Pittsburgh Corning USA (Corporate Headquarters)800 Presque Isle Drive Pittsburgh, PA 15239Telephone: 1-724-327-6100FAX: 1-724-387-3807 Pittsburgh Corning Corporation Asia (Asia Headquarters)Pittsburgh Corning Corporation3-7-4-304 HikarigaokaNerima-ku, Tokyo, Japan 179-0072Telephone & Fax: 011 81-3-5997-0248
Pittsburgh Corning Europe NV (Europe / Middle East Africa Headquarters)Albertkade, 1B-3980 TessenderloBelgiumTelephone: +32-13-66-17-21Fax: +32-13-66-78-54
www.foamglas.com
Protect ing Companies and Their People Worldwide
for Industr ia l Appl icat ions with Operat ing Temperatures of -268°C to +482°C (-450°F to +900°F)
F O A M G L A S ® I N S U L AT I O N S Y S T E M S
FI-201 5M Rev. 2/09Replaces Rev. 12/04
Section 11: Temperature Limits ..........................23
Section 12: Insulation Thicknesses for ................26Process Piping
Section 13: Insulation Thicknesses for ................27Personnel Protection
Section 14: Above Ground and ...........................28Underground Installation
Section 15: General Specifications ......................31
Section 16: Accessory Materials ..........................33
PRODUCT VALUESFOAMGLAS® cellular glass insulation is
the result of more than a half-century
of proven performance and continual
product improvement by Pittsburgh
Corning Corporation, the developer of
cellular glass insulation.
Selection and ExperienceFOAMGLAS® insulation is comprised of a
family of seven material grades providing
the precise properties and performance
for your specific applications, from
-450°F to +900°F (-286°C to +482°C).
Billions of units have been installed
throughout the world in thousands of
industries and operations.
Worldwide AvailabilityWith plants in the U.S. and Europe,
Pittsburgh Corning can uniquely provide
consistency of supply, a millions-of-units
inventory and ready availability.
Accessory ProductsIn addition, Pittsburgh Corning
offers a full line of complementery
accessory products, each laboratory-
and service-proven to provide
maximum performance specifically with
FOAMGLAS® cellular glass insulation.
SERVICE VALUESEqually critical to product performance is
the added value of Pittsburgh Corning’s
support services to ensure that the
product is smoothly and properly
incorporated into the customer’s
requirements, project and facility.
Technical ServicePittsburgh Corning’s Technical Service
Staff provides product, application
and materials testing—standardized
and customized specifications—on-site
customer assistance and installation
guidance.
Energy Analysis ServiceTo simplify your insulation specification
process, Pittsburgh Corning offers and
Energy/Economic Analysis Service,
resulting in our exclusive Energy
Analysis Report (EAR). Developed
with customer-specific data subjected
to computer analysis and other
calculations, EARs assist systems
designers in specifying the proper
insulation thicknesses for above or
below ground pipelines and for storage
vessels, tanks and other equipment.
Typical reports present heat flow rates,
interface and surface temperatures,
and insulation thicknesses required to
prevent condensation.
Energy Survey ServicePittsburgh Corning offers this service
free to all prospective clients to assist
in planning for building renovations
and to identify deteriorating insulation
systems. This service helps to determine
payback periods for reinsulated systems
and will evaluate the performance of
existing thermal insulation on piping and
equipment. The survey is conducted
on-site and can result in energy savings
and condensation-ice control.
Specialized reports are available for:
• Underground pipelines
• Predicting outlet temperatures
• Estimating exit pressure and quality of steam for long steamlines
• Determining the time for water and sewage to freeze in pipelines
• Calculating heat flow and interface temperatures for tank base systems
Requests for EARs can be made
through your local Pittsburgh Corning
representative.
Sales SupportA system of local sales representatives
and distributors are available for
consultation and problem resolution.
Training videos, CD-ROM presentations
and literature, are also available from
your local sales personnel. Literature
is also available electronically on our
website at: www.foamglas.com.
Industry SupportPittsburgh Corning supports technical
and trade and certifying organizations,
including ASTM, CSI, CEN, FESI, UDI,
CEPMC, ASHRAE, NACE, NIA, UL and
FM. The result is an ever-growing series
of application and regional certifications
and approvals (see page 18) that provide
you will complete assurance of materials
compliance for a variety of installations.
Pittsburgh Corning is ISO 9001:2000
certified with registered production
processes regarding quality control.
FOAMGLAS® CELLULAR GLASS INSULATION IS PROVEN VALUETABLE OF CONTENTS
Section 1: Introduction ....................................... 2
Section 2: Properties/Benefits/Applications ........... 3
Section 3: Moisture Resistance ............................ 4
Section 4: Noncombustibility ............................... 7
Section 5: Chemical Durability ............................11
Section 6: Dimensional Stability ..........................13
Section 7: Compressive Strength ........................17
Section 8: Vermin Resistance .............................18
Section 9: Properties and Certifications ...............19
Section 10: Selection Guide ................................21
2FOAMGLAS® INSULATION SYSTEMS
INTRODUCTION SECTION 1
SUPERIOR PHYSICAL ATTRIBUTESFOAMGLAS® insulation is a lightweight,
rigid insulating material composed
of millions of completely sealed
glass cells, each an insulating space.
This all-glass closed-cell structure
provides an unmatched combination of
physical properties ideal for piping and
equipment above ground, as well as
underground, indoors or outdoors, at
operating temperatures from -450°F to
+900°F (-268°C to +482°C):
• Resistant to water in both liquid and vapor forms
• Noncorrosive
• Noncombustible/nonabsorbent of combustible liquids
• Resistant to most industrial reagents
• Dimensionally stable under a variety of temperature and humidity conditions
• Superior compressive strength
• Resistant to vermin, microbes and mold
• Fiber, CFC and HCFC free
MANY UNIQUE BENEFITSFOAMGLAS® insulation’s diversity of
properties results in an equally unmatched
combination of benefits, proven over
decades of in-the-field performance:
• Constant, long-term energy efficiency provides low, predictable energy costs
• Enhanced process control allows improved, consistent product quality
• Minimal maintenance/repair/ replacement of insulation or facility infrastructure reduces life cycle costs
Fire resistance protects the • insulated equipment, and helps minimize subsequent plant shutdown time
Virtual elimination of the • potential for auto-ignition from absorbed combustible liquids or fire from condensed low- temperature gases
Proven durability for • underground and exterior installations
Manufacturing of FOAMGLAS• ® insulation puts no stress on the atmosphere’s ozone layer … while its long-term thermal efficiencies reduce energy demand and the effects of burning fossil fuels on the environment
WIDE-RANGING, SERVICE-PROVEN APPLICATIONSFOAMGLAS® insulation has over 60 years of applications that have stood the test of time with a record untouched by any other insulation product on the market:
Cryogenic and low-temperature • pipelines, vessels, tanks and equipment
Medium- and high-temperature • pipelines and equipment
Hot oil/asphalt storage tanks•
Heat transfer fluid systems•
Hydrocarbon and sulfur • processing systems
Underground steam and chilled • water piping
Chilled and hot water service • lines
Off-shore platforms•
Above ground steam lines•
Pulp/paper mills and water • treatment plants
Food processing/cold storage • facilities and breweries
Cyclic and dual temperature • applications
Heat traced pipes and • equipment
For each of these applications and for all
special conditions, FOAMGLAS® insulation
is fabricated in a wide range of shapes,
thicknesses and sized to meet virtually
all industrial requirements. Pittsburgh
Corning’s many accessory products
are designed to produce the maximum
insulation system performance.
A UNIQUE COMBINATION OF PROPERTIES CREATES THE INSULATION OF CHOICE
MOISTURE RESISTANCE DELIVERS LONG-TERM PERFORMANCE
CONSTANT THERMAL EFFICIENCYLost thermal efficiency due to moisture
absorption is the single most common
cause of insulation failure. In fact, just
4% by volume, can reduce thermal
efficiency by 70%*!
* “Thermal Conductivity of Wet Insulations.” Ludwig Adams, ASHRAE JOURNAL, October 1974.
For over 60 years, FOAMGLAS®
insulation has proven itself to resist
moisture and provide constant
thermal resistance. No other insulation manufacturer can make this claim.
WATER’S EFFECTSEventually, other insulation materials
absorb moisture. So, eventually other
insulations lose thermal efficiency.
This is because liquid water has a
thermal conductivity up to 20 times
greater than most insulation materials.
And, the thermal conductivity of ice
is 100 times greater—a major threat
for cryogenic systems (see Figure 1).
When moisture in any form invades
insulation, thermal efficiency is
destroyed and energy consumption
increases.
OPERATIONS PROBLEMSThe problems that can result when
moisture enters an insulation are
multiple. Foremost, is the effect
on operating cost. When moisture
reduces an insulation’s thermal
efficiency, the system it protects is not
functioning optimally and production
costs increase—often very insidiously.
When a system is not operating at its
proper temperature, process control
and product quality and quantity are
compromised. Simultaneously, as
invasive moisture causes production
costs to go up and product quality to go
down, the facility’s infrastructure itself
can fall prey to corrosion.
LONG-TERM PROTECTIONBecause FOAMGLAS® insulation is an
all-glass, totally closed-cell material with
minimal absorption, it eliminates moisture
intrusion. Even after total immersion in
water, the only measurable moisture found
on FOAMGLAS® insulation is that which
adheres to its surface cells (see Table 1).
43
SECTION 3SECTION 2 MOISTURE RESISTANCEPROPERTIES/BENEFITS/APPLICATIONS
FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
Phenolic
Aerogels
Polyurethane/Polyisocyanurate
Glass/Mineral Fiber
FOAMGLAS® Insulation
Calcium Silicate
Perlite
Water
FIGURE 1: Comparative Thermal ConductivitiesBTU-in/hr•ft2•°F
at -200°F-129°C
at 32°F 0°CIce
W/mK
0.28 0.57 0.87 1.15 1.44 1.73 2.02 2.31 3.75 4.04
≈
FOAMGLAS® insulation—in 2" (50.8mm)-thick, 12" x 18" (304.8mm x 457.2mm) blocks—being applied to a petroleum storage tank at a West Coast refinery. Industrial Applications include pipelines as well as vessels of all types.
FOAMGLAS® insulation is ideal for low temperature applications—including chill water piping and equipment.
2 4 6 8 10 12 14 16 26 28
≈
jacketing. System heat can now drive
moisture out of the original insulation
as vapor, through jacketing seams
and the open joins of the FOAMGLAS®
insulation overfit, and, finally, out of the
system. At one refinery where overfit
was employed, operating costs were
reduced 56% and a potential $10
million shutdown was averted.
If FOAMGLAS® insulation can perform
like this on a high-temperature
operation with wet insulation of some
other material, imagine how it performs
when installed initially. In one instance,
after 30 years of unjacketed services
(not recommended) on a refinery’s
heated (190°F/88°C) wax and oil tank,
FOAMGLAS® insulation remained dry,
with a thermal conductivity increase of
0.01Btu-in/hr•ft2•°F.
HIGH-TEMPERATURE SYSTEMSFOAMGLAS® insulation can be fabricated
for specific high-temperature piping
and equipment requirements. Systems
include various bonding agents,
composite insulation systems, and the
StrataFab® and Advantage® systems.
See page 20 for selection chart.
CORROSION UNDER INSULATIONSignificant metallic corrosion—
with major economic and safety
consequences—can develop in systems
using absorptive insulations, particularly
when these sytems are at temperatures
which allow water to exist in the liquid
state. With carbon steel, ions leached
from the insulation by intrusive moisture
can produce acids that accelerate
corrosion; and chlorides rom insulation
products can promote stress cracking in
stainless steel.
The corrosion rate under wet insulation
can be up to 20 times greater than
the rate of corrosion by the ambient
atmosphere. With “invisibility”
compounding the situation, it has been
described as the greatest corrosion
problem facing the chemical industry.
The cost for system replacement at just
one plant can be millions of dollars,
not including lost production and the
potential of total shutdown.
Because under-insulation corrosion
can progress undetected, hazardous
leaks are possible. And, results can
be catastrophic—to personnel, plant
equipment and production.
There are three approaches to averting
under-insulation corrosion:
The use of suitable weather or • vapor retarders … but these are not reliable.
The physical “encapsulation” of • equipment via paints or mastics, including silicones, epoxy phenolics, coal tar epoxies and bitumens … but these require critical surface preparation and a defect-free coating
An insulation that minimizes • water intrusion and does not retain water
Impermeable, inert FOAMGLAS®
insulation provides the third approach
and resists the development of corrosion
in three ways:
Protection against water • intrusion and retention
No acceleration of the corrosion • due to water soluble chlorides or other corrosive agents
Acting as a barrier to corrosion•
65
SECTION 3SECTION 3 MOISTURE RESISTANCEMOISTURE RESISTANCE
FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
TABLE 1: Permeability (E 96 Wet Cup) and Moisture Absorption (C 240)
1 Perm-Inch is the accepted unit of water vapor permeability
1 Grain•Inch 1 Grain•Cm
Ft2•Hr•Inch of Mercury 1 Perm-Inch = SqM•Hr•Cm Mercury
2 The only moisture retained is that adhering to surface cells after immersion 3 Waterproofing agents may be destroyed when exposed to temperatures of 250°F (121°C) or higher
1 Perm-Inch =
Aging and moisture penetration can
cause a chronic, increasing loss of
thermal efficiency in other insulating
materials. FOAMGLAS® insulation
provides constant thermal efficiency
for the life of the system. Constant
insulating efficiency minimizes the need
for insulation replacement, and long-
term, life-cycle costs are among the
lowest and most predictable.
COLD & CRYOGENIC SERVICEMoisture can enter an insulation directly
as absorbed water, but with cold
applications an even more significant
source of moisture penetration is
diffusion of water vapor which can
condense as a liquid or as ice. As the
temperature gradient increases between
the exterior insulation surface and the
surface of the insulated equipment itself,
so does the potential rate of water vapor
penetration. Thus, it is even more critical
that an insulation have a low vapor transmission rate than an initially low
thermal conductivity. Any vapor retarders
that are used with permeable insulations
are subject to mechanical damage,
temperature change and weather. And,
because retarders are normally adhered
directly to these insulations, movement
can contribute to their damage.
More recently, some manufacturers of
permeable insulation have given up trying
to protect their products with vapor
barriers. They have introduced perforated
jacket systems with wicking materials that
supposedly draw the moisture away from
the pipe. Meanwhile these systems ignore
the continuous vapor drive towards the
cold line. In this type of system, the
equipment will be continuously wet and
subject to corrosion and mold growth.
Most low-temperature system insulations
are closed-cell organic foams subject
to water vapor permeability. With these
organic foams, moisture can penetrate
and be transmitted through the
insulation via the water vapor gradient
pressure previously mentioned. These
wet insulations in low-temperature
service have no opportunity to dry out,
so moisture builds to permanent liquid
saturation or ice accumulation.
However, the water vapor permeability
of FOAMGLAS® insulation (0.00 perm-
inch) is at least 100 to 10,000 times lower than competitive insulation
materials (see Table 1). As a result,
water vapor intrusion into low-
temperature systems is virtually
eliminated and thermal efficiency
maintained. Thus, FOAMGLAS®
insulation does not require a vapor
barrier (although they can be used for
added protection).
