Supporting Information for
Evaluation of the SERS performance of Ag nanoparticles
immobilized on glass by silanes using protic or aprotic
solvents
Andressa B. E. Reis1, Gabriela P. Oliveira1, Mariana R. Almeida1,
Benjamin Fragneaud2, Gustavo F. S. Andrade*,1
1 – Laboratório de Nanoestruturas Plasmônicas, Núcleo de Espectroscopia e Estrutura
Molecular, Departamento de Química, Universidade Federal de Juiz de Fora, R. José
Lourenço Kelmer s/n, Martelos, CEP 36036-900, Juiz de Fora, MG, Brazil.
2 – Departamento de Física, Universidade Federal de Juiz de Fora, R. José Lourenço
Kelmer s/n, Martelos, CEP 36036-900, Juiz de Fora, MG, Brazil.
S.1. SERS mapping of two bands of the CV dye for w-glass@AgNP and t-glass@AgNP in two exciting radiations (532 and 785 nm)
Figures S1 and S2 present the SERRS mappings at λ0= 532 nm of the band at
910 cm-1 of CV for APTMS deposited from water and toluene, respectively. Figures S3
and S4 present the SERRS mappings at λ0= 532 nm of the band at 1180 cm-1 of CV for
APTMS deposited from water and toluene, respectively Figures S5 and S6 present the
SERS mappings at λ0= 785 nm for the band at 910 cm-1 of CV for APTMS deposited
from water and toluene, respectively. Figures S7 and S8 present the SERS mappings at
λ0= 785 nm for the band at 1180 cm-1 of CV for APTMS deposited from water and
toluene, respectively.
1
Figure S1- SERRS mappings at λ0= 532 nm of the band at 910 cm-1 of CV for APTMS deposited from water.
Figure S2- SERRS mappings at λ0= 532 nm of the band at 910 cm-1 of CV for APTMS deposited from toluene.
2
Figure S3- SERRS mappings at λ0= 532 nm of the band at 1180 cm-1 of CV for APTMS deposited from water.
Figure S4- SERRS mappings at λ0= 532 nm of the band at 1180 cm-1 of CV for APTMS
deposited from toluene.
3
Figure S5- SERS mappings at λ0= 785 nm for the band at 910 cm-1 of CV for APTMS
deposited from water.
Figure S6- SERS mappings at λ0= 785 nm for the band at 910 cm-1 of CV for APTMS
deposited from toluene.
4
Figure S7- SERS mappings at λ0= 785 nm for the band at 1180 cm-1 of CV for APTMS
deposited from water.
Figure S8- SERS mappings at λ0= 785 nm for the band at 1180 cm-1 of CV for APTMS
deposited from toluene.
5
Figure S9 - SERRS mapping results for the CV band at 910 cm-1 after 5 AgNP depositions in both water and toluene excited with 532 nm.
Figure S10- SERS mapping results for the CV band at 910 cm-1 after 5 AgNP depositions in both water and toluene excited with 785 nm.
6