Bone cement based nanohybrid as super biomaterial for bone healing
Govinda Kapusetti1, Nira Misra1, Vakil Singh2, Swati Srivastava3, Partha Roy3, Kausik
Dana4 and Pralay Maiti5,*
1School of Biomedical Engineering, Indian Institute of Technology
(Banaras Hindu University), Varanasi 221 005, India.
2Department of Metallurgical Engineering, Indian Institute of Technology
(Banaras Hindu University), Varanasi 221 005, India
3Department of Biotechnology, Indian Institute of Technology Roorkee 247667
Roorkee 247667, India
4Central Glass and Ceramic Research Institute, Kolkata 700 032, India
5School of Materials Science and Technology, Indian Institute of Technology
(Banaras Hindu University), Varanasi 221 005, India
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry B.This journal is © The Royal Society of Chemistry 2014
Figure S1: Low angle XRD plots revealing the nanostructures of (a) 30B nanoclay and its
intercalated nanohybrids with bone cement, (b) NK 75 nanoclay and its exfoliated nanohybrids
with bone cement and (c&d) High resolution TEM images of 1wt% of 30B and NK 75
nanofillars reinforced bone cement nanohybrids, respectively. Both XRD and TEM studies
indicate intercalated pattern of BC-B while BC-N nanohybrid exhibit exfoliated structure.
c d
a b
2 3 4 5 6 7 8
Inte
sity
(a.u
)
2deg
BC-N-2
BC-N-1.5
BC-N-1NK75
2 3 4 5 6 7 8
2.23
2.33
BC-B-1.5
Inte
nsity
(a.u
)
2deg
BC-B-1
30B 1.83
Figure S2: DSC thermogrammes of pure bone cement (BC) and its two indicated nanohybrids
(BC-B and BC-N) and vertical lines represent the Tg values of the indicated specimens. Scanning
rate was kept at 10o/min for all the specimens. The glass transition temperature show the
increasing trends for nanohybrids and amongst the nanohybrids BC-N exhibit highest glass
transition temperature owing to the better interaction between polymer and organophilic
nanoparticles.
50 75 100 125 150
98
101
H
eat f
low
endo
up
/ (a.
u)
T / (oC)
BC-B
BC- N
BC
108
Figure S3: Experimental setup for fatigue testing (a) metallic cemented stem implanted human
femur bone and its schematic diagram, (b) human hip joint (ilium) like setup (c) total
experimental setup with MTS machine.
Figure S4: Surface morphology through SEM after the cell attachment on bone cement and its
nanohybrids specimens for one day of incubation, (a) in pure bone cement, maximum cell are
found to be detached from the surface, (b) some number of cells are spread (shown by the arrow
and circle) and some are detached from the surface (rounded) of BC-B, and, (c) BC-N; it is
clearly visible that the cells have been fully spread tightly holding the surface of the BC-N
nanohybrid, and, (d) high resolution of the same image showing the cells grown on top of BC-N
nanohybrid tightly.
a b
c d
Figure S5: Hydroxy Apatite (HAP) formation on BC, BC-B and BC-N after 15 days of SBF
immersion. SEM and EDAX spectra show higher deposition of HAP is in the order of BC-N>
BC-B> BC. Inserted tables represent the Ca and P percentages as analyzed from the EDAX
patterns showing greater percentage of Ca and P on BC-N nanohybrid as compared to BC-B
nanohybrid.
Table shows the deposition of calcium (Ca) and phosphorous (P) content in BC, BC-B and
BC-N surface for 15 days SBF immersion.
Element BC BC-B BC-N
P 7.06 9.5 11.92
Ca 8.4 14.34 24.56
BC-N
100µm
BC
100µm
BC-B
100µm
Element Wt% At%
OK 77.67 82.79 PK 07.06 03.89 CaK 08.40 03.57
Element Wt% At%
OK 62.01 77.79 PK 09.50 06.16 CaK 14.34 7.18
Element Wt% At%
OK 63.53 79.92 PK 11.92 07.75 CaK 24.56 12.33
Table S1 shows the Mg and Fe contents in 30B and NK-75 nanoclays, calculated from Fig.
1.
Figure S6: Cell viability in different concentrations of Fe (2, 6 and 8%) and Mg (1, 3 and 5%)
ion containing systems were analyzed through apoptosis study in which green color represents
live cells and red color represent dead cells. From these images, it is clear that at low
concentrations of Mg (1 wt.%) shows high number of live cells but live cell density has reduced
Mg % Fe %
30B 2.5 2
NK75 0.9 8
1% 3% 5%
2% 6% 8%
Mg
Fe
with increasing concentration of Mg. In case of iron (Fe), live cell density has enhanced with
increasing its concentration up to 8%. The percentage of Fe or Mg was chosen to mimic the
concentration of respective ions in the composition of nanoclays (30B and NK-75).