I/C: Kalluri Vinayak
Introduction
• The static load is a stationary force or couple applied to a member.
• Stationary means, the load should be unchanging in…
– magnitude
– point or points of application
– direction
9/24/2011 [email protected] 2
– direction
– or in any other manner
• A stationary force may cause
– axial tension or compression, shear load or bending moment or a torsional load or any combination of these
9/24/2011 [email protected]
Introduction• Failure means a part has had:
– separated into two or more pieces
– become permanently distorted and thus ruined its geometry
– its reliability downgraded
9/24/2011 [email protected] 3
– its reliability downgraded
– its function compromised
9/24/2011 [email protected]
Focus of this chapter is on first two cases i.e. predictability
of permanent distortion or separation
Introduction
• Static strength data of various materials may be available in two forms
– Data obtained in tests conducted in the similar conditions as the actual service life
– Data collected in tests conducted in certain ideal conditions that may not necessary simulate the exact service conditions
9/24/2011 [email protected] 4
exact service conditions
• The first type of data is always desirable but difficult to produce
• When second type of data is used, then the engineer must be clever enough to apply suitable factors
9/24/2011 [email protected]
Failure Theories• There is no general theory that is sacrosanct and unique; hence
we call them “failure theories”
• Rather it is a choice based on the design requirement and nature of material, whether ductile or brittle
• Ductile materials are designed based on yield criteria
�Maximum shear stress (MSS) theory
�Distortion energy (DE) theory
9/24/2011 [email protected] 5
�Distortion energy (DE) theory
�Ductile Coulomb-Mohr (DCM) theory
• Brittle materials, are designed based on fracture criteria
�Maximum normal stress (MNS) theory
�Brittle Coulomb-Mohr (BCM) theory
9/24/2011 [email protected]
Failure Theories• How do we know that the given material is ductile? The
judgment is based on the fracture strain.
• Ductile materials
Fracture strain, εf ≥ 0.05 and
identifiable yield strength is often the same in
compression as in tension i.e. Syt = Syc = Sy
9/24/2011 [email protected] 6
compression as in tension i.e. Syt = Syc = Sy
• Brittle materials
9/24/2011 6
ucut
f
SS
and
≠
< 05.0strain Fracture ε
Maximum-Shear-Stress (MSS) Theory
• Also referred to as the Tresca or Guest theory.
• Theory predicts that “yielding begins whenever the
maximum shear stress in any element equals or
exceeds the maximum shear stress in a tension test
specimen of the same material when that specimen
begins to yield”
9/24/2011 [email protected] 7
begins to yield”
• For a general state of stress, the maximum-shear-
stress theory predicts yielding when
9/24/2011 [email protected]
y
ySor
S≥−≥
−= 31
31max
22σσ
σστ
ysy SS 5.0 by, given isshear in strength yieldThe =
Maximum-Shear-Stress (MSS) Theory
• For design purposes, Equation can be modified to
incorporate a factor of safety, n.
for plane stress (one of the principal stresses is zero) and
assuming that σA ≥ σB:
n
Sor
n
S yy =−= 31max2
σστ
9/24/2011 [email protected] 8
assuming that σA ≥ σB:
9/24/2011 8
Case 1: σA ≥ σB ≥ 0.
For this case, σ1 = σA and σ3 = 0. Equation reduces to a yield condition of
Case 2: σA ≥ 0 ≥ σB .
Here, σ1 = σA and σ3 = σB , and Equation becomes
Case 3: 0 ≥ σA ≥ σB .
For this case, σ1 = 0 and σ3 = σB and Equation gives
n
S yA ≥σ
n
S yBA ≥−σσ
n
S yB
−≤σ
Maximum-Shear-Stress (MSS) Theory
n
S
n
S y
A
y
BA
BA
≥≥−
===
≥≥
σσσ
σσσσσ
σσ
,
0,,
,0
31
321
9/24/2011 [email protected] 99/24/2011 9
unmarked lines are cases for σB ≥ σA
n
S
n
S y
BA
y
BA
BA
≥−≥−
===
≥≥
σσσσ
σσσσσ
σσ
,
,0,
,0
31
321
n
S
n
S
y
B
y
B
A
BA
−≥−
≥−
=
=
=
≥≥
σ
σσ
σσ
σσ
σ
σσ
,
,
,0
,0
31
3
2
1
Problem
A ductile hot-rolled steel bar has minimum yield
strength in tension and compression of 350MPa.
Using the maximum-shear-stress theory,
determine the factors of safety for the following
plane stress states:plane stress states:
(a) σx = 100 MPa, σy = 50 MPa
(b) σx = 100 MPa, τxy = −75 MPa
(c) σx = −50 MPa, σy = −75MPa, τxy = −50 MPa
(d) σx = 100 MPa, σy = 20 MPa, τxy = −20 MPa
9/24/2011 [email protected] 10
Problem• The figure shows a crank loaded by a force F = 800 N which
causes twisting and bending of the 20 mm-diameter shaft fixed toa support at the origin of the reference system. In actuality, thesupport may be an inertia which we wish to rotate, but for thepurposes of a strength analysis we can consider this to be a staticsproblem. The material of the shaft AB is hot-rolled AISI 1018steel (Table A–20; Page: 1040). Using the maximum-shear-stresstheory, find the factor of safety based on the stress at point A.
