0871706903_ASM Electircl and Magnetic Properties of Metals

8/4/2019 0871706903_ASM Electircl and Magnetic Properties of Metals

1/292

ASM Ready Reference

Electrical and Magnetic

Properties of MetalsPrepared under the direction of theASM International Materials Properties Database Committee

Charles Moosbrugger, Technical EditorFran Cverna, Manager, Center for Materials Data

ASM International

Materials Park, Ohio 44073-0002www.asminternational.org

2000 ASM International. All Rights Reserved.ASM Ready Reference: Electrical and Magnetic Properties of Metals Data Book (#06333G)

www.asminternational.org


2/292

Copyright 2000by

ASM International All rights reserved

No part of this book may be reproduced, stored in a retrieval system, or transmitted, in any form or by anymeans,electronic, mechanical, photocopying,recording, or otherwise, without the written permissionof the copy-right owner.

First printing, December 2000

Great care is taken in the compilation and production of this book, but it should be made clear that NO WAR-RANTIES, EXPRESS OR IMPLIED, INCLUDING, WITHOUT LIMITATION, WARRANTIES OF MER-CHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE, ARE GIVEN IN CONNECTION WITHTHIS PUBLICATION. Although this information is believed to be accurate by ASM, ASMcannot guarantee thatfavorable results will be obtained from theuse ofthis publicationalone. This publicationis intended foruse by per-

sons havingtechnical skill, at their sole discretion andrisk.Since theconditions of product or material use are out-side of ASMs control, ASM assumes no liability or obligation in connection with any use of this information. Noclaim of any kind, whether as to products or information in this publication, and whether or not based on negli-gence,shallbe greater in amountthanthe purchase price of this product or publicationin respect ofwhichdamagesare claimed. THE REMEDY HEREBY PROVIDED SHALL BE THE EXCLUSIVE AND SOLE REMEDY OFBUYER,AND IN NO EVENT SHALL EITHERPARTY BE LIABLEFOR SPECIAL, INDIRECT OR CONSE-QUENTIAL DAMAGES WHETHER OR NOT CAUSED BY OR RESULTING FROM THE NEGLIGENCEOF SUCH PARTY. As with any material, evaluation of the material under end-use conditions prior to specifica-tion is essential. Therefore, specific testing under actual conditions is recommended.

Nothing contained in this book shall be construed as a grant of any right of manufacture, sale, use, or reproduc-tion, in connection with any method, process, apparatus, product, composition, or system, whether or not coveredby letters patent, copyright, or trademark, and nothing contained in this book shall be construed as a defenseagainst anyalleged infringementof letters patent, copyright, or trademark, or as a defense against liabilityfor suchinfringement.

Comments, criticisms, and suggestions are invited, and should be forwarded to ASM International.

Library of Congress Cataloging-in-Publication DataASM ready reference electrical and magnetic properties of metals / prepared under the direction of the ASM

International Materials Properties Database Committee; ASM International staff, Charles Moosbrugger,technical editor; Fran Cverna, manager, Center for Material Data.

p. cm.Includes bibliographical references and index.

1. MetalsElectric properties. 2. MetalsMagnetic properties. I. Title: Electrical and magnetic properties of metals. II. ASM International. Materials Properties Database Committee.

TA459.A79 2000 620.1697dc21 00-046881

ISBN: 0-87170-690-3

SAN: 204-7586

ASM International

Materials Park, OH 44073-0002www.asminternational.org

Printed in the United States of America




3/292

iii

Contributors and Reviewers

ASM International Materials PropertiesDatabase Committee, 20002001

J. Gilbert KaufmanKaufman Associates, Ltd.

Stephen R. Crosby

Stanley Tools

Paul J. SikorskyThe Trane Company

Howard W. Sizek

Special Metals Corporation

Bruce E. Boardman, ChairDeere & Company

Paul J. Sikorsky, Vice Chair

The Trane Company

J. Gilbert Kaufman, Past ChairKaufman Associates, Ltd.

Samir K. BanerjiCaterpillar, Inc.

