Salzgitter: Fe- 2,5Al- 15 Mn- 2,5 Si steel grips 1 (2003) n5, pp333-339

Bleck steel research 79(2008)n2, 77-84

Hot stamping 22MnB5

Steel research 79 (2008) n2, pp 92-97

AS = Hot-dip aluminized

Numisheet 2008 22MnB5

Typical hot-stamping lines

Metallurgical structure after hot-stamping

100% martensitic

Hardness : 400 to 500 HV1

Homogeneous mechanical properties in any point of the parts : Ys 1100 MPa, Ts 1500 MPa, E (ISO) 6%

USIBOR 1500P

AlSi Coating after hot-stamping

Parts in Usibor 1500P