1
Hybrid Polymer Electrolytes for Use in Secondary Lithium
Ion Batteries
Anisha T. Joenathan
G410 Senior Thesis
Spring, 2014
Research Advisor: Lyudmila Bronstein
2
Abstract
In this work, we focused on improving ionic conductivity and transference
numbers by adding ionic liquids (ILs) to polymer electrolytes (PEs) containing organic-
inorganic nanoparticles (OINs) formed in situ within a salt-in-poly(ethylene glycols)
(PEG) material. We also studied the effects of various molecular weight PEGs as bases
for these hybrid polymer electrolytes (HPEs), as well as the effects of different ion
sources on ionic conductivity. Scanning transmission electron microscopy (STEM),
differential scanning calorimetry (DSC), and conductivity measurements were used to
study and characterize the HPEs. The addition of ionic liquids, specifically1-Butyl-3-
methylimidazolium trifluoromethanosulfonate (IL2), resulted in an enhancement of
conductivity by over two orders of magnitude. To study the effect of molecular weight of
PEG, 400, 600, 1000, and 2000 Da PEG samples were used in the syntheses of HPEs.
The results showed that the highest conductivity was achieved using 400 Da PEG. In
another series of experiments, lithium trifluoromethanosulfonate (LiTf), the lithium salt
used regularly, was replaced with lithium bix(oxalate)borate (LiBOB). Conductivity
measurements showed that the samples containing LiBOB display lower ionic
conductivity. On the other hand, replacement of LiTf with NaTf allowed us to achieve
similar conductivity showing promise for inexpensive sodium ion batteries.
3
Introduction
In recent years, lithium ion batteries have gained considerable attention, mostly as
a result of efforts to miniaturize devices, because of their advantageous properties as
compared to traditional batteries. Lithium has the lightest weight, highest voltage, and
greatest energy density of all metals making it the most sensible metal ion source for use
in secondary batteries.1 A typical commercial lithium ion battery system contains a
carbonaceous anode, an organic electrolyte that acts as an ionic path between electrodes
and separates the two electrode materials, and a transition metal oxide cathode.1
However, there are disadvantages of using liquid organic electrolytes; specifically
flammability, due to the reactivity of metallic lithium with electrolyte solution, as well as
their limited battery life, and temperature sensitivity.2, 3 Because of these issues, solid
polymer electrolytes (SPEs) have drawn interest due to their superior safety and utility. In
order for these polymer electrolytes to become viable alternatives to liquid organic
electrolytes however, the challenges that must be overcome include, but are not limited
to, low ionic conductivity, low lithium transference numbers, low capacity and
insufficient power density.4 Polymer electrolytes in their most simple form, are a
polymer coupled with a lithium salt.5, 6 In this research, the issues of low ionic
conductivity and low lithium transference numbers were addressed. Hybrid polymer
electrolytes (HPEs), PEs containing ionic liquids, have been synthesized and studied in
order to determine what additional chemicals components yield more desirable
electrochemical properties. We studied these using two Li salts, specifically lithium
trifluoromethanosulfonate (LiTf) and lithium bis(oxalate)borate (LiBOB), as lithium ion
sources in the synthesis of HPEs for use as a viable alternative energy source.
4
Although lithium ions display many favorable properties, its supplies are limited
and costly.7 Due to the low abundance of elemental lithium in nature, sodium in contrast
has a high availability and it has gained interest as a lower-cost alternative ion source, in
order to produce the most cost-effective ion-batteries. Thus, sodium
trifluoromethanosulfonate (NaTf) was explored as a sodium ion source in these HPEs.
The benefits of using PEs based on poly(ethylene glycol) (PEGs) include low
cost, longer shelf life, non-flammability, longer exploitation life, and its low glass
transition temperature, which allows lithium ions to remain mobile through the
electrolyte at the sub-freezing temperatures.8 Although PEG-based PEs have many
advantageous properties, they tend to undergo crystallization, thereby disturbing cation
transference, and decreasing ionic conductivity. The crystallization of PEGs can be
suppressed through a variety of methods which include cross-linking, polymer grafting,
polymer blending, and the introduction of organic/inorganic fillers.9-11
It is known that in PEG-based SPEs, anions can form ion pairs of different
compositions, which results in lowered conductivity and lower lithium transference
numbers. With respect to these SPEs application in batteries, these aggregations are
particularly disadvantageous, because as a result, more energy, time, and electrochemical
potential would then be required to recharge the battery.12 In previous papers we reported
enhancement of conductivity for SPEs that contained aluminosilicate or silicate organic-
inorganic nanoparticles (OINs), formed in situ within PEG compared to other composite
SPEs. The incorporation of the OINs into the polymetric matrix should result in not only
increased conductivity due to suppression of crystallization, but also increased
transference numbers if anion movement is impeded. These OINs were made from (3-
5
glycidoxypropyl)trimethoxysilane (GLYMO), tetramethyl orthosilicate (TMOS), and
aluminum (tri-sec-butoxide) (AB) in situ allowing fresh OINs/PEG-LiTf interfaces. AB
acts as a catalyst of epoxy group polymerization in GLYMO, allowing for its cross-
linking with terminal hydroxyl groups in PEG and leading to the formation of a network.
