Description :
.Features and applications :
This film complies with the EC and FDA food contact regulations. Detailed documentation is available on your request.
BOPET FILMS
POLIKAP
http://www.polinas.com
* PVdC coated side is heat sealable
* Excellent aroma, moisture and oxygen barrier
Available gauge(s) (µm) : 12,14
PSA
Properties Unit Technical Values Test Method
kg/mm² TD
% TD
F: Front B: Back *130˚C , 1 sn, 1atm
Thickness µm 12 14 ASTM D 2673
Yield m2/kg 59,5 51 ASTM D 2673
Elongation % MD 120 120 ASTM D 882
Tensile strength at break kg/mm² MD 22 22 ASTM D 882
humidity during pasteurization after lamination (PVdC side should be laminated).
1. This information is the best currently available on product and it is subject to revision as additional knowledge and experienceis gained.
2. The results obtained and the above properties refer to average value of laboratory tests. Therefore, such results have only to be considered as an indicative general guide to material properties and not as an implied guarantee that the product actually has said properties and/or a warranty of fitness for a particular purposes and/or suggestion for infringement of any existing patents.
3. Due to many factors which may affect customer production process, including but not limited by different equipments and techniques used, PSA film must be qualified before being used in any application.
for PVdC
Dimensional stability % MD =<1,5 =<1,5 ASTM D 1204
% TD
Haze % =<5 =<5 ASTM D 1003
Heat seal strength* gr/25mm FF =>200 =>200 POLINAS
PSA needs to be stocked in a closed warehouse and preserved from the light. Polinas will not acceptany responsibilty for material older than 1 year from the delivery
Polinas PSA is a bi-axially oriented polyester (BOPET) film with one side coated with PVdC water latex
* Designed for lamination and printing with inks
* Offers a good resistance to heat and
OTR (23C, 0%RH) cm3/m2/24h =<8 =<8 ASTM D 3985
WVTR (38C, 90%RH) gr/m2/24h =<7 =<7 ASTM F 1249
Date : 14.04.2017