www.WorldofTest.com/ames-portable-rockwell-hardness-testerQUALIMAG-R - Magnetic Rockwell Hardness Tester
Fix Rockwell test head to the surface of iron and steel parts to test the hardness by applying magnetic force. Follow Rockwell hardness test method completely and the test condition complies with standard of ISO 6508 and ASTM E18.
ApplicationApply in on-site quick test body hardness of steel parts Test steel plate, steel pipe, axis, mould, huge forgings and huge and medium-size heat treatment parts if surface available. Test hardness of weld joint in boiler, pressure vessels, and pressure pipes. Replace low accurate and reliable Leeb hardness testers.
Features• Attach to one side of part to test, no need to move it.
• Quick, convenient, no damage test.
• Similar reading system as micrometers, easy to read, and good repeatability.
• Rather high accuracy, complying with ISO 6508 and ASTM E18.
Technical parameters
Preliminary test force: 10Kg
Total test force: 60Kg, 100Kg, 150Kg
Test head: 120°diamond cone indenter, 1.588mm hard alloy ball
Indication Error: complying with ISO 6508 and ASTM E18
Repeatability Error: complying with ISO 6508 and ASTM E18
Test Resolution: 0.5HR
Weight: 4.7Kg
Surface: Flat: Area≥180mm×60mm, Thickness≥5mm
Cylinder: Diameter≥60mm, Lenghth≥200mm, Thickness≥8mm
Standard assembly• Tester
• 120°diamond cone indenter
• 1.588mm hard alloy ball
• Rockwell hardness block
• Adapter
• Microscope with light
• Carrying case
Optional accessories• 120°diamond
• 1.588mm hard alloy ball
• Rockwell hardness block (HRB, HRC high value, HRC middle value, HRC low value)
• Microscope with light
• Special Adapter (customized by required size)
Figure 1QualiMag-R - Magnetic Rockwell Hardness Tester
Toll-Free: 1.877.884.TEST (8378) | Fax: 954.697.8211
info@qualitest-inc.com | www.WorldofTest.com
USA Canada UAE Mexico India Hong Kong
TESTING TECHNOLOGIES
It permits customer to calibrate the tester with a standard block at any time. It could be operated under a temperature range of 0°C to 50°C either indoor or outdoor.
Standard Assembly• Tester
• 120°Diamond Indenter
• 1.588mm Carbide Alloy Ball Indenter
• Rockwell Hardness Block
• Seat Iron
• Recharger Battery Box
• Carrying Case
Technical Parameters
Initial Test Force : 10Kg
Total Test Force: 60Kg, 100Kg, 150Kg
Testing Range: 20~88HRA, 20~100HRB, and 20~70HRC
Testing Resolution: 0.1HR
Indication Error: complying with ISO6508,ASTM E18 standards
Repeatability Error: complying with ISO6508,ASTM E18 standards
Test Force Error: ≤±1%
Operating Temperature: 0~50°C
Nominal Dimension: 245mm×105mm×138mm
Weigh: 5.3Kg
Test Piece Surface: Flat : Area≥195mm×60mm, Thickness≥5mm
Cylinder: Diameter≥50mm, Lenghth≥200mm,Thickness≥8mm
Figure 2
QualiMag-DR - Digital Magnetic Rockwell Hardness Tester
QUALIMAG-DR - Digital Magnetic Rockwell Hardness Tester
ApplicationDigital magnetic rockwell hardness tester can be used to test too large or heavy iron and steel parts for the desk testers. It test the hardness of steel parts, bearings, moulds; large and medium-sized heating parts. Test a large batch of parts piece by piece on site. Replace inaccu-rate and unreliable Leeb hardness tester, in a wide range of manufacture industry.
FeaturesWorld leading product designed and manufactured by Qualitest, because of high-accuracy sensor and unique distance measuring technol-ogy, reaching far higher test accuracy than other portable hardness.It is onto the surface of a iron and steel part smartly with magnetic chucks. Simply reached one side of the part, the test could be accom-plished. Only if the surface is available, a iron and steel part could be tested, no matter what shapes and sizes are. It follows the Rockwell Hardness Test Principle, and complies with relevant regulation of ISO6508, and ASTM E18 standards. It the operation steps of Rockwell Hardness Test: directly load total test force; maintain it for a few seconds; release the total test force and then the test is It takes about only 10 seconds for a test, highly effective. It permits customer to calibrate the tester with a standard block at any time. It could be operated under a temperature range of 0°C to 50°C either indoor or outdoor.
Toll-Free: 1.877.884.TEST (8378) | Fax: 954.697.8211
info@qualitest-inc.com | www.WorldofTest.com
USA Canada UAE Mexico India Hong Kong
TESTING TECHNOLOGIES
QUALIMAG-DRB - Magnetic Digital Brinell And Rockwell Hardness Tester
ApplicationOnly if there is suitable surface, it could test large iron and steel work pieces whereas the desk tester could not. It could test the hardness of steel parts, bearings, moulds, castings, forge pieces and large and medium-sized heating parts.
FeaturesWorld portable Rapid Indentation Brinell hardness tester. It realizes rapid test and direct read of Brinell hardness and solves the world level of rapid and accurate body Brinell. It is a world leading product from Qualitest. For the high-accuracy sensor and unique distance measuring technology, it reaches far higher test accuracy than other portable hardness testers.It possesses test functions of both Brinell hardness and Rockwell hardness, satisfying most of hardness test demand of iron and steel work
pieces in the manufacturing industry. It the operation steps of Rockwell Hardness Test and Brinell Hardness Test: directly load total test force; maintain it for a few seconds; release the total test force and then the value of Rockwell hardness or Brinell hardness will display. It takes about only 10 to 20 seconds for a test, very effective.
