CONCRETE COMPRESSIVE STRENGTHS
ITEM
CONCRETE STRENGTH
1 C12/15 12 1,741.00 2 C16/20 16 2,321.00 3 C20/25 20 2,902.00 4 C25/30 25 3,627.00 5 C30/37 30 4,352.00 6 C35/45 35 5,078.00 7 C40/50 40 5,803.00 8 C45/55 45 6,528.00 9 C50/60 50 7,254.00 10 C55/67 55 7,979.00 11 C60/75 60 8,704.00 12 C70/85 70 10,155.00 13 C80/95 80 11,605.00 14 C90/105 90 13,056.00
NOTE:As per EN 1992-1-1 per EN 206-1 (Standard)
CONCRETEGRADE
CYLINDERSTRENGTH
(MPa)
CYLINDERSTRENGTH
(psi)
CONCRETE STRENGTH MATERIAL WEIGHT AND MASS
15 2,176.00 24.9926 2,548.538 20 2,902.00 24.9926 2,548.538 25 3,627.00 24.9926 2,548.538 30 4,352.00 24.9926 2,548.538 37 5,368.00 24.9926 2,548.538 45 6,528.00 24.9926 2,548.538 50 7,254.00 24.9926 2,548.538 55 7,979.00 24.9926 2,548.538 60 8,704.00 24.9926 2,548.538 67 9,720.00 24.9926 2,548.538 75 10,880.00 24.9926 2,548.538 85 12,331.00 24.9926 2,548.538 95 13,781.00 24.9926 2,548.538 105 15,232.00 24.9926 2,548.538
CUBESTRENGTH
(MPa)
CUBESTRENGTH
(psi)
WEIGHT PER UNIT
VOLUME(kN/m3)
MASS PER UNITVOLUME(kg/m3)
MECHANICAL PROPERTY DATA
27,000 3,916,674 0.20 0.00001 29,000 4,206,798 0.20 0.00001 30,000 4,351,860 0.20 0.00001 31,000 4,496,922 0.20 0.00001 33,000 4,787,046 0.20 0.00001 34,000 4,932,108 0.20 0.00001 35,000 5,077,170 0.20 0.00001 36,000 5,222,232 0.20 0.00001 37,000 5,367,294 0.20 0.00001 38,000 5,512,356 0.20 0.00001 39,000 5,657,418 0.20 0.00001 41,000 5,947,542 0.20 0.00001 42,000 6,092,604 0.20 0.00001 44,000 6,382,728 0.20 0.00001
MODULUS OFELASTICITY
(MPa)
MODULUS OFELASTICITY
(psi)POISSON'SRATIO (U)
COEFFICIENT OF THERMAL
EXPANSION (A)(1/oC)
MECHANICAL PROPERTY DATA
11,250.00 1,631,948 12,083.33 1,752,833 12,500.00 1,813,275 12,916.67 1,873,718 13,750.00 1,994,603 14,166.67 2,055,046 14,583.33 2,115,488 15,000.00 2,175,930 15,416.67 2,236,373 15,833.33 2,296,815 16,250.00 2,357,258 17,083.33 2,478,143 17,500.00 2,538,585 18,333.33 2,659,470
SHEAR MODULUS (G)
(MPa)
SHEAR MODULUS (G)
(psi)
ETABS