David L. BourellUniversity of Texas at Austin

Steven A. BradleyUOP

Bryan R. Cope

American Spring Wire CorporationStephen R. Crosby

Stanley Tools

Earl (Bob) EatonGM PowertrainGeneral Motors Corporation

Barry HindinBattelle Memorial Institute

Gorden Lippa

North Star Casteel

Guiri L. NashElectromotive DivisionGeneral Motors Corporation

Charles A. ParkerHoneywell Aircraft Landing Systems

Howard W. SizekSpecial Metals Corporation

Jason M. SmithUniversity of Kentucky

John E. SmugereskySandia National Laboratories

Gary A. VolkIllinois Central College

Jack H. WestbrookBrookline Technologie




4/292

Contents

Preface. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . v

Materials Groups in Tables. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . vii

Part 1 Electrical Properties . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1

Chapter 1 Introduction to Electrical Properties. . . . . . . . . . . . . . . . . . . 3Chapter 2 High Conductivity Materials . . . . . . . . . . . . . . . . . . . . . . . . 6

Table 2.1 Volume Conductivity at Ambient Temperature of High Conductivity Material Families. . . . . . . . . . . . . . . . . . . . . . 7

Table 2.2 Volume Resistivity at Ambient Temperature of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . 42

Table 2.3a Weight Conductivity at Ambient Temperature of High Conductivity Aluminum Material Families . . . . . . . . . . . 60

Table 2.3b Weight Conductivity at Ambient Temperature of High Conductivity Copper Material Families . . . . . . . . . . . . . . 65

Table 2.4 Weight Resistivity at Ambient Temperature of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . 73

Table 2.5 Volume Resistivity at High and Low Temperatures of High Conductivity Material Families. . . . . . . . . . . . . . . . . . . . . 82

Table 2.6 Thermal Coefficient of Resistivity of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . 88

Table 2.7 Relative Resistivity at Extreme Temperatures of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . 92

Chapter 3 Higher Resistivity Materials. . . . . . . . . . . . . . . . . . . . . . . . 93Table 3.1 Volume Conductivity at Ambient Temperature of

Higher Resistivity Material Families . . . . . . . . . . . . . . . . . . . . . 94Table 3.2 Volume Resistivity at Ambient Temperature of

Higher Resistivity Material Families . . . . . . . . . . . . . . . . . . . . 102Table 3.3 Volume Resistivity at High and Low Temperatures of

Higher Resistivity Material Families . . . . . . . . . . . . . . . . . . . . 121Table 3.4 Thermal Coefficient of Resistivity of Higher

Resistivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . 143Chapter 4 Solders and Fusible Links . . . . . . . . . . . . . . . . . . . . . . . . 146

Table 4.1 Volume Conductivity of Solders and Fusible Links . 147Table 4.2 Volume Resistivity of Solders and Fusible Links. . . 150Table 4.3 Thermal Coefficient of Resistivity of Solders and

Fusible Links . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Chapter 5 Contact Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 156

Table 5.1 Volume Conductivity at Ambient Temperature of Contact Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 157

Table 5.2 Volume Resistivity at Ambient Temperature of Contact Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169

Table 5.3 Thermal Coefficient of Resistivity of Contact Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177

Chapter 6 Superconductivity. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 179Table 6.1 Volume Resistivity at Low and Superconducting

Temperatures . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 180

Table 6.2 Critical Temperature for Superconductors . . . . . . . . 186Table 6.3 Critical Fields of Superconductors . . . . . . . . . . . . . . 189Table 6.4 Critical Current Density for Superconductors . . . . . 190

Part 2 Magnetic Properties . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 191

Chapter 7 Introduction to Magnetic Properties. . . . . . . . . . . . . . . . . 193Chapter 8 Magnetically Soft Materials . . . . . . . . . . . . . . . . . . . . . . . 196

Table 8.1 Relative Permeability ( r) of Magnetically SoftMaterial Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 197

Table 8.2 Coercive Force (H c) of Magnetically SoftMaterial Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 209Table 8.3 Peak Induction (B m, Bmax ) Magnetically Soft

Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 215Table 8.4 Residual Induction (B r) Magnetically Soft

Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219Table 8.5 Curie Temperature (T c) of Magnetically Soft

Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222Table 8.6 Core Loss (P c) of Magnetically Soft Materials

Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 225Table 8.7 Hysteresis Loss (W h) of Magnetically Soft

Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 246Chapter 9 Magnetically Hard Materials . . . . . . . . . . . . . . . . . . . . . . 247

Table 9.1 Coercive Force (H c) of Magnetically Hard MaterialFamilies . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248

