Nuclear Fuels and Materials - 151-2017-00L
Manuel A. Pouchon :: Head of LNM :: Paul Scherrer Institut
Master of Nuclear Engineering ‐ Spring Semester 2016
Lecture 4: Cladding, ….
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 2/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 3/86
Pellet
FuelCladding
Fuel tube
Fuel rod Assembly
Introduction – From the pellet to the assembly
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 4/86
PWR(pressurized water reactor)
BWR(boiling water reactor)
Introduction – Thermal reactors (selection)
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 5/86
Rods• Zircaloy tube filled with U(Pu)O2 tablets and helium • cylindrical rods put into bundles
PWR• 179-264 fuel rods per fuel bundle (14×14 to 17×17)• 121 to 193 fuel bundles• bundles are about 4 meters long
BWR• Similar to above, but …• canned• 91, 92, or 96 fuel rods per assembly• 368-800 assemblies
Introduction – Thermal reactors – assembly II
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 6/86
BWR
PWR
Introduction – Thermal reactors – assembly
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 7/86
BWR PWR
Cladding Thickness (mm) 0.813 0.57-0.65
Cladding Zircaloy 2 Zircaloy-4
Advanced Cladding Barrier Zircaloy 2 ZIRLO, M5, low-Sn Zry-4
Grid (#fuel locations) 8 x 8 square (62) 17 x 17 (264) or 16 x 16 (236)
Pitch (mm) 16.2 12.6
Cladding outer diameter (mm) 12.7 9.5-9.7
Height (m) 4.1 4.0-4.1
Active Fuel height (m) 3.81 3.6-3.8
Fuel enrichment (wt. %) 2.8 3.3 (now almost 5%)
Pellet diameter (mm) 10.4 8.2
Pellet Height (mm) 10.4 9.5-13.0
Inlet Temperature (ºC) 278 292-301
Outlet Temperature (ºC) 288 325-332
Linear Power (kW/m) average 19 16-17.8
Linear Power (kW/m) max 44 41-42.7
Number of assemblies 748 193-241
Reactivity Control Rods Cruciform Rod cluster
Absorber material B4C AgInCd or B4Chttp
://w
ww
2.m
ne.p
su.e
du/m
otta
/Cha
pter
s/B
ook%
20A
ug%
2020
11/
Cha
pter
17_Z
rAllo
ys.p
dfht
tp://
ww
w2.
mne
.psu
.edu
/mot
ta/C
hapt
ers/
Boo
k%20
Aug
%20
2011
/C
hapt
er17
_ZrA
lloys
Fuel Assembly Characteristics for BWR and PWR
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 8/86
Two CANDU fuel bundles: Each about 50 cm in length and 10 cm in diameter, and generating about 1 GWh of electricity during its time in the reactor. Photo courtesy of Atomic Energy of Canada Limited.
CANDU
Introduction – Thermal Reactors –Special systems
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 9/86
(V)HTR
Cladding• porous carbon buffer layer • pyrolytic carbon (PyC), • SiC • PyC
Introduction – Thermal Reactors –Special systems
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 10/86
Liquid metal (sodium) cooled fast breeder reactor (LMFBR / SFR)
Introduction – Fast reactors (selection)
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 11/86
Joyo – Oarai / Japan
Introduction – Fast reactors – SFR Assembly
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 12/86
GFR
http://www.sckcen.be/en/Media/Images/Our-Research/ANS/IrrDemo-Fuel
Cladding: SiCf/SiC
MT Aerospace AG, Augsburg
Introduction – Fast reactors – Special Systems
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 13/86
• Purpose: Enclosure of fuel pellets
• Mechanical stability(under temperature, pressure and irradiation)
• Chemical stability in the special environment(water, pressure, temperature, radiation)
• Small capture cross section for neutrons (especially thermal neutrons)
• Available in large quantities, comparable cheap(BWR80t, PWR 40t)
Requirements
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 14/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 15/86
• Zircaloy: Zirconium based alloys (thermal reactors)
• Steel / ODS Steel (fast reactors, thermal reactors)
• Aluminum and beryllium alloys(low power pool type reactors)
• Magnesium with small amount of aluminum and other metals (Magnox: Magnesium non-oxidizing)
• SiC: Fiber-reinforced:(Gas cooled fast reactor, today also in discussion for LWR)
Materials for Cladding
westinghouse
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 16/86
• First test reactors (mild environment, pool-type, i.e. water < 100°C ): Aluminum and beryllium alloys were used, due to their low thermal neutron capture cross section.
