2).
The Joncryl addition makes more distinct the melting peak at 160°C and the shoulder at
154°C observed in the neat PLA thermogram. The double melting peak observed for
PLA/Joncryl blends can be connected to a different morphology of the crystalline phase
(width of the lamellar structure and spherulites dimensions), obtained by crystallization in
the melt and isothermal crystallization (Pilla et al.2009).
A chain extender concentration above 2% produces an increment for the isothermal
temperature about of 10°C for PLAJ5 (Tcc= 127°C) composite compared to that of neat PLA
(Tcc= 118°C), thus the presence of a branched structure makes slow the crystallization
process
Joncryl addition until .2%, the inorganic component and the lignin (10%) increase the
crystallinity degree for the composites compared to that of neat PLA (Xc = 43.1), whereas
the lower values have been recorded for PLAJ5, PLALN20J5, PLALN20D3, PLALN20D3J5
composites. This trend can be explained considering an increment for the composites
molecular weight (Perego et al. 2006), as detected by the GPC analysis.
The high value for the glass transition temperature (Tg=60°C) confirms the rigidity for the
polymeric material and its composites
The lignin addition (10% and 20%) can be underlined by the presence of an exothermic peak
near to the endothermic peak of the polymer, well pronunced and visible in the respective
thermograms. This phenomemenon is connected with PLA isothermal crystallization, that
occurs during the heating process (Li et al. 2003).
Increasing ligni amount until to 40%, a decrease for the melting temperature from 169.9°C to
161.8°C and for the glass transition temperature from 63.4°C to 57.3°C, was observed.
This trend can be explained, considering the mobility of the _OH phenolic groups, able to
create strong intermolecular hydrogen bonds with the PLA carbonilic groups (Li et al. 2003).
Figure 4.9. Thermograms Traces of PLA Composites at Different Concentration of Lignin:
0%, 10% and 20%.
In the case of PLA composite, which the results are shown in Figure 4.10, was concluded
that the addition of both additives lignin and Joncryl in different percentage seems not
originated significant changes in the DSC thermograms. However, by increasing the
percentage of lignin at 20% and Joncryl at 5%, a notorious modification on the heat flow
traces was observed. In particular, these changes can be attributed to the presence of Joncryl
Chen Haiyan PhD Thesis
- 110 -
instead of lignin. Contrary to PLA, the PHBV matrix has been affected either by Joncryl as
by lignin.
Figure 4.10. Thermograms Traces for PLA Based Composites Having Organic Filler as
Hazelnut Shells Powder (Lignin) at Different Concentration: 10% and 20%, and with
Additive as Joncryl at 5% by Weight.
4.2 ThermoGravimetric Analysis (TGA)
4.2.1. PHBV Based Blends & Composites
The onset temperature (Ton
) of decomposition was determined as the temperature
corresponding to the crossover of tangents drawn on both sides of the thermogravimetric
trace. The residue was evaluated as the residual weight at the end of the experiment generally
stopped at 700°C. The main results of thermal characterization-TGA data of PHBV based
composites with respect to thermal properties as thermal stability (Ton) and the residue (%) at
700°C are reported in Table 4.5.
Result and Discussion
- 111 -
Table 4.5. Thermal Properties for PHBV Based Blends and Composites as recorded
Under Nitrogen Atmosphere.
Sample Codes TGA N2 DTGA
Tonset
a)
(°C)
Residueb)
(%)
Tp1
(°C)
Tp2
(°C)
Tp3
(°C)
PHBV 250 0.54 274 - -
Joncryl (J) 241 0.80 294 349 402
Lignina (LN) 260 22.6 286 360 431
Montmorillonite (Dellite D) 251 62.4 321 407 589
PHBV + J0.2 256 0.40 279 - -
PHBV + J2 249 0.39 274 375 -
PHBV + J5 252 0.58 265 399 -
PHBV + LN10 257 2.62 278 352 -
PHBV + LN20 252 3.81 272 348 -
PHBV + LN10 + J5 269 2.67 284 362 406
PHBV + LN20 + J5 269 3.50 282 361 410
PHBV + D3 261 2.32 283 - -
PHBV + D6 227 4.82 266 463 -
PHBV + D3 + J2 260 2.38 286 384 -
PHBV + LN10 + D3 268 4.00 287 367 -
PHBV + LN20 + D3 264 5.61 284 367 -
PHBV + LN10 + D3 + J2 264 3.42 286 371 -
PHBV + LN20 + D3 + J2 271 4.78 285 372 -
PHBv + LNF10 215 2.54 243 311 -
a) At 10%-wt loss b) Residue at 700°C
TGA data for PHBV composites (Table 4.5) indicated that lignin and inorganic filler can
significantly increase the onset temperature and residue for PHBV composites. These
additives increased the thermo stability of the materials, meanwhile, Joncryl‗s addition has
not significant effect on the above parameters. From the results, addition of 3% of Dellite
shows better thermo-stability compared with the addition of 6%.
The organic composites PHBV + LN, PHBV + LN + J, the inorganic (PHBV + D) ones and
hybrid ones, PHBV + LN + D, PHBV + LN + D + J, based on PHBV were investigated in
respect of the thermal properties by TGA (Table 4.5) with the aim to obtain useful
information on better suited processing temperatures to be applied eventually by the
converters.
TGA (a) and DTGA (b) traces for PHBV based composites containing the chain extender (J)
are reported in Figure 4.11a-b) whereas those relevant to the lignin, alone or in combination
with Joncryl are reported in Figure 4.12a-d). The Joncryl dispersion (0.2%, 2%, 5%) in the
polymer matrix produces a light thermal destabilization at Joncryl concentrations of 2%, as
observed by the drop of the onset temperature.
Chen Haiyan PhD Thesis
- 112 -
The blend containing Joncryl (0.2% - wt) is the only one that presents a higher thermal
stability with respect to PHBV processed in Brabender.
Figure 4.11. TGA (a) e DTGA (b) Traces Recorded for PHBV/Joncryl Blends.
DTGA traces (b) shows only one degradation peak for all PHBV based blends containing
Joncryl with a shoulder at 375°C for the composite PHBV/J2 and at 399°C for the blend
PHBV/J5.
The lignin addition to PHBV produces an increase of 20°C for the thermal stability of
PHBV/LN/J composites respect to neat PHBV and the binary system PHBV/Lignin, as
observed by the registered Ton values (Table 4.5).
This trend was confirmed also by the residue value (3.5%) as determined at 700°C. The
recorded higher data can be correlated to the minor propensity towards degradative
reactions for the material composites.
The ternary systems PHBV/LN/J show a multiple trend for the DTGA trace, that has
three degradation peaks connected to the major material weight losses.
Also the ternary systems PHBV/LN/D and quaternary ones PHBV/LN/D/J shows Ton
values by 20°C higher than PHBV processed in Brabender. The derivative trend has a
simple profile as noticed from the loss of one degradation peak. The chain extension
reaction promoted by Joncryl can stabilize the quaternary systems making possible their
thermal degradation with a minor number of weight losses (figure 4.13).
Result and Discussion
- 113 -
Figure 4.12. TGA (a, c) e DTGA (b, d) Traces Recorded for PHBV/Lignin and
PHBV/Lignin/Joncryl Composites.
Figure 4.13. TGA (a, c) e DTGA (b, d) Traces Recorded for PHBV/Lignin/Dellite and
PHBV/Lignin/Dellite/Joncryl Hybrid Composites.
PHBV/D6 composite is characterized by a lower onset temperature (Ton = 227°C) compared
to PHBV/D3 composite (Ton = 261°C) which posses higher thermal stability than the pure
PHBV (Ton = 250°C).
Chen Haiyan PhD Thesis
- 114 -
Figure 4.14 shows a comparison between the TGA (a) and DTGA (b) traces for PHBV
based composites loaded with lignin and functionalized lignin with stearate groups, at
content of 10%-wt of lignin.
Figure 4.14. TGA (a) e DTGA (b) Traces of PHBV/LN10 and PHBV/LNF10 Composites.
The introduction of functionalized lignin results in about 35°C decrease with respect to
PHBV and PHBV/LN10 composite. The thermal degradation for PHBV/LNF10 composite
starts at lower temperatures connected to a derivative shift toward temperatures lower than
200°C.
4.2.2. PLA Based Blends & Composites
Thermogravimetric analysis, under air atmosphere, was performed on native PLA and on
PLA based blends and composites loaded with Joncryl, lignin, alone or in combination.
Figure 4.15 shows TGA (a) and DTGA (b) traces for these blends and composites; also the
thermal decomposition profile for lignin and Joncryl was recorded to make a comparison
between the single components and their synergistic effect inside the composite.
The chain extender (Joncryl) has a minor thermal stability than pure PLA, as observed by the
lower Ton value (Table 4.6).
The first degradation peak, present in the Joncryl DTGA profile, showed three shoulders,
that derive from the overlapping between the main peak and smaller peaks located at
temperature of 269°C, 293°C, 314°C. These thermal effects can be correlated with the
formation of low molecular weight components or ring opening reactions for the epoxy
groups.
Lignin powder has a TGA trace (Fig. 4.15a), placed in a temperature range larger than the
same recorded for the selected blends and composites.
Its onset temperature is 261°C, whereas the residue recorded at 700°C is around at 1.15%,
that is an high value connected with the presence of aromatic rings, thermally stable, in the
lignin structure.
The peaks molteplicity, present in the DTGA trace (Fig. 4.15b), was an experimental
evidence of the ligno-cellulosic material composition. In fact the organic filler derives from
the grinding of the hazelnut shells and from sieving its powder: so lignin is not the only
component of this material, because of notable amount of cellulose and hemicellulose are
contained onto the material.
Result and Discussion
- 115 -
(a) (b)
Figura 4.15.TGA (a) e DTGA (b) Traces of PLA/Lignin, PLA/Joncryl Blends and Hybrid
Composites (PLA/Lignin/Joncryl) Under Air Atmosphere.
The onset temperature represents the starting for the composite degradation and it is
connected with the thermal stability of the material. This parameter gives suitable
information on the polymeric materials processing temperature and features.
The Joncryl addition (5 wt-%) alone or in combination with the organic filler (lignin) showed
a decrease of about 30°C for the PLAJ5 blend and for PLA/LN20/J5 composite thermal
stability, while PLA/LN20 blend and PLA/LN10/J5 composite showed an increment of
about 10°C.
The residue consists in the material amount that remains uncombusted at the end temperature
of the experiment. So it is quite high for all the analyzed blends and composites that contain
aromatic and epoxy rings for which, high temperature are needed to be utilized for the
starting of thermal degradation.
Thermal properties are collected in Table 4.6.
Table 4.6. Thermal Properties of PLA Based Blends & Composites Under Air Atmosphere.
Samples TGA air DTGA
Tonset
(°C)
Residue
(%)
Tp1
(°C)
Tp2
(°C)
Tp3
(°C)
Tp4
(°C)
PLA 309 0.23 359 402 - -
Lignin 261 1.15 292 323 390 452
Joncryl 254 0.18 328 345 416 499
PLA + J0.2 326 0.45 302 365 429 460
PLA + J5 284 0.23 306 323 336 409
PLA + LN10 295 0.47 337 399 441 -
PLA + LN20 315 0.39 276 362 461 -
PLA + LN10 + J5 319 0.30 334 366 482 505
PLA + LN20 + J5 295 0.57 290 357 461 495
Chen Haiyan PhD Thesis
- 116 -
Figure 4.16 shows the Joncryl concentration effect on the PLA thermal degradation profile.
(a) (b)
Figura 4.16. TGA (a) and DTGA (b) Traces for PLA/Joncryl Blends Under Air Atmosphere.
A small concentration of chain extender does not modify the shape of PLA thermal
degradation profile (Fig. 4.16a) and the temperature range (260-330°C) in which, the onset
temperature is comprised. Increasing the concentration until to 5%, a more complex profile
with a degradation peaks molteplicity (Fig. 4.16b) was produced and it connected with
oxidative reactions and cross-linking that occur between the polymer and the chain extender.
Table 4.7 collects the data related to PLA based blends and composites thermal properties
obtained for TGA analysis under nitrogen atmosphere in order to make a comparison
between the blend or composite behavior and the component effect under the two different
atmospheres.
Table 4.7. Thermal Properties for PLA Based Blends & Composites Under Nitrogen
Atmosphere.
Samples
TGA
DTGA
Tonset
(°C)
Residue
(%)
Tp1
(°C)
Tp2
(°C)
Tp3
(°C)
Tp4
(°C)
PLA 313 0.91 359 441 - -
Lignin 260 22.5 286 360 431 -
Joncryl 240 0.86 294 320 350 402
PLA + J0.2 313 1.19 300 356 - -
PLA + J5 276 0.94 317 399 470 -
PLA + LN10 266 4.61 265 309 460 -
PLA + LN20 276 5.01 258 313 775 -
PLA + LN10 + J5 271 3.95 271 319 402 462
PLA + LN20 + J5 291 7.94 278 324 375 439
Result and Discussion
- 117 -
Figure 4.17 reports TGA (a) and DTGA (b) for Pure PLA and Its Composites, Recorded
under Nitrogen Atmosphere.
(a) (b)
Figura 4.17. TGA (a) e DTGA (b) Traces of PLA/Lignin, PLA/Joncryl Blends and Hybrid
Composites (PLA/Lignin/Joncryl) Under Nitrogen Atmosphere.
In nitrogen atmosphere, the addition of the organic filler (lignin), the chain extender (Joncryl)
and their combination loaded inside the composite with the neat PLA, produces for the
blends and composites a lower thermal stability than the native PLA, as observed by the Ton
values (Table 4.7).
DTGA profile (Fig. 4.17b) is very complex (presence of four peaks) for Joncryl and for the
based PLA composites loaded with Joncryl and lignin. These peaks (Fig. 4.17b) are
comprised in the temperature range of 270-470°C and they are connected with the
degradation of low molecular weight component contained in the composites and with the
reactions on polymer and chain extender carbon backbone without taking into account the
oxidative phenomena that can occur between the composite components with the oxygen of
the air.
The residue value is higher than those recorded in air atmosphere for the same composites:
the Carbon residue remains in large amount after the burning of the sample.
The lignin powder shows a residue (22.5%) that can be correlated with the real lignin
fraction contained in the ligno-cellulosic material, because of the lignolitic part degrades
before 700°C (Brebu et al. 2010).
Figure 4.18 reports TGA (a) and DTGA (b) traces for PLA/Joncryl blends.
(a) (b)
Figura 4.18. TGA (a) and DTGA (b) Traces of PLA/Joncryl Blends Under Nitrogen
Atmosphere.
PLA/J5 blend showed a lower thermal stability (Ton = 276°C) than the pure PLA and
PLA/J0.2 blend (Ton = 313°C). So a small amount of chain extender does not affect the
thermal stability of the polymer. The additive results diluted in the polymer matrix and it
Chen Haiyan PhD Thesis
- 118 -
does not react with the end-groups of the polymer chains. Also the residues for PLA/J0.2
blend results rather high (1.19%).
4.3. Molecular Weight by Gel Permeation Cromatography (GPC) Analysis
The numeral (Mn) and the ponderal (Mw) molecular weight and the poly-dispersivity index
(Mn/Mw) were determined for PLA/Joncryl and PLA/Lignin blends (Table 4.8) with the aim
to investigate the organic filler and the chain extender concentration effect on the molecular
weight for PLA matrix and to obtain same informations related to possible reactions that can
be occurred between the polymer and these components.
Table 4.8. Numeral Molecular Weight (Mn), Ponderal Molecular Weight (Mw) and
Polidispersivity Index (Mn/Mw) for PLA/Joncryl and PLA/Lignin Based Blends.
Sample Mn
(kDa)
Mw
(kDa)
Mn/Mw
PLA 89 163 1.83
PLAJ0.2 90 208.5 2.31
PLAJ2 207 308 1.48
PLAJ5 149 233 1.56
PLALN10 101 152 1.51
PLALN20 105 163 1.55
PLALN10J5 142 239 1.68
PLALN20J5 145 226.5 1.56
The Joncryl loading inside the composite (Figure 4.19) caused a molecular weight increment
compared to neat PLA processed in Brabender, as observed by the lower retention times, at
which, the solutions containing Joncryl in concentration of 0.2%, 2%, 5%, eluted, producing
the resulting cromatograms.
The polidispersivity index showed a maximum value for the PLAJ0.2 blend and lower and
nearer values to PLA matrix (1.83) for PLAJ2 and PLAJ5 blends.
These blends have polymeric chains with different length and molecular weight that act as
functional groups, in major number compared to PLA polymer matrix.
Figure 4.19. Cromatograms for PLA and PLA/Joncryl Blends.
Result and Discussion
- 119 -
The lignin addition, alone or in combination with Joncryl did not create notable variations in
the polidispersivity index values, as observed from the overlapping and the same shape of
the recorded cromatograms (Figure 4.20).
(a) (b) Figura 4.20. Cromatograms for PLA, PLA/Lignin Blends (a) and PLA/Lignin/Joncryl
Composites (b).
4.4 PHAs Based Composites Processing Characteristic
The torque stability evaluation during the melt-blending process gives useful information
that can be correlated with the degradation of the material inside the Brabender mixer
chamber and with chemical reactions that can be occurred inside it such as cross linking and
chain extension. Likewise, the influence of the filler on the torque (plasticization) and the
induction time can be studied. In this way it is possible to suggest optimal processing
conditions for melt-processing blends and composites. The use of PHBV also has limitations.
One such limitation is its narrow processing window. The polymer is thermally unstable at
temperature above the melting point (around 170oC to 180
oC), and a drastic reduction in
molecular weight occurs during processing at temperatures in 180-200oC range. The
composites obtained by using inorganic and organic filler and innovative additive Joncryl
ADR-4368C results still brittles and present poor mechanical properties. It was difficult to
produce thin film by compression moulding for mechanical test, thus plasticization can be a
valid strategy to improve the final properties of the composites as well as their processability.
The other limitation is its relatively low impact resistance. In order to overcome these
shortcomings, efforts have been made to co-polymerize HB with other monomers HA, but
the cost is considerably high, and this is limiting its use. One possible approach to obtain a
less expensive thermoplastic polymer of improved mechanical properties is to blend PHBV
with another suitable polymer. Earlier studies have shown that blending polymers could lead
to improve properties, lower the cost and impart functionalities in blends (De Carvaho et al.
2008).
The presence of organic and inorganic fillers becomes an important parameters in the
assessment of the optimal processing conditions for the developed composite formulations.
Figures 4.20 - 4.21 shows the torque behaviour vs. time for the organic composites based on
lignin flour, obtained from the hazelnut shell grinding. Figure 4.20 reports on the profiles
obtained with lignin particle with size above 39 μm, whereas Figure 4.21 reports on the
profiles obtained with lignin particle size below 39 μm. Figure 4.22 reports on the traces
obtained for the torque behaviour recorded for the inorganic composites based on LDH and
Chen Haiyan PhD Thesis
- 120 -
Dellite at a load of 3 and 6wt-%.
Figure 4.23 shows the torque trend for the PHBV based samples and the additive Joncryl,
dispersed in the PHBV powder, at different concentrations (0.2, 2 and 5 weight percent).
Figures 4.24-4.25 show the torque trend for the hybrid composites, whereas the temperature,
inside the blending chamber (Brabender), and the final torque measures are listed in Table
4.8.
Figure 4.21. Torque Behavoiur vs. Time Recorded for Organic Composites Loaded with
Lignin (LN) with Particle Dimensions Up 39 Micron.
Figure 4.22. Torque Behaviour vs. Time Recorded for Organic Composites Loaded with
Lignin (LN) with Particle Dimensions Under 39 Micron.
Result and Discussion
- 121 -
Figure 4.23. Torque Behaviour vs. Time Recorded for the Inorganic Composites Loaded
with Nano/Micro Structured Clays (Dellite, D – Montmorillonite) and Synthetic Lamellar
Perkalite (LDH).
Figure 4.24. Torque Behaviour vs. Time Recorded for PHBV Samples Loaded with Joncryl
at Different Concentrations (0.2, 2 and 5% by Weight).
Figure 4.25. Torque Behaviour vs. Time Recorded for the Hybrid PHBV Based Composites
Loaded with Lignin (LN) and Dellite (D).
Chen Haiyan PhD Thesis
- 122 -
Figure 4.26. Torque Behaviour vs. Time Recorded for the Hybrid PHBV Based Composites
Loaded with Lignin (LN), Dellite (D) and Joncryl (J).
In general, from the Figures 4.21 to 4.26, it has been observed that all the additives blended
with the PHBV in binary and ternary system decreases substantially the starting torque value
(during feeding) and the final one (trial end) compared to neat PHBV processed in the
Brabender (see Table 4.8). This result confirms that the choice of additives and organic
and/or inorganic fillers was appropriated for PHBV and they don‘t constitute components
that can give adverse reactions such as degradation and cross-linking in the melt.
From the Figure 4.22 it is possible to observe that the hazelnut shell powder (lignin) with
particle dimensions below 39 micron and concentration 5% is the only additive that shows
similar torque behaviour as PHBV starting raw material.
Organic PHBV based composites loaded with lignin (10 and 20%) and the blend containing
Joncryl at 5% and the inorganic composite loaded with lamellar double hydroxide (LDH) (at
3% by wt.) show the major torque stability (see Figure 4.21-4.24). The minor final torque
value is observed for the sample PHBV + LDH3 (Table 4.8).
Moreover, the hazelnut shell powder was used without any treatment of purification and
initial fractionation. So some fractions can contain natural antioxidant agents that can
stabilize PHBV polymer matrix during its processing (see Figures 4.21 and 4.22), thus
protecting it from its thermal degradation via a crotonization reaction, responsabile of a
molecular weight decrease for the starting biopolymer. The lignin addition is useful also for
(1)Rreducing the retail price for various composite formulations, (2) Reinforcing the PHBV
mechanical properties.
Figure 4.24 shows the effect of the Joncryl dispersion on the torque stability and process
ability of pristine PHBV polymer. The Joncryl dispersion in the polymeric matrix shows a
small stabilization effect on the torque during the entire resident time. Considering that the
Joncryl is an additive useful to rebuild the polymer chains in reground condensation
polymers and to restore the melt strength of the polymer into a level sufficient for stable
processing, and for good mechanical strength of the polymer, can be expected an increment
of the torque during the PHBV processing as has been observed during the PLA processing
(see Figures 4.31 and 4.32). Contrary, the variation of PHBV torque was less than expected
and two possible explanations have been put forward:
1) The high molecular weight of PHBV polymer makes unfavourable the chain
extension reaction between the reactive terminal groups from PHBV with the epoxy
groups from Joncryl additive due to a dissolution effect of the end chains reactive
groups inside the melted polymer bulk.