In the preceding research, with the incorporation of the OINs in the SPEs, the Li
transference numbers were significantly increased from 0.3-0.5 in pure PEG-LiTf to 0.6-
0.8 with OINs. In order to increase the Li transference numbers further, the introduction
of a stronger Lewis acid was proposed in order to more strongly interact with anions and
thus reduce the migration of anions. 13, 14 It was demonstrated that through the
introduction of triethyl borate (TEB), a Lewis acid, into the OINs, anion-trapping
tricoordinate boron species were formed, further increasing lithium ion transference
numbers and lesser so, ionic conductivity. Scheme 1 displays the SPE based on PEG,
LiTf and TEB-modified OINs and how they are believed to provide a cross-linked
polymeric matrix.
6
Figure 1. Schematic representation of SPE containing boron species.
Next, to increase ionic conductivity and Li ion mobility, ionic liquids were
introduced, which might behave as a medium the lithium ion movement within the
sample. Ionic liquids (ILs) have recently gained attention due to their various
applications, especially with respect to “green” technology. ILs are molten salts that are
7
composed solely from anions and cations (often bulky ones) and melt below
100-150 °C.15 The main advantages of using ILs in batteries are their large
electrochemical windows, nonvolatility, higher conductivity compared to SPEs, large
operation range of temperatures, and non-flammability.16 We explored the addition of
three different ionic liquids 1-Butyl-3-methylimidazolium tetrafluoroborate (IL1), 1-
Butyl-3-methylimidazolium trifluoromethanosulfonate (IL2), and 1-Ethyl-3-
methylimidazolium trifluoromethanosulfonate (IL3), in various amounts to see the effects
on our samples. The structures are displayed in Figure 2.
Figure 2. Chemical structures of ionic liquids incorporated into polymer electrolytes.
To observe the effects of the chain length of the PEG, samples were synthesized
using 400, 600, 1000, and 2000 Da PEG. The difference in chain length was expected to
affect the structure of the cross-linked polymeric matrix, and thus affect the various
properties of the samples, such as ionic conductivity.
IL1: 1-Butyl-3-methylimidazolium
tetrafluoroborate
IL2: 1-Butyl-3-methylimidazolium trifluoromethanosulfonate
IL3: 1-Ethyl-3-methylimidazolium
trifluoromethanosulfonate
8
Experimental
I. Materials
Poly(ethylene glycol) (PEG) with molecular weights of 400, 600, 1000, and 2000
Daltons were obtained from Aldrich and were not further modified before use. Lithium
trifluoremethanosulfonate (LiTf) (96%), lithium bis(oxalato)borate (LiBOB), sodium
trifluoromethanosulfonate (NaTf), tetrahydrofuran (THF) (≥99.9%), aluminum-tri-sec-
butoxide (AB) (97%), (3-glycidyloxypropyl)trimethoxysilane (GLYMO) (≥98%),
tetramethyl orthosilicate (TMOS) (≥99%), triethyl borate (TEB) (99%), 1-Butyl-3-
methylimidazolium tetrafluoroborate (IL1), 1-Butyl-3-methylimidazolium
trifluoromethanosulfonate (IL2), and 1-Ethyl-3-methylimidazolium
trifluoromethanosulfonate (IL3) were all purchased from Aldrich and used without
further purification. Chloroform (100%) was purchased from Mallinckrodt and used as
received.