• First nuclear power reactors (submarine propulsion): higher efficiency. Zirconium as possible candidate (very low thermal neutron capture cross section): poor ductility and corrosion resistance, Hf to be separated. Therefore stainless steel
• Strong development after WW II fro nuclear submarine program: Improved Hf separation process, industrial production procedures. Tests with binary and ternary alloys
History of Zircaloy - 1
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 17/86
Base Metal UTS (MPa) Macroscopic neutron capture Cross Section (cm¯¹)
Relative neutron absorption for a given design stress
Zirconium 900 0.01 1
Iron 1100 0.17 4
Nickel 1100 0.31 25
Titanium 1000 0.26 28
Aluminum 90 0.014 14
Magnesium 90 0.005 5
Beryllium 180-350 0.001 0.25-5
Properties of metals
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 18/86
• Tests with binary and ternary alloys:
• Zircaloy-1: Zr - 2.5%Sn:increased corrosion resistance, mitigated nitrogen content
• Zircaloy-2: Zr - 1.45%Sn, 0.1%Cr, 0.135%Fe, 0.055%Ni, 0.01%Hf [*]:accidental contamination of Zircalloy-1 with stainless steel lead to an alloy with good corrosion resistance
• Zircaloy-3: was a low tin variant of Zircaloy-2
• Zircaloy-4: Zr - 1.45%Sn, 0.1%Cr, 0.21%Fe, 0.01%Hf [*] :a Ni-free variant fo Zircaloy-2
• Former Soviet Union & Canada:Zr - Nb binary system:Today:
Zr-2.5 in CANDU (HWR) and RBMK Zr-1Nb/(Zirlo)/M5 in PWR
[*] http://iriaxp.iri.tudelft.nl/~leege/SCALE44/stdcmp.pdf
History of Zircaloy - 2
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 19/86
• Earth‘s crust: 0.002 wt% Zr (more than Cu or Zn)
• Zircon (ZrSiO4) is most important source Tetragonal ditetragonal dipyramidal Hyacinth (reddish gem, already known in
antiquity) is a zircon with impurities Fe2O3 / CaO / Hf impurities
• Baddeleyite (ZrO2) is another important source Monoclinic zirconoxide with impurities and
only 90-95% ZrO2
Zirconium Ressources
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 20/86
• Name, symbol, number: zirconium, Zr, 40• Element category: transition metal• Melting point 2128 K / 1855 °C• Crystal lattice: < 862 °C: hexagonal, hpd (α) ─ density: 6.5g·cm−3
> 862 °C: cubic body centered, cbc (β) ─ density: 6.5g·cm−3
• Thermal expansion• α-Zr parallel to c-axis: 6.4·10-6 K-1
• α-Zr perpendicular to c-axis: 5.6·10-6 K-1
• β-Zr parallel to c-axis: 9.7·10-6 K-1c-axisα
Zirconium – Physical Properties
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 21/86
• Forms dense layers of stable oxides with high melting point and well bond to the metal
• In most environments more stable than titanium and stainless steels. Examples
Sulphuric acid: in problematic concentration range of 40-60% one of the best structural materials
Hydrochloric acid: stable at boiling temperature up to an acid concentration of some 37 %
Nitric acid: Outstanding stability fo all concentrations and temperatures
Zirconium – Chemical Properties
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 22/86
• Oxidation behavior : Zr + 2H2O = ZrO2 + 2H2 + 140 kCal/mol
Time to consume a 0 .087’’ (2.2 mm) thick plate as a function of temperature
Bostrom, W.A., THE HIGH TEMPERATURE OXIDATION OF ZIRCALOY IN WATER, (1957) OSTI ID: 4360187
(140 kCal = 585.76 kJ)
Zirconium – Chemical Properties
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 23/86
• What is the oxidation energy in a• BWR (80t Zircaloy)• PWR (40t Zircaloy) • How much hydrogen is produced?
