July 2008

METGRAF™ Products

  Controlled Expansion, Lightweight, High Thermal Conductivity Aluminum and Copper Graphite 

Fiber Composites for Thermal Management y Data METGRAF 4-230 METGRAF 7-200

  Al MetGraf 4‐230  Al MetGraf 7‐200  Cu MetGraf 7‐300  Cu MetGraf 4‐280 

Matrix Alloy  Al  Al  Cu  Cu TC (W/mK)         

In Plane (x‐y)  220‐230  185‐200  285‐300  265‐280 Thickness (z)  120  125  210  200 

Cp (J/g‐K)  0.852  0.879  0.433  0.448 CTE (Avg. 20°C to 150°C ppm/C)         

In Plane (x‐y)  4  7  7  4 Thickness (z)  24  24  16  16 

Tensile Strength (ksi)         In Plane (x‐y)  15  13.5  10  9.9 Thickness (z)    5.5  5   

Compressive Strength (ksi)  29.4  29.4  28.5   Yield Strength (ksi In Comp)  15.9  15.9  12.2   Young’s Modulus (msi)  14.3  12.9  11.0  10.4 Flexure Strength (ksi)  27  23  23   Electrical Resistivity (µ∙ohm∙cm)    6.89  4.36   Hardness (Rockwell E)    60‐80     Density (g/cc)  2.40  2.46  6.07  5.5 Plating  Ni, Au, Ag  Ni, Au, Ag  Ni, Au, Ag  Ni, Au, Ag Machinability  Excellent  Excellent  Excellent  Excellent 

METGRAF

™ is a trademark of Metal Matrix Cast Composites, LLC  

Technical information contained herein is furnished without charge or obligation, and is given and accepted at recipients sole risk.  