9/24/2011 [email protected] 11
F
Distortion-Energy (DE) Theory
�Other names of distortional energy criterion
• The Hencky von- Mises or von-Mises theory
• The shear energy theory
• The octahedral shear stress theory
9/24/2011 [email protected] 129/24/2011 12
• The octahedral shear stress theory
Distortion-Energy (DE) Theory
9/24/2011 [email protected] 139/24/2011 13
ijσ pijδ'
ijij orS σ
ijijij Sp += δσ
• The strain energy per unit volume for simple tension
• For tri-axial stress, the strain energy per unit volume is
Distortion-Energy (DE) Theory
εσ2
1=u
][2
1332211 σεσεσε ++=u
9/24/2011 [email protected] 14
• Substituting for the principal strains gives
][2
332211 σεσεσε ++=u
[ ])(22
1133221
2
3
2
2
2
1 σσσσσσνσσσ ++−++=E
u
( )[ ] ( )[ ] ( )[ ]
+−=+−=+−= 213313223211
11;
1.. σσνσεσσνσεσσνσε
Eand
EEei
• The strain energy for producing only volume change is
• Substituting σav = (σ1 + σ2 + σ3)/3 gives
Distortion-Energy (DE) Theory
)21(2
3 2
νσ
−=E
u avv 321, σσσσ andforngsubstitutiby av[ ]
9/24/2011 [email protected] 15
• Substituting σav = (σ1 + σ2 + σ3)/3 gives
[ ]133221
2
3
2
2
2
1 2226
21σσσσσσσσσ
ν+++++
−=
Euv
Distortion-Energy (DE) Theory
[ ]
[ ]( ) ( ) ( ) −+−+−+
=
+++++−
−
++−++=−=
1
2226
21
)(22
1
222
133221
2
3
2
2
2
1
133221
2
3
2
2
2
1
σσσσσσν
σσσσσσσσσν
σσσσσσνσσσ
E
Euuu vd
• Then the distortion energy is
9/24/2011 [email protected] 16
( ) ( ) ( )
−+−+−+=
23
1 133221 σσσσσσνE
ud
2
321
3
1,
0
,
yd
y
SE
uenergydistortionthe
andS
yieldattesttensionsimpletheFor
ν
σσσ
+=
===
Distortion-Energy (DE) Theory• Theory predicts that “yielding occurs when the
distortion strain energy per unit volume reaches or
exceeds the distortion strain energy per unit volume
for yield in simple tension or compression of the
same material”
• For a general state of stress, the Distortion-Energy
Theory predicts yielding when
9/24/2011 [email protected] 17
Theory predicts yielding when
9/24/2011 17
Where “σ′ “is a single, equivalent, or effective stress called von Mises stress
( ) ( ) ( )yy SorS ≥≥
−+−+− '2
12
13
2
32
2
21
2σ
σσσσσσ
Distortion-Energy (DE) Theory
• For plane stress, let σA and σB be the two nonzero
principal stresses, then the von Mises stress is
• The above equation is a rotated ellipse in the σA, σB
plane with σ′ = S
( )21
22'
BBAA σσσσσ +−=
9/24/2011 [email protected] 18
plane with σ′ = Sy
9/24/2011 [email protected]
Distortion-Energy (DE) Theory
• Using xyz components of three-dimensional stress,
the von Mises stress can be written as
( ) ( ) ( ) ( )[ ]21
222222' 62
1zxyzxyxzzyyx τττσσσσσσσ +++−+−+−=
9/24/2011 [email protected] 19
• and for plane stress
9/24/2011 [email protected]
[ ]21
222' 3 xyyyxx τσσσσσ ++−=
• According to DE (von Mises) criterion, substituting
the pure shear state of stress in the 2-D DE criterion,
the two normal stresses being zero,
y
y
xyyxy SS
S 577.03
3 2 === ττ
SHEAR YIELD STRENGH:
Distortion-Energy (DE) Theory
9/24/2011 [email protected] 20
ysy
yxyyxy
SSyieldAt 577.0,
3
=
ysy SS 5.0=
According to the MSS criterion,
DE criterion predicts the shear yield strength to be 15 percent more than
that predicted by the MSS criterion. Hence MSS is more conservative.
9/24/2011 [email protected]
Distortion-Energy (DE) TheoryOctahedral shear stress:
� Considering the principal directions as the coordinate
axes, a plane whose normal vector makes equal angles
with each of the principal axes (i.e. having direction
cosines equal to ) is called an octahedral plane
� The shear stress acting on the so-called ‘octahedral
planes’ which are the eight planes that are normal to the
3
1
9/24/2011 [email protected] 219/24/2011 [email protected]
planes’ which are the eight planes that are normal to the
equi-inclined directions in the eight quadrants formed by
the principal stresses.