• What is thermal power of the oxidation reaction of a 1 mm cladding at a temperature of 1450 °C ?
• BWR
Zr: 91.224 g·mol−1
H: 1.00794 g·mol−10.08988 g/L
R = 13.9·P1/6·exp(−1.47/kBT)
solution
Zirconium – Chemical Properties
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 24/86
Remark
Use as metal: only 5% of the zirconium ores worldwide (rest is used as oxides, e.g. ZrO2 as high temperature ceramic, …..)
• Nuclear application
• Chemical industry (in corrosive environment)
• As alloying element in steels
• Application for medical technique and surgery
• Supra conducting magnets (in combination with niobium)
Zirconium – Use
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 25/86
Hexagonal structure• Less gliding planes than cubic lattice• Distinct formation of
twin boundaries Complex behavior under
plastic deformation Strong anisotropy Strong formation
of structure
Thermo-mechanical fabrication process is essential for the evolution the microstructure, the mechanical properties and the corrosion resistance
Hexagonal lattice..ABABCBCBCBCBABA..(= Stacking fault)
= Twin
Zirconium – Mechanical Properties
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 26/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 27/86
Chloration:Zircon (ZrSiO4, ZrO2, HfO2) + carbon + chlorine: Chloration (@ 1200 °C)
ZrO2(+ SiO2+HfO2) + 2C + 2Cl → ZrCl4(+SiCl4↑+HfCl4)+2CO
Zr/Hf separation by chloride distillations process (@ 350 °C in vacuum)
Hf-free ZrCl4 is compacted and subjected to the Kroll reduction:
ZrCl4+Mg → Zr, Mg + MgCl2 (@ 850 °C in vacuum)
Excess Mg is separated by vacuum distillation 1000 °C → zirconium sponge
Zirconium/Cladding – Fabrication I
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 28/86
Zirconium sponge:
Compaction to electrode-part:
K.Baur, 2002
Zirconium/Cladding – Fabrication II
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 29/86
Welding of electrode parts to full electrode – mixing with scrap and alloying elements
Electrode of company ABSS
K.Baur, 2002
Zirconium/Cladding – Fabrication III
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 30/86
K.Baur, 2002
consumable electrode
water cooled copper chill
electric arc
ingot
Melting 3 times in a consumable electrode vacuum arc furnace
Ingot of CEZUS
Zirconium/Cladding – Fabrication IV
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 31/86
http://www2.mne.psu.edu/motta/Chapters/Book%20Aug%202011/Chapter17_ZrAlloys.pdf
Zircaloy Tubing Fabrication Process
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 32/86
Forging to a rod (in β and α-region) then temperature treatment for microstructure.