Table 9.2 Peak Induction (Bm

, Bmax

) of MagneticallyHard Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 253

Table 9.3 Residual Induction (B r) of MagneticallyHard Materials Families. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 254

Table 9.4 Curie Temperature (T c) of MagneticallyHard Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 258

Table 9.5 Energy Product (B dHd) of MagneticallyHard Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 260

Chapter 10 Paramagnetic and Diamagnetic Materials . . . . . . . . . . . 263Table 10.1 Relative Permeability ( r) of Paramagnetic and

Diamagnetic Material Families . . . . . . . . . . . . . . . . . . . . . . . . 264Table 10.2 Susceptibility ( ) of Paramagnetic and

Diamagnetic Material Families . . . . . . . . . . . . . . . . . . . . . . . . 267Table 10.3 Mass Susceptibility ( ) of Paramagnetic and

Diamagnetic Material Families . . . . . . . . . . . . . . . . . . . . . . . . 268

Part 3 Appendix. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 271Table A.1 Material Hierarchy . . . . . . . . . . . . . . . . . . . . . . . . . . 273Table A.2 Abbreviations Used in Qualifiers and Notes . . . . . . 280Table A.3 References . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 281Table A.4 Sizes of round wire in the American Gauge (AWG)

system and the properties of solid annealed copper wire(ASTM B 3) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 285

iv




5/292

Preface

This book is designed to serve the needs of the engineering andtechnical communities for high-quality and comprehensive informationregarding specific electrical and magnetic properties of metals.

In 1997, the ASM International Materials Properties DatabaseCommittee sponsored and reviewed the ASM Ready Reference: Properties& Units for Engineering Alloys. The Committee recognized the need forconsistency and equivalency when integrating materials properties datafrom multiple sources into printed or electronic reference publications.This second book in the Ready Reference series applies the principles of the first book to selected electrical and magnetic properties of metals. The

materials are sorted by a common materials hierarchy, and their propertyvalues are given in a consistent system of International Standard (SI) andcustomary units. The quality of the data and source of the data also arelisted to enable the user to assess the data.

The book chapters are broad categories of materials application:conductors, higher-resistance materials, permanent magnet materials, andso on. Materials properties significant to a specific application are listed ineach chapter. Each chapter begins with a brief explanation of the relatedproperties, derivation, and conversion of the units used within, along witha discussion of other units that the reader may encounter. We trust thiswill be of benefit to the reader already familiar with the basics of electricity and magnetism. We do not attempt to present a textbook onelectricity and magnetism in these brief introductions but seek to clarifypossibly confusing terminology.

The chapters naturally lend themselves to a division according tomaterials groups as well. Materials commonly used for the application arefound in the appropriate chapter.

The data tables in each chapter have the materials sorted by the materialhierarchy. The complete hierarchy for materials found in this book isgiven in Table A.1 of the Appendix. The Materials Groups in Tables,which follows, lists the materials groups found in each chapter. As withthe classification systems for materials in general use, the hierarchy ispredominantly based on composition, but there are subdivisions that areapplication based.

Data Format

Data entries include the following:

Material name: Trade name, generic alloy, element, or description asassigned by a standards organization

Temper: As stated UNS number: If assigned Property values in the preferred (SI) and alternate (customary) units:

The units used are those designated in ASM Ready Reference: Prop-erties & Units for Engineering Alloys. SI is the International Systemof Units (modernized metric system). The customary units are eitherEnglish (lb, in.) units, or cgs-emu (gauss, oersted),depending which isthe most prevalent alternative to the International Standard.

Qualifier for the value: This is the qualifier as stated in the source of the data, such as typical, nominal, or maximum. The most often usedabbreviations are listed on the bottom of the page. The complete list isgiven in Table A.2 in the Appendix.

Often, the source document will list the data as not for design, forinformation only. Not for design is applicable to all values listed

because there is no documented quality control process in place. It is,therefore, not listed on each record. If the value was derived from theinformation given in the source, such as conductivity is derived fromresistivity, or if units were converted, a d follows the value. Unitconversions that are merely a change in the value by a power of 10 are notlabeled as derived. Values without the d are those most directlyattributable to the source. A value can be established by definition or byspecification. There is still latitude as to how strictly the standard controlsthe material. It may be a mandatory or nonmandatory requirement, or onethat is at the mutual consent of the buyer and seller.