Result and Discussion
- 123 -
2) When the processing temperature is near to the depolymerization temperature of the
polymer, many reactions can have been occurred: the reaction between the Joncryl
epoxidic groups with the reactive site of crotonic acid (obtained from the PHBV
thermal degradation) becomes a competitive reaction with the terminal groups of
the PHBV and it doesn‘t give a relevant effect on the torque evaluation caused by
the small dimensions of the crotonic acid molecules.
However, the Joncryl effect on PHAS results in the combination of two or more
contemporary factors, which become relevant considering the distribution of polymer
molecular weight, the starting molecular weight and the processing conditions.
Deep study must be conducted in order to elucidate the real mechanism of Joncryl on the
PHBV chains during the melt processing and the factor that affects it.
Table 4.8. Final Torque and Stock Temperature Values Recorded for PHBV Based Blends
and Composites.
Sample Code Final Torque
(N*m)
Stocka)
Temperature
(°C)
PHBV 10.1 174
PHBVJ0.2 6.2 175
PHBVJ2 5.3 174
PHBVJ5 5.0 174
PHBVLN5 11.2 176
PHBVLN10 8.2 175
PHBVLN20 9.5 175
PHBVLN10J5 9.5 173
PHBVLN20J5 8.5 174
PHBVLDH3 3.2 173
PHBVD3 5.7 174
PHBVD6 4.4 174
PHBVD3J2 4.9 174
PHBVLN10D3 5.4 174
PHBVLN20D3 6.9 175
PHBVLN10D3J2 5.8 174
PHBVLN20D3J2 6.5 174
PHBVLNF10 0.7 170
a) Stock temperature = set up temperature + 20°C
Functionalized lignin was prepared (see chapter 2) with the aim to improve the compatibility
between the lignin flour, collected from grinding hazelnut shells, and the hydrophobic PHBV
. By using functionalized lignin (LNF), it is possible to observe from Figure 4.27 a dramatic
drop in the torque from the beginning until the end of the processing experiment. This
behaviour has been attributed to a loss on the PHBV molecular weight, suggesting that this
modified organic filler is not useful for maintaining the molecular weight integrity during the
processing operation. This could be correlated with some degradation reactions between the
hazelnut shells components and the modified lignin. This lignin results an unstable
component for the presence of esters groups: the obtained composite resulted very fragile.
Chen Haiyan PhD Thesis
- 124 -
Figure 4.27. Torque Behaviour vs. Time Recorded for PHBV Based Composites loaded with
Lignin (LN) and functionalized Lignin at 10% by wt.
Figure 4.28 shows the dispersion effect promoted by Joncryl on the torque stability and the
PHBV processing. The additive dispersion in the PHBV powder, produces a small stabilizing
effect for the torque during the whole residence time (7 minutes). Joncryl is an additive able
to regenerate the polymeric chain lengths in condensation polymers, giving to the polymer a
good strength in the melt. So we can use stable processing conditions best suited for the
attainment of the required mechanical properties for the final composite material .
Figure 4.28. Torque Behaviour vs. Time Recorded for PHBV/Joncryl at 5%- Assessment of
the Joncryl Dispersion.
In terms of processing in the melt, the most suitable concentration in %-wt for each additive
is reported by following (Table 4.9).
Table 4.9. Better Components Percentage as Ranked on the Torque Response
Lignin (LN) 10
Perkalite (LDH) 3
Dellite (D) 6
Chain extender (Joncryl- J) 0.2 -2
Result and Discussion
- 125 -
Figures 4.29, 4.30 and 4.31 shows the PLA processing characteristic related with the
influence of Joncryl and lignin additives. Figure 4.32 shows the torque behaviour for the
composites varying the amount of lignin by keeping constant the amount of Joncryl. Figure
4.33 shows a comparison for the torque behaviour for the most representative PHBV based
composites vs. PLA based composites.
0
10
20
30
40
50
60
70
0 1 2 3 4 5 6 7 8
Time (min.)
To
rqu
e (
N*m
)
PLA
PLA + J0.2
PLA + J2
PLA + J5
Figure 4.29. Torque Behaviour vs. Time Recorded for PLA Samples Loaded with Joncryl at
Different Concentrations (0.2, 2 and 5% by Weight).
10
11
12
13
14
15
16
17
18
19
20
0 1 2 3 4 5
Time (min.)
To
rqu
e (
N*m
)
PLA
PLA + J0.2
PLA + J2
PLA + J5
Figure 4.30. Enlargement of Torque Behaviour vs. Time Recorded for PLA Samples Loaded
with Joncryl at Different Concentrations (0.2, 2 and 5% by Weight).
0
10
20
30
40
50
60
70
0 1 2 3 4 5 6 7 8
Time (min.)
To
rqu
e (
N*m
)
PLA
PLA + LN10 up 39 microns
PLA + LN10 under 39 microns
PLA + LN20 up 39 microns
PLA + LN20 under 39 microns
Figure 4.31. Torque Behaviour vs. Time Recorded for PLA Composites Loaded with Lignin
at Different Concentrations and Size (10 and 20% by Weight).
Chen Haiyan PhD Thesis
- 126 -
Figures 4.32 and 4.33, show the effect of the Joncryl dispersion and concentration on the
torque stability and processability of PLA pristine polymer. The Joncryl dispersion in the
polymeric matrix shows a small stabilization effect on the torque during the entire resident
time. In particular, a notorious increment in early torque values (Figure 4.33) constitutes an
experimental evidence for the reaction between Joncryl and PHBV when the amount of
Joncryl increases from 2 until 5%.
0
10
20
30
40
50
60
70
0 1 2 3 4 5 6 7 8
Time (min.)
To
rqu
e (
N*m
)
PLA
PLA + LN10 + J5
PLA +LN20 + J5
Figure 4.32. Torque Behaviour vs. Time Recorded for PLA Samples Loaded with Joncryl at
5% by Weight and Different Amount of Lignin (LN).
Figure 4.32 shows the torque behaviour for PLA based composites blended with different
amount and size of lignin. By varying the amount and the size of the organic filler was not
possible observe significant changes in the PLA torque behaviour and the results reported in
Table 4.10 confirm this tendency.
Figure 4.33 shows the torque behaviour for PLA based composites having different amount
of lignin and constant amount of Joncryl. The sample containing 20% of LN and 5% of
Joncryl presents the higher torque stability during the processing, suggesting that this
composite is a suitable candidate for further formulations.
Table 4.10. Final Torque and Stock Temperature Values Recorded for PLA Based Blends &
Composites.
Sample Code Final Torque
(N*m)
Stocka)
Temperature
(°C)
PLA 8.3 186
PLA + J0.2 11.0 189
PLA + J2 13.0 251
PLA + J5 12.0 191
PLA + LN10 39 µm 8.0 187
PLA + LN20 39 µm 7.0 186
PLA + LN10 < 39 µm 7.1 187
PLA + LN20 < 39 µm 9.5 188
PLA + LN10 + J5* 13.4 191
PLA + LN20 + J5* 15.6 193
a) Stock temperature = set up temperature + 20°C
* LN < 39 µm
The effect of the Joncryl and the organic filler on the rheological characteristic of PHA‘s
composites are more evident in PLA matrix than PHBV matrix (see Figure 4.34).
Result and Discussion
- 127 -
0
10
20
30
40
50
60
70
0 1 2 3 4 5 6 7 8
Time (min.)
To
rqu
e (
N*m
)
PHB
PLA
PHB + LN10 + J5
PLA + LN10 + J5
PHB + LN20 + J5
PLA + LN20 + J5
Figure 4.34. Torque Behaviour vs. Time Recorded for PHBV Samples loaded with Joncryl at
Different Concentrations (0.2, 2 and 5% in Weight).
4.5. PHBV Based Blends and Composites Structural Characteristic by Infrared
Spectroscopy (IR)
Figures 4.35-4.37 show the IR spectra recorded for pure PHBV sample and its blends and
composites loaded with the organic filler (lignin), the chain extender (Joncryl) and an
organophilic clay such as montmorillonite named Dellite.
Figure 4.35. IR Spectra Recorded for Pure PHBV Sample and PHBV/Joncryl Blends.
Chen Haiyan PhD Thesis
- 128 -
(a) (b)
Figure 4.36. IR Spectra Recorded for Pure PHBV Sample, PHBV/Lignin Blends and
PHBV/Lignin/Joncryl Composites.
Figure 4.37. IR Spectra Recorded for Pure PHBV Sample and PHBV/Clay (Dellite) Blends.
Figure 4.35 shows the effect of Joncryl concentration on PHBV matrix. The position and the
shape of the IR bands remain unalterate, whereas the intensity of same bands are different in
the analyzed spectra when we consider the neat polymer or its blends and composites
containing an organic filler, a synthetic additive or an organophilic clay.
The addition of the organic filler (lignin), the chain extender (Joncryl) and the organophilic
clay (Dellite) do not create any relevant shift for the C-O, C=O and O-H stretching bands for
all PHBV based blends and composites compared to neat PHBV, except for the blend
PHBV/J0.2 and the composites PHBV/LN20, PHBV/LN10/J5 and PHBV/LN20/J5.
In their IR traces, the IR band correlated to the C=O stretching, falls down at lower
wavenumbers than the value recorded for the same band of neat PHBV: this effect can be
attributed to the resonance effect caused by the epoxy ring in the case of the blend
PHBV/J0.2 and by the aromatic rings in the the case of the hybrid composites (PHBV/LN/J).
Figure 4.38 reports the IR spectra recorded for PLA pure sample and its blends and
composites loaded with the organic filler (lignin) and the chain extender (Joncryl).
Result and Discussion
- 129 -
(a) (b)
Figure 4.38. IR Spectra recorded for Pure PLA Sample, PLA/Joncryl Blend (a) and
PLA/Lignin/Joncryl Composite (b).
The addition of lignin alone or in combination with Joncryl decreases the intensity of the
band correlated to -CH2 stretching band and the shape of the band correlated to -OH
stretching one.
These additives do not modify in a consistent manner the remained part of the spectra.
The only difference, that we can detect, regards the IR spectra recorded for PLA pure sample
and the blend PLA/J containing the additive in a percentage of 5 by weight. The epoxy rings
contained in the additive chains shift to upper value the band correlated to the -C-O
stretching for this selected blend.
4.6. Biodegradation Experiments
The assessment of the extent of biodegradation under different conditions (soil, compost and
water river) for the bio-based polymer composites, constitutes another step to better know
the ultimate environmental fate of these materials and the effect of each component,
comprised in the composite, on the propensity to biodegrade of the material. The requirement
of two steps, abiotic and biotic, in the degradation mechanism of biodegradable plastic
materials has recently led to the preparation and approval of ASTM D5988-03 ―Standard
Test Method for Determining Aerobic Biodegradation in Soil of Plastic Materials or
Residual Plastic Materials After Composting‖. This standard provides a framework to assess
and compare the determining aerobic biodegradation in soil of polymers or residual plastic
materials after composting as well as the degree of biodegradation and ecological impacts in
defined environments after abiotic degradation.
All the experiments have been set up according to standardized procedures relevant to the
evaluation of the biodegradability of plastic items in soil (ISO 17556), compost (ISO 14855)
and aqueous medium (OECD 301B).
The biodegradation in mature compost have been carried out up to completion (6 months of
incubation), whereas the biodegradation tests in soil and water media are still ongoing even
though in a advanced stage with respect to the incubation time frame suggested by the
adopted standardized test procedures.
The results so far collected are thus allowing to formulate conclusive remarks relevant to the
effects on the biodegradation propensity of the analyzed materials as promoted by the
additives and fillers used in the formulation of PHBV based blends and composites. In
particular ligno-cellulosic fillers exhibited a positive effect on the rate and extent of
biodegradation particularly in solid media (soil and mature compost) tests, whereas the
polymeric chain extender additive (Joncryl ADR-4368C) was promoting a general
depressive effect, whose extent was correlated to the amount used in the material formulation.
Chen Haiyan PhD Thesis
- 130 -
4.6.1 PHBV Based Blends and Composites in Soil Medium
In the soil burial respirometric test, the biodegradation kinetics of several PHBV based
composites were compared with those of a pure PHBV sample, with the aim to investigate
the influence of additive and fillers utilized in the composites preparation. In particular, it
was possible to analyze the effect of several components such as the organic filler (lingo-
cellulosic material from hazelnut shells), the inorganic filler (a modified montmorillonite
named Dellite 72T), and special additives such as the chain extender Joncryl ADR-4368 on
the kinetic of the biodegradation process. The analyzed samples, their organic carbon content
and the relevant theoretical CO2 amounts are collected in Table 4.11.
Table 4.11. Organic Carbon Content and Theoretical CO2 for Relevant PHB Based Blends
and Composites.
N Test Sample Code Weight Sample 1
(mg)
Weight Sample 2
(mg)
C org
(%)
ThCO2
(mg)
1 PHBV 382.4 380.1 57.5 803.1
2 PHBV-LN20-D3-J2 380.7 380.3 55.6 775.0
3 PHBV-LN20 381.5 380.4 55.1 768.9
4 PHBV-LN20-J5 380.8 380.0 53.9 751.8
5 PHBV-LN20-D3 380.1 380.5 55.3 770.4
6 PHBV-D3-J2 380.8 381.1 56.1 782.9
7 PHBV-LN10-D3-J2 380.3 382.6 54.5 762.3
8 PHBV-LN10 381.7 380.0 55.8 778.5
9 PHBV-LNF10 384.1 381.6 56.0 786.1
10 PHBV-D3 380.8 384.7 56.6 793.6
11 PHBV-J5 380.3 382.4 59.1 825.7
12 PHBV-LN10-J5 381.3 382.7 56.8 794.9
13 PHBV-LN10-D3 381.2 384.2 55.9 784.4
14 Cellulose 382.2 381.6 44.4 621.7
In Figure 4.40 (a-c), the biodegradation profile of the analyzed materials and reference
compound (cellulose) collected within 12 months of incubation, are reported. The collected
results suggested that the addition of the ligno-cellulosic filler improved the rate and extent
of biodegradation, as recorded in the case of PHBVLN20 sample, whose extent of
mineralization approached a 90% level within the incubation time, whereas the pure PHBV
sample did not exceed 70% biodegradation in the same time frame (Figure 4.40a).
Comparable effects were also recorded in the case of composites containing the combination
of organic and inorganic (Dellite 72T) fillers (Figure 4.40c). Moreover, the biodegradation
trends were similar in the case of the composites having 10% and 20% by weight of hazelnut
shells (lignin), thus suggesting that the biodegradation trend is not affected by the selected
concentrations. On the other hand, the presence of significant amount of the chain extender
additive reduced the rate and the extent of the mineralization process independent of the
presence of organic and inorganic fillers, thus exhibiting a stronger effect as a function of the
concentration utilized in the composites processing (Figures 4.40a, 4.40b and 4.40c).
Result and Discussion
- 131 -
(a) (b)
(c) (d)
Figure 4.40. Mineralization Trend for PHBV/Lignin Composites (a); PHBV/Lignin/Joncryl
Blends (b); PHBV/Inorganic/Organic Filler Composites (c), PHBV/Inorganic/Organic
Filler/Joncryl Composites (d).
Biodegradation takes place through the action of enzymes and/or chemical deterioration
associated with living organisms. This event occurs in two steps, that are the fragmentation
of the polymer into lower molecular weight species by means of either abiotic reactions, such
as oxidation, photo-degradation, hydrolysis, or biotic reactions, such as degradations
promoted by microorganisms. This is followed by bio-assimilation of the polymer fragments
by microorganisms and their mineralisation.
Biodegradability depends not only on the origin of the polymer but also on its chemical
structure and the environmental degrading conditions (Vroman 2009).
The most important factors related to the PHAs characteristics that influence their
degradation are (a) microtacticity, since only monomers in configuration (R) are hydrolyzed
by depolymerases, (b) crystallinity, since the degradation decreases with higher crystalline,
(c) molecular weight, because the polymer of low molecular weight are generally degraded
more rapidly than those with high molecular weight, (d) monomeric composition of PHAs
(Lutz and Falcao 2011).
Also the composition and the compatibilization between the components inside the
formulation play an important role in the biodegradation process for PHBV based
composites loaded with organic filler. In our case, the lignin addition can make more
favourable the hydrolytic degradation of PHBV polymer matrix, even if lignin was found to
exert a protective function against PHBV biodegradation (Mousavioun et al. 2012).
The mineralization trend for PHBV containing melts strength enhancer like Joncryl ADR-
4368 alone or together with lignin showed an inhibitory effect. It can be hypothesized that
the additive promoted a scavenging activity connected to the epoxydic groups responsible of
a possible antibacterial and antifungal activity, thus making very slow the biodegradation
process for PHBV/Joncryl based composites. On the other hand it can be also hypothesized
that the detrimental effect on the biodegradation process could be determined by the
Chen Haiyan PhD Thesis
- 132 -
structural modification (e.g. cross-linking) promoted by the Joncryl addition. A slight, but
significant improvement in the biodegradation process in soil was also observed when PHBV
was processed in the presence of an inorganic component such as Dellite 72T.
Dellite is a modified montmorillonite with quaternary ammonium salts, it can be thereof
hypothesized tha the nitrogen release from the PHBV/Dellite composites, may act a fertilizer
action towards the microorganisms population in the soil (Burkart et al. 2005), making more
favorable the mineralization process.
4.6.2. PHAs Based Blends and Composites Biodegradation in Mature Compost
In the mature compost respirometric tests, the biodegradation kinetics of several PHBV
based composites were compared with the same ones submitted to the biodegradation
experiments in soil, with the aim to investigate the influence of additives and fillers utilized
in the composites preparation on the kinetic of the biodegradation process, as well as to
evaluate the influence of the composting environment with respect to the soil.
The values of total organic carbon content (TOC) and relevant theoretical evolution of
carbon dioxide (ThCO2), necessary to obtain the mineralization percent versus time for the
investigated samples, are collected in Table 4.12.
Table 4.12. Organic Carbon Content (TOC) and Theoretical CO2 (ThCO2) for PHBV Based
Blends & Composites.
N Test Sample Code Weight
Sample 1
(mg)
Weight
Sample 2
(mg)
C org
(%)
ThCO2
(mg)
1 PHBV 146.4 134.1 57.5 295.7
2 PHBV-LN20 148.3 142.5 55.1 293.8
3 PHBV-LN20-J5 146.1 148.3 53.9 290.9
4 PHBV-J5 145.0 149.2 59.1 318.8
5 PHBV-J0.2 149.2 167.3 57.7 334.8
6 Cellulose 144.7 153.7 43.9 240.2
Figure 4.41 shows the mineralization trend for PHBV based composites in compost medium.
(a) (b)
Figure 4.41. Mineralization Trend for PHBV/Joncryl Blends (a) and PHBV/Lignin
Composites (b).
The detrimental effect upon Joncryl addition on PHBV polymer matrix on the mineralization
process of the analyzed materials recorded during the soil burial respirometric test was also
Result and Discussion
- 133 -
observed during the mature compost test (Figure 4.41a). The effect was dramatic once the
concentration of the additive reached 5% by weight (Figure 4.41a). On the other hand, the
presence of ligno-cellulosic filler was found to mitigate the negative effect of the chain
extender additive. Under the adopted incubation condition, the PHBV composite containing
both Joncryl and the organic filler underwent to an extensive mineralization process even
though exhibiting a multi step biodegradation profile (Figure 4.41b).
4.6.3. PLA Based Blends and Composites Biodegradation in Mature Compost
The effect of Joncryl concentration is showed in Figure 4.42a whereas the effect of the
organic filler addition on the biodegradation propensity for PLA polymer matrix is depicted
in Figure 4.42b.
The values of total organic carbon content (TOC) and relevant theoretical evolution of
carbon dioxide (ThCO2), necessary to obtain the mineralization percent versus time for the
investigated samples, are collected in Table 4.13.
Table 4.13. Organic Carbon Content (TOC) and Theoretical CO2 (ThCO2) for PLA Based
Blends & Composites.
N Test Sample Code Weight
Sample 1
(mg)
Weight
Sample 2
(mg)
C org
(%)
ThCO2
(mg)
1 PLA 165.0 154.0 49.7 290.7
2 PLA-LN20 156.0 147.0 50.4 280.0
3 PLA-LN20-J5 157.0 142.0 50.8 278.5
4 PLA-J5 148.0 145.0 51.2 275.0
5 PLA-J0.2 156.0 147.0 52.2 300.5
6 Cellulose 144.7 153.7 43.9 240.2
(a) (b)
Figure 4.42. Mineralization Trend for PLA/Joncryl Blends (a) and PLA/Lignin Composites
(b).
The biodegradation process for PLA based blend containing Joncryl in low concentration
(0.2%) presents a light inhibition respect to the pure PLA sample, as observed from the
traces that remain below the PLA trace (Fig. 4.42a). The same trend can be observed for the
trace of PLALN20J5 composite, where the organic filler try to mitigate the inhibition created
Chen Haiyan PhD Thesis
- 134 -
by Joncryl. The additive concentration increasing until 5% has a dramatic effect on the
biodegration propensity of PLA matrix, in the same manner observed for PHBV
biodegradation pathway.
The chain extender Joncryl posses an antibacterial activity able to decrease the number of
microorganisms, that can degrade the polymer (Mousavioun et al. 2012).
Figure 4.43 reports the hydrolitic degradation mechanism for PLA, in which the molecoles of
water adsorbed by the polymer are able to break down the ester linkages in the polymer
chains. This process can be auto-catalyzed by terminal carboxilic groups and it follows a first
order kinetic, that is influenced by the starting cristallinity, the sample widht and shape
(Siracusa et al. 2008).
Figure 4.43. Hydrolytic Degradation Mechanism for PLA.
The presence of lactic acid and low molecular weight products show an important role in
promoting the starting of a biodegradation process for a film, because of fungi and bacteria
assimilate the inizial lactic acid, colonizing the film superficial area (Hakkarainem 2000).
4.6.4 Qualitative Compost Experiment
In Figures 4.42 and 4.43 the pictures of the most representatives PHBV based composites
samples analyzed for the determination of the degree disintegration within 45 days
incubation, are reported. The test was carried out in accordance with the ISO 14855
normative. More recent norms such as EN-13432-02, ASTM6400-04 and ISO 17088, are
suggesting to increase the incubation time up to twelve weeks (84 days).
After 37 days of incubation, an appreciable growth of filamentous microorganisms (i.e. fungi
and actinomycetes) was observed on the PHBVLN10 and PHBVLNF10 specimens surface
(Figures 4.44 and 4.45). The observed microbial growth was accompanied by a marked
discoloration of the samples specimens (Figure 4.44), whereas no significant trace of
microbial deterioration was observed in the case of PHBVD3 and PHBVJ5 specimens,
containing the inorganic filler and the chain extender, respectively. These observations were
thus suggesting that the samples, containing 10 % by weight of ligno-cellulosic filler and
esterified lignin, are more susceptible to the microbial attack.
