Flocculates of Au nanoparticles in catalysis. NMSL – nanoAu and catalysis. Nanoparticle : AuNS-L-Pd. Goal Catalytic reaction within nanoparticle flocculates Experiment Cyclotrimerization of 3-hexyne in chloroform at r.t. Dispersed in DMSO. 取出上層. Dispersed in CHCl 3. 靜置. + DMSO. - PowerPoint PPT Presentation
Citation preview
Flocculates of Au nanoparticles in catalysis
NMSL – nanoAu and catalysis
04/21/23 B. Y. Wang, J. H. Chen 1
Nanoparticle : AuNS-L-Pd
• Goal– Catalytic reaction within nanoparticle
flocculates
• Experiment– Cyclotrimerization of 3-hexyne in chloroform
at r.t.
04/21/23B. Y. Wang, J. H. Chen 2
Dispersed in DMSO
Dispersed in CHCl3 + DMSO靜置
取出上
層
Sub-micron Flocculates Sub-micron Flocculates
Results
04/21/23 B. Y. Wang, J. H. Chen 3
(A)
(B)
(A)(A)
157±23 nm
300 400 500 600 700 800 900 1000 11000.00
0.05
0.10
(A) (B) (C)
Wavelength (nm)
Absorb
ance (A
U)
0.0
0.1
0.2
0.3
Dispersed in DMSO
Dispersed in CHCl3 + DMSOAging
Upper Soln
(C) (A) (B)(D)
(D)
Results
04/21/23 B. Y. Wang, J. H. Chen 4
(A) (B)
300 400 500 600 700 800 900 1000 11000.00
0.05
0.10
(A) (B) (C)
Wavelength (nm)
Absorb
ance (A
U)
0.0
0.1
0.2
0.3
(C)
(C)
(A)
(B)
Dispersed in DMSO
Dispersed in CHCl3 + DMSO
(C) (A) (B)(D)Aging
Upper Soln
Types Diagrams TEM images
A
B
C
Catalysis of different types
04/21/23 B. Y. Wang, J. H. Chen 5
Catalytic results
04/21/23 B. Y. Wang, J. H. Chen 6
Types Pd molParticle
weight (mg)Reaction time (hr)
Yield (%)
B 3x10-6 - 0.5 >99
A 3.92x10-7 1 0.5 11.52
B 3.92x10-7 1 0.5 14.47
C 4.02x10-7 1.7 0.5 0
A 0.92x10-7 0.6 1.5 2.69
B 0.92x10-7 0.6 1.5 5.19
C 1.07x10-7 2.2 1.5 0
1 c.c. CDCl3; 0.075 mmol reactant; R.T. ; Stir rate: 300 rpm
04/21/23 Richard Wang 7
樣品 Cat. M Cat. mol% 觸媒重量(mg)
反應時間 (min)
產率 (%)
RS/ L-Pd:
轉速(rpm)
備註
A 3x10-3 4 - 30 >99 - - A.林玉雲學姐的論文B.3.92x10-7 mol Pd/mgC.1.54x10-7 mol Pd/mgD.3,22x10-7 mol Pd/mgE.1.67x10-7 mol Pd/mgF.2.60x10-7 mol Pd/mg G.2.21x10-7 mol Pd/mgH.3.35x10-7 mol Pd/mg
CDCl3:1 ml ; 反應物 :0.075 mmol ;
*CDCl3:686 l反應物 :0.05 mmol
# CDCl3:500 l反應物 :0.0375 mmol
B(13) 3.92x10-4 0.52 1 30 14 - 300
C 0.92x10-4 0.12 0.6 90 5.2 1.1 300
D 1.6x10-4 0.21 0.50 1200 0 1.6 600
D 1.19x10-3 1.58 3.7 600 3.2 1.6 1200
E 1.67x10-4 0.22 1 780 0 - 600
F 6.24x10-4 0.83 2.40 720 0 1.4 600
F* 3.00x10-3 4.13 7.86 30 0 1.4 990
G 3.01x10-3 4.01 13.7 50 7.5 1 1200
G# 6.10x10-3 8.13 13.9 120 74 1 1200
H#(13)
6.10x10-3 8.13 9.1 60 53 0.8 1200
1(Liquid)
6.08x10-3 8.10 16.5 120 0 1.8 12001. 1.84x10-7 mol Pd/mg
04/21/23 B. Y. Wang, J. H. Chen 8
LL+L-Pd
L+L-Pd+thiol
L-Pd L-Pd8.28.6
507-Pd毒化實驗
04/21/23 B. Y. Wang, J. H. Chen 9
攪拌前攪拌後
8.28.6
Sample 1 攪拌前後光譜變化
04/21/23 B. Y. Wang, J. H. Chen 10
樣品 Cat MCat. mol
% 觸媒重量
(mg)
反應時間 (hr)
產率 (%)
RS/ L-Pd:
轉速(rpm)
備註
CyclotrimerizationG.2.21x10-7 mol
Pd/mgF. 1.84x10-7 mol Pd/mg
G 6.10x10-3 8.13 13.9 2 74 1 1200
1 6.08x10-3 8.10 16.5 2 0 1.8 1200
Heck reaction
G 1.33x10-7 0.00133 0.6 1.5 95 1 600
1 1.29x10-7 0.00129 0.7 1.5 85 1.8 600
04/21/23 B. Y. Wang, J. H. Chen 11
Sample G
04/21/23 B. Y. Wang, J. H. Chen 12
Sample 1
反應系統• Heck reaction
• Reaction condition : 115 oC for 1.5 hr
04/21/23 Richard Wang 13
O
O
I
O
O
10 mmol0.278 ml
Bp: 182 oC; MW: 203; D: 1.823 g/ml
10 mmol0.355 ml
Bp: 160 oC; MW: 128; D: 0.899 g/ml
Pd: 0.001 mol%
NEt3
0.375 mlBp: 88.8 oC;
0.25 ml DMSO
Need Pd 1x10-7 mol
反應系統• Cyclotrimerization
• Reaction condition : r.t. for 0.5 hr
04/21/23 Richard Wang 14
Et Et EtEt
Et Et
EtEt
0.075 mmol8.52 l
Bp: 81 oC; MW: 82.14; D: 0.723 g/ml
1 ml CHCl3 、 THF
Pd: 4 mol%
Need Pd 3x10-6 mol
RAW DATA
04/21/23 B. Y. Wang, J. H. Chen 15
A-1
04/21/23 B. Y. Wang, J. H. Chen 16
B-1
04/21/23 B. Y. Wang, J. H. Chen 17
A-2
04/21/23 B. Y. Wang, J. H. Chen 18
B-2
04/21/23 B. Y. Wang, J. H. Chen 19
C. AuNS-L-Pd
D. AuNS-L
D. AuNS-L-Pd
F. AuNS-L
F. AuNS-L-Pd
G. AuNS-L-Pd
H. AuNS-L
H. AuNS-L-Pd
04/21/23 B. Y. Wang, J. H. Chen 28
1. L-AuNS-L-Pd