Technical data sheet
H08 – ISO/NPG-gelcoat - topcoat
Description
Gelcoat: based on iso-neopentylglycol – ISO/NPG pre-accelerated
Advantages: H08 ISO/NPG-gelcoat is distinguished especially by excellent UV resistance, very good osmosis resistance, good weather resistance, low yellowing and excellent mechanical values.
Process: brushable – PZ sprayable – SZ
Chemical and physical characteristics of the liquid gelcoat H08
Characteristics Typical values Unit Method
Appearance white liquid
Viscosity RFA at 25°C s 2 rpm 71,500 mPa.s I.O.801
20 rpm 11,000 mPa.s I.O.801
Thixotropic index 6.5 I.O.802
Gel time 25°C * 12 minutes I.O.803
Density at 25°C 1.25 g/cm³ I.O.805
Shelf life ** 3 months
* Gelcoat 200g + 2% MEKP 50
** Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened gelcoat H08***
Characteristics Typical values Unit Method
HDT 100 °C ASTM D 648
Elongation after tensile 2.5 % ASTM D 638
Barcol hardness 50 --- ASTM D 2583
*** Hardening parameter: gelcoat 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
To achieve best results we recommend:
1) a working temperature between 15°C and 28°C 2) addition of 1% to 2% hardener MEKP50 3) a layer thickness between 500 and 700 µ
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions. .
160418 order by phone: +49 9635 9202-0 barrier gelcoat – Silkcare M08 by E-mail: [email protected]
Technical data sheet
M08 ISO/NPG barrier gelcoat - SILKCARE
Description
Gelcoat: Isophthalic-neopentylene-buffer layer („barrier coat“) pre-accelerated, green gelcoat
Specifics: M08 – barrier coat was developed for optimizing the chemical-esthetical performance of the gelcoats in the field of shipbuilding and for mould making. It is a product easy to handle which allows a high quality finish on all fiber glass reinforced plastic parts.
Advantages: M08 – barrier coat is either used in spraying- or brushing process. Thus a first coat in vinylester is prevented, which guarantee the following advantages: time saving – less marks on the gelcoat – higher osmosis resistance – removal of the defects which were caused by incorrect rolling – low costs for the finish (sanding and polishing).
Process: Spraying-/ Brushing process
Chemical and physical characteristics of the liquid M08 - barrier coat
Characteristics Typical values Unit Method
Appearance bluish, liquid
Viscosity RFA at 25°C s 2 rpm 18,000 mPa.s I.O.801
20 rpm 3,000 mPa.s I.O.801
Thixotropic index 6.0 I.O.802
Gel time 25°C * 17 minutes I.O.803
Density at 25°C 0.95 g/cm³ I.O.805
Shelf life ** 3 months
* M08S53G15 200g + 2% MEKP 50 Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened M08 - barrier coat***
Characteristics Typical values Unit Method
HDT 60 °C ASTM D 648
*** Hardening parameter: M08S53G15 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
To achieve best results we recommend:
1) a working temperature between 15°C and 28°C 2) addition of 1% to 2% hardener MEKP50 3) a layer thickness between 900 and 1000 µ 4) to keep a distance of ca. 70/100 cm to the component part (rectangular
position) whilst spraying All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions. .
160418 order by phone: +49 9635 9202-0 Mould making gelcoat H09 by E-mail: [email protected]
Technical data sheet
H09 – Mould making-gelcoat
Description
Gelcoat: for mould making based on isophthalic acid, pre-accelerated
Specifics: H09 Mould making-gelcoat has a long-lasting gloss, good styrene resistance, very high surface hardness, no micro pore formation
Advantages: H09 Mould making-gelcoat is especially recommended for mould making, it is available in the colors orange, red, transparent-green, green, black.
