Bioabsorbable stents: early clinical results Dr Angela Hoye MB ChB, PhD Senior Lecturer in...

Bioabsorbable stents: early clinical results

Dr Angela Hoye MB ChB, PhD

Senior Lecturer in Cardiology

Hull & East Yorkshire Hospitals

MY CONFLICTS OF INTEREST ARE:

Clinical Events Committee member for SPIRIT II, V and SPIRIT Woman, fees paid by Abbott Vascular Inc

• Review the clinical evidence available

Igaki-Tamai stent (Kyoto Medical Planning, Japan)• Poly-L-lactic acid (PLLA) self-expanding stent

• Strut thickness of 170µm

• FIM study of 50 patients (63 lesions)– 1 in-hospital stent thrombosis and Q-wave MI

– 1 non-cardiac death

– TLR (all with PCI): at 6 months 12%

at 12 months 17%

at 4 years 18%

– Late loss index (in the first 15 patients) was 0.48mm at 6 months

• Further studies in the SFA with this stent demonstrated feasibility and safety in deployment of these stents over a length of 70 mm – the stent has CE mark for use in PVD.

Tamai et al Circulation 2000;102(4):399-404; Tamai CCT 2004

Magnesium stent (AMS, Biotronik)• Balloon-expandable magnesium alloy

absorbable stent• The first clinical trial was performed in

20 patients with severe PVD with disease in the proximal two-thirds of one or more infrapopliteal arteries

• All were candidates for amputation and underwent PCI with the magnesium stent on a compassionate basis

• Following pre-dilatation, the 3.0×15 and 3.5×15 mm AMS were successfully deployed with good angiography and ultrasound results

• At 3 and 6 months post-implantation, the stent patency rates were 89% and 78%, respectively

• At 3 months, USS & MRI demonstrated complete AMS absorption • At 6 months follow-up, only 1 patient required amputation

Magnesium stent (AMS, Biotronik)• Coronary FIM multicentre study of 63 patients – PROGRESS-AMS

• The primary endpoint was MACE at 4 months and ischemia-driven TLR

• Safe: no death, no MI, no stent thrombosis

• The stent was well-expanded on deployment with no immediate recoil

• High restenosis rate with an in-stent late loss of 1.08 ± 0.49mm

Erbel et al Lancet 2007;369:1869-75Waksman et al JACC Cardiovasc Interv. 2009 Apr;2(4):312-20

Cumulative frequency curves of in-segment luminal narrowing before, immediately after and at 4 months follow-up after AMS

Ischaemia-driven TLR was 24% at 4 months, and 45% at 1 year

Erbel et al Lancet 2007;369:1869-75

Magnesium stent (AMS, Biotronik)• PROGRESS-AMS: results of IVUS

Magnesium stent (AMS, Biotronik)

Waksman et al JACC Cardiovasc Interv. 2009 Apr;2(4):312-20

Magnesium stent (AMS, Biotronik)• Return of coronary vaso-reactivity following absorption

• 5 patients treated with AMS compared with 10 treated with metal stents

• QCA was measured on two orthogonal views at 0.2mm intervals throughout the stented segments and a 1cm proximal reference segment before and after administration of 2mg intra-coronary ISDN

Ghimire et al Eurointervention 2008;4:481-4

REVA stent (Reva Medical)• Polycarbonate tyrosine-derived stent which

breaks down to amino acids, alcohol, and carbon dioxide. It is impregnated with iodine to improve radio-opacity

• Balloon-expandable and has a ratchet-like system so that as it expands the stent ratchets open and can't reclose down

• Radial support for 6 months• Stent absorption over 2 years• Interim analysis of 27 FIM patients demonstrated “unfavourable

results between 4 and 6 months with higher than expected TLR driven by reduced stent diameter”

Grube TCT 2008

REVA stent (Reva Medical)

OCT performed at 12 months demonstrated the presence of neointimal tissue covering the entire treated segment, and signs of stent absorption

