The CX6 line by Carbitex features six core materials which offer a range in flexibility, haptics, appearance and performance. There are a remarkable array of new applications and opportunities this line of advanced materials offers.
CX6 Flexible Carbon Fiber
A324 A399 A368 A377 A386
Thin, lightweight & waterproof. Top surface matte, back surface gloss
Thin, lightweight weave textured top surface. Easy to wrap and clean
Durable, weave textured top surface with soft touch, matte finish
Characteristics similar to A368 with a semi-gloss finish on top surface
Thin, lightweight weave textured top surface with soft touch, matte finish
PHONE +1 (509) 591-9775 EMAIL [email protected]
Technical SpecificationsMATERIAL 材料 BASE FABRIC WEIGHT FIBER / DENSITY WEAVE STYLE A SIDE TEXTURE A SIDE FINISH B SIDE
WEIGHT 重量
THICKNESS 厚度
ABRASION RESISTANCE 耐磨 TABER CS-10 TABER H-18
BREAKING STRENGTH 拉力
WARP FILL 45º
TONGUE TEAR 撕力 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
FLEXURAL PROPERTIES 弯曲性能 TOP BOTTOM
ELONGATION 延伸率 WARP FILL 45º
200 GSM CARBON2 x 2 Twill ZB Smooth SurfaceMatte FinishGloss Finish
418 GSM
0.33 mm ASTM D1777
ASTM D38844000 Cycles ASTM D3884
575 lb/in ASTM D751-A590 lb/in ASTM D751-A660 lb/in ASTM D751-A
87 ASTM D2261-1339 ASTM D4704-1381 ASTM D4704-13
509 ASTM D751-B (1” Strip) 570 ASTM D751-B (1” Strip) 138 ASTM D751-B (1” Strip)
39313 PSI43980 PSI10674 PSI
4558 mg-cm BIS IS-6490-1971 (Cantilever)5289 mg-cm BIS IS-6490-1971 (Cantilever)
5%5%53%
A324
11/14/2015
A324 is one of the thinnest versions of CX6. It uses a lighter base fabric that is more flexible, light and thin. It’s finished on both sides: High Gloss & Matte Finish and has no surface topology, It is easy to clean and bonds well to other materials/substrates.
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
PHONE +1 (509) 591-9775 EMAIL [email protected]
Technical SpecificationsMATERIAL 材料 BASE FABRIC WEIGHT FIBER / DENSITY WEAVE STYLE A SIDE TEXTURE A SIDE FINISH B SIDE
WEIGHT 重量
THICKNESS 厚度
ABRASION RESISTANCE 耐磨 TABER CS-10 TABER H-18
BREAKING STRENGTH 拉力
WARP FILL 45º
TONGUE TEAR 撕力 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
FLEXURAL PROPERTIES 弯曲性能 TOP BOTTOM
ELONGATION 延伸率 WARP FILL 45º
200 GSM CARBON2 x 2 Twill Textured SurfaceSemi-Gloss FinishCoated
418 GSM
0.43 mm ASTM D1777
3000 Cycles ASTM D3884
431 lb/in ASTM D751-A569 lb/in ASTM D751-A396 lb/in ASTM D751-A
24 ASTM D2261-1318 ASTM D4704-1326 ASTM D4704-13
410 ASTM D751-B (1” Strip) 492 ASTM D751-B (1” Strip) 70 ASTM D751-B (1” Strip)
26527 PSI33810 PSI8112 PSI
3987 mg-cm BIS IS-6490-1971 (Cantilever)3475 mg-cm BIS IS-6490-1971 (Cantilever)
5%6%48%
A399
11/14/2015
A399 is one of the thinnest versions of CX6 with a textured top surface. A Semi-Gloss finish makes this an easy material to keep clean while maintaining the integrity, look and feel of real carbon fiber weave. This is a flexible material that provides both aesthetic and functional attributes and can be a great replacement for leathers and synthetics.
