SINTESA NANOPARTIKEL MAGNETIK DENGAN METODE ELEKTROKIMIA
SYNTHESIS OF MAGNETIC NANOPARTICLES
USING ELECTROCHEMICAL METHOD
Created by WAHYU RAHARJO ; ENDIK SENTOSA
Subject : Elektrokimia
Subject Alt : Chemical engineering
Keyword : : elektrokimia ; nanopartikel magnetik; X-Ray Diffraction; Scanning Electron Microscopy
Description :
Tujuan penelitian ini adalah membuat nanopartikel magnetik Fe3O4 dengan metode elektrokimia dan mengevaluasi
pengaruh kondisi operasi (pH, suhu dan rapat arus) terhadap karakteristik partikel. Proses sintesa nanopartikel magnetik
Fe3O4 ini diawali dengan elektroplating besi dalam larutan elektrolit FeSO4 0.072 mol/L pada rapat arus 0.167 A/dm2
selama 6 jam. Kemudian elektroda besi yang telah mengalami proses elektroplating tersebut dipakai untuk proses
elektrokimia pada sintesa Fe3O4. Dengan menggunakan air demin sebagai elektrolit, proses elektrolisa untuk sintesa
Fe3O4 dilakukan selama 12 jam. Untuk mendapatkan hasil yang terbaik, percobaan dilakukan dengan memvariasikan
suhu larutan elektrolit, pH dan rapat arus yang mengalir dalam sel. Untuk variabel pH digunakan pH 7, 9 dan 11,
variabel suhu larutan adalah suhu 30 , 40 dan 50 C, sedangkan variabel rapat arus adalah 70 /A/cm2,100 /A/cm2 dan
130 /A/cm2 dan untuk variabel pH, digunakan pH 7, 9 dan 11. Partikel Fe3O4 yang dihasilkan masih tercampur dengan
larutan elektrolit sehingga harus dipisahkan untuk selanjutnya dianalisa dengan metode XRD (X-Ray Diffraction) dan
SEM (Scanning Electron Microscopy). Dalam percobaan ini juga dilakukan pengukuran verpotensial untuk mengetahui
pengaruh arus terhadap reaksi elektroda yang terjadi di batas fase. Metode elektrokimia dengan bahan yang sederhana
mampu menghasilkan partikel Fe3O4 meskipun diiringi dengan terbentuknya sedikit senyawa lain yaitu Fe3O4. Darihasil analisa XRD dan SEMpada variabel yang telah ditentukan, hasil terbaik produk Fe3O4 didapat pada kondisi pH 7,
suhu 30 C dan rapat arus 70 ^A/cm2. Jadi dapat disimpulkan karakteristik partikel Fe3O4 dipengaruhi oleh kondisi pH,
suhu larutan elektrolit dan rapat arus yang digunakan.
Description Alt:
he main objectives of this research are to synthesize of magnetic nanoparticles using electrochemical method and to
evaluate the effect of operating conditions on particles characteristics.
The anode was prepared by electroplating iron plate FeSO4 solution with current density of 0.167 A/dm2 for 6 hours.
Then, the electroplated was functioned as anode in the next experiment that was used to produce Fe3O4 particles. Usingdeionized water as an electrolyte, electrolysis process for synthesizing of Fe3O4 was performed for 12 hours. To get the
best result, experiments were performed with using various parameters such as temperature, pH, and current density.
Particle produced that were dispersed in the solution were then separated and dried. The dried particles were
characterized by X-ray Diffraction and Scanning Electron Microscopy. In these experiments, Overpotential was also
measured, to know the effect of electric current on the electrode reaction occured at the interface.
Electrochemical method with simple route can produce Fe3O4 particles although there was a little formation impurities
such as Fe3O4 and tend to form agglomerate. From the result of XRD and SEM analysis at hose variables, showed that
the best result of Fe3O4 particles were obtained at pH 7, temperature of 30 C and under current density of 70 /A/cm2.
Contributor : Dr. Ir. Heru Setyawan, M.Eng.
Date Create : 21/12/2009
Page 1
8/13/2019 Docimun
2/2
Type : Text
Format : pdf
Language : Indonesian
Identifier : ITS-Undergraduate-3100009035650
Collection : 3100009035650
Call Number : RSK 660.297 8 Rah s
Source : Undergraduate Theses, Chemical Engineering, RSK 660.297 8 Rah s, 2009
COverage : ITS Community Only
Right : Copyright @2009 by ITS Library. This publication is protected by copyright and permissionshould be obtained from the ITS Library prior to any prohibited reproduction, storage in aretrievel system, or transmission in any form or by any means, electronic, mechanical,photocopying, recording, or likewise. For information regarding permission(s), write to ITSLibrary
Full file - Member Only
If You want to view FullText...Please Register as MEMBER
Contact Person :
Administrator ([email protected])
Taufik Rachmanu ([email protected])
Dewi Eka Agustina ([email protected])
Ansi Aflacha Putri ([email protected])
Tondo Indra Nyata ([email protected])
Aprillia Tri Wulansari ([email protected])
Thank You,
Nur Hasan ( [email protected] )
Supervisor
Page 2
Recommended