II. Synthetic Procedures
i. Synthesis of HPEs with 55% OIN and 10% TEB
Synthesis of HPEs based on poly(ethylene glycol) (PEG) and OINs was carried
out by a procedure modified somewhat from that described in ref 17. In a standard
procedure, 0.8 g of PEG (0.091 mmol) in 5 mL of chloroform was mixed with 0.2 g (1.28
mmol) of lithium triflate in 5 mL of THF. After 1 hour stirring at room temperature, the
solution was put aside. The inorganic part of the composite was prepared by a sol-gel
reaction of a mixture of GLYMO with TMOS in a molar ratio of 4:1, with aluminum-tri-
sec-butoxide used as a catalyst. The weighed vial with a stir bar was filled with 2.337 g
(9.88 mmol) of GLYMO, 0.426 g (2.81 mmol) of TMOS, and 0.04 g (0.16 mmol) of AB.
9
Hydrolysis was initiated by addition of 15 % (0.12 mL) of all calculated water containing
HCl (0.01 N solution). After 15 minutes of stirring in an ice bath at 0°C , it was stirred
for 15 more minutes at room temperature. The reaction mixture was then charged with
0.64 mL of 0.01 N HCl solution and stirred for 40 minutes at room temperature. Then
the reaction temperature was raised to 50°C, the vial was opened and stirring was
maintained for 15 minutes. After weighing the vial, the calculated amount of the
precondensed silicate sol was added to the solution containing PEG and Li salt, along
with the calculated amount of IL and stirred for 1 hour at room temperature. The amount
of OIN added was determined by the desired ratio of inorganic component to PEG-LiTf,
and was based on a 55 wt. % OIN content in HPE. The desired amount of IL was
calculated as a weight fraction of the amounts of PEG and OIN in the sample. Afterward,
the reaction solution was placed in two small Teflon dishes on a heater at 70°C and left
overnight for evaporation of solvent and further OIN condensation. The solid film was
treated at 130°C in a vacuum oven for 1 hour to complete condensation. The HPE films
were carefully removed from the dishes and then sealed in a plastic container.
Previously, TEB was incorporated into the OIN through 4 different methods and
it was found that method C yielded a sample with the highest conductivities.12 TEB was
incorporated in amounts of 5, 10, 15, 20, 25, and 30 mol % of OIN. For example, in the 5
mol. % TEB sample, 0.103 g (0.705 mmol) of TEB was added along with 2.504 g
(10.595 mmol) of GLYMO, while in the 10 mol.% TEB sample, 0.206 g (1.41 mmol) of
TEB was added along with 2.337 g (9.89 mmol) of GLYMO, etc.
The various ILs were added to the samples during the final addition of OIN. IL1,
IL2, and IL3 were incorporated in amounts of 10, 20, 30, 40, and 50 wt, % of the total
10
sample weight or until a compatibility threshold was met. For example, in the 10 wt. %
IL1 sample, 0.22 g of IL1 was added, while in the 20% wt. % IL1 sample, 0.44 g of IL1
was added.
3.3. Characterization
Conductivity was measured as follows. The samples were vacuum-dried at room
temperature overnight to minimize the effects of water absorption on measurements.
Using a micrometer, the thickness of the sample polymer film was determined. Gold
contacts of the area of 1.18 × 10-5 ± 0.05 m2 were coated directly onto the polymer films
by using a Polaron E5100 sputter coater. Sputtering of the gold was accomplished in 3
minutes, and during this time the samples were held between -10 and -15°C, as
monitored with a thermocouple. After the gold was sputtered, electrodes were attached,
and each sample was placed into a measurement rig and attached to an LF impedance
analyzer. The oscillation level of the applied pulse was 1 V over a frequency range of 10
Hz to 10 MHz at room temperature. The samples were modeled to a parallel circuit
comprised of a resistor and capacitor. Admittance data was recorded using this circuit
model and subsequently converted to obtain impedance plots.
Differential Scanning Calorimetry (DSC) was performed with a TA Instruments
Q Series calorimeter. Sample masses varied from 5-20 mg and were hermetically sealed
in aluminum pans. The samples were scanned between -80 and +200°C at a scan rate of
10°C/min, using refrigerated cooling systems (RCS) as coolant. Glass transition regions
were then determined using the fictive temperature method.
11
Scanning Transmission Electron Microscopy (STEM) images were obtained at
30 keV. The SPE samples were ground into powder then embedded in epoxy resin and
cut very finely with a diamond knife. Images of the resulting thin sections (ca. 50 nm
thick) were obtained with a Quanta FEG SEM instrument using STEM detector and
analyzed with the ImageJ software. Transmission Electron Micrscopy (TEM) was carried
out at an accelerating voltage of 80 kV on a JEOL JEM1010 transmission electron
microscope.