HIGH-TEMPERATURE SERVICEFor high-temperature conditions,
absorptive fibrous or particulate
insulations are often used. These include
calcium silicate which can hold over
400% of its weight in water without
dropping; up to 90% is not unusual.
In many cases complete saturation can
occur in less than three hours. Even
the effects of silicone water-repellent
treatments on mineral wools and perlite
are very short-lived, with performance
deteriorating at temperatures as low as
265°F (129°C) for the former, and 100°F
(38°C) for the latter. And, once moisture
gets into insulation it may never dry
out, even on steam lines at 1000°F
(538°C). The process heat involved can
drive water back to a certain point, but
some always remains in the insulation
layers that are below 212°F (100°C),
resulting in substantial heat loss and
a compromise in process control.
Non-absorbent FOAMGLAS® insulation
protects against moisture penetration.
Where this condition has occurred on
an existing system, the FOAMGLAS®
“OVERFIT” System can reverse the
problem. FOAMGLAS® insulation and
jacketing are installed directly over
the existing wet insulation and metal
Insulation Permeability Permeability AbsorptionMaterial Perm-Inch1 Perm-Cm % by Vol.
FOAMGLAS® Insulation 0.00 0.0 0.22
Polyurethane or 1–3 1.67–5.01 1.6 Polyisocyanurate
Polystyrene 0.5–4 0.835–6.68 0.7
Phenolic 0.1–7 0.17–11.69 10
Fibrous Glass 40–110 66.8–183.7 50–90
Mineral Fiber3 40–99 66.8–165.3 zero–903
Calcium Silicate 24–38 40.08–63.46 90
Expanded Perlite3 32 53.44 2–903
Aerogels N/A N/A N/A
FOAMGLAS® insulation being installed as an "OVERFIT" system.
Corroded flange under absorbent insulation.
With many FOAMGLAS® insulation projects, an insulation sample is removed after many years of service for testing and replaced with new FOAMGLAS® insulation.
Even after 32 years of service, the properties measured for the FOAMGLAS® insulation on this tank compare favorably with the same properties at the time of insulation.
Corrected Sample Date Steel Steel Thickness of Fire I.D. Tested Shape Length FOAMGLAS® Resistance 1 November W10x49 8' 6" 3 hrs, 48 min 11, 2006 2 November 6"x6"3/16" 2' 4" 1 hr, 27 min 11, 2006 Structural Tube 3 June 13, W10x49 8' 4" 2 hrs, 23 min 2007 4 June 13, 10"Ø Schedule 8' 5" 1 hr, 2 min 2007 40 Pipe 5 June 13, 6"x6"x3/16" 2' 4" 1 hr, 31 min 2007 Structural Tube SALT SPRAY 6 June 13, 6"x6"3/16" 2' 4" COMBO 1 hr, 54 min 2007 Structural Tube WET/FREEZE/DRY
TABLE 2: Intertek Fire Test Chart
Notes:Sample #2—Control sample for subsequent environmental exposure tests.
Sample #5, #6—Environmental exposure samples must perform within 75% of the small-
scale control (Sample #2). Conclusion: Both passed.
A separate data appendix includes results from three samples not used in this report,
including a 6”x6”x3/16” structural tube with 6” FOAMGLAS®, a W10x49 with 4” FOAM-GLAS®, and 10” Schedule 40 Pipe with 5” of FOAMGLAS®.
The conclusions of this test report may be used as part of the requirements for Intertek
product certification. Authority to Mark must be issued for a product to become certified.
When reviewing an insulation material’s
fire endurance, three factors must be
considered: fire resistance, toxicity
and performance in the presence of
combustible chemicals. It can be said
that FOAMGLAS® cellular glass insulation
has proven to be totally noncombustible,
nontoxic and nonabsorptive of
combustible fluids.
FIRE RESISTANCEBecause FOAMGLAS® insulation is
100% glass, without binders or fillers, it simply cannot burn, even when
in direct contact with intense flame.
“Thermal insulation” is usually
considered as a material limited to
helping maintain operating system
temperatures, while acknowledged as
having a potentially active role in fire
propagation. However, in the case of
FOAMGLAS® insulation, it can actually
serve to protect piping and equipment from fire damage, retard fire spread and help safeguard personnel.
PLASTIC FOAMSThe fire performance of FOAMGLAS®
insulation contrasts greatly with
the manufacturers’ warnings that
accompany many other insulations:
• “[Polyisocyanurate] foam insulation products are combustible. They should be properly protected from exposure to fire during storage, transit and application ...”
• “Warning—Polyisocyanurate is an organic material which will burn when exposed to an ignition source of sufficient heat and intensity, and may contribute to flames spreading.”
• “Warning—These [expanded polystyrene] products will burn and may pose a fire hazard. They will ignite with exposure to heat
sources of sufficient intensity, such as open flames and welders’ torches. Once ignited, they can burn with intense heat and smoke.”
Organic and foamed insulations are not
only flammable, but often act to rapidly
spread fire with molten plastic, while
generating toxic fumes and chemicals
and massive quantities of smoke.
FIRE PERFORMANCE CONFUSIONInsulation designations such as “self-
extinguishing” and “fire retarding” often
are thought to mean “noncombustible.”
And, even “slow-burning” or “self-
extinguishing” materials can produce
deadly smoke and toxic fumes. In fact,
flames are the least likely cause of death
from fire.
One test, for surface burning
characteristics (ASTM E 84, to be
discussed), can give dramatically
different results depending on the
presence of fire retarding additives.
With polyurethanes, for example,
additives can reduce flame spread under
test conditions, but have little retardant
effect in an actual fire. Additionally,
retardants can contribute their own
toxic fumes, as well as attack metallic
structures, reinforced concrete and
electronics for months after a fire with
their corrosive composition.
Other factors that can have a critical
effect on actual fire performance versus
test behavior are the substrate material
on which an insulation is used and how
fast maximum temperatures are reached
in petrochemical as opposed to building
fires. Compounding the confusion is
an international lack of fire testing
uniformity in this area.
TESTINGFOAMGLAS® insulation has been
subjected to scores of national
and international tests. The following
are four of the United States fire-
resistance tests, covering both building
and petrochemical fire performance.
ASTM E 119—Standard Fire Tests of Building Construction Materials This test examines the performance of
materials under fire exposure conditions
within a furnace. The basic test is run
at an ambient temperature reaching
1700°F (925°C).
The test is continued until failure occurs,
or until the average temperature of the
protected steel reaches 1000°F (538°C).
This maximum represents the threshold
of structural failure for carbon steel.
Above this temperature, piping/structural
steel would have to be replaced.
In ASTM E 119 testing, FOAMGLAS®
insulation has demonstrated exceptional
fire protection, as shown in Figure 2.
ASTM E 814/UL 1479—FOAMGLAS®
insulation is approved for use in
through-penetration firestop systems
described in Vol. 2 of the U.L. Fire
Resistance Directory.
A firestop system is a specific
construction consisting of a wall or floor
assembly. A penetrating item such as
chilled water pipes passes through an
opening in the wall or floor assembly
and the materials designed preserve the
fire resistance rating of the assembly.
See page 18 for a list of approved
systems. Call Pittsburgh Corning for a
list of UL approved fabricators.
NONCOMBUSTIBLE ... PERSONNEL AND EQUIPMENT PROTECTION
87
ASTM E 136—Behavior of Materials in a Vertical Tube Furnace at 1382°F (750°C)
This test also examines the combustion and heat generating characteristics of building materials within a furnace environment; limited flaming is allowable. The specimen, with thermocouples, is inserted into the furnace and the test continued until the specimen thermocouples reach the 1382°F (750°C) furnace temperature, or the specimen fails. A material passes the test if three of four specimens: (1) do not have thermocouple temperatures more than 54°F (12°C) above the furnace temperature; (2) show no flaming after the first 30 seconds; and (3) show no temperature rise or flaming, if their weight loss exceeds 50%.
This test, and similar international tests, are applied by United States Coast Guard; Factory Mutual Research; Japan Ship Machinery Quality Control; Lloyd’s Register of Shipping; Campbell Shillinglaw/ University of Hong Kong; Singapore Institute of Standards and Industrial Research; and The Technical Center for Fire Prevention, The Netherlands. In every case, FOAMGLAS® insulation has been classified “noncombustible.”
ASTM E 84—Surface Burning Characteristics of Building Materials
This test observes the comparative surface burning characteristics of building materials—versus red oak and inorganic reinforced cement board. “Flame spread index” is a comparative, numerical measure relating to the progress of a flame zone. “Surface flame spread” is the advancement of flame away from an ignition source across a specimen’s surface. And, “smoke developed index” is a comparative classification based on smoke obscuration.
Test results for FOAMGLAS® insulation show a smoke density of 0 and a flame spread of 0.
SECTION 4SECTION 4 NONCOMBUSTIBILITYNONCOMBUSTIBILITY
FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
Specifications for Specimens • 3.5” (90 mm) NPS pipe, 4” (102 mm) OD
• Double layers of FOAMGLAS® insulation, each with stainless steel bands, having tightly butted joints, Hydrocal® B-11 bore-coated inner layers, and outer layer joints staggered and sealed with PITTSEAL® 444N sealant
• Galvanized 0.012” (0.305 mm) steel jacketing secured with stainless steel bands on 12” (30.5 cm) centers
Sample Inner Layer Outer Layer Protection Time
A 2" (50 mm) Thick 2" (50 mm) Thick 120 min
B 3" (75 mm) Thick 2" (50 mm) Thick 138 min
C 3" (75 mm) Thick 3" (75 mm) Thick 158 min
Performance
FIGURE 2: ASTM E 119 Performance Test2000°F1093°C
1500°F815°C
1000°F538°C
500°F260°C
20 40 60 80 100 120 140 160 1800Time, Minutes
Sample C
Sample A
Sample B
Avg.PipeTemp.
Tem
pera
ture 1000°F
538°CTemp. Limit
ASTM E 119Standard Time -Temperature Curve
ASTM E 136Noncombustible
ASTM E 84 Flame Spread Smoke Developed 0 0
Material Rating FOAMGLAS® Noncombustible Insulaion Layer
UL1709 (Modified)—Fire Resistance Test for Petrochemical Facility Structural Elements
Unlike most fire ratings developed for interior building fires, this test, specially designed for the unique conditions of a petrochemical plant conflagration, measures the hourly protection afforded steel during a rapid-temperature-rise fire that reaches 2000°F (1093°C) within five minutes. A material’s performance is based on its ability to limit the temperatures measured on a steel member to an average value of 1000°F (538°C). This test is necessary because the burning rate and fuel energy potential at a petrochemical facility—as well as its normal corrosive atmosphere—are totally unlike those with fires involving typical building materials of construction.
Thermocouples monitor the furnace chamber temperature, while temperatures of the steel sample are measured by additional thermocouples within the sample. During the test, the average temperature of the sample must not exceed 1000°F (538°C) and no thermocouple can exceed 1200°F (649°C) within the control period. The furnace used allows the specimen uniform time/temperature exposure.
109
SECTION 4SECTION 4 NONCOMBUSTIBILITYNONCOMBUSTIBILITY
FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
FIGURE 3: UL1709 (Modified) Performance Test
LIQUID TYPE
CyclodecanoneLube Oil
Essential Oils
Coal TarDistillates
Mineral Oil
Low ViscosityTransformer Oil
Therminol
Dowtherm A
Max. Use Temps.#55 #66 #88
0 200 400 600 800 1000Ignition Temperature, °F
FIGURE 4: Ignition Temperatures for Combustible Liquids
100 200 300 400 500 600 700 800 900 1000 1100 1200 1300 1400
100
90
80
70
60
50
40
30
20
10
0
Time, Minutes
Vol
ume
Per
cent
0
Mineral Wool
Calcium Silicate
PerliteFOAMGLAS®
Insulation
FIGURE 5: 10w30 Oil Absorption Rates for Various Materials
Max. UseTemp.
fatty acids, explosives, oxidizers and
chemical intermediates. Consequently,
the effect of these insulation materials
is not only to fail to protect from fire
the system they are insulating, but
also to contribute to fire spread. And,
while such insulations can ignite due
to an external fire source, there are
also certain conditions under which
the combustible fluids within them will
auto-ignite. With applications prone to
leaking organic fluids—valve packing
glands, thermocouple connections,
and equipment flanges, as well as
flat surfaces that collect leakage, the
elevated-temperature petrochemical
environment is particularly ripe for this
clandestine development.
Three FOAMGLAS® insulation systems
have been submitted to this testing as
jacketed double-layer systems on a pipe,
a small column and a large column.
The results are shown in Figure 3.
COMBUSTIBLE FLUID ABSORPTIONFactory Mutual (FM) Engineering and
Research has a document known
as “Loss Prevention Data Sheet:
7-99/12-19, Heat Transfer by Organic
and Synthetic Fluids,” rev. 4/92. The
scope of the document provides
recommendations for the location,
design, operation, maintenance,
inspection and fire protection of systems
circulating heat transfer fluids (HTF).
In the section addressing insulation of
these systems the following is listed:
2.3.7.1 The insulation used to cover
HTF piping and equipment should be
of the type that is nonabsorbent.
Any type of insulation may be used
where the pipe is all welded (i.e.,
without flanged fittings) and where
there are no other sites prone to
leakage such as valves or pumps.
Commonly used insulating materials
are grouped as follows:
NONABSORBENT: closed cell cellular
glass, foamed glass, reflective
aluminum foil or sheets.
ABSORBENT: calcium silicate, 85%
magnesia, glass fiber batts, ceramic
wool, mineral wool, silicate-bonded
asbestos fibers.
WICKING OF ORGANICSThere are several inorganic insulations
that technically are noncombustible—
fiberglass, calcium silicate, mineral wool
and perlite. However, each of these
can absorb, or “wick,” combustible
liquids, such as oils, heat transfer
fluids, resins, solvents, silicones,
AUTO-IGNITIONAuto-ignition appears to result from
slow oxidation between the leaked
organic and air, a temperature buildup
within the saturated insulation, and,
ultimately, spontaneous combustion.
With heat transfer fluids, oxidation
occurs on systems above 500°F
(260°C). Then, with porous insulations,
the combination of a large reaction
surface, vapor volume space, poor
heat dissipation and possible catalysis
by the insulation itself all contribute to
temperature buildup. Finally, when the
insulation is exposed to a large volume
of air during repairs, etc., ignition of the
organic, already above its auto-ignition
temperature (see Figure 4), can occur.
Research has shown that this ignition
temperature can be reduced almost
50% when fluids are absorbed by
insulation.
Noncombustible, nonabsorptive FOAMGLAS® insulation is ideal for
these applications. In fact, the leading
manufacturers of heat transfer fluids are
unanimous in recommending closed-cell
insulation where organic leakage and
contamination are likely. Impermeability
to liquids and air eliminates the risk of
self-heating due to leakage. And, even
in low-temperature service the potential
dangers of condensed hydrocarbon
gases or liquid oxygen are minimized.
This same spontaneous ignition
phenomenon is exhibited by oils, which
have auto-ignition temperatures much
lower than heat transfer fluids. In
fact, studies have shown spontaneous
combustion with oil-soaked lagging at
routine operating temperatures as low
as 176°F (80°C).