CEZUS
K. Baur, 2002
Zirconium/Cladding – Fabrication V
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 33/86
K. Baur, 2002
Drilling of central hole, then hot extrusion:
Zirconium/Cladding – Fabrication VI
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 34/86
http://www.smst-tubes.com/
Zirconium/Cladding – Fabrication VII
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 35/86
K. Baur, 2002Zircaloy tubes before final
pilgering step
Zirconium/Cladding – Fabrication VIII
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 36/86
The extruded tube is then cold pilgered
K. Baur, 2002
Zirconium/Cladding – Fabrication XIV
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 37/86
http://www.smst-tubes.com/en/products-services/production/cold-pilgering-and-cold-drawing/
Zirconium/Cladding – Fabrication XV
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 38/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 39/86
Radial orientation of c-axis due to high reduction in diameter (beneficial for later hydride precipitation):
K. Baur, 2002
Zircaloy Cladding – Texture I
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 40/86
Radial orientation of c-axis due to high reduction in diameter (beneficial for later hydride precipitation):
K. Baur, 2002
Zircaloy Cladding – Texture II
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 41/86
• Oxygen (800-1600 ppm): stabilizes the α-phase (solid solution), increases yield strength
• Tin (0.5-1.8 wt%) stabilizes the α-phase (solid solution), mitigates nitrogen impurities, increases slightly yield strength
• Iron, chromium and nickel: stabilizes the β-phase (solid solution in β-phase, precipitates in α-phase), increase corrosion resistance by formation of second phase particles (SPP‘s)
• Niobium (0-2.5 wt%): stabilizes the β-phase precipitates in α-phase), increases yield strength and corrosion resistance
Zircaloy – Alloying elements
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 42/86
wt% Zr Sn Fe Cr Ni Nb O
Zircaloy-2 Bal. 1.2-1.7 0.07-0.2 0.05-0.15 0.03-0.08 - 0.1-0.14
Zircaloy-4 Bal. 1.2-1.7 0.18-0.24 0.07-0.13 0.007 max - 0.1-0.14
ZIRLO Bal. 1.0 0.1 - - 1 ca 0.1
M5 Bal. - 0.015-0.006 - - 0.8-1.2 0.09-0.12
Zr-2.5Nb Bal. 0.05 max 0.15 max 0.02 max 0.007 max 2.4-2.8 0.09-0.13
Zircaloy – Some Alloys
Zirconium alloys used in nuclear reactor
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 43/86
Zircaloy-2 Zircaloy-4 Zr -2.5Nb
Sn 1.20 - 1.70 1.20 - 1.70
Fe 0.07 - 0.20 0.18 - 0.24
Cr 0.05 - 0.15 0.07 - 0.13
Ni 0.03 - 0.08 -
Nb 2.40 - 2.80
O 0.09 - 0.13
Zircaloy – Some Alloys
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 44/86
Classical:• Zircaloy-2: for BWR application, an alloy with about 1.5% Sn and 0.3% Fe+Cr+Ni)
• Zircaloy-4: with a composition similar to Zircaloy-2 but free of Ni and with lower tendency of hydrogen pick-up, for PWR application
• USSR binary Zr-Nb alloy 1%Nb adn 2.5% Nb were selected for the Soviet PWR and HPWRs
Recent developments:• Zircaloy-2 types with optimized microstructure in BWRs
• Optimized Zircaloy-4 in microstructure and material chemistry)
• Modified Zircaloy-4 a low Sn Zircaloy with increased Fe+Cr)
• ZIRLO (1% Sn, 1%Nb and 0.1% Fe)
• M5 (1% Nb) are used for fuel elements in western PWR‘s
• DUPLEX-ELS – Zircaloy tube having an outer layer with increased Fe+Cr and decreased Sn
Zircaloy – Important Alloys
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 45/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 46/86
• The ceramic fuel has a lower thermal expansion coefficient but runs at higher temperatures.
• At elevated burn-ups the fuel might give a load on the cladding axially and in circumference.
Radial temperature distribution in a pin
PCMI (Pellet Cladding Mechanical Interaction) I
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 47/86
•Which are the relevant processes for the PCMI?
•Try to draw the pellet-cladding gap evolution as function of time. When the gap closes try to represent the influence to the cladding.
