This product information is presented in good faith and is to the best of our knowledge , accurate. Itis intended to be used as a guide and is not to be considered as a specification for productsdescribed here, Harrisons Malayalam Ltd does not guarantee satisfactory results in any applicationfrom reliance upon this information and assumes no liability for any loss or damage arising out ofits use. Harrisons Malayalam Ltd recommends that the user of our products thoroughly tests themunder end use conditions to assure that they meet the requirements of intended application

Natural Rubber Latex Based Pressure Sensitive AdhesiveSpecially Developed for many end applications

Latxsive Pressure Sensitive Adhesives , are a solvent free Natural Rubber Latex and TackifierResin Emulsion PSA’s . These Adhesives are compounded especially for coating on , a variety ofsubstrates like Pper, film , foil, foam , fabrics etc , for a lot’s of end Applications .These adhesiveexhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) , Rolling BallTack , and good ageing resistance. The Viscosity of the Adhesive is precisely controlled , to enableor allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar or even Comma / ReverseRoller coating.Latxsive PSA’s , are based on the “go green” movement and environmentally friendly . TheseAdhesives are PVC free, lead free, phthalate free, and manufactured directly from the RubberEstate in Kerala , India.

Adhesive Application Method :1. Comma Coating2. Gravure Coating3. Kiss coating with Myer bar

Application :For General Purpose , Packaging, Holding, Bonding , Protection , Insulation Heat and Cold orElectrical Insulation , Repositionable , adhesive coated products.These adhesives are formulated with a most suitable, coat ability, wettablity , spreading properties .These Adhesives can be coated with great ease on

Low energy surfaces like , PVC, PP, PET, PE films

Latxsive




Variety of papers like , calendared Kraft , crepe paper etcMetal FoilsElastomeric / polymeric FoamsCotton or Synthetic FabricsNon Woven Fabrics

Tape / Coated Product Applications Areas

AutomobileWhite goods/ EquipmentsInsulation , Heat and ColdInsulation ElectricalSurface ProtectionMaskingMounting and HoldingRepositionable packagingPackaging especially for Cold StorageReduction of Noise Pollution , etc.

Latxsive Grades

We have following Grades available1. Latxsive HML RP : for Repositionable Tapes2. Latxsive HML HC : for Heat and cold Insulation3. Latxsive HML RUB : for tyre fabrics4. Latxsive HML MSK : FOR Masking Tapes5. Latxsive HML PET : for Polyester Insulation Tapes6. Latxsive HML SPT HT IN/OUT : for surface protection tapes7. Latxsive HML SPT LT IN/OUT : for surface Protection applications8. Latxsive HML PKG : for BOPP , PVC , Paper based Packaging Tapes9. Latxsive HML 16 PVC INSUL : for PVC Insulation Tapes10. Latxsive HML DS : for Foam, Film , paper based Double side Adhesive

Tapes




CONTACT US

FOR TRADE ENQUIRIES

Mr. Jobsy ThomasHead : Rubber Sales,& MarketingHarrisons Malayalam LimitedCochin - 682 003KERALA STATECell : 0091 9446005410Tel : 0091 484-2668023email : [email protected]

OR

Mr. Vikas BhagatMarketing ManagerHarrisons Malayalam LimitedMumbaiCell : 0091 97020 97461email : [email protected]

FOR TECHNICAL ADVICE

Mr. Shrikant AthavaleTechnical AdvisorHarrisons Malayalam LimitedPuneCell : 0091 7588288204 / 9850242282email : [email protected]




001. Latxsive RP

Natural Rubber Latex Based Pressure Sensitive Adhesive

Specially Developed for Repositionable Tape

Latxsive RP , is a solvent free Natural Rubber and Tackifier Resin Emulsion Pressure SensitiveAdhesive . This Adhesive is compounded for coating on Plastic Films or Paper , especially forRepositionable Applications. .This adhesive exhibits, a very good balance of controlled peeladhesion , holding power ( Shear Strength ) , Rolling Ball Tack , and good ageing resistance.The adhesive is compounded for a special purpose and hence it do not leave a residue on the appliedsurface even at higher temperatures up to 80-90 deg C. The Viscosity of the Adhesive is preciselycontrolled , to enable or allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar oreven Comma / Reverse Roller coating. This specialty formulated adhesive is strong enough to holdon the applied the substrate and when removed it does not leave a residue or damage the surface.This adhesive does not build up tack .