In Table 4.14, the gravimetric analysis of the tested samples is reported. The collected data
confirmed the observation obtained by the visual inspection of the analyzed specimen. In
accordance significant specimen weight losses ranging between 2.5-6.0 of the original
Result and Discussion
- 135 -
weight were recorded after 45 days of incubation only in the case of samples processed with
the organic fillers.
The collected observation are suggesting the microbial attack of PHBV based composites
proceeds via surface erosion in accordance with the results obtained by Yun-Xuan Weng et
al (2010) that analyzed the biodegradation behavior of PHBV at pilot scale composting
conditions.
The qualitative results suggested that the presence of lignin can modify the characteristic of
the PHBV based composites leading to a surface more compatible with the surrounding
media and the microbial adhesion thereof.
Table 4.14. Weight Variations During the Biodegradation in Compost for PHBV Most
Representative Composites
Sample Initial Weight at
t=0 (mg)
Final Weight at
t=45 (mg)
Variation (%)
PHBV + LN10% 320,1 311,2 2,8
PHBV + LNF10% 306,4 287,7 6,1
PHBV + D3% 329,2 325,5 1,1
PHBV + J5% 356,2 356,3 0
Figure 4.44. Evolution of the Disintegration Within 45 Days (Setup 1)
Chen Haiyan PhD Thesis
- 136 -
Figure 4.45. Evolution of the Disintegration Within 45 Days (Setup 2)
a) Organic filler b) Inorganic filler
Figure 4.46. Variation of the Colors Sample for PHBV Composites.
4 .6.5. River Water Respirometric Test
The biodegradation experiment in aqueous medium was performed on selected PHBV based
blends and composites in order to investigate the influence of the organic filler (ligno-
cellulosic material from hazelnut shells) and special additives on the kinetic of the
biodegradation process. The propensity to biodegradation in aqueous medium of selected
PHBV based samples was compared with those of reference materials (cellulose and sodium
acetate, CH3COONa), as well as with a low density polyethylene sample (Riblene FL30) and
commercial PLA.
The values of total organic carbon content (TOC) and of the theoretical evolution of carbon
dioxide (ThCO2), necessary to obtain the mineralization percent versus time for the
investigated samples, are collected in Table 4.15.
PHBV-LNF10 PHBV-LN10 PHBV-D3 PHBV-J5
Result and Discussion
- 137 -
Table 4.15. Organic Carbon Content (TOC) and Theoretical CO2 (ThCO2) for PHB Based
Composites and Formulations, References.
Test Sample Code Organic Carbon (TOC)
(%)
ThCO2
(mg)
PHBV 57.5 110.3
PHBV-J0.2 57.7 101.9
PHBV-J5 59.1 108.1
PHBV-LN20-J5 53.9 99.6
PLA 49.7 88.2
Cellulose 43.9 81.3
Riblene FL30 85.6 154.1
CH3COONa 29.2 54.6
In Figure 4.47a-c the biodegradation profiles recorded within 90 days of incubation in
aqueous medium of PHBV based composites and reference materials are reported.
(a) (b)
(c)
Figure 4.47. Mineralization Trend for PHBV/Joncryl Blends (a), PHBV/Lignin/Joncryl
Composite (b), References (c).
Under the adopted incubation conditions, the detrimental effect of relatively high
concentration (5% by weight) of the chain extender Joncryl was confirmed (Figure 4.47a and
4.47b). It was also observed that lower concentration (0.2%) of the additive did not affect
significantly the rate and extent of PHBV biodegradation (Figure 4.47a).
The organic filler did not try to mitigate the inhibition effect created by Joncryl at high
concentration (5%) on PHBV biodegradation propensity (Figure 4.47b).
Finally it is interesting to note the negligible, if any, biodegradation of the ―biodegradable‖
polyester PLA, whose propensity to microbial attack in aqueous medium at room
Chen Haiyan PhD Thesis
- 138 -
temperature resulted strictly comparable with tha exhibited by the not-biodegradable LDPE
sample (Figure 4.47c).
4.7. Biodegradation of Fossil Fuel Based Polymers (ECOFLEX, PE and PS) in Soil-
Plant Systems (Avena sativa –Raphanus sativus)
In the present investigation the potential eco-toxicological effects in soil-plant systems of
polymeric materials represented by thermally degraded Polyethylene (PE) and Polystyrene
(PS) containing proprerly pro-degradant additives were studied; the effects exerted by PE
and PS polymers were compared with those of biodegradable materials such as Ecoflex and
Cellulose, used as positive controls.
The definition of the environmental parameters to be considered when planning a soil
biodegradation test is the first dilemma encountered by researchers. This problem is less
critical when defining biodegradability under composting conditions, because the variability
of the composting environment is low. The composting environment is a rather
homogeneous ecological niche and can be considered as a consistent micro-cosmos. On the
other hand, the environmental factors in soil can be very different from one location to
another and consequently the rate of degradation can be different. Therefore, when studying
biodegradation in soil, characterization of the environmental factors can be important to
relate the biodegradation behavior to a specific soil.
4.7.1. Potential Eco-toxicological Effects of Polymer Materials
The values of seed germination and plant growth were reported in Table 4.16.
Table 4.16. Plant germination and growth measured after 10 days from seedling (45 day
from the beginning of the experimentation)
Sample
Seed
germination
(%)
Average Plant
Length
(mm)
Avena 67 106
Cellulose+Avena 73 103
PE+Avena 74 104
PS+Avena 85 132
Ecoflex+Avena 77 115
Radish 92 53.9
Cellulose+Radish 82 39.3
PE+Radish 70 57.1
PS+Radish 80 49.0
Ecoflex+Radish 65 45.4
The results suggested that the germination of the Avena sativa seeds is not negatively
affected by the application of biomaterials, while for Raphanus sativus there is evidence of a
light inhibition played by all polymers. As regards Avena sativa system, the germination
percentage in degraded polystyrene (PS) treated soil sample was higher than in the other
treatments; moreover, the values of the polymer treatments were always higher than the
Result and Discussion
- 139 -
untreated soil sample (Avena sativa). On the contrary, the soil Raphanus sativus control
system showed the highest value, with the other treatments being in the order:
Cellulose=PS>PE>Ecoflex. The results of average plant lengths reflected the germination
percentage, confirming the different sensitivity of the two selected plant species.
In fact, based on the GI % parameter (Fig. 4.48), a negative effect of polymer application on
soil plant germination and growth is only evident in the presence of Raphanus sativus.
Therefore, in order to give assessment of eco-toxicological effect in a short period, Raphanus
sativus should be considered as a more appropriate indicator.
Fig. 4.48. Plant Germination and Growth Index (GI%).
4.7.2. Soil biochemical parameters
Two categories of microbial enzymes are involved in the degradation of plastic polymers,
namely extracellular and intracellular enzymes. Exoenzymes from microorganisms first
breakdown the complex polymers giving short chains that are small enough to permeate
through the cell walls to be utilized as carbon and energy sources. The process is called
degradation. When the end products are carbon dioxide, water or methane, the process is
called mineralization.
In the degradation of polymers, enzymes function as catalysts for a specific reaction or a
series of reactions, such as oxidation, reduction, hydrolysis, esterification, synthesis and
molecular inter-conversions. Hydrophobic polymers with no hydrolyzable bonds such as PE
and PS are expected to be the most stable (Zeng et al., 2005).
Several soil factors including the availability of water, temperature, oxygen availability,
minerals, pH, redox potential, carbon and energy source influence the growth and activity of
microorganisms (Sand 2003). All these factors, joined together in different combinations,
create different environments and strongly affect the soil ecology. As a consequence the
microbiology and the biodegradation activity can change from soil to soil and from season to
season.
Soil enzyme activities have been considered as useful markers of the impact of pollutants on
the metabolic activity of soil (Ceccanti et al. 2006; Doni et al., 2012). They are the catalysts
of important metabolic functions, including the decomposition and the detoxification of
contaminants; they can rapidly change in response to changes in soil caused by both natural
and anthropogenic factors and they are fairly easy to measure (Nannipieri et al. 2002). As a
result of these advantages, it has been suggested that soil enzyme activities are useful as
early and sensitive indicators of soil alteration in both natural ecosystems and ecosystems
Chen Haiyan PhD Thesis
- 140 -
altered by anthropogenic activities, and, in addition, they are well suited to measure the
impact of pollution on soil quality.
Phosphatases are a large group of intra- and extra-cellular enzymes in soil related to the
phosphorus cycle. They are essential for plant nutrition, since catalyze the hydrolysis of
phosphoric esters releasing inorganic phosphate. Most of phosphorus in soil is in organic
form, and this results from the decomposition of nucleotides, proteins, phospholipids or other
soluble organic compounds. Plants absorb this element in inorganic form through their root
system. The mineralization of organic compounds containing phosphorus is performed by
phosphatases in the nutrient medium or by the root surface. These enzymes play a
particularly important role in soil since that catalyze reactions from different types of
substrate despite having a low specificity (Alef and Nannipieri, 1995).
In the present experimentation (Table 4.17), phosphatase activity generally increased in the
presence of both plant species, Avena sativa and Raphanus sutivus, from T0 (planting time)
to T1 (ten days after planting), suggesting a stimulation of microbial metabolism at root level.
The Ecoflex treatment is the only one that showed a decrease in this enzyme activity. The
highest phosphatase activity was shown in the cellulose treatment with Raphanus sativus
plant at T1.
Protease activity showed very little variation; in general, higher values were observed in the
polymer treatments with respect to the untreated soil. Proteases are a group of hydrolytic
enzymes associated with the nitrogen cycle; they are involved in the first reaction of the
metabolic sequence responsible for the transformation of protein nitrogen into ammonia
(mineralization). As previously reported for phosphatase activity, also protease showed the
lower values in the Ecoflex treatments.
Table 4.17. Enzymes Activity from T0 (Planting Time) to T1 (Ten Days After Planting) for
Some Polymers and Plants Treatments.
Protease
(mgNH3/kg*h)
Phosphatase
(mgPNP/kg*h)
DH-ase
(mgINTF/kg*h)
T0 T1 T0 T1 T0 T1
Control 17.5 16.2 254 226 3.59 3.52
Avena 20.1 20.2 212 234 3.61 2.83
Cellulose+Avena 23.0 24.3 227 240 4.27 4.63
PE+Avena 19.0 20.7 207 257 3.27 5.48
PS+Avena 20.7 23.6 213 281 3.27 3.79
Ecoflex+Avena 16.4 14.9 220 191 4.27 4.54
Radish 18.2 16.3 202 231 3.42 3.20
Cellulose+Radish 22.1 20.1 243 452 4.57 4.70
PE+Radish 22.4 20.1 239 313 2.01 4.63
PS+Radish 20.7 20.8 181 276 2.75 3.46
Ecoflex+Radish 18.7 18.4 238 181 3.23 3.41
T0, soil samples after 35 days from the beginning of experimentation (50% of water
retention capacity; 25 °C of temperature); T1, soil samples after 45 days from the beginning
of experimentation.
Result and Discussion
- 141 -
Dehydrogenases are principally intracellular enzymes and belong to the group of
oxidoreductases; they catalyze the oxidation of organic compounds with the removal of two
hydrogen atoms that are transferred to the molecule of NAD+ or NADP+ (Nannipieri and
Bollag 1991). Dehydrogenase activity is therefore a good indicator of the redox
microbiological system and can be considered a good measure of microbial oxidative activity
in soil (Laudicina, et al. 2012; Masciandaro, et al. 2000).
In the present experimentation, dehydrogenase activity increased over time in all the
treatments, while decreased or remain stable in the unplanted (control) and in the untreated
planted soil (Avena sativa and Raphanus sativus) (Table 4.17 and Figure 4.49), thus
indicating an effect of the polymer addition on microbial metabolism stimulation. This
microbial activity stimulation can be responsible for the hydrolytic enzyme activity increase,
especially phosphatase.
Fig. 4.49. Dehydrogenase Activity of Soil Samples.
The metabolic index, calculated as the ratio between dehydrogenase activity and water
soluble carbon (DH-ase/WSC) represents a parameter related to metabolic activity and
availability of easily degradable organic carbon, which represents also a source of nutrients
(Masciandaro et al., 2004).
This parameter seems to be stimulated at T1 in the presence of both plant species. This trend
indicates a general improvement of soil metabolism being both plants capable to remove the
inhibitory effect of polymer in soil.
Fig. 4.50. Metabolic Index of Soil Samples.
Chen Haiyan PhD Thesis
- 142 -
Even though with these laboratory tests it is not possible to prove biodegradation in terms of
metabolization by microorganisms, the short and reproducible test conditions make them
especially useful for a preliminary assessment and comparison of polymer biodegradability
in soil.
4.7.3. Chemical parameters of soil samples treated with different polymers
Soil chemical parameters measured during the experimentation were shown in Table 4.18.
The pH values did not show evident differences in the biopolymer treated soil samples with
respect to the control. However, a general increase in electrical conductivity was observed at
T1 sampling time in the presence of Raphanus sativus, in particular in the treatment with
cellulose and polyethylene. The higher electrical conductivity in these soil samples is
probably due to the higher content of nitrate, which reached the highest value in the cellulose
treatment. This suggests the establishment of the better aeration conditions for
microorganisms in carrying out their activity. In agreement with this result, the Raphanus
sativus planted soil in the presence of cellulose showed, at T1 sampling time, the high
dehydrogenase activity.
These results suggest the positive effect of legume plant Raphanus sativus towards microbial
activity and N cycle. Both plant species improve the availability of the nutrients, usually
expressed by the ratio nitrate/ammonia ions. The WSC showed a different trend; the lower
values were, in fact, generally observed in correspondence of higher values of nitrate. In
view of this, a negative correlation nitrate/WSC has been found in presence of Raphanus
sativus (Table 4.18; r=-0.639).
These results clearly indicated the best capability of Raphanus sativus in reducing water
soluble carbon (WSC) during polymer degradation in soil, which prevent loss of carbon and
a potential surface and ground water pollution.
Result and Discussion
- 143 -
0, soil samples after 35 days from the beginning of experimentation (50% of water retention capacity; 25 °C of temperature); T1, soil samples after 45
days from the beginning of experimentation.
Tab. 4.18. Chemical Parameters of the Soil in the Different Treatments
pH Electrical
Conductivity (µS/cm)
Water soluble
carbon (WSC)
(mgC/kg)
NO3-/NH4
+
Nitrate
(mgNO3-/Kg)
Ammonia
(mgNH3/Kg)
T0 T1 T0 T1 T0 T1 T0 T1 T0 T1 T0 T1
Control 7.1 7.2 106.3 113 466 455 18.26 14.6 225.12 175.09 12.33 12.0
Avena 7.04 7.31 109.4 95.7 391 391 11.18 12.62 178.64 140.26 15.98 11.12
Cellulose+Aven
a 7.02 7.22 127.3 118.9 445 649 14.22 10.79 229.97 158.44 16.18 14.69
PE+Avena 7.17 7.21 123 118.3 670 455 34.75 28.21 263.23 296.49 7.58 10.51
PS+Avena 7.07 7.18 128.1 125.7 466 455 15.3 22.89 320.23 314.69 20.93 13.75
Ecoflex+Avena 7.02 7.1 116.9 51.1 573 327 14.53 61.56 170.33 392.55 11.72 1.50
Radish 6.98 7.43 112.1 125.8 531 370 12.26 42.59 188.45 421.81 15.37 9.90
Cellulose+Radis
h 7.11 7.25 108.4 142.9 531 391 6.24 154.04 126.92
1229.3
1 20.33 7.98
PE+Radish 7.08 7.27 82.4 136.5 777 423 24.17 23.0 183.07 344.68 7.58 15.27
PS+Radish 6.95 7.28 114.5 117 702 391 9.14 86.50 177.50 620.24 19.42 7.17
Ecoflex+Radish 7.14 7.19 99.4 120.1 434 434 15.23 90.88 175.44 679.31 11.52 7.47
Chen Haiyan PhD Thesis
- 144 -
4.7.4. Statistics analyzes about Biplot PC1 versus PC2
Figures 4.51-4-52 are the statistics analysis of all parameters Principal Component Analysis
(PCA). The STATISTICA 6.0 software (StatSoft Inc., Tulsa, Oklahoma, USA) was used for
all statistical analysis. All numerical parameters before statistical analysis were normalized
and autoscaled: the result for each variable is a zero mean and an unit standard deviation
(Latorre et al., 1999).
Scatterplot (statistic undegraded log 12v*24c)
C t0
A t0
A-CE t0
A-PE t0
A-PS t0
A-E t0
C t1
A t1
A-CE t1
A-PE t1
A-PS t1
A-E t1
C t0
R t0
R-CE t0
R-PE t0
R-PS t0
R-E t0
C t1
R t1
R-CE t1
R-PE t1
R-PS t1
R-E t1
Ammonium
Nitrate
protease
phosphatase
heavy metal
pH
E.C
MI
-3,0 -2,5 -2,0 -1,5 -1,0 -0,5 0,0 0,5 1,0 1,5 2,0
PC1
-2,5
-2,0
-1,5
-1,0
-0,5
0,0
0,5
1,0
1,5
PC
2
Figure 4.51. Biplot PC1 Versus PC2.
Result and Discussion
- 145 -
Scatterplot (statistic undegraded log 13v*24c)
C t0
A t0
A-CE t0A-PE t0
A-PS t0
A-E t0
C t1
A t1
A-CE t1
A-PE t1A-PS t1
A-E t1
C t0
R t0
R-CE t0R-PE t0
R-PS t0
R-E t0
C t1R t1
R-CE t1
R-PE t1
R-PS t1
R-E t1
Ammonium
Nitrate
protease
phosphataseheavy metal
pH
E.C
MI
-3,0 -2,5 -2,0 -1,5 -1,0 -0,5 0,0 0,5 1,0 1,5 2,0
PC1
-3
-2
-1
0
1
2
3
PC
3
Figure 4.52. Biplot PC1 Versus PC3.
The chemical and biological results were studied using the Principal Component Analysis
(PCA). PCA is a multivariate statistical data analysis technique which reduces a set of raw
data into a number of principal components which retain the most of the variance within the
original data in order to identify possible patterns or clusters between treatments and
variables. The PCs were extracted by applying the principal of main axis method. Only
component loadings >0.7 were considered for interpretation of the PCs. In PCA analysis, the
data are decomposed into separate sets of scores and loadings for each of the two modes of
interest (treatments and variables) and the whole variability of the data is explained in order
to provide a clear and more interpretable visualization of data structure in a reduced
dimension. In addition, PCA analysis gives information that can also be clearly presented
graphically (Carroll, et al. 2004).
In Tables 4.19-4.20 are reported the correlation analysis of all test parameters of two plants,
Oat (Avena sativa) and Radish (Raphanus sativus).
PCA analysis isolated three principal components (PC) (Total variance explained: 70.2%)
covering variables related to chemical and biochemical parameters of the different treatments
(Table 4.19). The highest loadings of the first PC (PC1, 24.2% of the total variance) included
the phosphatase activity and the metabolic index (DH-ase/WSC) which show positive
correlation (Figure 4.51), meaning that the carbon cycling was activated and was able to
sustain microbial activity. The second PC (PC2, 23.2% of the total variance) included the
ammonium and the protease activity, indicating the activation of nitrogen cycle. Finally, the
third PC (PC3, 22.8% of the total variance) included the nitrate and the electrical
conductivity demonstrating also that nitrate contributed to soil electrical conductivity, and
that the system is evolving toward the production of nitrate nutrients.
Chen Haiyan PhD Thesis
- 146 -
PC1 and PC2 were chosen for the interpretation of the biplot of scores and loadings (Figure
4.52), in order to draw conclusions about the effects of polymer materials application on the
soil chemical and biochemical characteristics.
The treatments, at T1 sampling time were shifted on the right of the biplot with respect to T0
and resulted located nearer to the biochemical parameters. This indicated a stimulation over
time of the phosphatase activity (Table 4.17) and metabolic index (Figure 4.50), which were
significant on PC1 axis.
On the contrary, the treatments at T1 were generally shifted towards negative values of the
second principal component (PC2), which represents the variation of ammonium and
protease activity, thus indicating a decrease of these parameters.
Considering the different treatments, PS and PE at T0 are located on the left negative side in
the biplot (PC1 axis) indicating a negative effect of these polymers on microbial metabolism.
After forty-five days (T1) incubation, such negative effects resulted less evident; the
treatments are, in fact, cluster in the positive side of the biplot.
Table 4.19. Principal Component Analysis (PCA) of Paremeters
PC1 PC2 PC3
Ammonium -0.220 0.881 -0.089
Nitrate 0.148 -0.291 0.866
protease 0.044 0.832 0.088
phosphatase 0.719 0.193 0.453
heavy metal -0.665 0.327 -0.105
pH 0.509 -0.117 0.410
E.C 0.012 0.384 0.813
MI 0.802 -0.008 -0.118
Variance explained (%) 24.2 23.2 22.8
Total variance explained: 70.2%)
Result and Discussion
- 147 -
Table 4.20. Correlation Analysis about Testing Paremeters of Oat (Avena sativa) and Radish (Raphanus sativus)
AVENA SATIVA
45 days WSC Amm Nitrate protease phosph Heavy-Me DH-ase pH E.C. M. Index Plant
biomass GI%
WSC 0.599 0.037 0.715 0.419 0.293 0.250 0.265 0.629 -0.569 0.405 -0.165
RA
PH
AN
US
SA
TIV
US
Amm -0.254 -0.535 0.977 0.755 0.761 0.076 0.504 0.406 -0.460 0.817 0.079
Nitrate -0.639 -0.314 -0.396 -0.028 -0.626 -0.268 -0.012 0.542 -0.299 0.259 0.519
protease 0.017 0.626 0.087 0.802 0.634 0.105 0.428 0.536 -0.522 0.758 0.172
phosph -0.226 -0.099 0.689 0.580 0.288 0.043 0.355 0.750 -0.425 0.623 0.450
heavy-Me -0.360 0.653 -0.365 0.024 -0,510 -0.214 0.774 0.023 -0.436 0.711 -0.533
DH-ase 0.023 0.358 0.231 0.95 0.822 -0.275 -0.483 -0.067 0.631 -0.697 -0.131
pH -0.801 0.155 0.271 -0.282 0.048 0.394 -0.143 0.423 -0.707 0.697 -0.468
E.C. -0.127 -0.154 0.364 0.313 0.817 -0.395 0.681 0.326 -0.667 0.636 0.178
M.Index -0.363 0.399 0.489 0.823 0.872 -0.135 0.922 0.163 0.691 -0.955 0.023
Plant
biomass -0.696 -0.777 0.851 -0.258 0.518 -0.714 0.054 0.384 0.393 0.292 0.206
GI% -0.579 -0.650 0.931 0.236 0.857 -0.511 0.444 0.196 0.657 0.673 0.670
Chen Haiyan PhD Thesis
- 148 -
The correlation coefficients among the parameters have been calculated separately for
Raphanus sativus and Avena sativa, to better relate soil metabolic processes and plant
germination and growth (Figure 4.50).