solution
PCMI - Question
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 48/86
Radial expansion of pellets might lead to long axial cracks
PCMI II
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 49/86
PCMI III – Pellet cracking during irradiation
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 50/86
BeforeIrradiation
AfterIrradiation
• Pellet swelling• Pellet bambooing• Pellet cracking• PCMI• Iodine release
B.R.T. Frost (Ed), 1994, Nuclear Materials, Vol. 10B, Materials Science and Technology, VCH, p.43
PCMI IV – Pellet cracking during irradiation
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 51/86
PCMI V – Increase of diameter
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 52/86
Aggressive environment:
Iodine
Tensile stress:Power Ramp
Sensitive Material:Zry-2, Zry-4
SCC
ANT international
SCC:stress corrosion cracking
PCI (Pellet Cladding (chemical) Interaction) I: SCC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 53/86
AN
T in
tern
atio
nal
PCI II: Stress concentration at cracks
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 54/86
Sofer G.A. et al. Proc. ANS Top Meeting LWR Fuel Performance, Williamsburg VA, p. 41-53, Apr. 17-20, 1988
PCI III: Example
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 55/86
More cracks in the pellet (new development)
PCI IV: Countermeasure
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 56/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 57/86
• Debris fretting is the most common failure cause for leakers • Debris are caught in the spacer
Westinghouse Atom
Debris fretting I
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 58/86
Taken from filter of feed water pump
Debris fretting II: Typical Debris
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 59/86
Debris fretting mark in spacer position 7
Hydride plunge between spacer 1 and 2
Debris fretting often cause secondary failures ….
Westinghouse A
tomDebris fretting III: Secondary Failures
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 60/86
Severe circumferential break above
… sometimes ending with the total destruction of the fuel rod.
Westinghouse A
tom
Debris fretting mark in spacer position 6
Debris fretting III: Secondary Failures
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 61/86
Water ingress causes the oxidation of the inner cladding surface. The oxide protects the surface against H-uptake. At a certain distance to the leak, the protection is diminishing and hydride lenses can be developed due to massive hydrogen uptake
Debris fretting IV: Consequences of Fretting Leaks
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 62/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 63/86
• Hydrogen is taken up during normal corrosion of the cladding (pick-up fraction).
• When the solubility limit is exceeded, hydrogen precipitated as zirconium hydrides
• Zirconium hydride has a considerable high yield strength, but is brittle.
• Zirconium hydrides are normally distributed over the whole cladding thickness (PWR) and form lines due to the texture
• In BWRs we can often observe a “hydride rim“ of 5 to 10 μm in thickness at the outer cladding surface
• Hydrogen can diffuse to the cold spots (sites of oxide spalling) and form hydride lenses
Hydrides I
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 64/86
• terminal solid solubility at dissolution (TSSD)
• terminal solid solubility at precipitation (TSSP)
McMinn et al., 12th Symp. On Zirconium in the Nuclear Industry, 2000
Hydrides II: solubility limits. Irradiation effects irradiated
non‐irradiated
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 65/86
Distribution due to texture
Hydrides III: “Normal” hydride distribution
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 66/86
• Lately cracks have been observed in high burnup rods going from outside to inside, i.e. no PCI
• The crack propagation is connected with the formation of hydrides in front of the crack tip
The mechanism is described as follows: Hydride is diffusing to lattice under high strain, i.e. to the crack tip. At the crack tip, the solubility limit is exceeded and the hydrides are formed perpendicular to the maximum stress. The crack can now propagate along the hydride. New hydride will diffuse to the new crack tip.
Hydrides IV: Delayed Hydride Cracking - DHC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 67/86
The crack propagation is connected with the formation of hydrides in front of the crack tip
D. Rogers, AECL/Chalk River
Hydrides V: Delayed Hydride Cracking - DHC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 68/86
A. Alam / PSI
Hydrides VI: Delayed Hydride Cracking - DHC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 69/86
• Operational transients can support DHC.
• During a higher power period, more hydrides are dissolved. Additionally higher cladding strain might be present due to PCMI.
• A larger international research projects.
Hydrides VII: DHC and operational transients
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 70/86
• Modern alloys with high burnup have taken up 300 ppm (BWR), resp. some 600 ppm (PWR) hydrogen, i.e. far above the solubility limit.
• When transported to the dry storage, the cladding can reach up to 400 °C. At this temperature, hydrides are dissolved. During the subsequent cooling, the hydrides precipitate. If the (circumferential) stress is high enough, they will be radially oriented. If cracks are present, this might cause DHC and lead to rod failure
• This has to be excluded by limitation in stress and max. temperature. example from the lab
Hydrides VIII: DHC and dry storage
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 71/86
Neutron irradiation effects the atom-scale arrangement of the elements in each zirconium alloy
For 50 MWd/kgU, each atom in the lattice has been displaced 20 times (20 dpa) in average.