Spontaneous ignition has been observed
when liquid loadings occupied 6% to
12% by volume of the void spaces in
insulation. However, tests have shown
10w30 oil absorption rates significantly
higher than this for calcium silicate,
perlite and mineral wool after only a few
hours (see Figure 5). In fact, mineral
wool absorbed almost 90%, by volume,
within minutes. FOAMGLAS® insulation,
however, does not absorb any oil, regardless of time elapsed.
FOAMGLAS® insulation (above) remains non-wicking and non-burning while mineral wool, calcium silicate and two brands of perlite sustain flames from wicking or oil.
Sample Inner Layer Outer Layer Protection Time
Pipe 3" (75 mm) Thick 2" (50 mm) Thick 64 min
Column 2" (50 mm) Thick 2" (50 mm) Thick 122 min
Column 3" (75 mm) Thick 3" (75 mm) Thick 153 min
Performance
2500°F1371°C
2000°F1093°C
1500°F815°C
1000°F538°C
500°F260°C
20 40 60 80 100 120 140 160 1800
Tem
pera
ture
Time, Minutes
Furnace
Pipe
Column with4” thick
FOAMGLAS®
insulation
Columnwith 6” thickFOAMGLAS®
insulation
Specifications for Specimens
Pipe section test—10” • (25.4 cm ø, sch 40 steel pipe columntests—W10 x 49 steel column
Double layers of FOAMGLAS• ® insulation, each with stainless steel bands: Pipe test—Bore coating of
Hydrocal® B-11 applied to both layers Column tests—Layers adhered with PC® 88 adhesive; column voids filled with insulation
Stainless steel 0.016”-thick • (0.406 mm) jacketing secured with 0.5” (12.7 mm) stainless steel bands
1211
SECTION 5SECTION 5 CHEMICAL DURABILITYCHEMICAL DURABILITY
FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
Solvent Polyisocyanurate Polyolefin Polystyrene Phenolic FOAMGLAS®
Insulation
Concentrated Nitric Acid X Dissolved
Concentrated Hydrochloric Acid X X
Concentrated Sulfuric Acid Dissolved X
Concentrated Phosphoric Acid
40% Nitric Acid X Dissolved
10% Hydrochloric Acid X
30% Sulfuric Acid X
5% Carbolic Acid X X
5% Acetic Acid X X X
10% Citric Acid X X
Orange Terpenes X Dissolved
Citrus Peel Oil X Dissolved
Orange Juice X X X
Concentrated Ammonium Hydroxide X X X
Concentrated Potassium Hydroxide X X
10% Ammonium Hydroxide X X
10% Sodium Hydroxide X X X
2% Sodium Carbonate X X
Heptane X X
Methanol X X X
Formaldehyde X X
Dichloromethane X X Dissolved X
Benzene X X Dissolved
Methyl Ethyl Ketone X X Dissolved X
1-Butanol X X
Toluene X X Dissolved
Acetone X X Dissolved X
Ethyl Acetate X X Dissolved X
Mineral Spirits X Dissolved
Ethylene Glycol X X
Kerosene X Dissolved
TABLE 3: Materials Which Showed Significant Changes in Volume and Weight When Immersed in Solvents
All-glass FOAMGLAS® insulation is
unaffected by most chemicals and by
most corrosive plant atmospheres which
can quickly destroy other materials.
CHEMICAL DURABILITY PROBLEMSAn insulation’s chemical durability is
often the most important criterion in
insulation system selection. Chemical
absorption can not only mechanically
destroy an insulation and its thermal
performance, but also increase fire
risk and lead to structural corrosion
of pipelines and equipment. This
potential for chemical attack comes
both externally—from the atmosphere
and spillage, and internally—from the
system being insulated, itself, by way
of leaks at joints, valves or flanges.
Organic Foam InsulationsFoamed plastics are significantly
deteriorated by immersion in chemical
reagents—even water—for just 30
days (see Table 2). Polyisocyanurate
manufacturers’ own literature states
that the material should not be exposed
to any chemicals or solvents which
might soften or degrade the foam.
The literature from one manufacturer
of phenolic foam states that their
product is severely attacked by
concentrated nitric acid and has only
fair to poor resistance to phosphoric
acids, concentrated hydrochloric acid,
10% sodium hydroxide, acetone,
methylated spirits and methyl acetate.
Glass and Mineral FibersWhile these materials are essentially
silicate glass, as is FOAMGLAS®
insulation, their form is a fiber, not a
closed cell. And, when submerged in
water, glass wool loses its strength
and elasticity while mineral fiber
becomes brittle. Both actions subject
the materials to a higher rate of
chemical attack. Also, when the organic
binders that often coat these fibers
are destroyed by heat or chemicals,
these insulations can absorb potentially
hazardous chemicals, as well as water.
Calcium Silicate/PerliteWith these highly absorptive materials,
liquid and vapor absorption not only
cause a significant loss in thermal
efficiency—serious safety and fire
hazards also can exist when acid or
caustic spillage occurs.
Perlite often contains organic-based
water repellents which are rapidly
destroyed by temperatures over 392°F
(200°C) and by petrochemicals; and its
inorganic binders are frequently water-
leachable. The result is an absorptive
insulation.
ONE-HUNDRED-PERCENT GLASSFOAMGLAS® insulation is both
all-glass and closed-cell—a
critical combination for providing
its unmatched chemical durability.
Unlike the other insulating materials
discussed, it has no fibers, binders or
other components subject to chemical
attack or degradation. The chemical
resistance of glass has been universally
recognized and applied for food and
chemical products, laboratory containers
and for industrial applications requiring
exceptional durability.
All-glass FOAMGLAS® insulation is commonly used on chemical storage tanks because its high corrosion resistance extends equipment service life.
CHEMICALLY DURABLE ... CHEMICALLY RESISTANT
1413
SECTION 6SECTION 6 DIMENSIONAL STABILITYDIMENSIONAL STABILITY
FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
DIMENSIONAL STABILITY ENHANCESTHERMAL PERFORMANCE
Proper insulation performance, and thus system integrity, is directly related to the dimensional stability of the insulating material. Poor dimensional stability can cause swelling, expansion, shrinkage and buckling of a system’s insulation. These actions can eventually lead to thermal bridges between insulation and equipment, coating/waterproofing breaches, and, most critically, unpredictable insulation performance.
However, with FOAMGLAS® insulation, all of these potential problems are avoided because of its excellent stability under a variety of temperature and humidity conditions.
FACTORS AFFECTING STABILITYReversible Changes at Low TemperaturesThe rate of reversible, dimensional change—the thermal contraction coefficient—exhibited when an insulation material is cooled is
most often related to its chemical composition. Organics, such as plastic foams, display coefficients five to ten times greater than those of the metals they insulate (see Figure 6). This will result in open joints which not only create a thermal short circuit path but may totally destroy joints that had been sealed against water intrusion. FOAMGLAS® insulation exhibits a predictable, minimal, reversible coefficient of thermal contraction.
Because this expansion is so close to that of the steel and concrete most often being insulated, virtually no relative movement occurs at the insulation joints during system temperature cycling.
At low temperatures, severe shrinkage cracking can also occur within the foam. In tests on a two-layer urethane system under cryogenic conditions, the joints opened enough to permit convection
and substantial heat gain (+174% on liquid nitrogen systems), while with polystyrene insulation, open joints reduced thermal efficiency about 10%.
Reversible Changes at Moderate TemperaturesAt elevated temperatures the problem is reversed; the high thermal expansion coefficient of organic foams (see Figure 7) can lead to warping and buckling, putting severe stress on weather barriers and vapor retarders. In contrast, FOAMGLAS® insulation remains stable since it is well matched in expansion coefficient to typical steel piping and equipment.
Irreversible Changes at High TemperaturesAt high temperatures, inorganic insulation must be used. And unfortunately, as temperatures rise and metal pipes and vessels expand, some insulations actually shrink (see Figure 7). This shrinkage leads to open joints and cracks which can cause thermal short circuits and serious damage to weather barriers. FOAMGLAS® insulation has a reversible coefficient of expansion similar to metals and will not shrink.
Other Irreversible ChangesThese permanent dimensional changes have many causes, including aging of the insulation material—i.e., the post-production shrinkage of plastic foams (particularly polyurethane), blistering with foamed-in-place PUR, and outgassing of foaming agents from expanded polystyrene causing shrinkage of up to 2%. On cold systems, low-density polyurethane’s in-cell gases can condense, break down cell walls and lead to insulation collapse.
50 0 -50 -100 -150 -200 -250 -300
-1.0
-2.0
-3.0
-4.0
-5.0
-6.0
Temperature (°F)
(in
./10
0 lin
. ft.
)
FOAMGLAS®
Insulation
Steel
StainlessSteel
PolystyrenePhenolic
Polyisocyanurate
FIGURE 6: Thermal Contraction of Insulations versus Steel(70°F to -300°F)
FIGURE 6A: Coefficient of Thermal ExpansionThe coefficient of thermal expansion of FOAMGLAS® celular glass is given by the following graph. As can be seen, it slightly increases with the higher temperature and decreases more sharply a low temperature.
-200 -100 0 100 200 300 400
109.5
98.5
87.5
76.5
65.5
54.5
4
Temperature in º C
10-6 K-1
Temperature and HumidityMoisture can enter some insulations during its storage, transportation or installation, then can be trapped by waterproofing or admitted by malfunctioning vapor barriers. Combined with temperature changes, a significant alteration of insulation dimensions can occur.
Polyurethane at 158°F (70°C) and 85% relative humidity shows an irreversible expansion of 3% (one manufacturer states that even greater changes are possible). On the other hand, under similar conditions phenolic foams shrink up to 2%. Polyisocyanurate is affected by humid aging. Its rapid, permanent warping puts severe stress on external vapor and weather barriers.
But with FOAMGLAS® insulation, service and testing have again proven that it remains dimensionally stable under extreme humidity. Testing at 68°F (20°C) and 95% relative humidity have shown no changes in the material.
+8.0
+6.0
+4.0
+2.0
0
-2.0
-4.0
-6.0
100 200 300 400 500 600 700 800
Steel
(in
./10
0 lin
. ft.
)
Calcium Silicate
Expanded Perlite
MineralWool
Phenolic
Polyisocyanurate
Polystyrene
StainlessSteel
FOAMGLAS®
Insulation
Temperature (°F)
FIGURE 7: Thermal Expansion/Contraction of Insulations versus Steel (70°F to 800°F)
Temperature and LoadingLoad on an insulation at elevated temperatures is a potential source of dimensional change with possibly severe consequences. Therefore, foamed plastics manufacturers publish temperature-related load recommendations. The combination of FOAMGLAS® insulation’s high-temperature resistance, rigidity and strength (discussed later), however, creates excellent dimensional stability under load at low, ambient or high temperatures.
High-Temperature SystemsSee page 20 for recommended systems.
When exposed to laboratory heat lamps, polyisocyanurate (top) and polystyrene (middle) both exhibit significant thermal distortion. FOAMGLAS® insulation (bottom) remains dimensionally stable.
DIMENSIONAL STABILITY SECTION 6SECTION 6 DIMENSIONAL STABILITY
1615 FOAMGLAS® INSULATION SYSTEMSFOAMGLAS® INSULATION SYSTEMS
18
SECTION 8VERMIN RESISTANCE
FOAMGLAS® INSULATION SYSTEMS
Grades of FOAMGLAS® InsulationFOAMGLAS® insulation, with a
compressive strength of 90 psi
(6.3 kg/cm2) and itself stronger than
almost every other insulation material,
is just one of seven grades available,
ranging up to FOAMGLAS® HLB 1600
(High-Load Bearing) insulation with a
compressive strength of 232 psi (16.3
kg/cm2) (see Table 4). The full family
of FOAMGLAS® insulation is available
worldwide. Where high loading is
anticipated, consideration should be
given to adequate surface preparation
to avoid undue overstresses.
Problems and ApplicationsTanksFor low- and cryogenic-temperature
tank bottom applications, the use of
insulation lacking proper compressive
strength can allow settlement. In turn,
this can result in lost thermal efficiency,
ground heaving and elevation of
foundation temperatures that may cause
major failures, including bottom rupture.
Because of its compressive strength,
FOAMGLAS® insulation has been the
dominant choice for base applications on
LPG, LNG, LOX, ammonia, ethylene and
liquid nitrogen tanks. In fact, it has been
installed on over 80% of the world’s
above-ground cryogenic storage tanks.
With high-temperature tank bases, an
insulation’s poor compressive strength
can also lead to settlement. The
resulting thermal performance loss can
unstabilize the processing environment
causing reduced viscosity control and
possible solidification of the contents.
Again, FOAMGLAS® insulation is ideal for
these hot base applications.
Underground Systems and Pipe Support and Hanger ApplicationsSee page 31.
FOAMGLAS® insulation has been installed in over 75% of the world's LNG tanks.
FOAMGLAS® insulation provides constant thermal efficiency for LNG transfer and storage facilities. Because of its compressive strength, it withstands extreme loads without deterioration and can be used on long vertical pipe runs without special supports.
VERMIN RESISTANTAn insulation’s resistance to vermin—rats, mice, insects and fungi—is often given little consideration during material specification. But this “out of sight, out of mind” potential problem can lead to serious trouble for underground piping and storage vessels, agricultural/ food processing buildings and exterior industrial applications. Gnawing, boring, nesting and microbial infestation can seriously affect thermal performance and mechanical strength to the point of complete destruction of the insulating system. Organic and open-structured insulations, by their physical form encourage nesting and tunneling. However, over 50 years of testing and field applications have proven FOAMGLAS® insulation’s superior, total vermin resistance.
Three-Fold ProblemAs insulation is attacked by vermin and partially or totally destroyed, thermal efficiency suffers or is rendered totally lost. Secondly, there are the resulting, potentially enormous economic losses, including increased energy consumption, repair cost of the equipment or installations damaged by gnawing, and even infrastructure loss and the compromise of products produced or stored at the facility. And, finally, there is the possibility of transmission of infectious diseases to humans and domestic animals through contamination of food products, or via airborne microorganisms, with chilled or hot water and HVAC systems.
The “Vermin Barrier”With FOAMGLAS® insulation in place, not only are the potential vermin problems found with other materials eliminated, but the presence of cellular glass can even provide a physical barrier blocking the entrance of mice, rats, etc. To view the total resistance of FOAMGLAS® insulation to rodents another way: its vermin endurance is so great that it can be categorized with concrete, sheet metal and glass—which is, of course, what FOAMGLAS® insulation is—as a building material that discourages gnawing.