Raphanus sativus plant biomass correlated negatively with the WSC and ammonia, while it
was positively correlated with the nitrate. In the presence of this plant species, a high positive
correlation between metabolic index (MI) and protease and phosphatase activities was also
showed. On the contrary, in the presence of Avena sativa plant biomass was correlated with
ammonia and MI, but with the opposite trend. This confirmed again a more active
metabolism in Raphanus sativus than Avena sativa.
Result and Discussion
- 149 -
4.8. PHB biodegradation in soil
After one week from the treatments, total microbial cultivable population significantly
increased in both the PHB treatments (Figure 4.53) with respect to the untreated soil (B). The
highest dose showed the highest value. This trend is more evident when considering the
cultivable Pseudomonas genus (Figure 4.54). This means that the soil microorganism were
ready to utilize the PHB as a carbon source.
PHB-degrading microorganisms are ubiquitous in the environment and several extracellular
PHB depolymerases from Alcaligenes, Comamonas and Pseudomonas have been isolated,
purified and characterized (Yutaka Tokiwa, Buenaventurada P. Calabia 2004). PHB
depolymerases of Pseudomonas lemoignei hydrolyze PHB mainly into the dimeric and
trimeric esters of 3-hydroxybutyrate (Jendrossek, et al. 1993).
0,0E+00
1,0E+07
2,0E+07
3,0E+07
4,0E+07
5,0E+07
6,0E+07
7,0E+07
8,0E+07
B1 H1 L1
CFU
g-1
Total microbial population
Figure 4.53.Total Cultivable Microbial Population After One Week Incubation.
B, untreated soil, H, 2% of PHB in soil; L, 1% of PHB in soil.
0,0E+00
5,0E+04
1,0E+05
1,5E+05
2,0E+05
2,5E+05
B1 H1 L1
CFU
g-1
Pseudomonas
Figure 4.54. Pseudomonas Population After One Week Incubation.
B, untreated soil, H, 2% of PHB in soil; L, 1% of PHB in soil.
The stimulation of microbial growth and activity was confirmed by the activation of the
arylesterase and PHB depolymerase activities (Figures 4.55, 4.56).
Arylesterase activity showed a significant increase after four weeks from treatments in both
PHB doses with respect to untreated soil, while the depolymerase was activated just after one
Chen Haiyan PhD Thesis
- 150 -
week.
This could mean that the two enzymes act consecutively on the PHB degradation:
depolymerase activity release ester fragments which are the substrate of other enzymes,
including arylesterase activity.
PHB can be degraded either by the action of intracellular or extracellular depolymerases
(Calabia and Tokiwa, 2006).
0,00
50,00
100,00
150,00
200,00
250,00
300,00
350,00
control soil high PHB Low PHB
mm
olP
NP
/Kg*
h)
Arylesterase activity1 week
3 week4week
Figure 4.55. Aryl Esterase Activity After One, Three and Four Week Incubation.
Control soil, untreated soil; high PHB, 2% of PHB in soil; Low PHB, 1% of PHB in soil.
Figure 4.55. PHB-Depolymerase Activity After One and Four Week Incubation.
B, untreated soil, H, 2% of PHB in soil; L, 1% of PHB in soil.
Conclusion
- 151 -
5. CONCLUSIONS
The research work devoted to the accomplishment of the Doctorate Thesis can be divided in
two parts. The first was related to the assessment of processing profile, thermal properties
and biodegradation propensity for synthetic commercially available polyesters (Ecoflex and
Ecovio) and bio-based polymers (PHBV, PLA and their blends and composites).
The main conclusions of this part were, as follow, in details:
Biodegradation respirometric tests were carried out under different incubation
conditions, in the presence of microbial consortia present in different environmental
compartments such as forest soil, mature compost and river water.
Polymers biodegradation depends on the soil microorganisms activity and moisture
condition of the incubation medium.
Useful information on the effect of the composition of PHBV based materials on their
biodegradation behaviors have been collected.
It was confirmed that pure PHBV samples are readily biodegradable under all the
adopted test conditions.
Additive and fillers utilized in the preparation of the analyzed materials may affect
significantly the biodegradation kinetics in different environmental compartments.
The presence of the chain extender in a concentration of 5 percent by weight, which
was utilized with the aim to improve the mechanical properties of PHBV, induced a
negative impact on the PHBV biodegradation process.
The addition of ligno-cellulosic fillers can modify the negative impact of the chain
extender, thus increasing the biodegradation propensity as a function of its amount
inside the PHBV composite. The mitigating effect is more evident once the samples
were submitted to biodegradation in mature compost at 58°C.
The same evidences were noticed in the biodegradation experiments carried out in soil
& aqueous media.
The addition of a chain extender (Joncryl) in high concentration (5%) strongly affects
PHBV and PLA based composites biodegradation propensity in all analyzed media. On
the other side, a little concentration (0.2%) for this additive did not create a great impact
on the composites biodegradation behavior.
PLA and its blends and composites, in compost conditions, showed biodegradation
kinetics slower than those recorded for the analogous PHBV based blends and
composites.
Joncryl addition to neat PLA produced more stringent limits for biodegradation
propensity than those recorded for PHBV based samples.
The preliminary studies on PHBV processing profile showed that the suitable
concentration for the organic filler was 10%, for the inorganic filler was 3% and the
Joncryl amount was 0.2%. For PLA processing profile, the suitable concentration was
20% for lignin and 0.2% for Joncryl.
The addition of an organic ligno-cellulosic filler (powder obtained by the grinding of
hazelnut shells) alone or in combination with the chain extender Joncryl and the
inorganic filler (Dellite 72T) showed a reinforcing and compatibilizing action of these
components for PLA, as detected by the torque trend stability for the PLA/LN20/J5
composite compared to neat PLA.
Lignin and inorganic filler can significantly increase the onset temperature and residue
values for PHBV based composites. The composites become more thermally stable than
the neat polymer, thus they start their degradation at higher temperature. The results
Chen Haiyan PhD Thesis
- 152 -
obtained on PHBV/D3 composite show better thermal properties than PHBV/D6
composite.
PLA mixing with lignin, alone or in combination with a synthetic additive (Joncryl)
and/or an inorganic component (Dellite) produced a thermal stability increasing (Ton)
for the composites PLA/LN20 and PLA/LN20/J5.
PLA/Joncryl blends showed a complex DTGA trace, thus the chain extender promoted
cross-linking and oxidative reactions between epoxy –OH groups and the PLA end
capping OH groups.
Joncryl addition produced a molecular weight increase for PLA/Joncryl blends, as
detected by GPC analysis. Joncryl reactive sites selected preferably some polymeric
chains respect to others (double eluition peak), when its concentration did not exceed 2
percent by weight.
From DSC results, lignin and inorganic components can decrease the melting enthalpy
for the composites increasing experiment temperature.
A little amount Joncryl (0.2-2%) had no effect on the melting enthalpy, whereas a
significant decrease was observed by using a chain extender amount of 5 percent by
weight of addition produces a decrease of the enthalpy. PHBV/LN20/D3/J2 is the best
composite in terms of the lowest melting enthalpy.
The addition of Joncryl and Dellite produced a decrease in composites melting
temperatures, whereas lignin addition showed an increase of that parameter.
DSC thermograms, for PLA based composites, showed fairly high glass transition
temperature (Tg). That can be correlated with the rigidity and fragility of the composite
material.
The second part consisted of two experiments carried out at the Institute of Ecosystem Study
(ISE) of the National Research Council (CNR).
The experiment performed on the polymer materials PE, PS, Ecoflex and cellulose in a soil-
plant system, under controlled environmental conditions, showed that the selected
parameters were efficient and appropriate in discriminating the effect of the polymer
degradation on soil properties. In this experiment we selected several chemical and
biochemical parameters usually used to assess soil quality and its response to xenobiotic
compounds. The experiment has focused especially with a soil plant system to assess the
unbalance of nutrients and plant growth inhibition. Since PE, PS and Ecoflex represent three
different potential sources of available carbon, the water soluble carbon fraction of soil
organic matter (WSC) was studied in attempt to relate soil nutrient response to carbon
induced metabolism.
The biomaterial application increased the microbial metabolism in soil through the
supply of a potential carbon and nitrogen source.
The germination index (GI %) showed a negative effect of polymer application on plant
germination and growth only in the presence of Raphanus sativus, while Avena sativa
was not negatively affected. Therefore, in a short period, Raphanus sativus could be
considered as a most appropriate indicator of eco-toxicological effect of polymers. This
effect was consolidated by an appropriate statistical treatment, which clearly indicated
that the polymers promoted the carbon cycle and in turn activated organic nitrogen
metabolism, bringing the soil plant system towards the nitrate nutrient production.
Ecoflex compared to PE and PS showed the higher nitrate/ammonia ratio and the lower
water soluble carbon content (WSC). This indicated that the system prevents the loss of
carbon and the potential surface and ground water pollution, while maintains an
equilibrate level of available nitrogen nutrients.
In the preliminary experiment of the PHB polymer biodegradation, specific
Conclusion
- 153 -
microorganisms and enzyme activities were investigated. Total microbial cultivable
population and Pseudomonas genus significantly increased in both high (H) and low (L)
PHB treatments with respect to the untreated soil. The stimulation of microbial growth
and activity was confirmed by the activation of the arylesterase and PHB depolymerase
activities. The very high stimulation of Pseudomonas genus, particularly at the high
dose of PHB (2%), suggested its involvement in the PHB degradation through the
synthesis of the depolymerase enzyme. This preliminary approach must be better
investigated in details with appropriate experiments where the enzymes are extracted
from soil and purified in order to plan efficient enzyme-assisted processes of polymers
biodegradation in a real environment.
Chen Haiyan PhD Thesis
- 154 -
REFERENCES
Aarnio T., Hämäläinen A. (2008), ―Challenges in packaging waste management in the fast
food industry‖ Resources, Conservation and Recycling, 52(4): p. 612-621.
Abe H., Doi Y. (1999), ―Structural effects on enzymatic degradability for poly[(R)-3-
hydroxybutyric acid] and its copolymers‖ International Journal of Biological
Macromolecules 25:p. 185-192
Abe, M., Kobavashi K., Homma N., Nakasaki K. (2010), ―Microbial degradation of
poly(butylene succinate) by Fusarium solani in soil environments‖ Polymer Degradation and
Stability, 95(2): p. 138-143.
Abou-Zeid D.M., Muller R.J., Deckwer J.D. (2001), ―Degradation of natural and synthetic
polyesters under anaerobic conditions‖ Journal of Biotechnology, 86: p. 113–126.
Akerdi A.A.M., Shokoufeh Hakim A.R., Fazeli N. (2007), ―Investigation of Physical and
Mechanical Properties of General Purpose Polystyrene with Bimodal Molecular Weight
Distribution‖ Iranian Polymer Journal, 16(2): p. 75-81.
Akmal D., Azizan M.N., Majid M.I.A. (2003), ―Biodegradation of microbial polyesters
P(3HB) and P(3HB-co-3HV) under the tropical climate environment‖ Polymer Degradation
and Stability, 80: p. 513–518.
Albertsson A.C., Andersson S.O, Karlsson S. (1987), ―The mechanism of biodegradation of
polyethylene‖. Polymer Degradation and Stability, 18(1): p. 73-87.
Albertsson, Ann-Christine, Camilla Barenstedt, and Sigbritt Karlsson (1994), Degradation of
enhanced environmentally degradable polyethylene in biological aqueous media:
Mechanisms during the first stages. Journal of Applied Polymer Science 51(6):1097-1105.
Albertsson A.-C., and S. Karlsson. (1988), The three stages in degradation of polymers-
Polyethylene as a model substance. J. Appl. Polym. Sci. 35: 1289-1302
Albertsson A.-C., Erlandsson B., Hakkarainen M., and Karlsson S. (1998), Molecular weight
changes and polymeric matrix changes correlated with the formation of degradation products
in biodegraded polyethylene. J. Environ. Polym. Degrad. 6: 187-195
Albertsson A.-C., C. Barenstedt, S. Karlsson, T. Lindberg, (1995), Polymer, 36, 3075.
Albertsson A.-C., C. Barenstedt, S. Karlsson, (1993) Acta Polym., 45, 97.
Albertsson A.-C., Banhidi Z.G. (1980), Microbial and oxidative effects in degradation of
polyethylene. J. Appl. Polym. Sci., 25: 1655-1671
Albertsson, A.-C., Barenstedt, C., Karlsson, S., and T. Lindberg. (1995) Degradation product
pattern and morphology changes as means to differentiate abiotically and biotically aged
degradable polyethylene. Polymer 36: 3075-3083
Albertsson, C. Barenstedt, S. Karlsson.(1994), Abiotic degradation products from enhanced
environmentally degradable polyethylene. Acta Polym 45:97-103.
Reference
- 155 -
Albertsson, A. C. (1980), The shape of the biodegradation curve for low and high density
polyethenes in prolonged series of experiments. European Polymer Journal 16(7):623-630.
Alef K., and P. Nannipieri. (1995), Methods in Applied Soil Microbiology and Biochemistry.
London: Academic Press.
Al-Malaika S., Β. Chakraborty, G. Scott, (1983), Dev. Polym. Stab., 6, 73.
Al-Malaika S., G. Scott, (1983) Polym. Degrad. Stab., 5, 415.
Al-Malaika S., G. Scott, in: N. S. Allen (Ed), (1983), Degradation and stabilisation of
polyolefins. London: Applied Science Publishers; [chapters 6 and 7].
Altan M., Yildirim H. (2010), ―Mechanical and morphological properties of polypropylene
and high density polyethylene matrix composites reinforced with surface modified nano
sized TiO2 particles‖ World Academy of Science, Engineering and Technology, 46: p. 289-
294.
Amass W., Amass A., Tighe B. (1998), ―A review of biodegradable polymers: uses, current
developments in the synthesis and characterization of biodegradable polyesters, blends of
biodegradable polymers and recent advances in biodegradation studies‖ Polymer
International, 47(2): p. 89-144.
Arena M., Abbate C., Fukushima K., Gennari M. (2011), ―Degradation of poly (lactic acid)
and nanocomposites by Bacillus licheniformis‖ Environ Sci Pollut Res, 18: p. 865-870.
Ariffin H., Nishida H., Shirai Y., Hassan M.A. (2008), ―Determination of multiple thermal
degradation mechanisms of poly(3-hydroxybutyrate)‖ Polymer Degradation and Stability,
93(8): p. 1433-1437.
Ariffin H., Nishida H., Shirai Y., Hassan M.A. (2009), ‖Anhydride production as an
additional mechanism of poly(3-hydroxybutyrate) pyrolysis‖ Journal of Applied Polymer
Science 111: p. 323-328.
Artham, Trishul, and Mukesh Doble. (2008), Biodegradation of Aliphatic and Aromatic
Polycarbonates. Macromolecular Bioscience 8(1):14-24.
Arnaud, R., Dabin, P., Lemaire, J., Al-Malaika, S., Chohan, S., Coker, M., Scott, G., Fauve,
A., and A. Maaroufi. (1994), Photooxidation and biodegradation of commercial
photodegradable polyethylenes. Polym. Degrad. Stab. 46: 211-224
ASTM 883-1991, ―Standard terminology relating to plastics‖
ASTM D6400-04, Standard specification for compostable plastics”
ASTM D5988-03 ―Standard test method for determining aerobic biodegradation in soil of
plastic materials or residual plastic materials after composting‖
ASTM, A. S. f. T. a. M. (2003), Standard Test Method for Determining Aerobic
Biodegradation of Plastic Materials under Controlled Composting Conditions., Vol. 2003b.
ASTM International: West Conshohocken, PA.
Chen Haiyan PhD Thesis
- 156 -
Atlas R.M., R. Bartha, (1997), Microbial Ecology: Fundamentals and Applications. Menlo
Park, CA enjamin/Cummings Publishing Company.
Avella M., Rota G., Martuscelli E., Raimo M., Sadocco P. (2000), ―Poly(3-hydroxybutyrate-
co-3-hydroxyvalerate) and wheat straw fibre composites: thermal, mechanical properties and
biodegradation behaviour‖ J Mater Sci, 35: p. 428-436.
Avella M., Di Pace E., Immirzi B., Impallomeni G., Malinconico M., Santagata G. (2007),
―Addition of glycerol plasticizer to seaweeds derived alginates: Influence of microstructure
on chemical–physical properties‖ Carbohydrate Polymers, 69(3): p. 503-511.
Balasuriya P.W., Ye L., Mai Y.W. (2001), ―Mechanical properties of wood flake–
polyethylene composites. Part I: effects of processing methods and matrix melt flow
behaviour‖ Composites Part A: Applied Science and Manufacturing, 32(5): p. 619-629.
Banar M., Cokaygil Z., Ozkan A. (2009), ―Life cycle assessment of solid waste management
options for Eskisehir, Turkey‖ Waste Management, 29(1): p. 54-62.
Barlaz, Morton A., Robert K. Ham, and Daniel M. Schaefer, (1989), Mass-balance analysis
of anaerobically decomposed refuse. Journal of Environmental Engineering 115(6):1088-
1102.
ssig J. (2008), ―Impact and tensile properties of PLA/cordenka and PLA/flax
composites‖ Composites Science and Technology, 68: p. 1601-1607
Belhassen R., Mendez J.A., Boufi S., Lopez J.P. Puig J., Pelach A., Mutje P. (2009),
―Preparation and properties of biocomposites based on jute fibers and blend of plasticized
starch and poly(beta-hydroxybutyrate)‖ Journal of Applied Polymer Science, 114(1): p. 313-
321.
Bengtsson, M., Gatenholm P., Oksman K. (2005), ―The effect of crosslinking on the
properties of polyethylene/wood flour composites‖ Composites Science and Technology,
65(10): p. 1468-1479.
Benitez, S., Sosa, C., Tomasini, N., Macias, A.(2010) Both JNK and apoptosis pathways
regulate growth and terminalia rotation during Drosophila genital disc development. Int J
Dev Biol 54(4):643-53.
Billingham N. C., and P. D. Calvert (1983). In Degradation and stabilisation of polyolefins.
N.S. Allen, ed, Vol. 1. London: Applied Science Publishers.
Biresaw G., Carriere C.J. (2002), ―Interfacial tension of polycaprolactone/polystyrene blends
by the imbedded fiber retraction method‖ Journal of Applied Polymer Science, 83(14): p.
3145-3151.
Biresaw G., Carriere C.J. (2004), ―Compatibility and mechanical properties of blends of
polystyrene with biodegradable polyesters‖ Composites Part a-Applied Science and
Manufacturing, 35(3): p. 313-320.
Reference
- 157 -
Biresaw G., Mohamed A., Gordon S.H., Harry-O'kuru R. E., Carriere C.C. (2008),
―Compatibility study in poly(tetramethyleneadipate-co-terephthalate)/polystyrene bioblends‖
Journal of Applied Polymer Science, 110(5): p. 2932-2941.
Bianchi V. and Ceccanti B. (2010), A three components system (TRIAS) in the
phytoremediation of polluted environmental matrices. Toxicological & Environmental
Chemistry, 92 (3): 477-493
Bikiaris, D., Aburto, J., Alric, I., Borredon, E., Botev, M., Betchev, C., Panayiotou, C.(1999),
Mechanical Properties and Biodegradability of LDPE Blends with Fatty-Acid Esters of
Amylose and Starch. Journal of Applied Polymer Science 71(7):1089-1100.
Bhatt R., Shah D., Patel K.C., Trivedi U. (2008), ―PHA–rubber blends: synthesis,
characterization and biodegradation‖ Bioresource Technology, 99: p. 4615–4620.
Bledzki A.K., Jaszkiewicz A. (2010), ―Mechanical performance of biocomposites based on
PLA and PHBV reinforced with natural fibres- A comparative study to PP‖ Composites
Science and Technology, 70: p. 1687-1696.
Bledzki A.K., Jaszkiewicz A., Scherzer D. (2009), ―Mechanical properties of PLA
composites with man-made cellulose and abaca fibres‖ Composites. Part A, 40: p. 404-412.
Bogaert J.C., Coszach P. (2000), ―Poly(lactic acids): a potential solution to plastic waste
dilemma‖ Macromolecular Symposia, 153(1): p. 287-303.
Bonartseva G.A., Myshkina V.L., Nikolaeva D.A., Rebrov A.V., Gerasin V.A., Makhina T.K.
(2002), ―The biodegradation of poly-β-hydroxybutyrate (PHB) by a model soil community:
the effect of cultivation conditions on the degradation rate and the physicochemical
characteristics of PHB‖ Microbiology, 71(2): p. 221-226.
Bonartseva G.A., Myshkina V.L., Nikolaeva D.A., Kevbrina M.V., Kallistova A., Gerasin
V.A., Iordanskii A.L., Nozhevnikova A.N. (2003), ―Aerobic and anaerobic microbial
degradation of poly-β-hydroxybutyrate produced by azotobacter chroococcum‖ Applied
Biochemistry and Biotechnology, 109(1-3): p. 285-301.
Bonartsev A.P., Myshkina V.L., Nikolaeva D.A., Furina E.K., Makhina T.A., Livshits V.A.,
Boskhomdzhiev A.P., Ivanov E.A., Iordanskii A.L., Bonartseva G.A. (2007), ―Biosynthesis,
biodegradtion, and application of poly(3-hydroxybutyrate) and its copolymers-natural
polyesters produced by diazotropic bacteria‖ Communicating Current Research and
Educational Topics and Trends in Applied Microbiology, p. 295-307.
Bonhomme, S., Cuer, A., Delort, A. M., Lemaire, J., Sancelme, M., Scott, G. (2003),
Environmental biodegradation of polyethylene. Polymer Degradation and Stability
81(3):441-452.
Bonmatì M., Ceccanti B, Nannipieri P, and Valero J, (2009), Characterization of humus-
protease complexes extracted from soil, . Soil Biology & Biochemistry 41:1199-1209.
Bordes P., Hablot E., Pollet E., Avérous L. (2009), ―Effect of clay organomodifiers on
degradation of polyhydroxyalkanoates. Polymer Degradation and Stability‖, 94(5): p. 789-
796.