Consequences:
• Enhances diffusion rates
• Creation of small dislocations, loop dislocation
• Dissolution of SPP‘s
• Solubility changed
• Composition of alloy matrix changed
Irradiation damage I: Embrittlement
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 72/86
o INTRODUCTION TO CLADDING MATERIALS REACTOR / ASSEMBLY / FUEL PIN / CLADDING / PELLET – ADVANCED SYST. REQUIREMENTS
MATERIAL
• ZIRCONIUM / OTHERS
HISTORY OF ZIRCALOY
ZIRCONIUM PROPERTIES
PRODUCTION OF ZIRCONIUM AND CLADDING
TEXTURE, ALLOYING ELEMENTS, ZIRCALOY, …
o POTENTIAL FAILURE MECHANISMS FOR CLADDING MATERIALS PCMI AND PCI/SCC FRETTING
HYDRIDES
IRRADIATION EMBRITTLEMENT
GROWTH AND CREEP
TOC
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 73/86
Every neutron “shot into” the metal matrix cause local amorphization of the crystal structure. Upon recrystallization, interstitials and vacancies are produced.
Lem
aign
an a
n M
otta
, 199
4
Loss of ductilityHardening
Irradiation damage II: Formation of dislocations
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 74/86
• Irradiation growth in the change in shape of a solid at constant volume that occurs during irradiation in absence of stress
• Growth occurs in solids with crystallographic anisotropy; e.g. in orthorhombic α-uranium and hcp α-zirconium; it does not occur in cubic materials such as Fe of steel
• In addition to crystal anisotropy, macroscopic anisotropy (texture) is necessary for growth. The orientation of grains(crystallites) in a polycrystalline specimen can not be random but must be anisotropic as well
• Texture results from the fabrication process
Irradiation damage III: Growth
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 75/86
Crystallographic anisotropy:
fcc structures:(isotropic, no growth)
α-uranium:• elongates along b• shrinks along a• unchanged along c
α-Zr:• elongates along a• shrinks along ca
Irradiation damage IV: Growth
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 76/86
Irradiation damage V: Growth
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 77/86
For Zircaloy: • expansion along <a>-direction• contraction along <c>-direction
For Zircaloy cladding
with a radial basal plane
texture:
• wall thickness decreasing,
• axial length (and diameter) increasing.
For Zircaloy cladding
with a radial basal plane
texture:
• wall thickness decreasing,
• axial length (and diameter) increasing.
Lem
aign
anan
Mot
ta,
1994
CW: cold-worked stress-relieved
RX: recristallized alloy
CW: cold-worked stress-relieved
RX: recristallized alloy
Irradiation damage VI: Growth
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 78/86
• Rod length growth is limited due to the assembly design
• Asymmetric irradiation might lead to asymmetric length growth might lead to bowing
• Also relevant for fuel channels (BWR)
Irradiation damage VII: Growth
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 79/86
• Creep occurs at elevated temperatures. It is a diffusion controlled deformation under stresses lower than the yield stress
• Irradiation creep is the additional contribution of irritation to the creep behavior
• The irradiation affects both the primary and the secondary creep; creep rate is increased in proportion to the dose rate
Lemaignan and Motta, 1994
Irradiation damage VIII: Creep
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 80/86
U.S. LWR Fuel Failure Rates / Total power:101 GWe
Failures
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 81/86
Appendix: Phase Diagram: Zr-Sn
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 82/86
Appendix: Phase Diagram: Zr-Cr
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 83/86
Appendix: Phase Diagram: Zr-Fe
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 84/86
Appendix: Phase Diagram: Ni-Zr
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 85/86
Appendix: Phase Diagram: Zr-O
Nuclear Fuels and Materials - 151-2017-00L ⌸ Lecture 4 - Page 86/86
Appendix: Phase diagram: Zr-H