TABLE 4: Compressive Strengths of Various Materials
Insulation Compressive Strength Density
Material psi kPa lb/ft3 Kg/m3
FOAMGLAS® Insulation 90 600 7.5 120Polyisocyanurate 30 207 2.0 32Polystyrene 45 310 2.0 32Phenolic 22@10% def. 152 2.5 40Fiberglass 2.3@10% def. 16 6.0 96Mineral Fiber 10@10% def. 69 5–15 80–240Calcium Silicate 100@5% def. 689 11–15 176–240Perlite 80@5% def. 620 5–13 80–208
DENSITY AND COMPRESSIVE STRENGTH
Grade of Nominal Compressive StrengthFOAMGLAS® Lot Avg. (Tested According to ASTM C 165/C 240)HLB Density Average Lower Spec. LimitInsulation
kg/m3 pcf N/mm2 psi kg/cm2 N/mm2 psi kg/cm2
HLB 800 120 7.5 0.80 116 8.12 0.55 80 5.6
HLB 1000 130 8.1 1.00 145 10.15 0.69 100 7.0
HLB 1200 140 8.7 1.20 174 12.18 0.83 120 8.4
HLB 1600 160 10 1.60 232 16.24 1.10 160 11.2
TABLE 5: Physical Properties of FOAMGLAS® HLB Cellular Glass InsulationThe following is a summary of the acceptance values for lot average compressive strength as defined in the Quality Assurance Specifications.
Note: 0.8 N/mm2 = 800 kPA
HIGH COMPRESSIVE STRENGTHWITHOUT DEFORMATION
Because commonly used insulations,
such as fibrous materials, have limited
compressive strength, the property
is often not seriously considered
when specifying thermal insulation.
This is a critical mistake, for in many
applications insulation strength is vital to system performance and should be a
prerequisite when selecting materials.
FOAMGLAS® insulation provides a
compressive strength of 90 psi (620
kPa) when capped according to ASTM C
240. When capped, it provides high
compressive strength without deforming
or consolidating (see Table 3). And
FOAMGLAS® insulation combines rigidity
with its outstanding compressive and
flexural strengths. In addition, its
relative light weight of 7.5 lb/ft3 (120 kg/
m3) gives an ideal strength-to-weight
ratio; lighter materials have a fraction
of FOAMGLAS® insulation’s strength.
This combination of properties—virtually
unaffected by temperatures over a wide
service range—allows simplified design
for load-bearing insulation systems.
Compressive Strength versus DeformationWhile compressive strength technically
measures the stress at which a material
fails under load, deformation monitors
a material’s structural distortion with or without actual failure. So, with
compressible insulations, such as
foamed plastics, fibrous glass and
calcium silicate, “failure” is recorded
as the point when an insulation’s
deformation reaches a percentage of
its thickness—usually between 5% and
25%—for various densities.
With FOAMGLAS® insulation, however,
the data is totally nonsubjective,
making its specification a relatively
uncomplicated, direct calculation.
Deformation is insignificant and
independent of insulation thickness.
Time and Temperature EffectsAdding to compressive strength
ambiguities are the effects of time and
temperature. Studies have shown that
for phenolics and urethanes compressive
strength at 10% deformation is
reduced by greater than 50% with a
temperature increase from 68°F to
266°F (20°C to 130°C). In other tests
of polyurethane foam, when under a
moderate 3 psi (0.2 kg/cm2) load at
266°F (130°C), thickness deformation
of up to 10% developed after just 75
days. That deformation puts urethane
at its maximum compression tolerance,
according to some test methods, in less
than three months.
With FOAMGLAS® insulation, time and
temperature have a negligible effect
on creep and compressive strength
throughout the insulation’s wide service
temperature range.
Safety FactorsBecause deformation and resulting
strength reduction can seriously affect
performance of some compressible
insulations, higher engineering safety
factors are generally required with
cellular plastics and fibrous materials.
COMPRESSIVE STRENGTHSECTION 7
17 FOAMGLAS® INSULATION SYSTEMS
19
SECTION 9 PROPERTIES AND CERTIFICATIONS
FOAMGLAS® INSULATION SYSTEMS
Partial Certifications* and Approvals ListFOAMGLAS® insulation can be certified to conform to the requirements of:
ASTM C 552 “Specification for Cellular Glass • Thermal Insulation”
Canadian Standard CAN/CGSB51.38M•
Military Specification MIL-I-24244C, “Insulation • Materials, Thermal, with Special Corrosion and Chloride Requirement”
Nuclear Regulatory Guide 1.36, ASTM C 795, • C 692, C 871
Flame Spread 5, Smoke Developed 0 (UL 723, • ASTM E 84), UL R2844; also classified by UL of Canada
ISO 9001:2000•
Through-Penetration Firestop Systems UL 1479 • (www.ua.com)
UL Through-Penetration Firestop Approved Systems For a listing of UL Through-Penetration Firestop Approved Systems please search the UL Database at http://www.ul.com. Once on this page click on CERTIFICATIONS on the left hand side. Under General Search click on UL FILE NUMBER and type in R15207 and then SEARCH.
Board of Steamship Inspection (Canada) • Certificate of Approval No. 100/F1-98
General Services Administration, PBS • (PCD): 15250, Public Building Service Guide Specification, “Thermal Insulation (Mechanical)”
New York City Dept. of Bldgs., MEA #138-81-M • FOAMGLAS® insulation for piping, equipment, walls and ceilings
New York State Uniform Fire Prevention • and Building Code Dept. of State (DOS) 07200-890201-2013
City of Los Angeles General Approval RR22534•
U.S. Coast Guard•
Rosstroy•
SINTEF•
NORSOK•
Det Norske Veritas•
See-Berufsgenossenschaft•
Allgemeine Bauaufsichtliche • Zulassung (ABZ, DIBTt)
DCC•
Russian Maritime•
Allgemeine Bauaufsichtliche • Prufzeugnisse (ABP, MPA)
FOAMGLAS® insulation is identified by Federal Supply Code for Manufacturers (FSCM 08869)
*Written request for certificate of compliance must accompany order
PROPERTIES AND CERTIFICATIONSOF FOAMGLAS® INSULATION
FIGURE 8: Thermal Conductivity of FOAMGLAS® Insulation
20
SECTION 9PROPERTIES AND CERTIFICATIONS
FOAMGLAS® INSULATION SYSTEMS
NOMINAL NOMINAL NOMINAL NOMINAL NOMINAL NOMINAL NOMINAL PIPE SIZES 1.5" 2" 2.5" 3" 3.5" 4"
O.D. of O.D. of O.D. of O.D. of O.D. of O.D. of Covering Covering Covering Covering Covering Covering O.D. O.D. Nominal inch mm DN inch mm inch mm inch mm inch mm inch mm inch mm
1/4 0.540 14 8 3.50 89 4.50 114 5.56 141 6.62 168 7.62 194 8.62 219 3/8 0.675 17 10 4.00 102 5.00 127 5.56 141 6.62 168 7.62 194 8.62 219 1/2 0.840 21 15 4.00 102 5.00 127 6.62 168 7.62 194 8.62 219 9.62 244 3/4 1.050 27 20 4.00 102 5.00 127 6.62 168 7.62 194 8.62 219 9.62 244 1 1.315 33 25 4.50 114 5.56 141 6.62 168 7.62 194 8.62 219 9.62 244
1-1/4 1.660 42 32 5.00 127 5.56 141 6.62 168 7.62 194 8.62 219 9.62 244 1-1/2 1.900 48 40 5.00 127 6.62 168 7.62 194 8.62 219 9.62 244 10.75 273 2 2.375 60 50 5.56 141 6.62 168 7.62 194 8.62 219 9.62 244 10.75 273 2-1/2 2.875 73 65 6.62 168 7.62 194 8.62 219 9.62 244 10.75 273 11.75 298 3 3.500 89 80 6.62 168 7.62 194 8.62 219 9.62 244 10.75 273 11.75 298
3-1/2 4.000 102 90 7.62 194 8.62 219 9.62 244 10.75 273 11.75 298 12.75 324 4 4.500 114 100 7.62 194 8.62 219 9.62 244 10.75 273 11.75 298 12.75 324 4-1/2 5.000 127 115 8.62 219 9.62 244 10.75 273 11.75 298 12.75 324 14.00 356 5 5.563 141 125 8.62 219 9.62 244 10.75 273 11.75 298 12.75 324 14.00 356 6 6.625 168 150 9.62 244 10.75 273 11.75 298 12.75 324 14.00 356 15.00 381
7 7.625 194 10.75 273 11.75 298 12.75 324 14.00 356 15.00 381 16.00 406 8 8.625 219 200 11.75 298 12.75 324 14.00 356 15.00 381 16.00 406 17.00 432 9 9.625 244 12.75 324 14.00 356 15.00 381 16.00 406 17.00 432 18.00 457 10 10.750 273 250 14.00 356 15.00 381 16.00 406 17.00 432 18.00 457 19.00 483 11 11.750 298 15.00 381 16.00 406 17.00 432 18.00 457 19.00 483 20.00 508
12 12.750 324 300 16.00 406 17.00 432 18.00 457 19.00 483 20.00 508 21.00 533 14 14.000 356 350 17.00 432 18.00 457 19.00 483 20.00 508 21.00 533 22.00 559 15 15.000 381 18.00 457 19.00 483 20.00 508 21.00 533 22.00 559 23.00 584 16 16.000 406 400 19.00 483 20.00 508 21.00 533 22.00 559 23.00 584 24.00 610 17 17.000 432 20.00 508 21.00 533 22.00 559 23.00 584 24.00 610 25.00 635
18 18.000 457 450 21.00 533 22.00 559 23.00 584 24.00 610 25.00 635 26.00 660 19 19.000 483 22.00 559 23.00 584 24.00 610 25.00 635 26.00 660 27.00 686 20 20.000 508 500 23.00 584 24.00 610 25.00 635 26.00 660 27.00 686 28.00 711 21 21.000 533 24.00 610 25.00 635 26.00 660 27.00 686 28.00 711 29.00 737 22 22.000 559 25.00 635 26.00 660 27.00 686 28.00 711 29.00 737 30.00 762
23 23.000 584 26.00 660 27.00 686 28.00 711 29.00 737 30.00 762 31.00 787 24 24.000 610 600 27.00 686 28.00 711 29.00 737 30.00 762 31.00 787 32.00 813
TABLE 8: Pipe Insulation Dimensional Standards (Metric)
Sizes in this area are furnished in segmental form. (Number of segments vary with pipe O.D.)
Sizes in this area are furnished in sectional form.
Pipe InsulationWhen requested by the purchaser,
FOAMGLAS® pipe and tubing insulation
can be fabricated worldwide in
accordance with ASTM Standard C 552
and C 585. Specifying FOAMGLAS® pipe
and tubing insulation in accordance with
these standards will ensure proper fit to
pipe or tubing and nesting in multiple
layer applications. Minimum single layer
thickness is 1.5” (38 mm).
In Accordance with ASTM C 585
For your convenience, the following
table lists the suggested single layer
thickness of FOAMGLAS® insulation,
to a maximum of 4” (100 mm). The
use of this table permits nesting or
construction of multiple layer assembles
in order to obtain greater thicknesses.
TABLE 7: Pipe Insulation Dimensional Standards (English)
Sizes in this area are furnished in segmental form. (Number of segments vary with pipe O.D.)
Sizes in this area are furnished in sectional form.
NOMINAL PIPE SIZES NOMINAL NOMINAL NOMINAL NOMINAL NOMINAL NOMINAL (inches) 1.5" 2" 2.5" 3" 3.5" 4"
1/4 0.540 1.47 3.50 1.97 4.50 2.50 5.56 3.03 6.62 3.53 7.62 4.03 8.62 3/8 0.675 1.66 4.00 2.16 5.00 2.44 5.56 2.97 6.62 3.47 7.62 3.97 8.62 1/2 0.840 1.57 4.00 2.07 5.00 2.89 6.62 3.39 7.62 3.89 8.62 4.38 9.62 3/4 1.050 1.47 4.00 1.97 5.00 2.79 6.62 3.29 7.62 3.78 8.62 4.28 9.62 1 1.315 1.58 4.50 2.12 5.56 2.67 6.62 3.15 7.62 3.65 8.62 4.15 9.62
1-1/4 1.660 1.67 5.00 1.94 5.56 2.49 6.62 2.97 7.62 3.47 8.62 3.97 9.62 1-1/2 1.900 1.54 5.00 2.36 6.62 2.86 7.62 3.36 8.62 3.86 9.62 4.43 10.75 2 2.375 1.58 5.56 2.11 6.62 2.61 7.62 3.11 8.62 3.61 9.62 4.17 10.75 2-1/2 2.875 1.87 6.62 2.37 7.62 2.87 8.62 3.37 9.62 3.94 10.75 4.44 11.75 3 3.500 1.56 6.62 2.05 7.62 2.55 8.62 3.05 9.62 3.61 10.75 4.11 11.75
3-1/2 4.000 1.80 7.62 2.30 8.62 2.80 9.62 3.36 10.75 3.86 11.75 4.36 12.75 4 4.500 1.55 7.62 2.05 8.62 2.56 9.62 3.11 10.75 3.61 11.75 4.11 12.75 4-1/2 5.000 1.78 8.62 2.28 9.62 2.84 10.75 3.34 11.75 3.84 12.75 4.49 14.00 5 5.563 1.49 8.62 1.99 9.62 2.56 10.75 3.06 11.75 3.56 12.75 4.18 14.00 6 6.625 1.47 9.62 2.03 10.75 2.53 11.75 3.03 12.75 3.66 14.00 4.16 15.00
7 7.625 1.53 10.75 2.03 11.75 2.53 12.75 3.16 14.00 3.66 15.00 4.16 16.00 8 8.625 1.53 11.75 2.03 12.75 2.66 14.00 3.16 15.00 3.66 16.00 4.16 17.00 9 9.625 1.53 12.75 2.16 14.00 2.66 15.00 3.06 16.00 3.66 17.00 4.16 18.00 10 10.750 1.58 14.00 2.08 15.00 2.58 16.00 3.08 17.00 3.58 18.00 4.08 19.00 11 11.750 1.58 15.00 2.08 16.00 2.58 17.00 3.08 18.00 3.58 19.00 4.08 20.00
12 12.750 1.58 16.00 2.08 17.00 2.58 18.00 3.08 19.00 3.50 20.00 4.08 21.00 14 14.000 1.50 17.00 2.00 18.00 2.50 19.00 3.00 20.00 3.50 21.00 4.00 22.00 15 15.000 1.50 18.00 2.00 19.00 2.50 20.00 3.00 21.00 3.50 22.00 4.00 23.00 16 16.000 1.50 19.00 2.00 20.00 2.50 21.00 3.00 22.00 3.50 23.00 4.00 24.00 17 17.000 1.50 20.00 2.00 21.00 2.50 22.00 3.00 23.00 3.50 24.00 4.00 25.00
18 18.000 1.50 21.00 2.00 22.00 2.50 23.00 3.00 24.00 3.50 25.00 4.00 26.00 19 19.000 1.50 22.00 2.00 23.00 2.50 24.00 3.00 25.00 3.50 26.00 4.00 27.00 20 20.000 1.50 23.00 2.00 24.00 2.50 25.00 3.00 26.00 3.50 27.00 4.00 28.00 21 21.000 1.50 24.00 2.00 25.00 2.50 26.00 3.00 27.00 3.50 28.00 4.00 29.00 22 22.000 1.50 25.00 2.00 26.00 2.50 27.00 3.00 28.00 3.50 29.00 4.00 30.00
23 23.000 1.50 26.00 2.00 27.00 2.50 28.00 3.00 29.00 3.50 30.00 4.00 31.00 24 24.000 1.50 27.00 2.00 28.00 2.50 29.00 3.00 30.00 3.50 31.00 4.00 32.00
Act
ual
O.D
.