Process: Brushing process, PZ Spraying process„ SZ“
Packaging: 25kg – plastic bucket / 220 kg - barrel
Chemical and physical characteristics of the liquid mould making gelcoat H09
Characteristics Typical values Unit
Viscosity – sprayable version (aspo4 20rpm) 4,500 ± 500 cps Brookfield
– brushable version (aspo5 20rpm) 12,000 ± 1000 cps Brookfield
Thixotropic – sprayable version (2/20rpm) 7.3 ± 0.3
– brushable version (2/20rpm) 6.5 ± 0.3
Gel time (200g + 2% MEKP at 50% vol.) 13 ± 4 minutes
Density depending on the colour) 1.15 ± 0.05 g/cm³
Burning point >21 °C
Shelf life * 3 months
*Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened mould making gelcoats H09**
Characteristics Typical values Unit Method
HDT 100° °C ISO R75
Elongation after tensile 2.0 % DIN 53455
Barcol hardness 50 --- ASTM 2583
** Hardening parameter: after 24 hours room temperature and 2 hours at 80°C
To achieve best results we recommend:
1) a room- and mould temperature between 15°C and 28°C 2) good mixing / stirring 3) addition of 1% to 2% hardener MEKP50 4) a layer thickness between 450 and 750 µ 5) not to add any solvents
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions.
160418 Bestellung per Telefon: +49 9635 9202-0 VE Formenbau-Gelcoat H13 per E-Mail: [email protected]
Technical data sheet
H13 – VE Mould making-gelcoat
Description
Gelcoat: based on vinylester-resin pre-accelerated
Specifics: H13 VE gelcoat for mould making
Advantages: H13 VE mould making gelcoat is a special developed gelcoat with following characteristics: no micro porosity, high surface hardness,
high styrene resistance and brilliant surface gloss.
Process: Brushing process – PZ Spraying process – SZ
Chemical and physical characteristics of the liquid VE mould making gelcoat H13
Characteristics Typical values Unit Method
Appearance green liquid
Viscosity RFA at 25°C s 2 rpm 37,500 mPa.s I.O.801
20 rpm 10,000 mPa.s I.O.801
Thixotropic index 7.0 I.O.802
Gel time 25°C * 13 minutes I.O.803
Density at 25°C 1.15 g/cm³ I.O.805
Shelf life ** 3 months
* gelcoat 200g + 2% MEKP 50
** Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened mould making gelcoat H13***
Characteristics Typical values Unit Method
HDT 100 °C ASTM D 648
Elongation after tensile 2.0 % ASTM D 638
Barcol hardness 50 --- ASTM D 2583
*** Hardening parameter: gelcoat 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
To achieve better results we recommend:
1) a working temperature between 15°C and 28°C 2) the addition of 1% to 2% hardener MEKP50 3) a layer thickness between 500 and 700 µ
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions. .
160418 order by phone: +49 9635 9202-0 H15 – Epocare -gelcoat by E-mail: [email protected]
Technical data sheet
H15 EPOCARE-gelcoat
Description
H15 Epocare is a pre-accelerated product, based on polyester resin, suitable for spraying- and brushing
process. It is deliverable in different colors.
Advantages:
H15 Epocare is distinguished by excellent osmosis resistance, good weather resistance, low yellowing, connected with a very low reduction of the gloss grade.
Due to its special composition Epocare offers good adhesion, also at components which aren’t produced with polyester resin but e.g. with epoxy resin.
Due to these characteristics it’s possible to laminate with epoxy resin on the Epocare-surface directly, without using a coupling agent.
Before using Epocare in your production, it’s urgently recommended to check the adhesion and compatibility with the epoxy resin.
Chemical and physical characteristics of the liquid Epocare
Characteristics Typical values Unit Method
Appearance pink liquid
Viscosity RFA at 25°C s 2 rpm 71,500 mPa.s I.O.801
20 rpm 11,000 mPa.s I.O.801
Thixotropic index 6.5 I.O.802
Gel time 25°C * 12 minutes I.O.803
Density at 25°C 1.20 g/cm³ I.O.805
Shelf life ** 3 months
* Epocare 100g + 2% MEKP 50
** Epocare must be stored in original packages, sealed, undamaged, dry, at a temperature between 5°C and 25°C.
Mechanical characteristics of the hardened Epocare***
Characteristics Typical values Unit Method
Barcol hardness 40 --- ASTM D 2583
*** Hardening parameter: gelcoat 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
2
160418 order by phone: +49 9635 9202-0 H15 – Epocare -gelcoat by E-mail: [email protected]
2
To achieve best results we recommend:
1) a working temperature between 15°C and 28°C 2) addition of 1% to 2% hardener MEKP50 3) a layer thickness between 400 and 600 µ 4) to make a trial before use in production.