Chen Haiyan PhD Thesis
- 158 -
Bourban C., Karamuk E., de Fondaumière M. Ruffieux K., Mayer J., Wintermantel E. (1997),
―Processing and characterization of a new biodegradable composite made of a PHB/V matrix
and regenerated cellulosic fibers‖ Journal of Polymers and the Environment, 5(3). p. 159-
166.
Brandrup J., Immergut E.H., Grulke E.A. (1999) Polymer Handbook. p 163., 4th Edition.
John Wiley and Sons, New York.
Brebu M., Vasile C. (2010), ―Thermal degradation of lignin – A Review‖, Cellulose
Chemistry & Technology, 44(9): p. 353-363.
Briassoulis, D. (2005). In Polym. Degrad. Stabil. Pp. 489-503, Vol. 88.
Bucci D.Z., Tavares L.B.B., Sell I. (2007), ―Biodegradation and physical evaluation of PHB
packaging‖ Polymer Testing, 26(7): p. 908-915.
Burkart M., James D., Liebman M., Herndl C. (2005), ―Impacts of Integrated Crop-
Livestock Systems on Nitrogen Dynamics and Soil Erosion in Western Iowa Watersheds‖,
Journal Of Geophysical Research, 110: p. 1-16.
Cabedo L., Plackett D., Giménez E., Lagarón J.M. (2009), ―Studying the degradation of
polyhydroxybutyrate-co-valerate during processing with clay-based nanofillers‖ Journal of
Applied Polymer Science, 112(6): p. 3669-3676.
Cai H., Vipul D., Richard A.G, Stephen P.M.C. (1996), ―Effects of physical aging,
crystallinity, and orientation on the enzymatic degradation of poly(lactic acid)‖ Journal of
Polymer Science Part B: Polymer Physics, 34(16): p. 2701-2708.
Calabia B.P., Tokiwa Y. (2006) ―A novel PHB depolymerase from a thermophilic
Streptomyces sp‖ Biotechnol Lett, 28: p. 383–388.
Castelli J.M., Urmeneta J., Lafuente R., Navarrete A., Guerriero R. (1995), ―Biodegradation
of poly(hydroxyalkanoates) in anaerobic sediments‖ International Biodeterioration &
Biodegradation , 35(1-3): p. 155-114.
Carlsson D. J., Garton A., Wiles. D. M. (1979), In: G. Scott (Ed), Developments in polymer
stabilisation 1. London: Applied Science Publishers; p. 220.
Carroll, S., Goonetilleke, A., Dawes, L. (2004), Framework for soil suitability evaluation for
sewage effluent renovation. Environmental Geology 46, : 195-208.
Ceccanti, B., Masciandaro, G., Garcia, C., Macci, C., Doni, S. (2006), Soil Bioremediation:
Combination of Earthworms and Compost for the Ecological Remediation of a Hydrocarbon
Polluted Soil. Water, Air, and Soil Pollution 177(1-4):383-397.
Chandra R., Rustgi R. (1998), « Biodegradable polymers‘‘. Progress in Polymer Science,
23(7): p. 1273-1335.
Chang J.H., An Y.U., Sur G.S.(2003), ―Poly(lactic acid) nanocomposites with various
organoclays. I. Thermomechanical properties, morphology and gas permeability‖ Journal of
Polymer Science : Part B: Polymer Physics, 41: p. 94-103.
Reference
- 159 -
Chanprateep S. (2010), ―Current trends in biodegradable polyhydroxyalkanoates‖ Journal of
Bioscience and Bioengineering, 110(6): p. 621–632.
Chen G.R., Ke L.J., and H.Y. Zhao H.Y. (2001), ―Separation and purification of the pepsin
from snake stomach by it's affinity with substrate‖ Journal of Chinese Institute of Food
Science and Technology, 1(1): p. 50-54.
Chen G., Wu Q., Chen J. (2001), ―Biosynthesis of polyhydroxyalkanoates‖ Tsinghua Science
and Technology, 6(3): p. 193-199.
Chen H., Li X. (2008), ―Effect of static magnetic field on synthesis of
polyhydroxyalkanoates from different short-chain fatty acids by activated sludge‖
Bioresource Technology, 99: p. 5538–5544.
Chen J.S., Poliks M.D., Ober C.K.; Zhang Y.M.; Wiesner U., Giannelis E. (2002), ―Study of
the interlayer expansion mechanism and thermal-mechanical properties of surface-initiated
epoxy nanocomposites‖ Polymer, 43 (18); p. 4895-4904.
Chiellini E., Solaro R (2003), ―Biodegrable polymers and plastics‖ In World Conference on
Biodegradable, Polymers Plastics, New York: Kluwer Academic/Plenum Publishers.
Chiellini E., Corti A., ―A simple method suitable to test the ultimate biodegradability of
environmentally degradable polymers‖, Macromol. Symp. 2003, 197: 381-395
Chiellini E., Corti A., D‘Antone S. (2007), ―Oxo-biodegradable full carbon backbone
polymers- biodegradation behaviour of thermally oxidized polyethylene in an aqueous
medium‖. Polymer Degradation & Stability, 92(7): p. 1378-1383.
Chiellini, E. (2007), ―Bioactive Polymeric Materials Laboratory for Biomedical &
Environmental Applications‖In International Conference on GREENOLYMPICS, Green
Materials/Plastics and Sustainable Industri GREENOLYMPICS, Green Materials/Plastics
and Sustainable Industrial Production‖. Beijing (China): ICS-UNIDO & The Science and
Technology Committee for the Games of th UNIDO & The Science and Technology
Committee for the Games of the XXIX Olympiad.
Chiellini E., Corti A., D‘Antone S., Baciu R., (2006) Polym. Degrad. Stab., 91, 2739-2747.
Chiellini, E., Corti, A., and G. Swift. (2003), Biodegradation of thermally-oxidized,
fragmented low-density polyethylenes. Polym. Degrad. Stab. 81: 341-351
Cho H.S., Moon H.S., Kim M., Nam K., Kim J.Y. (2011), ―Biodegradability and
biodegradation rate of poly(caprolactone)-starch blend and poly(butylene succinate)
biodegradable polymer under aerobic and anaerobic environment‖ Waste Management, 31: p.
475–480.
Choi M.W., Kim W.T., Park O.O., Chang K.Y., Lee W. J. (2003), ―Preparation and
characterization of poly(hydroxybutyrate-co-hydroxyvalerate)–organoclay nanocomposites‖
Journal of Applied Polymer Science, 90(2): p. 525-529.
Chouzouri G., Xanthos M. (2007), ―Degradation of aliphatic polyesters in the presence of
inorganic fillers‖ Journal of Plastic Films & Sheeting, 23: p. 19-36.
Chen Haiyan PhD Thesis
- 160 -
Chowdhury S.R. (2008), ―Some important aspects in designing high molecular weight
poly(L-lactic acid)-clay nanocomposites with desired properties‖ Polymer International, 57:
p. 1326-1332.
Chart, Kunstoff Plastics Business Data . (2004).
Ciesielski R.J., Collins R.J. (1994), ―Recycling and use of waste materials and by-products in
highway construction‖ NCHRP Synthesis of Highway Practice, 84 p.
Colak A., Guner S. (2004), ―Polyhydroxyalkanoates degrading hydrolase-like activities by
Pseudomonas sp. isolated from soil‖ International Biodeterioration & Biodegradation, 53: p.
103-109.
Combeaud C., Demay Y., Vergnes B. (2004), ―Experimental study of the volume defects in
polystyrene extrusion‖ Journal of Non-Newtonian Fluid Mechanics, 121(2-3): p. 175-185.
Corti A, Muniyasami S, Vitali M., Imam SH, Chiellini E. (2010), Oxidation and
biodegradation of polyethylene films containing pro-oxidantadditives: Synergistic effects of
sunlight exposure, thermalaging and fungal biodegradation. Polym. Degrad. Stab 95: 1106-
114
Consonni S., Giugliano M., Massarutto A., Ragazzi M., Saccani C. (2011), ―Material and
energy recovery in integrated waste management systems: Project overview and main
results‖, Waste Management, 31(9–10): p. 2057-2065.
Correa M.C.S., Rezende M.L., Rosa D.S., Agnelli J.A.M., P.A.P. Nascente P.A.P. (2008),
―Surface composition and morphology of poly(3-hydroxybutyrate) exposed to
biodegradation‖ Polymer Testing, 27: p. 447–452.
Costantino U., Gallipoli A., Nocchetti M., Camino G., Bellucci F., Frache A. (2005), ―New
nanocomposites constituted of polyethylene and organically modified ZnAl-hydrotalcites‖
Polymer Degradation and Stability, 90: p. 586-590.
Czvikovszky, T. (1996), ―Electron-beam processing of wood fiber reinforced polypropylene‖
Radiation Physics and Chemistry, 47(3): p. 425-430.
Davis G., Song J.H. (2006), ―Biodegradable packaging based on raw materials from crops
and their impact on waste management‖ Industrial Crops and Products, 23(2): p. 147-161.
Day M., Nawaby A.V., Liao X., (2006), ―A DSC study of the crystallization behaviour of
poly(lactic acid) and its nanocomposites‖, Journal of Thermal Analysis and Calorimetry
86(3): p. 623-629.
De Carvalho F.P., Quental A. C., Felisberti M.I. (2008), ―Polyhydroxybutyrate/acrylonitrile-
g-(ethylene-co-propylene-co-diene)-g-s tyrene blends: Their morphology and thermal and
mechanical behaviour‖ Journal of Applied Polymer Science,, 110(2): p. 880-889.
De Jong S.J., Ariasa E.R., Rijkersb D.T.S., van Nostruma C.F., Kettenes-van den Boschc J.J,
Hennink W.E. (2001), ―New insights into the hydrolytic degradation of poly(lactic acid):
participation of the alcohol terminus‖ Polymer, 42: p. 2995-2802.
Reference
- 161 -
De Lucas A., Rodr´ıguez L., Villase˜nor J., Fern´andez F.J. (2005), ―Biodegradation kinetics
of stored wastewater substrates by a mixed microbial culture‖ Biochemical Engineering
Journal, 26: p.191–197.
De Prisco N., Immirzi B., Malinconico M., Mormile P., Petti L., Gatta G. (2002),
―Preparation, physico-chemical characterization, and optical analysis of polyvinyl alcohol-
based films suitable for protected cultivation‖ Journal of Applied Polymer Science, 86(3): p.
622-632.
Decree, Legislative. (2006), Norme in materia ambientale. In Consolidated Environmental,
Vol. 88: the ordinary supplement to Official Gazette.
Dias J.M., Alvim-Ferraz M.C., Almeida M.F., Rivera-Utrilla J., Sánchez-Polo M. (2007),
―Waste materials for activated carbon preparation and its use in aqueous-phase treatment: A
review‖, Journal of Environmental Management, 85(4): p. 833-846.
Dikobe D.G., Luyt A.S. (2007), ―Effect of poly(ethylene-co-glycidyl methacrylate)
compatibilizer content on the morphology and physical properties of ethylene vinyl acetate–
wood fiber composites‖ Journal of Applied Polymer Science, 104(5): p. 3206-3213.
Dilara P.A., Briassoulis D. (2000), ―Degradation and stabilization of low-density
polyethylene films used as greenhouse covering materials‖ Journal of Agricultural
Engineering Research, 76(4): p. 309-321.
Dintcheva N.T., La Mantia F.P. (2007), ―Durability of a starch-based biodegradable polymer‖
Polymer Degradation and Stability, 92(4): p. 630-634.
Doi Y., Kanesawa Y., Kunioka M. (1990), ‖ Biodegradation of microbial copolyesters:
poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and poly( 3-hydroxybutyrate-co-4-
hydroxybutyrate)‖ Macromolecules, 23: p. 26-31.
Doi Y., Kanesawa Y., Tanahashi N., Kumagai Y. (1992), ―Biodegradtion of microbial
polyesters in the marine environment‖ Polym. Deg. Stab., 36: p. 173-177.
Doi Y., Kitamura S., Abe H. (1995), ―Microbial synthesis and characterization of poly(3-
hydroxybutyrate-co-3-hydroxyhexanoate)‖ Macromolecules, 28(14): p. 4822-4828.
Doi Y., Kasuya K., Abe H., Koyama N., Ishiwatari S., Takagi K., Yoshida Y. (1996),
―Evaluation of biodegradabilities of biosynthetic and chemosynthetic polyesters in river
water‖ Polym. Deg. Stab., 51: p. 281-286.
Doi Y., Abe H. (1997), ―Structural effects on biodegradation of aliphatic polyesters‖
Macromolecular Symphosia, 118: p. 725-731.
Doi, Y. (1990), Microbial Polyesters. New York: VCH Publishers.
Doni, S., Macci C, Peruzzi E, Arenella M, Ceccanti B, Masciandaro G. (2012), In situ
phytoremediation of a soil historically contaminated by metals, hydrocarbons and
polychlorobiphenyls. J Environ Monit 14(5):1383-90.
Drumright R.E., P.R. Gruber P.R., Henton D.E. (2000), ―Polylactic Acid Technology‖
Advanced Materials, 12(23): p. 1841-1846.
Chen Haiyan PhD Thesis
- 162 -
Durmus A., Kas A., Go Z., Macosko C.W (2008), ―Mechanical properties of linear low-
density polyethylene (LLDPE)/clay nanocomposites: estimation of aspect ratio and
interfacial strength by composite models‖ Journal of Macromolecular Science, Part B:
Physics, 47: p. 608–619.
Dzantor EK. (2007), Phytoremediation: the state of rhizosphere ―engineering‖ for
accelerated rhizodegradation of xenobiotic contaminants. J Chem Technol Biotechnol
82:228–232
El-Shafei H., N.H.A. EI-Nasser, A.L. Kansoh, A.M. Ali. (1998), Biodegradation of
disposable polyethylene by fungi Streptomyces species. Polym Degrad Stab 62:361-365.
Elvy S.B., G.R. Dennis G.R., Ng L.T. (1995), ―Effects of coupling agent on the physical
properties of wood-polymer composites‖ Journal of Materials Processing Technology, 48(1–
4): p. 365-371
EN 13432 ―Requirements for packaging recoverable through composting and
biodegradation‖
EN ISO 14593, ―Water quality-evaluation of ultimate aerobic biodegradability of organic
compounds in aqueous medium. Method by analysis of inorganic carbon in sealed vessels
(CO2 Headspace Test)‖, 1999, CEN European Committee for Standardization, Brussels,
www.cen.eu/cenorm/aboutus/index.asp.
Erceg M., Kovacic T., Klaric I. (2005), ―Dynamic thermogravimetric degradation of poly(3-
hydroxybutyrate)/aliphatic-aromatic copolyester blends‖ Polymer Degradation and Stability,
90(1): p. 86-94.
.
Erlandsson B., Karlsson S., Albertsson A.-C., (1997) Polym. Degrad. Stab., 55, 237.
Espert A., Vilaplana F., Karlsson S. (2004), ―Comparison of water absorption in natural
cellulosic fibres from wood and one-year crops in polypropylene composites and its
influence on their mechanical properties‖ Composites Part A: Applied Science and
Manufacturing, 35(11): p. 1267-1276.
Espì E., Salmeron A., Fontecha A., Garcia Y., Real A.I. (2006), ―Plastic films for agricultural
applications‖ Journal of Plastic Film & Sheeting, 22: p. 85-102.
Estelle R., Walls M., Guerin P., Langlois V. (2004), ―Hydrolytic degradation of blends of
polyhydroxyalkanoates and functionalized polyhydroxyalkanoates‖ Polymer Degradation
and Stability 85: p. 779-787.
Espí, E., A. Salmerón, A. Fontecha, Y. García and A. I. Real.(2006), PLastic Films for
Agricultural Applications. Journal of Plastic Film and Sheeting 22(2):85-102.
Eubeler J.P., Bernhard M., Knepper T.P. (2010), ―Environmental biodegradation of synthetic
polymers II. Biodegradation of different polymer groups‖ Trends in Analytical Chemistry,
29(1): p. 84-100.
European Bioplastics Bulletin, Issue 05/(2012)
Reference
- 163 -
Fedulova N., Chermenskaya G.I.E., Romanov V.I., Kretovich V.L. (1980), ―Enzymes of poly-
β-hydroxybutyrate metabolism in Rhizobium lupini bacteroids‖ Fiziol. Rast., 27(3): p. 544-
550.
Fan, K., D. Gonzales, and M. Sevoian. (1996), Hydrolytic and Enzymatic Degradation of
Poly(y-Glutamic Acid) Hydrogels and Their Application in Slow-Release Systems for
Proteins. Journal of Environmental Polymer Degradation 4(4):253-260.
Finkenstadt V.L., Liu C.K., Evangelista R., Liu L., Cermak S., M.H.E.; Willet J.L. (2007),
―Poly(Lactic acid) green composites using oilseed coproducts as fillers‖ Industrial Crops
and Products, 26: p. 36-43.
Finkenstadt V.L., Tisserat B. (2010), ―Poly(lactic acid) and Osage orange wood fiber
composites for agricultural mulch films‖ Industrial Crops and Products, 31: p. 316-320.
Frazer, Anne Cornish. (1995), O-Demethylation and Other Transformations of Aromatic
Compounds by Acetogenic Bacteria. In Acetogenesis. H. Drake, ed. Pp. 445-483. Chapman
& Hall Microbiology Series: Springer US.
Fukuzaki H., Yoshida M., Asano M., Kumakura M. (1989), ―Synthesis of copoly(D,L-lactic
acid) with relatively low-molecular weight and invitro degradation‖ European Polymer
Journal, 25(10): p. 1019-1026.
Fukushima K., C. Abbate Tabuani D., Gennari M., Camino G. (2009), ―Biodegradation of
poly(lactic acid) and its nanocomposites‖ Polymer Degradation and Stability, 94: p. 1646–
1655.
Gallet G., Lempiaèinen R., Karlsson S. (2001), ―Characterisation by solid phase
microextraction-gas chromatography-mass spectrometry of matrix changes of poly(l -lactide)
exposed to outdoor soil environment‖ Polymer Degradation and Stability,71: p. 147-151.
García de María C., Domínguez K.B.H. (2010), ―Simultaneous kinetic determination of 3-
hydroxybutyrate and 3-hydroxyvalerate in biopolymer degradation processes‖ Talanta, 80: p.
1436–1440.
Garcia C., M.T. Hernandez, F. Costa. (1990), Study on water extract of sewage sludge
compost,. Soil Sci. Plant Nutr. 37: 399–408.Gilan,
Gebauer B., Jendrossek D. (2006), ―Assay of poly (3-hydroxybutyrate) depolymerase
activity and product determination‖ Applied and Enviromental Microbiology, 72(9): p. 6094-
6100.
Glass G.B., and G. Swift. (1989), Agricultural and Synthetic Polymers, Biodegradation and
Utilization, ACS Symposium Series. American Chemical Society:9-64.
Goddard H.C. (1995), ―The benefits and costs of alternative solid waste management
policies‖ Resources, Conservation and Recycling, 13(3–4): p. 183-213.
Goldberg, D. (1995), A review of the biodegradability and utility of poly (caprolactone).
J Environ Polym Degrad 3:61-68.
Gopferich, A. (1997) Mechanisms of polymer degradation and elimination. Handbook
Chen Haiyan PhD Thesis
- 164 -
of Biodegradable Polymers:451-471.
Gopakumar T.G., Lee J.A., Kontopoulou M., Parent J.S. (2002), ―Influence of clay
exfoliation on the physical properties of montmorillonite/polyethylene composites‖ Polymer,
43: p. 5483–5491.
Graupner N. (2008), ―Application of lignin as natural adhesion promoter in cotton fibre-
reinforced poly(lactic acid) (PLA) composites‖ Journal of Material Science, 43: p. 5222-
5229.
Grima S., Bellon-Maurel V., Feuilloley P., Silvestre F. (2000), ―Aerobic biodegradation of
polymers in solid-state conditions: a review of environmental and physicochemical
parameter settings in simulations‖ J Polym Environ, 8: p. 183-195.
Gross R.A., Kalra B. (2002), ―Biodegradable Polymers for the Environment‖ Science,
297(5582):p. 803-807.
Gruber P., O‘Brien M. (2002) Polylactides “Natureworks® PLA‖. In: Doi, Y., Steinbüchel, A.
(eds) Biopolymers- polyesters III applications and commercial products. Vol 4. Weinheim:
Wiley-VCH p235-249.
Griffin, G. J. L. (1980), Synthetic polymers and the living environment. Pure Appl Chem
52:399-407.
Gross, Richard A., and Bhanu Kalra. (2002), Biodegradable Polymers for the Environment.
Science 297(5582):803-807.
Gu JD, Ford TE, Mitton DB, Mitchell R. (2000), Microbial degradation and deterioration of
polymeric materials. In The Uhlig Corrosion Handbook. I.R. W, ed. Pp. 439-460: New York:
Wiley.
Gu, J. D. (2003), Microbiological deterioration and degradation of synthetic polymeric
materials: Recent research advances. International Biodeterioration and Biodegradation
52(2):69-91.
Gugumus F., (1996), Polym. Degrad. Stab., 52, 131.
Gugumus, F. (2001), Re-examination of the thermal oxidation reactions of polymers 1. New
views of an old reaction. Polym. Degrad. Stab. 74: 327-339
Guillet, James E., Thomas W. Regulski, and T. Brian McAneney. (1974), Biodegradability of
photodegraded polymers. II. Tracer studies of biooxidation of Ecolyte PS polystyrene.
Environmental Science & Technology 8(10):923-925.
Guillet J. E., Norrish R.G.W., (1954), Nature, 173, 625.
Guillet J. E., (1973), Polymers with controlled life times. In: J. E. Guillet (Ed.) Polymers and
ecological problems, Plenum, New York.
Guo Q.P., Zheng H.F. (1999), ―Miscibility and crystallization of thermosetting polymer
blends of unsaturated polyester resin and poly(epsilon-caprolactone)‖ Polymer, 40(3): p.
637-646.
Reference
- 165 -
Hablot E., Bordes P., Pollet E., Averous L. (2008), ―Thermal and thermo-mechanical
degradation of poly(3-hydroxybutyrate)-based multiphase systems‖ Polymer Degradation
and Stability, 93: p. 413-421.
Hakkarainen M., Albertsson A.C., Karlsson S. (1996), ―Weight losses and molecular weight
changes correlated with the evolution of hydroxyacids in simulated in uivo degradation of
homo and copolymers of PLA and PGA‖ Polym Degrad Stab, 52: p. 283-291.