Repositionable Adhesive Labels

Tape Applications




Typical Properties

. Total Solids 40-45%Viscosity As per coaters requirementpH 9Minimum Application Temperature 20 deg CService Temperature Range Up to 75 deg C

Coated Web Polyester 25 micCoat weight , Grams / Sq. Mtr. 15 gsm

180 Peel Strength , grams/ 25 mm 180-200Shear Strength.25 mm X 25 mm X 1000 grams

60 hours

Rolling Ball Tack , mm >250Loop Tack , grams /25 mm 40Samples are Prepared by direct coating with help of Myer Bar no. 5 and dried for 5minutes at 70 degree C




Latxsive HC

Natural Rubber Latex Based Pressure Sensitive AdhesiveSpecially Developed for Heat and Cold Insulation Tape

Latxsive HC , is a solvent free Natural Rubber and Tackifier Resin Emulsion Pressure SensitiveAdhesive . This Adhesive is compounded especially for coating on Aluminum Foil, FSK ( FoilScrim Kraft ) Aluminum Glass Cloth , and a variety of Elastomeric Foams , for Heat and ColdInsulation Applications .This adhesive exhibits , a very good balance of peel adhesion , holdingpower ( Shear Strength ) , Rolling Ball Tack , and good ageing resistance. The Viscosity of theAdhesive is precisely controlled , to enable or allow coating by Gravure plus Myer bar or Kisscoating plus Myer Bar or even Comma / Reverse Roller coating.Latxsive PSA’s , are based on the “go green” movement and environmentally friendly . TheseAdhesives are PVC free, lead free, phthalate free, and manufactured directly from the RubberEstate in Kerala , India.

Application :

Heat and Cold Insulation Adhesive Tapes, are designed for ultimate performance in extremetemperatures. They are used to insulate in cold and hot environments, These Tapes are used topromote heat dissipation and protect parts from overheating.

Adhesive Tapes




Tape Applications




Typical Properties

. Total Solids 45-50%Viscosity As per coaters requirementpH 8.5Minimum Application Temperature 20 deg CService Temperature Range Up to 75 deg C

Coated Web Silicone Paper / Silicone PET 70 mic/ 36 ic

Coat weight , Grams / Sq. Mtr. 25 gsm


100 hours

Rolling Ball Tack , mm >250Loop Tack , grams /25 mm 400

Samples are Prepared by direct coating with help of Myer Bar no. 5 and dried for 5minutes at 70 degree C

HARRISONS MALAYALAM LIMITEDRegd.Office: Bristow Road, Willingdon Island,

Cochin - 682 003, India.Tel.: +91 484 2668023. Fax: +91 484 2667485.

Web: www.harrisonsmalayalam.com


003. Latxsive RUB


Specially Developed for Tire Cord

Latxsive Tire Cord , is a solvent free Natural Rubber and Tackifier Resin Emulsion PressureSensitive Adhesive . This Adhesive is compounded especially for coating on Rayon, Nylon or CottonCord for reinforcement in Rubber Tires, Conveyor Belt, V Belts and other Rubber coated Products.This adhesive exhibits, a very good balance of peel adhesion , holding power ( Shear Strength ) ,Rolling Ball Tack , and good ageing resistance. The Viscosity of the Adhesive is preciselycontrolled , to enable or allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar oreven Comma / Reverse Roller coating.

Application : for coating on Rayon, Nylon or Cotton Cord for reinforcement in Rubber Tires,Conveyor Belt, V Belts and other Rubber coated Products

Adhesive Tapes

Suitable for coating on loosely woven Mesh , Specialty Fabrics

Tape Applications

HARRISONS MALAYALAM LIMITEDRegd.Office: Bristow Road, Willingdon Island,




Typical Properties

. Total Solids 55%Viscosity @30degC by Brooke Field RVT SPL 12.20RPM

40-60 poise

pH >8.5Minimum Application TemperatureService Temperature Range -10 to 70 deg C

Coated Web Nylon, Rayon Cord, Mesh

Coat weight , Grams / Sq. Mtr. 10-20

18 Peel Strength , grams/ 25 mm >200Shear Strength.25 mm X 25 mm X 1000 grams

24 hrs

Rolling Ball Tack , mm NALoop Tack , grams /25 mmSamples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5 minutes at 70degree C