No need of measuring indentation diameter by optical system prevents man-made error.It permits customer to calibrate the tester with a standard block at any time.
Standard Assembly• Tester
• 120°Diamond Indenter
• 1.588mm Carbide Alloy Ball Indenter
• 2.5mm Carbide Alloy Ball Indenter
• Rockwell Hardness Block
• Brinell Hardness Block
• Iron Seat
• Recharger
• Battery Box
• Carrying Case
Technical Parameters
Initial Test Force: 10Kg
Total Test Force: 60Kg, 100Kg, 150Kg,187.5kg
Testing Range: 20~88HRA, 20~100HRB, 20~70HRC and 100~450HBWT
Testing Resolution: 0.1HR or 1HBW
Indication Error: complying with ISO,ASTM standards
Repeatability Error: complying with ISO,ASTM standards
Test Force Error: ≤±1%
Operating Temperature: 0~50°C
Nominal Dimension: 245mm×105mm×138mm
Weight: 5.3Kg
Test Piece Surface: Flat: Area≥195mm×60mm,Thickness≥5mm
Cylinder: Diameter≥60mm, Lenghth≥200mm, Thickness≥8mm
Figure 3
Qualimag-DRB - Magnetic Digital Brinell And Rockwell Hardness Tester
Toll-Free: 1.877.884.TEST (8378) | Fax: 954.697.8211
info@qualitest-inc.com | www.WorldofTest.com
USA Canada UAE Mexico India Hong Kong
TESTING TECHNOLOGIES
Standard Assembly• Tester
• 120°Diamond Indenter
• 1.588mm Carbide Alloy Ball Indenter
• 2.5mm Carbide Alloy Ball Indenter
• Rockwell Hardness Block
• Brinell Hardness Block
• Seat Iron
• Recharger
• Battery Box
• Carrying Case
Figure 4
Qualimag-DRB II - Oil Drill Pipe Hardness Tester
QUALIMAG-DRB II - Oil Drill Pipe Hardness Tester
ApplicationTest the hardness of pipes, connects and weld bead of oil drill pipe piece by piece. Test the hardness of oil drill collars, steel oil pipes and other large machine parts in oil industry. Test the hardness of steel parts, bearings, moulds, castings, forge pieces and large and medium-sized heating parts and weld bead.
FeaturesIt possesses test functions of both Brinell hardness and Rockwell hardness, satisfying most of accurate hardness test demand of iron and steel work-pieces in the manufacturing industry. World portable Rapid Indentation Brinell hardness tester, realizing rapid test and direct read of Brinell hardness, complying with ASTM E103. World leading product from Qualitest with high-accuracy sensor and unique distance measuring technology, reaches far higher test accuracy than other portable hardness testers. Its single magnetic chuck structure solves the of rapid, non- destructive and accurate weld bead hardness test of oil drill pipe. It the operation of Rockwell Hardness Test and Brinell Hardness Test: directly load total test force; maintain it for a few seconds; release the total test force and then the value of Rockwell hardness or Brinell hardness will display. It takes about only 10 to 20 seconds for a test, high effective. No need of measuring indentation diameter by optical system, preventing personal error. It permits customer to calibrate the tester with a standard block at any time. It could be operated under a temperature range of 0°C to 50°C, indoor or outdoor.
Technical Parameters
Initial Test Force: 10Kg
Total Test Force: 60Kg, 100Kg, 150Kg,187.5kg
Testing Range: 20~88HRA, 20~100HRB, 20~70HRC, and 100~450HBWT
Testing Resolution: 0.1HR or 1HBW
Indication Error: complying with ISO,ASTM standards
Repeatability Error: complying with ISO,ASTM standards
Test Force Error: ≤±1%
Operating Temperature: 0~50°C
Nominal Dimension: 245mm×105mm×138mm
Weight: 11Kg
Test Piece Surface: Flat: Area≥195mm×60mm, Thickness≥5mm
Cylinder: Diameter≥50mm, Lenghth≥200mm
Thickness≥8mm
QUALIMAG
Toll-Free: 1.877.884.TEST (8378) | Fax: 954.697.8211
info@qualitest-inc.com | www.WorldofTest.com
USA Canada UAE Mexico India Hong Kong
TESTING TECHNOLOGIES
Figure 5Qualimag-B750 - Magnetic Hydraulic Brinell Hardness Tester
-B750 - Magnetic Hydraulic Brinell Hardness Tester
FeaturesTest applicable if attached to one side of part. No need to move the part. No need to search for a spot for clamping. Test condition of 5mm test ball, 750Kg test force, causes a larger indentation and better representativeness and easier to read than 2.5mm test ball condition. Compared with other hydraulic Brinell hardness testers, simpler operation, easier to carry. If surface available, test materials, parts and structural steel in any shape and size.
ApplicationFor castings, forgings, steel plates, steel pipes, structural and die steel, which other testers could not test or hard to test. For macro axis, crossbeam, huge or super-huge heat treatment parts. For pipe, huge equipment and huge steel structural parts that welded or assembled already. Only for the magnetizer steel.
Technical Parameters
Test force: 750kg
Test ball: 5mm hard alloy ball
Test range: 100~650HBW
Indicator Error: complies with ISO 6506, and ASTM E10.
Repeatability Error: complies with ISO 6506, and ASTM E10.
Test Force Error: complies with ISO 6506, and ASTM E10.
Weight: 15.8kg
Standard Assembly• Tester
• Load Handle
• Pinch bar
• Brinell Harness Block
• Seat Iron
• 40X Reading Microscope
• 5mm Spare Carbide Alloy Test Ball