1. In a Positive Material Identification program, amaterial non-conformance is a test result that:
3.8 material nonconformance:
Is not consistent with the specified alloy.
2.
What is the remaining life of a piping system witha short-term corrosion rate of 0.010 in/yr (0.25mm/yr) and a long-term corrosion rate of 0.005
in/yr (0.13 mm/yr)? A minimum requiredthickness of 0.150" (3.8 mm), a remaining
thickness of 0.210" (5.3 mm), and an originalthickness of 0.270" (6.8 mm).
7.1.1 Long-term and short-term corrosion rates should be
compared to see which results in the shortest remaining life aspart of the data assessment.
3. How do you evaluate the effects of fire damage
on a piping system? 7.4 Utilizing API 579 Fitness-for-Service
4. The remaining life of a piping system shall be
calculated with what formula? 7.1.1 T actual - T minimum / corrosion rate
9/5/13 Printable Flashcard on API 570 Flashcards: Free Flash cards
www.proprofs.com/flashcards/cardshowall.php?title=api-570-flashcards 2/3
5. The owner-user shall specify industry qualified
UT Shear Wave Examiners when:
570 5.10 Trying to detect and size flaws for Fitness-for-Service evaluation.
6. What is the level of examination in a Material
Verification program?
578 3.5 level of examination:
The specified percentage of the number of components to be
examined.
7.
Substituting appropriate NDE procedures for apressure test after a repair may only be done
after:
570 8.2.6 Pressure Testing
Consultation with the inspector and the piping engineer.
8. API RP 579 provides procedures for:
570 5.3.11
API RP 579, Section 3 provides procedures for theassessment
of equipment for resistance to brittle fracture.
9.
When positive material identification (PMI) testingis required, portable X-ray fluorescence
spectrometer:
578 5.2.1 Portable X-ray Fluorescence
cannot be used to detect elements lighter than sulfur (S).
9/5/13 Printable Flashcard on API 570 Flashcards: Free Flash cards
www.proprofs.com/flashcards/cardshowall.php?title=api-570-flashcards 3/3
10. Piping system corrosion rates shall be calculated
on: 7.1.1 Either a short-term or long-term basis
11. API 578, Material Verification program for new
and existing alloy piping systems covers:
4.2.5 Components Covered in a MaterialVerification Program
Process valves (including control valves) and reliefvalves.
12.
A piping system with a high potentialconsequence of failure has a corrosion rate of 10
MPY, 0.010 in/yr (0.25 mm/yr), a retirement
thickness of .350" (8.9 mm), a required thickness
of .250 (6.4 mm), and an actual thickness today
of .500" (12.7 mm). What is the remaining life?
7.1.1 Remaining Life Calculations
13. Piping components identified by PMI as not
meeting the original piping specifications:
570 5.8
Would be targeted for replacement.