Results and Discussion
I. Addition of Triethyl Borate
We began by determining the optimal amount of TEB to be added to the OINs. In
previous research it was determined that at 40 wt.% OINs based on GLYMO and AB, the
best conductivity was achieved, but the solid polymer electrolyte (SPE) was rather weak.
At 75 wt.% of the same OIN, the mechanical properties improved, but the conductivity
significantly dropped.18 At 55% OIN, the highest conductivity was achieved while also
maintaining mechanical properties.
Li ion transference number measurements were conducted on the SPE samples
containing TEB. The lithium ion transference number, T+, was determined from the ratio
of the corresponding ionic mobilities (with assumption of equal densities of anions and
cations) and the values obtained are presented in Table 1.17 For moderate amounts of
added TEB, lithium transference increases significantly as compared to the reference
sample. At 10% TEB the highest conductivity and Li transference numbers were
achieved but the conductivity was mediocre.
12
Li transference numbers were determined by a series of measurements in order to
determine what percent of ionic conductivity is solely lithium ion based.
Table 1. Li transference numbers and ionic conductivity of SPE with boron species17
TEB % T+ (±0.05) Ionic Conductivity (S/cm)
0 0.76 7.12 x 10 -6
5 0.88 8.53 x 10 -6
10 0.89 4.34 x 10 -5
20 0.79 1.64 x 10 -5
These data suggest that the incorporation of boron species into the OINs resulted in a
stronger anion interaction with the boron species, a strong Lewis acid, thus reducing
anion migration. As a result, a majority of the ionic conductivity is based on solely
lithium ion migration.
II. Addition of Ionic Liquids
To further enhance the ionic conductivity of the HPEs, the incorporation of
different ILs into polymer electrolytes was studied based on promising results of
others.19-21 Figure 3 shows the dependence of conductivity on the amount of IL1 added to
the samples containing PEG, LiTf, and 55 wt. % OIN with 10 mol. % TEB.
13
Figure 3. Conductivity of PEs as a function of the IL1 amount in the samples containing
55 wt. % OIN prepared with 10 mol. % TEB.
The addition of 30 wt. % of IL1 resulted in an increase in conductivity by over two orders
of magnitude compared to the samples containing no ionic liquid. However, when added
in amounts greater than 30 wt. %, IL1 appeared as drops on the PE film surface. This is
most likely due to the IL1 saturating the cross-linked PE network and being released from
the structure.
Next, the incorporation of IL2 was studied. Figure 4 displays the dependence of
conductivity on the amount of IL2.
14
Figure 4. Conductivity of PEs as a function of the IL2 amount in samples containing 55 wt. % OIN prepared with 10 mol. % TEB.
The addition of IL2 resulted in an increase in conductivity by over three orders of
magnitude as compared to the samples containing no ionic liquid. Compared to IL1, IL2
was miscible with the PEG-OIN network up to 50 wt. %, after which poor mechanical
properties were and the film became weak. The difference between IL1 and IL2 is the
structure of anions, which are tetrafluoroborate and trifluoromethanosulfonate,
respectively, while cations are identical. The expulsion of IL1 may have been due to
more hydrophobic nature of the tetrafluoroborate in IL1 as compared to
trifluoromethanosulfonate in IL2.15 As a result, rather than being further incorporated like
IL2, IL1 was expelled from the polymer matrix due to the repulsion of the hydrophobic
anion from the hydrophilic matrix.15, 17
Furthermore, the effects of IL3 addition were studied. The difference between IL2
and IL3 is the cation structure. Each of these ionic liquids contain the same anion,
15
however the tail on position 1of the 3-methylimidazolium, is an ethyl group in IL3 and a
butyl group in IL2. However, IL3 prevented cross-linking between silica particles and
PEG so no solidification occurred (no film was formed). This is probably due to the
behavior of ionic liquids to undergo molecular layering at a charged surface.22 As was
shown previously,17 the incorporation of boron species into OINs, resulted in higher Li
transference numbers, meaning that anion interaction with OINs was significantly
strengthened. Also, there are the epoxy groups of GLYMO on the surface of the OINs,
which interact with the hydroxyl groups of the PEG chains, resulting in cross-linking.