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions.
160418 order by phone: +49 9635 9202-0 Avanti UP>EP coupling additive by E-mail: [email protected]
Technical data sheet
Avanti UP>EP coupling additive UP-gelcoat converter
Brief description:
With Avanti UP>EP coupling additive high quality SIRCA® ISO- or ISO-NPG-gelcoats become compatible gelcoats for numerous epoxy resins.
Avanti UP>EP coupling additive is no primer.
Avanti UP>EP coupling additive is ready for use and will be given into the SIRCA®-gelcoat directly without changing its premium characteristics.
Product advantages:
> Wide scope of use possibilities You can use the complete variety of SIRCA® ISO- or ISO-NPG-gelcoats. If transparent, grindable,
fire protection etc.; with Avanti UP>EP coupling additive the characteristics of the SIRCA®-gelcoats will not change.
> No color changes
You can choose any color from the wide SIRCA®-gelcoat-offer, Avanti UP>EP coupling additive doesn’t change the color.
> Resistance against UV-light and weather influences High quality SIRCA® ISO- or ISO-NPG-gelcoats are known for its high gloss grade and color
fidelity also under high UV load and changing weather influences.- Avanti UP>EP coupling
additive doesn’t change these positive characteristics.
> Multi compatible
Avanti UP>EP coupling additive is compatible to the most common epoxy-resin/hardener combinations. The epoxy laminate keeps all requested characteristics unchanged.
> Fast application The reactivity of SIRCA®-gelcoat remains unchanged. The epoxy laminate can be laminated at once after complete polymerization of the gelcoat. No additional treatment of the gelcoat surface is necessary.
> Hardening at room temperature Tempering follows is only necessary when gelcoat or EP resin are requesting it. Please consider here the technical data sheet of the producer.
2
160418 order by phone: +49 9635 9202-0 Avanti UP>EP coupling additive by E-mail: [email protected]
2
Working instruction:
Before the additive is mixed it must be heated to min. 25°C (e.g. in a bain-marie) and
shaken very well, to dissolve the components completely.
At room temperature Avanti UP>EP coupling additive is not completely clear. That‘s normal and no indicator for overlong storage.
Avanti UP>EP coupling additive is added in a dosage of 2% to SIRCA®-gelcoat. A packing unit with 500ml is calculated for a gelcoat package with 25 kg.
Avanti UP>EP coupling additive reduces viscosity and gel time of the gelcoat a little. Apply the gelcoat according to manufacturers‘ instructions. Here the mould can have room
temperature. At higher temperatures (30 - 35°C) the production cycle will shorten.
On the gelcoat epoxy resin can be laminated as soon as the gelcoat polymerized
completely and the surface of the complete face is non-adhesive and obviously free of
grease. Normally this is fact at latest after 48 hours. Using highly reactive gelcoats and hardeners it can be laminated further with epoxy resin already after few hours.
Prevent gelcoats which already contain paraffin or internal separating agents.
The shelf life of the gelcoat in principle remains unchanged by adding Avanti UP>EP
coupling additive. But for all opened packages it‘s recommended to use it promptly.
Storage:
At storage in the dark in closed original packages and max. 20°C the product is workable for 24 months after production date. At storage over this space of time and other storage conditions as described the characteristics can change resp. make the product unusable.
Avanti UP>EP coupling additive can get frozen, if it’s stored at very low temperatures.
Important note:
Due to various epoxy resin – and hardener combinations on the market we absolutely recommend to make a test laminate under production conditions before working.
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions.
160418 order by phone: +49 9635 9202-0 Gelcoat/Topcoat - survey by E-Mail: [email protected]
Product-survey
Gelcoat / Topcoat in all RAL-colours deliverable
within 36 hours !