The parameter for which the value is valid is listed: Some propertieshave multiple parameters, such as magnetic properties having bothfield strength and frequency.

Notes: May include product forms, sizes, or processing informationfor whichthe value applies. Commonuses of thealloy maybe listed.

Limitations on the Use and Interpretation of Data

This book is intended to provide the materials engineer, scientist, orother specialist with a comparative listing of materials and their magneticand electrical properties, to aid in the materials selection process. Just asmost of the sources listed bear the caveat not for design, the compilationof this data requires the same warning. Great effort has been expended toensure that the source material has been faithfully duplicated, but ASM

International has no formal program whereby the validity of the data canbe ensured. The source references allow further investigation by thereader. It is the readers responsibility to take the prudent engineering andquality assurance steps necessary to ensure that any material selectedmeets the design requirements.

Significant Figures

Individual sources have listed values to varied significant figures inthe same data sets. The significant figures in values with trailing zeros(50,000), cannot be determined without more information. ASTM standardslist sufficient decimal places to improve the accuracy of conversion andreconversion of the data. They stress that this does not imply the need totest the material to an accuracy beyond what the specification or thereferenced test specification demands. For this reason, although the value

has been listed to the same number of significant figures as the originalwhen no derivation was required, no comparison should be made as to theprecision of the values based on the significant figures shown. Valuesshown as derived have at least as many significant figures as theoriginal source. Because the conversion calculations were done in mass,significant figures were added to some values to ensure that all hadsufficient significant figures to preserve the original accuracy.

Availability of Materials

Because it is often useful to have a source of data for historicalmaterials, obsolete materials and materials listed by former trade namesare included in the alloy field. No attempt was made to verify thecommercial availability of materials. If a source has identified a

v




6/292

designation as obsolete, this has been noted ( Woldmans Engineering Alloys, 9th ed., ASM International, 2000, offers this information).

Call for Future Action

Gil Kaufman, committee member, stated that the lack of comprehensive sources of accurate data that make this book valuablemakes compiling the data for the book difficult. A material database must

be a dynamic creation, under constant revision. We at ASM International,who have the dissemination of materials information at the core of ourvision statement, would ask that qualified parties contribute material datato the Society for the betterment of the technical community. Yoursuggestions, corrections, and comments are also welcome. They can bedirected to the addresses found on the title page.

Charles Moosbrugger

August 2000

vi




7/292

Materials Groups in Tables

Table 2.1 Volume Conductivity at Ambient Temperature of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7

Aluminum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7Sintered Powder Aluminum. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 11Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 11

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 19Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 19Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 22Welding filler copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 38Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 38Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 38Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 39Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 39

Thermostat Metals . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 41Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 41

Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 41

Table 2.2 Volume Resistivity at Ambient Temperature of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . 42

Aluminum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 42

Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 42Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 43

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 51Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 51Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 52Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 52

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 55Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 55Iridium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 56Osmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 56Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 56Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 56Rhodium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 57Ruthenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 57Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 57

Thermostat Metals . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 58Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 58

Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 59

Table 2.3a Weight Conductivity at Ambient Temperature of HighConductivity Aluminum Material Families. . . . . . . . . . . . . . . . . . 60

Aluminum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 60Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 60

Table 2.3b Weight Conductivity at Ambient Temperature of HighConductivity Copper Material Families . . . . . . . . . . . . . . . . . . . . 65

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 65Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 65

Table 2.4 Weight Resistivity at Ambient Temperature of HighConductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . 73

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 73Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 73

Table 2.5 Volume Resistivity at High and Low Temperatures of High Conductivity Material Families. . . . . . . . . . . . . . . . . . . . . . . 82


Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 83Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 83

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 84Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 84

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 84Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 84Iridium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 84Osmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 85Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 85Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 85Rhodium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 86Ruthenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 86Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 87

Table 2.6 Thermal Coefficient of Resistivity of High Conductivity

Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88Aluminum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88

Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 90Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 90

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 90Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 90Iridium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91Osmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91Rhodium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91Ruthenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91

Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91Table 2.7 Relative Resistivity at Extreme Temperatures of High

Conductivity Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . 92


Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 92Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 92Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 92

Table 3.1 Volume Conductivity at Ambient Temperature of HigherResistivity Material Families. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 94

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 94Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 94

vii




8/292

Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 94Magnesium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 94

Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 94Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 95