The cations of the ionic liquids should therefore be found in the second layer surrounding
the OINs, resulting in the possibility of cations to interact with the epoxy groups of
GLYMO, impeding cross-linking. The general trend in liquid density for ionic liquids
with imidazolium-based cations, is that as the alkyl tail lengthens, the liquid density
decreases.16 Then, the ethyl group on the cation in IL3 should result in a denser layer as
compared to the IL2 with the bulkier butyl group, resulting in the prevention of the epoxy
group cross-linking with the hydroxyl groups of PEG.
DSC measurements were performed on the samples in order to estimate the
mobility of the PEG polymer chains and their possible crystallinity in the HPEs. The
results are displayed in Table 2.
16
Table 2. DSC data and OIN sizes for the HPEs with different amounts of TEB and different amounts of ILs.
Sample % TEB Ionic
Liquid
Tg (C)
NP size (nm)/
Std. Dev. (%)
Conductivity
(S/cm)
GTA-PEG-1 0 --- -43 214/ 53 7.12 x 10 -6
GTA-PEG-2 5 --- -47 203 /35 8.53 x 10 -6
GTA-PEG-3 10 --- -60 36 /58 4.34 x 10 -5
GTA-PEG-4 10 10 wt.%
IL1
No Tg
observed
5.5 /24 5.81 x 10 -4
GTA-PEG-5 10 30 wt.%
IL1
No Tg
observed
5.4 /42 3.22 x 10 -3
GTA-PEG-6 10 30 wt.%
IL2
No Tg
observed
6.9 /36 1.71 x 10 -2
The DSC traces of various PEs are displayed in Figure 5. The DSC trace of the HPE
based on OIN including boron species as well as IL1 is presented in Figure 5c. The DSC
traces of the PEs based on OIN without boron species or ILs and PE based on OIN
including boron species17 (Fig. 5a and b) show glass transitions. However, in the case of
addition of ILs (Fig. 5c), no glass transition is observed, indicating that the glass
transition occurs below the scanned temperature range. This means that the PEG polymer
chains maintain mobility even at extremely low temperatures.
Figure 5. DSC traces of SPEs which contain 55 wt.% OIN without boron species (a), with 10 mol. % TEB (b) and with 10 mol.% TEB and 10 wt.% IL1.
In previous work, it was demonstrated that OIN particle size significantly
influences the electrochemical performance of composite SPEs.17 Thus, in this work, we
again used STEM and TEM to determine sizes of the OIN particles in the native HPE
-100 -50 0 50 100 150 200-0.8
-0.6
-0.4
-0.2
0.0
0.2
0.4
He
at
Flo
w (
W/g
)
Temperature (°C)
a
17
environment, i.e., without calcination at 500 C in oxidizing media as was performed
earlier. One issue, however, with this method of characterization is the brief exposure of
the HPE sample to water during sectioning for STEM or TEM imaging. As a result of
this brief exposure, PEG swelling and OIN aggregation could occur, thus particle
distribution within an HPE section cannot be determined. This moisture-induced effect
does not alter the size of the OIN particles, allowing for the study of particle sizes and
morphologies. Representative images obtained from the STEM and TEM measurements
are shown in Figure 6. Mean OIN particle sizes and the particle size distributions are
displayed in Table 2.
Figure 6. STEM (A, B, and C) and TEM (D, E, and F) images of the HPE samples with different amounts of TEB added to OINs by method C and ILs: without TEB (A), 5 mol.% TEB (B), 10 mol.% TEB (C), 10 mol.% TEB and 10 wt.% IL1 (D), 10 mol.% TEB and 30 wt.% IL1 (E), and 10 mol.% TEB and 30 wt.% IL2 (F).
In previous research, the size analysis of the HPEs with OIN containing boron
species showed some correlation between the OIN particle size and conductivity; an
18
inverse relationship between particle size and ionic conductivity was observed.17 The
decrease in the particle size, results in increased surface area, thus a higher interaction of
anions with OINs. The average OIN size decreased almost by an order of magnitude with
the incorporation of ILs and the increase of conductivity was also observed.
Although previous research demonstrated that a decrease in the OIN size, results
in the increase in ionic conductivity, the magnitudes of the conductivity increase, which
was observed with the incorporation of ILs, are most likely due to high mobility of Li
ions in the ILs. Table 3 shows conductivities of ILs, organic electrolytes and various
polymer electrolytes as compared to the HPEs described here.15, 23
Table 3. Comparison of conductivities of the samples prepared in this work with the literature data.