HARRISONS MALAYALAM LIMITEDRegd Office: Bristow Road, Willingdon Island,




004. Latxsive SPL-MSKNatural Rubber Latex Based Pressure Sensitive AdhesiveSpecially Developed for Crepe Paper Masking Tape

Latxsive SPL MSK , is a solvent free Natural Rubber and Tackifier Resin Emulsion PressureSensitive Adhesive . This Adhesive is compounded especially for coating on Crepe Paper ,Electrical grade Kraft paper , specialty non tear able Plastic Paper This adhesive exhibits , a verygood balance of peel adhesion , holding power ( Shear Strength ) , Rolling Ball Tack , and goodageing resistance. The Viscosity of the Adhesive is precisely controlled , to enable or allow coatingby Gravure plus Myer bar or Kiss coating plus Myer Bar or even Comma / Reverse Roller coating.

Adhesive Tapes

Tape Applications





Typical Properties

. Total Solids 50-55 %Viscosity @ 30 DegC by BrookeField PVT ,SPL 12.20 RPM

40-60 poise

pH >8.5Minimum Application Temperature -10Service Temperature Range 75 Deg C

Coated Web Crepe PaperCoat weight , Grams / Sq. Mtr. 20-24 gsm

18 Peel Strength , grams/ 25 mm 750Shear Strength.25 mm X 25 mm X 1000 grams

48 hrs

Rolling Ball Tack , mm 10 cmLoop Tack , grams /25 mm 185Samples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C




This product information is presented in good faith and is to the best of ourknowledge , accurate. It is intended to be used as a guide and is not to beconsidered as a specification for products described here, HarrisonsMalayalam Ltd does not guarantee satisfactory results in any application fromreliance upon this information and assumes no liability for any loss ordamage arising out of its use. Harrisons Malayalam Ltdrecommends that the user of our products thoroughly tests themunder end use conditions to assure that they meet therequirements of intended application

005. Latxsive SPL- PET


Specially Developed for Polyester Film Tape

Latxsive SPL PET , is a solvent free Natural Rubber and Tackifier Resin Emulsion PressureSensitive Adhesive . This Adhesive is compounded especially for coating on Polyester Film , AndFabrics Like , Cotton , Nylon , Rayon, Glass Cloth , For Electrical Insulation .This adhesiveexhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) , Rolling BallTack , and good ageing resistance. The Viscosity of the Adhesive is precisely controlled , to enableor allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar or even Comma / ReverseRoller coating.

Adhesive Tapes

Tape Applications




This product information is presented in good faith and is to the best of ourknowledge , accurate. It is intended to be used as a guide and is not to beconsidered as a specification for products described here, HarrisonsMalayalam Ltd does not guarantee satisfactory results in any application fromreliance upon this information and assumes no liability for any loss ordamage arising out of its use. Harrisons Malayalam Ltdrecommends that the user of our products thoroughly tests themunder end use conditions to assure that they meet therequirements of intended application

Typical Properties

. Total Solids 45-50%Viscosity @ 30 DegC , Brookfield PVT SPL12.20 RPM

125-500 poise

pH >8.5Minimum Application Temperature -10 deg CService Temperature Range 75 -120 Deg C

Coated Web Polyester film 25 micCoat weight , Grams / Sq. Mtr. 25-27

18 Peel Strength , grams/ 25 mm >850Shear Strength.25 mm X 25 mm X 1000 grams

>98 hours

Rolling Ball Tack , mm 12 cmLoop Tack , grams /25 mm >200Samples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C





006. Latxsive SPT HT IN


Specially Developed for Surface Protection Tape

Latxsive SPT INDOOR, is a solvent free Natural Rubber and Tackifier Resin EmulsionPressure Sensitive Adhesive . This Adhesive is compounded especially for coating on , Co ExtrudedPoly Ethylene film, PVC Film , BOPP Film , Polyester Film or Electrical Grade Kraft paper .This adhesive exhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) ,Rolling Ball Tack , and good ageing resistance. The Viscosity of the Adhesive is preciselycontrolled , to enable or allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar

Adhesive Tapes

Tape Applications





Typical Properties

. Total Solids 40-45 %Viscosity 125-500 poisepH >8.5Minimum Application Temperature -10 Deg CService Temperature Range 75 Deg C

Coated Web PolyEthylene 35 mic, 70mic, 90 micCoat weight , Grams / Sq. Mtr. 6-8


>2 hours

Rolling Ball Tack , mm 25 cmLoop Tack , grams /25 mmSamples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C





007. Latxsive SPT HT OUT



Latxsive SPT OUTDOOR, is a solvent free Natural Rubber and Tackifier Resin EmulsionPressure Sensitive Adhesive . This Adhesive is compounded especially for coating on , Co ExtrudedPoly Ethylene film, PVC Film , BOPP Film , Polyester Film or Electrical Grade Kraft paper .This adhesive exhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) ,Rolling Ball Tack , and very good Outdoor Resistance , or UV Resistance . The Viscosity of theAdhesive is precisely controlled , to enable or allow coating by Gravure plus Myer bar or Kisscoating plus Myer Bar

Adhesive Tapes

Tape Applications





Typical Properties




>2 hours

Rolling Ball Tack , mm 25 cmLoop Tack , grams /25 mmSamples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C





008. Latxsive SPT LT IN



Latxsive SPT INDOOR, is a solvent free Natural Rubber and Tackifier Resin EmulsionPressure Sensitive Adhesive . This Adhesive is compounded especially for coating on , Co ExtrudedPoly Ethylene film, PVC Film , BOPP Film , Polyester Film or Electrical Grade Kraft paper .This adhesive exhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) ,Rolling Ball Tack , and very good Outdoor Resistance , or UV Resistance . The Viscosity of theAdhesive is precisely controlled , to enable or allow coating by Gravure plus Myer bar or Kisscoating plus Myer Bar

Typical Properties



18 Peel Strength , grams/ 25 mm 40- 80Shear Strength.25 mm X 25 mm X 1000 grams

>2 hours

Rolling Ball Tack , mm OUT OF SCALELoop Tack , grams /25 mmSamples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C





009. Latxsive SPT LT OUT



Latxsive SPT OUTDOOR, is a solvent free Natural Rubber and Tackifier Resin EmulsionPressure Sensitive Adhesive . This Adhesive is compounded especially for coating on , Co ExtrudedPoly Ethylene film, PVC Film , BOPP Film , Polyester Film or Electrical Grade Kraft paper .This adhesive exhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) ,Rolling Ball Tack , and very good Outdoor Resistance , or UV Resistance . The Viscosity of theAdhesive is precisely controlled , to enable or allow coating by Gravure plus Myer bar or Kisscoating plus Myer Bar

Typical Properties



18 Peel Strength , grams/ 25 mm 40- 80Shear Strength.25 mm X 25 mm X 1000 grams

>2 hours

Rolling Ball Tack , mm OUT OF SCALELoop Tack , grams /25 mmSamples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C




010. Latxsive PKGNatural Rubber Latex Based Pressure Sensitive AdhesiveSpecially Developed for Packaging Tape

Latxsive PKG , is a solvent free Natural Rubber and Tackifier Resin Emulsion Pressure SensitiveAdhesive . This Adhesive is compounded especially for coating on BOPP Film, HDPE Film , Kraft <Reinforced Kraft Paper . This adhesive exhibits , a very good balance of peel adhesion , holdingpower ( Shear Strength ) , Rolling Ball Tack , and good ageing resistance. The Viscosity of theAdhesive is precisely controlled , to enable or allow coating by Gravure plus Myer bar or Kisscoating plus Myer Bar .

Application : General Purpose Packaging Tapes based on Films , paper etc.