Hakkarainen M., Karisson S., Albertsson A.C. (2000a), ‖Rapid (bio)degradation of
polylactide by mixed culture of compost microorganisms—low molecular weight products
and matrix changes‖ Polymer, 41: p. 2331-2338.
Hakkarainen M., Karlsson S., Albertsson A.C. (2000b), ‖Influence of low molecular weight
lactic acid derivatives on degradability of polylactide‖ J Appl Polym Sci, 76: p. 228-239.
Harris A.M., Lee E.C. (2008), ―Improving mechanical performance of injection molded pla
by controlling crystallinity‖ Journal of Applied Polymer Science, 107: p. 2246–2255.
Hartley G. H., Guillet J. E., (1968) Macromolecules;1, 165
Harlan G., Kmiec C., (1995) Ethylene-carbon monoxide copolymers. In: G. Scott, D. Gilead
(Eds) Degradable polymers: principles and applications. Chapman & hall, London, chap 8.
Hadar I. Y. and A. Sivan, (2004), Colonization, biofilm formation and biodegradation of
polyethylene by a strain of Rhodococcus ruber. Applied Microbiology and Biotechnology
65(1):97-104.
Haines J. R., Alexander M., (1974), Appl. Environ. Microbiol., 28, 1084.
Haines J. R., Alexander M. (1974), Microbial degradation of high-molecular weight alkanes.
Appl. Environ. Microbiol., 28, 1084-1085
Hakkarainen M., A.-C- Albertsson. (2004), Environmental degradation of polyethylene. Adv.
Polym. Sci., 169, 177-199
Hamilton, J. D., Reinert, K. H., Hagan, J. V., Lord, W. V. (1995), Polymers as solid
waste in municipal landfills. Journal of the Air and Waste Management Association
45(4):247-251.
Hasan, F., Shah, A. A., Hameed, A., Ahmed, S. (2007), Synergistic effect of photo- and
chemical treatment on the rate of biodegradation of low density polyethylene by fusarium sp.
AF4. Journal of Applied Polymer Science 105(3):1466-1470.
Heat D. J., Lewis C. A., Rowland S. J., (1997), The use of high temperature gas
chromatography to study the biodegradation of high molecular weigh hydrocarbons. Org.
Geochem., 26, 769-785
Heidary, S., and B. Gordon Iii. (1994), Hydrolyzable poly(ethylene terephthalate). Journal of
Environmental Polymer Degradation 2(1):19-26.
Hermida E.B., Yashchuk O., Miyazaki S.S. (2009), ―Changes in the mechanical properties of
Chen Haiyan PhD Thesis
- 166 -
compression moulded samples of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) degraded
by Streptomyces omiyaensis SSM 5670‖ Polymer Degradation and Stability, 94: p. 267–271.
Heskins M., Guillet J. E., (1968), Macromolecules, 1, 97.
Hiltunen, K., Seppälä, J. V., Itävaara, M., Härkönen, M. (1997), The biodegradation of lactic
acid-based poly(ester-urethanes). Journal of Environmental Polymer Degradation 5(3):167-
173.
Hindryckx F., Dubois P., Jerome R., Teyssie P., Garcia Marti M. (1996) ―Polymerization-
filled composites prepared with highly active filler-supported Al/Ti/Mg catalysts. I. Synthesis
of homogeneous polyethylene-based composites‖
Hiraishi T., Hirahara Y., Doi Y., Maeda M., Taguchi S. (2006) ―Effects of mutations in the
substrate-binding domain of poly[(R)-3-hydroxybutyrate] (PHB) depolymerase from
Ralstonia pickettii T1 on PHB degradation" Applied and Environmental Microbiology,
72(11): p. 7331-7338.
Hisano T., Kasuya K., Tezuka Y., Ishi N., Kobayashi T., Shiraki M., Oroudjiev E., Hansma
H., Iwata T., Doi Y., Saito T., Miki K. (2006), ―The Crystal structure of polyhydroxybutyrate
depolymerase from Penicillium funiculosum provides insights into the recognition and
degradation of biopolyesters‖ Journal of Molecular Biology, 356(4): p. 993-1004.
Hong S.G., Lin Y.C., Lin C.H. (2008), ―Crystallization and degradation behaviors of treated
polyhydroxybutyrates‖ Reactive & Functional Polymers, 68: p. 1516–1523.
Huang S.J. (1995), ―Polymer waste management–biodegradation, Incineration, and
recycling‖ Journal of Macromolecular Science, Part A, 32(4): p. 593-597.
Ikura Y., Kudo T. (1999), ―Isolation of a microorganism capable of degrading poly-(L-
lactide)‖ J Gen Appl Microbiol, 45: p. 247-251.
Immirzi B., Santagata G., Vox G., Schettini E. (2009), ―Preparation, characterization and
field-testing of a biodegradable sodium alginate-based spray mulch‖ Biosystems Engineering,
102: p. 461-472.
Imam, S. H., Gould, J. M., Gordon, S. H., Kinney, M. P., Ramsey, A. M., Tosteson, T. R.
(1992) Fate of starch-containing plastic films exposed in aquatic habitats. Current
Microbiology 25(1):1-8.
Iovino R., Zullo R., rao M.A., Cassar L., Gianfreda L. (2008) ―Biodegradation of poly(lactic
acid)/starch/coir biocomposites under controlled composting conditions‖ Polymer
Degradation and Stability, 93(1): p. 147-157.
Ishida K., Asakawa N., Inoue Y. (2005), ―Structure, Properties and Biodegradation of Some
Bacterial Copoly(hydroxyalkanoate)s‖ Macromolecular Symposia, 224(1): p. 47-58.
ISO 472 Plastics-Vocabulary, ―General terms and terms relating to degradable plastics‖
ISO 17088-12 “Specifications for compostable plastics”
Reference
- 167 -
ISO 14855, ―Evaluation of the ultimate aerobic biodegradability and disintegration of
plastics under controlled composting conditions – Method by analysis of released carbon
dioxide‖
Itavaara M., Karjomaa S., Selin J.F. (2002),‖ Biodegradation of polylactide in aerobic and
anaerobic thermophilic conditions‖ Chemosphere, 46: p. 879-885.
Iwata, T.; Doi, Y. (1999), Crystal structure and biodegradation of aliphatic polyester crystals.
Macromol Chem Phys, 200: p. 2429-2442.
Iwata T., Shiromo M., Doi Y. (2002), ―Surface structures of poly[(R)-3-hydroxybutyrate] and
its copolymer single crystals before and after enzymatic degradation with an extracellular
PHB depolymerase‖ Macromolecular Chemistry and Physics, 203(10-11): p. 1309-1316.
Jakubowicz I., (2003), Polym. Degrad. Stab., 80, 39.
Jandas P., Mohanty S., Nayak S. (2012), ―Renewable resource-based biocomposites of
various surface treated banana fiber and poly lactic acid: Characterization and
biodegradability‖ Journal of Polymers and the Environment, 20(2): p. 583-595
Jang Y.J., Kim D., Bae H.W., Choi K.Y., Chae J.C., Zylstra G.J., Kim Y.M., Kim E. (2005),
―Isolation and characterization of Rhodococcus species strain able to grow on ortho- and
para-xylene‖ J. Microbiol., 43, p. 325-330.
Jarerat A., Tokiwa Y. (2003), ―Poly(L-lactide) degradation by Saccharothrix
waywayandensis‖ Biotech Lett, 25: p. 401-404.
Jayasekara N.Y., Heard G.M., Cox J.M., Fleet G.H. (1999), ―Association of micro-organisms
with the inner surfaces of bottles of non-carbonated mineral waters‖ Food Microbiology,
16(2): p. 115-128.
Jendrossek, Dieter, et al. (1993), Degradation of poly(3-hydroxybutyrate), PHB, by bacteria
and purification of a novel PHB depolymerase fromComamonas sp. Journal of
Environmental Polymer Degradation 1(1):53-63.
Jendrossek D., Knoke I., Habibian R.B., Steinbüchel A., Schlegel H.G. (1993), ―Degradation
of poly(3-hydroxybutyrate), PHB, by bacteria and purification of a novel PHB depolymerase
from Comamonas sp‖ Journal of environmental polymer degradation, 1: p. 53-63.
Jendrossek D., Schirmer A., Schlegel H.G. (1996), ―Biodegradation of polyhydroxyalkanoic
acids‖ Appl. Microbiol. Biotechnol., 46: p. 451-463.
Jendrossek, D. (2001), ―Microbial degradation of polyesters‖ Adv. Biochem. Eng. Biotechnol,
71: p. 293-326.
Jen-hou L., Schwartz A. (1961), Zum verhalten von bakterien-gemischen gegenüber
polyäthylen verschiedenen mittleren molekularwichts. Kunstoffe, 51: 317-320
Johnson, L. R., Farb, C., Morrison, J. H., McEwen, B. S., LeDoux, J. E. (2005), Localization
of glucocorticoid receptors at postsynaptic membranes in the lateral amygdala. Neuroscience
136(1):289-299.
Chen Haiyan PhD Thesis
- 168 -
Jung Y.M., and Y.-H. Lee Y.H. (2000), ―Utilization of oxidative pressure for enhanced
production of poly-β-hydroxybutyrate and poly(3-hydroxybutyrate-3-hydroxyvalerate) in
Ralstonia eutropha‖ Journal of Bioscience and Bioengineering, 90(3): p. 266-270.
Jun, Hae Sang, Kim, Bong Oh, Kim, Yeon Chul, Chang, Ho Nam, Woo, Seong Ihl. (1994),
Synthesis of copolyesters containing poly(ethylene terephthalate) and poly(ε-caprolactone)
units and their susceptibility to Pseudomonas sp. lipase. Journal of Environmental Polymer
Degradation 2(1):9-18.
Kale G., Auras R., Singh S.P. (2006), ―Degradation of commercial biodegradable packages
under real composting and ambient exposure conditions‖ Journal of Polymer and the
Environment, 14: p. 317-334.
Khabbaz F., Albertsson A.-C., (2000) Biomacromolecules, 1, 665.
Khanna S., Srivastava A.K. (2005), ‖Recent advances in microbial polyhydroxyalkanoates‖
Process Biochemistry, 40: p. 607–619.
Kallistova A., Kevbrina M., Bonartseva G., Nozhevnikova A., Proceedings of the 7th
FAO/SPEN-Workshop ‖Anaerobic digestion for suistainability in waste (water) treatment
and re-use‖ Moscow, Russia, 19-11 May 2002, pp.395-402.
Karnani R., Krishnan M., Narayan R. (1997), ―Biofiber-reinforced polypropylene
composites‖ Polymer Engineering & Science, 37(2): p. 476-483.
Karjomaa S., Suortti T., LempiaÈinen R., Selin J.F., ItaÈvaara M. (1998), ‖Microbial
degradation of poly-(L-lactic acid) oligomers‖ Polym Degrad Stab, 59: p. 333-3
Kasuga T., Maeda H., Kato K., Nogami M., Hata K., Ueda M. (2003), ―Preparation of
poly(lactic acid) composites containing calcium carbonate (vaterite)‖ Biomaterials, 24: p.
3247-3253.
Kasuya K., Takagi K., Ishiwatari S., Yoshida Y., Doi Y. (1998), ―Biodegradabilities of
various aliphatic polyesters in natural waters‖ Polym. Deg. Stab., 59: p. 327-332.
Kasuya K.I., Ishii N., Inoue Y., Yazawa K., Tagaya T., Yotsumoto T., Kazahaya J.I., Nagai D.
(2009), ―Characterization of a mesophilic aliphatic–aromatic copolyester-degrading fungus‖
Polymer Degradation and Stability, 94(8): p. 1190-1196.
Kawai F., Nakadai K., Nishioka E., Nakajima H., Ohara H., Masaki K., Iefuji H. (2011),
―Different enantioselectivity of two types of poly(lactic acid) de polymerases toward
poly( L-lactic acid) and poly(D -lactic acid)‖ Polymer Degradation and Stability, 96: p.
1342-1348.
Kawai F., Watanabe M., Shibata M., Yokoyama S., Sudate Y. (2002), Experimental analysis
and numerical simulation for biodegradability of polyethylene. Polym. Degrad. Stab., 76:
129-135
Kawai F., Watanabe M., Shibata M., Yokoyama S., Sudate Y., Hayashi S. (2004),
Comparative study on biodegradability of polyethylene wax by bacteria and fungi. Polym.
Degrad. Stab., 86: 105-114
Reference
- 169 -
Kawai F. (1999), Sphingomonads involved in the biodegradation of xenobiotic polymers. J.
Ind. Microbiol. Biotechnol., 23: 400-407
Kawai, F., Shibata, M., Yokoyama, S., Maeda, S., Tada, K., and S. Hayashi. (1999)
Biodegradability of Scott-Gilead photodegradable polyethylene and polyethylene wax by
microorganisms. Macromol. Symp. 144: 73-84
Kamal, M. R., and and B. Huang. (1992), Natural and artificial weathering of polymers. In
Handbook of Polymer Degradation. S.H. (Hamid, M.B. Ami, and A. G. Maadhan., eds).
Kasuya, Junko, Kaas, Garrett, Kitamoto, Toshihiro. (2009a), Effects of lithium chloride on
the gene expression profiles in Drosophila heads. Neuroscience Research 64(4):413-420.
Keller A. (2003), ―Compounding and mechanical properties of biodegradable hemp fibre
composites” Composites Science and Technology, 63(9): p. 1307-1316.
Khanna, Shilpi, and Ashok K. Srivastava. (2005), Recent advances in microbial
polyhydroxyalkanoates. Process Biochemistry 40(2):607-619.
Kijchavengkul T., Auras R., Rubino M., Ngouajio M., R. Thomas Fernandez R.T. (2008),
―Assessment of aliphatic–aromatic copolyester biodegradable mulch films. Part II:
Laboratory simulated conditions‖. Chemosphere, 71(9): p. 1607-1616.
Kim M.N., Lee A.R., Yoon J.S., Chin I.J. (2000), ―Biodegradation of poly(3-
hydroxybutyrate), Sky-Green® and Mater-Bi® by fungi isolated from soils‖ European
Polymer Journal, 36(8): p. 1677-1685.
Kim H.J., Kim D.Y., Nam J.S., Bae K.S., Rhee Y.H. (2003), ―Characterization of an
extracellular medium-chain-length poly(3-hydroxyalkanoate) depolymerase from
Streptomyces sp. KJ-72‖ Antonie van Leeuwenhoek, 83: p. 183-189.
Kim D.Y., Rhee Y.H. (2003), ―Biodegradation of microbial and synthetic polyesters by
fungi‖ Appl Microbiol Biotechnol, 61: p. 300–308.
Kim H., Biswas J., Choe S. (2006), ―Effects of stearic acid coating on zeolite in LDPE,
LLDPE, and HDPE composites‖ Polymer; 47: p. 3981–3992
Kim D.Y., Kim H.W., Chung M.G., Rhee Y.H. (2007), ―Biosynthesis, modification, and
biodegradation of bacterial medium-chain-length polyhydroxyalkanoates‖ The Journal of
Microbiology, 45(2): p. 87-97.
Kijchavengkul, Thitisilp, Auras, Rafael, Rubino, Maria, Ngouajio, Mathieu, Fernandez, R.
Thomas. (2008), Assessment of aliphatic–aromatic copolyester biodegradable mulch films.
Part I: Field study. Chemosphere 71(5):942-953.
Kitamoto, H. K., Shinozaki, Y., Cao, X. H., Morita, T., Konishi, M., Tago, K., Kajiwara, H.,
Koitabashi, M., Yoshida, S., Watanabe, T., Sameshima-Yamashita, Y., Nakajima-Kambe, T.,
Tsushima, S. (2011), Phyllosphere yeasts rapidly break down biodegradable plastics.
AMB Express 1(44):2191-0855.
Kleeberg I, Hetz C, Kroppenstedt RM, Muller R-J, Deckwer W-D. (1998), ―Biodegradation
of aliphatic–aromatic copolyesters by Thermomonospora fusca and other thermophilic
Chen Haiyan PhD Thesis
- 170 -
compost isolates‖ Appl Environ Microbiol, 64(5): p. 1731–1735.
Klingbeil B., Kroppenstedt R.M., Jendrossek D. (1996), ‗‘Taxonomic identification of
Streptomyces exfoliatus K10 and characterization of ist poly(3-hydroxybutyrate)
depolymerase gene― FEMS Microbiol. Lett., 142: p. 215-221.
Koutny M., Lemaire J., Delort A.-M., (2006), Chemosphere, 64, 1243.
Kulkarni S.O., Kanekar P.P., Jog J.P., Patil P.A., Nilegaonkar S.S., Sarnaik S.S., Kshirsagar
P.R. (2011), ―Characterisation of copolymer, poly (hydroxybutyrate-co-hydroxyvalerate)
(PHB-co-PHV) produced by Halomonas campisalis (MCM B-1027), its biodegradability and
potential application‖ Bioresource Technology, 102(11): p. 6625–6628.
Kuiper I., Ellen L. Lagendijk, Guido V. Bloemberg, and Ben J. J. Lugtenberg. (2004),
Rhizoremediation: A Beneficial Plant-Microbe Interaction. The American Phytopathological
Society 17(1):6-15
Kumar R., Yakubu M.K., Anandjiwala R.D. (2010), ―Biodegradation of flax fiber reinforced
poly lactic acid‖ Express Polymer Letters, 4(7): p. 423–430.
Kunioka M., Ninomiya F., Funabashi M. (2006), ―Biodegradation of poly(lactic acid)
powders proposed as the reference test materials for the international standard of
biodegradation evaluation methods‖ Polymer Degradation and Stability, 91: p. 1919 – 1928.
Kwpp LR, and and Jewell WJ. (1992), Biodegradability of modified plastic films in
controlled biological environments. Environ Technol 26:193-198.
Kyrikou I., and Demetres Briassoulis D. (2007), ―Biodegradation of Agricultural Plastic
Films: A Critical Review‖ Journal of Polymers and the Environment, 15(3): p. 227-227.
Lamont W.J.J.(1999), ―Vegetable Production Using Plasticulture, in Food & Fertilizer
Technology Center‖, University Park, Pennsylvania 16802-4200 USA: Department of
Horticulture, 114 Tyson Building,The Pennsylvania State University. p. 9.
Lamont, W. J. (1991), The use of plastic mulches for vegetable production, Food and
Fertilizer Technology Center, Kansas State University.
Latorre M.J., Peña R., Pita C., Botana A., García S., Herrero C. (1999), ―Chemometric
classification of honeys according to their type. II. Metal content data‖ Food Chemistry, 66:
p. 263-268.
Laudicina, Vito Armando, Dennis, PaulG, Palazzolo, Eristanna, Badalucco, Luigi. (2012),
Key Biochemical Attributes to Assess Soil Ecosystem Sustainability. In Environmental
Protection Strategies for Sustainable Development. A. Malik and E. Grohmann, eds. Pp. 193-
227. Strategies for Sustainability: Springer Netherlands.
Le Digabel F., Boquillon N., Dole P., Monties B., Averous L. (2004), ―Properties of
thermoplastic composites based on wheatstraw lignocellulosic fillers‖ J Appl Polym Sci, 93:
p. 428-436.
Lee, B., Pometto Iii, A. L., Fratzke, A., Bailey Jr, T. B. (1991), Biodegradation of degradable
plastic polyethylene by Phanerochaete and Streptomyces species. Applied and Environmental
Reference
- 171 -
Microbiology 57(3):678-685.
Lee, S.Y. (1996), ―Bacterial polyhydroxyalkanoates‖ Biotechnology and Bioengineering,
49(1): p. 1-14.
Lee S.Y., Choi J. (1999), ―Production and degradation of polyhydroxyalkanoates in waste
environment‖ Waste Management, 19: p. 133-139.
Lepidi A.A., Nuti M.P., Bertoldi M. (1972), ―Metabolismo del poly-β-idrossibutirrato nel
terreno e nella rizosfera‖ Agricoltura Italiana (Pisa), 72: p. 166-184.
Li Z., Lin H., Ishii N., Chen G.Q., Inoue Y. (2007), ―Study of enzymatic degradation of
microbial copolyesters consisting of 3-hydroxybutyrate and medium-chain-length 3-
hydroxyalkanoates‖ Polymer Degradation and Stability, 92(9): p. 1708-1714.
Li J., He Y., Inoue Y. (2003), ―Thermal and mechanical properties of biodegradable blends of
poly(L-lactic acid) and lignin” Polymer International, 52(6): p. 949-955.
Li Y., Venkateshan K., Sun X.S. (2010), ―Mechanical and thermal properties, morphology
and relaxation characteristics of poly (lactic acid) and soy flour/wood flour blends‖ Polymer
International, 59: p. 1099-1109.
Liao B., Huang Y., Cong G. (1997), ―Influence of modified wood fibers on the mechanical
properties of wood fiber-reinforced polyethylene‖ Journal of Applied Polymer Science, 66(8):
p. 1561-1568.
Lim H., Seunghee Han Y.L., Yoo Y., Kim K.J. (1999), ―Investigation of polystyrene,
polyisoprene, and poly(2-vinylpyridine) using matrix-assisted laser desorption/ionization
time-of-flight mass spectrometry‖. Bull. Korean Chem. Soc., 20(7): p. 853-856.
Lim S.T., Hyun Y.H., Lee C.H., Choi H.J. (2003), ―Preparation and characterization of
microbial biodegradable poly(3-hydroxybutyrate)/organoclay nanocomposite‖ Journal of
Materials Science Letters, 22,(4): p. 299-302.
Lim J.H. (2006), ―Expression, purification and characterization of Rhodococcus equi P2 mcl-
PHA depolymerase in Escherichia coli‖ MS Thesis.
Lim J.S., Noda I., Im S.S. (2007), ―Effect of hydrogen bonding on the crystallization
behavior of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate)/silica hybrid composites‖
Polymer, 48(9): p. 2745-2754.
Lucas N., Bienaime C., Belloy C., Queneudec M., Silvestre F., Nava-Saucedo J.E. (2008),
―Polymer biodegradation: mechanisms and estimation techniques‖ Chemosphere, 73: p. 429–
442.
Lutz Ienczak J. & Falcao de Aragao G.M., (2011), ―Biotechnologically Produced
Biodegradable Polyesters‖ Inside- Handbook of Biodegradable Polymers: Synthesis,
Characterization and Applications, First Edition. Edited by Andreas Lendlein, Adam Sisson;
Wiley- VCH Verlang GmbH & Co. KGaA.
Luzier W.D. (1992), ―Materials derived from biomass/biodegradable materials‖ Proc Natl
Acad sci USA, 89: p. 839-842.
Chen Haiyan PhD Thesis
- 172 -
Maiti P., Batt C., Giannelis E. (2003), ―Renewable plastics: synthesis and properties of PHB
nanocomposites‖ Polym Mat Sci Eng, 88.