Polymer Electrolyte Sample Conductivity (S/cm)
No TEB 7.12 E-06
10 mol.% TEB 4.34 E-05
30 wt.% IL1 3.22 E-03
50 wt. % IL2 3.86E-02
Ionic liquid15 Range from 4.5E-04 to 1.6E-02
Ionic liquid +polymer23 0.18E-03
Ionic liquid + polymer + liquid organic23 0.81E-03
Liquid organic23 1.0E-02
These data show that the HPEs that we have synthesized, have even higher ionic
conductivities than those of any reported samples found in literature. This observation
can be attributed to the ionic liquid being confined in a restricted geometry, resulting in
the alteration of the ionic liquid physical properties, i.e. viscosity.15 In our case,
19
confinement of the ionic liquid can occur within the PE-SiO2 network, which resulted in
decreased viscosity, and thus increased conductivity.
Along with LiTf, we explored another lithium salt, lithium bis(oxalate)borate
(LiBOB), as well as a sodium salt, sodium trifluoromethanosulfonate (NaTf), to study the
influence of the Li salt anion structure and the replacement of Li with Na on
conductivities. The results are displayed in Figure 8.
Figure 8. Comparison of conductivity measurements for HPEs based on different amounts of IL2 and different salts.
The use of LiBOB, resulted in a decrease of conductivity. This decrease in
conductivity may have been due to the bulkier anion and its weaker interactions with the
OINs, thus leading to more ion pairs and lower conductivity. The substitution of lithium
ions for sodium ions, by the use of NaTf, yielded conductivities similar to those of LiTf.
The latter fact opens great opportunities for development of sodium ion batteries with
very high conductivity.
20
We also studied the effects of using different molecular weight PEGs in the
synthesis of our HPEs. The results for using 400, 600, 1000, and 2000 Da PEG, on
conductivity, are displayed in Figure 9.
Figure 9. Comparison of the conductivities of HPEs based on different amounts of IL2
and the PEG molecular weights.
The data presented in Figure 9 show a clear dependence of conductivity on the
length of PEG chains. PEG 400, which is the shortest, exhibited the highest
conductivities, which could be associated with the structure of the HPE network. From
the explanation given earlier for the increase in ionic conductivity of ionic liquids in
confined spaces, the observation with these different length PEG chains reinforces this
statement. Shorter PEGs form networks with smaller cells allowing better IL
confinement, reduced viscosity and higher conductivity.24
21
III. Li Ion Transference
Once the conductivity was significantly enhanced, the measurement of lithium ion
transference numbers was attempted. However, the speed with which the lithium ions
migrate, through the sample, is less than a millisecond, making the determination of a
firm transference numbers difficult. Therefore two different sets of measurements were
performed on samples in order to calculate the transference numbers. The results are
displayed in Figure 5 and Figure 6.
Figure 5. Current discharge with respect to time after bias reversal with Pt electrodes for the HPE with 30 wt.% of IL2.
1.00E-05
1.00E-04
1.00E-03
1.00E-02
1.00E-01
1.00E+00
1.00E+01
1.00E-06 1.00E-04 1.00E-02 1.00E+00 1.00E+02 1.00E+04
Cu
rren
t D
isch
arg
e (
mA
)
Time (s)
-1 V -> 1 V
-2 V -> 2 V
-3 V -> 3 V
-1 V -> 1 V (short times)
-2 V -> 2 V (short times)
-3 V -> 3 V (short times)
22
In Figure 5, the set of measurements displayed are of discharge experiments,
where the sample was placed between two platinum (blocking) electrodes, and the
current discharge after a bias reversal was measured. The observed discharge is much
more rapid with blocking electrodes, since the lithium cations themselves will accumulate
at the interfaces. The peak in the graph signifies the maximum discharge and thus the
maximum movement of the lithium ions. As a consequence, it is difficult to assign a
characteristic time to this process other than to note that it is much faster than the
characteristic time that was previously seen in samples without IL2, which were by the
three orders of the magnitude slower.
Figure 6. Current with respect to time after a bias reversal for the HPE with 30 wt.% of IL2 30% and the HPE without IL2 with lithium contacts.
0.00E+00
2.00E-02
4.00E-02
6.00E-02
8.00E-02
1.00E-01
1.20E-01
0 500 1000 1500 2000
Cu
rren
t (m
A)
Time (s)
-1 V -> +1 V
-2 V -> +2 V
-3 V -> +3 V
no IL -1 -> 1 V
23
In Figure 6, a similar set of measurements from further experiments are displayed,
however the sample was placed between two lithium contacts, and the current after a bias
reversal was measured. In contrast, since lithium contacts were used, the accumulation of
ions other than lithium, on the lithium interfaces, blocked the current.
