1  

Ceramic Heater

Specially Designed For Solar Water Heater

Suitable For: A: Instant Hot Water Tap, Traditional Electrical Water Heater, Storage Water Heater, Boiling Water Heater, Water Dispenser, Coffee Machine, Beverage Dispenser and House/Apartment/Hotel Water Heating Solution.

B: Industry Boiler, Electric Heating, Electrolyte Heating Source etc.

Features: 1. Guaranteed Safety: Heating wire will be oxidized immediately when the ceramic is broken. producing leakage current much lower than body safety value: ( 10 mA) 2. High Energy Efficiency: With high thermal conductivity ceramic, higher energy efficiency was achieved compared with traditional heater. 3. Corrosion Resisting: No need for corrosive-resistant coating, silicon nitride ceramic has excellent anti-acid/alkali properties, never rust. 4. Fast Circulating: High power was concentrated in a small ceramic heater, and circulating of water in the tank was accelerated, results in uniform temperature distribution. 5. Anti Incrustation Scale:

  2  

The ceramic surface was well polished, avoiding scale adhesion. 6. Intelligent temperature Control: Integrated temperature control device was used to control the heater according to water-temperature automatically. No intervention needed.Models:

Item No. Heating Size Install Hole Power Joint Connector

A1 85*17*4mm 17*4mm 2000-2500W 1” 1.25” 1.5”

A2 85*17*4mm 17*4mm 200-800W 1” 1.25” 1.5”

B1 73*30*4mm 30*4mm 2500-3500W 1” 1.25” 1.5”

C1 60*17*4mm 17*4mm 1500-2000W 1” 1.25” 1.5”

D1 102*24*4mm 24*4mm 3000-3800W 1” 1.25” 1.5”

Technical Parameters:

Rated Voltage AC 220/110V 50/60HZ

Rated Power: 200-3800W

Insulation Electric Strength: No breakdown in 60s under 2500V/50HZ

Leakage Current: < 0.025 mA in normal condition, < 10mA after breakdown

Use of media: Water, Acid and alkali solution, Air, Oils, Organic solvents, Gas, etc.

Volume Density 3.2-3.3g/cm3

Fracture Toughness 5.0-8.0 MPa*m 1/2

Room Temperature Strength Resistance > 900MPa

High Temperature Strength Resistance > 700MPa

Vickers Hardness 15-20GPa

Relative Dielectric Constant 6-7

Volume Resistivity 10^14 Ω·cm Thermal Conductivity 20-50W(m*K)

Thermal Expansion Coefficient 3.0*10-6/K