BACK TO MAIN DATABASE BOGIE FASTENERS BACK TO EXCEL
CHEMICAL PROPERTIESs.no DESIGNA
TION C
Si
Mn P S Cr Al V Mo Ni Cu
1 IS 1079 St-42
≤0.25
≤0.050
≤0.050
2 IS 1875 CLASS 4
0.40-
0.50
0.15-0.35
0.60-0.90
≤0.04 ≤0.04
3 SAE 1006(BS
970 040A04)
≤0.080
0.25-0.40
≤0.040
≤0.050
4 SAE1008 ≤0.10
0.30-0.50
≤0.040
≤0.050
5 IS 5517 30C8
0.25-
0.35
0.10-0.35
0.60-0.90
≤0.035
≤0.035
6 IS 5517 35C8
0.30-
0.40
0.10-0.35
0.90-0.90
≤0.035
≤0.035
7 IS 5517 40C8
0.35-
0.45
0.10-0.35
0.60-0.90
≤0.035
≤0.035
8 IS 5517 45C8
0.40-
0.50
0.10-0.35
0.60-0.90
≤0.035
≤0.035
9 IS 5517 50C8
0.45-
0.55
0.10-0.35
0.60-0.90
≤0.035
≤0.035
10 IS 5517 55C8
0.50-
0.66
0.10-0.35
0.60-0.90
≤0.035
≤0.035
11 IS 5517 40C10S1
8
0.35-
0.45
≤0.25 0.80-1.20
≤0.035
≤0.035
12 IS 5517 40C15S1
2
0.35-
0.45
≤0.25 1.30-1.70
0.08-0.15
13 IS 5517 20C15
0.16-
0.24
0.10-0.35
1.30-1.70
≤0.035
≤0.035
14 IS 5517 27C15
0.22-
0.32
0.10-0.35
1.30-1.70
≤0.035
≤0.035
15 IS 5517 37C15
0.32-
0.42
0.10-0.35
1.30-1.70
≤0.035
≤0.035
16 IS 5517 35Mn6M
o3
0.30-
0.40
0.10-0.35
1.30-1.80
≤0.035
≤0.035
0.20-0.35
17 IS 5517 35Mn6M
o4
0.30-
0.40
0.10-0.35
1.30-1.80
≤0.035
≤0.035
0.35-0.55
18 IS 5517 37Mn5Si
5
0.33-
0.41
0.10-1.40
1.10-1.40
≤0.035
≤0.035
19 IS 5517 42Cr6V1
0.37-
0.47
0.15-0.35
0.50-0.80
≤0.035
≤0.035
1.40-
1.70
0.07-
0.1220 IS 5517
45CrSi90.40
-0.50
2.75-3.25
0.30-0.60
≤0.035
≤0.035
8.50-
9.5021 IS 5517
46V1S30.42
-0.50
≤0.60 0.60-1.00
≤0.035
0.045-0.065 0.08-
0.1322 IS 5517
58Cr4V10.53
-0.63
0.15-0.50
0.80-1.10
≤0.035
≤0.035
0.90-
1.20
0.07-
0.1223 IS 5517
50Cr4V20.45
-0.55
0.15-0.40
0.70-1.10
≤0.035
≤0.035
0.90-
1.20
0.10-
0.2024 IS 5517
55Cr30.50
-0.60
0.10-0.35
0.60-0.80
≤0.035
≤0.035
0.60-
0.80
25 IS 5517 55Si6Cr3
0.50-
0.60
1.20-1.60
0.50-0.80
≤0.035
≤0.035
0.50-
0.8026 IS 5517
40Cr40.35
-0.45
0.10-0.35
0.60-0.90
≤0.035
≤0.035
0.90-
1.2027 IS 5517
42Cr4Mo2
0.38-
0.45
0.10-0.35
0.60-0.90
≤0.035
≤0.035
0.90-
1.20
0.15-0.30
28 IS 5517 15Cr13M
o6
0.10-
0.20
0.10-0.35
0.40-0.70
≤0.035
≤0.035
2.90-
3.40
0.45-0.65
29 IS 5517 25Cr13M
o6
0.20-
0.30
0.10-0.35
0.40-0.70
≤0.035
≤0.035
2.90-
3.40
0.45-0.65
30 IS 5517 40Cr13M
o10V2
0.35-
0.45
0.10-0.35
0.40-0.70
≤0.035
≤0.035
3.00-
3.50
0.15-
0.25
0.90-1.10
31 IS 5517 40Cr7Al1
0Mo2
0.35-
0.45
0.10-0.35
0.40-0.70
≤0.035
≤0.035
1.50-
1.80
0.90-
1.30
0.10-0.25
32 IS 5517 40Ni14
0.35-
0.45
0.10-0.35
0.50-0.80
≤0.035
≤0.035
≤0.30
3.20-
3.6033 IS 5517
35Ni5Cr20.30
-0.40
0.10-0.35
0.60-0.90
≤0.035
≤0.035
0.45-
0.75
1.00-
1.5034 IS 5517
30Ni13Cr5
0.26-
0.34
0.10-0.35
0.40-0.90
≤0.035
≤0.035
1.00-
1.40
3.990-
4.3035 IS 5517
40Ni6Cr4Mo2
0.35-