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
PHONE +1 (509) 591-9775 EMAIL [email protected]
Technical SpecificationsMATERIAL 材料 BASE FABRIC WEIGHT FIBER / DENSITY WEAVE STYLE A SIDE TEXTURE A SIDE FINISH B SIDE
WEIGHT 重量
THICKNESS 厚度
ABRASION RESISTANCE 耐磨 TABER CS-10 TABER H-18
BREAKING STRENGTH 拉力
WARP FILL 45º
TONGUE TEAR 撕力 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
FLEXURAL PROPERTIES 弯曲性能 TOP BOTTOM
ELONGATION 延伸率 WARP FILL 45º
245 GSM CARBON2 x 2 Twill Textured SurfaceMatte Finish (Soft Touch)Coated
475 GSM
0.47 mm ASTM D1777
4000 Cycles ASTM D38842500 Cycles ASTM D3884
584 lb/in ASTM D751-A495 lb/in ASTM D751-A529 lb/in ASTM D751-A
25 ASTM D2261-137 ASTM D4704-1332 ASTM D4704-13
524 ASTM D751-B (1” Strip) 467 ASTM D751-B (1” Strip) 220 ASTM D751-B (1” Strip)
29317 PSI25979 PSI9339 PSI
6743 mg-cm BIS IS-6490-1971 (Cantilever)5817 mg-cm BIS IS-6490-1971 (Cantilever)
6%6%49%
A368
11/14/2015
A368 is an exquisite version of CX6 with a textured and matte top surface. It has a heavier weight base fabric - 245 GSM that provides good handle and substance which likens it to heavy duty leather, canvas and Cordura.
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
PHONE +1 (509) 591-9775 EMAIL [email protected]
Technical SpecificationsMATERIAL 材料 BASE FABRIC WEIGHT FIBER / DENSITY WEAVE STYLE A SIDE TEXTURE A SIDE FINISH B SIDE
WEIGHT 重量
THICKNESS 厚度
ABRASION RESISTANCE 耐磨 TABER CS-10 TABER H-18
BREAKING STRENGTH 拉力
WARP FILL 45º
TONGUE TEAR 撕力 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
FLEXURAL PROPERTIES 弯曲性能 TOP BOTTOM
ELONGATION 延伸率 WARP FILL 45º
245 GSM CARBON2 x 2 Twill Textured SurfaceSemi-Matte FinishCoated
475 GSM
0.47 mm ASTM D1777
2800 Cycles ASTM D3884
584 lb/in ASTM D751-A495 lb/in ASTM D751-A529 lb/in ASTM D751-A
25 ASTM D2261-137 ASTM D4704-1338 ASTM D4704-13
524 ASTM D751-B (1” Strip) 467 ASTM D751-B (1” Strip) 176 ASTM D751-B (1” Strip)
29317 PSI25979 PSI9339 PSI
6743 mg-cm BIS IS-6490-1971 (Cantilever)5817 mg-cm BIS IS-6490-1971 (Cantilever)
6%6%49%
A377
11/14/2015
A377 is identical to A368 with exception of a Semi-Gloss top finish versus Matte. A377 is easy to keep clean
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
PHONE +1 (509) 591-9775 EMAIL [email protected]
Technical SpecificationsMATERIAL 材料 BASE FABRIC WEIGHT FIBER / DENSITY WEAVE STYLE A SIDE TEXTURE A SIDE FINISH B SIDE
WEIGHT 重量
THICKNESS 厚度
ABRASION RESISTANCE 耐磨 TABER CS-10 TABER H-18
BREAKING STRENGTH 拉力
WARP FILL 45º
TONGUE TEAR 撕力 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
TENSILE STRENGTH 抗张强度 WARP FILL 45º
FLEXURAL PROPERTIES 弯曲性能 TOP BOTTOM
ELONGATION 延伸率 WARP FILL 45º
200 GSM CARBON2 x 2 Twill Textured SurfaceMatte Finish / Soft TouchCoated
419 GSM
0.51 mm ASTM D1777
2500 Cycles ASTM D3884
288 lb/in ASTM D751-A544 lb/in ASTM D751-A400 lb/in ASTM D751-A
22 ASTM D2261-1332 ASTM D4704-1314 ASTM D4704-13
436 ASTM D751-B (1” Strip) 598 ASTM D751-B (1” Strip) 172 ASTM D751-B (1” Strip)
21834 PSI29871 PSI8615 PSI
5027 mg-cm BIS IS-6490-1971 (Cantilever)5100 mg-cm BIS IS-6490-1971 (Cantilever)
5%6%52%
A386
11/14/2015
A386 is one of the thinnest, more flexible versions of CX6. It uses a lighter base fabric that is more flexible, light and thin. It’s characterized by it’s textured finish that takes on the actual weave pattern of the Carbon Fiber and it’s matte, soft touch top surface coating.