H00 – Sanding-gelcoat Ortho - Brushing-/spraying process
grindable on base of orthophthalic acid grindable, pre-accelerated, contains fillers, is used at laminates, which will be varnished later, easy grindability, low shrinking and low pore formation. Suitable for products at which UV resistance and weather resistance is not in the fore.
H01 – Orthophthalic-gelcoat - Brushing-/spraying process
in nearly all RAL-colours available ideal for parts that are only exposed to low environmental influences.
H02 – Isophthalic-gelcoat - Brushing-/spraying process
in nearly all RAL-colours available good osmosis resistance, low yellowing, used in shipbuilding, transport, container building, building industry.
H03 – Iso-/Ortho-gelcoat - Brushing-/spraying process
pre-accelerated, good weather resistance, excellent water resistance, especially for silo building, small boats, billboards, coverings in outdoor areas, decorating materials etc.
H07 – Fire protection-gelcoat - Brushing-/spraying process
halogen free, available in many colours, high gloss, low yellowing and good fire resistance, suitable for applications at which esthetic but also functionality is requested.
H08 – ISO/NPG-gelcoat - Brushing-/spraying process
pre-accelerated, excellent UV-resistance, very good osmosis resistance, good weather resistance, low yellowing, excellent mechanical values.
M08 – ISO/NPG barrier gelcoat - Brushing-/spraying process
Easy usable product, that allows a high quality finish at all glass fiber reinforced plastic parts. Developed for the chemical-esthetical performance of gelcoats in shipbuilding and mould making.
H09 – Mould making gelcoat - Brushing-/spraying process
available in the colours, orange, black, green and transparent-green, long lasting glass, good stability against styrene, very high surface hardness, no micro pore formation, especially developed for mould making
H13 – VE-gelcoat - Brushing-/spraying process
no micro pore formation, high surface hardness, great stability against styrene and brilliant surface gloss.
H15 - Epocare-gelcoat - Brushing-/spraying process
pre-accelerated, based on unsaturated polyester resin, available in different colour versions. It’s distinguished by good osmosis- and weather resistance, low yellowing, connected with very low reduction of the glass grade. Clings to materials of polyester resin and epoxy resin.
Avanti UP>EP Coupling Additives - With this UP-gelcoat converter high quality SIRCA® ISO-
UP-gelcoat converter or ISO-NPG-gelcoats become compatible gelcoats for a great number of epoxy-resins.
160418 order by phone: +49 9635 9202-0 Sanding-gelcoat H00 - grindable by E-mail: [email protected]
Technical data sheet
H00 – Sanding-gelcoat – grindable
Description
Gelcoat: based on orthophthalic acid pre-accelerated, contains fillers
Specifics: H00 – sanding-gelcoat is used in laminates which are varnished later.
Advantages: H00 – sanding-gelcoat stand out for its easy grind ability, low shrinkage and low pore formation. It is recommended for products where UV resistance and weather resistance is not in the fore.
Process: Brushing process – PZ Spraying process – SZ
Chemical and physical characteristics of the liquid gelcoat H00
Characteristics Typical values Unit Method
Appearance white liquid
Viscosity RFA at 25°C s 2 rpm 91,000 mPa.s I.O.801
20 rpm 13,000 mPa.s I.O.801
Thixotropic index 7.0 I.O.802
Gel time 25°C * 12 minutes I.O.803
Density at 25°C 1.20 g/cm³ I.O.805
Shelf life ** 3 months
* Gelcoat 200g + 2% MEKP 50
** Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened gelcoat H00***
Characteristics Typical values Unit Method
HDT 60 °C ASTM D 648
Elongation after tensile 2.0 % ASTM D 638
Barcol hardness 45 --- ASTM D 2583
*** Hardening parameter: gelcoat 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
To achieve better results we recommend:
1) a working temperature between 15°C and 28°C 2) the addition of 1% to 2% hardener MEKP50 3) a layer thickness between 500 and 700 µ
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions. .