REVA stent (Reva Medical)• Second generation stent with sirolimus on the

abluminal surface• Absorption time: 4 years• Duration strength 4-6 months• FIM due to start shortly

Pollman Eurointervention Suppl 2009,F54

BVS stent (Abbott Vascular)• PLA backbone, releases everolimus (80% by 30 days)• Struts are 150µm, radiopaque markers at either end• ABSORB cohort A FIM trial• 3x12 then 3x18mm BVS• Simple lesions

Ormiston et al Lancet 2008Serruys et al Lancet 2009

BVS stent (Abbott Vascular)• MACE rate was 3.4% (1 patient)• No “stent” thrombosis• In-”stent” late loss at 6 months was 0.43mm (0.47mm at 2 yrs)• Vessel and scaffold area changes:

Ormiston et al Lancet 2008Serruys et al Lancet 2009

• Vasomotion study (n=7)• Methergine (non-endothelial

dependent vasoconstrictor)• Shows the vessel is no

longer “splinted”

• Comparison of a Cypher stent and BVS on MSCT

• Allows non-invasive FU with quantification

• Results of ABSORB Cohort A were encouraging with only 1 MACE and resorption largely complete by 2 yrs

• The Cohort A scaffold had shrinkage at 6 months that was the major contributor to the late loss

device

– Same strut material, thickness, drug (everolimus) and resorption time

– More uniform strut distribution, vessel support and drug application

0.871.25

BVS 1.0 BVS 1.1

BVS stent (Abbott Vascular)• ABSORB Cohort B FIM trial• 3.0x18mm BVS to treat lesions ≤14mm in length

No thrombosis by ARC or ProtocolMACE: cardiac death, MI, ischaemia-driven TLRTLF: cardiac death, MI, ischaemia-driven TLR, ischemia-driven TVR

BVS stent (Abbott Vascular): Cohort B FIM trial

30 daysN=101

6 monthsN=101

Cardiac death (%) 0 0

MI (all non-Q-wave) (%) 2 3

Ischaemia-driven TLR (%) 0 2

PCI 0 2

CABG 0 0

MACE (%) 2 5

TLF (%) 2 5

In-”stent” late loss of BMS / Xience V / BVS 1.0 / BVS 1.1

Δ Vessel Area = +0.3%

Δ Stent Area = -11.8%

Δ Lumen Area = -16.8%

NIH Area (mm2) = 0.29% VO = 5.3%

ABSORB: BVS 1.0

Δ Vessel Area = +2.4%

Δ Stent Area = -2.0%

Δ Lumen Area = -3.1%

NIH Area (mm2) = 0.08 % VO = 1.2%

ABSORB: BVS 1.1

• Appears safe and effective • Limitations: Markers difficult to see in large patients

– Not tested in more complex anatomy– Should not re-introduce an undeployed stent as less

securely mounted– Aggressive post-dilatation will cause strut fracture

Summary & conclusions• Potential advantages of biodegradable stents:

– Shorter duration of dual anti-platelet therapy– Recovery of endothelial function– No remaining prosthesis therefore enabling future revascularization without

the increased MACE associated with treating an “in-stent restenosis”; no “full metal jacket”

– Potential for applications such as angiogenesis and gene transfer– Compatibility with non-invasive imaging modalities (CTA and MRI)

• The potential (long-term) advantages of biodegradable stents have to be weighed up against the limitations:– Lower strength compared to metallic stents → recoil– Relatively poor crossing profile– Radiolucent

Summary & conclusions• However, we have learnt much from the early clinical studies

– The importance of recoil and speed of stent absorption– The advantage of combining with anti-proliferative drug-elution

• Future work will focus on optimising the trade-off between stent deliverability, strut thickness, and optimal drug-elution – BVS testing in more complex disease– 2nd generation REVA which is sirolimus-eluting– 2nd generation AMS with drug-elution (DREAMS)– Elixir medical device (PLA sirolimus-eluting stent)– Biocorrodible iron stents etc etc etc.......................