Malinconico M., Immirzi B., Massenti M., La Mantia F.P., Mormile P., Petti L. (2002),
―Blends of polyvinylalcohol and functionalised polycaprolactone. A study on the melt
extrusion and post-cure of films suitable for protected cultivation‖ Journal of Materials
Science, 2002. 37(23): p. 4973-4978.
Malunka M.E., Luyt A.S., Krump H. (2006), ―Preparation and characterization of EVA–sisal
fiber composites‖ Journal of Applied Polymer Science, 100(2): p. 1607-1617.
Masciandaro G., Ceccanti B., Ronchi V., Bauer C. (2000), ―Kinetic parameters of
dehydrogenase in the assessment of the response of soil to treatments by vermicompost and
inorganic fertilisers‖ Biology and Fertility of Soils, 32: p. 479-483.
Masciandaro, G., Ceccanti, B., Benedicto, S., Lee, H. C., Cook, H. F. (2004) Enzyme activity
and C and N pools in soil following application of mulches. Canadian Journal of Soil
Science 84(1):19-30.
Matavulj M., Sad N., Molitoris H.P. (2000), ―Biodegradation of polyhydroxyalkanoate-based
plastic (BIOPOL) under different environmental conditions‖ Bresinsky-Festschrift, 61: p.
735-749.
Matsusaki H., Abe H., Doi Y. (2000), ―Biosynthesis and properties of poly(3-
hydroxybutyrate-co-3-hydroxyalkanoates) by recombinant strains of Pseudomonas sp. 61-3‖
Biomacromolecules, 1(1): p. 17-22.
Mecking S. (2004), ―Nature or petrochemistry?—Biologically degradable materials‖.
Angewandte Chemie International Edition, 43(9): p. 1078-1085.
Mergaert J., Anderson C., Wouters A., Swings J., Kersters K. (1992), FEMS Microbiol. Rev.,
103: 317.
Mergaert J., Webb A., Anderson C., Wouters A., Swings J. (1993), ‗‘Microbial degradation of
poly83-hydroxybutyrate-co-3-hydroxyvalerate) in soils‖ Appl. Environ. Microbiol., 59: p.
3233-3238.
Mergaert C.M., Liao Q., Criddle C.S., Curtis W.F. (2011), ―Anaerobic biodegradation of the
microbial copolymer poly(3-hydroxybutyrateco-3-hydroxyhexanoate): effects of comonomer
content, processing history, and semi-crystalline morphology‖ Polymer, 52: p. 547-556.
Metabolix (2007a) Bioplastics: Markets and Application. Metabolix Website.,
http://www.metabolix.com/natures%20plastic/markets.html
Mohamed A., Gordon S.H., Biresaw G. (2007a), ―Poly(lactic acid)/polystyrene bioblends
characterized by thermogravimetric analysis, differential scanning calorimetry, and
photoacoustic infrared spectroscopy‖ Journal of Applied Polymer Science, 106(3): p. 1689-
1696.
Reference
- 173 -
Mohamed A., Gordon S.H., Biresaw G. (2007b), ―Polycaprolactone/polystyrene bioblends
characterized by thermogravimetry, modulated differential scanning calorimetry and infrared
photoacoustic spectroscopy‖ Polymer Degradation and Stability, 92(7): p. 9.
Mohanty A.K., Misra M., Hinrichsen G. (2000), ―Biofibres, biodegradable polymers and
biocomposites: An overview‖ Macromolecular Materials and Engineering, 276-277: p. 1-24.
Mokeeva V., Chekunova L., Myshkina V.L., Nikolaeva D.A., Gerasin V., Bonartseva G.A.
(2002), Mikologia and Fitopatologia, 36(5): 59.
Mousavioun P., Doherty W.O.S., George G. (2010), ―Thermal stability and miscibility of
poly(hydroxybutyrate) and soda lignin blends‖ Industrial Crops and Products, 32(3): p. 656-
661.
Mousavioun P., Graeme A.G., Doherty W.O.S. (2012), ―Environmental degradation of
lignin/poly(hydroxybutyrate) blends‖. Polymer Degradation & Stability, 97: p. 1114-1122.
Muller R.J., Kleeberg I., Deckwer W.D. (2001), ― Biodegradation of polyesters containing
aromatic
constituents‖ Journal of Biotechnology, 86: p.87-95.
Muniyasamy S. (2011), ―Oxo-Biodegradation of full carbon backbone polymers under
different environmental conditions‖ In Chemistry and Chemical Industrial Science,
University Of Pisa: Galileo Galilei Schoo. p. 285.
Murphy J., Riley J.P. (1962), ―A modified single solution method for the determination of
phosphate in natural waters‖, Anal. Chim. Acta, 27: p. 31–36.
M. Weiland, A. Daro, C. David, (1995), Polym. Degrad. Stab., 48, 275
Nakamura K., Tomita T., Abe N., Kamio Y. (2001), ―Purification and characterization of an
extracellular poly(l-lactic acid) depolymerase from a soil isolate, amycolatopsis sp. strain
K104-1‖ Appl Environ. Microbiol, 67: p. 345-353.
Nakayama, A.(1996), Synthesis and Biodégradation of Poly(y-Butyrolactone-co-L-Lactide).
Journal of Environmental Polymer Degradation 4(3):205-211.
Nam J.S., Kim H.C., Kim D.Y., Rhee Y.H. (2002), ―Distribution and diversity of
microbiological communities relating to biodegradation of medium-chain-length poly(3-
hydroxyalkanoates) in soils‖ Proceedings of 9th
International Symphosium on the Genetics of
Industrial Microorganisms (Korea), pp.192.
Nampoothiri, M.K., N.R. Nair N.R., John R.P. (2010), ―An overview of the recent
developments in polylactide (PLA) research‖ Bioresource Technology, 101(22): p. 8493-
8501.
Nannipieri P., Grego S., Ceccanti B. (1990), ―Ecological significance of the biological activity
in soil‖ In: J.M. Bollag and G. Stotzky (eds). Soil biochemistry, vol. 6, pp. 293-355.
Nannipieri, P., and J.-M. Bollag. (1991), Use of Enzymes to Detoxify Pesticide-
Contaminated Soils and Waters. J. Environ. Qual. 20(3):510-517.
Chen Haiyan PhD Thesis
- 174 -
Nannipieri P., E. Kandeler, P. Ruggiero. (2002), Enzyme activities and microbiological and
biochemical processes in soil. In Enzymes in the Environment: Activity, Ecology and
Applications. R.P.D. R.G. Burns, ed. New York, NY: Marcel Dekker, Inc.
Narayan, R. (1993), Biodegradation of polymeric materials (anthropogenic macromolecules)
during composting. In Science and Engineering of Composting: Design, Environmental,
Microbiological and Utilization Aspects. H.M.K. H.A.J. Hoitink, ed. Pp. 339-362.
Washington, OH Renaissance Publishers.
Newman, L.A., Reynolds, C.M. (2004), Phytodegradation of organic compounds. Current
Opinion in Biotechnology 15:225-230.
Nojiri M., and T. Saito T. (1997), ―Structure and function of poly(3-hydroxybutyrate)
depolymerase from Alcaligenes faecalis T1‖ Journal of Bacteriology, 179(22): p. 6965-6970.
Oda Y, Asari H, Urakami T, Tonomura K. (1995), ―Microbial degradation of poly(3-
hydroxybutyrate) and polycaprolactone by filamentous fungi‖ J Ferment Bioeng, 80(3): p.
265–269.
Ogata N., Jimenez G., Kawai H., Ogihara T. (1997), ―Structure and thermal/mechanical
properties of \poly(L-lactide)-clay blend‖ Journal of Polymer Science: Part B: Polymer
Physics, 35: p. 389-396.
Ohkita T., Lee S.H. (2006), ―Thermal degradation and biodegradability of poly (lactic
acid)/corn starch biocomposites‖ Journal of Applied Polymer Science, 100(4): p. 3009–3017.
Ohura T., Aoyagi Y., Takagi K., Yoshida Y., Kasuya K., Doi Y. (1999), ―Biodegradation of
poly(hydroxyalkanoic acid)-degrading microorganisms under aquatic environment‖ Polym.
Deg. Stab., 63: p. 23-29.
Ohtake, Y., Kobayashi, T., Asabe, H., and N. Murakami. (1998), Studies on biodegradation
of LDPE-observation of LDPE films scattered in agricultural fields or in garden soil. Polym.
Degrad. Stab. 60: 79-84.
Ohtake, Y., Kobayashi, T., Asabe, H., and N. Murakami. (1998) Studies on biodegradation of
LDPE-observation of LDPE films scattered in agricultural fields or in garden soil. Polym.
Degrad. Stab. 60: 79-84.
Ohtaki, A., Sato, N., Nakasaki, K. (1998), Biodegradation of poly-ε-caprolactone under
controlled composting conditions. Polymer Degradation and Stability 61(3):499-505.
Olsen, M., and A. and Schoeberl Douglass, M. (2003), A comparison of Northern and
Southern Hemisphere cross-tropopause ozone flux. Geophysical Research Letters
30(7):0094-8276
Oksman K., Skrifvars M., Selin J.F. (2003), ―Natural fibres as reinforcement in polylactic
acid (PLA) composites‖ Composites Science and Technology, 63: p. 1317-1324.
Orhan Y, Buyukgungor H. (2000), ―Enhancement of biodegradability of disposable
polyethylene in controlled biological soil‖ International Biodeterioration and
Biodegradation, 45(1): p. 49-55.
Reference
- 175 -
OTA (1993) Biopolymers: Making materials nature's way - background paper. Report No.
OTA-BP-E-102, U.S. Congress, Office of Technology Assessment, Washington D.C., US
Government Printing Office
Othman N., Ismail H., Mariatti M. (2006), ―Effect of compatibilisers on mechanical and
thermal properties of bentonite filled polypropylene composites‖ Polymer Degradation and
Stability, 91: p. 1761-1774.
Otake, Yoshito, Kobayashi, Tomoko, Asabe, Hitoshi, Murakami, Nobunao, Ono, Katsumichi.
(1995), Biodegradation of low-density polyethylene, polystyrene, polyvinyl chloride, and
urea formaldehyde resin buried under soil for over 32 years. Journal of Applied Polymer
Science 56(13):1789-1796.
Paabo M., Levin B.C. (1987), ―A literature review of the chemical nature and toxicity of the
decomposition products of polyethylenes‖ Fire and Materials, 11(2): p. 55-70.
Pandey J.K., Raghunatha K., Reddy A., Kumar P., Singh R.P. (2005), ―An overview on the
degradability of polymer nanocomposites‖, Polymer Degradation and Stability, 88: p. 234-
250.
Patnaik P.R. (2006), ―Dispersion optimization to enhance PHB production in fed-batch
cultures of Ralstonia eutropha‖ Bioresource Technology, 97(16): p. 1994-2001.
Paul M. A., Alexandre M., Degee P., Henrist C., Rulmont A., Dubois P. (2003), ―New
nanocomposites materials based on plasticized poly(L-lactide) and organo-modified mont
morillonites: thermal and morphological study‖ Polymer, 44: p. 443-450.
Perego G., Cella G.D., Bastioli C. (1996), ―Effect of molecular weight and cristallinity on
poly(lactic acid) mechanical properties‖ Journal of Applied Polymer Science, 59: p. 37-46.
Petersen, K., Nielsen P.V., Bertelen G., Lawther M., Olsen M.B., Nilsson N.H., Mortensen G.
(1999), ―Potential of biobased materials for food packaging‖ Trends in Food Science &
Technology, 10(2): p. 52-68.
Petinakis E., Liu X., Yu L., Way C., Sangwan P., Dean K., Bateman S., Edward G. (2010)
―Biodegradation and thermal decomposition of poly(lactic acid)-based materials reinforced
by hydrophilic fillers‖ Polymer Degradation and Stability, 95(9): p. 1704-1707.
Philip S., Keshavarz T., Roy I. (2007), ―Polyhydroxyalkanoates: biodegradable polymers
with a range of applications‖ Journal of Chemical Technology & Biotechnology, 82(3): p.
233-247.
Phithakrotchanakoon C., Rudeekit Y., Tanapongpipat S., Leejakpai T., Aiba S., Noda I.,
Champreda V. (20099, ―Microbial degradation and physico-chemical alteration of
polyhydroxyalkanoates by a thermophilic Streptomyces sp.‖ Biologia, 64(2): p. 246-251.
Pilla, S., Gong S., O‘Neill E., Rowell R.M., Krzysik A.M. (2010), ―Polylactide-pine wood
flour composites” Polymer Engineering and Science, 48(3): p. 578-587.
Pilla S., Kramschuster A., Yang L., Lee J., Gong S., Turng L.S. (2009), ―Microcellular
injection-molding of polylactide with chain-extender‖ Materials Science & Engineering C,
29: p. 1258-1265.
Chen Haiyan PhD Thesis
- 176 -
Pillin I., Montrelay N., Grohens Y. (2006), ―Thermo-mechanical characterization of
plasticized PLA: Is the miscibility the only significant factor?‖ Polymer, 47: p. 4676-4682.
Picci G., Nannipieri P. (coord.) (2002), Metodi di analisi microbiologica del suolo, Milano,
FrancoAngeli (editor)
Plastics- The Facts 2012- An analysis of European plastics production, demand and waste
data for 2011, www.plasticeurope.com
Pluta M., Galeski A., Alexandre M., Paul M.A., Dubois P. (2002),
―Polylactide/Montmorillonite nanocomposites and microcomposites prepared by melt
blending: structure and some physical properties‖ Journal of Applied Polymer Science, 86: p.
1497-1506.
Potts, J. E., Clendinning, R. A., and W. B. Ackart. (1972), An investigation of the
biodegradability of packaging plastics. EPA-R2-72-046.Washington DC: US Environmental
Protection Agency.
Potts J.E., Clendinning R.A., Ackart W. B., (1972) Niegishi W. D. Polym. Prep., 13: 629
Pranamuda H., Tokiwa Y., Tanaka H. (1997), ―Polylactide degradation by an Amycolatopsis
sp.‖ Applied and Environmental Microbiology, 63(4): p. 1637-1640.
Pranamuda H., Tokiwa Y. (1999), ―Degradation of poly (l-lactide) by strains belonging to
genus amycolatopsis.‖ Biotechnol Lett, 21: p. 901–905
Pranamuda H., Tsuchii A., Tokiwa Y. (2001), ―Poly( L-lactide)-degrading enzyme produced
by Amycolatopsis sp.‖ Macromol Biosci, 1: p. 25-29.
Quinteros R., Goodwin S., Lenz R.W., Park W.H. (1999), ―Extracellular degradation of
medium chain length poly (b-hydroxyalkanoates) by Comamonas sp.‖ International Journal
of Biological Macromolecules, 25: p. 135–143.
Rai R., Keshavarz T., Roether j. A., Boccaccini A.R., Roy I. (2011), ―Medium chain length
polyhydroxyalkanoates, promising new biomedical materials for the future‖ Materials
Science and Engineering R, 72: p. 29–47.
Ray S.S., Bousmina M. (1995), ―Biodegradable polymers and their layered silicate nano
composites: In greening the 21st century materials world‖ Progress in Materials Science,
50(8): p. 962-1079.
Ray S.S., Okamoto M. (2003), ―Polymer/layered silicate nanocomposites: a review from
preparation to processing‖ Progress in Polymer Science, 28(11): p. 1539-1641.
Reddy C.S.K., Rashmi R.G. Kalia V.C. (2003), ―Polyhydroxyalkanoates: an overview‖
Bioresource Technology, 87(2): p. 137-146.
Reeve, M. S.; McCarthy, S. P.; Downey, M. J.; Gross, R. A., Polylactide sterochemistry-
effect on enzymatic degradability. Macromolecules 1994, 27, (3), 825-831.
Reis R.L., Cunha A.M., Allan P.S., Bevis M.J. (1996), ―Mechanical behavior of injection-
Reference
- 177 -
molded starch-based polymers‖ Polymers for Advanced Technologies, 7(10): p. 784-790.
Renarda E., Walls M., Guerina P., Langlois V. (2004), ―Hydrolytic degradation of blends of
polyhydroxyalkanoates and functionalized polyhydroxyalkanoates‖ Polymer Degradation
and Stability, 85: p. 779-787.
Reti C., Casetta M., Duquesne S., Bourbigot S., Delobel R. (2008), ―Flammability properties
of intumescent PLA including starch and lignin‖ Polymers for Advanced Technologies, 19: p.
628-635.
Rezwan, K., Chen Q.Z., Blaker J.J., Boccaccini A.R. (2006), ―Biodegradable and bioactive
porous polymer/inorganic composite scaffolds for bone tissue engineering‖ Biomaterials,
27(18): p. 3413-3431.
Rosa D.d.S., Rodrigues T.C., ―Fassina Guedes C.d.G., Calil M.R. (2003), Effect of thermal
aging on the biodegradation of PCL, PHB-V, and their blends with starch in soil compost‖
Journal of Applied Polymer Science, 89(13): p. 3539-3546.
Rudnik E., Briassoulis D. (2011), ―Degradation behaviour of poly(lactic acid) films and
fibres in soil under Mediterranean field conditions and laboratory simulations testing‖
Industrial Crops and Products, 33: p. 648–658.
Rutiaga M., Galan L., Morales L., Gordon S., Imam S., Orts W., Glenn G., Niño K. (2005)
―Mechanical property and biodegradability of cast films prepared from blends of oppositely
charged biopolymers‖ Journal of Polymers and the Environment, 13(2): p. 185-191.
Rychter P., Kawalec M., Sobota M., Kurcok P., Kowalczuk M. (2010), ―Study of aliphatic-
aromatic copolyester degradation in sandy soil and its ecotoxicological impact‖
Biomacromolecules, 11(4): p.839-847.
Sadi R.K., Fechine G.J.M., Demarquette N.R. (2010), ―Photodegradation of poly(3-
hydroxybutyrate)‖ Polymer Degradation and Stability, 95: p. 2318-2327.
Saeki T., Tsukegi T., Tsuji H., Daimon H., Fujie K (2005), ―Hydrolytic degradation of
poly[(R)-3-hydroxybutyric acid] in the melt‖ Polymer 46: p. 2157-2162.
Sakai K., Kawano H., Iwami A., Nakamura M., Moriguchi M. (2001), ―Isolation of a
thermophilic poly-l-lactide degrading bacterium from compost and its enzymatic
characterization‖ J Biosci Bioeng., 92: p. 298-300.
Sakai K, Hamada N, and Watanabe Y. (1986), Studies on the poly(vinyl alcohol)-degrading
enzyme. In Agric Biol Chem. Pp. 989-996. Degradation mechanism of poly(vinyl alcohol) by
successive reactions of secondary alcohol oxidase and b-diketone hydrolase from
Pseudomonas sp, Vol. 50.
Salt, D.E.; , R.D. Smith, and I. and Raskin, (1998), Phytoremediation. Annual Review of
Plant Physiology and Plant Molecular Biology 49:643-668.
Sanchez-Garcia M.D., Gimenez E., Lagaron J.M. (2008), ―Morphology and barrier
properties of solvent cast composites of thermoplastic biopolymers and purified cellulose
fibres‖ Carbohydrate Polymers, 71: p. 235-244.
Chen Haiyan PhD Thesis
- 178 -
Sanchez-Garcia M.D., Gimenez E., Lagaron J.M. (2010a), ―On the use of plant cellulose
nanowhiskers to enhance the barrier properties of polylactic acid‖ Cellulose, 17: p. 987-1004.
Sanchez-Garcia M.D., Lopez-Rubio A., Lagaron J.M. (2010b), ―Natural micro and nano-
biocomposites with enhanced barrier properties and novel functionalities for food
biopackaging Applications‖. Trends in Food Science & Technology, 21: p. 528-536.
Sang B.I., Hori K., Tanji Y., Unno H. (2001), ―A kinetic analysis of the fungal degradation
process of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) in soil‖ Biochemical Engineering
Journal, 9: p. 175–184.
Sang B.I., Hori K., Tanji Y., Unno H. (2002), ‖Fungal contribution to in situ biodegradation
of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) film in soil‖ Appl. Microbiol. Biotechnol.,
58: p. 241-247.
Sarasua J.R., López Arraiza A., Balerdi P., Maiza I. (2005), ―Crystallinity and mechanical
properties of optically pure polylactides and their blends‖ Polymer Science & Engineering,
45(5): p. 745-753.
Sangwan, Parveen, Cameron Way, and Dong-Yang Wu, (2009), New Insight into
Biodegradation of Polylactide (PLA)/Clay Nanocomposites Using Molecular Ecological
Techniques. Macromolecular Bioscience 9(7):677-686.
Sand W, (2003), Microbial life in geothermal waters. Geothermics 32:231-251.
Schirmer A.D., Jendrossek D., Schlegel H.G. (1993), ―Degradation of poly(3-hydroxy-
octanoic acid) [(P(3HO)] by bacteria: purification and properties of a P(3HO) depolymerise
from Pseudomonas fluorescens GK13‖ Appl. Environ, Microbiol., 59: p. 1220-1227.
Schroeder R.L. (1994), ―The use of recycled materials in highway construction‖ 58(2).
Scott G., and Wiles. D. M. (2001), Biomacromolecules. Pp. 615, Vol. 2.
Scott, G. (1965), ―Atmospheric oxidation and antioxidants‖ Amsterdam, London and New
York Elsevier Publishing Co.
Scott, G. (1999), ―Polymers and the environment: Royal Society of Chemistry‖.
Scott, G. (1994) Environmental biodegradation of hydrocarbon polymers:initiation and
control. In Biodegradable plastic and polymers, ed. Y. Doi, and K. Fukuda, 79-92.
Amsterdama: Elsevier
Scott, G. In: G. (1993), Atmospheric oxidation and antioxidants, Vol. II: Elsevier. chapters 3
and 8
Scott, G., and D. M. Wiles, (2001), Programmed-life plastics from polyolefins: a new look at
sustainability. Biomacromolecules 2(3):615-22.
Scott G. In: G. Scott (Ed), (1981) Developments in polymer stabilisationd4 London: Applied
Science Publishers; [chapter 1].
Sedlacek, T., et al. (2011), ―On the influence of nutrient agents on accelerated physical aging
Reference
- 179 -
of LDPE based mulch foil‖, in Proceedings of the 4th WSEAS international conference on
Energy and development - environment - biomedicine, World Scientific and Engineering
Academy and Society (WSEAS): Corfu Island, Greece. p. 401-406.
Sedláčková, M., Lacík I., Chodák I. (2001), ―Poly(ethylene-co-methacrylic acid) copolymer
as an effective compatibilizer of LDPE/wood flour composite‖ Macromolecular Symposia,
170(1): p. 157-164.