Sec. 2.4.4 (page : 36) of Arthur P. Boresi and Richard J.
Schmidt, Advanced Mechanics of Materials, 6th ed., John
Wiley & Sons, New York, 2003,
Distortion-Energy (DE) TheoryTHE OCTAHEDRAL PLANES: Octahedral shear stress theory
Failure occurs when the octahedral shear stress in the
given state of stress reaches the octahedral shear
stress in simple tension at yield.
9/24/2011 [email protected] 229/24/2011 [email protected]
Problem
A ductile hot-rolled steel bar has minimum yield
strength in tension and compression of 350MPa.
Using the distortion energy theory, determine
the factors of safety for the following plane
stress states:stress states:
(a) σx = 100 MPa, σy = 50 MPa
(b) σx = 100 MPa, τxy = −75 MPa
(c) σx = −50 MPa, σy = −75MPa, τxy = −50 MPa
(d) σx = 100 MPa, σy = 20 MPa, τxy = −20 MPa
9/24/2011 [email protected] 23
Problem• The figure shows a crank loaded by a force F = 800 N which
causes twisting and bending of the 20 mm-diameter shaft fixed toa support at the origin of the reference system. In actuality, thesupport may be an inertia which we wish to rotate, but for thepurposes of a strength analysis we can consider this to be a staticsproblem. The material of the shaft AB is hot-rolled AISI 1018steel (Table A–20; Page: 1040). Using the distortion energytheory, find the factor of safety based on the stress at point A.
9/24/2011 [email protected] 24
F
Table A–20; Page: 1040
9/24/2011 [email protected] 25
Ductile/Brittle Coulomb-Mohr TheoryTo be applied when the material has unequal strength in tension and
compression,ycyt SS ≠
Examples: magnesium alloy materials, for which ytyc SS 5.0≅
DCM is a simplification of the Coulomb- Mohr yield criteria.
Sec. 4.5.1 (page : 126) of Arthur P.
Gray Cast iron materials, for whichtuuc SoftimesS 43−≅
9/24/2011 [email protected] 269/24/2011 [email protected]
OR ⇒
where either yield strength or ultimate strength can be used
Sec. 4.5.1 (page : 126) of Arthur P.
Boresi and Richard J. Schmidt,
Advanced Mechanics of Materials,
6th ed., John Wiley & Sons, New
York, 2003,
Ductile Coulomb-Mohr Theory or Internal friction theory
For design equations, incorporating the factor of safety n, divide all strengths by n.
nSS ct
131 =−σσ
for plane stress (one of the principal stresses is zero) and assuming that σA ≥ σB:
Case 1: σA ≥ σB ≥ 0. Here, σ1 = σA and σ3 = 0. Equation reduces ton
StA ≥σ
1σσ
9/24/2011 [email protected] 27
Case 2: σA ≥ 0 ≥ σB . Here, σ1 = σA and σ3 = σB , Equation reduces to
Case 3: 0 ≥ σA ≥ σB . Here, σ1 = 0 and σ3 = σB, Equation reduces to
n
nSS c
B
t
A 1≥−
σσ
n
ScB ≤σ
Maximum-Normal-Stress Theory
• The maximum-normal-stress (MNS) theory
states that failure occurs whenever one of the
three principal stresses equals or exceeds the
strength.
• For the principal stresses for a general stress
state in the ordered form σ ≥ σ ≥ σ ; This
9/24/2011 [email protected] 28
state in the ordered form σ1 ≥ σ2 ≥ σ3; This
theory then predicts that failure occurs
whenever
σ1 ≥ Sut or σ3 ≤ −Suc
9/24/2011 28
where Sut and Suc are the ultimate tensile and compressive strengths, respectively,
given as positive quantities.
Maximum-Normal-Stress Theory• For plane stress, with σA ≥ σB,
σA ≥ Sut or σB ≤ −Suc
9/24/2011 [email protected] 299/24/2011 [email protected]
Modified Mohr Theory
9/24/2011 [email protected] 30
Failure theory selection flowchart
9/24/2011 [email protected] 31
ProblemThe figure shows a shaft mounted in bearings at A and D and having pulleys at
B and C. The forces shown acting on the pulley surfaces represent the belt
tensions. The shaft is to be made of ASTM grade 25 cast iron using a design
factor of 2. Based on Brittle Coulomb Mohr theory, What diameter should
be used for the shaft?
150 mm dia
1200 N
9/24/2011 [email protected] 32
A
B
C
D
200 mm
200 mm
150 mm200 mm dia
200 N120 N
1600 N
Table A–24 ; Page :1046-1047
Mechanical Properties of Three Non-Steel (Gray cast iron,
Aluminum, Titanium Alloy) Metals
(a) Typical Properties of Gray Cast Iron
9/24/2011 [email protected] 33
9/24/2011 [email protected] 34
9/24/2011 [email protected] 35