Next, a comparison of the samples with and without IL2, where d is the sample
thickness and tmax is the time of maximum current in the bias reversal experiment is
displayed in Figure 7. The slope on this type of graph would typically represent the
anion mobility but there is not enough data to claim a value here. Primarily this
comparison shows that the mobility of ions other than lithium differs by a much smaller
factor than the enhancement of the conductivity with the ionic liquid..
Figure 7. Comparison of the HPE with 55 wt. % OIN and 10 mol.% TEB with and without IL2.
Figure 7 displays the “d” sample thickness over the “tmax” the time of maximum
current in the bias reversal experiment of two HPE samples, one containing IL2 and the
other without IL2. The slope on this type of graph would typically represent the anion
mobility, however due to the lack of data points, it is difficult to claim a definite value.
0
5E-10
1E-09
1.5E-09
2E-09
2.5E-09
3E-09
0 0.5 1 1.5 2 2.5 3 3.5
d2
/tm
ax
(m2/s
)
Voltage (V)
30 wt. % IL2
no IL2
24
From the few data points displayed, the trend observed shows that the mobility of ions
other than lithium differs by a much smaller factor than the enhancement of the
conductivity with the ionic liquid.
Using the two sets of measurements, a few general statements on the ion mobility
within the HPEs containing IL2 can be made. In previous discharge experiments,
performed on samples without IL2, a peak in the measurements was determined to be
between 0.01 seconds. In the experiments performed on samples containing IL2, the
peaks in the measurements, occur mostly around 0.0001 seconds. These times, refer to
the time it takes for the majority of the lithium to travel between the electrodes. With
respect to the results of the bias reversal experiments, the anion mobility remains fairly
constant between samples not containing and containing IL2, although there are too few
data points to be certain. These two sets of experiments suggest that since the anion
mobility is constant, but the lithium movement has increased almost by two orders of
magnitude, the lithium transference numbers of these HPEs are superior to that of our
best sample without ILs.
Conclusion
For the HPEs, the data obtained from conductivity measurements demonstrates
that the addition of 50 wt. % IL2 to the sample containing 55 wt. % of OIN along with 10
mol.% of TEB yields the best results. The DSC data obtained displays the glass
transition temperature of the samples containing ILs to be below -80C, permitting
lithium ion mobility in these HPEs even further below freezing temperatures than
samples without ILs. STEM and TEM images of the samples show that the OIN size is
25
significantly reduced with the incorporation of ILs, which may be one of the reasons for
such high ionic conductivities. We also studied the influence of the Li salt structure and
the replacement of Li with Na on conductivities, however LiTf produced better ionic
conductivity than LiBOB. This trend is perhaps a result of the bulkier anion of LiBOB,
resulting in weaker interactions with OINs. Interestingly, the conductivity of the samples
containing Na triflate shows comparable ionic conductivities to those with Li triflate.
This opens up possibilities for the development of highly conductive sodium ion
batteries. PEG chain length was then compared between samples, and a dependence on
chain length was observed. It was found that the shortest PEG400 yielded the highest
conductivity. This observation may be associated with the structure of the PEG-SiO2
network, i.e., confinement of ILs within this network. Lastly, Li transference was studied,
and although a definitive Li transference number was not measured, due to the extremely
high Li ion mobility, it was shown through current measurements that Li transference
numbers are significantly increased as compared to the samples without ILs. Further
research is necessary for determining the HPE structure, Li transference numbers, and
synthesizing HPEs based on sodium salts, as well as further enhancing the conductivity.
26
References
1. Balbuena, P. B. W., Y., Lithium-ion Batteries: Solid-Electrolyte Interphase.
Imperial College Press: London, 2004; Vol. 2004.
2. van Schalkwijk, W., & Scrosati, B., In Advances in lithium-ion batteries, van
Schalkwijk, W., & Scrosati, B. , Ed. Springer: New York, 2002.
3. Xu, K., Nonaqueous Liquid Electrolytes for Lithium-Based Rechargeable
Batteries. Chem. Rev. 2004, 104, 4303-4417.
4. Alamgir, F. M. C., J; Liu, M; Park, S; Song, M, Mater. Sci. Engin. 2011, 72, (203-
204).
5. Abraham, K. M.; Alamgir, M., Room-temperature polymer electrolytes and
batteries based on them. Solid State Ionics 1994, 70-71, 20-26.