Adhesive Tapes

Tape Applications




Typical Properties

. Total Solids 50-55 %Viscosity @ 30 DegC by BrookeField PVT ,SPL 12.20 RPM

125-500 poise

pH >8.5Minimum Application Temperature -10Service Temperature Range 75 Deg C

Coated Web BOPP Film, or 40 gsm Kraft PaperCoat weight , Grams / Sq. Mtr. 20-21 gsm

18 Peel Strength , grams/ 25 mm 550Shear Strength.25 mm X 25 mm X 1000 grams

72 hrs

Rolling Ball Tack , mm 15 cmLoop Tack , grams /25 mm 120Samples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5minutes at 70 degree C





011. Latxsive 16


Specially Developed for PVC Insulation Tape

Latxsive 16 , is a solvent free Natural Rubber and Tackifier Resin Emulsion Pressure SensitiveAdhesive . This Adhesive is compounded especially for coating on Semi Plasticized PVC Filmsuitable for General Electrical Insulation Application. The adhesive is formulated to strike a balanceof Peel , Shear and Tack properties. This adhesive has excellent wetting on any Corona treatedplastic film such as PVC, BOPP, PET or Co Extruded PE and exhibits excellent anchorage. Thisadhesive exhibits, a very good balance of peel adhesion , holding power ( Shear Strength ) , RollingBall Tack , and good ageing resistance. The Viscosity of the Adhesive is precisely controlled , toenable or allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar or even Comma /Reverse Roller coating. Latxsive PSA’s , are based on the “go green” movement andenvironmentally friendly . These Adhesives are PVC free, lead free, phthalate free, andmanufactured directly from the Rubber Estate in Kerala , India.

Application : General Purpose Electrical Insulation Tapes based on , films like PVC, PE ,Polyester, or Fabrics like , Cotton, Rayon, Nylon, Acetate Rayon , and even Paper like Electricalgrade Kraft Paper etc.Another Application is Glass Etching Tapes based on PVC Film

dhesive Tapes





Tape Applications

Typical Properties

. Total Solids 50-55 %Viscosity As per requiredpH 9+/- 0.5Minimum Application Temperature 10 deg CService Temperature Range -20 deg C to 75 deg C

Coated Web PVC film 120 micron

Coat weight , Grams / Sq. Mtr. 25 +/- 2


50 hours at 27 deg C

Rolling Ball Tack , mm 250-260Loop Tack , grams /25 mm 380Samples are Prepared by direct coating with help of Myer Bar no. 7 and dried for 5 minutes at 70degree C




Natural Rubber Latex Based Pressure Sensitive AdhesiveSpecially Developed for Heat and Cold Insulation Tape

Latxsive DS , is a solvent free Natural Rubber and Tackifier Resin Emulsion Pressure SensitiveAdhesive . This Adhesive is compounded especially for coating on a variety of Elastomeric Foams ,Tissue Paper, variety of Films, Nov Woven Fabrics, Woven Fabric for variety of HoldingApplications . This is most suited PSA for the Manufacture of Double side Adhesive Coated Tapes.This adhesive exhibits , a very good balance of peel adhesion , holding power ( Shear Strength ) ,Rolling Ball Tack , and good ageing resistance. The Viscosity of the Adhesive is preciselycontrolled , to enable or allow coating by Gravure plus Myer bar or Kiss coating plus Myer Bar oreven Comma / Reverse Roller coating.Latxsive PSA’s , are based on the “go green” movement and environmentally friendly . ThisAdhesive is specially developed for Transfer Coating method. The Adhesive Wet ability , andRheology is specially modified for defect free coating on all silicone coated surfaces.

Application :

Double Sided Adhesive Tapes, are designed for variety of Holding applications ultimateperformance in extreme temperatures. They are used to insulate in cold and hot environments, TheseTapes are used to many types of Holding , mounting applications

Adhesive Tapes

012. Latxsive DS




Tape Applications

Typical Properties

. Total Solids 45-50%Viscosity @ 30 deg C , Brookefield PVT, SPL12.20 RPM

50-60 poise

pH 9.5Minimum Application Temperature 20 deg CService Temperature Range Up to 75 deg C

Coated Web Silicone Paper / Silicone PET 70 mic/ 36 ic

Coat weight , Grams / Sq. Mtr. 25- 30 gsm


100 hours

Rolling Ball Tack , mm >250Loop Tack , grams /25 mm 400

Samples are Prepared by direct coating with help of Myer Bar no. 5 and dried for 5minutes at 70 degree C