FOA
MG
LAS
®
Thic
knes
s
O.D
. o
fC
ove
rin
g
FOA
MG
LAS
®
Thic
knes
s
O.D
. o
fC
ove
rin
g
FOA
MG
LAS
®
Thic
knes
s
O.D
. o
fC
ove
rin
g
FOA
MG
LAS
®
Thic
knes
s
O.D
. o
fC
ove
rin
g
FOA
MG
LAS
®
Thic
knes
s
O.D
. o
fC
ove
rin
g
FOA
MG
LAS
®
Thic
knes
s
O.D
. o
fC
ove
rin
g
No
min
alO
.D.
FOAMGLAS® cellular glass insulation is manufactured in 12” x 18” (305 mm x 457 mm) blocks, 1-1/2” (38 mm) through 5” (127 mm) thick, in 1/2” (13 mm) increments and in 18” x 24” (600 mm x 450 mm) blocks 2” (51 mm) through 6” (150 mm) thick in 1/2” (13 mm) increments. For the nearest source of FOAMGLAS® insulation, contact your Pittsburgh Corning representative.
FOAMGLAS® insulation is fabricated into coverings for virtually all standard pipes, valves, fittings, and curved segments, and beveled head and lag segments. Contact your Pittsburgh Corning representative for the nearest fabricating distributor. FOAMGLAS® insulation shapes can be easily modified on-site with ordinary hand tools to insulate valves, tees, flanges, etc.
TABLE 6: Physical and Thermal Properties of FOAMGLAS® ONETM Insulation
ASTM EN ISO PHYSICAL PROPERTIES
SI ENGLISH Method Method
0.2% 0.2% C 240 EN 1609 EN 12087 Absorption of Moisture
(Water % by Volume) Only moisture retained is that adhering to surface cells after immersion
Water-Vapor Permeability 0.00 perm-cm 0.00 perm-in E96
Wet Cup Procedure B
EN 12086 EN ISO 10456
Acid Resistance Impervious to common acids and their fumes except hydrofluoric acid
Capillarity None
Combustibility & Reaction to Fire
Noncombustible - will not burn Flame Spread 0
Smoke Development 0
E 136 E84
EN ISO 1182 (Class A1)
Composition Soda-lime silicate glass – inorganic with no fibers or binders 620 kPa 90 psi
Compressive Strength, Block Strength for flat surfaces capped with hot asphalt.
C 165 C 240 C 552
EN 826 Method A
Density 120 kg/m3 7.5 lb/ft3 C 303 EN 1602
Dimensional Stability Excellent—does not shrink, swell or warp EN 1604
(DS 70/90)
Flexural Strength, Block 480 kPa 70 psi C 203 C 240
EN 12089 (BS450)
Hygroscopicity No increase in weight at 90% relative humidity Linear Coefficient of Thermal Expansion
9.0 x 10-6/K 25ºC to 300ºC
5.0 x 10-6/°F 75°F to 575°F
E 228 EN 13471
Maximum Service Temperature 482˚ C 900˚ F
Modulus of Elasticity, Approx. 900 MPa 1.3 x 105 psi C 623 EN 826
Method A1
Thermal Conductivity W/mK
0.040 @ 10°C 0.042 @ 24°C
Btu-in/hr.ft2.°F 0.28 @ 50°F 0.29 @ 75°F
C 177 C 518
EN 12667 EN 12939
( D (90/90) 0.041 W/mK @ 10˚ C) Specific Heat 0.84 kJ/kg.K 0.18 Btu/lb.°F Thermal Diffusivity 4.2 x 10-7 m2/sec 0.016 ft2/hr
Note: FOAMGLAS® ONE™ is manufactured to meet or exceed the minimum requirements of ASTM C552-07 Standard Specification for Cellular Glass Insulation (or most recent revision). Unless otherwise specified, measurements were collected using ASTM guidelines at 24°C (75ºF) and are average or typical values recommended for design purposes and not intended as specification or limit values. Values under EN ISO are declared as limit values under the specific set of standard test conditions. Properties may vary with temperature. Where testing method or reporting values differ between ASTM and EN ISO methodologies, values are denoted within parentheses in the EN ISO column.
PHYSICAL AND THERMAL PROPERTIES OF FOAMGLAS® ONE™ INSULATION
21
SECTION 10 SELECTION GUIDE
FOAMGLAS® INSULATION SYSTEMS
Recommended Temperature System Benefits Range
FABRICATED FOAMGLAS® INSULATION SYSTEMS
Bitumen BondedSingle or multiple layers ofFOAMGLAS® insulation fabricated with hot asphalt (ASTM D 312, Type III) in all joints.
Hydrocal® B-11* BondedSingle or multiple layers ofFOAMGLAS® insulation fabricated with a special inorganic adhesive.
*A product of U.S. Gypsum Co.
StrataFab® SystemA patented method of fabricatingFOAMGLAS® insulation by bondingblocks together with a high-temperature-resistant, flexibleadhesive to create a uniform, multi-layered stack from which are cut the desired insulation shapes.
Composite SystemInsulation consisting of innerlayer(s) of high-density fibrous glass blanket or mineral wool and outer layer(s) ofFOAMGLAS® insulation.
• Standard, readily available fabrication technique for cold to moderately warm applications.
• Fabrication technique allows usage over broadest temperature range.
• Minimal breakage during shipment and installation.
• Can be installed directly on hot surfaces.
• Provides excellent control of stress relief cracking.
• Wide range of thickness eliminates need for double layering.
• Fabrication technique allows usage on systems:
– undergoing continuous thermal cycling.
– undergoing excessive vibration.
– operating above 900°F (482°C).
-290°F (-179°C) to
250°F (121°C)
251°F (122°C) to
400°F (204°C)
-450°F (-268°C) to
Ambient
Ambient to
900°F (482°C)
-100°F (-73°C) to
Ambient
Ambient to
900°F (482°C)
401°F (205°C) to
1200°F (649°C)
22
SECTION 10SELECTION GUIDE
FOAMGLAS® INSULATION SYSTEMS
Limits
FOAMGLAS® insulation was installed as part of a composite insulation system. It incorporates a one-inch layer of fibrous glass felt material directly around the pipe, covered with FOAMGLAS® insulation.
StrataFab® sections were installed in succession and butted against one another with PITTWRAP® butt stripes at the interfaces, and heat sealed.
• Do not use at or below temperatures where liquid oxygen (LOX) will form (-297°F/-183°C).
• When above ground, recommended only in well ventilated areas.
• Bonding adhesive softens and may smoke in contact with hot surfaces above 125°F (52°C).
• Where stainless steel stress corrosion potential exists, contact your PCC representative.
• Joint zone is permeable to water vapor below ambient. Use a double layer system, seal joints of outer layer with PITTSEAL® 444N, cover with a vapor retarder finish.
• Where stainless steel stress corrosion potential exists, contact your PCC representative.
• Use a double layer system at temperatures above 400°F (204°C).
• Joint zone is permeable to water vapor below ambient. Use a double layer system, seal joints of outer layer with PITTSEAL® 444N, cover with a vapor retarder finish.
• When used in a tunnel, vault, or other confined air space, ventilation is recommended. Bonding adhesive may smoke in contact with shot surfaces above 125°F (52°C). See MSDS for safe handling and use.
• Not for service on systems containing combustible liquids.
23
SECTION 11 TEMPERATURE LIMITS
FOAMGLAS® INSULATION SYSTEMS
RECOMMENDED LOWER PIPE TEMPERATURELIMITS TO PREVENT CONDENSATION
24
SECTION 11TEMPERATURE LIMITS
FOAMGLAS® INSULATION SYSTEMS
FOAMGLAS® INSULATION THICKNESS, MM NPS 25.4 38.1 50.8 63.5 76.2 88.9 101.6 114.3 127.0 139.7 152.4 165.1 177.8 190.5 203.2 215.9 228.6 241.3 254.0 279.4 304.8 0.50 -10 -37 -67 -128 -176 -237 0.75 -4 -28 -54 -107 -148 -198 -262 1.00 -9 -29 -56 -87 -122 -164 -216 1.50 -4 -22 -58 -85 -116 -153 -203 -259 2.00 -3 -20 -41 -64 -90 -121 -161 -204 -257
2.50 -2 -28 -48 -70 -96 -130 -165 -207 3.00 0 -15 -32 -51 -73 -101 -129 -163 -213 -262 4.00 0 -13 -28 -45 -68 -90 -115 -152 -187 -228 5.00 1 -10 -24 -42 -61 -81 -110 -136 -167 -202 -243 6.00 3 -8 -23 -38 -55 -79 -100 -125 -152 -183 -219 -262
8.00 -8 -21 -38 -54 -71 -90 -112 -136 -162 -193 -228 10.00 -9 -21 -34 -48 -64 -81 -100 -121 -145 -171 -201 -236 12.00 -8 -19 -32 -45 -60 -77 -94 -114 -136 -160 -188 -220 -256 14.00 -5 -16 -28 -41 -55 -70 -87 -106 -126 -149 -175 -204 -237 16.00 -4 -15 -27 -39 -53 -67 -84 -102 -121 -143 -167 -194 -224 -259
18.00 -4 -14 -26 -38 -51 -66 -81 -98 -117 -138 -161 -186 -215 -247 20.00 -3 -14 -25 -37 -50 -64 -79 -96 -114 -134 -156 -180 -207 -237 24.00 -3 -13 -24 -36 -48 -62 -76 -92 -109 -128 -148 -170 -195 -223 -254 28.00 -3 -13 -23 -35 -47 -60 -74 -89 -105 -123 -142 -163 -187 -213 -241 30.00 -3 -13 -23 -34 -46 -59 -73 -88 -104 -121 -140 -161 -183 -208 -236
36.00 -3 -12 -23 -34 -45 -58 -71 -85 -100 -117 -135 -154 -175 -198 -224 -253 42.00 -2 -12 -22 -33 -44 -56 -69 -83 -98 -114 -131 -149 -169 -191 -216 -242 48.00 -2 -12 -22 -32 -44 -56 -68 -82 -96 -111 -128 -146 -165 -186 -209 -235 -263 60.00 -2 -12 -21 -32 -43 -54 -66 -79 -93 -108 -124 -141 -159 -179 -200 -224 -249 72.00 -2 -11 -21 -31 -42 -53 -65 -78 -91 -106 -121 -137 -155 -174 -194 -216 -241
96.00 -2 -11 -21 -31 -41 -52 -64 -76 -89 -103 -117 -133 -149 -167 -186 -207 -230 -254120.00 -2 -11 -20 -30 -41 -52 -63 -75 -88 -101 -115 -130 -146 -163 -182 -201 -223 -246168.00 -2 -11 -20 -30 -40 -51 -62 -74 -86 -99 -113 -127 -143 -159 -176 -195 -215 -237 FLAT -2 -10 -20 -29 -39 -49 -60 -71 -82 -94 -107 -120 -133 -148 -163 -180 -197 -215 -256
TABLE 9: Metric (°C)SEVERE INDOOR DESIGN CONDITIONS: 26.7°C Ambient • 80.0% Relative Humidity • 22.9°F Dew Point • 0.0 kmph Wind Velocity • 0.90 Emittance
MINIMUM HEAT GAIN=20.5 KCAL/HR SQM • MAXIMUM HEAT GAIN=25.4 KCAL/HR SQM
FOAMGLAS® INSULATION THICKNESS, INCHES NPS 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 6.0 6.5 7.0 7.5 8.0 8.5 9.0 9.5 10.0 11.0 12.0 0.50 15 -35 -85 -195 -285 -395 0.75 25 -15 -65 -160 -235 -325 -440 1.00 15 -20 -65 -125 -185 -260 -355 1.50 25 -5 -70 -120 -175 -240 -330 -430 2.00 30 -5 -40 -80 -130 -185 -255 -335 -430
2.50 30 -15 -50 -95 -140 -200 -265 -340 3.00 35 5 -25 -60 95 -150 -200 -260 -350 -440 4.00 35 10 -15 -50 -90 -130 -175 -240 -305 -375 5.00 35 15 -10 -45 -75 -110 -165 -210 -265 -330 -405 6.00 40 20 -10 -35 -65 -110 -145 -190 -240 -295 -360 -435
8.00 20 -5 -35 -65 -95 -130 -170 -210 -260 -315 -375 10.00 15 -5 -25 -55 -80 -115 -145 -185 -225 -275 -330 -390 12.00 20 0 -25 -50 -75 -105 -135 -170 -210 -255 -305 -360 -425 14.00 25 5 -15 -40 -65 -95 -125 -155 -195 -235 -280 -335 -390 16.00 25 5 -15 -35 -60 -90 -115 -150 -185 -225 -265 -315 -370 -435
18.00 25 5 -10 -35 -60 -85 -115 -145 -175 -215 -255 -300 -355 -410 20.00 25 10 -10 -35 -55 -80 -110 -140 -170 -205 -245 -290 -340 -395 24.00 25 10 -10 -30 -55 -75 -105 -130 -165 -195 -235 -275 -320 -370 -425 28.00 25 10 -10 -30 -50 -75 -100 -125 -155 -190 -225 -260 -300 -350 -400 30.00 30 10 -10 -30 -50 -75 -100 -125 -155 -185 -220 -255 -295 -340 -390
36.00 30 10 -5 -25 -50 -70 -95 -120 -145 -175 -210 -245 -280 -325 -370 -420 42.00 30 10 -5 -25 -45 -70 -90 -115 -145 -170 -200 -235 -270 -310 -355 -405 48.00 30 10 -5 -25 -45 -65 -90 -115 -140 -165 -195 -230 -265 -300 -345 -390 -440 60.00 30 10 -5 -25 -45 -65 -85 -110 -135 -160 -190 -220 -250 -290 -325 -370 -415 72.00 30 10 -5 -25 -40 -60 -85 -105 -130 -155 -185 -215 -245 -280 -315 -355 -400
96.00 30 15 -5 -20 -40 -60 -80 -105 -125 -150 -180 -205 -235 -265 -300 -340 -380 -425120.00 30 15 -5 -20 -40 -60 -80 -100 -125 -150 -175 -200 -230 -260 -295 -330 -370 -410168.00 30 15 -5 -20 -40 -60 -80 -100 -120 -145 -170 -195 -225 -250 -285 -320 -355 -395 FLAT 30 15 0 -20 -35 -55 -75 -95 -115 -135 -160 -180 -205 -235 -260 -290 -320 -355 -425
TABLE 9: English (°F)SEVERE INDOOR DESIGN CONDITIONS: 80°F Ambient • 80.0% Relative Humidity • 73.3°F Dew Point • 0.0 mph Wind Velocity • 0.90 Emittance
MINIMUM HEAT GAIN=7.6 BTU/HR SQFT • MAXIMUM HEAT GAIN=9.4 BTU/HR SQFT
Compare different pairs of tables • to determine the effect when one ambient condition changes.
Compare 8 and 9 for the effect of a • change of relative humidity indoors.
Compare 10 and 11 for the effect • of a change in surface emittance outdoors.
The tables on these pages provide the
minimum operating temperatures for
pipe diameter/ insulation thickness
combinations below which condensation
can be expected to occur for the
ambient conditions given.