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 95Low Expansion. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 95Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 95Permanent Magnet . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 96

Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 97Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 97Electrical Resistance Nickel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 97Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 97Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 97

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98Molybdenum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98Niobium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98Rhenium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98Tantalum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 98

Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 99Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 99Carbon Steel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 100Cast Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 100Wrought Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 100

Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 101Zinc . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 101

Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 101

Table 3.2 Volume Resistivity at Ambient Temperature of HigherResistivity Material Families. . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102

Actinide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Plutonium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Uranium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102

Aluminum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102

Carbon . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Graphite . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102

Cast Iron. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Ductile . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Gray . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102White . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102

Ceramic Permanent Magnet. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103

Lanthanide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Dysprosium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Erbium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Europium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Gadolinium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Holmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Lutetium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Neodymium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Praseodymium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Samarium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Terbium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 103Thulium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 104Ytterbium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 104

Magnesium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 104Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 104Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 105

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 105Low Expansion. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 105Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 105Permanent Magnet . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 107Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Antimony . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Barium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Calcium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Manganese . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Potassium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Scandium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108

Sodium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Strontium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Technetium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 108Thallium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 109

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 109Electrical Resistance Nickel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . 109Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 109Miscellaneous Nickel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 109Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 109

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111

Rare Earth. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111Cerium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111Lanthanum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111Thorium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 112Yttrium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 112

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 112Beryllium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 112Chromium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 112Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 112Halfnium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113Molybdenum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113Niobium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113Rhenium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113Tantalum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113Vanadium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 115Zirconium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 115

Silicon . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 115Carbide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 115

Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 115Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 115Carbon Steel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 116Cast Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 116Wrought Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 117

Titanium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 119Titanium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 119

Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 120Zinc . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 120

Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 120Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 120

Table 3.3 Volume Resistivity at High and Low Temperatures of Higher Resistivity Material Families . . . . . . . . . . . . . . . . . . . . . . 121

Actinide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 121Neptunium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 121Plutonium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 121Uranium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 121

Lanthanide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 122Dysprosium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 122Erbium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 122Europium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 122Holmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 122Lutetium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 122Neodymium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123Praseodymium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123Samarium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123Terbium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123

viii




9/292

Thulium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123Magnesium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123

Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 123Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 124

Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 124Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 124

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 125Antimony . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 125

Barium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 125Calcium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 125Manganese . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 125Potassium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 126Scandium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 126Sodium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 127Strontium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 127Technetium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 127

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 128Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 128Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 128

Rare Earth. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 131Cerium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 131Lanthanum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 132Thorium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 132Yttrium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 132


Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 138Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 138Carbon Steel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 138Wrought Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 140


Zinc . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 141Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 141

Table 3.4 Thermal Coefficient of Resistivity of Higher Resistivity Material Families . . . . . . . . . . . . . . . . . . . . . . 143

Actinide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Uranium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143


Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143

Magnesium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Low Expansion. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Antimony . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Calcium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Sodium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143Thallium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 143

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Electrical Resistance Nickel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144

Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Beryllium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Chromium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144

Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Halfnium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144Molybdenum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Niobium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Rhenium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Tantalum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Vanadium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Zirconium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145

Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Wrought Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145


Zinc . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 145Table 4.1 Volume Conductivity of Solders and Fusible Links. . . . 147

Low melting . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 147Bismuth . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 147Indium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 147Lead . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 147Mercury . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 148Tin . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 148

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 150Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 150

Table 4.2 Volume Resistivity of Solders and Fusible Links . . . . . 151

Low Melting. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151Bismuth . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151

Cadmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151Cesium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151Gallium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151Indium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151Lead . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 152Lithium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 152Mercury . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 152Rubidium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 152Tin . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 153

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 154Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 154

Table 4.3 Thermal Coefficient of Resistivity of Solders and Fusible Links . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155

Low Melting. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155

Bismuth . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Cadmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Cesium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Indium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Lead . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Lithium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Rubidium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155Tin . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155

Table 5.1 Volume Conductivity at AmbientTemperature of Contact Materials . . . . . . . . . . . . . . . . . . . . . . . 157

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 157Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 157Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 157

ix




10/292

Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 157Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 158

Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 158Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 159Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 159Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 159

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 165Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 165

Molybdenum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 165Tantalum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 165Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 165

Table 5.2 Volume Resistivity at AmbientTemperature of Contact Materials. . . . . . . . . . . . . . . . . . . . . . . . 169