160418 order by phone: +49 9635 9202-0 ORTHO-gelcoat - topcoat H01 by E-mail: [email protected]
Technical data sheet
H01 – Orthophthalic-gelcoat - topcoat
Description
Gelcoat: based on orthophthalic acid
Specifics: H01-series products, exclusively produced on base of orthophthalic acid. They unite easy working and the good characteristics of the final product. The dyes of this gelcoat are the same as at ISO or ISO/NPG.
H01 is ideal for parts, which are only exposed to less environmental influences.
Versions: usually pre-accelerated available in nearly all RAL-colours
Process: Brushing process PZ Spraying process SZ paraffined PP or SP int. releasing agent SA or PA
Packaging: 25 kg – bucket with inliner / 220 kg – barrel/ 1000-1250 kg container
Chemical and physical characteristics of the liquid ortho-gelcoat H01
Characteristics Typical values Unit
Viscosity – sprayable version (aspo4 20rpm) 5,100 ± 400 cps Brookfield
-brushable version (aspo5 20rpm) 13,000 ± 1,000 cps Brookfield
Thixotropic – sprayable version (2/20rpm) 7.3 ± 0.3
– brushable version (2/20rpm) 6.5 ± 0.3
Gel time (200g + 2% MEKP with 50% vol.) 12 ± 4 minutes
Density (depending on the colour) 1.30 ± 0.05 g/cm³
Burning point >21 °C
Shelf life * 3 months
* Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
2
160418 order by phone: +49 9635 9202-0 ORTHO-gelcoat - topcoat H01 by E-mail: [email protected]
2
Mechanical characteristics of the hardened ortho-gelcoat H01**
Characteristics Typical values Unit Methode
HDT 70 °C ASTM D 648
Elongation after tensile 2.5 % ASTM D 638
Barcol hardness 45 --- ASTM D 2583
** Hardening parameter: after 24 hours room temperature and 2 hours at 80°C
To achieve best results we recommend:
1) gelcoat, mould- and room temperature between 15°C and 28°C 2) good mixing / stirring of the gelcoat before working starts 3) addition of 1% to 2% hardener MEKP50 4) a layer thickness between 450 and 750 µ 5) don’t add any solvents
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions.
First emission 04/08/1999 Erste Ausgabe
160418 order by phone: +49 9635 9202-0 ISO-gelcoat - topcoat H02 by E-mail: [email protected]
Technical data sheet
H02 – Isophthalic-gelcoat - topcoat
Description
Gelcoat: based on isophthalic acid resin
Specifics: H02-series products exclusively produced with isophthalic acid resin. Good chemical resistance, without disturbance of an easy working process. Good osmosis resistance, low yellowing.
H02 – Iso-gelcoat can be used in nearly all fields like e.g. shipbuilding, transport, container building and building industry.
Versions: usually pre-accelerated available in nearly all RAL-colours
Process: Brushing process PZ Spraying process SZ paraffined PP oder SP int. Releasing agent with SA or PA
Packaging: 25 kg – bucket with inliner / 220 kg – barrel / 1000-1250 kg container
Chemical and physical characteristics of the liquid isophthalic acid-gelcoat H02
Characteristics Typical values Unit
Viscosity – sprayable version (aspo4 20rpm) 5,100 ± 300 cps Brookfield
– brushable version (aspo5 20rpm) 13,000 ± 1,000 cps Brookfield
Thixotropic – sprayable version (2/20rpm) 7.5 ± 0.3
– brushable version (2/20rpm) 6.7 ± 0.3
Gel time (200g + 2% MEKP with 50% vol.) 12 ± 4 minutes
Density (depending on the colour) 1.19 ± 0.05 g/cm³
Burning point >21 °C
Shelf life * 3 months
* Gelcoat have to be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
2
160418 order by phone: +49 9635 9202-0 ISO-gelcoat - topcoat H02 by E-mail: [email protected]
2
Mechanical characteristics of the hardened isophthalic acid -gelcoats H02**
Characteristics Typical values Unit Method
HDT 90 °C ASTM D 648
Elongation after tensile 2.5 % ASTM D 638
Barcol hardness 45 --- ASTM D 2583
** Hardening parameter: after 24 hours at room temperature and 2 hours at 80°C
To achieve best results we recommend:
1) gelcoat, mould- and room temperature between 15°C and 28°C 2) good mixing / stirring of the gelcoat before working starts 3) addition of 1% to 2% hardener MEKP50 4) a layer thickness between 450 and 750 µ 5) don’t add any solvents
All information contained in this data sheet is based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions.