Compare 9 and 10 for the effect • of a change in wind velocity.
For design conditions not covered in
these tables, contact your Pittsburgh
Corning representative.
FOAMGLAS® INSULATION THICKNESS, MM NPS 25.4 38.1 50.8 63.5 76.2 88.9 101.6 114.3 127.0 139.7 152.4 165.1 177.8 190.5 203.2 215.9 228.6 241.3 254.0 279.4 304.8 0.50 -47 -109 -184 0.75 -33 -85 -148 1.00 -42 -88 -151 -239 1.50 -32 -70 -154 -227 2.00 -29 -66 -112 -168 -241
2.50 -26 -81 -126 -182 -256 3.00 -22 -53 -89 -132 -187 4.00 -20 -47 -79 -118 -171 -231 5.00 -17 -41 -70 -109 -151 -203 6.00 -14 -37 -67 -99 -137 -196 -256
8.00 -36 -61 -97 -132 -173 -223 10.00 -36 -59 -86 -117 -153 -195 -247 12.00 -34 -56 -81 -110 -143 -182 -228 14.00 -28 -49 -72 -99 -130 -165 -207 -257 16.00 -26 -47 -69 -95 -124 -157 -197 -245
18.00 -25 -45 -67 -91 -120 -152 -191 -236 20.00 -24 -43 -65 -89 -117 -149 -186 -229 24.00 -23 -42 -63 -87 -113 -143 -178 -219 28.00 -23 -42 -62 -85 -111 -139 -172 -211 -256 30.00 -23 -41 -62 -84 -109 -138 -170 -208 -252
36.00 -23 -41 -61 -82 -107 -134 -165 -201 -242 42.00 -22 -40 -60 -81 -105 -131 -161 -195 -235 48.00 -22 -40 -59 -80 -103 -129 -158 -192 -230 60.00 -22 -39 -58 -79 -101 -126 -154 -186 -264 72.00 -22 -39 -58 -78 -100 -125 -152 -182 -217 -257
96.00 -21 -38 -57 -77 -98 -122 -148 -178 -211 -249120.00 -21 -38 -56 -76 -97 -121 -146 -175 -207 -244168.00 -21 -38 -56 -75 -96 -119 -144 -172 -203 -238 FLAT -21 -37 -54 -73 -93 -115 -138 -164 -193 -224 -260
TABLE 10: English (°F)OUTDOOR DESIGN CONDITIONS: 80°F Ambient • 80.0% Relative Humidity • 73.3°F Dew Point • 7.5 mph Wind Velocity • 0.90 Emittance
MINIMUM HEAT GAIN=11.6 BTU/HR SQFT • MAXIMUM HEAT GAIN=16.0 BTU/HR SQFT
TABLE 10: Metric (°C)OUTDOOR DESIGN CONDITIONS: 26.7°C Ambient • 80.0% Relative Humidity • 22.9°C Dew Point • 12.1 kmph Wind Velocity • 0.90 Emittance
MINIMUM HEAT GAIN=35.7 KCAL/HR SQM • MAXIMUM HEAT GAIN=49.8 KCAL/HR SQM
FOAMGLAS® INSULATION THICKNESS, INCHES NPS 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 6.0 6.5 7.0 7.5 8.0 8.5 9.0 9.5 10.0 11.0 12.0
0.50 -30 -125 -235 0.75 -10 -90 -180 -400 1.00 -25 -95 -190 -310 1.50 -10 -70 -190 -295 -430 2.00 -5 -60 -130 -215 -315 -445
2.50 0 -85 -150 -235 -335 3.00 5 -45 -95 -160 -240 -350 4.00 5 -35 -85 -140 -220 -305 -410 5.00 10 -25 -70 -130 -190 -265 -380 6.00 15 -20 -65 -115 -170 -255 -340 -440
8.00 -20 -55 -110 -165 -225 -295 -380 10.00 -20 -55 -95 -140 -195 -255 -325 -415 12.00 -15 -50 -90 -130 -180 -235 -300 -380 14.00 -5 -40 -75 -115 -160 -215 -270 -340 -430 16.00 -5 -35 -70 -110 -150 -200 -260 -325 -405
18.00 0 -30 -65 -105 -145 -195 -250 -315 -390 20.00 0 -30 -65 -100 -145 -190 -245 -305 -375 24.00 0 -30 -60 -95 -135 -180 -230 -290 -355 -435 28.00 0 -25 -60 -95 -135 -175 -225 -280 -340 -415 30.00 0 -25 -60 -95 -130 -175 -220 -275 -335 -405
36.00 0 -25 -55 -90 -125 -170 -215 -265 -320 -390 42.00 0 -25 -55 -90 -125 -165 -210 -255 -310 -375 48.00 0 -25 -55 -85 -120 -160 -205 -250 -305 -365 -435 60.00 5 -25 -55 -85 -120 -155 -200 -245 -295 -350 -415 72.00 5 -25 -50 -85 -115 -155 -195 -240 -285 -345 -405
96.00 5 -20 -50 -80 -115 -150 -190 -230 -280 -330 -390120.00 5 -20 -50 -80 -115 -150 -185 -230 -275 -325 -380 -445168.00 5 -20 -50 -80 -110 -145 -185 -225 -265 -315 -370 -430 FLAT 5 -20 -45 -75 -105 -140 -175 -210 -255 -295 -345 -400
25
SECTION 11 TEMPERATURE LIMITS
FOAMGLAS® INSULATION SYSTEMS 26
SECTION 12INSULATION THICKNESSES FOR PROCESS PIPING
FOAMGLAS® INSULATION SYSTEMS
TABLE 11: English (°F)OUTDOOR DESIGN CONDITIONS: 80°F Ambient • 80.0% Relative Humidity • 73.3°F Dew Point • 7.5 mph Wind Velocity • 0.40 Emittance
MINIMUM HEAT GAIN=8.5 BTU/HR SQFT • MAXIMUM HEAT GAIN=12.4 BTU/HR SQFT
FOAMGLAS® INSULATION THICKNESS, INCHES NPS 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 6.0 6.5 7.0 7.5 8.0 8.5 9.0 9.5 10.0 11.0 12.0
0.50 -5 -70 -140 -290 -415 0.75 10 -45 -110 -235 -335 1.00 0 -50 -110 -185 -265 -370 1.50 10 -30 -110 -175 -245 -335 2.00 15 -25 -70 -125 -185 -255 -350
2.50 15 -40 -85 -135 -195 -270 -355 3.00 20 -10 -50 -90 -140 -200 -265 -345 4.00 25 -5 -40 -75 -125 -175 -230 -310 -390 5.00 30 0 -30 -65 -105 -150 -210 -270 -340 -420 6.00 30 5 -25 -55 -95 -145 -190 -240 -300 -370
8.00 10 -20 -55 -85 -125 -165 -210 -260 -315 -380 10.00 10 -15 -45 -70 -105 -140 -180 -225 -275 -330 -390 12.00 10 -10 -35 -65 -95 -130 -165 -205 -250 -300 -360 -430 14.00 15 -5 -30 -55 -85 -115 -150 -185 -230 -275 -335 -395 16.00 20 0 -25 -50 -75 -105 -140 -175 -220 -265 -315 -375 -445
18.00 20 0 -20 -45 -75 -105 -135 -170 -210 -255 -300 -360 -420 20.00 20 0 -20 -45 -70 -100 -130 -165 -205 -245 -290 -345 -405 24.00 20 0 -20 -40 -65 -95 -125 -155 -190 -230 -275 -325 -380 -440 28.00 25 5 -15 -40 -65 -90 -120 -150 -185 -220 -265 -310 -360 -415 30.00 25 5 -15 -40 -65 -90 -120 -150 -180 -220 -260 -300 -350 -405
36.00 25 5 -15 -40 -60 -85 -115 -145 -175 -210 -245 -290 -335 -385 -445 42.00 25 5 -15 -35 -60 -85 -110 -140 -170 -200 -240 -280 -320 -370 -425 48.00 25 5 -15 -35 -60 -80 -110 -135 -165 -195 -230 -270 -310 -360 -410 60.00 25 5 -15 -35 -55 -80 -105 -130 -160 -190 -225 -260 -300 -340 -390 -440 72.00 25 5 -15 -35 -55 -80 -100 -130 -155 -185 -215 -250 -290 -330 -375 -425
96.00 25 5 -10 -30 -55 -75 -100 -125 -150 -180 -210 -245 -280 -315 -360 -405120.00 25 5 -10 -30 -50 -75 -95 -120 -150 -175 -205 -235 -270 -310 -350 -390 -440168.00 25 5 -10 -30 -50 -75 -95 -120 -145 -170 -200 -230 -265 -300 -335 -380 -425 FLAT 25 10 -10 -30 -50 -70 -90 -115 -135 -160 -185 -215 -245 -275 -310 -345 -380 -425
TABLE 11: Metric (°C)OUTDOOR DESIGN CONDITIONS: 26.7°C Ambient • 80.0% Relative Humidity • 22.9°C Dew Point • 12.1 kmph Wind Velocity • 0.40 Emittance
MINIMUM HEAT GAIN=27.1 KCAL/HR SQM • MAXIMUM HEAT GAIN=40.1 KCAL/HR SQM
FOAMGLAS® INSULATION THICKNESS, MM NPS 25.4 38.1 50.8 63.5 76.2 88.9 101.6 114.3 127.0 139.7 152.4 165.1 177.8 190.5 203.2 215.9 228.6 241.3 254.0 279.4 304.8 0.50 -32 -76 -126 -240 0.75 -21 -60 -102 -196 1.00 -28 -61 -104 -158 -222 1.50 -20 -47 -105 -149 -205 2.00 -17 -44 -77 -113 -157 -210
2.50 -15 -55 -86 -121 -164 -223 3.00 -11 -35 -60 -89 -123 -169 -219 4.00 -10 -30 -53 -79 -113 -148 -190 -256 5.00 -7 -26 -46 -73 -100 -131 -178 -222 6.00 -5 -22 -44 -66 -91 -126 -160 -199 -246
8.00 -21 -39 -64 -86 -112 -141 -174 -212 -257 10.00 -21 -37 -56 -76 -99 -124 -152 -185 -223 12.00 -19 -35 -52 -71 -92 -115 -141 -170 -204 -245 14.00 -14 -29 -46 -64 -83 -105 -129 -156 -188 -226 16.00 -13 -28 -43 -60 -79 -99 -123 -150 -180 -215
18.00 -12 -26 -41 -58 -76 -97 -119 -145 -174 -207 -246 20.00 -12 -25 -40 -57 -75 -94 -117 -141 -169 -201 -237 24.00 -11 -24 -39 -55 -72 -91 -112 -135 -161 -191 -224 -263 28.00 -11 -24 -38 -54 -70 -89 -109 -131 -156 -183 -215 -251 30.00 -11 -24 -38 -53 -70 -88 -107 -129 -153 -180 -211 -246
36.00 -10 -23 -37 -52 -68 -85 -104 -125 -148 -174 -202 -234 42.00 -10 -23 -36 -51 -67 -84 -102 -122 -144 -169 -196 -226 -261 48.00 -10 -23 -36 -50 -66 -82 -100 -120 -141 -165 -191 -220 -253 60.00 -10 -22 -35 -49 -64 -81 -98 -117 -137 -160 -184 -212 -243 72.00 -10 -22 -35 -49 -64 -79 -96 -115 -135 -156 -180 -206 -235
96.00 -9 -22 -34 -48 -62 -78 -94 -112 -131 -152 -174 -199 -226 -257120.00 -9 -21 -34 -47 -62 -77 -93 -110 -129 -149 -171 -195 -221 -250168.00 -9 -21 -34 -47 -61 -76 -92 -108 -126 -146 -167 -190 -215 -243 FLAT -9 -21 -33 -46 -59 -73 -88 -104 -121 -138 -157 -178 -200 -224 -250
INSULATION THICKNESSES FOR PROCESS PIPINGTO LIMIT HEAT GAIN TO 9 BTU/HR•FT2 (28.4 W/SQM)
TABLE 12: English (°F)SEVERE DESIGN CONDITIONS: 90.0°F Ambient • -9.0 ± 0.1 BTU/hr•ft2 Heat Flow Limit • 7.5 mph Wind Velocity • 0.40 Emittance
FOAMGLAS® INSULATION THICKNESS, INCHES NPS 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 6.0 6.5 7.0 7.5 8.0 8.5 9.0 9.5 10.0 11.0 12.0
0.50 29 -18 -71 -181 -271 -384 0.75 40 -2 -48 -144 -220 -314 -433 1.00 31 -5 -53 -110 -174 -253 -349 1.50 38 6 -58 -107 -166 -235 -331 -437 2.00 40 8 -29 -71 -119 -176 -253 -336 -438
2.50 41 -5 -41 -83 -131 -195 -263 -344 3.00 45 17 -13 -48 -89 -142 -197 -261 -359 4.00 45 20 -7 -39 -81 -123 -172 -243 -312 -393 5.00 47 24 -1 -35 -69 -107 -163 -215 -274 -344 -427 6.00 49 27 0 -28 -60 -105 -147 -194 -248 -310 -382
8.00 26 3 -29 -59 -93 -130 -171 -218 -272 -334 -405 10.00 25 2 -22 -49 -80 -113 -151 -193 -240 -294 -355 -426 12.00 26 4 -19 -45 -74 -106 -141 -180 -224 -273 -329 -392 14.00 32 11 -11 -36 -64 -94 -127 -164 -205 -250 -302 -360 -427 16.00 32 12 -10 -34 -61 -90 -121 -156 -195 -238 -286 -340 -402
18.00 33 12 -8 -32 -58 -86 -116 -150 -187 -228 -273 -325 -382 -448 20.00 33 13 -7 -31 -56 -83 -113 -145 -181 -220 -263 -312 -367 -428 24.00 33 14 -6 -28 -52 -78 -107 -137 -171 -207 -248 -293 -343 -399 28.00 34 15 -5 -26 -50 -75 -102 -132 -164 -199 -237 -279 -326 -378 -436 30.00 34 15 -4 -26 -49 -74 -100 -129 -161 -195 -232 -273 -319 -369 -426
36.00 34 16 -3 -24 -47 -71 -96 -124 -154 -186 -222 -260 -303 -350 -402 42.00 35 16 -2 -23 -45 -68 -93 -120 -149 -180 -214 -251 -291 -335 -384 -438 48.00 35 17 -2 -22 -43 -66 -91 -117 -145 -175 -208 -244 -282 -325 -371 -423 60.00 35 17 -1 -21 -42 -64 -88 -113 -140 -169 -200 -233 -270 -309 -353 -400 72.00 35 18 0 -20 -40 -62 -85 -110 -136 -164 -194 -227 -261 -299 -340 -385 -435
96.00 36 18 0 -19 -39 -60 -83 -107 -132 -159 -187 -218 -251 -286 -325 -367 -412120.00 36 18 0 -18 -38 -59 -81 -104 -129 -155 -183 -213 -245 -279 -316 -356 -399 -446168.00 36 19 1 -17 -37 -57 -79 -102 -126 -151 -178 -207 -237 -270 -305 -343 -384 -428 FLAT 36 19 2 -15 -34 -54 -74 -96 -118 -141 -166 -192 -219 -248 -279 -311 -346 -384
TABLE 12: Metric (°C)SEVERE DESIGN CONDITIONS: 32.2°C Ambient • -9.0 ± 0.1 BTU/hr•ft2 Heat Flow Limit • 12.1 kmph Wind Velocity • 0.40 Emittance
FOAMGLAS® INSULATION THICKNESS, MM NPS 25.4 38.1 50.8 63.5 76.2 88.9 101.6 114.3 127.0 139.7 152.4 165.1 177.8 190.5 203.2 215.9 228.6 241.3 254.0 279.4 304.8
0.50 -1 -28 -57 -118 -168 -231 0.75 4 -19 -44 -98 -140 -192 -258 1.00 0 -20 -47 -79 -114 -158 -212 1.50 3 -14 -50 -77 -110 -148 -201 -261 2.00 4 -13 -34 -57 -84 -116 -158 -204 -261
2.50 5 -21 -41 -64 -90 -126 -164 -209 3.00 7 -8 -25 -44 -67 -96 -127 -163 -217 4.00 7 -6 -22 -39 -62 -86 -113 -153 -191 -236 5.00 8 -4 -18 -37 -56 -77 -108 -137 -170 -209 -255 6.00 9 -2 -18 -33 -51 -76 -99 -125 -155 -190 -230