0.45
0.10-0.35
0.40-0.70
≤0.035
≤0.035
0.90-
1.30
0.10-0.20
1.20-
1.6036 IS 5517
40Ni6Cr4Mo3
0.35-
0.45
0.10-0.35
0.40-0.70
≤0.035
≤0.035
0.90-
1.30
0.20-0.35
1.25-
1.7537 IS 5517
30Ni10Cr3Mo6
0.27-
0.35
0.10-0.35
0.40-0.70
≤0.035
≤0.035
0.50-
0.80
0.40-0.70
2.25-
2.7538 IS 5517
40Ni10Cr3Mo6
0.36-
0.44
0.10-0.35
0.40-0.70
≤0.035
≤0.035
0.50-
0.80
0.40-0.70
2.25-
2.75
MECHANICAL PROPERTIES
s.no DESIGNATION E(GPa) YS(MPa),min UTS(MPa),min Elongation(mm) HARDNESS1 IS 1079 St-42 236 412-491 222 IS 1875 CLASS 4 320 620 15 BHN(175)3 SAE 1006(BS 970
040A04) 190-210 285 330 20 BHN(95)
4 SAE1008 190-210 285 340 20 BHN(95)5 IS 5517 30C8 400 600-750 18 BHN(187-240)6 IS 5517 35C8 400 600-750 18 BHN(197-240)7 IS 5517 40C8 380 600-750 18 BHN(207-240)8 IS 5517 45C8 380 600-750 17 BHN(207-240)9 IS 5517 50C8 460 700-850 15 BHN(210-240)
10 IS 5517 55C8 460 700-850 15 BHN(220-250)11 IS 5517 40C10S18 380 600-750 18 BHN(200-240)12 IS 5517 40C15S12 500 700-850 18 BHN(200-240)13 IS 5517 20C15 440 600-750 18 BHN(200-240)14 IS 5517 27C15 440 600-750 18 BHN(200-240)15 IS 5517 37C15 440 600-750 18 BHN(220-250)16 IS 5517 35Mn6Mo3 540 700-850 18 BHN(220-250)17 IS 5517 35Mn6Mo4 600 800-950 16 BHN(220-250)18 IS 5517 37Mn5Si5 550 800-950 14 BHN(220-250)19 IS 5517 42Cr6V1 540 740-880 14 BHN(220-250)20 IS 5517 45CrSi9 685 880-1030 10 BHN(240-250)21 IS 5517 46V1S3 BHN(220-250)22 IS 5517 58Cr4V1 735 980-1180 12 BHN(250)23 IS 5517 50Cr4V2 590 780-980 13 BHN(250)24 IS 5517 55Cr3 660 900-1050 12 BHN(220-250)25 IS 5517 55Si6Cr3 1200 1400-1600 6 BHN(220-250)26 IS 5517 40Cr4 540 700-850 18 BHN(241-250)27 IS 5517 42Cr4Mo2 490 700-850 13 BHN(241-250)28 IS 5517 15Cr13Mo6 540 700-850 18 BHN(200-240)29 IS 5517 25Cr13Mo6 600 800-950 16 BHN(230)30 IS 5517 40Cr13Mo10V2 1120 1350 8 BHN(230)31 IS 5517 40Cr7Al10Mo2 540 700-850 18 BHN(230)32 IS 5517 40Ni14 600 800-950 16 BHN(229-250)33 IS 5517 35Ni5Cr2 540 700-850 18 BHN(229-250)34 IS 5517 30Ni13Cr5 1300 1550 8 BHN(250)35 IS 5517 40Ni6Cr4Mo2 600 800-950 16 BHN(241-250)36 IS 5517 40Ni6Cr4Mo3 600 800-950 16 BHN(241)37 IS 5517 30Ni10Cr3Mo6 700 900-1050 15 BHN(269)38 IS 5517 40Ni10Cr3Mo6 800 1000-1150 12 BHN(269)
MICROSTRUCTURE
MICROSTRUCTURE OF AISI 1008
MICROSTRUCTURE OF SAE 1006
MICROSTRUCTURE OF SAE 1008
REFERENCE
http://www.calculatoredge.com/charts/mshot.htmhttp://rdso.indianrailways.gov.in/works/uploads/File/IRS-T-1-2011.pdfhttp://www.azom.com/article.aspx?ArticleID=6537http://www.azom.com/article.aspx?ArticleID=6538https://law.resource.org/pub/in/bis/S10/is.1570.4.1988.pdfhttp://steelplate.co.in/corten-types-grades.html