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
PHONE +1 (509) 591-9775 EMAIL [email protected]
Functional SpecificationsA378
11/14/2015
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
Carbitex CX6 378: Directional Stretch.A 200 GSM - 2 x 2 Twill fabric, CX6 378 is a unique fabric with similar physical characteristics to 377 but incorporates Carbitex’s patent pending technology of directional stretch control.
DIRECTIONAL STRETCH CONTROLCX6 378 allows for variable stretch along different axis. FIG 1.0 shows a sheet sample (11x17 in) with axis called out in the “portrait” orientation. Different stretch properties along different axis is possible. FIG 1.1 & 1.2 demonstrate how orientation of fabric will vary stretch properties.
X (63%)
Y (42%)
Z (5%)
FIG 1.0
FIG 1.1Limited stretchin longitudinal direction
FIG 1.2Limited stretch
in transverse direction
PHONE +1 (509) 591-9775 EMAIL [email protected]
Functional SpecificationsA378
12/20/2015
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
Carbitex CX6 378: Directional Stretch.The following graphs highlight the different tensile performance results for A378. To conduct this test, sample strips from different orientations were evaluated.
90 degree Tensile Test 75 degree Tensile Test
45 degree Tensile Test60 degree Tensile Test
30 degree Tensile Test 8 degree Tensile Test
lbs/in
elongation
lbs/in
elongation
lbs/in
elongation
lbs/in
elongation
lbs/in
elongation
lbs/in
elongation
PHONE +1 (509) 591-9775 EMAIL [email protected]
CX6 Use, Care & Integration Support
12/20/2015
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
SolventsDepending on the type of alcohol-based solvent used, the effect on the matrix may differ. Aliphatic alcohols such as ethanol and isopropanol can trigger slight swelling.
MicrobialResistant to microbial degradation.
Hydrolysis ResistanceCan be used in underwater applications as well as humid and damp situations. Also good hydrolysis resistance at a high temperature and a good solution for applications located on the exterior of automobiles, which come into constant contact with dirt and water.
Oil & GreaseTypically stable when it comes into contact with greases, lubricants and test oils in tests like ASTM 1, IRM-902 and IRM-903. However, some oil-based fluids may be prepared with additives that could damage the material and should be tested for compatibility before use.
UV RangeWill not yellow or degrade with outdoor exposure.
Material Compatibil i ty.
PHONE +1 (509) 591-9775 EMAIL [email protected]
CX6 Use, Care & Integration Support
12/20/2015
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
Material Compatibil i ty.
Cutt ingStandard composite cutting tools such as scissors, utility knives, fabric wheel cutters and other traditional methods. Some customers have utilized computer controlled cutting tables for part cut nesting and fiber orientation control.
SewingCX6 has been sewn to itself and in combinations of leather, other fabrics, and foams. The seam strength is generally very good. Seam strength should be evaluated based on the stitch design, thread size, and seam design for the specific application and tested.
BondingCX6 has been bonded with hot melt fusing films to fabrics and itself. It has also been used with water based cements with solvent based and water based primers. It is recommended to test the bond strength with the desired substrate being bonded too.
PHONE +1 (509) 591-9775 EMAIL [email protected]
CX6 Use, Care & Integration Support
12/20/2015
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
Material Compatibil i ty.
Riveting, Bolt ing & ZippersWith CX6 it is possible to add rivets and secure hardware onto. Bolting items to and integrating zipper assemblies are common. Die presses, punches and traditional sewing machines can be used to finish with these methods.
Wrapping & FormingCX6 can be used to wrap panels and form to 2D & 3D shapes. Materials can be pre laminated with adhesives for use in thermal forming processes. A peel-back, pressure adhesive is also available pre laminated.
PHONE +1 (509) 591-9775 EMAIL [email protected]
CX6 Sheet Sizes
12/20/2015
© COPYRIGHT CARBITEX LLC 2015 • PROPRIETARY & CONFIDENTIAL
Samples & Orders.
SamplesCX6 provides finished & R&D samples in 3 sizes. Custom sizing and precutting may be available upon request.
Production OrdersCX6 fulfills production orders in 2 sizes. Custom sizing and precutting may be available upon request.
• 5 x 8 in (12.7 x 20.3 cm)
• 9 x 9 in (22.8 x 22.8 cm)
• 24 x 34 in (60.9 x 86.3 cm)
• 24 x 34” (60.9 x 86.3 cm)
• 34 x 48” (86.3 x 121.9 cm)