8.00 -2 -15 -34 -50 -69 -90 -113 -139 -169 -203 -243 10.00 -3 -16 -30 -45 -62 -81 -101 -125 -151 -181 -215 -254 12.00 -2 -15 -28 -43 -59 -76 -96 -118 -142 -169 -200 -235 14.00 0 -11 -24 -38 -53 -70 -88 -109 -131 -157 -185 -218 -255 16.00 0 -11 -23 -36 -51 -67 -85 -104 -126 -150 -176 -207 -241
18.00 0 -10 -22 -35 -50 -65 -82 -101 -121 -144 -169 -198 -230 -266 20.00 0 -10 -22 -35 -49 -64 -80 -98 -118 -140 -164 -191 -221 -256 24.00 1 -9 -21 -33 -47 -61 -77 -94 -112 -133 -155 -180 -208 -239 28.00 1 -9 -20 -32 -45 -59 -74 -91 -108 -128 -149 -173 -199 -228 -260 30.00 1 -9 -20 -32 -45 -59 -73 -89 -107 -126 -147 -169 -195 -223 -254
36.00 1 -8 -19 -31 -43 -57 -71 -86 -103 -121 -141 -162 -186 -212 -241 42.00 1 -8 -19 -30 -42 -55 -69 -84 -100 -118 -136 -157 -179 -204 -231 -261 48.00 1 -8 -18 -30 -42 -54 -68 -83 -98 -115 -133 -153 -174 -198 -224 -252 60.00 2 -7 -18 -29 -41 -53 -66 -80 -95 -111 -129 -147 -167 -189 -214 -240 72.00 2 -7 -18 -28 -40 -52 -65 -79 -93 -109 -125 -143 -163 -184 -207 -232 -259
96.00 2 -7 -17 -28 -39 -51 -63 -77 -91 -106 -122 -139 -157 -177 -198 -221 -247120.00 2 -7 -17 -28 -39 -50 -63 -76 -89 -104 -119 -136 -153 -172 -193 -215 -239 -265168.00 2 -7 -17 -27 -38 -49 -61 -74 -87 -102 -116 -132 -149 -167 -187 -208 -231 -255 FLAT 2 -6 -16 -26 -37 -47 -59 -71 -83 -96 -110 -124 -139 -155 -172 -191 -210 -231
27
SECTION 13 INSULATION THICKNESSES FOR PERSONNEL PROTECTION
FOAMGLAS® INSULATION SYSTEMS
NOMINAL PIPE DIAMETER, INCHES 0.5 1.0 1.5 2.0 3.0 4.0 6.0 8.0 10.0 12.0 14.0 18.0 24.0 30.0 36.0 FLAT
DEG C FOAMGLAS® INSULATION THICKNESS, MM 93.3 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 148.9 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 204.4 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 260.0 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 51.0 51.0 51.0 51.0 51.0 51.0 315.6 38.5 38.5 38.5 38.5 51.0 51.0 51.0 51.0 51.0 51.0 63.5 63.5 63.5 63.5 63.5 63.5 371.1 38.5 51.0 51.0 51.0 63.5 63.5 63.5 63.5 76.5 76.5 76.5 76.5 89.0 89.0 89.0 89.0 426.7 51.0 63.5 51.0 63.5 76.5 76.5 89.0 89.0 89.0 89.0 102.0 102.0 102.0 102.0 114.5 114.5 482.2 63.5 63.5 76.5 76.5 89.0 89.0 102.0 102.0 114.5 114.5 127.0 127.0 127.0 140.0 140.0 152.5
NOMINAL PIPE DIAMETER, INCHES 0.5 1.0 1.5 2.0 3.0 4.0 6.0 8.0 10.0 12.0 14.0 18.0 24.0 30.0 36.0 FLAT
DEG F FOAMGLAS® INSULATION THICKNESS, INCHES 200.0 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 300.0 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 400.0 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 2.0 2.0 2.0 2.0 2.0 2.0 500.0 1.5 1.5 1.5 2.0 2.0 2.0 2.5 2.5 2.5 2.5 2.5 3.0 3.0 3.0 3.0 3.0 600.0 2.0 2.0 2.0 2.5 2.5 3.0 3.0 3.0 3.5 3.5 3.5 3.5 4.0 4.0 4.0 4.5 700.0 2.5 2.5 2.5 3.0 3.5 3.5 3.5 4.0 4.0 4.5 4.5 5.0 5.0 5.0 5.0 5.5 800.0 2.5 3.0 3.0 3.5 4.0 4.5 4.5 5.0 5.5 5.5 6.0 6.0 6.0 6.5 6.5 7.5 900.0 3.0 4.0 4.0 4.5 5.0 5.0 6.0 6.0 6.5 7.0 7.0 7.5 7.5 8.0 8.0 9.5
NOMINAL PIPE DIAMETER, INCHES 0.5 1.0 1.5 2.0 3.0 4.0 6.0 8.0 10.0 12.0 14.0 18.0 24.0 30.0 36.0 FLAT
DEG F FOAMGLAS® INSULATION THICKNESS, INCHES 200.0 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 300.0 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 400.0 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 500.0 1.5* 1.5* 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 2.0 2.0 2.0 2.0 2.0 2.0 600.0 1.5 1.5 1.5 1.5 2.0 2.0 2.0 2.0 2.0 2.0 2.5 2.5 2.5 2.5 2.5 2.5 700.0 1.5 2.0 2.0 2.0 2.5 2.5 2.5 2.5 3.0 3.0 3.0 3.0 3.5 3.5 3.5 3.5 800.0 2.0 2.5 2.0 2.5 3.0 3.0 3.5 3.5 3.5 3.5 4.0 4.0 4.0 4.0 4.5 4.5 900.0 2.5 2.5 3.0 3.0 3.5 3.5 4.0 4.0 4.5 4.5 5.0 5.0 5.0 5.5 5.5 6.0
NOMINAL PIPE DIAMETER, INCHES 0.5 1.0 1.5 2.0 3.0 4.0 6.0 8.0 10.0 12.0 14.0 18.0 24.0 30.0 36.0 FLAT
DEG C FOAMGLAS® INSULATION THICKNESS, MM 93.3 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 148.9 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 204.4 38.5* 38.5* 38.5 38.5 38.5 38.5 38.5 38.5 38.5 38.5 51.0 51.0 51.0 51.0 51.0 51.0 260.0 38.5 38.5 38.5 51.0 51.0 51.0 63.5 63.5 63.5 63.5 63.5 76.5 76.5 76.5 76.5 76.5 315.6 51.0 51.0 51.0 63.5 63.5 76.5 76.5 76.5 89.0 89.0 89.0 89.0 102.0 102.0 102.0 114.5 371.1 63.5 63.5 63.5 76.5 89.0 89.0 89.0 102.0 102.0 114.5 114.5 127.0 127.0 127.0 127.0 140.0 426.7 63.5 76.5 76.5 89.0 102.0 114.5 114.5 127.0 140.0 140.0 152.5 152.5 152.5 165.5 165.5 190.5 482.2 76.5 102.0 102.0 114.5 127.0 127.0 152.5 152.5 165.5 178.0 178.0 190.5 190.5 203.5 203.5 241.5
TABLE 13: English (inches)Hot Pipe Worse Case 80.0°F Ambient for Surface Temperature ≤140.0°F: 0.40 Surface Emittance • 0.0 mph Average Wind Velocity
TABLE 13A: English (inches)Hot Pipe Worse Case 80.0°F Ambient for Surface Temperature ≤140.0°F: 0.90 Surface Emittance • 0.0 mph Average Wind Velocity
TABLE 13: Metric (mm)Hot Pipe Worse Case 26.7°C Ambient for Surface Temperature ≤60.0°C: 0.40 Surface Emittance • 0.0 kmph Average Wind Velocity
TABLE 13A: Metric (mm)Hot Pipe Worse Case 26.7°C Ambient for Surface Temperature ≤60.0°C: 0.90 Surface Emittance • 0.0 kmph Average Wind Velocity
* Thickness based on mechanical requirements and not necessarily personnel protection.
MAXIMUM HEAT FLOW = 71.6 BTU/HR SQ FT
MAXIMUM HEAT FLOW = 107.4 BTU/HR SQ FT
MAXIMUM HEAT FLOW = 194.1 KCAL/HR SQ M
MAXIMUM HEAT FLOW = 291.3 KCAL/HR SQ M
RECOMMENDED INSULATION THICKNESSES FORPERSONNEL PROTECTION SURFACE TEMPERATURE ≤ 140°F (60°C)
FOAMGLAS®
Insulation
Finish(Metal Jacket or Mastic) 2"
(50 mm)8"
(203 mm)2"
(50 mm)
Cushioning MaterialHOT and COLD Process
COLD Process Only:PITTSEAL® 444N SealantBoth Sides To Bare Insulation
COLD Process Only:Vapor Barrier Sheet
COLD Process Only:Stainless Steel Bands Both SidesCOLD Process: PITTSEAL® 444N Sealant
HOT Process: Hydrocal® B11To Provide Slip Surface
9"(228 mm)
FOAMGLAS® InsulationSupport Ring
Finish(Metal Jacket or Mastic)
COLD Process Only:PITTSEAL® 444N SealantBoth Sides To Bare Insulation
COLD Process Only:Vapor Barrier Sheet
COLD Process:PITTSEAL® 444N SealantHOT Process: Hydrocal® B11
FOAMGLAS® Insulation
COLD Process Only:Stainless Steel Bands Both Sides
CushioningMaterial
28
SECTION 14ABOVE GROUND AND UNDERGROUND INSTALLATION
FOAMGLAS® INSULATION SYSTEMS
FIGURE 9: Two-Layer Expansion Contraction Joint
FIGURE 10: Vertical Contraction Joint
TYPICAL ABOVE GROUND INSTALLATION DETAILS
Contact your Pittsburgh Corning representative for assistance on other typical details.
Insulation Finishor Metal Jacket
Bore Coating
Joint Sealantfor Cold Applications
Clevis Hanger
Pipe Insulation ToBe Continuous
Insulation Shield
Finish
11/2"T
T
4TMin.
Flash Finish AroundHanger Rod
Hanger Rod
FOAMGLAS®
Insulation
T
Heavy Fillet ofCaulking Mastic
CushioningMaterial
29
SECTION 14 ABOVE GROUND AND UNDERGROUND INSTALLATION
FOAMGLAS® INSULATION SYSTEMS
FIGURE 11: Insulation on Line Flanges
FIGURE 12: Pipe Hanger Assembly Insulation
Cushioning material typically TYPE E Glass Fiber Pelt. Contact your Pittsburgh Corning representative for assistance on other typical details.
FOAMGLAS® Insulation
Finish
11/2"TMin.
Round OutsideCorners
Heavy Filletof Caulking Mastic
2" Min.(51 mm)
T
T
FOAMGLAS®
InsulationFinish
Round OutsideCorners
Heavy Fillet ofCaulking Mastic
11/2"TMin.
2" Min.(51 mm)
T
T
Oversize FOAMGLAS®
Insulation
Circumferential Sizing Insertto Locate Oversize FOAMGLAS®
Insulation Outside O.D. of Flange
CushioningMaterial
30
SECTION 14ABOVE GROUND AND UNDERGROUND INSTALLATION
FOAMGLAS® INSULATION SYSTEMS
FIGURE 13: Insulated Pipe Hanger (Clevis Type Only)
Contact your Pittsburgh Corning representative for assistance on other typical details.
UNDERGROUND SYSTEMS ANDPIPE SUPPORTS/HANGERS
Underground SystemsFor direct burial of insulated pipes
and vessels, FOAMGLAS® insulation
is uniquely qualified for such remote,
inaccessible applications. In this type
of an installation without protective
tunnels, high compressive strength in
an insulation material is mandatory.
When properly designed and installed
with FOAMGLAS® insulation
incorporating a protective jacketing,
neither overburden loads nor above
ground traffic are critical design
issues. The long-term thermal
efficiencies, impermeability, corrosion
resistance and extended service life of
FOAMGLAS® insulation make it an ideal
choice for cost-effective field installed
systems.
For design information, refer to
Pittsburgh Corning Corporation’s
FOAMGLAS® Insulation Systems for Underground Direct Burial Applications (FI-213).
Pipe Supports and HangersAn insulation that has the ability to
be used as a support component
eliminates or significantly reduces the
potential problems of direct thermal
paths in the system. Resistance to
settlement or failure of insulated pipe
supports also means that pipes remain
in their proper alignment, without
stresses at nozzles, flanges or fittings.
FOAMGLAS® insulation also supports
its own weight without sagging or
slumping, making it ideal for vertical
pipe runs of all heights (see Figure 13).
For design information, refer to
Pittsburgh Corning Corporation’s
Guidelines for Using FOAMGLAS® Insulation at Pipe Hangers and Supports (Specification I-S-83-07-01).
FIGURE 13B: Insulated Pipe HangerFOAMGLAS® For Chilled Water Pipes, Pipe Hanger
Steel pipe, withanticorrosion painting
Half pipe sections,typ PSH, full adheredto the pipe and jointssealed with PC18
Pressure distributiongalv. Steel sheet,1,0 mm thick
Standard pipe clamp,applied free of clearance,without any imput tensions.
31
SECTION 15 GENERAL SPECIFICATIONS
FOAMGLAS® INSULATION SYSTEMS
GENERAL SPECIFICATIONS
This specification is offered as a guide
for the purpose described herein and
should be employed at the discretion
of the user. These specifications are
written specifically for FOAMGLAS®
cellular glass insulation. No
warranty of procedures, either
expressed or implied, is intended.
Before using this specification, contact
Pittsburgh Corning to ensure that
current details and revisions are
incorporated. Pittsburgh Corning will
review plans and specifications of
users at no charge to assist in ensuring
that proper procedures and materials
are used. However, the ultimate
design and installation are the
responsibility of the engineer or
architect.