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169Iridium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 170Osmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 170Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 170Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 170Rhodium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 171Ruthenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 171Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 171



Table 5.3 Thermal Coefficient of Resistivity of Contact Materials. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Iridium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Osmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Rhodium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Ruthenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 177



Table 6.1 Volume Resistivity at Low andSuperconductingTemperatures . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 180


Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 180Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 180

Low Melting. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181Cesium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181Lithium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181Rubidium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181

Magnesium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181Barium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 181Calcium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 182Manganese . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 182Potassium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 182Sodium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 182Strontium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 182

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183Gold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183Palladium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183Silver . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 183

Rare Earth. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Cerium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Lanthanum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Thorium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Beryllium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Chromium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Halfnium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Molybdenum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 184Tantalum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 185

Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 185Vanadium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 185Zirconium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 185

Zinc . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 185Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 185

Table 6.2 Critical Temperature for Superconductors . . . . . . . . . 186

Actinide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Protactinium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Uranium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186


Lanthanide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Lutetium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186

Low Melting. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186

Bismuth . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Cadmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Gallium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Indium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Lead . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Mercury . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Tin . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Antimony . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Arsenic . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Barium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Germanium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Phosphorus. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Technetium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186

x




11/292

Thallium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 186Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187

Iridium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Osmium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Ruthenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187

Rare Earth. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Lanthanum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Thorium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187

Yttrium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Beryllium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Halfnium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Molybdenum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Niobium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Rehenium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Tantalum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Vanadium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 187Zirconium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 188


Zinc . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 188Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 188

Table 6.3 Critical Fields of Superconductors . . . . . . . . . . . . . . . . 189

Low Melting. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189Lead . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189

Rare Earth. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189Yttrium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189Niobium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189Vanadium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 189

Table 6.4 Critical Current Density for Superconductors. . . . . . . 190

Low Melting. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 190Lead . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 190

Rare Earth. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 190Yttrium. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 190

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 190Niobium . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 190

Table 8.1 Relative Permeability ( r) of MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 197

Cast Iron. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 197Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 197

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 197Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 197Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 203



Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 205Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 205Carbon Steel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 205Cast Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 205Wrought Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 206

Table 8.2 Coercive Force (H c) of MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 209

Cast Iron. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 209Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 209

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 209Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 209Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 210

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 210

Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 210Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 211



Table 8.3 Peak Induction (B m , B max ) MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 215

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 215Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 215

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 217Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 217



Table 8.4 Residual Induction (B r) of MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219

Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 219


Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 220Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 220Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 220


Table 8.5 Curie Temperature (T c) of MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222Low Expansion. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222Permanent Magnet . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222Unclassified . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 222

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 223Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 223Miscellaneous Nickel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 223Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 223


Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 224

Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 224Wrought Stainless . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 224

Table 8.6 Core Loss (P c) of MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 225


Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 243Magnetically Soft Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 243

Table 8.7 Hysteresis Loss (W h) of MagneticallySoft Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 246


xi




12/292

Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 246Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 246


Table 9.1 Coercive Force (H c) of Magnetically HardMaterial Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248

Cast Iron. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248

Miscellaneous. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248Ceramic Permanent Magnet. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248

Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248

Permanent Magnet . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 248Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 251

Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 251Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 251

Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 251Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 252

Table 9.2 Peak Induction (B m , B max ) of MagneticallyHard Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 253

Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 253

Permanent Magnet . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 253Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 253

Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 253

Table 9.3 Residual Induction (B r) of MagneticallyHard Materials Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 254

Ceramic Permanent Magnet. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 254Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 254

Magnetically Soft Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 254Permanent Magnet . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 254

Noble . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 256Platinum . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 256

Refractory. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 256Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 256Tungsten. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 256


Table 9.4 Curie Temperature (T c) of MagneticallyHard Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 258

Ceramic Permanent Magnet. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 258Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 258



Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 259

Table 9.5 Energy Product (B dH d) of Magnetically

Hard Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 260Ceramic Permanent Magnet. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 260Miscellaneous Iron Alloy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 260



Cobalt . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 261

Table 10.1 Relative Permeability ( r) Paramagnetic andDiamagnetic Material Families . . . . . . . . . . . . . . . . . . . . . . . . . . . 264

Copper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 264Cast. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 264Wrought . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 265


Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 265Nickel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 265

Refractory. . . .

Documents

0871706903_ASM Electircl and Magnetic Properties of Metals