FavorSea Magnesium Oxide BoardSerial No.:FSMO2013.1.1

http//www.FavorSea.com 1 info@favorsea.com

History

Characteristics

Magnesium oxide boards are a type of inorganic-bonded composite, Inorganic-bonded composites are those that contain a mineral or mineral mix as binder system, the three most common inorganic binder systems are magnesium oxide. Gypsum, and portland cement, The products produced from these binder systems are magnesium oxide boards, gypsum boards and fiber cement boards.Gypsum products, the most common of which is drywall board, have a long history, Conventional drywall board is a gypsum panel is wrapped with paper, the paper wrap gives the gypsum panel much of its strength.Another form of inorganic-bonded composites, cement-bonded wood composites, or as they are more commonly called, Cement boards, have a long history in Europe. The Philippines, Japan, and the United States were starting to use this material from 1980/1990s, Enforcement of stricter building codes accelerated the use of cement board, It is likely that there may have been less damage caused by the fires if fire-resistant roofing slates and cement-bond exterior panels had used earlier Cement board is a mixture of cement and wood or other lignocelluloses fiber, Cement-bonded wood composites are used in a wide range of building types.Compared with Gypsum boards and cement boards. Mgo (magnesium oxide) boards Is relatively unknown to most board users. There are two reasons.Firstly: Magnesium oxide (Mgo) boards are manufactured in Mainland China, as China has the suitable raw materials of good quality, in large volume at low cost.Secondly: Mgo boards have only 10 years of successful commercial history. Back in the 1950 the first generation of Mgo boards appeared on the market. The first generation Mgo boards were made by unskilled labor with rudimentary tools and the quality was low. The boards were easily broken and of variable thickness. Soon the first Generation Mgo boards lost much of its market due to low quality. However the technical experts of Mgo boards worked hard to improve the quality with various technical innovations. In 1990, the quality of Mgo board was improved considerably with the introduction of two layers of fiber glass mesh put into the Mgo board. As the market for Mgo board increased, concurrently with the gradual introduction of more sophisticated technology. From 1994, Mgo board begin to be exported to the world market. The first oversea market was Tainwan. In only about

three yesrs Mgo board established its good reputation From then on Mgo borad has repeated its success story in other oversea markets. Now mgo boards have been exported in large volumes of Mgo boards have been exported into Europe Japan and North America.

Magnesium oxide (MGO) Board is a building product with the following charactenstics Appearance: Mgo boards are white in color. Standard production is square edge or bevel edge boards with one smoother side and one rougher side

Size: Standard production is 4’x8.3’x6 and 3’x7. Maximum width is 4’a Maximum length is 8’, widths and lengths less than maximum can be custom produced on special orderThickness：Standard stock thickness is metric. From 3mm to 12mm

Square edge

Bevel edge

I N D U S T R I A L C H A N N E L

http//www.FavorSea.com 2info@favorsea.com

Applications

Mineral based. The main ingredient is magnesium oxide.Environmentally friendly. It does not contain asbestos or any other known toxic materialFire Resistant. A similar material is used in some parts of the world to line industrial blast furnaces Test results：Combustibility Non-combustibleFire- resistant limit (min) >180Fire and smoke development 0Heated size shrinkage ratio (%) 1.0Water Resistant: And does not leach.Test results：Moisture deformability（%）0.25Water drip-though 0Flexible, Does not break or crack easily. Wastage is therefore reduced. Flexibility is enhanced when wet.Test results:Dry-state bending strength (Mpa) 15Water-absorbing state bending strength 22Impact Resistant: 3mm mgo boards are at the same level with 9mm gypsum boards. Thicker mgo boards 6-12mm are mucsh trongerDampens sound. Can be used where sound insulation is requiredLightweight. Considerably Lighter than fiber cement boardTest results:Density (g/cm3) 900kg/M3 to 1100kg/m3 (56lbs/Ft3 to 68lbs/Ft3)Installs easily like gypsum board and fiber cement boards using stud, grid, nails or screws. The type of tape and mud used will depend on the application, I. e: fireproof or waterproofCompetitively pricedcompared to existing fireproof and waterproof material

Favorsea Mgo boards can be used wherever fire safety. Moisture, bug/fungus/moid resistance, and impact resistance, and impact resistance are primary considerations. These could be commercial high rise building s, single family home , multiple dwelling apartments, theaters, museums, schools, hospitals, malls, shopping centers , hotels, restaurants, night clubs, airports, subway stations, tunnels, fire separations, etc. Favorsea Mgo Board is now being introduced to the world market, you may wish to consider the advantages this revolutionary product offers over the materials you are now using, You might be able to save injury, breakage, time, and money, and at the same time deliver a better and safer finished product.

This combination of characteristics, unique among building materials .makes Mgo Board suitable for a wide range of applications:Partition walls Substrate for laminated panelsBacker board for tile installation Wrapping for steel structures Sub floors in framed structures Exterior sub walls Exterior signage (road, advertising)Construction site enclosure

Horizontal pallet

Vertical pallet

Favorsea warehouse

Mgo boards is being loaded into Container