160418 order by phone: +49 9635 9202-0 ISO-ORTHO gelcoat - topcoat H03 by E-mail: [email protected]
Technical data sheet
H03 – ISO/Ortho-gelcoat - topcoat
Description
Gelcoat: based on isophthalic-orthophthalic acid, pre-accelerated; deliverable natural colored but also in nearly all RAL colors
Specifics: H03 – Iso/ortho-gelcoat was especially developed for the building of silos, small boats, which don’t have continuous water contact (like canoes, kayaks), billboards, coverings in outdoor areas, decorating materials a.s.o.
Advantages: H03 – Iso/ortho-gelcoat stands out especially for easy working, good weather resistance but also excellent water resistance.
Process: Brushing process – PZ Spraying process – SZ
Chemical and physical characteristics of the liquid gelcoats H03
Characteristics Typical values Unit Method
Appearance white liquid
Viscosity RFA at 25°C s 2 rpm 78,000 mPa.s I.O.801
20 rpm 12,000 mPa.s I.O.801
Thixotropic index 6.5 I.O.802
Gel time 25°C * 12 minutes I.O.803
Density at 25°C 1.3 g/cm³ I.O.805
Shelf life ** 3 months
* Gelcoat 200g + 2% MEKP 50
** Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened gelcoats H03***
Characteristics Typical values Unit Method
HDT 75 °C ASTM D 648
Elongation after tensile 2.5 % ASTM D 638
Barcol hardness 45 --- ASTM D 2583
*** Hardening parameter: gelcoat 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
To achieve best results we recommend:
1) a working temperature between 15°C and 28°C 2) addition of 1% to 2% hardener MEKP50 3) a layer thickness between 500 and 700 µ
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions. .
160418 order by phone: +49 9635 9202-0 Fire protection gelcoat H07 by E-mail: [email protected]
Technical data sheet
H07 – Fire protection gelcoat «Firecare gel»
Description
Gelcoat: halogen free fire protection gelcoat
Specifics: H07 is distinguished by high gloss, low yellowing and good fire resistance.
Advantages: H07 for applications where esthetic and functionality are requested.
H07 can be produced in many colours.
Process: Spraying- and brushing process
Certification: UNI CEI 11170-3 class 1A UNI 8457-UNI 9174 F1 AFNOR CEN-TS 45545-2 class HL 1 und HL 2, DIN 5510-2, class S4, SR2, ST2
Chemical and physical characteristics of the liquid fire protection gelcoat H07
Characteristics Typical values Unit Method
Appearance grey liquid
Viscosity RFA at 25°C s 2 rpm 35,750 mPa.s I.O.801
20 rpm 5,500 mPa.s I.O.801
Thixotropic index 6.5 I.O.802
Gel time 25°C * 13 minutes I.O.803
Density at 25°C 1.45 g/cm³ I.O.805
Shelf life ** 3 months
*Gelcoat 200g + 2% MEKP 50
** Gelcoat must be stored in original packages, sealed, undamaged, dry, at a temperature
between 5°C and 25°C.
Mechanical characteristics of the hardened fire protection-gelcoat H07***
Characteristics Typical values Unit Method
Elongation after tensile 2.0 % ASTM D 638
Barcol hardness 40 --- ASTM D 2583
*** Hardening parameter: gelcoat 100gr + 1.50 g MEKP50 - 24h RT + 2h at 100°C
To achieve best results we recommend:
1) a working temperature between 15°C and 28°C 2) addition of 1% up to 2% hardener MEKP50 3) a layer thickness between 500 and 700 µ, 4) to keep a working distance of 70 – 100 cm and to spray vertically
All information contained in this data sheet are based on our technical and scientific knowledge, but buyer and user should make their own trials with our products under their own use conditions.