General Notes1. These specifications are general in
nature. For specific applications,
contact your Pittsburgh Corning
representative as listed on the
back cover. The final application
procedure is the responsibility of the
project designer and/or owner. No
warranty of any nature, either
expressed or implied, is made as
to application or installation.
2. Prior to application of insulation,
surfaces to be insulated must be
dry and clean. The use of primers
or corrosion-resistant coatings is at
the discretion of the owner or the
design engineer. All testing, such as
hydrostatic, X-ray, etc., should be
completed prior to the application of
the insulation.
3. The proper insulation thickness
should be determined through
calculations based on operating,
environmental, and any other special
conditions. Contact your Pittsburgh
Corning representative if calculations
are desired.
4. Multiple layers may be required:
When the total insulation thickness • required is greater than the maximum single-layer thickness available.
To provide an outer layer that • falls entirely within the applicable temperature range of a sealant, if one is used.
To eliminate through joints on • piping or equipment operating at extreme temperatures.
5. The use of a bore-coating on the
inner surface of the insulation in
contact with the pipe may be required
if the piping undergoes frequent
temperature cycles or if pronounced
vibration is present. Contact your
Pittsburgh Corning representative for
bore-coating recommendations.
6. Ambient temperature is to be defined
by the design engineer based on job-
site conditions.
7. Precautions. There are three
situations which require precautions.
Contact Pittsburgh Corning for
proper procedures to overcome these
situations.
Direct exposure to:
Hydrofluoric acid or strong caustics•
Water during freeze-thaw cycling•
Prolonged exposure to condensing • steam or boiling water.
Temperatures below -290°F (-179°C)Because of the highly specialized
nature of applying insulation in this
temperature range, it is recommended
that you contact your Pittsburgh
Corning representative for materials
and procedures. Of prime concern is
that components of such a system be
compatible with liquid oxygen.
-290°F to -60°F (-179°C to -51°C)FOAMGLAS® insulation shall be
applied in multiple layers with all
joints staggered between layers. The
number and thickness of layers shall be
calculated so that the innermost layer
is entirely above -60°F (-51°C). The
outermost layer shall have all joints
sealed with joint sealant.
Inner layers of piping insulation may be
secured with fiber-reinforced tape. The
outermost layer of insulation shall be
secured with metal bands of appropriate
width and thickness, two bands per
insulation section.
The finish over the insulation may be
either vapor retarder or weather-barrier
reinforced mastic, and/or metal jacketing.
The exterior surface of the insulation
under metal jacket shall be coated
with PITTCOTE® 300 coating to fill the
surface cells.
FOAMGLAS® insulation is impermeable
to water or water vapor under most
conditions, and providing that all joints
between insulation sections are properly
sealed, no vapor retarder is required.
The designer may desire the use of a
vapor retarder as a redundant measure.
32
SECTION 15GENERAL SPECIFICATIONS
FOAMGLAS® INSULATION SYSTEMS
-60°F (-51°C) to AmbientFOAMGLAS® insulation may be applied in
a single layer where thickness permits.
The use of joint sealant is recommended
on all systems that operate below
ambient temperature for any length of
time, and is required on systems that
operate at or below 36°F. In cases where
the below ambient system is operating at
a temperature higher than 36°F, and the
outdoor relative humidity is not routinely
expected to exceed 50%, the use of a
joint sealant is at the discretion of the
design engineer.
For securement and finish
recommendations, see the above
procedures given for -290°F to
-60°F (-179°C to -51°C).
The exterior surface of the insulation
under metal jacket shall be coated
with PITTCOTE® 300 coating to fill the
surface cells.
Tanks, spheres, and vessels operating
in this temperature range may also
be insulated by adhering FOAMGLAS®
insulation to curved or flat surfaces using
PC® 88 adhesive. This adhesive may also
be used as the joint sealant. Contact your
Pittsburgh Corning representative for
specifications of materials and procedures
for this method.
Ambient to 400°F (204°C)FOAMGLAS® insulation shall be applied
in a single layer. No joint sealant is
required. Staggering of joints is at the
discretion of the owner or the design
engineer. Pipe insulation may be secured
using fiber-reinforced tape if a metal
jacket will be used, or with metal bands
if a reinforced weather-barrier mastic
will be used.
Insulation on vessels shall be secured
using metal bands. For operating
temperatures up to 160°F (71°C), PC®
88 adhesive may be used to secure
the insulation. Contact your Pittsburgh
Corning representative for details
concerning the use of PC® 88 adhesive.
The finish over FOAMGLAS® insulation
on either piping or vessels may be a
reinforced weather-barrier mastic or a
metal jacket.
Above 400°F (204°C)Pittsburgh Corning offers several
different procedures for applying
FOAMGLAS® insulation to piping and
vessels operating above 400°F (204°C).
The preferred system is the StrataFab®
System. Contact your Pittsburgh Corning
representative for recommendations on
various alternatives.
StrataFab® System-100°F to 900°F (-73°C to 482°C)The StrataFab® System shall be applied
as a single layer for the temperature
range of -60°F to 900°F (-51°C to
482°C). The use of joint sealant is
recommended on all systems that
operate below ambient temperature
for any length of time, and is required
on systems that operate at or below
36°F. In cases where the below ambient
system is operating at a temperature
higher than 36°F, and the outdoor
relative humidity is not routinely
expected to exceed 50%, the use of a
joint sealant is at the discretion of the
design engineer. For the temperature
range of ambient to 900°F (482°C) no
sealant is necessary.
StrataFab® System pipe insulation may
be applied using fiber-reinforced tape
or metal bands. StrataFab® System
insulation for vessels tanks and
equipment may be applied with metal
bands, weld pins or PC® 88 adhesive, as
appropriate for the application. Contact
your Pittsburgh Corning Corporation
Representative for more information
about these systems.
The finish used over the FOAMGLAS®
Insulation StrataFab® System may be a
weather barrier mastic or metal jacket.
On below-ambient systems, the exterior
surface of the insulation under metal
jacket shall be coated with PITTCOTE®
300 coating to fill the surface cells.
* For applications from -100°F to -60°F (-73°C to -51°C) refer to the application procedures for FOAMGLAS® insulation in the temperature range of -290°F to -60°F (-179°C to -51°C).
33
SECTION 16 ACCESSORY MATERIALS
FOAMGLAS® INSULATION SYSTEMS
Pittsburgh Corning Corporation offers a line
of accessory materials exclusively designed
for FOAMGLAS® cellular glass insulation
for use in major types of industrial
applications.
Pittsburgh Corning Corporation is
continually evaluating accessory
materials. While these materials are
tested and selected especially for use with
FOAMGLAS® insulation, the information
given here is for general guidance. For
the latest recommendations and specific
data sheets on the individual accessories,
consult your distributor or Pittsburgh
Corning Corporation.
Pittsburgh Corning makes no
warranties whatsoever, and
specifically disclaims warranties
of merchantability and fitness
for a particular use for these
accessory products.
ACCESSORY MATERIALS
SECTION 16ACCESSORY MATERIALS
FOAMGLAS® INSULATION SYSTEMS 3433
US
A
Source+
EU
R
+ PC Accessories are available for shipment for projects worldwide. The sources are either at PCC plant locations or Pittsburgh Corning Europe locations. Pricing for all PC Accessories is available from your customer support representative.¹NOTE: Do not use in underground tunnels or trenches where jacketing will be exposed to air temperatures in excess of 140ºF (60ºC)
Product Description continuous-support substrates. Service temperature from -30°C to 80°C (-22°F to 176°F).
HYDROCAL® B-11 A reactive gypsum product which, when mixed with water, forms an inorganic, noncombustible adhesive or coating for fabricating or bore coating X FOAMGLAS® insulation.
PC® 11 A single component, cold bituminous adhesive ready to use. It is especially suitable for adhering FOAMGLAS® to metal substrates. PC® 11 cures to form X a flexible, non-aging adhesive with very good adhesion to different materials.
PC® 136 Adhesive A reactive cementitious product that is mixed with water to form an inorganic, noncombustible adhesive or coating for fabricating, bore coating or forming HT X reinforced FOAMGLAS® insulation shapes. It is normally used at ambient above temperatures to 900ºF (482ºC) where stress-crack corrosion is a concern with stainless steel
PC® 150 An open mesh, alkali-resistant glass fabric for reinforcing mastic finishes over FOAMGLAS® insulation. The large mesh openings (approx. 3mm) allow X heavy mastics or mineral coatings to easily penetrate and bond to the insulation and fabric surfaces. The thickness of the fabric ensures proper application thickness of the coating. Its tensile resistance is greater than that of PC® Fabric 79, with lower deformation. It is especially suitable for use with PC® 74 A2.
PC® 18 A single component, cold bituminous adhesive ready to use. PC® 18 is used to seal the longitudinal and circumferential insulation joints of FOAMGLAS® X insulation on chilled water lines. Cures to form a flexible, non-aging adhesive with very good adhesion to different materials.
PC® 500 A single-component, bituminous adhesive with low solvent content and a high content of extenders. PC® 500 retains long-term flexibility, does not freeze and X is thixotropic. Adheres FOAMGLAS® to continuous-support substrates. Service temperature from -30ºC to 80ºC (-22ºF to 176ºF). PC® 56 Adhesive A two-component, solvent-free adhesive. Component one is based on bitumen emulsion with synthetic additives. Component two is cement. Service X temperature range -15ºC to 45ºC (5º F to 113º F).
PC® 74A2 A dry, manufactured mineral coating used with glass fabric as a non-combustible coating and as an adhesive for FOAMGLAS® insulation. Contains a X mixture of special sands, cement and hydrated lime.
PC® 80M Mortar A two-component inorganic mortar based on specially formulated glass powder and fillers for component one and modified silica dispersion for component X two. PC® 80M MORTAR is used to adhere FOAMGLAS® cellular glass to itself within a large temperature range when temperatures are very low, very high, or cycle rapidly, using the laminated technique that consists of embedding a specific reinforcement in the adhesive layer. Service temperature from -196°C to +380°
PC® 85 A mineral-based, totally inorganic powder that has been especially formulated for filling the open surface cells of FOAMGLAS® cellular glass when X used for the insulation of liquid oxygen, liquid nitrogen and hot tank bases. When used with appropriate interleaving membranes the desired load distribution can be achieved with slightly reduced compressive strength versus reference values under EN 826 or ASTM C240-91 testing conditions.
PC® 86T A single component bitumen emulsion product with fillers. Offers good resistance to high temperatures. PC® 86T is suitable for use on FOAMGLAS® cellular glass X as a bedding compound in specific load bearing applications. Service temperature from -10°C to +90°C
PC® 88 Adhesive A multi-purpose, two component adhesive for adhering FOAMGLAS® insulation to itself or to other porous or nonporous substrates. Air curing is not X X required. It has excellent wetting characteristics and cures to form a flexible bond that absorbs mechanical and thermal shock. Service temperature range: low to moderate.
PC® Fabric 79 An open mesh polyester fabric for reinforcing mastics such as PITTCOTE® 404 or PITTCOTE® 300 coating over FOAMGLAS® insulation. Service temperature X X range: low to moderate.
PC® High Temp Anti Abrasive A one-component, dry mix of modified calcium sulphate with inert meneral fillers. PC® High Temp Anti-Abrasive is applied to FOAMGLAS® insulation as a X reinforcement for high temeperature applications, and when needed for dual temperature applications. When dry it forms a protective hard surface, filling the surface cells of the insulation and providing protectcion from abrasion up to 350º C (662ºF).
PC® Primer Sealer 3A A thin-bodied bitumen and volatile solvent blend, particularly suited for use as a tack coat for nonporous substrates such as steel or aluminum prior X to the application of FOAMGLAS® insulation with hot bitumen. Can also be used on dense concrete.
PC® RTV 450 Sillicone Adhesive A one-part, acetoxy cure, silicone adhesive/sealant formulated for use at high temperatures. It cures to an elastomeric solid at room temperature. Service X temperature range: -50ºF to 400ºF (-45ºC to 204º). PITTCOTE® 300 Coating Vapor and weather barrier single component asphalt coating especially formulated for use with FOAMGLAS® insulation. Service temperature range: X X low to moderate.
PITTCOTE® 404 Coating A highly flexible acyrlic latex coating used with FOAMGLAS® insulation where a superior weather barrier coating is required. Used with polyester fabric X X reinforcement. Service temperature: low to moderate.
PITTSEAL® 444 Sealant Non-setting, single component butyl sealant used for sealing joints in FOAMGLAS® insulation systems, and to seal protrusions and metal jacket laps. Service X temperature range: low to moderate.
PITTSEAL® 444N Sealant Non-setting, single component butyl sealant used for sealing joints in FOAMGLAS® insulation systems, and to seal protrusions and metal jacket laps. X Stainless steel compatible. Service temperature range: low to moderate.
PITTWRAP CW30 Jacketing A 30mil (0.8mm) thick self-sealing, modified bituminous membrane for protecting above ground FOAMGLAS® insulation systems on chilled water and hot service X pipelines. Manual pressure seals the jacketing without the use of a torch or heater. Metal jacketing must be used over the PITTWRAP® CW30 jacketing for UV protection. PITTWRAP® CW30 jacketing cannot be factory applied on the insulation.¹
PITTWRAP® CW Plus Jacketing A 50mil (1.3mm) thick self-sealing, modified bituminous membrane for protecting underground FOAMGLAS® insulation systems on chilled water and hot X service¹ pipelines. Manual pressure seals the jacketing without the use of a torch or heater. PITTWRAP® CW Plus jacketing may also be factory applied on the insulation. PITTWRAP® CW Plus jacketing consists of a polymer modified bituminous compound reinforced with a glass fabric and a 1mil (0.03mm) aluminum top film and release paper backing.
PITTWRAP® IW50 Jacketing A 50mil (1.33mm) thick self-sealing, non-metallic sheet for protecting above ground FOAMGLAS® insulation systems on chilled water and hot service pipelines. X Manual pressure seals the jacketing without the use of a torch or heater. Metal jacketing must be used over the PITTWRAP® IW50 jacketing for UV protection. PITTWRAP® IW50 jacketing consists of a polymer modified bituminous compound reinforced with a glass fabric, a 1mil polyester film and release paper backing.
PITTWRAP® Jacketing A 125mil (3.2mm) thick heat-sealable, multi-ply laminate for protecting underground FOAMGLAS® systems with outer surface temperatures below X 190ºF (87.7ºC). PITTWRAP® jacketing consists of three layers of a polymer-modified, bituminous compound separated by glass reinforcement and aluminum foil. An outer layer of polyester film is laminated to the bituminous compound. Release paper prevents sticking in the roll before use. PITTWRAP® jacketing may also be factory applied on the insulation.
PITTWRAP® SS Jacketing A 70mil (1.8mm) thick self-sealing, modified bituminous membrane for protecting underground FOAMGLAS® insulation systems with outer surface X X temperatures below 170ºF (76.7ºC). Manual pressure seals the jacketing without the use of a torch or heater. PITTWRAP® SS jacketing may also be factory applied on insulation. Terostat-PC FR A sprayable and gunable, single component sealant, coating and adhesive. Terostat® - FR is a silane modified polymer base (MS® Polymer) that X cures on reaction with moisture. Contains no solvents, isocyanates, silicones or PVC. Terostat® - FR has good weathering, chemical and UV resistance.