6. Wright, P. V., Electrical conductivity in ionic complexes of poly(ethylene oxide).
Br. Polymer J. 1975, 7, 319-327.
7. Palomares, V. S., P; Villaluenga, I; Hueso, K.B.; Carretero-Gonzalez, J; Rojo,T,
Na-ion Batteries, Recent Advnaces and Present Challenges to Become Low Cost Energy
Storage Systems. Energy & Environmental Sciences 2012, (3).
8. Shriver, D. F.; Bruce, P. G., Polymer electrolytes {I}: General principles. In Solid
State Electrochemistry, Bruce, P. G., Ed. University Press: Cambridge, 1997; pp 95-118.
9. Dias, F. B. P., L.; Veldhuis, J., B., J.; , J. Power Sources 2000, 88, (169).
10. Patil, A. P., V.; Shin, D. W.; Choi, J., W.; Paik, D. S.;Yoon, S., J.;, Mater. Res.
Bull. 2008, 43, 1913.
11. Aurbach, D. L., M.D.; Levi, E.;, Solid State Ionics 2008, 179, 742.
27
12. Mandal, B. K.; Walsh, C. J.; Sooksimuang, T.; Behroozi, S. J.; Kim, S.-G.; Kim,
Y.-T.; Smotkin, E. S.; Filler, R.; Castro, C., New Class of Single-Ion-Conducting Solid
Polymer Electrolytes Derived from Polyphenols. Chem. Mater. 2000, 12, 6-8.
13. Budgin, A. Indiana University, Bloomington, 2011.
14. De Souza, P. H. B., R. F.; Dahmouche, K.; Judeinstein, P.; Faria, R. M.;
Bonagamba, T. J.; , J. Mater. Chem. 2001, 13, 3685.
15. Fedorov, M. V. K., A.A, Ionic Liquids at Electrified Interfaces. Chem. Rev. 2014,
114, (5), 2978-3036.
16. Shirota, H. M., T.; Fukazawa, H.; Tatsuya, K, Comparison between Dicationic
and Monocationic Ionic Liquids: Liquid Density, Thermal Properties, Surface Tension,
and Shear Viscosity. J. Chem. Eng. Data 2011, 56, (5), 2453-2459.
17. Mathews, K. L.; Budgin, A. M.; Beeram, S.; Joenathan, A. T.; Stein, B. D.;
Werner-Zwanziger, U.; Pink, M.; Baker, L. A.; Mahmoud, W. E.; Carini, J. P.; Bronstein,
L. M., Solid polymer electrolytes which contain tricoordinate boron for enhanced
conductivity and transference numbers. J. Mater. Chem. A 2013, 1, (4), 1108-1116.
18. Bronstein, L. M.; Joo, C.; Karlinsey, R. L.; Zwanziger, J. W., Chem. Mater 2001,
13, 3678-3684.
19. Guerfi, A.; Dontigny, M.; Kobayashi, Y.; Vijh, A.; Zaghib, K., Investigations on
some electrochemical aspects of lithium-ion ionic liquid/gel polymer battery systems. J.
Solid State Electr. 2009, 13, (7), 1003-1014.
20. Garcia, B.; Lavallee, S.; Perron, G.; Michot, C.; Armand, M., Room temperature
molten salts as lithium battery electrolyte. Elecrochim. Acta 2004, 49, (26), 4583-4588.
28
21. Shin, J.-H.; Henderson, W. A.; Passerini, S., Ionic liquids to the rescue?
Overcoming the ionic conductivity limitations of polymer electrolytes. Electrochem.
Commun. 2003, 5, (12), 1016-1020.
22. Mezger, M. S., H.; Reichert, H.; Schramm, S.; Okasinski, J. S.; Schöder, S.;
Honkimäki, V.; Deutsch, M.; Ocko, B. M.; Ralston, J.; Rohwerder, M.; Stratmann, M.;
Dosch, H., Molecular Layering of Fluorinated Ionic Liquids at a Charged Sapphire
(0001) Surface. Science 2008, 322, 424-428.
23. Goodenough, J. B.; Kim, Y., Challenges for Rechargeable Li Batteries. Chem.
Mater. 2010, 22, (3), 587-603.
24. Rajput, N. N. M., J.; Hung, R.H., Ionic Liquids Confined in a Realistic Activated
Carbon Model: A Molecular Simulation Study. J. Phys. Chem. C 2014, 118, (3), 1540-