Selke S.E., Wichman I. (2004), ―Wood fiber/polyolefin composites‖ Composites Part A:
Applied Science and Manufacturing, 35(3): p. 321-326.
Selke S.E. (2006), Plastics recycling and biodegradable plastics. In Handbook of Plastics
Technologies, Charles, H., Ed. McGraw-Hill Companies: USA.
Semple, Sean, Maccalman, Laura, Naji, Audrey Atherton, Dempsey, Scott, Hilton, Shona,
Miller, Brian G., Ayres, Jon G. (2007), Bar Workers' Exposure to Second-Hand Smoke: The
Effect of Scottish Smoke-Free Legislation on Occupational Exposure. Annals of Occupational
Hygiene 51(7):571-580.
Sen A., Bhattachaya M. (2000), ―Residual stresses and density gradient in injection molded
starch/synthetic polymer blends‖ Polymer, 41(26): p. 9177-9190.
Shah A.A., Hasan F., Hameed A., Ahmed S. (2007), ―Isolation and characterization of poly(3-
hydroxybutyrate-co-3-hydroxyvalerate) degrading bacteria and purification of PHBV
depolymerase from newly isolated Bacillus sp. AF3‖ Int. Biodeterior. Biodegrad., 60: p. 109-
115.
Shah A.A.; Hasan F.; Hameed A.; Ahmed S. (2008), ―Biological degradation of plastics: a
comprehensive review‖ Biotechnology Advances, 26(3): p. 246-245.
Shah A.A., Hasan F., Hameed A. (2010), ―Degradation of poly(3-hydroxybutyrate-co-3-
hydroxyvalerate) by a newly isolated Actinomadura sp. AF-555, from soil‖ International
Biodeterioration & Biodegradation, 64: p. 281-285.
Shangguana Y.Y., Wang Y.W., Wu Q., Chen G.Q. (2006), ―The mechanical properties and in
vitro biodegradation and biocompatibility of UV-treated poly(3-hydroxybutyrate-co-3-
hydroxyhexanoate)‖ Biomaterials, 27: p. 2349–2357.
Shanks R.A., Hodzic A., Wong S. (2004), ―Thermoplastic biopolyester natural fiber
composites. Journal of Applied Polymer Science, 91(4). p. 2114-2121.
Shen L., Haufe J., Patel M.K. (2009), ―Product overview and market projection of emerging
bio-based plastics‖ PRO-BIP 2009, Final Report, June 2009.
Shimao M. (2001), ―Biodegradation of plastics‖ Biotechnology, 12: p. 242–247.
Shnean Z.Y. (2008), ―Effect of grain and calcinations kaolin additives on some mechanical
and physical properties on low density polyethylene composites‖ Al-Khwarizmi Engineering
Journal, 4(4): p. 37-44.
Shogren R.L., Doaneb W.M., Garlotta D., Lawtona J.W., Willetta J.L. (2003),
―Biodegradation of starch/polylacticacid/poly(hydroxyester-ether) composite bars in soil‖
Chen Haiyan PhD Thesis
- 180 -
Polymer Degradation and Stability, 79: p. 405–411.
Sinha Ray S., Yamada K., Okamoto M., Ogami A., Ueda K. (2002), ―New
polylactide/layered silicate nanocomposite: nanoscale control over multiple properties‖
Macromol. Rapid Commun., 23: p: 943-947.
Sinha Ray S., Okamoto M. (2003), ―Polymer/layered silicate nanocomposites: a review from
preparation to processing‖ Progress in Polymer Science, 28 (11): p. 1539-1641.
Siracusa V., Rocculi P., Romani S., Dalla Rosa M. (2008), ―Biodegradable polymers for food
packaging. A review‖ Trends in Food Science & Technology, 19: p. 634-643.
Sohail O.B., Sreekumar P.A., Khan m.J., Hakeem A., Alshaiban A.A., Al-Harthi M.A. (2012),
―Thermal effect of ceramic nanofiller aluminium nitride on polyethylene properties‖ Journal
of Nanomaterials, doi:10.1155/2012/250364.
Sorrentino A., Gorrasi G., Vittoria V. (2007), ―Potential perspectives of bio-nanocomposites
for food packaging applications‖ Trends in Food Science & Technology, 18: p. 84-95
Spyros A., Kimmich R., Briese D.H., Jendrossek D. (1997), ―1H NMR Imaging study of
enzymatic degradation in poly(3-hydroxybutyrate) and poly(3-hydroxybutyrate-co-3-
hydroxyvalerate). evidence for preferential degradation of the amorphous phase by phb
depolymerase b from pseudomonas lemoignei‖ Macromolecules, 30: p. 8218-8225.
Srideshi N., Bhubalan K., Sudesh K. (2006), ―Degradation of commercially important
polyhydroxyalkanoates in tropical mangrove ecosystem‖ Polymer Degradation and Stability,
91: p. 2931-2940.
Subramanian P.M. (2000), ―Plastics recycling and waste management in the US‖ Resources,
Conservation and Recycling, 28(3–4): p. 253-263.
Sudesh K., Abe H., Doi Y. (2000), ―Synthesis, structure and properties of
polyhydroxyalkanoates: biological polyesters‖ Progress in Polymer Science, 25(10): p.
1503-1555.
Suriyamongkol P., Weselake R., Narine S., Moloney M., Shah S. (2007), ―Biotechnological
approaches for the production of polyhydroxyalkanoates in microorganisms and plants — A
review‖ Biotechnology Advances, 25(2): p. 148-175.
Suzuki, T. (1979), Degradation of poly(vinyl alcohol) by microorganisms. J. Appl. Polym.
Sci., Appl. Polym. Symp 35:431-437.
Swift, G. (1997), Non-medical biodegradable polymers: Environmentally degradable
polymers. In Handbook of Biodegradable Polymers. J.K. A. J. Domb, and D. M. Wiseman,
ed. Pp. 473-511. Amsterdam: Harwood Academic.
Tabatabai M.A. (1969), ―Use of ρ-nitrophenol phosphate in assay of soil phosphatase
activity‖ Soil Biol. Biochem., 1: p. 301-307.
Tanio T., Fukui T., Shirakura Y., Saito T., Tomita K., Kahio T., Masume S. (1982), ‖An
extracellular poly(3-hydroxybutyrate) depolimerase from Alcaligenes faecalis‖ Eur. J.
Biochem., 124: p. 71-77.
Reference
- 181 -
Tao J., Song C., Cao M., Hu D., Liu L., Liu N., Wang S. (2009), ―Thermal properties and
degradability of poly(propylene carbonate)/poly (β-hydroxybutyrate-co-β-hydroxyvalerate)
(PPC/PHBV) blends‖ Polymer Degradation and Stability, 94: p. 575–583.
Takaku H., Kimoto A., Kodaira S., Nashimoto M., Takagi M. (2006), ‖Isolation of gram-
positive poly(3-hydroxybutyrate) (PHB)-degrading bacterium from compost, and cloning
and characterization of a gene encoding PHB depolymerase of Bacillus megaterium N-18-
25-9‖ FEMS Microbiol. Lett., 264: p. 152-159.
Takatani M., Ikeda K., Sakamoto K., Okamoto T. (2008), ―Cellulose esters as compatibilizers
in wood/poly(lactic acid) composite” J Wood Sci, 54: p. 54-61.
Taki H., Syutsubo K., Mattison R.G., Harayama S. (2007), ‖Identification and
characterization of o-xylene-degrading Rhodococcus sp.‖ Biodegradation, 18: p. 17-26.
Teeraphatpornchai T., Nakajima-Kambe T., Shigeno-Akutsu Y., Nakayama M., Nomura N.,
Nakahara T. (2003), ―Isolation and characterization of a bacterium that degrades various
polyester-based biodegradable plastics‖ Biotech Lett, 25: p. 23-28.
Teramoto N., Urata K., Ozawa K., Shibata M. (2004), ―Biodegradation of aliphatic polyester
composites reinforced by abaca fibre‖ Polym Degrad Stab, 86: p. 401-409.
Tokiwa Y., Jarerat A. (2004), ―Biodegradation of poly (L-lactide)‖, Biotechnol. Lett., 26: p.
771–777.
Tokiwa Y., Calabia B.P. (2004), ―Review: degradation of microbial polyesters‖ Biotechnol.
Lett, 26: p. 1181–1189.
Todo M., Park S.D, Takayama T., Arakawa K. (2007), ―Fracture micromechanisms of
bioabsorbable PLLA/PCL polymer blends‖ Engineering Fracture Mechanics, 74. p. 1872-
1883.
Tomita K., Kuraki Y., Nagai K. (1999), ―Isolation of thermophiles degradating poly (L-lactic
acid)‖ J Biosci Bioeng, 87: p. 752–755.
Tomita K., Nakajima T., Kikuchi Y., Miwa N. (2004), ―Degradation of poly( L-lactic acid) by
a newly isolated thermophile‖ Polymer Degradation and Stability, 84: p. 433-438.
Toncheva, V. (1996), Synthesis and Environmental Degradation of Polyesters Based on
Poly(ε-caprolactone). Journal of Environmental Polymer Degradation 4(2):71-83.
Ton-That M.T., Denault J., Perrin F., Leelapornpisit W., Hu W., Cole K.C. (2009), ―New high
performance natural fiber composites‖ Composites & Polycon .
Torres A., Li S.M., Roussos S., Vert M. (1996), ―Poly (lactic acid) degradation in soil or
under controlled conditions‖ J Appl Polym Sci, 62: p. 2295-2302.
Trinh Tan, F., Copper D.G., Maric M., Nicell J.A. (2008), ―Biodegradation of a synthetic co-
polyester by aerobic mesophilic microorganisms‖ Polymer Degradation and Stability, 93(8):
p. 1479-1485.
.
Chen Haiyan PhD Thesis
- 182 -
Tsuchii, A., T. Suzuki, and Y. Takahara. (1977), Microbial degradation of styrene oligomer.
Agricultural and Biological Chemistry 41(12):2417-2421.
Tseng M., Hoang K.C., Yang M.K., Yang S.F., Chu W.S. (2007), ―Polyester-degrading
thermophilic actinomycetes isolated from different environment in Taiwan‖ Biodegradation,
18(5): p. 579-583.
Tserki V., Zafeiropoulos N.E., Simon F., C. Panayiotou C. (2005), ―A study of the effect of
acetylation and propionylation surface treatments on natural fibres‖ Composites Part A:
Applied Science and Manufacturing.
Tsuji H., Ikada Y. (1998), ―Properties and morphology of poly (L-lactide). II. hydrolysis in
alkaline solution‖ Journal of Polymer Science: Part A: Polymer Chemistry, 36, p. 59-66.
Tsuji H., Echizen Y., Nishimura Y. (2006), ―Photodegradation of biodegr adable polyes ters:
A comprehensive study on poly( L-lactide) and poly( 3 -caprolactone)‖ Polymer
Degradation and Stability, 91: p. 1128-1137.
Tuominen J., Tuominen J., Kylmä J., Kapanen A., Venelampi O., Itävaara M., Seppälä J.
(2002), ―Biodegradation of lactic acid based polymers under controlled composting
conditions and evaluation of the ecotoxicological impact‖ Biomacromolecules, 3(3): p. 445-
455.
Urayama H., Kanamori T., Fukushima K., Kimura Y. (2003), ―Controlled crystal nucleation
in the melt-crystallization of poly(l-lactide) and poly(L-lactide/poly(D-lactide)
stereocomplex‖ Polymer, 44: p. 5635-5641.
Valappil S.P., Boccaccini A.R., Bucke C., Roy I. (2007), ―Poly-hydroxyalkanoates in Gram-
positive bacteria: insights from the genera Bacillus and Streptomyces‖ Antonie van
Leeuwenhoek, 91: p. 1-17.
Van der Sloot H.A. (1990), ―Leaching behaviour of waste and stabilized waste materials;
characterization for environmental assessment purposes‖ Waste Management & Research,
8(3): p. 215-228.
Vasile C., Kulshreshtha A.K. (2003), Handbook of polymer blends and composites. Rapra
Technology Ltd: UK; Vol. 4B.
Verhoogt H., Pierre N.S., trucon B.A., Ramsay B.D. (1995), ―Blends containing
poly(hydroxybutyrate-co-12%-hydroxyvalerate) and thermoplastic starch‖ Canadian Journal
of Microbiology, 41(13): p. 323-328.
Volova T.G., Gladyshev M.I., Trusova M.Y., Zhila N.O. (2006), ―Degradation of
polyhydroxyalkanoates and the composition of microbial destructors under natural
condition‖ Microbiology, 75(5): p. 593-598.
Volova T.G., Gladyshev M.I., Trusova M.Y., Zhila N.O. (2007), ―Degradation of
polyhydroxyalkanoates in eutrophic reservoir‖ Polymer Degradation and Stability, 92: p.
580-586.
Volova T.G., Boyandin A.N., Vasiliev A.D., Karpov V.A., Prudnikova S.V., Mishukova O.V.,
Boyarskikh U.A., Filipenko M.L., Rudnev V.P., Xuân B.B., Dung V.V., Gitelson I.I. (2010),
Reference
- 183 -
―Biodegradation of polyhydroxyalkanoates (PHAs) in tropical coastal waters and
identification of PHA-degrading bacteria‖ Polymer Degradation and Stability, 95: p. 2350-
2359.
Voigt, J. (1966) Atmospheric Oxidation and Antioxidants. Von G. Scott. Elsevier Publishing
Company, Amsterdam-London-New York 1965. X, 528 S., zahlr. Abb., geb. Dfl. 72.50.
Angewandte Chemie 78(22):1027-1027.
Volke-Sepúlveda, T., Favela-Torres, E., Manzur-Guzman, A., Limon-Gonzalez, M., and G.
Trejo-Quintero. (1999), Microbial degradation of thermo-oxidized low-density polyethylene.
J. Appl. Polym. Sci. 73: 1435-1440
Volke-Sepŭlveda, T., Saucedo-Castañeda, G., Gutiérrez-Rojas, M., Manzur, A., and E.
Favela-Torres. (2002), Thermally treated low density polyethylene biodegradation by
Penicillium pinophilum and Aspergillus niger. .J. Appl. Polym. Sci. 83: 305-314
Vroman I. & Tighzert L. (2009), Biodegradable Polymers. Materials, p. 307-344.
Wang Y.W., Mo W., Yao H., Wu Q., Chen J., Chen G.Q. (2004), ―Biodegradation studies of
poly(3-hydroxybutyrate-co-3-hydroxyhexanoate)‖ Polymer Degradation and Stability, 85: p.
815-821.
Wang S., Song C., Chen G., Guo T., Liu J., Zhang B., Takeuchi S. (2005), ―Characteristics
and biodegradation properties of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/organophilic
montmorillonite (PHBV/OMMT) nanocomposite‖ Polymer Degradation and Stability, 87
(1): p. 69-76.
Wang N., Yu J., Ma X. (2007), ―Preparation and characterization of thermoplastic starch/PLA
blends by one-step reactive extrusion” Polymer International, 56(11): p. 1440-1447.
Wang S., Ma P., Wang R., Wang S., Zhang Y., Zhang Y. (2008), ―Mechanical, thermal and
degradation properties of poly(d,l-lactide)/poly(hydroxybutyrate-
cohydroxyvalerate)/poly(ethylene glycol) blend‖ Polymer Degradation and Stability, 93: p.
1364–1369.
Wang X., Chen Z., Chen X., Pan J., Xu K. (2010), ―Miscibility, crystallization kinetics, and
mechanical properties of poly (3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) /Poly(3-
hydroxybutyrate-co-4- hydroxybutyrate) (P3/4HB) blends‖ DOI 10.1002/ app.31215.
Wang, Y. Z., Yang, K. K., Wang, X. L., Zhou, Q., Zheng, C. Y., Chen, Z. F. (2004),
Agricultural application and environmental degradation of photo-biodegradable polyethylene
mulching films. Journal of Polymers and the Environment 12(1):7-10.
Watanabe T., Ohtake Y., Asabe H., Murakami N. (2009), Biodegradability and degrading
microbes of low-density polyethylene. J. Appl. Polym. Sci., 111: 551-559
Weihua K., He Y., Asakawa N., Inoue Y. (2004), ―Effect of lignin particles as a nucleating
agent on crystallization of poly(3-hydroxybutyrate)‖ Journal of Applied Polymer Science,
94(6): p. 2466-2474
Weiland M., Daro A., David C. (1995), Biodegradation of thermally oxidized polyethylene.
Polym. Degrad. Stab.; 48, 275-289
Chen Haiyan PhD Thesis
- 184 -
Wiles D. M., Scott G., (2006) Polym. Degrad. Stab., 91, 1581
Weng Y.X., Wang X.L., Wang Y.Z. (2010), ―Biodegradation behaviour of PHBV films in a
pilot-scale composting condition‖ Polymer Testing, 29: p. 579–587.
Weng Y.X., Wang X.L., Wang Y.Z. (2011), ―Biodegradation behavior of PHAs with different
chemical structures under controlled composting conditions‖ Polymer Testing, 30: p. 372–
380.
Williams D.F. (1982), ―Review, biodegradation of surgical polymers‖ .J. Mater. Sci., 17: p.
1233–1246.
Witt U., Einig T, Yamamoto M., Kleeberg I., Deckwer W.D., Müller R.J. (2001),
―Biodegradation of aliphatic–aromatic copolyesters: evaluation of the final biodegradability
and ecotoxicological impact of degradation intermediates‖ Chemosphere, 44(2): p. 289-299.
William James Lamont, Jr.(1999),Vegetable Production Using Plasticulture. In Food &
Fertilizer Technology Center. Pp. 9, Vol. 16802. Department of Horticulture, 114 Tyson
Building,The Pennsylvania State University: University Park, Pennsylvania 16802-4200
USA.
Winursito, Isananto, and Shuichi Matsumura. (1996), Biodegradability, hydrolytic
degradability, and builder performance in detergent formulations of partially dicarboxylated
alginic acid. Journal of Environmental Polymer Degradation 4(2):113-121.
Wong S., Shanks R., Hodzic A. (2002), ―Properties of poly(3-hydroxybutyric acid)
composites with flax fibres modified by plasticiser absorption‖ Macromolecular Materials
and Engineering, 287(10): p. 647-655.
Woodings C. (2000) Crop-based polymers for non-wovens. Paper presented at the Insight
Conference. Calvin Woodings Consulting. November 2000, Toronto.
More information: http://www.nonwoven.co.uk/CRWINSIGHT2000.htm
Wu C.S. (2009), ―Renewable resource-based composites of recycled natural fibers and
maleated polylactide bioplastic: Characterization and biodegradability‖ Polymer
Degradation and Stability, 94: p. 1076–1084.
Xanthos, M. and S.S. Dagli S.S. (1991), ―Compatibilization of polymer blends by reactive
processing‖ Polymer Engineering & Science, 31(13): p. 929-935.
Xu, S., Lehmann, R. G., Miller, J. R., Chandra, G. (1998), Degradation of
polydimethylsiloxanes (silicones) as influenced by clay minerals. Environmental Science and
Technology 32(9):1199-1206.
Xu J., and Bao-Hua Guo B.H. (2010), ―Poly(butylene succinate) and its copolymers:
Research, development and industrialization‖ Biotechnology Journal, 5(11): p. 1149-1163.
Yamamoto M.S.C., Skupin G., Beimborn D., Müller R.J (2002)., ―Biodegradable aliphatic-
aromatic polyesters: "Ecoflex®‖, In Polyesters III: Applications and Commercial Products,
Y.D.a.A. Steinbüchel, Editor: German. p. 299-305.
Reference
- 185 -
Yamamoto M., et al. (2005), ―Biodegradable Aliphatic-Aromatic Polyesters: ―Ecoflex®‖, In
Biopolymers Online2005, Wiley-VCH Verlag GmbH & Co. KGaA.
Yamada-Onodera K., Mukumoto H., Katsuyaya Y., Saiganji A., Tani Y. (2001) Degradation
of polyethylene by a fungus, Penicillium simplicissimum YK. Polymer Degradation and
Stability 72(2):323-327.
Yang H., Li Z.S., Qian H.J., Yang Y.B., Zhang X.B., Sun C.C. (2004), ―Molecular dynamics
simulation studies of binary blend miscibility of poly(3-hydroxybutyrate) and poly(ethylene
oxide)‖ Polymer, 45(2): p. 453-457.
Yang K.K., Wang X.L.; Wang Y.Z. (2007), ―Progress in nanocomposite of biodegradable
polymer‖ J.Ind.Eng.Chem., 13(4): p. 485-500.
Yeomans J.C., Bremmer J.M. (1988), ―A rapid and precise method for routine determination
of organic carbon in soil‖. Comm. Soil Sci. Plant Anal., 19: p. 1467–1476.
Yew S.P., Tang H.Y., Sudesh K. (2006), ―Photocatalytic activity and biodegradation of
polyhydroxybutyrate films containing titanium dioxide‖ Polymer Degradation and Stability,
91: p. 1800-1807.
Yu L.,K..D., Li L. (2006), ―Polymer blends and composites from renewable resources‖
Progress in Polymer Science 31(6): p. 576-602.
Yu F., Liu T., Zhao X., Yu X., Lu A., Wang J. (2012), ―Effects of talc on the mechanical and
thermal properties of polylactide‖ Journal of Applied Polymer Science, 125(529: p. 99-109.
Yutaka Tokiwa, Buenaventurada P. Calabia. (2004), Review Degradation of microbial
polyesters. Biotechnology Letters 26(15):1181-1189.
Zhang S., Cao X.Y., Ma Y.M., Ke Y.C., Zhang J.K., Wang F.S. (2011) ―The effects of particle
size and content on the thermal conductivity and mechanical properties of Al2O3 /high
density polyethylene (HDPE) composites‖ eXPRESS Polymer Letters, 5(7): p. 581-590.
Zhao Q., Cheng G., Song C., Zeng Y., Tao J., Zhang L. (2006), ‗‘Crystallization behavior and
biodegradation of poly(3-hydroxybutyrate) and poly(ethylene glycol) multiblock
copolymers‖ Polymer Degradation and Stability, 91: p. 1240-1246.
Zheng Y., Yanful E.K., Bassi A.S. (2005), ―A Review of plastic waste biodegradation‖
Critical Reviews in Biotechnology, 25(4): p. 243-250.
Zini E., Focarete M.L., Noda I., Scandola M. (2007), ―Bio-composite of bacterial poly(3-
hydroxybutyrate-co-3-hydroxyhexanoate) reinforced with vegetable fibers‖ Composites
Science and Technology, 67(10): p. 2085-2094.